一种Fe-C-Si-Mn-Cr-Mo钢碳配分行为对组织的影响

 利用Formastor-FⅡ全自动相变仪模拟研究了一种Fe-0.24C-0.3Si-1.0Mn-0.56Cr-0.17Mo（质量分数,%）钢在冷却过程中的碳配分行为及其对马氏体和残余奥氏体的影响,用扫描电镜、透射电镜进行微观组织表征,用X射线衍射法和电子背散射衍射法测定残余奥氏体体积分数。结果表明,试验钢分别经末段慢冷和直接快冷工艺冷却后均获得马氏体＋残余奥氏体两相组织,其中直接快冷工艺所得马氏体相对杂乱,尺寸较小,残余奥氏体体积分数较少;而末段慢冷工艺所得马氏体板条较长,且发生了碳的配分,残余奥氏体体积分数较多,以薄膜状分布在马氏体板条间,板条内部含有高密度位错。     

调质低碳贝氏体钢的组织和性能

研究了C-Mn-Mo-Cu-Nb-Ti-B系低碳微合金钢915℃淬火和490~640℃回火的调质工艺对钢的组织及力学性能的影响.用扫描电镜和透射电镜对实验钢的组织、析出物形态和分布以及断口形貌进行观察,采用X射线衍射仪分析钢中残余奥氏体的体积分数.结果表明:调质后,实验钢获得贝氏体、少量马氏体及残余奥氏体复相组织,贝氏体板条宽度只有250 nm,残余奥氏体的体积分数随着回火温度的升高而降低,经淬火与520℃回火后残余奥氏体的体积分数为2.1%.调质后析出物的数量激增,6~15 nm的析出物占70%以上.实验钢经过915℃淬火与520℃回火后,其屈服强度达到915 MPa,抗拉强度990 MPa,-40℃冲击功为95 J.细小的析出物及窄的板条提高了钢的强度.板条间有残余奥氏体存在,改善了实验钢的韧性.      

1800MPa级低合金超高强度工程机械用钢显微组织与力学性能

 设计了一种新型的超高强度工程机械用钢,在中试轧机上进行了不同工艺模拟轧制,对比研究了工艺1（80%变形量+直接淬火+250℃回火）、工艺2（90%变形量+层流冷却快冷至650℃/1h+空冷+250℃回火）和工艺3（90%变形量+空冷至650℃/1h+空冷+250℃回火）3种不同控轧控冷工艺对试验用钢的显微组织和力学性能的影响。结果表明：工艺1条件下试验钢的抗拉、屈服强度最高,塑韧性最好,分别可达到1816,1473MPa,伸长率为9.5%,断面收缩率为45%,室温冲击功为28J,-40℃冲击功为21J,硬度值达到50HRC,认为获得的是板条马氏体+残余奥氏体的复相组织和析出的复合微合金碳化物、ε-碳化物强韧化机制的综合作用;工艺2,3分别得到的是板条马氏体+块状贝氏体+残余奥氏体、板条马氏体+针状铁素体+片层状珠光体+残余奥氏体,力学性能下降明显;第二相析出物主要是Nb,V,Ti的复合析出颗粒。     

900MPa热轧板Q-P-T工艺及其工程可行性的研究

 基于合金设计制备出2种低合金试验热轧板钢,在采用水淬＋盐浴回火的淬火-分配-回火（Q-P-T）工艺处理后,达到了屈服强度900MPa和伸长率15％的设计指标,为后期自行设计的单道次穿水淬火冷却装置用于热轧板的Q-P-T工艺工程可行性的研究奠定了基础。X射线衍射、扫描电镜和透射电镜的微观组织分析表明:与传统的淬火回火（Q&T）工艺相比,Q-P-T先进高强度钢中位错型板条马氏体基体及其内弥散分布的合金碳化物贡献于高的强度,板条马氏体间的薄片状奥氏体贡献于优良的塑性。此外,还进一步探讨了Q-P-T工艺中残余奥氏体的作用和多道次穿水淬火冷却装置用于不同厚度热轧板在线Q-P-T处理的可行性。     

800MPa级水电用钢的微观组织和力学性能研究

采用控轧控冷与调质工艺相结合的方法,开发了一种力学性能满足要求的800 MPa级高强度水电用钢,并利用组织观察和性能测试手段研究了该水电用钢的显微组织和力学性能。结果表明：经调质处理后,该水电用钢的显微组织为回火索氏体＋回火马氏体,抗拉强度达880 MPa,断后延伸率为18.5%,40℃的冲击功为126 J。微观组织观察表明,该实验钢中碳化物在回火索氏体中分布均匀,在回火马氏体中主要分布在马氏体板条界处。     

