1.
本文对Cu-0.1Ag-0.18Zr-0.068Ce合金时效后的导电率和显微硬度以及电滑动磨损性能进行了研究.结果表明合金940℃固溶1 h后,在560℃时效可获得较高的导电率;在480℃时效可获得较高的显微硬度.时效前冷变形能大大加快第二相的析出过程,使合金综合性能得到显著提高.固溶合金经60%变形后在480℃时效1 h其导电率和显微硬度分别可达83%IACS和135 HV.在载流条件下,Cu-0.1Ag-0.18Zr-0.068Ce合金的耐磨性能较Cu-0.1Ag-0.18Zr合金大幅度提高. 相似文献
2.
3.
稀土Y掺杂对Cu-Cr-Zr合金时效性能的影响 总被引:6,自引:0,他引:6
研究了时效参数和变形量对Cu-Cr-Zr-Y合金时效性能的影响.结果表明:Cu-0.41Cr-0.10 Zr合金在950℃×1h固溶后,在520℃时效2 h能获得较高的显微硬度和导电率;固溶后合金经60%变形后在520℃时效30 min时,硬度可达147.9 HV,导电率可达83.97%IACS,比固溶后直接时效分别高出约41HV和14%IACS.而加入稀土元素Y后,使Cu-Cr-Zr合金的显微硬度提高了约9HV,而导电率降低了约3%IACS. 相似文献
4.
5.
本文在中频感应炉中采用大气熔铸方法制备了CuCr25合金触头材料,探讨了时效以及变形对导电率和显微硬度的影响,并测定了该合金的抗软化温度。结果表明:在950×1h固溶后,经440℃时效6h可获得较高的导电率和显微硬度:固溶后经40%变形在440℃时效2h后,导电率和显微硬度分别可达57%IACS和174Hv,比固溶后直接时效分别高出10%IACS和27HV:并测得合金的抗软化温度约为55℃。 相似文献
6.
7.
8.
9.
10.
研究了时效温度和时效时间对不同冷变形条件下Cu-2.0Ni-0.5Si-0.15Ag合金组织和性能的影响.结果表明,Cu-2.0Ni-0.5Si-0.15Ag合金经900 ℃×1 h固溶处理和不同预冷变形,在450 ℃和500 ℃时效处理,第二相呈弥散分布,能获得较高的显微硬度与导电率,析出相为Ni2Si相.当变形量为80%、时效温度达到500 ℃时,其显微硬度达到252 HV0.1,导电率达到45%IACS;合金经40%变形、450 ℃×4 h时效处理后,其抗拉强度达到680 MPa. 相似文献
11.
Deng-Kui Zhang Guo-Qing Wang Ai-Ping Wu Ji-Guo Shan Yue Zhao Tian-Yi Zhao Dan-Yang Meng Jian-Ling Song Zhong-Ping Zhang 《金属学报(英文版)》2019,32(6):684-694
In as-welded state, each region of 2219 aluminum alloy TIG-welded joint shows diff erent microstructure and microhardness due to the diff erent welding heat cycles and the resulting evolution of second phases. After the post-weld heat treatment, both the amount and the size of the eutectic structure or θ phases decreased. Correspondingly, both the Cu content in α-Al matrix and the microhardness increased to a similar level in each region of the joint, and the tensile strength of the entire joint was greatly improved. Post-weld heat treatment played the role of solid solution strengthening and aging strengthening. After the post-weld heat treatment, the weld performance became similar to other regions, but weld reinforcements lost their reinforcing eff ect on the weld and their existence was more of an adverse eff ect. The joint without weld reinforcements after the post-weld heat treatment had the optimal tensile properties, and the specimens randomly crack in the weld zone. 相似文献
12.
