Spontaneous copolymerization of N‐butyl maleimide and ethyl α‐phenyl acrylate with high alternating tendency

The copolymerization of N‐butyl maleimide (BMI) and ethyl α‐phenyl acrylate (EPA) was successfully carried out without an initiator. A high alternating tendency was observed. The Q, e values were derived by Alfrey–Price equations: Q = 0.09, e = 0.81 for BMI and Q = 0.21, e = ?0.5 for EPA, and the monomer reactivity ratios were r_BMI = 0.15 ± 0.01 and r_EPA = 0.18 ± 0.08, respectively. In this system BMI was donor and EPA was acceptor. The maximum copolymerization rate and molecular weight appeared at 70 mol % (BMI) in the feed ratio. The spontaneous alternating copolymerization was considered to be completed by a contact‐type charge‐transfer complex formed by the monomer pairs. © 2004 Wiley Periodicals, Inc. J Appl Polym Sci 94: 355–360, 2004     

Design and synthesis of zero–zero‐birefringence polymers using N‐methylmaleimide

Zero–zero‐birefringence polymers which exhibit no orientational birefringence and no photoelastic birefringence may be suitable candidates for the components of optical devices. To develop zero–zero‐birefringence polymers, a novel copolymerization system is required. We investigated two types of birefringence of poly(N‐methylmaleimide) (PMeMI) and showed that PMeMI exhibits positive orientational and photoelastic birefringence. On the basis of the results, we calculated the optimal composition for compensating both types of birefringence by solving three equations which describe the relationship between birefringence properties and weight fraction of monomers. When the copolymer compositions were MMA/BzMA/MeMI = 86/8/6 and 88/8/4 (wt %), zero–zero‐birefringence polymers were obtained. By using MeMI as a comonomer, these zero–zero‐birefringence polymers have a much higher glass transition temperature (T_g) than those of previous researches. Also, this polymer film has high transparency comparable with that of PMMA film. Therefore, we conclude that we successfully prepared zero–zero‐birefringence polymers using N‐substituted maleimide and that N‐substituted maleimide is a promising material for zero–zero‐birefringence polymers for optical devices. © 2014 Wiley Periodicals, Inc. J. Appl. Polym. Sci. 2014 , 131, 40423.     

Magnetic properties of polystyrene‐b‐poly(2‐hydroxylethyl methacrylate)/metal hybrids

Hybrids, which were composed of the amphiphilic diblock copolymer polystyrene‐b‐poly(2‐hydroxylethyl methacrylate) (PSt‐b‐PHEMA) and nickel, cobalt, or a nickel–cobalt alloy, were characterized with infrared absorption spectroscopy and ultraviolet–visible (UV–vis) absorption spectroscopy. UV–vis spectroscopy analysis showed that a redshift happened after the PSt‐b‐PHEMA/metal‐ion complexes were reduced by KBH₄. The PSt‐b‐PHEMA/nickel–cobalt alloy hybrids had the biggest redshift [difference of the UV‐vis absorption wavelength between (PSt‐b‐PHEMA)/metal ion complex and (PSt‐b‐PHEMA)/metal hybrids (Δλ_m = 19.9 nm)]. In comparison with the PSt‐b‐PHEMA/nickel hybrids (Δλ_m = 3.5 nm) and PSt‐b‐PHEMA/cobalt hybrids (Δλ_m = 9.0 nm). The magnetic properties of PSt‐b‐PHEMA/metal were studied with vibrating sample magnetometry. The results of magnetic hysteresis loop studies showed that the obtained PSt‐b‐PHEMA/metal hybrids could be categorized as ferromagnetic materials. The results showed that the magnetic susceptibility decreased with increasing temperature in the range of 150–400 K and increased with increasing temperature above 400 K. © 2005 Wiley Periodicals, Inc. J Appl Polym Sci, 2006     

