Effect of fluorine in the preparation of Li(Ni1/3Co1/3Mn1/3)O2 via hydroxide co-precipitation

Uniform and spherical Li(Ni_1/3Co_1/3Mn_1/3)O_(2−δ)F_δ powders were synthesized via NH₃ and F⁻ coordination hydroxide co-precipitation. The effect of F⁻ coordination agent on the morphology, structure and electrochemical properties of the Li(Ni_1/3Co_1/3Mn_1/3)O_(2−δ)F_δ were studied. The morphology, size, and distribution of (Ni_1/3Co_1/3Mn_1/3)(OH)_(2−δ)F_δ particle diameter were improved in a shorter reaction time through the addition of F⁻. The study suggested that the added F improves the layered characteristics of the lattice and the cyclic performance of Li(Ni_1/3Co_1/3Mn_1/3)O₂ in the voltage range of 2.8-4.6 V. The initial capacity of the Li(Ni_1/3Co_1/3Mn_1/3)O_1.96F_0.04 was 178 mAh g⁻¹, the maximum capacity was 186 mAh g⁻¹ and the capacity after 50 cycles was 179 mAh g⁻¹ in the voltage range of 2.8-4.6 V.     

Electrochemical and thermal studies of Li[NixLi(1/3−2x/3)Mn(2/3−x/3)]O2 (x = 1/12, 1/4, 5/12, and 1/2)

Samples of the layered cathode materials, Li[Ni_xLi_(1/3−2x/3)Mn_(2/3−x/3)]O₂ (x = 1/12, 1/4, 5/12, and 1/2), were synthesized at 900 °C. Electrodes of these samples were charged in Li-ion coin cells to remove lithium. The charged electrode materials were rinsed to remove the electrolyte salt and then added, along with EC/DEC solvent or 1 M LiPF₆ EC/DEC, to stainless steel accelerating rate calorimetry (ARC) sample holders that were then welded closed. The reactivity of the samples with electrolyte was probed at two states of charge. First, for samples charged to near 4.45 V and second, for samples charged to 4.8 V, corresponding to removal of all mobile lithium from the samples and also concomitant release of oxygen in a plateau near 4.5 V. Li[Ni_xLi_(1/3−2x/3)Mn_(2/3−x/3)]O₂ samples with x = 1/4, 5/12 and 1/2 charged to 4.45 V do not react appreciably till 190 °C in EC/DEC. Li[Ni_xLi_(1/3−2x/3)Mn_(2/3−x/3)]O₂ samples charged to 4.8 V versus Li, across the oxygen release plateau, start to significantly react with EC/DEC at about 130 °C. However, their high reactivity is similar to that of Li_0.5CoO₂ (4.2 V) with 1 μm particle size. Therefore, Li[Ni_xLi_(1/3−2x/3)Mn_(2/3−x/3)]O₂ samples showing specific capacity of up to 225 mAh/g may be acceptable for replacing LiCoO₂ (145 mAh/g to 4.2 V) from a safety point of view, if their particle size is increased.     

Comparative study of Li[Co1−zAlz]O2 prepared by solid-state and co-precipitation methods

Li[Co_1−zAl_z]O₂ (0 ≤ z ≤ 0.5) samples were prepared by co-precipitation and solid-state methods. The lattice constants varied smoothly with z for the co-precipitated samples but deviated for the solid-state samples above z = 0.2. The solid-state method may not produce materials with a uniform cation distribution when the aluminum content is large or when the duration of heating is too brief. Non-stoichiometric Li_x[Co_0.9Al_0.1]O₂ samples were synthesized by the co-precipitation method at various nominal compositions x = Li/(Co + Al) = 0.95, 1.0, 1.1, 1.2, 1.3. XRD patterns of the Li_x[Co_0.9Al_0.1]O₂ samples suggest the solid solution limit is between Li/(Co + Al) = 1.1 and 1.2. Electrochemical studies of the Li[Co_1−zAl_z]O₂ samples were used to measure the rate of capacity reduction with Al content, found to be about −250 ± 30 (mAh/g)/(z = 1). Literature work on Li[Ni_1/3Mn_1/3Co_1/3−zAl_z]O₂, Li[Ni_1−zAl_z]O₂ and Li[Mn_2−yAl_y]O₄ demonstrates the same rate of capacity reduction with Al/(Al + M) ratio. These studies serve as baseline characterization of samples to be used to determine the impact of Al content on the thermal stability of delithiated Li[Co_1−zAl_z]O₂ in electrolyte.     

