以硫酸钛为原料,采用水解法制备了硫掺杂偏钛酸粉体,采用场发射扫描电镜(FESEM)、激光粒度分析等技术对偏钛酸粉体的形貌及粒度进行了分析.系统研究了硫酸钛溶液浓度、水解温度、pH值对水解率、偏钛酸粉体粒径的影响,研究结果表明:硫酸钛溶液浓度、pH值及水解温度对偏钛酸颗粒粒径及原料水解率具有显著影响.最佳工艺条件为:硫酸钛溶液的质量浓度为65 g/L、水解温度60℃、pH值为7.     

碱法钛白粉生产工艺中硫酸钛溶液的制备和水解

研究了碱法钛白粉清洁生产工艺中硫酸钛溶液的制备及水解。硫酸钛溶液制备过程中,通过试验及MATLAB拟合,确定了硫酸质量分数、原料用量与硫酸钛溶液质量浓度及酸度系数(F值)间的函数关系;水解过程中,考察了水解温度、酸度系数(F值)、硫酸钛质量浓度对水解的影响。在优化水解条件下,钛水解率达90%以上,制得的偏钛酸在高温下煅烧可得到金红石型和锐钛矿型二氧化钛。     

钛渣熔盐反应制备TiO2体系中水解制备偏钛酸过程研究

NaOH熔盐法用钛渣制备TiO2是一种制备二氧化钛的新方法,水解制备偏钛酸是新工艺中重要的环节之一。试验考察了钛液的浓度、F值及水解时间等影响偏钛酸粒度及转化率的因素。结果表明,钛液水解率在开始的30 min左右均较低,50 min以后迅速提高,100 min以后水解率随时间变化趋于平缓。温度越高,F值越低,钛液浓度越低,水解反应进行得越快,且最终转化率较高。水解产物偏钛酸粒度开始随水解反应时间增加而增大,3 h后偏钛酸的粒度随时间增加略有波动,偏钛酸的粒径随钛液浓度及F值增大而减小,随钛液稳定度提高而减小。试验确定的偏钛酸制备工艺条件如下:TiO2浓度200 g/L左右,F值1.8～1.9,微沸状态下水解,水解时间4 h。     

氯化法偏钛酸的水解试验研究

以氯化钛液为原料,考察H~+和Ti~(4+)浓度、反应温度和时间对氯化法偏钛酸水解率及其粒径分布的影响。结果表明,随H~+浓度的增大,偏钛酸的水解率和粒径均先增大后减小;Ti~(4+)浓度对偏钛酸的水解率影响不大,但增大Ti~(4+)浓度有利于偏钛酸晶核的成长;提高反应温度有利于偏钛酸的水解及其晶核的长大;随着水解时间的增加,偏钛酸的水解率逐渐增加,但对偏钛酸粒径的影响甚微。在H~+浓度1.2 g/L、Ti~(4+)浓度20 g/L、水解温度108℃、水解时间2.5 h的最佳条件下可以得到呈片状团聚体、粒径2~10λm的偏钛酸。     

锐钛矿型TiO2纳米颗粒的水热法合成及其特性

以硫酸钛为钛源,浓氨水为沉淀剂,通过水热法水解合成TiO2.利用XRD、SEM和TEM对试样进行分析,结果表明:当硫酸钛溶液水解时不加入浓氨水,随着水解时间的延长,获得的锐钛矿型TiO2颗粒的粒径没有明显的变化;当硫酸钛溶液水解时加入浓氨水,合成锐钛矿型TiO2颗粒的粒径明显变小,在240℃、48.0h和pH =9.0...     

Study on Preparation of Mctatitanic Acid by Hydrolysis in the Process of Producing Titanium Dioxide by Decomposition of Titanium Slag with Alkali Molten Salt

NaOH熔盐法用钛渣制备TiO2是一种制备二氧化钛的新方法,水解制备偏钛酸是新工艺中重要的环节之一.试验考察了钛液的浓度、F值及水解时间等影响偏钛酸粒度及转化率的因素.结果表明,钛液水解率在开始的30 min左右均较低,50 min以后迅速提高,100 min以后水解率随时间变化趋于平缓.温度越高,F值越低,钛液浓度越低,水解反应进行得越快,且最终转化率较高.水解产物偏钛酸粒度开始随水解反应时间增加而增大,3h后偏钛酸的粒度随时间增加略有波动,偏钛酸的粒径随钛液浓度及F值增大而减小,随钛液稳定度提高而减小.试验确定的偏钛酸制备工艺条件如下:TiO2浓度200g/L左右,F值1.8～1.9,微沸状态下水解,水解时间4h.     

