Effect of Ni/tubular g-C3N4 on hydrogen storage properties of MgH2

Additive doping is one of the effective methods to overcome the shortcomings of MgH₂ on the aspect of relatively high operating temperatures and slow desorption kinetics. In this paper, hollow g-C₃N₄ (TCN) tubes with a diameter of 2 μm are synthesized through the hydrothermal and high-temperature pyrolysis methods, and then nickel is chemically reduced onto TCN to form Ni/TCN composite at 278 K. Ni/TCN is then introduced into the MgH₂/Mg system by means of hydriding combustion and ball milling. The MgH₂–Ni/TCN composite starts to release hydrogen at 535 K, which is 116 K lower than the as-milled MgH₂ (651 K). The MgH₂–Ni/TCN composite absorbs 5.24 wt% H₂ within 3500 s at 423 K, and takes up 3.56 wt% H₂ within 3500 s, even at a temperature as low as 373 K. The apparent activation energy (E_a) of the MgH₂ decreases from 161.1 to 82.6 kJ/mol by the addition of Ni/TCN. Moreover, the MgH₂–Ni/TCN sample shows excellent cycle stability, with a dehydrogenation capacity retention rate of 98.0% after 10 cycles. The carbon material enhances sorption kinetics by dispersing and stabilizating MgH₂. Otherwise, the phase transformation between Mg₂NiH₄ and Mg₂NiH_0.3 accelerates the re/dehydrogenation reaction of the composite.     

The hydrogen storage properties and catalytic mechanism of the CuFe2O4-doped MgH2 composite system

The influence of CuFe₂O₄ addition on the sorption performances of MgH₂ prepared by ball milling was studied for the first time. The MgH₂ + 10 wt% CuFe₂O₄ sample exhibited an enhancement in hydrogen storage performance compared to that of as-milled MgH₂, with the onset decomposition temperature decreased from 340 °C to 250 °C. Dehydrogenation kinetic result revealed that CuFe₂O₄-added MgH₂ released around 5.3 wt% H₂ within 10 min at 320 °C, while the as-milled MgH₂ released below 1.0 wt% H₂ under the same condition. Furthermore, about 5.0 wt% H₂ was absorbed at 250 °C in 30 min for the 10 wt% CuFe₂O₄-doped MgH₂ sample. In contrast, the un-doped MgH₂ only absorbed 4.0 wt% H₂ at 250 °C in 30 min. From the Kissinger analysis, the apparent activation energy of as-milled MgH₂ was 166.0 kJ/mol and this value decreased to 113.0 kJ/mol for 10 wt% CuFe₂O₄-added MgH₂. The enhanced sorption performance of MgH₂ in the presence of CuFe₂O₄ is believed to be due to the role of in situ formed Fe, Mg-Cu alloy, and MgO phases as an active species to catalyse the hydrogen storage properties of MgH₂.     

Improved hydrogen storage properties of Mg/MgH2 thanks to the addition of nickel hydride complex precursors

In order to improve the hydrogenation/dehydrogenation properties of the Mg/MgH₂ system, the nickel hydride complex NiHCl(P(C₆H₁₁)₃)₂ has been added in different amounts to MgH₂ by planetary ball milling. The hydrogen storage properties of the formed composites were studied by different thermal analyses methods (temperature programmed desorption, calorimetric and pressure-composition-temperature analyses). The optimal amount of the nickel complex precursor was found to be of 20 wt%. It allows to homogeneously disperse 1.8 wt% of nickel active species at the surface of the Mg/MgH₂ particles. After the decomposition of the complex during MgH₂ dehydrogenation, the formed composite is stable upon cycling at low temperature. It can release hydrogen at 200 °C and absorb 6.3 wt% of H₂ at 100 °C in less than 1 h. The significantly enhanced H₂ storage properties are due to the impact of the highly dispersed nickel on both the kinetics and thermodynamics of the Mg/MgH₂ system. The hydrogenation and dehydrogenation enthalpies were found to be of −65 and 63 kJ/mol H₂ respectively (±75 kJ/mol H₂ for pure Mg/MgH₂) and the calculated apparent activation energies of the hydrogen uptake and release processes are of 22 and 127 kJ/mol H₂ respectively (88 and 176 kJ/mol H₂ for pure Mg/MgH₂). The change in the thermodynamics observed in the formed composite is likely to be due to the formation of a Mg_0.992Ni_0.008 phase during dehydrogenation/hydrogenation cycling. The impact of another hydride nickel precursor in which chloride has been replaced by a borohydride ligand, namely NiH(BH₄)(P(C₆H₁₁)₃)₂, is also reported.     