After nearly two years'tense construction the first phase of industrialized base of Shenyang Research Institute of Foundry 《中国铸造》2008,5(1):63-64
After nearly two years' tense construction, the first phase of industrialized base of Shenyang Research Institute of Foundry (SRIF), located at the Tiexi Casting and Forging Industrial Park in the west of Tiexi District, has now been completed and formally put into operation. 相似文献
13.
Z. Sun S.L. Zheng Y. Zhang 《金属学报(英文版)》2007,20(3):187-192
Institute of Process Engineering, Chinese Academy of Sciences, China, has proposed a method for oxidative leaching of chromite with potassium hydroxide. Understanding the mechanism of chromite decomposition, especially in the potassium hydroxide fusion, is important for the optimization of the operating parameters of the oxidative leaching process. A traditional thermodynamic method is proposed and the thermal decomposition and the reaction decomposition during the oxidative leaching of chromite with KOH and oxygen is discussed, which suggests that chromite is mainly destroyed by reactions with KOH and oxygen. Meanwhile, equilibrium of the main reactions of the above process was calculated at different temperatures and oxygen partial pressures. The stable zones of productions, namely, K2CrO4 and Fe2O3, increase with the decrease of temperature, which indicates that higher temperature is not beneficial to thermodynamic reactions. In addition, a comparison of the general alkali methods is carried out, and it is concluded that the KOH leaching process is thermodynamically superior to the conventional chromate production process. 相似文献
14.
R. González-Martínez 《金属学报(英文版)》2007,20(4):235-240
The effect of isochronal heat treatments for 1h on variation of damping, hardness and microstructural change of the magnesium wrought alloy AZ61 was investigated. Damping and hardness behaviour could be attributed to the evolution of precipitation process. The influence of precipitation on damping behaviour was explained in the framework of the dislocation string model of Granato and Lücke. 相似文献
15.
The Lanthanum-doped bismuth ferrite–lead titanate compositions of 0.5(Bi LaxFe1-xO3)–0.5(Pb Ti O3)(x = 0.05,0.10,0.15,0.20)(BLxF1-x-PT) were prepared by mixed oxide method.Structural characterization was performed by X-ray diffraction and shows a tetragonal structure at room temperature.The lattice parameter c/a ratio decreases with increasing of La(x = 0.05–0.20) concentration of the composites.The effect of charge carrier/ion hopping mechanism,conductivity,relaxation process and impedance parameters was studied using an impedance analyzer in a wide frequency range(102–106Hz) at different temperatures.The nature of Nyquist plot confirms the presence of bulk effects only,and non-Debye type of relaxation processes occurs in the composites.The electrical modulus exhibits an important role of the hopping mechanism in the electrical transport process of the materials.The ac conductivity and dc conductivity of the materials were studied,and the activation energy found to be 0.81,0.77,0.76 and 0.74 e V for all compositions of x = 0.05–0.20 at different temperatures(200–300 °C). 相似文献
16.
This work was to reveal the residual stress profile in electron beam welded Ti-6Al-4V alloy plates(50 mm thick) by using finite element and contour measurement methods.A three-dimensional finite element model of 50-mmthick titanium component was proposed,in which a column–cone combined heat source model was used to simulate the temperature field and a thermo-elastic–plastic model to analyze residual stress in a weld joint based on ABAQUS software.Considering the uncertainty of welding simulation,the computation was calibrated by experimental data of contour measurement method.Both test and simulated results show that residual stresses on the surface and inside the weld zone are significantly different and present a narrow and large gradient feature in the weld joint.The peak tensile stress exceeds the yield strength of base materials inside weld,which are distinctly different from residual stress of the thin Ti-6Al-4V alloy plates presented in references before. 相似文献
17.