含钛硫酸浸出液的水解研究

制备了含钛硫酸浸出液,并通过单因素和正交试验考查了水解时间、水解温度和钛液浓度对水解率的影响。结果表明,影响二氧化钛水解率因素的主次顺序为:水解温度、钛液浓度和水解时间。较佳水解条件为:水解温度95℃、钛液浓度110g/L,水解时间210min,此时,水解率为97.12%,能满足工业生产要求。     

超声波场中硫酸氧钛的水解研究

本文简要介绍了硫酸氧钛溶液在超声场中水解的实验研究。实验中探讨了用分光光度计比色测定水解临界点的可行性，并通过分别测定超声波场作用下以及无场作用下硫酸氧钛溶液的水解临界点和水解率。探讨在自生晶种的钛水解工艺中，超声振动对晶核形成过程的促进作用。结合SEM形貌及元素含量分析，X射线衍射分析，初步探讨了超声波对水解过程的影响机理。     

加料速率对低浓度钛液水解的影响

对硫酸氧钛溶液的水解过程进行了试验研究,着重考察了钛液加料速率对低浓度钛液水解率、变灰点、水解物一次及二次颗粒尺寸等的影响。结果表明,随着加料速率的降低,钛液的水解率增加,这是因为慢的加料速率增大了初期钛液稀释度且其持续时间较长,形成晶种数量更多;随着加料速率降低,钛液变灰的时间缩短;加料速率影响了水解物一次颗粒尺寸,慢的加料速率有助于形成细小均匀的一次颗粒;低浓度水解物颗粒(二次颗粒)的平均粒径在1.69~1.78μm,随着加料速率降低,所得水解产物的粒度分布变窄,且水解物从无规则、较为密实的颗粒逐渐向球形、疏松颗粒变化。通过关于加料速率的研究,对钛液水解生产工艺改进起到进一步指导作用。     

工业钛液制备水解晶种粒径影响因素研究

以工业钛液为原料,采用目前硫酸法钛白企业常用的氢氧化钠溶液中和法制备水解晶种工艺,改变关键原料指标和工艺参数,考察晶种粒径和晶种稳定性的变化规律。然后将不同粒径的晶种用于水解,研究了晶种粒径对偏钛酸粒径及固定盐处理煅烧后所得金红石钛白初品粒径和消色力的影响。结果表明,随着钛液TiO₂浓度、F值、铁钛比以及碱液浓度的升高,相同稳定性下晶种粒径变大;随着晶种制备碱钛比、钛液预热温度、碱液预热温度的增加,相同稳定性下晶种粒径减小;随着熟化时间的延长,晶种稳定性降低,晶种粒径变大。随着晶种粒径的变大,水解所得偏钛酸D₅₀和径距逐渐变小,偏钛酸晶粒尺寸略增;对应金红石钛白初品的SEM平均粒径和标准差逐渐减小,同时其Tcs、Scx均增加。     

短流程制备金红石钛白的水解条件回归分析

以未浓缩低浓度工业钛液为水解原料,通过自生晶种稀释热水解的硫酸法钛白短流程工艺制备金红石型颜料钛白,研究了水解条件(底水量、熟化时间和水解时间)对偏钛酸和金红石产物的结构、粒径分布和颜料性能等的影响规律及数学回归关系。水解条件对水解初始形成晶种的数量和质量、晶粒的生长和聚集等起重要影响,并最终决定产品的颜料性能;水解条件与产物的晶体结构、颗粒多分散度和颜料性能间存在数学相关关系。最优水解条件为:底水量比例为0.123,熟化时间为29.05 min,二沸后的水解时间为2.6 h左右。     

钛钽铌矿强化分解工艺的研究

对难分解的钛钽铌矿的酸分解工艺进行了试验研究。在原钽铌矿酸分解工艺的基础上,通过降低矿粉粒度、加大酸用量和延长分解时的保温时间等措施,使Ta2O5、Nb2O5的分解率由原来的72 3%和73 6%均提高到>97%,获得了令人满意的结果。     