回火温度对Mn-Ni钢亚稳奥氏体形貌及其力学性能的影响

 利用了X射线衍射仪（XRD）、电子背散射衍射（EBSD）和透射电子显微镜（TEM）研究了回火温度对一种Mn-Ni钢亚稳奥氏体形貌及其力学性能的影响。结果表明,随着回火温度的升高,室温亚稳奥氏体的体积分数逐渐升高。当回火温度为600和625 ℃时,亚稳奥氏体主要以片层状在回火马氏体板条间析出,且排列方向与周围的马氏体板条平行,这种片层状亚稳奥氏体分布较为均匀,尺寸较小,约为60～100 nm,且稳定性较高;当回火温度为650 ℃时,试验钢中出现尺寸较大的块状奥氏体在回火马氏体界面的交叉处不均匀析出。分析表明,块状奥氏体有利于提高钢的塑性,不利于改善钢的低温韧性;而片层状奥氏体能大幅度的改善钢的低温韧性。     

锰对贝氏体钢中残余奥氏体回火稳定性的影响

为探索锰含量的变化(锰质量分数为0.1%(0.1Mn钢)和1.5%(1.5Mn钢))对无碳化物贝氏体钢中残余奥氏体(RA)回火稳定性的影响,利用扫描电镜(SEM)、电子背散射衍射(EBSD)及透射电镜(TEM)等试验方法对残余奥氏体稳定性和力学性能的变化规律进行研究。结果表明,0.1Mn钢的热轧态组织主要是由粒状贝氏体(GB)+板条贝氏体(LB)组成,而1.5Mn钢的热轧态组织主要以板条贝氏体为主,且1.5Mn钢中残余奥氏体含量较高,屈服强度和抗拉强度均优于0.1Mn钢。在经过300～500℃回火后,残余奥氏体体积分数逐渐下降至完全分解,屈服强度和抗拉强度均表现为先升高后降低,但伸长率逐步增加。300℃回火性能最佳,原因主要是由于残余奥氏体在300℃回火中,块状残余奥氏体分解为过饱和马氏体/贝氏体,碳从过饱和马氏体/贝氏体中扩散至邻近残余奥氏体中使其含量增加,热稳定性得到提高,在拉伸的过程中产生了TRIP效应,从而使试验钢的强塑性得到提升。1.5Mn钢的性能明显优于0.1Mn钢,因为锰可以与碳产生协同作用共同促进奥氏体的稳定,提高伸长率,另外锰含量的增加使碳当量也提高,强度增强。基于修...     

回火温度对1500MPa级直接淬火钢组织与性能的影响

设计了一种新型1500MPa级Si-Mn-Cr-Ni-Mo多组元系低合金、超高强度工程结构钢,研究了回火温度对直接淬火钢组织与力学性能的影响.结果表明,抗拉强度随回火温度的升高而不断降低,屈服强度随回火温度升高先升高后下降,延伸率和冲击功均随回火温度升高呈现先升高、后降低、再升高的变化趋势.分析认为,回火过程组织演变的物理机制一方面包括板条马氏体和位错亚结构的回复、再结晶软化过程,另一方面包括残余奥氏体的分解与马氏体中过饱和碳的脱溶及析出第2相的强化机制综合作用.250℃回火后,板条马氏体内析出ε碳化物;400℃回火后ε碳化物明显粗化,产生回火脆性;600℃回火后部分析出相在奥氏体中形核,在马氏体基体内长大和粗化,最终形态为近似球形,另一部分析出相在马氏体内形核、生长,呈现椭球形或矩形.     

1.6 GPa级中碳高强贝氏体钢残余奥氏体调控机理

 为了研究中碳高强贝氏体钢中的残余奥氏体体积分数在不同等温情况下的变化规律,通过X射线衍射试验、热模拟试验和扫描电子显微镜观察等,分析了等温淬火条件对中碳高强贝氏体钢中残余奥氏体体积分数和组织的影响。结果表明,最终残余奥氏体的体积分数受贝氏体相变和马氏体相变的共同影响。贝氏体相变量决定了未转变奥氏体的体积分数及其化学稳定性,从而影响随后的马氏体相变量及最终残余奥氏体体积分数。此外,随着相变温度的升高,开始由于贝氏体相变量逐渐减少,残余奥氏体体积分数先增加(300~350 ℃),随后由于马氏体相变量增加,残余奥氏体体积分数减少(350~400 ℃)。     

回火对00Cr15Ni6Mo2高强马氏体不锈钢组织和性能的影响

研究了一种高强马氏体不锈钢00Cr15Ni6Mo2在回火过程中的逆变奥氏体的体积分数变化及其对力学性能的影响.结果表明,在550 ～750℃之间回火,当回火温度达到670℃时,逆变奥氏体的体积分数达到峰值39％,该钢在670℃回火时的HV硬度为280,夏比V缺口冲击吸收能为187.5 J,也分别达到峰值.沿马氏体板条析出的逆变奥氏体,对提高该钢回火条件下低温冲击韧性具有重要作用.     