Copolymerization of butadiene with styrene using a rare‐earth metal compound – dialkylmagnesium – halohydrocarbon catalytic system

Copolymerizations of butadiene (Bd) with styrene (St) were carried out with catalytic systems composed of a rare‐earth compound, Mg(n‐Bu)₂ (di‐n‐butyl magnesium) and halohydrocarbon. Of all the rare earth catalysts examined, Nd(P₅₀₇)₃–Mg(n‐Bu)₂–CHCl₃ showed a high activity in the copolymerization under certain conditions: [Bd] = [St] = 1.8 mol l^?1, [Nd] = 6.0 × 10^?3 mol l^?1, Mg/Nd = 10, Cl/Nd = 10 (molar ratio), ageing for 2 h, copolymerization at 50 °C for 6–20 h. The copolymer of butadiene and styrene obtained has a relatively high styrene content (10–30 mol%), cis‐1,4 content in butadiene unit (85–90%), and molecular weight ([η] = 0.8–1 dL g^?1). Monomer reactivity ratios were estimated to be r_Bd = 36 and r_St = 0.36 in the copolymerization. © 2002 Society of Chemical Industry     

Stereochemical and compositional assignments of trans‐4‐methacryloyloxyazobenzene–methyl methacrylate copolymers by one‐ and two‐dimensional NMR spectroscopy

The microstructure of trans‐4‐methacryloyloxyazobenzene–methyl methacrylate copolymers prepared by solution polymerization process using AIBN as initiator is analyzed by one‐and two‐dimensional spectroscopy. Sequence distribution was calculated from the ¹³C(¹H)‐NMR spectra of the copolymers. Comonomer reactivity ratios were determined using the Kelen–Tudos and the nonlinear error‐in‐variables methods are r_A = 1.14 ± 0.08 and r_M = 0.51 ± 0.03; r_A = 1.13 ± 0.1 and r_M = 0.50 ± 0.04, respectively. The sequence distribution of A‐ and M‐centered triads determined from ¹³C(¹H)‐NMR spectra of copolymer is in good agreement with triad concentration calculated from a statistical model. The 2‐D heteronuclear single‐quantum correlation and correlated spectroscopy (TOCSY) was used to analyze the complex ¹H‐NMR spectrum. © 1999 John Wiley & Sons, Inc. J Appl Polym Sci 74: 3016–3025, 1999     

Sequencing of N‐vinyl‐2‐pyrrolidone/glycidyl methacrylate copolymers by one‐dimensional and two‐dimensional nuclear magnetic resonance spectroscopy

Copolymers of N‐vinyl‐2‐pyrrolidone (V) and glycidyl methacrylate (G) monomers of different compositions were prepared by free‐radical solution polymerization. The copolymer composition of these copolymers was determined with ¹H‐NMR spectra. The reactivity ratios calculated from the Kelen–Tudos and nonlinear least‐square error‐in‐variable methods were r_V = 0.03 ± 0.01 and r_G = 5.05 ± 0.84 and r_V = 0.02 and r_G = 4.72, respectively. The triad sequence distribution in terms of V and G centered triads was determined from ¹³C{¹H}‐NMR spectroscopy. The complete spectral assignment of ¹³C{¹H}‐ and ¹H‐NMR spectra was performed with the help of distortionless enhancement by polarization transfer and two‐dimensional ¹³C–¹H heteronuclear single quantum coherence. The ¹H–¹H couplings were explained with total correlation spectroscopy and nuclear Overhauser enhancement spectroscopy spectra. © 2002 Wiley Periodicals, Inc. J Appl Polym Sci 84: 50–60, 2002; DOI 10.1002/app.10186     

4‐Acetamidophenyl acrylate copolymers with acrylonitrile and N‐vinyl‐2‐pyrrolidone: Synthesis,characterization, and reactivity ratios

