高温回火对20Cr2Ni4A钢渗碳层中残留奥氏体的影响

减少20Cr2Ni4A钢渗碳后残留奥氏体的途径主要有高温回火和深冷处理.研究不同高温回火工艺对20Cr2Ni4A渗碳层中残留奥氏体转变的影响,尤其是高温回火时间的影响.结果表明:采取第一次回火温度高和第二次回火时间长的工艺后进行淬火,表面硬度超过62 HRC,渗层组织为细密的隐针马氏体+均匀的碳化物+较少的残留奥氏体,保证产品渗碳淬火后表面硬度满足了生产需要.     

18Cr2Ni4WA钢真空渗碳后热处理工艺的优化

制定了两种不同的热处理工艺,研究18Cr2Ni4WA钢真空渗碳后回火、淬火和深冷工艺对材料组织和性能的影响。结果表明,18Cr2Ni4WA钢渗碳后,经高温回火、淬火、深冷和低温回火处理后,渗碳层深度几乎不受影响,表面残留奥氏体含量显著降低。经680 ℃×5 h两次高温回火+860 ℃淬火+－115.3 ℃深冷+160 ℃低温回火工艺处理后,试样表面硬度为64.2 HRC,渗碳层深度为0.86 mm;并得到由针状回火马氏体、少量残留奥氏体和弥散分布的点状碳化物组成的渗碳层组织和由低碳板条状回火马氏体组成的心部组织,不仅使得表面获得高硬度,同时保证了心部的强韧性。     

提高20Cr2Ni4A钢齿轮渗碳淬火硬度的试验研究

针对20Cr2Ni4A钢制造的中大型齿轮在不允许冷处理的条件下渗碳淬火硬度偏低的问题,通过对渗碳淬火碳势、中间高温回火工艺、淬火温度的优化,在不冷处理的情况下使齿轮硬度提高了2 HRC以上至58~61 HRC,显微组织良好,达到了预期目的。试验发现,该材料渗碳后经过高温回火再重新加热淬火时,为了提高表面及次表面硬度,渗碳扩散碳势、渗碳降温保温阶段碳势和淬火碳势在碳化物不超标的前提下要尽量提高;反复试验与检测证明,中间高温回火也会导致渗碳层一定深度内碳含量的降低,从而影响渗碳淬火硬度,故高温回火时不仅要注意回火不足更要防止过回火,高温回火次数过多时间过长,淬火后硬度不升反降。     

20Cr2Ni4A齿轮钢高温渗碳工艺研究

对20Cr2Ni4A齿轮钢的高温渗碳工艺进行了研究,并对其显微组织、硬度梯度、晶粒度等指标进行了测试。结果表明,20Cr2Ni4A齿轮钢在高温渗碳后油淬及高温回火后的显微组织为回火马氏体加少量残留奥氏体,并在渗层表面弥散分布有碳化物颗粒,渗层表面硬度达58~62 HRC。高温渗碳后奥氏体晶粒度可达到8级,显著提高了渗碳效率。     

20Cr2Ni4A齿轮钢高温渗碳工艺

对20Cr2Ni4A齿轮钢的高温渗碳工艺进行了研究,并对其显微组织、硬度梯度、晶粒度等指标进行了测试。结果表明20Cr2Ni4A齿轮钢在高温渗碳后油淬及高温回火后的显微组织为回火马氏体加少量残留奥氏体,并在渗层表面弥散分布有碳化物颗粒,渗层表面硬度达58~62 HRC。高温渗碳后奥氏体晶粒度可达到8级,显著提高了渗碳效率。     

深冷处理对18Cr2Ni4WA渗碳淬火组织和性能的影响

对18Cr2Ni4WA钢进行了淬火和深冷处理试验,研究了不同淬火温度和深冷处理对渗碳后钢的组织和性能的影响。研究表明,18Cr2Ni4WA钢经深层渗碳淬火后,并进一步进行深冷处理,可降低渗碳淬火组织中的残余奥氏体占比,提高渗碳层表面的硬度,渗碳层中过共析层硬度平缓提高,而渗碳有效硬化层深度无明显增加,对渗碳层中原始碳化物大小和形态无明显影响。     