Kinetic improvement of H2 absorption and desorption properties in Mg/MgH2 by using niobium ethoxide as additive

The hydrogen absorption and desorption properties of a MgH₂ – 1 mol.% Nb(V) ethoxide mixture are reported. The material was prepared by hand mixing the additive with previously ball-milled MgH₂. Nb ethoxide reacts with MgH₂ during heating, releasing C₂H₆ and H₂, and producing MgO and Nb or Nb hydride. Hydriding and dehydriding are greatly enhanced by the use of the alkoxide. At 250 °C the material with Nb takes up 1.8 wt% in 30 s compared with 0.1 wt% of pure Mg, and releases 4.2 wt% in 30 min, whereas MgH₂ without Nb does not appreciably desorb hydrogen. The absorption and desorption activation energies are reduced from 153 kJ/mol H₂ to 94 kJ/mol H₂, and from 176 kJ/mol H₂ to 75 kJ/mol H₂, respectively. The hydrogen sorption properties remain stable after 10 cycles at 300 °C. The kinetic improvement is attributed to the fine distribution of amorphous/nanometric NbH_x achieved by the dispersion of the liquid additive.     

Synthesis of low-cost biomass charcoal-based Ni nanocatalyst and evaluation of their kinetic enhancement of MgH2

In this study, a low-cost biomass charcoal (BC)-based nickel catalyst (Ni/BC) was introduced into the MgH₂ system by ball-milling. The study demonstrated that the Ni/BC catalyst significantly improved the hydrogen desorption and absorption kinetics of MgH₂. The MgH₂ + 10 wt% Ni/BC-3 composite starts to release hydrogen at 187.8 °C, which is 162.2 °C lower than the initial dehydrogenation temperature of pure MgH₂. Besides, 6.04 wt% dehydrogenation can be achieved within 3.5 min at 300 °C. After the dehydrogenation is completed, MgH₂ + 10 wt% Ni/BC-3 can start to absorb hydrogen even at 30 °C, which achieved the absorption of 5 wt% H₂ in 60 min under the condition of 3 MPa hydrogen pressure and 125 °C. The apparent activation energies of dehydrogenation and hydrogen absorption of MgH₂ + 10 wt% Ni/BC-3 composites were 82.49 kJ/mol and 23.87 kJ/mol lower than those of pure MgH₂, respectively, which indicated that the carbon layer wrapped around MgH₂ effectively improved the cycle stability of hydrogen storage materials. Moreover, MgH₂ + 10 wt% Ni/BC-3 can still maintain 99% hydrogen storage capacity after 20 cycles. XRD, EDS, SEM and TEM revealed that the Ni/BC catalyst evenly distributed around MgH₂ formed Mg₂Ni/Mg₂NiH₄ in situ, which act as a “hydrogen pump” to boost the diffusion of hydrogen along with the Mg/MgH₂ interface. Meanwhile, the carbon layer with fantastic conductivity enormously accelerated the electron transfer. Consequently, there is no denying that the synergistic effect extremely facilitated the hydrogen absorption and desorption kinetic performance of MgH₂.     

