Cu对纳米晶复合合金Nd_(9.5)Fe_(76-x)Cu_xCo_5Zr_3B_(6.5)(x=0～2)磁性能的影响

采用快淬后真空晶化处理的方法制备出纳米晶复合合金Nd9.5Fe76-xCo5Zr3CuxB6.5(x=0～2),系统地研究了Cu元素对其磁性能的影响。结果表明:适量Cu元素的添加,可以提高磁体的剩磁Br、内禀矫顽力jHc和最大磁能积(BH)max,并且可以有效地提高磁体的剩磁温度系数α,但使磁体的矫顽力温度系数β略有降低。当Cu含量为0.25 at%时,该磁体具有最佳的综合磁性能:(BH)max=79 kJ/m3,jHc=685 kA/m,Br(T)=0.713 T;剩磁温度系数α20～150℃=0.071%/℃;矫顽力温度系数β20～150℃=0.36%/℃。     

添加Dy对纳米晶复合Nd8.5Fe77Ga0.6Co5Zr2.7B6.2永磁材料磁性能和温度系数的影响

采用快淬后真空晶化退火工艺制备了成分为Nd8.5-xDyxFe77Ga0.6Co5Zr2.7B6.2(x=0,0.5,1.0)的纳米晶复合永磁粘结磁体,研究其磁性能和温度系数的变化。结果表明,添加Dy元素能有效提高磁体的内禀矫顽力,但使其剩磁和较大磁能积略有下降。Dy含量为0.5at%时,制得的粘结磁体具有较佳磁性能:Br=0.728T,jHc=656.3kA/m,(BH)max=76.2kJ/m3。随着Dy元素的添加,合金的剩磁温度系数α逐渐降低,当Dy=1at%时,在20℃~150℃温度区间内平均剩磁温度系数α=-0.12%/℃。随着Dy元素的添加,合金的内禀矫顽力温度系数β呈先下降后上升的趋势。在Dy=0.5at%时,具有较低的β值,在20℃~150℃温度区间内平均内禀矫顽力温度系数β=-0.34%/℃。     

添加Dy对纳米晶复合Nd8．5Fe77Ga0．6C05Zr2．7B6．2永磁材料磁性能和温度系数的影响

采用快淬后真空晶化退火工艺制备了成分为Nd8.5-xDyxFe77Ga0.6Co5Zr2.7B6.2（x=0,0．5,1．0）的纳米晶复合永磁粘结磁体,研究其磁性能和温度系数的变化。结果表明,添加Dy元素能有效提高磁体的内禀矫顽力,但使其剩磁和较大磁能积略有下降。Dy含量为0．5at％时,制得的粘结磁体具有较佳磁性能：Br=0．728T,jHc=656．3kA／m,（BH）max=76．2kJ/m^3。随着Dy元素的添加,合金的剩磁温度系数α逐渐降低,当Dy=1at％时,在20℃～150℃温度区间内平均剩磁温度系数α=-0．12％／℃。随着Dy元素的添加,合金的内禀矫顽力温度系数β呈先下降后上升的趋势。在Dy=0．5at％时,具有较低的β值,在20℃～150℃温度区间内平均内禀矫顽力温度系数β=-0．34％／℃。     

Nd_2Fe_(14)B/α-Fe系纳米晶复合永磁合金的磁黏滞行为及其交互作用

利用扫描速率法研究纳米晶复合永磁合金Nd_(8.5)Fe_(76)Co_5Zr_3B_(6.5)Dy_1,Nd_(9.5)Fe_(75)Co_5Zr_3B_(6.5)Nb_1和Nd_(9.5)Fe_(75.4)Co_5Zr_3B_(6.5)Ga_(0.6)的磁黏滞行为,计算了合金的扰动场及磁交换长度,分析了其交互作用、微观结构和磁性能之间的关系.结果表明,3种合金的扰动场分别为4.80,4.87和5.09 k A/m;磁交换长度差别不大,分别为4.53,4.41和4.20 nm.Nd_(9.5)Fe_(75)Co_5Zr_3B_(6.5)Nb_1合金的交互作用最强,主要是因为合金中的晶粒尺寸细小(约为15 nm)且分布均匀.3种合金均呈单一的硬磁特征,其中Nd_(9.5)Fe_(75.4)Co_5Zr_3B_(6.5)Ga_(0.6)合金磁化反转的一致性最好,使得其剩磁较高,最大磁能积较大.     