Dissolution studies of mechanically activated Manavalakurichi ilmenite with HCl and H2SO4

The effect of the change in phase constitution, particle size distribution, surface area, crystallite size, strain and lattice parameters introduced by mechanical activation of the altered beach sand ilmenite from Manavalakurichi region, India on the dissolution kinetics of HCl and H₂SO₄ was investigated. The altered ilmenite showed different physico-chemical characteristics and was found to be more resistant to acid leaching than the less altered ilmenite from the Chatrapur beach sands, India investigated earlier. The dissolution behavior was also different in H₂SO₄ and HCl. For sulfuric acid leaching, the dissolution of Fe and Ti increased monotonically with time of milling and showed a continuous increase with time of leaching, whereas hydrolysis of titanium occurs in HCl medium, especially for the activated samples at lower acid concentration, lower solid to liquid ratio and higher temperature leading to lower solution recoveries. The dissolution kinetics in both H₂SO₄ and HCl prior to hydrolysis conforms initially to the reaction rate control model and for higher leaching times to the shrinking core model where diffusion through the product layer is rate controlling. It is postulated that the anatase formed by hydrolysis in milled samples impedes the further progress of leaching. The activation energies for the dissolution of Fe and Ti decreased with time of milling and were marginally lower in HCl than in H₂SO₄. An attempt has also been made to correlate the decrease in activation energy to the increase in the energy input to the material through high-energy milling. The relative contribution of the increase in surface area and structural disorder on the enhancement of the dissolution rates has been evaluated.     

（Y,Eu）2O3红生粉的粒度和形貌控制研究

以草酸共沉淀法制备（Y,Eu）₂O₃为红生粉,对比六种沉淀方式对红生粉形貌的影响,其中在沉淀过程中添加氨水并用双加料的方式可制备出形貌上优于红生粉商品,其粒度分布呈正态分布;通过调节草酸过量系数、沉淀过程中添加氨水的量、合成温度及草酸浓度等沉淀条件可控制红生D₅₀的变化。      

工业钛液制备掺杂多孔二氧化钛及其光催化性能研究

以工业钛液为钛源,调节钛液指标和钛液底水体积比,热水解制备出掺杂多孔锐钛型TiO2.采用XRD、粒度分布、等温N2吸附-脱附及XRF等对样品进行表征.不同的钛液底水体积比对合成多孔TiO2的晶体结构、粒径、比表面积和孔道结构等具有较大影响,锐钛相晶型改善、比表面积提高及离子掺杂等有助于其光催化活性的提高.钛液底水体积比...     

Reductive leaching of pyrolusite ore by using sawdust for production of manganese sulfate

Manganese compounds, such as manganese sulfate, can be obtained from pyrolusite, a manganese ore. Low-grade manganese ores is usually treated by hydrometallurgical methods. In this study, the leaching and recovery of manganese from pyrolusite ore in sulfuric acid solutions containing sawdust as reducing agent was investigated. The effects of experimental parameters, such as sulfuric acid concentration, sawdust amount, solid-to-liquid ratio, stirring speed, particle size, reaction temperature, and leaching time, on the manganese extraction from ore were examined. The results showed that the leaching rate of pyrolusite ore increased with an increasing sulfuric acid concentration, sawdust amount, stirring speed, reaction temperature and leaching time, and decreasing in solid to liquid ratio and particle size. The kinetic analysis of leaching process was carried out, and it was determined that the reaction rate was controlled by diffusion through the product layer under the experimental conditions in this work. The activation energy was found to be 22.35 kJ mol^?1. Manganese can be recovered as manganese sulfate by the evaporative crystallization of the purified leach liquor.     

高强度帘线钢中氮化钛夹杂的固溶行为分析

为了提高帘线钢盘条的质量,实现轧制过程高强度帘线钢中大颗粒氮化钛夹杂的有效控制,通过试验钢中氮化钛夹杂的固溶试验研究,探讨了高强度帘线钢在加热过程中氮化钛夹杂的固溶行为和影响机制。结果表明,氮化钛夹杂在加热升温阶段存在较为明显的固溶行为,且固溶效果与加热温度和保温时间密切相关。通过适当提高轧钢加热炉温度和延长保温时间以及随后的快速冷却,可以对高强度帘线钢中大颗粒氮化钛夹杂的尺寸和数量进行有效控制。