4‐Acetamidophenyl acrylate (APA) was synthesized and characterized by IR, ¹H and ¹³C NMR spectroscopies. Homo‐ and copolymers of APA with acrylonitrile (AN) and N‐vinyl‐2‐pyrrolidone (NVP) were prepared by a free radical polymerization. All the copolymer compositions have been determined by ¹H NMR technique, and the reactivity ratios of the monomer pairs have been evaluated using the linearization methods Fineman–Ross, Kelen–Tudos, and extended Kelen–Tudos. Nonlinear error‐in‐variable model (EVM) method was used to compare the reactivity ratios. The reactivity ratios for copoly(APA–AN) system were APA(r₁) = 0.70 and AN(r₂) = 0.333, and for copoly(APA–NVP) system the values were APA(r₁) = 4.99 and NVP(r₂) = 0.019. Thermal stability and molecular weights of the copolymers are reported. © 2005 Wiley Periodicals, Inc. J Appl Polym Sci 99: 1919–1927, 2006     

Moisture‐sorption characteristics of starch/low‐density polyethylene films

Moisture‐sorption characteristics of starch/low‐density polyethylene (LDPE) blends were carried out at 27°C for water activity (a_w) from 0.1 to 0.9. The sorption data were used to fit six different sorption isotherm models proposed in the literature. The model constants were determined by linear fitting of the sorption equations. The ranges of applicability of water activity for the isotherm models reported in the article lies between 0.1 and 0.4 (monomolecular layer) for the BET model and between 0.3 and 0.9 (multimolecular and capillary condensation layers) for other models. The value of the coefficient of determination (R² = 0.97 ± 0.02) confirms the linear fitting of the equations studied. © 2002 Wiley Periodicals, Inc. J Appl Polym Sci 84: 1193–1202, 2002; DOI 10.1002/app.10417     

Well‐functioned photovoltaics based on nanofibers composed of PBDT‐TIPS‐DTNT‐DT and graphenic precursors thermally modified by polythiophene,polyaniline and polypyrrole

Reduced graphene oxide nanosheets modified by conductive polymers including polythiophene (GPTh), polyaniline (GPANI) and polypyrrole (GPPy) were prepared using the graphene oxide as both substrate and chemical oxidant. UV–visible and Raman analyses confirmed that the graphene oxide simultaneously produced the reduced graphene oxide and polymerized the conjugated polymers. The prepared nanostructures were subsequently electrospun in mixing with poly(3‐hexylthiophene) (P3HT)/phenyl‐C71‐butyric acid methyl ester (PC₇₁BM) and poly[bis(triisopropylsilylethynyl)benzodithiophene‐bis(decyltetradecylthien)naphthobisthiadiazole] (PBDT‐TIPS‐DTNT‐DT)/PC₇₁BM components and embedded in the active layers of photovoltaic devices to improve the charge mobility and efficiency. The GPTh/PBDT‐TIPS‐DTNT‐DT/PC₇₁BM devices demonstrated better photovoltaic features (J_sc = 11.72 mA cm^?2, FF = 61%, V_oc = 0.68 V, PCE = 4.86%, μ_h = 8.7 × 10^?3 cm² V^–1 s^?1 and μ_e = 1.3 × 10^?2 cm² V^–1 s^?1) than the GPPy/PBDT‐TIPS‐DTNT‐DT/PC₇₁BM (J_sc = 10.30 mA cm^?2, FF = 60%, V_oc = 0.66 V, PCE = 4.08%, μ_h = 1.4 × 10^?3 cm² V^–1 s^?1 and μ_e = 8.9 × 10^?3 cm² V^–1 s^?1) and GPANI/PBDT‐TIPS‐DTNT‐DT/PC₇₁BM (J_sc = 10.48 mA cm^?2, FF = 59%, V_oc = 0.65 V, PCE = 4.02%, μ_h = 8.6 × 10^?4 cm² V^–1 s^?1 and μ_e = 7.8 × 10^?3 cm² V^–1 s^?1) systems, assigned to the greater compatibility of PTh in the nano‐hybrids and the thiophenic conjugated polymers in the bulk of the nanofibers and active thin films. Furthermore, the PBDT‐TIPS‐DTNT‐DT polymer chains (3.35%–5.04%) acted better than the P3HT chains (2.01%–3.76%) because of more complicated conductive structures. © 2019 Society of Chemical Industry     

