Facile synthesis and electrochemical properties of Fe3O4 nanoparticles for Li ion battery anode

Nanostructured Fe₃O₄ nanoparticles were prepared by a simple sonication assisted co-precipitation method. Transmission electron microscopy, X-ray diffraction and BET surface area analysis confirmed the formation of ∼20 nm crystallites that constitute ∼200 nm nanoclusters. Galvanostatic charge-discharge cycling of the Fe₃O₄ nanoaprticles in half cell configuration with Li at 100 mA g⁻¹ current density exhibited specific reversible capacity of 1000 mAh g⁻¹. The cells showed stability at high current charge-discharge rates of 4000 mA g⁻¹ and very good capacity retention up to 200 cycles. After multiple high current cycling regimes, the cell always recovered to full reversible capacity of ∼1000 mAh g⁻¹ at 0.1 C rate.     

Hybrid supercapacitor with nano-TiP2O7 as intercalation electrode

Nano-size (≤100 nm) TiP₂O₇ is prepared by the urea assisted combustion synthesis, at 450 and 900 °C. The compound is characterized by powder X-ray diffraction, Rietveld refinement, high resolution transmission electron microscopy and surface area methods. Lithium cycling properties by way of galvanostatic cycling and cyclic voltammetry (CV) showed a reversible and stable capacity of 60 (±3) mAh g⁻¹ (0.5 mole of Li) up to 100 cycles, when cycled at 15 mA g⁻¹ between 2-3.4 V vs. Li. Non-aqueous hybrid supercapacitor, TiP₂O₇ (as anode) and activated carbon (AC) (as cathode) has been studied by galvanostatic cycling and CV in the range, 0-3 V at 31 mA g⁻¹ and exhibited a specific discharge capacitance of 29 (±1) F g⁻¹stable in the range, 100-500 cycles. The Ragone plot shows a deliverable maximum of 13 Wh kg⁻¹ and 371 W kg⁻¹ energy and power density, respectively.     

High power and high capacity cathode material LiNi0.5Mn0.5O2 for advanced lithium-ion batteries

Single-phase lithium nickel manganese oxide, LiNi_0.5Mn_0.5O₂, was successfully synthesized from a solid solution of Ni_1.5Mn_1.5O₄ that was prepared by means of the solid reaction between Mn(CH₃COO)₂·4H₂O and Ni(CH₃COO)₂·4H₂O. XRD pattern shows that the product is well crystallized with a high degree of Li–M (Ni, Mn) order in their respective layers, and no diffraction peak of Li₂MnO₃ can be detected. Electrochemical performance of as-prepared LiNi_0.5Mn_0.5O₂ was examined in the test battery by charge–discharge cycling with different rate, cyclic voltammetry (CV), and electrochemical impedance spectroscopy (EIS). The cycling behavior between 2.5 and 4.4 V at a current rate of 21.7 mA g⁻¹ shows a reversible capacity of about 190 mAh g⁻¹ with little capacity loss after 100 cycles. High-rate capability test shows that even at a rate of 6C, stable capacity about 120 mAh g⁻¹ is retained. Cyclic voltammetry (CV) profile shows that the cathode material has better electrochemical reversibility. EIS analysis indicates that the resistance of charge transfer (R_ct) is small in fully charged state at 4.4 V and fully discharged state at 2.5 V versus Li⁺/Li. The favorable electrochemical performance was primarily attributed to regular and stable crystal structure with little intra-layer disordering.     

