CoMo/SBA-15-γ-Al2O3催化剂的加氢脱硫活性研究

采用介孔分子筛SBA-15和γ-Al2O3制备混合载体SBA-15-γ-Al2O3,担载Co-Mo金属活性组分制备深度加氢脱硫催化剂CoMo/SBA-15-γ-Al2O3。BET表征结果表明,混合载体负载金属后仍然具有介孔材料的特性,表面积略有下降。以直馏柴油为原料,在固定床微型反应器上评价了该催化剂的加氢脱硫反应活性。结果表明,在催化剂CoO和MoO3的质量分数分别为5％和20％、反应温度360 ℃、反应压力6 MPa、氢油体积比600、体积空速2 h-1的条件下,柴油硫含量可由829 μg/g降至6 μg/g。     

磷预处理对γ-Al_2O_3及其负载Ni_2P催化剂加氢脱硫性能影响

以磷酸二氢铵为磷源对γ-Al2O3进行磷预处理,得到了不同磷质量分数(0~7.2%)的改性γ-Al2O3,以其为载体采用等体积浸渍法和H2原位还原法制备了负载型Ni2P催化剂。以噻吩为模型化合物在固定床反应器上对催化剂的加氢脱硫(HDS)性能进行评价,并运用X射线衍射(XRD)、N2吸附/脱附、氨程序升温脱附(NH3-TPD)等技术对改性载体及催化剂进行表征。结果表明:对γ-Al2O3进行磷预处理可以提高其比表面积,并可以对其孔径分布进行一定的调节;同时,磷的加入可以调变γ-Al2O3的酸强度分布及总酸量。采用适量磷改性的γ-Al2O3为载体制备催化剂有利于生成纯相的Ni2P。当载体中的磷质量分数达到3.6%时,γ-Al2O3的总酸量及中强酸量较高,比表面积较大,以其为载体制备的负载型Ni2P催化剂具有更高的加氢脱硫性能。     

载体织构对Ni-Fe/γ-Al2O3催化剂结构和甲烷化活性的影响

采用等体积浸渍法制备了4种不同γ-Al2O3为载体的负载型Ni-Fe/γ-Al2O3催化剂,通过BET、XRD和H2-TPR等表征手段对载体和催化剂进行了表面微观结构分析,并考察了其低温浆态床催化CO甲烷化反应的活性和稳定性。结果表明,载体γ-Al2O3的表面织构性质对Ni-Fe/γ-Al2O3催化剂活性物质Ni的分布和甲烷化活性影响较大。比表面积和平均孔径分别为192m2/g和5.8nm的γ-Al2O3载体具有较好的低温浆态床CO甲烷化活性,有利于活性组分的分散,且与γ-Al2O3表面作用较强的β-NiO含量较多,还原后活性物质Ni晶粒较小,形成的活性中心数量多,甲烷化活性及稳定性较好,CO的平均转化率和CH4平均选择性分别达到97.0%和89.0%。而以比表面积较大的高硅γ-Al2O3载体制备的催化剂,游离态α-NiO含量较多,还原过程中容易迁移和团聚,形成较大的Ni晶粒,催化剂的活性和稳定性均差,CO的初始转化率为85.5%,反应17h后活性急剧下降。     

γ-Al2O3载体的固相法合成及Ni-Mo-P/γ-Al2O3催化剂的加氢脱硫性能

以硝酸铝和碳酸氢铵为原料,采用固相反应法,在低温条件下制备出γ-Al2O3的前驱体碳酸铝铵(AACH),然后挤条、焙烧,成功制备出高比表面积和大孔体积的γ-Al2O3载体。考察了原料配比、陈化温度等参数对碳酸铝铵合成的影响。采用X射线衍射、BET物理吸附、扫描电子显微镜、固体核磁共振、高分辨透射电镜等手段对AACH和γ-Al2O3载体进行了表征。以柴油中较难脱除的二苯并噻吩(DBT)为模型化合物,在高压微反装置上评价了由上述γ-Al2O3载体制备的Ni-Mo-P/γ-Al2O3催化剂的加氢脱硫活性。结果表明,最佳原料配比下,较高的陈化温度和添加PEG有利于得到结晶度较好的纯相碳酸铝铵;以其焙烧后的γ-Al2O3为载体的Ni-Mo-P/γ-Al2O3催化剂的加氢脱硫活性明显高于以传统γ-Al2O3作载体制备的催化剂。     