Dy元素对纳米复合(Nd,Pr)_(10.5-x)Dy_xFe_(83.5)B_6合金磁性能与显微结构的影响（英文）EI北大核心CSCD

采用快淬法制备了镨基(Nd,Pr)10.5-x Dyx Fe83.5B6(x=0.0,0.5,1.0,1.5,2.0,2.5)系列粘结磁体,研究了Dy元素添加对快淬合金显微组织结构、磁性能及快淬薄带热稳定性的影响。与Nd2Fe14B相比,硬磁相Dy2Fe14B具有较高的磁晶各向异性场HA和较低的饱和磁极化强度Js,因此,Dy元素添加能显著提高合金的内禀矫顽力Hcj,但会降低合金的剩磁Br。Dy元素替代Nd/Pr元素,增强了快淬薄带的热稳定性,提高了晶化退火温度。较高的晶化退火温度,使快淬薄带中已经形成的微晶更容易长大,形成一些粗大晶粒,降低了粘结磁体的磁性能。1.0%是较佳的Dy元素添加量,(Nd,Pr)9.5Dy1Fe83.5B6合金快淬粘结磁体的最大磁能积(BH)max为71.6 k J/m3,剩磁Br为0.638 T,内禀矫顽力Hcj为611 k A/m。     

Dy元素对纳米复合(Nd,Pr)_(10.5-x)Dy_xFe_(83.5)B_6合金磁性能与显微结构的影响（英文）

采用快淬法制备了镨基(Nd,Pr)10.5-x Dyx Fe83.5B6(x=0.0,0.5,1.0,1.5,2.0,2.5)系列粘结磁体,研究了Dy元素添加对快淬合金显微组织结构、磁性能及快淬薄带热稳定性的影响。与Nd2Fe14B相比,硬磁相Dy2Fe14B具有较高的磁晶各向异性场HA和较低的饱和磁极化强度Js,因此,Dy元素添加能显著提高合金的内禀矫顽力Hcj,但会降低合金的剩磁Br。Dy元素替代Nd/Pr元素,增强了快淬薄带的热稳定性,提高了晶化退火温度。较高的晶化退火温度,使快淬薄带中已经形成的微晶更容易长大,形成一些粗大晶粒,降低了粘结磁体的磁性能。1.0%是较佳的Dy元素添加量,(Nd,Pr)9.5Dy1Fe83.5B6合金快淬粘结磁体的最大磁能积(BH)max为71.6 k J/m3,剩磁Br为0.638 T,内禀矫顽力Hcj为611 k A/m。     

熔体温度对快淬法制备纳米晶复合Nd_(8.5)Fe_(77)Co_5Zr_3B_(6.5)合金微观结构和磁性能的影响

将Nd_(8.5)Fe_(77)Co_5Zr_3B_(6.5)(at%)合金熔化至不同温度后,以18 m/s的甩带速度快淬,对淬态条带进行了退火处理,分析了其微观结构和磁性能的变化。结果表明,熔体温度对淬态及其退火态合金的微观结构和磁性能可以产生重要影响,熔体温度为1210℃时制备的快淬条带由Nd_2Fe_(14)B相和部分非晶相组成,具有一定的硬磁性;随着快淬时熔体温度的升高,淬态条带中非晶相的质量分数逐渐增加,其磁性逐渐转变为软磁性。几种合金经退火处理后均由大量Nd_2Fe_(14)B相与少量软磁相组成,熔体温度较低的合金退火后其晶粒尺寸较小,磁性能较好。熔体温度为1210℃时制备的合金退火后磁性能最佳,内禀矫顽力Hci为559.2 kA/m,剩余磁化强度Br为0.98 T,最大磁能积(BH)_(max)为127.8 kJ/m~3。     

快淬速度对纳米晶复合Nd_(8.5)Dy_1Fe_(76)Co_5Zr_3B_(6.5)永磁材料磁性能和微观结构的影响

采用熔体快淬和随后的退火处理制备了Nd_(8.5)Dy_1Fe_(76)Co_5Zr_3B_(6.5)纳米晶复合永磁合金,研究了快淬速度对合金磁性能和微观结构的影响。随着快淬速度的增加,合金的磁性能呈现先升高再下降的趋势,当快淬速度为15 m/s时,合金有最佳的磁性能,B_r=0.70 T,H_(cj)=706.05 kA/m,(BH)_(max)=74.54 kJ/m~3。透射电镜的分析结果表明:合金的晶粒分布均匀,晶粒尺寸约为20 nm。三维原子探针的结果显示Zr元素在硬磁相Nd_2Fe_(14)B的晶界处富集,起到了抑制晶粒长大、细化晶粒的作用,从而提高了材料的磁性能。     