High-rate performance of all-solid-state lithium secondary batteries using Li4Ti5O12 electrode

The all-solid-state Li–In/Li₄Ti₅O₁₂ cell using the 80Li₂S·20P₂S₅ (mol%) solid electrolyte was assembled to investigate rate performances. It was difficult to obtain the stable performance at the charge current density of 3.8 mA cm⁻² in the all-solid-state cell. In order to improve the rate performance, the pulverized Li₄Ti₅O₁₂ particles were applied to the all-solid-state cell, which retained the reversible capacity of about 90 mAh g⁻¹ at 3.8 mA cm⁻². The 70Li₂S·27P₂S₅·3P₂O₅ glass–ceramic, which exhibits the higher lithium ion conductivity than the 80Li₂S·20P₂S₅ solid electrolyte, was also used. The Li–In/70Li₂S·27P₂S₅·3P₂O₅ glass–ceramic/pulverized Li₄Ti₅O₁₂ cell was charged at a current density higher than 3.8 mA cm⁻² and showed the reversible capacity of about 30 mAh g⁻¹ even at 10 mA cm⁻² at room temperature.     

Preparation and electrochemical properties of Li[Ni1/3Co1/3Mn1−x/3Zrx/3]O2 cathode materials for Li-ion batteries

Layer-structured Zr doped Li[Ni_1/3Co_1/3Mn_1−x/3Zr_x/3]O₂ (0 ≤ x ≤ 0.05) were synthesized via slurry spray drying method. The powders were characterized by XRD, SEM and galvanostatic charge/discharge tests. The products remained single-phase within the range of 0 ≤ x ≤ 0.03. The charge and discharge cycling of the cells showed that Zr doping enhanced cycle life compared to the bare one, while did not cause the reduction of the discharge capacity of Li[Ni_1/3Co_1/3Mn_1/3]O₂. The unchanged peak shape in the differential capacity versus voltage curve suggested that the Zr had the effect to stabilize the structure during cycling. More interestingly, the rate capability was greatly improved. The sample with x = 0.01 presented a capacity of 160.2 mAh g⁻¹ at current density of 640 mA g⁻¹(4 C), corresponding to 92.4% of its capacity at 32 mA g⁻¹(0.2 C). The favorable performance of the doped sample could be attributed to its increased lattice parameter.     

Morphology and electrochemical performance of Li[Ni1/3Co1/3Mn1/3]O2 cathode material by a slurry spray drying method

The spherical Li[Ni_1/3Co_1/3Mn_1/3]O₂ powders with appropriate porosity, small particle size and good particle size distribution were successfully prepared by a slurry spray drying method. The Li[Ni_1/3Co_1/3Mn_1/3]O₂ powders were characterized by XRD, SEM, ICP, BET, EIS and galvanostatic charge/discharge testing. The material calcined at 950 °C had the best electrochemical performance. Its initial discharge capacity was 188.9 mAh g⁻¹ at the discharge rate of 0.2 C (32 mA g⁻¹), and retained 91.4% of the capacity on going from 0.2 to 4 C rate. From the EIS result, it was found that the favorable electrochemical performance of the Li[Ni_1/3Co_1/3Mn_1/3]O₂ cathode material was primarily attributed to the particular morphology formed by the spray drying process which was favorable for the charge transfer during the deintercalation and intercalation cycling.     

Synthesis and electrochemical performance of the high voltage cathode material Li[Li0.2Mn0.56Ni0.16Co0.08]O2 with improved rate capability

The high voltage layered Li[Li_0.2Mn_0.56Ni_0.16Co_0.08]O₂ cathode material, which is a solid solution between Li₂MnO₃ and LiMn_0.4Ni_0.4Co_0.2O₂, has been synthesized by co-precipitation method followed by high temperature annealing at 900 °C. XRD and SEM characterizations proved that the as prepared powder is constituted of small and homogenous particles (100-300 nm), which are seen to enhance the material rate capability. After the initial decay, no obvious capacity fading was observed when cycling the material at different rates. Steady-state reversible capacities of 220 mAh g⁻¹ at 0.2C, 190 mAh g⁻¹ at 1C, 155 mAh g⁻¹ at 5C and 110 mAh g⁻¹ at 20C were achieved in long-term cycle tests within the voltage cutoff limits of 2.5 and 4.8 V at 20 °C.     