CNTs decorated with CoFeB as a dopant to remarkably improve the dehydrogenation/rehydrogenation performance and cyclic stability of MgH2

The chain-like carbon nanotubes (CNTs) decorated with CoFeB (CoFeB/CNTs) prepared by oxidation-reduction method is introduced into MgH₂ to facilitate its hydrogen storage performance. The addition of CoFeB/CNTs enables MgH₂ to start desorbing hydrogen at only 177 °C. Whereas pure MgH₂ starts hydrogen desorption at 310 °C. The dehydrogenation apparent activation energy of MgH₂ in CoFeB/CNTs doped-MgH₂ composite is only 83.2 kJ/mol, and this is about 59.5 kJ/mol lower than that of pure MgH₂. In addition, the completely dehydrogenated MgH₂−10 wt% CoFeB/CNTs sample can start to absorb hydrogen at only 30 °C. At 150 °C and 5 MPa H₂, the MgH₂ in CoFeB/CNTs doped-MgH₂ composite can absorb 6.2 wt% H₂ in 10 min. The cycling kinetics can remain rather stable up to 20 cycles, and the hydrogen storage capacity retention rate is 98.5%. The in situ formation of Co₃MgC, Fe, CoFe and B caused by the introduction of CoFeB/CNTs can provide active and nucleation sites for the dehydrogenation/rehydrogenation reactions of MgH₂. Moreover, CNTs can provide hydrogen diffusion pathways while also enhancing the thermal conductivity of the sample. All of these can facilitate the dehydrogenation/rehydrogenation performance and cyclic stability of MgH₂.     

Enhanced hydrogen properties of MgH2 by Fe nanoparticles loaded hollow carbon spheres

In the present investigation, we have reported the synergistic effect of Fe nanoparticles and hollow carbon spheres composite on the hydrogen storage properties of MgH₂. The onset desorption temperature for MgH₂ catalyzed with hollow carbon spheres and Fe nanoparticle (MgH₂-Fe-HCS) system has been observed to be 225.9 °C with a hydrogen storage capacity of 5.60 wt %. It could be able to absorb 5.60 wt % hydrogen within 55 s and desorb 5.50 wt % hydrogen within 12 min under 20 atm H₂ pressure at 300 °C. The desorption activation energy of MgH₂-Fe-HCS has been found to be 84.9 kJ/mol, whereas the desorption activation energies for as received MgH₂, Hollow carbon sphere catalyzed MgH₂ and Fe catalyzed MgH₂ are found to be 130 kJ/mol, 103 kJ/mol, and 94.2 kJ/mol respectively. MgH₂-Fe-HCS composite lowered the change in enthalpy of hydrogen desorption from MgH₂ by 20.02 kJ/mol as compared to pristine MgH₂. MgH₂-Fe-HCS shows better cyclability up to 24 cycles of hydrogenation and dehydrogenation of MgH₂. The mechanism for the better catalytic action of Fe and HCS on MgH₂ has also been discussed.     

Effect of Ti-based nanosized additives on the hydrogen storage properties of MgH2