FF-34新型蜡油加氢处理催化剂的开发及工业应用

为适应蜡油原料重质化、劣质化发展趋势,延长装置运转周期,采用具有粒子尺寸大且粒径分布集中、相对结晶度高的特种氧化铝载体材料及Ⅱ类活性相调节技术,开发了具有较大孔径和孔体积、更高抗金属和容金属能力的FF-34蜡油加氢处理催化剂。工业应用结果表明:在入口压力10.0 MPa、体积空速高达1.00 h-1、氢油体积比558、入口反应温度仅334℃条件下,精制蜡油硫质量分数约3000μg/g,氮质量分数为1321μg/g,化学氢耗为0.73%,说明了FF-34催化剂具有良好的加氢脱硫和加氢脱氮性能。     

载体焙烧温度对MoNiP/γ-Al_2O_3加氢催化剂活性的影响

采用不同焙烧温度制备了一系列γ-Al2O3载体,并利用等体积浸渍法制备相应的MoNiP/γ-Al2O3催化剂,借助N2物理吸附-脱附和XRD等方法对载体和催化剂进行表征,同时以甲苯、噻吩和喹啉为模型化合物,在微反装置上评价催化剂的芳烃加氢、加氢脱硫(HDS)和加氢脱氮(HDN)的活性。表征结果显示,随焙烧温度的升高,γ-Al2O3载体及其催化剂的孔体积变化不大,但平均孔径增大,比表面积降低。实验结果表明,适宜的焙烧温度为600℃,利用该温度焙烧的载体制得的MoNiP/γ-Al2O3催化剂表面的中强酸和强酸的含量较高,且芳烃加氢、HDS和HDN的活性最高。     

Co-Mo/meso-Al_2O_3蜡油加氢处理催化剂的制备

以Pluronic P123作结构导向剂,通过酸碱中和法制备氧化铝作载体,分别采用共浸渍法及分步浸渍法制备Co-Mo型蜡油加氢处理催化剂,其中MoO3的负载量为20.0%(w),CoO的负载量为7.81%(w)。样品的表征分析结果表明:与商用氧化铝相比,自制氧化铝具有部分有序的介孔结构、较高的比表面积及孔体积、较大的孔径及较高的结晶度;与分步浸渍法相比,共浸渍法制备的催化剂具有更大的比表面积以及更多的酸性位,且这两种催化剂中的活性组分都均匀地分散在载体上。在实验室固定床微反上对催化剂进行加氢处理性能评价,结果表明,以自制氧化铝为载体、采用共浸渍法制备的催化剂具有良好的加氢脱硫及脱氮活性。在反应温度380℃、反应压力15 MPa、体积空速0.6h-1、氢油体积比1 000∶1的条件下,催化剂的加氢脱硫率可达到99.75%,加氢脱氮率为99.86%,产品中的硫质量分数为9.4μg/g,氮质量分数为1.1μg/g,满足后续工艺的要求。     

