聚苯乙烯-聚甲基丙烯酸甲酯核-壳粒子的制备

由种子乳液聚合法制备了聚苯乙烯-聚甲基丙烯酸甲酯核-壳粒子。以过硫酸钾(KPS)为引发剂,辛基酚聚氧乙烯醚(OP-10)为乳化剂,合成了聚苯乙烯(PS)种子核;连续滴加甲基丙烯酸甲酯(MMA),在核表面富集MMA,制备了粒径范围在0.16~0.67μm的核-壳粒子;当单体苯乙烯与甲基丙烯酸甲酯(St/MMA)的比为30∶70(质量比)时,所得粒径在0.18μm,粒径分布为0.012。差示扫描量热(DSC)研究显示,复合粒子的玻璃化转变温度(Tg)为97.2℃,峰形单一,表现出良好的热性能。     

Prediction and experiment of core–shell particle morphology of vinyl acetate and butyl acrylate

In this article, the particle morphology in emulsion polymerization of the poly(vinyl acetate) (PVAc)/poly(butyl acrylate) (PBA) system is investigated. With the use of the basic data in literature, the relevant interface tensions and viscosity are estimated with the equation proposed in literature. The time achieved to equilibrium morphology is predicted with cluster dynamics proposed by Gonzalez. The experiment result is consistent with that of prediction. © 2002 Wiley Periodicals, Inc. J Appl Polym Sci 83: 2930–2937, 2002; DOI 10.1002/app.10297     

Synthesis and characterization of butyl acrylate/methyl methacrylate/glycidyl methacrylate latexes

The butyl acrylate (BA)/methyl methacrylate (MMA), and glycidyl methacrylate (GMA) composite copolymer latex was synthesized by seeded emulsion polymerization technique taking poly(methyl methacrylate) (PMMA) latex as the seed. Four series of experiments were carried out by varying the ratio of BA : MMA (w/w) (i.e. 3.1 : 1, 2.3 : 1, 1.8 : 1, and 1.5 : 1) and in each series GMA content was varied from 1 to 5% (w/w). The structural properties of the copolymer were analyzed by FTIR, ¹H‐, and ¹³C‐NMR. Morphological characterization was carried out using transmission electron microscopy (TEM). In all the experiments, monomer conversion was ～99% and final copolymer composition was similar to that of feed composition. The incorporation of GMA into the copolymer chain was confirmed by ¹³C‐NMR. The glass transition temperature (T_g) of the copolymer latex obtained from the differential scanning calorimetry (DSC) curve was comparable to the values calculated theoretically. With increase in GMA content, particles having core‐shell morphology were obtained, and there was a decrease in the particle size as we go from 2–5% (w/w) of GMA. The adhesive strength of the latexes was found to be dependent on the monomer composition. With increase in BA : MMA ratio, the tackiness of the film increased while with its decrease the hardness of the film increased. © 2009 Wiley Periodicals, Inc. J Appl Polym Sci, 2010     

中空聚合物乳胶粒子的制备

研究了在制备中空乳胶粒子的过程中,复合乳液（苯乙烯（Ｓｔ）－丙烯酸丁酯（ＢＡ）－甲基丙烯醛（ＭＡ））进行种子聚合时,Ｓｔ／ＢＡ的质量比和ＭＡ的用量对胶乳粒子的空径、粒径和表面羧基质量摩尔浓度的影响。实验结果表明,当Ｓｔ／ＢＡ的质量比为１９,ＭＡ质量分数为单体的５．６％时,形成的乳胶粒子的空径最大。     

Preparation of poly(tert‐butyl acrylate)‐poly(acrylic acid) amphiphilic copolymers via radiation‐induced reversible addition–fragmentation chain transfer mediated polymerization of tert‐butyl acrylate