MgH₂-based nanocomposites were synthesized by high-energy reactive ball milling (RBM) of Mg powder with 0.5–5 mol% of various catalytic additives (nano-Ti, nano-TiO₂, and Ti₄Fe₂O_x suboxide powders) in hydrogen. The additives were shown to facilitate hydrogenation of magnesium during RBM and substantially improve its hydrogen absorption-desorption kinetics. X-ray diffraction analysis showed the formation of nanocrystalline MgH₂ and hydrogenation of nano-Ti and Ti₄Fe₂O_x. The possible reduction of TiO₂ during RBM in hydrogen was not observed, which is in agreement with lower hydrogenation capacity of the corresponding composite, 5.7 wt% for Mg + 5 mol% nano-TiO₂ compared to 6.5 wt% for Mg + 5 mol% nano-Ti. Hydrogen desorption from the as-prepared composites was studied by Thermal Desorption Spectroscopy (TDS) in vacuum. A significant lowering of the hydrogen desorption temperature of MgH₂ by 30–90 °C in the presence of the additives is associated with lowering activation energy from 146 kJ/mol for nanosized MgH₂ down to 74 and 67 kJ/mol for MgH₂ modified with nano-TiO₂ and Ti₄Fe₂O_0.3 additives, respectively. After hydrogen desorption at 300–350 °C, these materials are able to absorb hydrogen even at room temperature. It is shown that nano-structuring and addition of Ti-based catalysts do not decrease thermodynamic stability of MgH₂. The thermodynamic parameters, obtained from hydrogen desorption isotherms for the Mg–Ti₄Fe₂O_0.3 nanocomposite, ΔH_des = 76 kJ/mol H₂ and ΔS_des = 138 J/K·mol H₂, correspond to the reported literature values for pure polycrystalline MgH₂. Hydrogen absorption-desorption characteristics of the composites with nano-Ti remain stable during at least 25 cycles, while a gradual decay of the reversible hydrogen capacity occurred in the case of TiO₂ and Ti₄Fe₂O_x additives. Cycling stability of Mg/Ti₄Fe₂O_x was substantially improved by introduction of 3 wt% graphite into the composite.     

Boosting low-temperature de/re-hydrogenation performances of MgH2 with Pd-Ni bimetallic nanoparticles supported by mesoporous carbon

Bimetallic Pd-Ni nano-particles supported by a mesoporous carbon material CMK-3 (denoted as Pd₃₀Ni₇₀/CMK-3) were synthesized through solution impregnation and hydrogen reduction methods. Among those hierarchical Ni-Pd nano-particles, majorly large ones (>10 nm) are dispersed over the surface of CMK-3, while a litter small ones (<10 nm) are embedded into the pores. It significantly improves the de/re-hydrogenation performances of MgH₂ at low temperature. The onset desorption temperature of MgH₂-Pd₃₀Ni₇₀/CMK-3 is lowered by 150 K from that of pristine MgH₂ (above 593 K). About 6 wt% hydrogen could be released during its decomposition below 561 K. Noticeably, MgH₂-Pd₃₀Ni₇₀/CMK-3 is capable of releasing 1.3 wt% H₂ even at 373 K. 4 wt% hydrogen can be absorbed at 343 K under a hydrogen pressure of 3 MPa within 18000 s. Activation energy values of both hydrogen decomposition (65.9 kJ mol⁻¹) and absorption (78.9 kJ mol⁻¹) for MgH₂-Pd₃₀Ni₇₀/CMK-3 are greatly improved from those of as-milled MgH₂. Thermal stability of the composite system is remarkably destabilized by 4.3 kJ mol H₂⁻¹ from pristine MgH₂ according to pressure-composition isotherm curves and van't Hoff plots. The enhanced performances can be ascribed to the synergistic effects of both destabilization and catalysis from nano-dispersed Pd and Ni particles, respectively.     

Effect of adding different percentages of HfCl4 on the hydrogen storage properties of MgH2

Magnesium hydride (MgH₂) is the best candidate material to store hydrogen in the solid-state form owing to its advantages such as good reversibility, high hydrogen storage capacity (7.6 wt%), low raw material cost and abundance in the earth. Nevertheless, slow desorption/absorption kinetics and high thermodynamic stability are two issues that have constrained the commercialization of MgH₂ as a solid-state hydrogen storage material. So, to boost the desorption/absorption kinetics and to alter the thermodynamics of MgH₂, hafnium tetrachloride (HfCl₄) was used as a catalyst in this study. Different percentages of HfCl₄ (5, 10, 15 and 20 wt%) were added to MgH₂ and their catalytic influences on the hydrogen storage properties of MgH₂ were investigated. Results showed that the 15 wt% HfCl₄-doped MgH₂ sample was the best composite to enhance the hydrogen storage performance of MgH₂. The onset decomposition temperature of the 15 wt% HfCl₄-doped MgH₂ composite was decreased by ~75 °C compared to as-milled MgH₂. Meanwhile, the desorption/absorption kinetic measurements showed an improvement compared to the undoped MgH₂. From the Kissinger analysis, the apparent dehydrogenation activation energy was 167.0 kJ/mol for undoped MgH₂ and 102.0 kJ/mol for 15 wt% HfCl₄-doped MgH₂. This shows that the HfCl₄ addition reduced the activation energy of the hydrogen decomposition of MgH₂. The desorption enthalpy change calculated by the van't Hoff equation showed that the addition of HfCl₄ to MgH₂ did not affect the thermodynamic properties. Scanning electron microscopy showed that the size of the MgH₂ particles decreased and there was less agglomeration after the addition of HfCl₄. It is believed that the decrease in the particle size and in-situ generated MgCl₂ and Hf-containing species had synergistic catalytic effects on enhancing the hydrogen storage properties of the HfCl₄-doped MgH₂ composite.     