Microstructure Evolution and Precipitation Behavior of 0Cr16Ni5Mo Martensitic Stainless Steel during Tempering Process

The microstructure,morphology of precipitates and retained austenite and the volume fraction of retained austenite in 0Cr16Ni5 Mo stainless steel during the tempering process were analyzed using optical microscope(OM),transmission electron microscope(TEM),X-ray diffraction(XRD)and scanning transmission electron microscope(STEM).The results show that the microstructure of the tempered steel is mainly composed of tempered martensite,retained austenite,and delta ferrite.In the case of samples tempered from 500 to 700 ℃,the precipitates are mainly M_(23)C_6,which precipitate along the lath martensite boundaries.The precipitate content increases with the tempering temperature.During the tempering process,the content of retained austenite initially increases and then decreases,the maximum content of retained austenite being 29 vol.% upon tempering at 600 ℃.TEM analysis of the tested steel reveals two morphology types of retained austenite.One is thin film-like retained austenite that exists along the martensite lath boundary.The other is blocky austenite located on packet at the boundary and the original austenite grain boundary.To further understand the stability of reversed austenite,the Ni content in reversed austenite was measured using STEM.Results show a significant difference in nickel concentrations between reversed austenite and martensite.     

Influence of Heat Treatment Temperature on Micro-structure and Property of 00Cr13Ni5Mo2 Su-permartensitic Stainless Steel

The microstructural evolution and mechanical property of 00Cr13Ni5Mo2supermartensitic stainless steel(SMSS)subjected to different heat treatments were investigated.Room tensile tests,hardness tests,scanning electron microscopy,transmission electron microscopy and X-ray diffraction were conducted on the heat-treated steels.It is found that the microstructure of the heat-treated steel is composed of tempered lath martensite,retained austenite andδ-ferrite.The austenitizing temperature and tempering temperature have a significant effect on the microstructural changes,which leads to the complex variations of mechanical properties.The fine tempered lath martensite and more dispersed reversed austenite in the microstructure facilitate improving the comprehensive mechanical properties of the studied steel.The optimal heat treatment process of 00Cr13Ni5Mo2SMSS is obtained by austenitizing at 1 000℃for 0.5h+air cooling followed by tempering at 630℃for 2h+air cooling,where the excellent combination of tensile strength,elongation and hardness can be achieved.     

回火时间对Fe-0.39C-3.69Mn中锰钢的组织和力学性能的影响

摘要：初始组织为片层珠光体的Fe-0.39C-3.69Mn（wt.%）钢板被快速加热到730℃保温90s后淬火至室温,获得包含13.2%残余奥氏体的板条马氏体组织。借助SEM、TEM、XRD和单向拉伸力学测试等试验手段,研究了在200℃回火时不同保温时间对微观组织和力学性能的影响,特别是对残余奥氏体体积分数和稳定性的影响。结果表明,随回火时间的增加,过渡碳化物逐渐增多并粗化,残余奥氏体含量先减少后不变;硬度、强度和均匀伸长率均逐渐降低,但断后伸长率由于马氏体回复而有所增加。片状残余奥氏体由于富Mn而具有较高稳定性,在200℃长时间回火后基本不发生分解。回火15min后获得最佳的综合力学性能,其屈服强度为1544MPa,抗拉强度为2031MPa,断后伸长率为10.1%。     

回火温度对COST-FB2转子钢析出相与力学性能的影响

 为了调整COST-FB2转子钢的强韧性,采用OM、SEM和TEM等手段研究了回火温度对COST-FB2转子钢的析出相类型与力学性能的影响。结果表明,随着回火温度由350 ℃升高到750 ℃,试验钢的强度、硬度不断下降,塑性和冲击功上升;试验钢350 ℃和570 ℃回火后的高强低韧性可通过再次在700 ℃回火改善。淬火后COST-FB2转子钢中的残余奥氏体,可通过在570 ℃回火消除;在350 ℃和570 ℃回火后马氏体板条内部有大量针状的M₃C,700 ℃回火后的显微组织中M₃C消失,M₂₃C₆在原奥氏体晶界和马氏体板条界上析出,750 ℃回火后晶界上的M₂₃C₆有聚集粗化的现象,部分马氏体板条存在回复现象。     