Poly(tert‐butyl acrylate) (PtBA) is a versatile hydrophobic macromolecule usually preferred in the development of new materials for a host of applications. PtBA homopolymers with well‐defined structure and controlled molecular weight in a wide range were successfully synthesized via radiation‐induced reversible addition–fragmentation chain transfer (RAFT) polymerization in the presence of a trithiocarbonate type RAFT agent. The polymerization of tBA was performed under ⁶⁰Co γ‐irradiation in the presence of 2‐(dodecylthiocarbonothioylthio)‐2‐methylpropionic acid (DDMAT) as the RAFT agent in toluene at room temperature with three [tBA]/[DDMAT] ratios (400, 600 and 1000) and different irradiation times. Radiation‐induced polymerization of tBA displayed controlled free radical polymerization characteristics: a narrow molecular weight distribution (M_w/M_n ~ 1.1), pseudo first order kinetics and controlled molecular weights. The system followed the RAFT polymerization mechanism even at very low amounts of RAFT agent ([tBA]/[DDMAT] = 1000), and molecular weights up to 113 900 with narrow dispersity (Ð =1.06) were obtained. PtBA was further hydrolysed into different amphiphilic PtBA‐co‐poly(acrylic acid) (PAA) copolymers by low (27.5%) and high (77.3%) degrees of hydrolysis. The pH sensitivity of the two copolymers was investigated by dynamic light scattering at pH 2 and pH 9 (above and below the pK_a value of PAA) and their hydrodynamic diameters and zeta potential values were determined. © 2020 Society of Chemical Industry     

Synthesis and characterization of thermosensitive composite microsphere latex

Monodisperse aqueous latex dispersions, prepared from mixtures of styrene, N‐isopropylacrylamide, and N,N′‐methylenebisacrylamide, were characterized. Thermosensitive composite microspheres with diameters greater than 1.0 μm, consisting of a polystyrene core and a poly(N‐isopropylacrylamide) shell, were prepared. The morphology of the composite microspheres was observed with transmission electron microscopy, and the particle size of the composite microspheres was estimated with dynamic light scattering. The thermosensitive properties of the composite microspheres were evaluated via the hydrodynamic size of the composite microspheres. The particle size of the composite microspheres decreased with increasing temperature. © 2005 Wiley Periodicals, Inc. J Appl Polym Sci 96: 824–828, 2005     

Control of monodisperse particle size of styrenic–acrylate copolymers in dispersion copolymerization

Syntheses of monodisperse poly[(styrene)‐co‐(n‐butyl acrylate)] and poly[(styrene)‐co‐(2‐ethylhexyl acrylate)] were carried out by dispersion polymerization. The reactions were performed in the mixed solvent of ethanol–water in the presence of azo‐bisisobutyronitrile and poly(N‐vinylpyrrolidone) as the initiator and dispersant, respectively. The effects of reaction parameters, that is the type and concentration of dispersant, ratio of the mixed solvent, reaction temperature, agitation rate, monomer composition between styrene and n‐butyl acrylate or 2‐ethylhexyl acrylate, crosslinking agent and reaction time on the particle size, size distribution and average molecular weights of the resulting copolymer were thoroughly investigated. The resulting copolymer particles were smooth on their spherical surface and the sizes were in the range 0.6–1.8 µm with a narrow size distribution. In most cases, a correlation between small particle sizes with high average molecular weights was observed. The average particle size generally increased with increasing reaction temperature, time and acrylate monomer content. In contrast, the particle size decreased as the molecular weight, concentration of dispersant, polarity of the medium or agitation rate was increased. The glass transition temperature (T_g) of the copolymers can be controlled by the mole ratio of the comonomer. The T_g values decreased when the content of acrylate monomers in the copolymer increased, and T_g values of the synthesized copolymer were in the range 66–102 °C. Instead of using n‐butyl acrylate monomer in the copolymerization, 2‐ethylhexyl acrylate copolymerization with styrene resulted in insignificant changes in the particle sizes but there were significant decreases in T_g values. In this study, the monodisperse particles can be obtained by monitoring the appropriate conditions regarding PVP K‐30 (2–8 wt%), ethanol/water (90/10 wt%), the reaction temperature (70 °C) and the agitation rate (100 rpm). © 2000 Society of Chemical Industry     