Chao Yang He-Fei Huang Massey de los Reyes Long Yan Xing-Tai Zhou Tian Xia De-Liang Zhang 《金属学报(英文版)》2015,28(7):809
Silicon carbide nanoparticle-reinforced nickel-based composites(Ni–Si CNP),with a Si CNPcontent ranged from1 to 3.5 wt%,were prepared using mechanical alloying and spark plasma sintering.In addition,unreinforced pure nickel samples were also prepared for comparative purposes.To characterize the microstructural properties of both the unreinforced pure nickel and the Ni–Si CNPcomposites transmission electron microscopy(TEM) was used,while their mechanical behavior was investigated using the Vickers pyramid method for hardness measurements and a universal tensile testing machine for tensile tests.TEM results showed an array of dislocation lines decorated in the sintered pure nickel sample,whereas,for the Ni–Si CNPcomposites,the presence of nano-dispersed Si CNPand twinning crystals was observed.These homogeneously distributed Si CNPwere found located either within the matrix,between twins or on grain boundaries.For the Ni–Si CNPcomposites,coerced coarsening of the Si CNPassembly occurred with increasing Si CNPcontent.Furthermore,the grain sizes of the Ni–Si CNPcomposites were much finer than that of the unreinforced pure nickel,which was considered to be due to the composite ball milling process.In all cases,the Ni–Si CNPcomposites showed higher strengths and hardness values than the unreinforced pure nickel,likely due to a combination of dispersion strengthening(Orowan effects) and particle strengthening(Hall–Petch effects).For the Ni–Si CNPcomposites,the strength increased initially and then decreased as a function of Si CNPcontent,whereas their elongation percentages decreased linearly.Compared to all materials tested,the Ni–Si CNPcomposite containing 1.5% Si C was found more superior considering both their strength and plastic properties. 相似文献
18.
Lei Li Bo Xu Wei-Ping Tong Hui Zhang Chun-Yan Ban Li-Zi He Zhi-Hao Zhao Yu-Bo Zuo Qing-Feng Zhu Jian-Zhong Cui 《金属学报(英文版)》2015,28(6):725
A new method was introduced to achieve directional growth of Sn crystals. Microstructures in liquid(Pb)/liquid(Sn) diffusion couples were investigated under various static magnetic fields. Results show that the β-Sn crystals mainly reveal an irregular dendritic morphology without or with a relatively low static magnetic field(B0.3 T). When the magnetic field is increased to 0.5 T, the β-Sn dendrites close to the final stage of growth begin to show some directional character. With a further increase in the magnetic field to a higher level(0.8–5 T), the β-Sn dendrites have an enhanced directional growth character, but the dendrites show a certain deflection. As the magnetic field is increased to 12 T, the directional growth of the β-Sn dendrites in the center of the couple is severely destroyed. The mechanism of the directional growth of the β-Sn crystals and the deflection of the β-Sn crystals with the application of static magnetic field was tentatively discussed. 相似文献
19.
The orientation relationships(ORs)between the martensite and the retained austenite in low-and medium-carbon steels after quenching–partitioning–tempering process were studied in this work.The ORs in the studied steels are identified by selected-area electron diffraction(SAED)as either K–S or N–W ORs.Meanwhile,the ORs were also studied based on numerical fitting of electron backscatter diffraction data method suggested by Miyamoto.The simulated K–S and N–W ORs in the low-index directions generally do not well coincide with the experimental pole figure,which may be attributed to both the orientation spread from the ideal variant orientations and high symmetry of the low-index directions.However,the simulated results coincide well with experimental pole figures in the high-index directions{123}_(bcc).A modified method with simplicity based on Miyamoto’s work was proposed.The results indicate that the ORs determined by modified method are similar to those determined by Miyamoto’method,that is,the OR is near K–S OR for the low-carbon Q–P–T steel,and with the increase of carbon content,the OR is closer to N–W OR in medium-carbon Q–P–T steel. 相似文献
20.
综述了常见的电化学噪声数据处理方法,介绍了直流趋势剔除、统计分析、快速傅立叶变换(FFT)法计算功率谱密度(PSD)以及小波变换处理电化学噪声信号的基本过程,并阐释了各种数学处理及所得参数的物理意义。 相似文献