多级孔TiO2/γ-Al2O3复合载体的制备及表征

以碳酸氢铵为沉淀剂,廉价的硫酸铝、硫酸钛为原料,采用液相共沉淀法制备了不同TiO2质量分数(0~15%)的TiO2/γ-Al2O3复合载体。运用X射线衍射(XRD)、N2吸附-脱附(BET)、电子显微镜扫描(SEM)方法对所制得的复合载体进行了表征。结果显示,当TiO2/γ-Al2O3复合载体中TiO2的质量分数逐渐增大到15%时,其中的TiO2由无定型高度分散态转变为锐钛矿晶型开始在γ-Al2O3上富集,复合载体中γ-Al2O3的存在提高了TiO2的热稳定性;采用此方法制得的TiO2/γ-Al2O3复合载体比表面积较高,具有介孔(2~50nm)-大孔(>50nm)双孔分布的多级孔结构,最可几孔径在7~11nm之间;TiO2/γ-Al2O3复合载体二次粒子形貌为短粗纤维状。     

流化催化裂化柴油和豆油耦合加氢生产高十六烷值清洁柴油

在高压固定床微反装置上研究了豆油在加氢催化剂CoMo/γ-Al2O3,NiMoP/γ-Al2O3,NiMoP/γ-Al2O3-HUSY上的加氢反应规律,并研究了NiMoP/γ-Al2O3-HUSY催化剂对豆油和流化催化裂化(FCC)柴油耦合加氢产物性质的影响。实验结果表明,在压力3.0MPa、温度320℃、液态空速2.0h-1、氢气与原料油体积比(氢油比)500的条件下,CoMo/γ-Al2O3和NiMoP/γ-Al2O3催化剂上豆油加氢产物主要为n-C15~18,而添加酸性组分的NiMoP/γ-Al2O3-HUSY催化剂的裂化性能增强,产物中n-C15~18含量明显减少,C1-5的含量增加;在压力4.0MPa、温度370℃、液态空速1.0h-1、氢油比500的条件下,豆油和FCC柴油的混合原料在NiMoP/γ-Al2O3-HUSY催化剂上的加氢脱硫率达97%左右,加氢脱氮率达80%以上,产物的十六烷值与未掺炼豆油的FCC柴油加氢产物相比,提高了1.8~6.5个单位。     

TiO2-Al2O3复合载体的比较

采用沉淀法、共沉淀法、溶胶凝胶法(W)和溶胶-凝胶法(E)制备TiO2-Al2O3复合载体,并采用XRD、BET和TEM等方法进行表征。结果表明,沉淀法、溶胶凝胶法(W)和溶胶-凝胶法(E)制成的复合载体基本保留了最初引入的γ-Al2O3的孔特征,具有较大的比表面积、孔体积和孔径,TiO2以锐钛矿晶型存在,且主要以表面富集的形式分散在γ-Al2O3表面;而共沉淀法制成的复合载体比表面积、孔体积和孔径最小,孔径分布更加集中,TiO2在整个体相均匀分散。     

超声波辐照浸渍法制备MnO2/γ-A12O3催化剂及其柴油催化氧化脱硫性能

 分别采用超声波辐照浸渍法和普通浸渍法制备了MnO₂/γ-Al₂O₃催化剂,运用电感耦合等离子体原子发射光谱（ICP-AES）和X射线衍射（XRD）对催化剂进行表征,在空气-异丁醛-MnO₂/γ-Al₂O₃体系中评价其对加氢柴油的氧化脱硫催化性能,并考察了反应温度、异丁醛用量、空气流量、溶剂类型和剂/油体积比对柴油氧化脱硫反应的影响。结果表明,超声波辐照浸渍法制备的MnO₂/γ-Al₂O₃催化剂对柴油氧化脱硫的催化性能明显优于普通浸渍法制备的催化剂。最适宜的催化柴油氧化脱硫反应的条件为：乙腈为溶剂、加氢柴油30 mL、温度35℃、异丁醛20 mmol、空气流量0.06 L/min、超声波辐照浸渍法制备的MnO₂/γ-Al₂O₃催化剂0.08 g、剂/油体积比1/6和催化氧化时间10 min。在此条件下可将柴油硫质量分数从542μg/g 降至31μg/g,柴油脱硫率和回收率分别为94.3%和93.3%。     

Analysis for surface coke deposition in used Mo-Co/γ-Al2O3 catalyst for diesel hydrodesulfurization