Structural and electrochemical characterization of xLi[Li1/3Mn2/3]O2·(1 − x)Li[Ni1/3Mn1/3Co1/3]O2 (0 ≤ x ≤ 0.9) as cathode materials for lithium ion batteries

A series of cathode materials with molecular notation of xLi[Li_1/3Mn_2/3]O₂·(1 − x)Li[Ni_1/3Mn_1/3Co_1/3]O₂ (0 ≤ x ≤ 0.9) were synthesized by combination of co-precipitation and solid state calcination method. The prepared materials were characterized by X-ray diffraction (XRD) and X-ray photoelectron spectroscopy (XPS) techniques, and their electrochemical performances were investigated. The results showed that sample 0.6Li[Li_1/3Mn_2/3]O₂·0.4Li[Ni_1/3Mn_1/3Co_1/3]O₂ (x = 0.6) delivers the highest capacity and shows good capacity-retention, which delivers a capacity ∼250 mAh g⁻¹ between 2.0 and 4.8 V at 18 mA g⁻¹.     

Improvement of the high rate capability of hierarchical structured Li4Ti5O12 induced by the pseudocapacitive effect

Hierarchical structured Li₄Ti₅O₁₂, assembling from randomly oriented nanosheets with a thickness of about 10-16 nm, is fabricated by a facile hydrothermal route and following calcination. It is demonstrated that the as-prepared sample has good cycle stability and excellent high rate performance. In particular, the discharge capacity of 128 mAh g⁻¹ can be obtained at the high current density of 2000 mA g⁻¹, which is about 87% of that at the low current density of 200 mA g⁻¹ upon cycling, indicating that the as-prepared sample can endure great changes of various discharge current densities to retain a good stability. In addition, the pseudocapacitive effect based on the hierarchical structure, also contributes to the high rate capability of Li₄Ti₅O₁₂, which can be confirmed in cyclic voltammograms.     

A study on the electrochemical characteristics of LiFePO4 cathode for lithium polymer batteries by hydrothermal method

Phospho-olivine LiFePO₄ cathode materials were prepared by hydrothermal reaction at 150 °C. Carbon black was added to enhance the electrical conductivity of LiFePO₄. LiFePO₄-C powders (0, 3, 5 and 10 wt.%) were characterized by X-ray diffraction (XRD) and transmission electron microscope (TEM). LiFePO₄-C/solid polymer electrolyte (SPE)/Li cells were characterized electrochemically by charge/discharge experiments at a constant current density of 0.1 mA cm⁻² in a range between 2.5 and 4.3 V vs. Li/Li⁺, cyclic voltammetry (CV) and ac impedance spectroscopy. The results showed that initial discharge capacity of LiFePO₄ was 104 mAh g⁻¹. The discharge capacity of LiFePO₄-C/SPE/Li cell with 5 wt.% carbon black was 128 mAh g⁻¹ at the first cycle and 127 mAh g⁻¹ after 30 cycles, respectively. It was demonstrated that cycling performance of LiFePO₄-C/SPE/Li cells was better than that of LiFePO₄/SPE/Li cells.     

High-density spherical Li4Ti5O12/C anode material with good rate capability for lithium ion batteries

Li₄Ti₅O₁₂ is a very promising anode material for lithium secondary batteries. To improve the material's rate capability and pile density is considered as the important researching direction. One effective way is to prepare powders composed of spherical particles containing carbon black. A novel technique has been developed to prepare spherical Li₄Ti₅O₁₂/C composite. The spherical precursor containing carbon black is prepared via an “outer gel” method, using TiOCl₂, C and NH₃ as the raw material. Spherical Li₄Ti₅O₁₂/C powders are synthesized by sintering the mixture of spherical precursor and Li₂CO₃ in N₂. The investigation of TG/DSC, SEM, XRD, Brunauer–Emmett–Teller (BET) testing, laser particle size analysis, tap-density testing and the determination of the electrochemical properties show that the Li₄Ti₅O₁₂/C composite prepared by this method are spherical, has high tap-density and excellent rate capability. It is observed that the tap-density of spherical Li₄Ti₅O₁₂/C powders (the mass content of C is 4.8%) is as high as 1.71 g cm⁻³, which is remarkably higher than the non-spherical Li₄Ti₅O₁₂. Between 1.0 and 3.0 V versus Li, the initial discharge specific capacity of the sample is as high as 144.2 mAh g⁻¹, which is still 128.8 mAh g⁻¹ after 50 cycles at a current density of 1.6 mA cm⁻².     