Microstructure determination of the acrylonitrile–styrene–methyl methacrylate terpolymers by NMR spectroscopy

Acrylonitrile–styrene–methyl methacrylate (A–S–M) terpolymers were prepared by photopolymerization using uranyl nitrate ions as photo initiators, which were analyzed by NMR spectroscopy. The terpolymer compositions were determined by Goldfinger's equation using comonomer reactivity ratios: r_as = 0.04; r_sa = 0.31; r_am = 0.17, r_ma = 1.45; r_sm = 0.52; r_ms = 0.47. The terpolymer compositions were also determined from the quantitative ¹³C(¹H)‐NMR spectroscopy. The sequence distribution of the acrylonitrile‐, styrene‐, and methyl methacrylate–centered triads were determined from the ¹³C(¹H)‐NMR spectra of the terpolymers and are in good agreement with triad concentrations calculated from the statistical model. © 1999 John Wiley & Sons, Inc. J Appl Polym Sci 74: 3026–3032, 1999     

Thermal decomposition behavior of oligo(4‐hydroxyquinoline)

In this study, the kinetic parameters and reaction mechanism of decomposition process of oligo(4‐hydroxyquinoline) synthesized by oxidative polymerization were investigated by thermogravimetric analysis (TGA) at different heating rates. TGA‐derivative thermogravimetric analysis curves showed that the thermal decomposition occurred in two stages. The methods based on multiple heating rates such as Kissinger, Kim–Park, Tang, Flynn–Wall–Ozawa method (FWO), Friedman, and Kissinger–Akahira–Sunose (KAS) were used to calculate the kinetic parameters related to each decomposition stage of oligo(4‐hydroxyquinoline). The activation energies obtained by Kissinger, Kim–Park, Tang, KAS, FWO, and Friedman methods were found to be 153.80, 153.89, 153.06, 152.62, 151.25, and 157.14 kJ mol^?1 for the dehydration stage, 124.7, 124.71, 126.14, 123.75, 126.19, and 124.05 kJ mol^?1 for the thermal decomposition stage, respectively, in the conversion range studied. The decomposition mechanism and pre‐exponential factor of each decomposition stage were also determined using Coats–Redfern, van Krevelen, Horowitz–Metzger methods, and master plots. The analysis of the master plots and methods based on single heating rate showed that the mechanisms of dehydration and decomposition stage of oligo(4‐hydroxyquinoline) were best described by kinetic equations of A_n mechanism (nucleation and growth, n = 1) and D_n mechanism (dimensional diffusion, n = 6), respectively. POLYM. ENG. SCI., 54:992–1002, 2014. © 2013 Society of Plastics Engineers     

Synthesis and properties of poly(amide–imide)s based on N,N′‐bis(4‐carboxyphenyl)‐4,4′‐oxydiphthalimide,p‐aminobenzoic acid and various aromatic diamines