The coked Mo-Co/γ-Al₂O₃ catalysts were Soxhlet extracted with the solvent of tetrahydrofuran. Experimental techniques like FT-IR, GC-MS, XPS, H₂-TPR, BET, etc. were applied for the characterization of coke and catalysts to make a comparison of their physical properties. The results showed that the active components of the catalyst were slightly less after the reaction. The specific surface area and the pore volume had recovered to some degree. These results indicated that the main cause of deactivation of Mo-Co/γ-Al₂O₃ catalysts is carbon deposit. The principal components of the soluble carbon deposit on Mo-Co/γ-Al₂O₃ catalysts were alkyl aromatics with 1–4 rings and C₁₉–C₂₉ long-chain alkane compounds.     

Production of Lubricating Base Oil Using a Moist SiO2/γ-Al2 O3 Catalyst

Abstract

The catalyst SiO₂/γ-Al₂ O₃ treated by micro-wetness air to produce lubricating base oil was studied in this article. The satisfactory reaction temperature, the treatment temperature, and the proper content of active composition was researched. Under the best reaction conditions with a reaction temperature of 170°C, a reaction pressure at 6.0 Mpa, the volume velocity at 0.5 h^?1. The polymerization of α-olefin was performed at a microreactor and produced lubricating base oil with the kinetic viscosity at 38.19 mm² · s^?1, the bromine number at 5.78 g(Br) · (100 g)^?1, and the pour point at ?43.0°C. Then the structure of the catalyst was determined by Brunauer, Emmett and Teller (BET) technology. The result shows that when the optimal micro-wetness air was 45°C, the reaction temperature was 800°C, and the amount of active composition was 12%, and the catalyst has high catalytic activity and wide market prospect.     

预处理方法对Mo-Ni/γ-Al2O3催化剂加氢脱氧性能的影响

采用浸渍法制备了Mo-Ni/γ-Al2O3催化剂,利用BET、XRD、NH3-TPD等方法对还原态和硫化态Mo-Ni/γ-Al2O3催化剂进行了表征,并以模型化合物乙酸和F-T合成轻质油为原料,研究了还原态和硫化态催化剂的加氢脱氧(HDO)性能。结果表明,还原态催化剂具有较大的比表面积和孔体积,活性组分分散度较高;硫化态催化剂的酸性大于还原态催化剂。还原态催化剂具有比硫化态催化剂更好的HDO催化活性,不论是对模型化合物乙酸还是F-T合成轻质油都能获得更高的转化率;但用模型化合物乙酸的研究结果表明,硫化态催化剂不利于C—C键的断裂。     

Co-Mo/γ-Al2O3加氢脱硫催化剂的吸附扩散性能

用智能质量分析仪(Intelligent Gravimetric Analyser)测得了不同温度下异戊二烯(Isoprene)、戊烯-1(Pentene-1)及噻吩(Thiophene)在Co-Mo/γ-Al2O3选择性加氢脱硫催化剂上的吸附-脱附等温线及程序升温脱附曲线(TPD),并研究了三者在该催化剂上的扩散性能。结果表明,噻吩、异戊二烯、戊烯-1在Co-Mo/γ-Al2O3选择性加氢脱硫催化剂上的饱和吸附量依次降低;噻吩与该催化剂存在2种吸附作用,即物理吸附和化学吸附,化学吸附形成Co-Mo-S相,可有效地提高加氢脱硫催化剂的脱硫效果,而戊烯-1和异戊二烯在该催化剂上只存在1种弱吸附作用;3种吸附质中,戊烯-1相对扩散系数最大,噻吩和异戊二烯的相对扩散系数较小且相近。     