Dy元素对快淬(Nd, Pr)FeB合金的磁性能和晶化转变温度的影响

采用快淬法制备了镨基(Nd,Pr)10.5-xDyxFe83.5B6 (x=0,1,2)系列粘结磁体,测定了快淬条带晶化转变温度,研究了添加Dy元素对快淬合金条带晶化转变温度的影响。合金中添加Dy元素,快淬态条带晶化过程中非晶态向晶态转变的开始温度及结束温度提高,转变的温度区间增大。由于热稳定性的提高,条带晶化退火需要采用较高的温度。添加2%Dy元素的(Nd,Pr)8.5Dy2Fe83.5B6合金,最佳退火温度比 (Nd,Pr)9.5Dy1Fe83.5B6和(Nd,Pr)10.5Fe83.5B6分别提高了15和30 ℃。添加Dy元素的粘结磁体,内禀矫顽力Hcj增加,但剩磁Br下降,实验制备的(Nd,Pr)9.5Dy1Fe83.5B6合金磁体的磁性能为Br=0.638 T,Hcj=611 kA/m,(BH)m=71.6 kJ/m3     

Co和Zr元素对纳米晶复合NdFeB永磁合金晶化行为和磁性能的影响

利用熔体快淬法和晶化退火处理工艺制备纳米晶复合NdFeB永磁合金,研究添加Co和Zr元素对合金晶化行为、微结构和磁性能的影响.结果表明,添加Co元素降低了晶化相的析出温度,提高了合金的剩磁;进一步增加Zr元素后,合金的晶化行为由两步晶化变为软硬磁相同步析出,合金的矫顽力明显提高,晶粒得到细化,软、硬磁相之间的交换耦合作用显著增强,从而使合金Nd9.5Fe76Co5Zr3B6.5表现出优异的综合磁性能,即Jr=0.93 T,iHc=687 kA/m,(BH)max=129 kJ/m3.     

Influence of zirconium addition on the microstructure and magnetic properties of nanocomposite Nd10.1Fe78.2-xCo5ZrxB6.7 permanent magnets

Nanocomposite Nd10.1Fe78.2-xCo5ZrxB6.7 （x= 0, 1.5, 2.5, 2.7, 3, 4） permanent magnets were prepared by melt-spun and annealing. The microstructure and magnetic properties of the permanent magnets were investigated. The resuits reveal that the addition of Zr element significantly reduces the grain size and improves the thermal stability of the amorphous phase. A fme nanocomposite microstructure with an average grain size of about 35 nm can be developed at a wheel speed of 16 m·s^-1 with the content of Zr up to 2.7 at.%. After optimal annealing （710℃ x 4 min）, the magnetic properties of the Ndl0.1Fe75.5Co5Zr2.TB6.7 bonded magnets were achieved as follows： Br= 0.72 T, jHc = 769 kA·m^-1, and （BH）max = 85.0 kJ·m^-3.     

Magnetic properties and thermal stability of anisotropic bonded Nd-Fe-B magnets by warm compaction

Anisotropic bonded magnets were prepared by warm compaction using anisotropic Nd-Fe-B powder. The forming process, magnetic properties, and temperature stability were studied. The results indicate that the optimal temperature of the process, which was decided by the viscosity of the binders, was 110℃. With increasing pressure, the density of the magnets increased. When the pressure was above 700 MPa, the powder particles were destroyed and the magnetic properties decreased. The magnetic properties of the anisotropic bonded magnets were as follows: remanence Br = 0.98 T, intrinsic coercivity iHc=1361 kA/m, and maximum energy product BHmax = 166 kJ/m3. The magnets had excellent thermal stability because of the high coercivity and good squareness of demagnetization curves. The flux density of the magnets was 35% higher than that of isotropic bonded Nd-Fe-B magnets at 120℃ for 1000 h. The flux density of the bonded magnets showed little change with regard to temperature.     

添加元素对稀土粘结磁体退磁曲线方形度的影响

采用快淬法制备镨基(Nd,Pr)10.5(Fe,Co)83.5-xMxB6(M=Zr,Nb,Ti)系列粘结磁体,研究添加Zr、Nb和Ti等元素对快淬合金显微结构和磁性能的影响.(Nd,Pr)10.5(Fe,Co)83.5B6合金中适量添加Zr、Nb和Ti元素能有效细化合金晶粒,获得细小、均匀的晶粒,平均晶粒尺寸为50～70 nm.添加Zr、Nb和Ti元素的粘结磁体,由于晶粒细化和非磁性相对磁畴畴壁钉扎的共同作用,Hk/Hcj值大幅度增加,退磁曲线方形度得到明显改善,磁性能也显著提高.在Zr、Nb和Ti3种元素中,Zr对细化晶粒和提高磁性能的效果最好.含1％Zr(原子分数)的(Nd,Pr)10.5(Fe,Co)82.5Zr1B6合金薄带晶粒细小、均匀,平均尺寸约为60 nm,其粘结磁体退磁曲线方形度最好,Hk/Hcj值达到了39.9％,剩磁Br为0.675 T,内禀矫顽力Hci为616 kA/m,最大磁能积(BH)m为77 kJ/m3.     