Determination of kinetic parameters and hydrogen desorption characteristics of MgH2-10 wt% (9Ni–2Mg–Y) nano-composite

Hydrogen desorption kinetic parameters of MgH₂ compounds were measured and compared with published gas solid reaction models. The compounds investigated in this study were as-received MgH₂, ball milled MgH₂, and MgH₂ ball milled with 9Ni–2Mg–Y catalyst compound. It was determined that different models were necessary to fit the hydrogen desorption data collected at different temperatures on the same sample, indicating that desorption mechanisms changed with respect to temperature. Addition of (9Ni–2Mg–Y) alloy as a catalyst to MgH₂ increased the hydrogen desorption capacity of MgH₂ from zero (for as-received MgH₂) to about 5 wt% at 350 °C within 500 s. The activation energy value was determined as 187 kJ/mol H₂ for the as-received MgH₂, 137 kJ/mol H₂ for 20 h ball milled MgH₂, and 62 kJ/mol H₂ for 20 h ball milled MgH₂-10 wt% (9Ni–2Mg–Y) nano-composite by the Arrhenius and Kissinger methods. Moreover, the integral heat of H₂ desorption for the MgH₂-10 wt% (9Ni–2Mg–Y) nano-composite was measured to be about 78 ± 0.5 kJ/mol H₂ by adsorption micro-calorimetry consistent with the results of the Arrhenius and Kissinger methods.     

Graphene-anchored Ni6MnO8 nanoparticles with steady catalytic action to accelerate the hydrogen storage kinetics of MgH2

Transition metal-based oxides have been proven to have a substantial catalytic influence on boosting the hydrogen sorption performance of MgH₂. Herein, the catalytic action of Ni₆MnO₈@rGO nanocomposite in accelerating the hydrogen sorption properties of MgH₂ was investigated. The MgH₂ + 5 wt% Ni₆MnO₈@rGO composites began delivering H₂ at 218 °C, with about 2.7 wt%, 5.4 wt%, and 6.6 wt% H₂ released within 10 min at 265 °C, 275 °C, and 300 °C, respectively. For isothermal hydrogenation at 75 °C and 100 °C, the dehydrogenated MgH₂ + 5 wt% Ni₆MnO₈@rGO sample could absorb 1.0 wt% and 3.3 wt% H₂ in 30 min, respectively. Moreover, as compared to addition-free MgH₂, the de/rehydrogenation activation energies for doped MgH₂ composites were lowered to 115 ± 11 kJ/mol and 38 ± 7 kJ/mol, and remarkable cyclic stability was reported after 20 cycles. Microstructure analysis revealed that the in-situ formed Mg₂Ni/Mg₂NiH₄, Mn, MnO₂, and reduced graphene oxide synergically enhanced the hydrogen de/absorption properties of the Mg/MgH₂ system.     