A new diimide–diacid monomer, N,N′‐bis(4‐carboxyphenyl)‐4,4′‐oxydiphthalimide (I), was prepared by azeotropic condensation of 4,4′‐oxydiphthalic anhydride (ODPA) and p‐aminobenzoic acid (p‐ABA) at a 1:2 molar ratio in a polar solvent mixed with toluene. A series of poly(amide–imide)s (PAI, III_a–m) was synthesized from the diimide–diacid I (or I′, diacid chloride of I) and various aromatic diamines by direct polycondensation (or low temperature polycondensation) using triphenyl phosphite and pyridine as condensing agents. It was found that only III_k–m having a meta‐structure at two terminals of the diamine could afford good quality, creasable films by solution‐casting; other PAIs III using diamine with para‐linkage at terminals were insoluble and crystalline; though III_g–i contained the soluble group of the diamine moieties, their solvent‐cast films were brittle. In order to improve their to solubility and film quality, copoly(amide–imide)s (Co‐PAIs) based on I and mixtures of p‐ABA and aromatic diamines were synthesized. When on equimolar of p‐ABA (m = 1) was mixed, most of Co‐PAIs IV had improved solubility and high inherent viscosities in the range 0.9–1.5 dl g^?1; however, their films were still brittle. With m = 3, series V was obtained, and all members exhibited high toughness. The solubility, film‐forming ability, crystallinity, and thermal properties of the resultant poly(amide–imide)s were investigated. © 2002 Society of Chemical Industry     

Thermodynamic hydrogen bonding inpoly(styrene‐co‐acrylic acid)/poly(styrene‐co‐4‐N,N‐dimethylacrylamide) blends

FTIR study of the hydrogen bonding interactions within blends of different ratios of poly(styrene‐co‐acrylic acid) containing 18, 27, and 32 mol% of acrylic acid (SAA) and poly(styrene‐co‐N,N‐dimethylacrylamide) containing 17 mol% of N,N‐dimethylacrylamide (SAD‐17) was carried out qualitatively and quantitatively in the temperature range varying from room temperature to 210°C. Two new bands characterizing these interactions appeared in the 1800–1550 cm^–1 region at 1730 cm^–1 and 1616 cm^–1 and are attributed to “liberated” carbonyl group of the acidic copolymer and the “associated amide” carbonyl group, respectively. Equilibrium constants describing both the self‐association K₂ and inter‐association K_A and the enthalpy of hydrogen bonding formation in the different blends were experimentally determined using a curve fitting analysis of the infra‐red spectra as a function of temperature using the appropriate equations derived from the Painter‐Coleman association model. The obtained results confirm the miscibility of these blends in the considered temperature range from the negative values of the total free energy of mixing ΔG_M. Optimization of the extent of intermolecular interactions between the two polymers in these blends is investigated. POLYM. ENG. SCI., 2008. © 2008 Society of Plastics Engineers     

cis‐trans Pair of a N‐Benzoylaziridine: Dependence of Carbonyl Reactivity on Nitrogen Pyramid

In a multistep process, anthracenide and both 1‐benzoyl‐2‐methyl‐3‐phenylaziridines 1a form carbanion 4a that abstracts a proton from the solvent THF. The steep N pyramid of cis‐ 1a makes attack of 4a on C=O of cis‐ 1a fast enough to compete with proton abstraction while C=O of trans‐ 1a with its flat and rapidly inverting pyramid did not react with 4a . The initially generated ketyls of 1a show another cis‐trans effect of steric repulsion: their homolytic ring opening forms benzylic radical 3a , the precursor of carbanion 4a , but this opening is regiospecific for the cis ketyl only. The trans ketyl forms some isomeric radical too.     

Synthesis of hydroxyethylcellulose‐graft‐poly(N,N‐dimethylacrylamide) copolymer by ATRP and as dynamic coating in capillary electrophoresis

Hydroxyethylcellulose‐graft‐poly (N, N‐dimethylacrylamide) was synthesized by successive atom transfer radical polymerization (ATRP) of N,N‐dimethylacrylamide (DMA) monomer using HEC‐Br as initiator, CuBr and 5,5,7,12,12,14‐hexamethyl‐1,4,8,11‐tetraazamacrocyclotetradecane (Me₆[14]aneN₄) as catalyst and ligand, with molar ratio DMA: HEC‐Br (C? Br): CuBr: Me₆[14]aneN₄ = 100 : 1 : 1 : 3. HEC–Br macroinitiator was synthesized by esterification of HEC with 2‐bromoisobutyryl bromide. GPC and ¹H NMR studies show that the molecular weight of the resulting PDMA increased linearly with the conversion. Within 6 h, the polymerization can reach almost 60% of conversion. The copolymer is applied for the separation of basic proteins in capillary electrophoresis. The results show that this medium has a powerful capability in resisting basic proteins adsorption because the polymer forms noncovalent coating in silica capillaries. With a broad range of pH 2–7, proteins were separated with sufficient efficiencies above 200,000 plates/m. © 2010 Wiley Periodicals, Inc. J Appl Polym Sci, 2010     