深冷处理对18Cr2Ni2MoNbA钢耐磨性的影响

使用正交试验对18Cr2Ni2MoNbA钢渗碳钢深冷处理工艺参数进行筛选优化,分析深冷处理时间、低温回火温度和时间对试样耐磨性的影响,并对试样磨痕形貌、显微组织、残留奥氏体以及显微硬度进行分析。研究表明,18Cr2Ni2MoNbA钢渗碳淬火后的-196 ℃深冷工艺参数对磨损量影响的显著性排序为:深冷处理时间＞低温回火时间＞低温回火温度。深冷处理能够有效增加试样的耐磨性,在深冷温度-196 ℃,深冷处理时间1 h,低温回火温度120 ℃,低温回火时间2 h的工艺下试样磨损量最小,与未深冷时相比减少46.67%,磨损机制变为磨粒磨损与氧化磨损。经过深冷处理后渗碳层的碳化物沿晶界析出,同时有小颗粒碳化物在基体上弥散析出。深冷处理能够降低钢的残留奥氏体含量,增加马氏体含量,使表层渗碳层的显微硬度增加,从而改善18Cr2Ni2MoNbA钢的耐磨性。     

18Cr2Ni4WA渗碳钢的热处理工艺研究

介绍了18Cr2Ni4WA钢渗碳时的碳势控制、渗碳后的高温回火和淬火工艺。该钢渗碳后于670℃回火两次是消除渗碳层中残余奥氏体的最有效方法。渗碳采用不同温度淬火可满足18Cr2Ni4WA钢零件不同的心部硬度要求。     

冷处理对0Cr16Ni5Mo马氏体不锈钢组织和性能的影响

通过对0Cr16Ni5Mo钢进行淬火+回火及淬火+冷处理+回火工艺的热处理,研究了冷处理对0Cr16Ni5Mo马氏体不锈钢组织和性能的影响。结果表明,0Cr16Ni5Mo钢经调质处理后具有良好的综合性能;其显微组织得到了改善,板条马氏体束发生碎化,位错缠结增加,且残留奥氏体组织转变彻底,其强度得到提高。冷处理后钢的性能改善与残留奥氏体转变及晶粒碎化有关。     

35Cr3SiMnMoV钢超饱和渗碳研究

对自行研发的35Cr3SiMnMoV渗碳钢进行超饱和渗碳,并对渗层的组织、硬度及耐磨性能进行了研究。结果表明:试验钢经超饱和渗碳、淬火加低温回火后,超饱和渗碳层由回火马氏体、残留奥氏体和大量弥散分布的碳化物构成,硬度可达1025HV0.1,其耐磨性比20CrMnMo、20Cr2Ni4钢常规渗碳层提高了约60%。     

航空轴承钢M50NiL真空低压渗碳热处理工艺研究

为探究渗碳全流程工艺对航空轴承用钢M50NiL渗层组织性能的影响规律,对M50NiL钢开展了真空低压渗碳热处理研究,分析了渗碳、淬火、冷处理和回火等工艺对渗层的组织演变及其对应硬度梯度分布的影响。结果表明,经渗碳淬火后,实验钢有效渗层深度为1.25 mm,随着碳浓度的降低,从渗层表面到芯部碳化物的体积分数和析出尺寸逐渐减小,显微硬度呈现逐渐下降趋势。冷处理工艺促使部分残余奥氏体组织转变为马氏体组织,进一步提高渗层整体硬度。经回火处理后,表面硬度有所降低。实验钢表面碳化物主要为Cr、V、Mo、Ni的碳化物。     

Experimental Study on Vacuum Carburizing Process for Low-Carbon Alloy Steel

As a low-carbon alloy steel, 20Cr2Ni4A steel has an excellent mechanical properties. It has been used for producing heavy-duty gears, which require good wear and fatigue resistance. The vacuum carburizing process can improve the quality of gears and extend the service life. In this article, a complete heat-treatment process for 20Cr2Ni4A, with carburizing, tempering, quenching and cryogenic steps involved, was proposed. A numerical method was employed to design the carburizing step. The carburized samples were characterized by analysis of carbon profile, surface-retained austenite content, microstructure, and hardness profile. A good microstructure was obtained with acicular-tempered martensite, less-retained austenite, fine granular-dispersed carbides, and was oxide free. The final surface hardness was 64.2HRC, and the case depth was 0.86 mm, which meet the requirements of products. The relationships among process, performance, and microstructure were investigated to understand the inner connection.     