Preparation and electrochemical properties of carbon-doped TiO2 nanotubes as an anode material for lithium-ion batteries

Carbon-doped TiO₂ nanotubes were synthesized through a sol–gel and subsequent hydrothermal process. Transmission electron microscopy and X-ray diffraction showed that the products are uniformly straight tubes with the diameter around 10 nm in anatase-type. The electrochemical performances of the nanotubes were tested by constant current discharge/charge, cyclic voltammetry, and electrochemical impedance spectroscopy. The initial discharge capacity reaches 291.7 mAh g⁻¹ with a coulombic efficiency of 91.7% at a current density of 70 mA g⁻¹. There is a distinct potential plateau near 1.75 and 1.89 V (versus Li⁺/Li) in the lithium intercalation and extraction processes, respectively, and the lithium insertion capacity is about 204 mAh g⁻¹ over the plateau of 1.75 V region in the first cycle. From the 2nd to the 30th cycles, the average reversible capacity loss is less than 1.73 mAh g⁻¹ per cycle. After 30 cycles, the reversible capacity still remains 211 mAh g⁻¹ with a coulombic efficiency larger than 99.7%, implying a perfect reversibility and cycling stability.     

Nanosized high voltage cathode material LiMg0.05Ni0.45Mn1.5O4: Structural,electrochemical and in situ investigation

In this study a modified solid state synthesis (auto-ignition method) is used to form nanosized spinel type material LiMg_0.05Ni_0.45Mn_1.5O₄. This material presents a high voltage plateau at 4.75 V vs. Li/Li⁺. Structural and electrochemical characterisations have been performed using a wide range of techniques (TEM, neutron diffraction, galvanostatic measurements, and impedance spectroscopy). Besides, in situ XAS has been performed to monitor the evolution of Ni and Mn oxidation state during Li intercalation. The material presents an ordered cubic spinel structure, good capacity retention upon cycling (131 mAh g⁻¹ at C/10 and 117 mAh g⁻¹ at 1C) and good electronic conductivity (10⁻⁶ S cm⁻¹ at RT). The simultaneous presence of Mn³⁺/Mn⁴⁺ in the structure has been investigated and explained by inclusion of disordered nanodomains in the structure.     

Basic molten salt process—A new route for synthesis of nanocrystalline Li4Ti5O12-TiO2 anode material for Li-ion batteries using eutectic mixture of LiNO3-LiOH-Li2O2

A nanocrystalline Li₄Ti₅O₁₂-TiO₂ duplex phase has been synthesized by a simple basic molten salt process (BMSP) using an eutectic mixture of LiNO₃-LiOH-Li₂O₂ at 400-500 °C. The microstructure and morphology of the Li₄Ti₅O₁₂-TiO₂ product are characterized by means of X-ray diffraction (XRD), field emission scanning electron microscopy (FE-SEM), and transmission electron microscopy (TEM). The sample prepared by heat-treating at 300 °C for 3 h (S-1) reveals dense agglomerates of ultra-fine nanocrystalline Li₄Ti₅O₁₂; with heat treatment at 400 °C for 3 h (S-2), there is a duplex crystallite size (fine < 10 nm, and coarse > 20 nm) of Li₄Ti₅O₁₂-TiO₂; at 500 °C for 3 h (S-3), a much coarser and less-dense distribution of lithium titanate (crystallite size ∼15-30 nm) is observed. According to the results of electrochemical testing, the S-2 sample shows initial discharge capacities of 193 mAh g⁻¹ at 0.2 C, 168 mAh g⁻¹ at 0.5 C, 146 mAh g⁻¹ at 1 C, 135 mAh g⁻¹ at 2 C, and 117 mAh g⁻¹ at 5 C. After 100 cycles, the discharge capacity is 138 mAh g⁻¹ at 1 C with a capacity retention of 95%. The S-2 sample yields the best electrochemical performance in terms of charge-discharge capacity and rate capability compared with other samples. Its superior electrochemical performance can be mainly attributed to the duplex crystallite structure, composed of fine (<10 nm) and coarse (>20) nm nanoparticles, where lithium ions can be stored within the grain boundary interfaces between the spinel Li₄Ti₅O₁₂ and the anatase TiO₂.     