Fe含量对高温稀土永磁Sm(CobalFexCu0.1Zr0.03)7.5 (x=0.09～0.21)磁性能的影响

采用粉末冶金工艺制备了高温稀土永磁Sm(CobalFexCu0.1Zr0.03)7.5 (x=0.09～0.21),研究了Fe含量对磁体磁性能的影响.结果表明:随着Fe含量的增加,剩磁Br和最大磁能积(BH)max逐渐增加,在x=0.21时获得最大值,分别为0.96 T和176.7 kJ/m3;内禀矫顽力Hci先增加后降低,在x=0.15时获得峰值2276.6 kA/m.最佳工艺制备(x=0.15)的磁体温度稳定性良好,B-H退磁曲线在温度为500 ℃时保持为直线;内禀矫顽力温度系数β为-0.16%/℃,最高使用温度(OT)max达到533 ℃.     

Structure and magnetic properties ofhigh-performanced Sm2（Co, Fe, Cu, Zr）17 alloys

ＩＮＴＲＯＤＵＣＴＩＯＮＴｈｅｈｉｇｈＣｕｒｉｅｔｅｍｐｅｒａｔｕｒｅａｎｄｌｏｗｅｓｔｔｅｍｐｅｒａ ｔｕｒｅｃｏｅｆｆｉｃｉｅｎｔｏｆｔｈｅＳｍ2 Ｃｏ17ｐｅｒｍａｎｅｎｔｍａｇｎｅｔｓｍａｋｅｔｈｅｍｂｅｉｄｅａｌｃａｎｄｉｄａｔｅｓｆｏｒｈｉｇｈｔ     

添加Zr元素对纳米复相Nd10．5Fe78．4-xCo5ZrxB6．1粘结永磁体结构和磁性能的影响

采用快淬、热处理及模压成形工艺，制备了成分为Nd10．5Fe78．4-xCo5ZrxB6．1（x=0，1．0，1．5，2．0，2．5）的5种粘结永磁体。采用XRD,DTA，TEM等方法对合金的组织结构和晶化行为进行了研究。结果表明：Zr含量的增加可提高材料的非晶形成能力；当Zr添加到一定量时，形成高熔点的Fe2Zr相，产生细化晶粒的作用；添加Zr元素显著地提高了合金的矫顽力，改善了退磁曲线矩形度，从而提高了最大磁能积。Nd10．5Fe78．4-xCo5ZrxB6．1永磁体在x=2时获得最佳磁性能，Br=0．659T，Hcj=628kA／m，Hcb=419kA／m，（BH）m=73kJ／m^3。     

High-pressure sintering and magnetic properties of Fe86Zr11-xNbxB3 （x=5.5, 6） amorphous alloys

1 INTRODUCTION Fe-based nanocrystalline soft magnetic alloys become the focus in the world because of their ex- cellent soft magnetic properties and high saturation induction.In engineering applications , soft mag- netic alloys are usually used in bulk form with complex shape . However , nanocrystalline soft magnetic alloys in engineering applications are pre- pared through the crystallization of amorphous al- loy which is controlled by melt spinning, accord- ingly the shape and size of th…     

Nanocrystalline Nd2Fe14B／α—Fe permanent magnet

Nd8.5Fe75Co5Cu1Zr3Nb1B6.5bonded magnet was prepared by melt-spinning(vs=18m/s)and subsequent heat treatment(670℃，4min).Excellent magnetic properties of the bonded magnet were achieved:Br=0.68T,iHc=620.3kA/m,(BH)max=74kJ/m^3.The addition of Cu and Zr elements shows to be advantageous in improving an intrinsic coercivity and squareness of hysteresis loop,as well as energy product.In has a remarkable remanence enhancement and the isotropic saturation remanence ratio Mr/Ms is 0.83.     

Nd2Fe14B/Fe3B与铁氧体磁粉复合效应的研究

本文研究了添加铁氧体磁粉对Nd2Fe14B／Fe3B双相纳米复合磁体性能的影响。实验表明，铁氧体的加入可改善该粘结磁体的工作稳定性，提高机械强度，减少磁不可逆损失，同时还能有效地降低成本。另外，由于加入磁粉中的同种粘结剂含量不同，得到的粘结磁体性能差距很大。