Synthesis and characterization of epoxy‐acrylate composite latex

A waterborne epoxy‐acrylate composite latex was synthesized. The effects of the concentration of the initiator, surfactant, and epoxy resin on the particle size, molecular weight, and grafting ratios of the composite latex were investigated. The increase of the concentration of the initiator and epoxy resin led to the decrease of the weight‐average molecular weight. The graft ratios increased with an increase in the initiator level and a decrease in the epoxy resin concentration whereas the variation of the concentration of the surfactant did not have much influence on the graft ratios. The increase in the initiator level caused the aggrandizement of the particle size, and the increase of the concentration of the surfactant and epoxy resin caused a decrease in the latex particle size. Fourier transform IR spectroscopy with attenuated total reflectance indicated that the epoxy resin molecules were enriched in the mold‐facing surface in the film from the composite latex. The differential scanning calorimetry analysis, dynamic mechanical analysis, and Instron test showed that the polymer films cast by the composite latex had lower tensile strength and glass transition than those by the blend latex. © 2002 Wiley Periodicals, Inc. J Appl Polym Sci 83: 1736–1743, 2002     

Effect of crosslinker,buffer, and blending on damping properties of poly(styrene‐acrylonitrile)/poly(ethyl acrylate‐ n‐butyl acrylate) latex interpenetrating polymer networks

A series of poly(styrene‐acrylonitrile)/poly(ethyl acrylate‐n‐butyl acrylate) latex interpenetrating polymer networks (LIPNs) are synthesized by changing the kind of crosslinker and introducing a buffer. The results show that the crosslinker has an important effect on the damping properties of the LIPNs; divinylbenzene is the best crosslinker in the study. Moreover, introducing a buffer into LIPNs leads to an increase of the damping values over the temperature range where the damping value surpasses 0.5. The LIPN blend prepared by mixing LIPNs results in broadening of the damping peak, therefore improving the damping properties. Tests of the damping properties show that the LIPNs have good practical value. © 2002 Wiley Periodicals, Inc. J Appl Polym Sci 84: 2347–2351, 2002     

Synthesis of diblock and triblock copolymers from butyl acrylate and styrene by reverse iodine transfer polymerization

Well‐defined AB and BA diblock copolymers were obtained by a one‐pot two‐step sequential block copolymerization by reverse iodine transfer polymerization (RITP), A being a poly(styrene) block and B a poly(butyl acrylate) block. High monomer conversions during the formation of the first block avoided the purification steps before growing the second block. In a third sequential step, the diblock copolymers were further extended to synthesize ABA and BAB triblock copolymers. Furthermore, the synthesis of ABA and BAB copolymers in only two steps by RITP was investigated starting with the formation of the central block using 2,5‐di(2‐ethylhexanoylperoxy)‐2,5‐dimethylhexane as a difunctional initiator and then resuming the polymerization to grow the external blocks in a second step. The obtained copolymers were analyzed by size exclusion chromatography, transmission electron microscopy, and differential scanning calorimetry. © 2010 Wiley Periodicals, Inc. J Appl Polym Sci, 2011     

环氧丙烯酸酯复合乳液的合成与研究

采用半连续种子乳液聚合法制备环氧-丙烯酸酯复合乳液。研究了乳化剂种类及用量、引发剂用量、环氧树脂用量及功能单体用量对乳液及其涂膜性能的影响,通过FTIR、DSC对乳液进行了分析和表征。     

Novel method to prepare charged mosaic membrane by using dipole‐like microspheres. I. Preparation and characterization of poly(4‐vinylpyridine/n‐butyl acrylate) seed latex with high solid content by soap‐free emulsion polymerization