Effect of Ni and SAPO-34 co-additive on enhancing hydrogen storage performance of MgH2

The hydrogen storage performances of MgH₂ improved by the addition of Ni and SAPO-34 were studied in detail. The mixture of MgH₂ with Ni and SAPO-34 was a physical reaction as shown by the X-ray diffraction (XRD) results. The SAPO-34 and Ni were uniformly distributed on the surface of MgH₂. The thermodynamic and kinetic properties of 90MgH₂/5Ni/5SAPO-34 were investigated by differential scanning calorimetry (DSC) and pressure-composition-isothermal (PCI) methods. The results showed that the dehydrogenation activation energy of 90MgH₂/5Ni/5SAPO-34 decreased by 64.3 kJ/mol compared with that of MgH₂. In addition, the relationship between the value of dehydrogenation heat and hydrogen content was also investigated by in-situ calorimetry. The enthalpy value of each sample in the dehydrogenation processes were calculated by in-situ calorimetry measurement. The dehydrogenation enthalpies of as-milled MgH₂ and 90MgH₂/5Ni/5SAPO-34 were 63.2 kJ/mol H₂ and 53.6 kJ/mol H₂, respectively. Thus, the co-doping of Ni and SAPO-34 contributed significantly to decrease the thermodynamic stability and improve the hydrogen sorption kinetic properties of MgH₂.     

Effect of in-situ formed Mg2Ni/Mg2NiH4 compounds on hydrogen storage performance of MgH2

Magnesium-based hydrogen storage materials (MgH₂) are promising hydrogen carrier due to the high gravimetric hydrogen density; however, the undesirable thermodynamic stability and slow kinetics restrict its utilization. In this work, we assist the de/hydrogenation of MgH₂ via in situ formed additives from the conversion of an MgNi₂ alloy upon de/hydrogenation. The MgH₂–16.7 wt%MgNi₂ composite was synthesized by ball milling of Mg powder and MgNi₂ alloy followed by a hydrogen combustion synthesis method, where most of the Mg converted to MgH₂, and the others reacted with the MgNi₂ generating Mg₂NiH₄, which produced in situ Mg₂Ni during dehydrogenation. Results showed that the Mg₂Ni and Mg₂NiH₄ could induce hydrogen absorption and desorption of the MgH₂, that it absorbed 2.5 wt% H₂ at 473 K, much higher than that of pure Mg, and the dehydrogenation capacity increased by 2.6 wt% at 573 K. Besides, the initial dehydrogenation temperature of the composite under the promotion of Mg₂NiH₄ decreased greatly by 100 K, whereas it is 623 K for MgH₂. Furthermore, benefiting from the catalyst effect of Mg₂NiH₄ during dehydrogenation, the apparent activation energy of the composite reduced to 73.2 kJ mol⁻¹ H₂ from 129.5 kJ mol⁻¹ H₂.     

Effects of KNbO3 catalyst on hydrogen sorption kinetics of MgH2

The influences of Nb-containing oxides and ternary compound in hydrogen sorption performance were investigated. As faster desorption kinetic and lower activation energy were reported by addition of a ternary compound catalyst such as K₂NiF₆, the influence of KNbO₃ on hydrogen storage properties of MgH₂ has been investigated for the first time. The MgH₂ - KNbO₃ composite desorbed 3.9 wt% of hydrogen within 10 min, while MgH₂ and MgH₂-Nb₂O₅ composites desorbed 0.66 wt% and 3.2 wt% respectively under similar condition. For MgH₂ with other Nb-contained catalysts such as Nb, NbO and Nb₂O₃, the desorption rate was almost the same as the one registered for as-milled MgH₂. The analysis of differential scanning calorimetry (DSC) showed that MgH₂-KNbO₃ composite started to release hydrogen at ∼335 °C which is 50 °C lower compared to as-milled MgH₂ without any additives. The activation energy for the hydrogen desorption was estimated to be about 104 ± 6.8 kJ mol⁻¹ for this material, while for the as-milled MgH₂ was about 165 ± 2.0 kJ mol⁻¹. It is believed that Nb-ternary oxide catalyst (KNbO₃) showed a good catalytic effect and enhance the sorption kinetics of MgH₂.     