Synthetic optimization of spherical Li[Ni1/3Mn1/3Co1/3]O2 prepared by a carbonate co-precipitation method

A carbonate co-precipitation method was employed to prepare spherical Li[Ni_1/3Co_1/3Mn_1/3]O₂ cathode material. The precursor, [Ni_1/3Co_1/3Mn_1/3]CO₃, was prepared using ammonia as chelating agent under CO₂ atmosphere. The spherical Li[Ni_1/3Co_1/3Mn_1/3]O₂ was prepared by mixing the precalcined [Ni_1/3Co_1/3Mn_1/3]CO₃ with LiOH followed by high temperature calcination. The preparation conditions such as ammonia concentration, co-precipitation temperature, calcination temperature and Li/[Ni_1/3Co_1/3Mn_1/3] ratio were varied to optimize the physical and electrochemical properties of the prepared Li[Ni_1/3Co_1/3Mn_1/3]O₂. The structural, morphological, and electrochemical properties of the prepared LiNi_1/3Co_1/3Mn_1/3O₂ were characterized by XRD, SEM, and galvanostatic charge-discharge cycling. The optimized material has a spherical particle shape and a well ordered layered structure, and it also has an initial discharge capacity of 162.7 mAh g^− 1 in a voltage range of 2.8-4.3 V and a capacity retention of 94.8% after a hundred cycles. The optimized ammonia concentration, co-precipitation temperature, calcination temperature, and Li/[Ni_1/3Co_1/3Mn_1/3] ratio are 0.3 mol L^− 1, 60 °C, 850 °C, and 1.10, respectively.     

Synthesis and characterization of high-density non-spherical Li(Ni1/3Co1/3Mn1/3)O2 cathode material for lithium ion batteries by two-step drying method

Non-spherical Li(Ni_1/3Co_1/3Mn_1/3)O₂ powders have been synthesized using a two-step drying method with 5% excess LiOH at 800 °C for 20 h. The tap-density of the powder obtained is 2.95 g cm⁻³. This value is remarkably higher than that of the Li(Ni_1/3Co_1/3Mn_1/3)O₂ powders obtained by other methods, which range from 1.50 g cm⁻³ to 2.40 g cm⁻³. The precursor and Li(Ni_1/3Co_1/3Mn_1/3)O₂ are characterized by X-ray photoelectron spectroscopy (XPS), X-ray diffraction (XRD) and scanning electron microscope (SEM). XPS studies show that the predominant oxidation states of Ni, Co and Mn in the precursor are 2⁺, 3⁺ and 4⁺, respectively. XRD results show that the Li(Ni_1/3Co_1/3Mn_1/3)O₂ material obtained by the two-step drying method has a well-layered structure with a small amount of cation mixing. SEM confirms that the Li(Ni_1/3Co_1/3Mn_1/3)O₂ particles obtained by this method are uniform. The initial discharge capacity of 167 mAh g⁻¹ is obtained between 3 V and 4.3 V at a current of 0.2 C rate. The capacity of 159 mAh g⁻¹ is retained at the end of 30 charge-discharge cycle with a capacity retention of 95%.     

Characterization of high tap density Li[Ni1/3Co1/3Mn1/3]O2 cathode material synthesized via hydroxide co-precipitation

Li[Ni_1/3Co_1/3Mn_1/3]O₂ cathode material for lithium ion batteries was prepared by mixing metal hydroxide, (Ni_1/3Co_1/3Mn_1/3)(OH)₂, with 6% excess LiOH followed by calcinations. The (Ni_1/3Co_1/3Mn_1/3)(OH)₂ with secondary particle of about 12 μm was prepared by hydroxide co-precipitation. The tap density of the obtained Li[Ni_1/3Co_1/3Mn_1/3]O₂ powder was 2.56 ± 0.21 g cm⁻³. The powder was characterized by X-ray diffraction (XRD), scanning electron microscope (SEM), particle size distribution (PSD) and galvanostatic charge-discharge cycling. The XRD pattern of Li[Ni_1/3Co_1/3Mn_1/3]O₂ revealed a well ordered hexagonal layered structure with low cation mixing. Secondary particles with size of 13-14 μm and primary particles with size of about 1 μm can be identified from the SEM observations. In the voltage range of 2.8-4.3 V, the initial discharge capacity of the Li[Ni_1/3Co_1/3Mn_1/3]O₂ electrode was 166.6 mAh g⁻¹, and 96.5% of the initial capacity was retained after 50 charge-discharge cycling.     