The stable latex of poly(4‐vinylpyridine‐co‐n‐butyl acrylate) (P4VP/nBA) with a solid content as high as 10 wt % was prepared by a modified soap‐free emulsion polymerization. A mixture of water and organic solvents was employed as the continuous phase for increasing the solid content of the latex. Several organic solvents were investigated and, among them, ethyl acetate (EA) and diethyl ether (DE) were effective. The stable latex with 10 wt % solid content was prepared by charging 10 wt % EA or a EA/DE mixture (5 wt % each); however, more than 10 wt % solid content of the stable latex could not be obtained even by charging more than 10 wt % EA or a EA/DE mixture. The stable latex with 10 wt % solid content, which was crosslinked with less than 0.5 wt % (based on monomer) of ethylene glycol dimethacrylate, was prepared by charging 10 wt % of EA. In this case, however, the pH of the continuous phase had to be adjusted to lower than 4. The effects of EA on the characteristics of the resulting uncrosslinked latex were investigated by employing ζ‐potential measurements and scanning electron microscopy. It was found that the mass of coagulum decreased as the EA increased. At 8 wt % of EA, a stable latex of 10 wt % solid content without any coagulum was obtained. The ζ potential of particles increased from −100 up to 45.7 mV as the EA increased from 0 to 10 wt %. The effects of batch and semicontinuous copolymerization on the morphology of the microspheres were investigated by using DSC and ultrathin cross‐sectional transmission electron miscroscopy photos. A core–shell structure was not found, despite the batch copolymerization of 4VP(1)/nBA(2) (r₁ = 4.3, r₂ = 0.23), even with disparate reactivity ratios. © 2000 John Wiley & Sons, Inc. J Appl Polym Sci 76: 1731–1740, 2000     

Synthesis and characterization of poly(fluorinated acrylate)/silica hybrid nanocomposites

The nanocomposite particles (NPs) with inorganic silica as core and fluorinated polymer shell have been in situ synthesized via emulsion polymerization. The chemical composition and core‐shell structure were characterized by Fourier‐transform infrared spectrometry and transmission electron microscopy. The results showed that silica nanoparticles were encapsulated in latex particles, with single‐ and multicore morphologies coexisting. Thermal gravimetric analysis also suggested the successful encapsulation of silica into NPs with enhanced thermal stability. The surface properties of the latex films produced from the core‐shell particles were also investigated by contact angle method and water absorption measurement. Both fluorinated polymer and silica contributed to less water absorption ratio and lower surface‐free energy, which was composed of larger polar component and smaller disperse component, just reversed as usual. © 2009 Wiley Periodicals, Inc. J Appl Polym Sci, 2010     

Study on synthesis and morphology control of poly(4‐vinylpyridine‐co‐butyl acrylate)/poly(styrene‐co‐butyl acrylate) composite microspheres

Monodispersed crosslinked cationic poly(4‐vinylpyridine‐co‐butyl acrylate) [P(4VP‐BA)] seed latexes were prepared by soapless emulsion polymerization, using 2,2′‐azobismethyl(propionamidine)dihydrochloride (V₅₀) as an initiator and divinylbenzene (DVB) or ethylene glycol dimethacrylate (EGDMA) as a crosslinker. The optimum condition to obtain monodispersed stable latex was investigated. It was found that the colloidal stability of the P4VP latex can be improved by adding an adequate amount of BA (BA/4VP = 1/4, w/w), and adopting a semicontinuous monomer feed mode. Subsequently, poly(4‐vinylpyridine‐co‐butyl acrylate)/Poly(styrene‐co‐butyl acrylate) [P(4VP‐BA)/P(ST‐BA)] composite microspheres were synthesized by seeded polymerization, using the above latex as a seed and a mixture of ST and BA as the second‐stage monomers. The effects of the type of crosslinker, the degree of crosslinking, and the initiators (AIBN and V₅₀) on the morphology of final composite particles are discussed in detail. It was found that P(4VP‐BA)/P(ST‐BA) composite microspheres were always surrounded by a PST‐rich shell when V₅₀ was used as initiator, while sandwich‐like or popcorn‐like composite particles were produced when AIBN was employed. This is because the polarity of the polymer chains with AIBN fragments is lower than for the polymer with V₅₀ fragments, hence leading to higher interfacial tension between the second‐stage PST‐rich polymer and the aqueous phase, and between PST‐rich polymer and P4VP‐rich seed polymer. As a result, the seed cannot be engulfed by the PST‐rich polymer. Furthermore, the decrease of T_g of the second‐stage polymer promoted phase separation between the seeds and the PST‐rich polymer: sandwich‐like particles formed more preferably than popcorn‐like particles. It is important knowledge that various morphologies different from PST‐rich core/P4VP‐rich shell morphology, can be obtained only by changing the initiator, considering P4VP is much more hydrophilic than PST. The zeta potential of composite particles initiated by AIBN in seeded polymerization shifted from a positive to a negative charge. © 2002 Wiley Periodicals, Inc. J Appl Polym Sci 83: 1190–1203, 2002     