Improvement of hydrogen storage properties in MgH2 catalysed by K2NbF7

The catalytic effects of K₂NbF₇ on the hydrogen storage properties of MgH₂ have been studied for the first time. MgH₂ + 5 wt% K₂NbF₇ has reduced the onset dehydrogenation temperature to 255 °C, which is 75 °C lower than the as-milled MgH₂. For the rehydrogenation kinetic, at 150 °C, MgH₂ + 5 wt% K₂NbF₇ absorbs 4.7 wt% of hydrogen in 30 min whereas the as-milled MgH₂ only absorbs 0.7 wt% of hydrogen under similar condition. For the dehydrogenation kinetic, at 320 °C, the MgH₂ + 5 wt% K₂NbF₇ is able to release 5.2 wt% of hydrogen in 5.6 min as compared to 0.3 wt% by the as-milled MgH₂ under similar condition. Comparatively, the E_a value of MgH₂ + 5 wt% K₂NbF₇ is 96.3 kJ/mol, which is 39 kJ/mol lower compared to the as-milled MgH₂. The MgF₂, the KH and the Nb that are found after the heating process are believed to be the active species that have improved the system properties. It is concluded that the K₂NbF₇ is a good catalyst to improve the hydrogen storage properties of MgH₂.     

Synthesis of BaFe12O19 by solid state method and its effect on hydrogen storage properties of MgH2

Previous studies have shown that ferrites give a positive effect in improving the hydrogen sorption properties of magnesium hydride (MgH₂). In this study, another ferrite, i.e., BaFe₁₂O₁₉, has been successfully synthesised via the solid state method, and it was milled with MgH₂ to enhance the sorption kinetics. The result showed that the MgH₂ + 10 wt% BaFe₁₂O₁₉ sample started to release hydrogen at about 270 °C which is about 70 °C lower than the as-milled MgH₂. The doped sample was able to absorb hydrogen for 4.3 wt% in 10 min at 150 °C, while as-milled MgH₂ only absorbed 3.5 wt% of hydrogen under similar conditions. The desorption kinetic results showed that the doped sample released about 3.5 wt% of hydrogen in 15 min at 320 °C, while the as-milled MgH₂ only released about 1.5 wt% of hydrogen. From the Kissinger plot, the apparent activation energy of the BaFe₁₂O₁₉-doped MgH₂ sample was 115 kJ/mol which was lower than the milled MgH₂ (141 kJ/mol)_. Further analyses demonstrated that MgO, Fe and Ba or Ba-containing contribute to the improvement by serving as active species, thus enhancing the MgH₂ for hydrogen storage.     

Enhanced hydrogen desorption/absorption properties of magnesium hydride with CeF3@Gn

In order to improve the hydrogen storage performance of MgH₂, graphene and CeF₃ co-catalyzed MgH₂ (hereafter denoted as MgH₂+CeF₃@Gn) were prepared by wet method ball milling and hydriding, which is a simple and time-saving method. The effect of CeF₃@Gn on the hydrogen storage behavior of MgH₂ was investigated. The experimental results showed that co-addition of CeF₃@Gn greatly decreased the hydrogen desorption/absorption temperature of MgH₂, and remarkably improved the dehydriding/hydriding kinetics of MgH₂. The onset hydrogen desorption temperature of Mg + CeF₃@Gn is 232 °C，which is 86 °C lower than that of as-milled undoped MgH₂, and its hydrogen desorption capacity reaches 6.77 wt%, which is 99% of its theoretical capacity (6.84 wt%). At 300 °C and 200 °C the maximum hydrogen desorption rates are 79.5 and 118 times faster than that of the as-milled undoped MgH₂. Even at low temperature of 150 °C, the dedydrided sample (Mg + CeF₃@Gn) also showed excellent hydrogen absorption kinetics, it can absorb 5.71 wt% hydrogen within 50 s, and its maximum hydrogen absorption rate reached 15.0 wt% H₂/min, which is 1765 times faster than that of the undoped Mg. Moreover, no eminent degradation of hydrogen storage capacity occurred after 15 hydrogen desorption/absorption cycles. Mg + CeF₃@Gn showed excellent hydrogen de/absorption kinetics because of the MgF₂ and CeH_2-3 that are formed in situ, and the synergic catalytic effect of these by-products and unique structure of Gn.     