预处理组织对低碳钢IQ&P工艺下组织及性能影响

采用γ单相区和γ+α双相区轧制并淬火工艺以及双相区再加热-淬火-碳配分(IQ&P)工艺,研究预处理组织对低碳钢室温状态多相组织特征及力学性能的影响规律.实验用低碳钢经两种工艺轧制并淬火处理,获得马氏体和马氏体+铁素体的预处理组织,再经双相区IQ&P工艺处理后均获得多相组织.马氏体预处理钢的室温组织由板条状亚温铁素体、块状回火马氏体以及一定比例的针状未回火马氏体和8.2%的针状残余奥氏体组成;马氏体+铁素体预处理钢由板条状亚温铁素体、块状和针状未回火马氏体以及14.3%的短针状或块状残余奥氏体组成.在相同的双相区IQ&P工艺参数下,预处理组织为马氏体的钢抗拉强度为770 MPa,伸长率为28%,其强塑积为21560 MPa·%;而预处理组织为马氏体+铁素体的钢抗拉强度为834 MPa,伸长率增大到36.2%,强塑积达到30190 MPa·%,获得强度与塑性的优良结合.      

淬火工艺对马氏体高强钢组织和性能的影响

摘要：采用拉伸、冲击、金相、电子背散射衍射、透射电镜、X射线衍射等试验手段,研究了在线直接淬火+回火（DQT）与离线再加热淬火+回火（RQT）工艺对马氏体高强钢组织性能的影响。结果表明,2种试验钢组织均为板条马氏体,RQT试验钢原奥氏体晶粒及板条束呈等轴状,板条块较短,板条较宽,DQT试验钢原奥氏体晶粒呈扁平状,板条束贯穿整个晶粒,板条块呈细长状,板条宽度较小;位错强化是DQT试验钢强度较RQT高的主要原因;板条束为控制DQT和RQT试验钢韧性的最小单元;DQT试验钢大角晶界比例较低,其具有较大的马氏体板条束尺寸以及更高的位错密度,断裂应力较低,低温韧性较差。     

Influence of Tempering Process on Mechanical Properties of 00Cr13Ni4Mo Supermartensitic Stainless Steel

To investigate the influence of tempering process on microstructural evolutions and mechanical properties of 00Cr13Ni4Mo supermartensitic stainless steel(SMSS),specimens were tempered in the temperature range of 520-720 ℃ for 3 h followed by air cooling and an optimized tempering temperature was chosen to prolong holding time from 3 to 12 h.After heat treatments,microstructure examination was conducted by scanning electron microscope,X-ray diffraction examinations,hardness measurements and tensile tests.The results revealed that the superior mechanical properties were achieved by quenching at 1040 ℃ for 1 h+water cooling and tempering at 600 ℃ for 3 h+air cooling.Increasing isothermal tempering time could improve the toughness notably.It was believed that the property was correlated with the microstructure of tempered lath martensite and retained austenite.More retained austenite content is beneficial to the higher toughness of the SMSS.     

Formation of Reversed Austenite in High Temperature Tempering Process and its Effect on Mechanical Properties of Cr15 Super Martensitic Stainless Steel Alloyed with Copper

Formation mechanism of the reversed austenite of Cr15 super martensitic stainless steel (SMSS) alloyed with copper after high temperature tempering was investigated by means of thermo‐calc software, transmission electron microscope (TEM), and X‐ray diffraction (XRD). The mechanical properties of the SMSS were also tested. The experimental results show that the reversed austenite with low dislocation density is formed at high temperature tempering processing. The transformation of the martensite to reversed austenite is a diffused phase transformation, and the growth of the reversed austenite is closely related to the diffusion process of Ni. The bulk reversed austenite with large amount of stacking faults is formed with the increase of the tempering temperature. The volume fraction of reversed austenite increases at first and then decreases with increasing tempering temperature, and the maximum amount of the reversed austenite is obtained at 650°C. The reversed austenite is unstable at the tempering temperature above 650°C and the martensitic phase transformation will occur at the following cooling process. The mechanical properties of Cr15 super martensitic stainless steel are significantly influenced by the volume fraction of reversed austenite.