Synthesis and thermal properties of poly(n‐butyl acrylate)/n‐hexadecane microcapsules using different cross‐linkers and their application to textile fabrics

This study focused on the preparation, characterization, and determination of thermal properties of microencapsulated n‐hexadecane with poly(butyl acrylate) (PBA) to be used in textiles with heat storage property. Microcapsules were synthesized by emulsion polymerization method, and the particle size, particle size distribution, shape, and thermal storage/release properties of the synthesized microcapsules were analyzed using Fourier‐transform infrared spectroscopy, scanning electron microscopy, and differential scanning calorimetry techniques. Allyl methacrylate, ethylene glycol dimethacrylate, and glycidyl methacrylate were used as cross‐linkers to produce unimodal particle size distribution. MicroPBA microcapsules produced using allyl methacrylate cross‐linker were applied to 100% cotton and 50/50% cotton/polyester blend fabrics by pad‐cure method. The mean particle size of microcapsules ranges from 0.47 to 4.25 μm. Differential scanning calorimetry analysis indicated that hexadecane in the microcapsules melts at nearly 17°C and crystallizes at around 15°C. The contents of n‐hexadecane of different PBA microcapsules were in the range of 27.7–50.7%, and the melting enthalpies for these ratios were between 65.67 and 120.16 J/g, respectively. The particle size and thermal properties of microcapsules changed depending on the cross‐linker type. The cotton and 50/50% cotton/polyester blend fabrics stored 6.56 and 28.59 J/g thermal energy, respectively. The results indicated that PBA microcapsules have the potential to be used as a solid‐state thermal energy storage material in fabrics. © 2011 Wiley Periodicals, Inc. J Appl Polym Sci, 2011     

Compatibility studies with blends based on poly(n‐butyl methacrylate) and polyacrylonitrile

In this study, poly(n‐butyl methacrylate) (PBMA) was prepared by a suspension polymerization process, and blending with polyacrylonitrile (PAN) in N,N‐dimethyl acetamide to prepare PAN/PBMA blends in various proportions. Hansen's three dimensional solubility parameters of PAN and PBMA were calculated approximately through the contributions of the structural groups. The compatibility in these blend systems was studied with theoretical calculations as well as experimental measurements. Viscometric methods, Fourier transform infrared spectroscopy, dynamic mechanical analysis, scanning electron microscopy, and thermogravimetric analysis were used for this investigation. All the results showed that a partial compatibility existed in PAN/PBMA blend system, which may be due to the intermolecular interactions between the two polymers. And, the adsorption experiment results showed that the addition of PBMA contributed to the enhancing adsorptive properties of blend fibers, which lays the foundation for further studying PAN/PBMA blend fibers with adsorptive function. © 2009 Wiley Periodicals, Inc. J Appl Polym Sci, 2010     

Preparation and properties of poly(WPSF‐co‐butyl acrylate) copolymer emulsion with ultrasonic radiation II. Monomer conversion rate and characterization