Synthesis and electrochemical performance of doped LiCoO2 materials

Layered intercalation compounds LiM_0.02Co_0.98O₂ (M = Mo⁶⁺, V⁵⁺, Zr⁴⁺) have been prepared using a simple solid-state method. Morphological and structural characterization of the synthesized powders is reported along with their electrochemical performance when used as the active material in a lithium half-cell. Synchrotron X-ray diffraction patterns suggest a single phase HT-LiCoO₂ that is isostructural to α-NaFeO₂ cannot be formed by aliovalent doping with Mo, V, and Zr. Scanning electron images show that particles are well-crystallized with a size distribution in the range of 1–5 μm. Charge–discharge cycling of the cells indicated first cycle irreversible capacity loss in order of increasing magnitude was Zr (15 mAh g⁻¹), Mo (22 mAh g⁻¹), and V (45 mAh g⁻¹). Prolonged cycling the Mo-doped cell produced the best performance of all dopants with a stable reversible capacity of 120 mAh g⁻¹ after 30 cycles, but was inferior to that of pure LiCoO₂.     

Cathode performance of olivine-type LiFePO4 synthesized by chemical lithiation

Chemical lithiation with LiI in acetonitrile was performed for amorphous FePO₄ synthesized from an equimolar aqueous suspension of iron powder and an aqueous solution of P₂O₅. An orthorhombic LiFePO₄ olivine structure was obtained by annealing a chemically lithiated sample at 550 °C for 5 h in Ar atmosphere. The average particle size remained at approximately 250 nm even after annealing. The lithium content in the sample was quantitatively confirmed by Li atomic absorption analysis and ⁵⁷Fe Mössbauer spectroscopy. While an amorphous FePO₄/carbon composite cathode has a monotonously decreasing charge–discharge profile with a reversible capacity of more than 140 mAh g⁻¹, the crystallized LiFePO₄/carbon composite shows a 3.4 V plateau corresponding to a two-phase reaction. This means that the lithium in the chemically lithiated sample is electrochemically active. Both amorphous FePO₄ and the chemically lithiated and annealed crystalline LiFePO₄ cathode materials showed good cyclability (more than 140 mAh g⁻¹ at the 40th cycle) and good discharge rate capability (more than 100 mAh g⁻¹ at 5.0 mA cm⁻²). In addition, the fast-charge performance was found to be comparable to that with LiCoO₂.     

Electrochemical performance of VOMoO4 as negative electrode material for Li ion batteries

Polycrystalline samples of VOMoO₄ are prepared by a solid-state reaction method and their electrochemical properties are examined in the voltage window 0.005–3 V versus lithium. The reaction mechanism of a VOMoO₄ electrode for Li insertion/extraction is followed by ex situ X-ray diffraction analysis. During initial discharge, a large capacity (1280 mAh g⁻¹) is observed and corresponds to the reaction of ∼10.3 Li. The ex situ XRD patterns indicate the formation of the crystalline phase Li₄MoO₅ during the initial stages of discharge, which transforms irreversibly to amorphous phases on further discharge to 0.005 V. On cycling, the reversible capacity is due to the extraction/insertion of lithium from the amorphous phases. A discharge capacity of 320 mAh g⁻¹ is obtained after 80 cycles when cycling is performed at a current density of 120 mA g⁻¹.     