The first cycle characteristics of Li[Ni1/3Co1/3Mn1/3]O2 charged up to 4.7 V

In this research, we studied the first cycle characteristics of Li[Ni_1/3Co_1/3Mn_1/3]O₂ charged up to 4.7 V. Properties, such as valence state of the transition metals and crystallographic features, were analyzed by X-ray absorption spectroscopy and X-ray and neutron diffractions. Especially, two plateaus observed around 3.75 and 4.54 V were investigated by ex situ X-ray absorption spectroscopy. XANES studies showed that the oxidation states of transition metals in Li[Ni_1/3Co_1/3Mn_1/3]O₂ are mostly Ni²⁺, Co³⁺ and Mn⁴⁺. Based on neutron diffraction Rietveld analysis, there is about 6% of all nickel divalent (Ni²⁺) ions mixed with lithium ions (cation mixing). Meanwhile, it was found that the oxidation reaction of Ni²⁺/Ni⁴⁺ is related to the lower plateau around 3.75 V, but that of Co³⁺/Co⁴⁺ seems to occur entire range of x in Li_1−x[Ni_1/3Co_1/3Mn_1/3]O₂. Small volume change during cycling was attributed to the opposite variation of lattice parameter “c” and “a” with charging-discharging.     

Hydrothermal synthesis of Li(Ni1/3Co1/3Mn1/3)O2 for lithium rechargeable batteries

Ultrafine powders of Li(Ni_1/3Co_1/3Mn_1/3)O₂ cathode materials for lithium-ion secondary batteries were prepared under mild hydrothermal conditions. The influence of the molar ratio of Li/(Ni + Co + Mn) was studied. The products were investigated by XRD, TEM and EDS. The final products were found to be well crystallized Li(Ni_1/3Co_1/3Mn_1/3)O₂ with an average particle size of about 10 nm.     

Effect of synthesis condition on the structural and electrochemical properties of Li[Ni1/3Mn1/3Co1/3]O2 prepared by the metal acetates decomposition method

In order to get homogeneous layered oxide Li[Ni_1/3Mn_1/3Co_1/3]O₂ as a lithium insertion positive electrode material, we applied the metal acetates decomposition method. The oxide compounds were calcined at various temperatures, which results in greater difference in morphological (shape, particle size and specific surface area) and the electrochemical (first charge profile, reversible capacity and rate capability) differences. The Li[Ni_1/3Mn_1/3Co_1/3]O₂ powders were characterized by means of X-ray diffraction (XRD), charge/discharge cycling, cyclic voltammetry and SEM. XRD experiment revealed that the layered Li[Ni_1/3Mn_1/3Co_1/3]O₂ material can be best synthesized at temperature of 800 °C. In that synthesized temperature, the sample showed high discharge capacity of 190 mAh g⁻¹ as well as stable cycling performance at a current density of 0.2 mA cm⁻² in the voltage range 2.3-4.6 V. The reversible capacity after 100 cycles is more than 190 mAh g⁻¹ at room temperature.     

One-step synthesis and improved electrochemical performance of Li(Ni1/3Co1/3Mn1/3)O2 by a modified radiated polymer gel method

We present the mechanism for the synthesis of a layered Li(Ni_1/3Co_1/3Mn_1/3)O₂ compound by a modified radiated gel method. Pure-phase Li(Ni_1/3Co_1/3Mn_1/3)O₂ material was achieved when the polymer gel was calcined at 900 °C between 15 and 30 h. The unit cell parameter c decreased, and a varied slightly with increased sintering time. Electrochemical characterization revealed that the optimized sample (25 h) had a high initial discharge capacity of 188 mAh/g (2.8-4.5 V, 20 mA/g), an excellent capacity retention of 90.1% after 30 cycles and a good rate performance.     