Effect of acrylic acid neutralization on ‘livingness’ of poly[styrene‐ran‐(acrylic acid)] macro‐initiators for nitroxide‐mediated polymerization of styrene

BACKGROUND: The effect of acrylic acid neutralization on the degradation of alkoxyamine initiators for nitroxide‐mediated polymerization (NMP) was studied using styrene/acrylic acid and styrene/sodium acrylate random copolymers (20 mol% initial acrylate feed concentration) as macro‐initiators. The random copolymers were re‐initiated with fresh styrene in 1,4‐dioxane at 110 °C at SG1 mediator/BlocBuilder^® unimolecular initiator ratios of 5 and 10 mol%. RESULTS: The value of k_pK (k_p = propagation rate constant, K = equilibrium constant) was not significantly different for styrene/acrylic acid and styrene/sodium acrylate compositions at 110 °C (k_pK = 2.4 × 10^?6–4.6 × 10^?6 s^?1) and agreed closely with that for styrene homopolymerization at the same conditions (k_pK = 2.7 × 10^?6–3.0 × 10^?6 s^?1). All random copolymers had monomodal, narrow molecular weight distributions (polydispersity index M?_w/M?_n = 1.10–1.22) with similar number‐average molecular weights M?_n = 19.3–22.1 kg mol^?1. Re‐initiation of styrene/acrylic acid random copolymers with styrene resulted in block copolymers with broader molecular weight distributions (M?_w/M?_n = 1.37–2.04) compared to chains re‐initiated by styrene/sodium acrylate random copolymers (M?_w/M?_n = 1.33). CONCLUSIONS: Acrylic acid degradation of the alkoxyamines was prevented by neutralization of acrylic acid and allowed more SG1‐terminated chains to re‐initiate the polymerization of a second styrenic block by NMP. Copyright © 2008 Society of Chemical Industry     

Synthesis and application of KM‐type reactive dyes containing 2‐ethoxy‐4‐chloro‐s‐triazine

A new kind of hetero‐bifunctional reactive dye containing 2‐ethoxy‐4‐chloro‐s‐triazine, with better activity matching with β‐hydroxyethyl sulphone sulphate at a low fixation temperature, was successfully synthesised and characterised. An ethoxy group was designed to be introduced into triazine to increase the substantivity and the reactivity of the dyes. Thereby, the fixation of mono‐s‐chlorotriazine/hydroxyethyl sulphone sulphate (KM‐type) bifunctional reactive dyes on cotton was improved, and dyeing under mild conditions with high fixation was realised. Nineteen dyes with orange, red and blue colours were synthesised and characterised by UV‐Vis and infrared spectroscopy and mass spectrometry. Synthesised dyes were dyed at 60, 75 and 90°C, respectively. Exhaustion and reactivity for all of the ethoxy‐containing KM‐type dyes was over 90% at the optimal temperature, and fixation was over 87%, which was higher than the ethoxy‐free comparative dyes. The optimal fixation temperature of ethoxy‐containing dyes was initially reduced to 75°C, and then to 60°C. Compared with comparative dyes, the wash fastness and light fastness were basically unchanged, and the wet rub fastness of the H‐acid series was reduced by one grade.     