2,6-二甲基苯酚催化胺化过程Pd/γ-Al2O3催化剂的失活和改性

 采用固定床反应器, 研究了Pd/γ-Al₂O₃催化剂在催化2,6-二甲基苯酚气相胺化合成2,6-二甲基苯胺反应中的稳定性,实验结果发现催化剂较易失活。采用BET、XPS、TG、TEM和IR手段对失活前后的Pd/γ-Al₂O₃催化剂进行了表征分析,并采用BaO对Pd/γ-Al₂O₃催化剂进行改性。结果表明,Pd/γ-Al₂O₃催化剂失活的原因主要是反应过程生成的胺类化合物吸附在γ-Al₂O₃载体的酸性中心产生积碳沉积所致。Pd/γ-Al₂O₃催化剂添加BaO,生成了铝钡尖晶石结构,有效地减少了Pd/γ-Al₂O₃的酸性,加快了反应中生成的2,6-二甲基环己胺和2,6-二甲基苯胺的脱附,有效地避免了催化剂因积炭失活,提高了催化剂的稳定性。     

复合SiO2-WO3催化剂的制备、表征及氧化脱除苯并噻吩性能

 采用溶胶-凝胶法制备了SiO₂-WO₃催化剂,并采用XRD、FT-IR、BET、TG-DTA等方法对催化剂进行表征。以苯并噻吩(BT)为模型化合物,H₂O₂为氧化剂,考察了催化剂的活性元素、制备方法、n(W)/n(Si)和焙烧温度对其催化氧化脱硫活性的影响。结果表明,W的引入降低了SiO₂的比表面积,SiO₂-WO₃催化剂中W的主物相为WO₃。在以W为活性组元,且n(W)/n(Si)为0.1时,500℃焙烧得到的SiO₂-0.1WO₃催化剂具有最好的催化脱硫活性。在模拟油20 mL、催化剂SiO₂-0.1WO₃用量0.04 g、n(H₂O₂)/n(S)为15.9、乙腈/模拟油体积比0.3、65℃反应60 min的条件下,苯并噻吩模拟油脱硫率可达99.3%。     

Pt/SO42-/ZrO2-Al2O3在正己烷异构化反应中的催化行为

采用连续流动的固定床微反装置考察了Pt/SO24-/ZrO2-Al2O3(PSZA)在正己烷异构化反应中的催化行为。采用NH3-TPD、H2-TPR及TG表征了催化剂的酸性、还原性能及硫物种含量。结果表明,PSZA的初始异构化催化活性几乎不受反应温度的影响,而稳定性则与反应温度密切相关。低温下反应,催化剂在短时间内迅速失活,而提高反应温度可大大提高PSZA的反应稳定性。PSZA具有良好的再生性能,与新鲜催化剂相比,多次再生后的催化剂异构化催化活性基本没有变化。PSZA在低温下的快速失活与其催化活性中心产生的机理有关,而与其硫损失或硫物种的还原无关。在异构化反应过程中,催化剂通过氢溢流可产生强酸活性中心,并在反应过程中不断被消耗;在高温下通过氢溢流不断产生新的强酸中心,使催化活性保持稳定;而低温下氢溢流难以发生,消耗的强酸活性中心不能及时补充,使催化活性下降。     

Conditions for nonhydrodewaxing reaction of hydrocracking tail oil

Hydrocracking tail oil is used in hydrogenation modification in the hydrocracking process and is an ideal material to produce lube-based oil. Through investigating the effect of operation conditions on properties of dewaxing products under atmospheric pressure, the optimum operation conditions are that reaction temperature is 360°C, volume space velocity is 1.0 h^?1, and distillation temperature is 140°C. Under the optimum condition, the yield of liquid products is higher, and the flash point, pour point, and viscosity of white oil are stable and meet the factory product requirements. Especially, properties of alkane and white oil change little when reaction time is 20 h, which indicates that HZSM-5/Al₂O₃ has better stability. When HZSM-5 molecular sieve catalyst was loaded by pseudo-boehmite, HZSM-5/Al₂O₃ catalyst activity and stability improved and became more beneficial to nonhydrodewaxing reaction of hydrocracking tail oil.