Effect of synthesis condition on the structure and electrochemical properties of Li[Ni1/3Mn1/3Co1/3]O2 prepared by hydroxide co-precipitation method

The layered Li[Ni_1/3Co_1/3Mn_1/3]O₂ powder with good crystalline and spherical shape was prepared by hydroxide co-precipitation method. The effects of pH value, NH₄OH amount, calcination temperature and extra Li amount on the morphology, structure and electrochemical properties of the cathode material were investigated in detail. SEM results indicate that pH value affected both the morphology and the property of the cathode material, and the highest discharge capacity in the first cycle of 163 mAh g⁻¹ (2.8-4.3 V) was obtained at pH value was 12. On the contrary, the NH₄OH amount, which was used as a chelating agent, only affected the particle size distribution of the material. The calcination temperatures caused great difference in the structure and property of layered Li[Ni_1/3Co_1/3Mn_1/3]O₂, and the best electrochemical properties were obtained at the calcination temperature of 800 °C. Extra Li amount not only caused difference in the material structure, but also affected their electrochemical properties. With increasing Li amount, the lattice parameters (a and c) increased monotonously, and the highest first cycle coulombic efficiency (the ratio of discharge capacity to charge capacity in the first cycle) was obtained with the Li/M of 1.10. Therefore, the optimum synthetic conditions for the hydroxide co-precipitation reaction were: pH value was 12, NH₄OH amount was 0.36 mol L⁻¹, calcination temperature was 800 °C and the Li/M molar ratio was 1.10.     

Improved electrochemical properties of Li1+x(Ni0.3Co0.4Mn0.3)O2−δ (x = 0, 0.03 and 0.06) with lithium excess composition prepared by a spray drying method

Layered Li_1+x(Ni_0.3Co_0.4Mn_0.3)O_2−δ (x = 0, 0.03 and 0.06) materials were synthesized through the different calcination times using the spray-dried precursor with the molar ratio of Li/Me = 1.25 (Me = transition metals). The physical and electrochemical properties of the lithium excess and the stoichiometric materials were examined using XRD, AAS, BET and galvanostatic electrochemical method. As results, the lithium excess Li_1.06(Ni_0.3Co_0.4Mn_0.3)O_2−δ could show better electrochemical properties, such as discharge capacity, capacity retention and C rate ability, than those of the stoichiometric Li_1.00(Ni_0.3Co_0.4Mn_0.3)O_2−δ. In this paper, the effect of excess lithium on the electrochemical properties of Li_1+x(Ni_0.3Co_0.4Mn_0.3)O_2−δ materials will be discussed based on the experimental results of ex situ X-ray diffraction, transmission electron microscopy (TEM) and galvanostatic intermittent titration technique (GITT)     

Improvement of electrochemical properties of Li[Ni0.4Co0.2Mn(0.4−x)Mgx]O2−yFy cathode materials at high voltage region

Spherical Li[Ni_0.4Co_0.2Mn_(0.4−x)Mg_x]O_2−yF_y (x = 0, 0.04, y = 0, 0.08) with phase-pure and well-ordered layered structure have been synthesized by heat-treatment of spherical [Ni_0.4Co_0.2Mn_0.4−xMg_x]₃O₄ precursors with LiOH·H₂O and LiF salts. The average particle size of the powders was about 10-15 μm and the size distribution was quite narrow due to the homogeneity of the metal carbonate, [Ni_0.4Co_0.2Mn_(0.4−x)Mg_x]CO₃ (x = 0, 0.04) precursors. Although the Li[Ni_0.4Co_0.2Mn_0.36Mg_0.04]O_1.92F_0.08 delivered somewhat slightly lower initial discharge capacity, however, the capacity retention, interfacial resistance, and thermal stability were greatly enhanced comparing to the Li[Ni_0.4Co_0.2Mn_0.4]O₂ and Li[Ni_0.4Co_0.2Mn_0.36Mg_0.04]O₂.     