Thermal Behavior and Thermolysis Kinetics of the Explosive Trans‐1,4,5,8‐Tetranitro‐1,4,5,8‐Tetraazadecalin (TNAD)

Trans‐1,4,5,8‐Tetranitro‐1,4,5,8‐Tetraazadecalin (TNAD), a cyclic nitroamine, has been studied with regard to the kinetics and mechanism of thermal decomposition, using thermogravimetry (TG), IR spectroscopy, and pressure differential scanning calorimetry (PDSC). The IR spectra of TNAD have also been recorded, and the kinetics of thermolysis has been followed by non‐isothermal TG. The activation energy of the solid‐state process was determined by using the Flynn‐Wall‐Ozawa method. Compared with the activation energy obtained from the Ozawa method, the reaction mechanism of the exothermic process of TNAD was classified by the Coats‐Redfern method as a nucleation and nuclear growth (Avrami equation 1) chemical reaction (α=0.30–0.60) and a 2D diffusion (Valensi equation) chemical reaction (α=0.60–0.90). E_a and ln A were established to be 330.14 kJ mol⁻¹ and 29.93 (α=0.30–0.60) or 250.30 kJ mol⁻¹ and 21.62 (α=0.60–0.90).     

Kinetics of azo‐initiated 1‐vinyl‐2‐pyrrolidone polymerizations at low conversions in aqueous media

The free‐radical polymerization behavior of 1‐vinyl,2‐pyrrolidone (NVP) was studied at low conversions, using capillary dilatometry. The aqueous media were kept at neutral pH and the studies were conducted isothermally, at 40 or 45°C. The azo‐type initiators used were 4,4′‐azobis‐4‐cyanopentanoic acid (ACPA), 2,2′‐azobisisobutyronitrile (AZBN), and 2,2′‐azobis[2‐(2‐imidazolin‐2‐yl)propane dihydrochloride] (ABDH). The monomer concentration and initiator concentration ranges were 1.17–2.34 mol L⁻¹ and 1–8 mmol L⁻¹, respectively. The rates of polymerization (R_p) and orders of reaction with respect to NVP and the initiator were evaluated and the kinetic equations were found to be R_p ∝ [NVP] [ACPA]^1.2; R_p ∝ [NVP] [AZBN]^1.1; and R_p ∝ [NVP]^2.2 [ABDH]^1.1. The polymers obtained were characterized by their viscosity numbers and correlation of the viscosity average molecular weights made with the type and amount of the azo initiator. © 2000 John Wiley & Sons, Inc. J Appl Polym Sci 75: 239–246, 2000     

Microstructure determination and thermal studies of n‐acryloylcarbazole/vinyl acetate copolymers

Copolymers of N‐acryloylcarbazole (A) and vinyl acetate (V) were synthesized by bulk polymerization using benzoyl peroxide (BPO) as free‐radical initiator at 65°C in different in‐feed ratios. The composition of the copolymer was determined by ¹H‐NMR spectrum. The comonomer reactivity ratios, determined by Kelen–Tudos (KT) and nonlinear error‐in‐variables (EVM) methods, were r_A= 16.75 ± 1.38, r_V = 0.015 ± 0.002, and r_A = 16.36, r_V = 0.015, respectively. Complete spectral assignments of the ¹H and ¹³C{¹H} NMR spectra of the copolymers were done by the help of distortionless enhancement by polarization transfer (DEPT) and two‐dimensional NMR techniques such as heteronuclear single quantum coherence (HSQC) and total correlation spectroscopy (TOCSY). The methine and methylene carbon resonances were found to be compositional as well as configurational sensitive. The signals obtained were broad pertaining to the restricted rotation of bulky carbazole group. The thermal stability and glass‐transition temperatures (T_g) of the copolymers were found to be dependant on polymer composition and characteristic of rotational rigidity of the polymer chain. Variation in the values of T_g with the copolymer composition was found to be in good agreement with theoretical values obtained from Johnston and Barton equations. © 2006 Wiley Periodicals, Inc. J Appl Polym Sci 103: 2720–2733, 2007