复合化学热处理对G13Cr4Mo4Ni4V钢组织和硬度的影响

采用扫描电镜、洛氏硬度计和维氏显微硬度计研究了渗氮140 h对渗碳+淬火+回火G13Cr4Mo4Ni4V钢微观组织及硬度的影响。结果表明,渗碳+淬火+回火后G13Cr4Mo4Ni4V钢有效渗碳层深度为1.45 mm,渗碳层最高硬度为785 HV,心部硬度为420 HV,经渗氮处理后有效渗碳+渗氮层深度降为1.34 mm,渗氮层深度为0.22 mm,渗氮层最高硬度可达到948 HV,心部硬度为451 HV,较未渗氮试样硬度略有提高。渗碳+淬火+回火和添加渗氮处理后G13Cr4Mo4Ni4V钢的表面洛氏硬度相当,均在62~65 HRC 之间,但渗氮处理后试样的硬度波动性较大。添加140 h渗氮的渗碳+淬火+回火后G13Cr4Mo4Ni4V钢实现了“表面硬心部韧”的目标,渗氮层深度满足工程需要,但添加渗氮处理后G13Cr4Mo4Ni4V钢在渗碳层和渗氮层出现类网状碳化物,因此在渗氮过程中需要综合考虑渗氮层深度和微观组织,以获得良好的综合力学性能。     

扩散时间对20MnCrS5齿轮钢真空渗碳的影响

采用真空低压渗碳高压气淬工艺对20MnCrS5齿轮钢进行表面真空渗碳处理,分析扩散时间对硬度梯度、渗层深度、显微组织以及碳含量分布的影响,并优化真空渗碳工艺。结果表明,随着扩散时间的延长,C原子由表层向基体发生扩散,当扩散时间超过100 min后,C原子的扩散速度减缓;当C含量超过1.0%后,淬火后容易形成尺寸较大的残留奥氏体,随着C含量的降低,显微组织由孪晶马氏体向位错马氏体转变,硬度下降;在本试验条件下,20MnCrS5钢合适的真空低压渗碳高压气淬工艺为930 ℃强渗42 min,扩散140 min,0.6 MPa高压气淬至室温,并在160 ℃低温回火2 h。经该工艺处理后,组织中碳化物等级为1级,残留奥氏体等级为2级,马氏体等级为3级,表层无内氧化,渗碳层厚度约为0.91 mm,符合技术要求。     

稀土低温高浓度气体渗碳工艺及其在20Cr2Ni4A钢上的应用

２０Ｃｒ２Ｎｉ４Ａ钢由于渗碳层奥氏体十分稳定，无法渗碳后直接淬火，而需经过复杂的热处理，本文采用稀土低温高浓度大气体渗碳，使渗层过共析区沉淀析出大量细小弥散的碳化物，奥氏体的稳定性大幅度下降，实现了渗后直接淬火，同时使组织和性能得到进一步改善。     

淬火后清洗和冷处理工艺对9Cr18钢轴承套圈残留奥氏体含量的影响

分析了9Cr18钢轴承套圈在相同淬、回火工艺条件下,油淬后清洗工艺、冷处理工艺以及清洗-冷处理间隔时间对产品最终残留奥氏体含量的影响。结果表明,油淬后清洗温度越高,清洗-冷处理间隔时间越长,则残留奥氏体含量越高。过低的冷处理温度对残留奥氏体的降低起相反作用,推荐冷处理温度－70～－80 ℃。     

铬镍渗碳钢的残余奥氏体

20CrZNi4、18CrZNi4W钢往往经诊碳（或碳氢共修）淬火后使用,由于合金元素Ni、Cr量较高,热处理后工件表面存在大量的残余奥氏体。残余奥氏体对性能的影响,其量多少为宜,是一个比较复杂而值得注意的问题。本文讨论了诊碳层不同的合碳量、渗碳后高温回火、淬火工艺、冷处理及喷九处理等对残余奥氏体量的影响,从而针对所要求的残余奥氏体量来选择合适的表面含碳量、相应的热处理方法及不同的工艺参数。     

16MnCr5钢大马力柴油机凸轮轴渗碳淬火组织演变

通过光学显微镜、扫描电镜、XRD测试、硬度梯度测试等研究16MnCr5低碳合金钢凸轮轴渗碳淬火+低温回火后沿径向的显微组织和硬度。结果表明,940 ℃强渗适用于16MnCr5钢凸轮轴,显微组织沿凸轮轴径向变化明显,渗碳层表面组织为高碳的针状马氏体和10%左右的残留奥氏体,表层硬度可达750 HV,有效硬化层深度可达1.5 mm以上,基体组织为贝氏体和低碳马氏体的混合组织。