Structural and electrochemical behaviors of metastable Li2/3[Ni1/3Mn2/3]O2 modified by metal element substitution

Layered metastable lithium manganese oxides, Li_2/3[Ni_1/3−xMn_2/3−yM_x+y]O₂ (x = y = 1/36 for M = Al, Co, and Fe and x = 2/36, y = 0 for M = Mg) were prepared by the ion exchange of Li for Na in P2-Na_2/3[Ni_1/3−xMn_2/3−yM_x+y]O₂ precursors. The Al and Co doping produced the T^#2 structure with the space group Cmca. On the other hand, the Fe and Mg doped samples had the O6 structure with space group R-3m. Electron diffraction revealed the 1:2 type ordering within the Ni_1/3−xMn_2/3−yM_x+yO₂ slab. It was found that the stacking sequence and electrochemical performance of the Li cells containing T^#2-Li_2/3[Ni_1/3Mn_2/3]O₂ were affected by the doping with small amounts of Al, Co, Fe, and Mg. The discharge capacity of the Al doped sample was around 200 mAh g⁻¹ in the voltage range between 2.0 and 4.7 V at the current density of 14.4 mA g⁻¹ along with a good capacity retention. Moreover, for the Al and Co doped and undoped oxides, the irreversible phase transition of the T^#2 into the O2 structure was observed during the initial lithium deintercalation.     

Synthesis and characterization of LiNi1/3Mn1/3Co1/3O2 by wet-chemical method

A series of LiNi_1/3Mn_1/3Co_1/3O₂ samples with α-NaFeO₂ structure belonging to the D_3d⁵ space group were synthesized using tartaric acid as a chelating agent by wet-chemical method. Different acid to metal-ion ratios R have been used to investigate the effect of this parameter on the physical and electrochemical properties. We have characterized the reaction mechanism, the structure, and morphology of the powders by TGA, XRD, SEM and TEM imaging, completed by magnetic measurements, Raman scattering spectroscopy, and complex impedance experiments. We find that the LiNi_1/3Mn_1/3Co_1/3O₂ sintered at 900 °C for 15 h with an acid to metal-ion ratio R = 2 was the optimum condition for this synthesis. For this optimized sample, only 1.3% of nickel-ions occupied the 3b Wyckoff site of the lithium-ions sublattice. The electrochemical performance has been investigated using a coin-type cell containing Li metal as the anode. The electronic performance is correlated to the concentration of the Ni(3b) defects that increase the charge transfer resistance and reduce the lithium diffusion coefficient. The optimized cell delivered an initial discharge capacity of 172 mAh g⁻¹ in the cut-off voltage of 2.8-4.4 V, with a coulombic efficiency of 93.4%.     

Zr-doped Li[Ni0.5−xMn0.5−xZr2x]O2 (x = 0, 0.025) as cathode material for lithium ion batteries

Layered Li[Ni_0.5−xMn_0.5−xZr_2x]O₂ (x = 0, 0.025) have been prepared by the mixed hydroxide and molten-salt synthesis method. The individual particles of synthesized materials have a sub-microsize range of 200-500 nm, and LiNi_0.475Mn_0.475Zr_0.05O₂ has a rougher surface than that of LiNi_0.5Mn_0.5O₂. The Li/Li[Ni_0.5−xMn_0.5−xZr_2x]O₂ (x = 0, 0.025) electrodes were cycled between 4.5 and 2.0 V at a current density of 15 mA/g, the discharge capacity of both cells increased during the first ten cycles. The discharge capacity of the Li/LiNi_0.475Mn_0.475Zr_0.05O₂ cell increased from 150 to 220 mAh/g, which is 50 mAh/g larger than that of the Li/LiNi_0.5Mn_0.5O₂ cell. We found that the oxidation of oxygen and the Mn³⁺ ion concerned this phenomenon from the cyclic voltammetry (CV). Thermal stability of the charged Li[Ni_0.5−xMn_0.5−xZr_2x]O₂ (x = 0, 0.025) cathode was improved by Zr doping.     

Particle size effect of Li[Ni0.5Mn0.5]O2 prepared by co-precipitation

Spherical (Ni_0.5Mn_0.5)(OH)₂ with different secondary particle size (3 μm, 10 μm in diameter) was synthesized by co-precipitation method. Mixture of the prepared hydroxide and lithium hydroxide was calcined at 950 °C for 20 h in air. X-ray diffraction patterns revealed that the prepared material had a typical layered structure with space group. Spherical morphologies with mono-dispersed powders were observed by scanning electron microscopy. It was found that the layered Li[Ni_0.5Mn_0.5]O₂ delivered an initial discharge capacity of 148 mAh g⁻¹ (3.0-4.3 V) though the particle sizes were different. Li[Ni_0.5Mn_0.5]O₂ having smaller particle size (3 μm) showed improved area specific impedance due to the reduced Li⁺ diffusion path, compared with that of Li[Ni_0.5Mn_0.5]O₂ possessing larger particle size (10 μm). Although the Li[Ni_0.5Mn_0.5]O₂ (3 μm) was electrochemically delithiated to Li_0.39[Ni_0.5Mn_0.5]O₂, the resulting exothermic onset temperature was around 295 °C, of which the value is significantly higher than that of highly delithiated Li_1−δCoO₂ (∼180 °C).     