Influence of K2TiF6 additive on the hydrogen sorption properties of MgH2

In this study, the hydrogen storage properties of MgH₂ with the addition of K₂TiF₆ were investigated for the first time. The temperature-programmed desorption results showed that the addition of 10 wt% K₂TiF₆ to the MgH₂ exhibited a lower onset desorption temperature of 245 °C, which was a decrease of about 105 °C and 205 °C compared with the as-milled and as-received MgH₂, respectively. The dehydrogenation and rehydrogenation kinetics of 10 wt% K₂TiF₆-doped MgH₂ were also significantly improved compared to the un-doped MgH₂. The results of the Arrhenius plot showed that the activation energy for the hydrogen desorption of MgH₂ was reduced from 164 kJ/mol to 132 kJ/mol after the addition of 10 wt% K₂TiF₆. Meanwhile, the X-ray diffraction analysis showed the formation of a new phase of potassium hydride and titanium hydride together with magnesium fluoride and titanium in the doped MgH₂ after the dehydrogenation and rehydrogenation process. It is reasonable to conclude that the K₂TiF₆ additive doped with MgH₂ played a catalytic role through the formation of active species of KH, TiH₂, MgF₂ and Ti during the ball milling or heating process. It is therefore proposed that this newly developed product works as a real catalyst for improving the hydrogen sorption properties of MgH₂.     

Effects of nano size mischmetal and its oxide on improving the hydrogen sorption behaviour of MgH2

This paper reports the catalytic effects of mischmetal (Mm) and mischmetal oxide (Mm-oxide) on improving the dehydrogenation and rehydrogenation behaviour of magnesium hydride (MgH₂). It has been found that 5 wt.% is the optimum catalyst (Mm/Mm-oxide) concentration for MgH₂. The Mm and Mm-oxide catalyzed MgH₂ exhibits hydrogen desorption at significantly lower temperature and also fast rehydrogenation kinetics compared to ball-milled MgH₂ under identical conditions of temperature and pressure. The onset desorption temperature for MgH₂ catalyzed with Mm and Mm-oxide are 323 °C and 305 °C, respectively. Whereas the onset desorption temperature for the ball-milled MgH₂ is 381 °C. Thus, there is a lowering of onset desorption temperature by 58 °C for Mm and by 76 °C for Mm-oxide. The dehydrogenation activation energy of Mm-oxide catalyzed MgH₂ is 66 kJ/mol. It is 35 kJ/mol lower than ball-milled MgH₂. Additionally, the Mm-oxide catalyzed dehydrogenated Mg exhibits faster rehydrogenation kinetics. It has been noticed that in the first 10 min, the Mm-oxide catalyzed Mg (dehydrogenated MgH₂) has absorbed up to 4.75 wt.% H₂ at 315 °C under 15 atmosphere hydrogen pressure. The activation energy determined for the rehydrogenation of Mm-oxide catalyzed Mg is ∼62 kJ/mol, whereas that for the ball-milled Mg alone is ∼91 kJ/mol. Thus, there is a decrease in absorption activation energy by ∼29 kJ/mol for the Mm-oxide catalyzed Mg. In addition, Mm-oxide is the native mixture of CeO₂ and La₂O₃ which makes the duo a better catalyst than CeO₂, which is known to be an effective catalyst for MgH₂. This takes place due to the synergistic effect of CeO₂ and La₂O₃. It can thus be said that Mm-oxide is an effective catalyst for improving the hydrogen sorption behaviour of MgH₂.