Synthesis and characterization of submicron-sized LiNi1/3Co1/3Mn1/3O2 by a simple self-propagating solid-state metathesis method

Submicron-sized LiNi_1/3Co_1/3Mn_1/3O₂ cathode materials were synthesized using a simple self-propagating solid-state metathesis method with the help of ball milling and the following calcination. A mixture of Li(ac)·2H₂O, Ni(ac)₂·4H₂O, Co(ac)₂·4H₂O, Mn(ac)₂·4H₂O (ac = acetate) and excess H₂C₂O₄·2H₂O was used as starting material without any solvent. XRD analyses indicate that the LiNi_1/3Co_1/3Mn_1/3O₂ materials were formed with typical hexagonal structure. The FESEM images show that the primary particle size of the LiNi_1/3Co_1/3Mn_1/3O₂ materials gradually increases from about 100 nm at 700 °C to 200–500 nm at 950 °C with increasing calcination temperature. Among the synthesized materials, the LiNi_1/3Co_1/3Mn_1/3O₂ material calcined at 900 °C exhibits excellent electrochemical performance. The steady discharge capacities of the material cycled at 1 C (160 mA g⁻¹) rate are at about 140 mAh g⁻¹ after 100 cycles in the voltage range 3–4.5 V (versus Li⁺/Li) and the capacity retention is about 87% at the 350th cycle.     

Electrochemical studies on LiCoO2 surface coated with Y3Al5O12 for lithium-ion cells

Synthesized yttrium aluminum garnet (YAG) sol was coated on the surface of the LiCoO₂ cathode particles by an in situ sol–gel process, followed by calcination at 923 K for 10 h in air. Based on XRD, TEM, and ESCA data, a compact YAG kernel with an average thickness of ∼20 nm was formed on the surface of the core LiCoO₂ particles, which ranged from ∼90 to 120 nm in size. The charge–discharge cycling studies for the coated materials suggest that 0.3 wt.% YAG-coated LiCoO₂ heated at 923 K for 10 h in air, delivered a discharge capacity of 167 mAh g⁻¹ and a cycle stability of about 164 cycles with a fading rate of 0.2 mAh cycle⁻¹ at a 0.2C-rate between 2.75 and 4.40 V vs. Li/Li⁺. The differential capacity plots revealed that impedance growth was slower for YAG surface treated LiCoO₂, when cells were charged at 4.40 V. DSC results exemplified that the exothermic peak at ∼468 K corresponded to the release of much less oxygen and greater thermal-stability.     

Synthesis and electrochemical properties of Li1−xFe0.8Ni0.2O2–LixMnO2 (Mn/(Fe + Ni + Mn) = 0.8) material

A new type of Li_1−xFe_0.8Ni_0.2O₂–Li_xMnO₂ (Mn/(Fe + Ni + Mn) = 0.8) material was synthesized at 350 °C in air atmosphere using a solid-state reaction. The material had an XRD pattern that closely resembled that of the original Li_1−xFeO₂–Li_xMnO₂ (Mn/(Fe + Mn) = 0.8) with much reduced impurity peaks. The Li/Li_1−xFe_0.8Ni_0.2O₂–Li_xMnO₂ cell showed a high initial discharge capacity above 192 mAh g⁻¹, which was higher than that of the parent Li/Li_1−xFeO₂–Li_xMnO₂ (186 mAh g⁻¹). We expected that the increase of initial discharge capacity and the change of shape of discharge curve for the Li/Li_1−xFe_0.8Ni_0.2O₂–Li_xMnO₂ cell is the result from the redox reaction from Ni²⁺ to Ni³⁺ during charge/discharge process. This cell exhibited not only a typical voltage plateau in the 2.8 V region, but also an excellent cycle retention rate (96%) up to 45 cycles.