Synthesis and improved electrochemical performance of Al (OH)3-coated Li[Ni1/3Mn1/3Co1/3]O2 cathode materials at elevated temperature

Spherical Li[Ni_1/3Co_1/3Mn_1/3]O₂ powders were synthesized from LiOH·H₂O and coprecipitated spherical metal hydroxide, (Ni_1/3Mn_1/3Co_1/3)(OH)₂ and coated with Al(OH)₃. The Al(OH)₃-coated Li[Ni_1/3Co_1/3Mn_1/3]O₂ showed a capacity retention of 80% at 320 mA g⁻¹ (2 C-rate) based on 20 mA g⁻¹ (0.1 C-rate), while the pristine Li[Ni_1/3Co_1/3Mn_1/3]O₂ delivered only 45% at the same current density. Also, unlike pristine Li[Ni_1/3Co_1/3Mn_1/3]O₂, the Al(OH)₃-coated Li[Ni_1/3Co_1/3Mn_1/3]O₂ cathode exhibits excellent rate capability and good thermal stability.     

Insignificant impact of designed oxygen release from high capacity Li[(Ni1/2Mn1/2)xCoy(Li1/3Mn2/3)1/3]O2 (x + y = 2/3) positive electrodes during the cycling of Li-ion cells

The properties of graphite/Li[(Ni_0.5Mn_0.5)_xCo_y(Li_1/3Mn_2/3)_1/3]O₂ (x + y = 2/3, y = 1/12 and 1/6) Li-ion cells are reported. There is an extended plateau near 4.5 V during the first charging of the cells that corresponds to the simultaneous removal of Li and oxygen from the Li[(Ni_0.5Mn_0.5)_xCo_y(Li_1/3Mn_2/3)_1/3]O₂ (x + y = 2/3, y = 1/12 and 1/6) electrodes. The release of this oxygen directly within a Li-ion cell has been a cause for concern. However, it was found that subsequent to O₂ release, Li-ion cells delivered a high reversible positive electrode specific capacity near 250 mAh/g at C/30 between 2.5 and 4.8 V, the cells did not display increased irreversible capacity relative to counterparts having Li metal negative electrodes and the cells retained 85% of their initial capacity after 70 cycles at C/6 between 2.5 and 4.6 V. Therefore, the O₂ released during the first charge does not significantly impact the electrochemical properties of graphite/Li[(Ni_0.5Mn_0.5)_xCo_y(Li_1/3Mn_2/3)_1/3]O₂ (x + y = 2/3) lithium-ion cells.     

Improvement of electrochemical and thermal properties of Li[Ni0.8Co0.1Mn0.1]O2 positive electrode materials by multiple metal (Al, Mg) substitution

Al and/or Mg-substituted Li[Ni_0.8Co_0.1Mn_0.1−x−yAl_xMg_y]O₂ were prepared by a co-precipitation method and characterized by X-ray diffraction with Rietveld refinement, thermogravimetric analysis, differential scanning calorimetry (DSC), and electrochemical measurements. The Rietveld refinement results show that cation mixing of Al and/or Mg-substituted Li[Ni_0.8Co_0.1Mn_0.1−x−yAl_xMg_y]O₂ was reduced with increased doping amounts of Al and Mg. The Al and/or Mg substitution in Li[Ni_0.8Co_0.1Mn_0.1]O₂ also resulted in improved electrochemical cycling behavior, structural stability, and thermal stability compared to pristine Li[Ni_0.8Co_0.1Mn_0.1]O₂. The improvements of electrochemical and thermal properties resulted from the stabilized host structure by Al and/or Mg incorporation into Li[Ni_0.8Co_0.1Mn_0.1]O₂.