A stable emulsion of poly(WPSF‐co‐butyl acrylate) based on butyl acrylate, waste polystyrene foam was synthesized through emulsion polymerization using sodium dodecyl sulfate and octyl phenyl polyoxyethylene ether as surfactant, ammonium persulfate and sodium hydrogen bisulfate as mixed redox initiator, under ultrasound irradiation in the absence of inert gas. The effects of various copolymerization conditions on the monomer conversion were reported. The copolymers were characterized by means of IR, ¹HNMR, and gel permeation chromatography. © 2009 Wiley Periodicals, Inc. J Appl Polym Sci, 2009     

Preparation of poly(styrene‐co‐butyl acrylate)/montmorillonite nanocomposite by emulsion polymerization: Characterization and nanoscratch behavior

Organic–inorganic hybrid poly(styrene‐co‐butyl acrylate)/organically modified montmorillonite (PSBA/organo‐MMT) latex particles have been prepared by in situ emulsion polymerization. The effects of modifier variety and the level of organo‐MMT have been investigated on the basis of the characteristics and mechanical properties of the resulting hybrid emulsion polymers. Although the more hydrophilic intercalated organic modifiers increased the latex particle size, the hydrophobic ones decreased the particle size. A more heterogeneous copolymer chain intercalation was seen by widespread XRD reflection as the organo‐MMT (organoclay) level increases. The tapping mode atomic force microscopy (AFM) and transmission electron microscopy (TEM) were used to determine the dispersion state of organoclay particles inside the nanocomposite copolymer films. Dynamic mechanical thermal analysis (DMTA) showed that adding the organoclay to the copolymer decreased the maximum loss tangent (tanδ) value and caused the shift to a lower temperature. Interestingly, the incorporation of organoclay decreased the glass storage modulus of the copolymer, while increased the rubbery storage modulus to some extent. In addition, a standard indenter for the nanoscratching of copolymer nanocomposite films was used under low applied loads of 150 and 250 μN. The nanoscratch results showed that incorporation of a 3 wt % hydrophobic organoclay, e.g., Closite15A, in the copolymer matrix enhanced considerably the near‐surface hardness and grooving resistance of the nanocomposite film at room temperature. In fact, copolymer nanocomposite films with higher near‐surface hardness and tanδ curve broadening exhibited more nanoscratch resistance through a specific variety of viscoelastic deformation, which did not create a bigger groove. © 2011 Wiley Periodicals, Inc. J Appl Polym Sci, 2012     

Miscibility and mechanical properties of poly(styrene-co-4-vinylpyridine) and poly(butyl acrylate-co-acrylic acid) ionomer blends

The miscibility of polystyrene with poly(butyl acrylate) is very poor. Ionic interactions have been utilized recently as miscibility enhancers. In this paper, dynamic mechanical studies indicate that ion pair–ion pair interactions can be utilized to achieve miscibility in blends of polystyrene and poly(butyl acrylate). The styrenes contain 0–15mol% quaternary ammonium salt of 4-vinylpyridine, while the butyl acrylates contain 0–15mol% potassium acrylate groups. The miscibility increases with increase of ion content. When the ion content exceeds 11mol%, the polymers can be completely miscible. The mechanical properties of the ionomers and their blends were also studied. The results indicate that the tensile strength of ionomer blends is higher than that of corresponding poly(butyl acrylate-co-potassium acrylate)s (PBA-AA-K). The elongation at break of ionomer blends is higher than that of the corresponding poly(styrene-co-N-methyl-4-vinylpyridinium iodide) (PS-4VP-Q). © 1998 SCI.     

羧基偏氯乙烯丁苯胶乳粒子的相态结构和应用性能

以过硫酸铵为引发剂，十二烷基硫酸钠为乳化剂，采用种子聚合工艺，合成了偏氯乙烯质量分数为２３％～４３％的羧基偏氯乙烯丁苯胶乳。通过电镜观察到所合成的胶乳粒子具有核－壳结构。通过测定胶闰子表面层的羧基数量，研究了羧基的分布，结果表明，羧酸种类对羧基在胶乳粒子中及在聚合体系中的分布有重要影响，该胶乳作为地毯背衬粘合剂，具有粘合力高，极限氧指数高的特点，是一种较好的阻燃性粘合剂。