聚合物干粉对加气混凝土用抹灰砂浆性能的影响

针对加气混凝土普通抹灰砂浆存在的保水性差、粘结强度低、易开裂空鼓等缺陷,研究了聚合物干粉对加气混凝土用抹灰砂浆性能的影响,并对该影响机理进行了讨论.研究表明,在砂浆中同时掺入羟乙基甲基纤维素醚和聚乙烯-醋酸乙烯酯可再分散乳胶粉,大大改善了砂浆的保水性、提高了和易性和粘结强度,较好地解决了普通抹灰砂浆用于加气混凝土存在的开裂、空鼓甚至脱落等问题.     

GLW型复合外加剂的研制

针对普通砂浆用于加气混凝土抹灰时,存在保水性差、粘结强度低、易开裂空鼓等缺陷,研制了一种可以改善砂浆和易性、提高砂浆保水性和粘结强度、降低砂浆收缩的GLW型复合外加剂。研究结果表明,用GLW型复合外加剂配制的砂浆性能远优于普通砂浆,具有保水性能好、粘结强度高、折压比大、收缩值小等特点,适合加气混凝土的抹灰。     

聚合物对抹灰砂浆性能的影响

预拌抹灰砂浆中的聚合物的种类和掺量对砂浆的性能有着重要的影响。本文研究纤维素醚、乳胶粉等聚合物对抹灰砂浆的保水性、柔韧性和力学性能的影响,并着重探讨了添加剂对加气混凝土基面粘结性能的影响,结果表明纤维素醚能够显著提高砂浆的保水性、粘聚性和柔性,提高抗下滑性能和减少开裂;纤维素醚和乳胶粉均能够提高砂浆的粘结力。     

干混砂浆复合改性在加气混凝土砌块墙体中的研究与应用

通过对加气混凝土砌块配套干混砂浆中粉煤灰、羟丙基甲基纤维素醚、可再分散乳胶粉及N型高效减水剂进行研究,得出各项材料对配套干混砂浆的影响程度,从而得出最佳的干混砂浆配合比;研究有机纤维和粉煤灰在专用抹灰砂浆中的作用和性能,得出最佳有机纤维配合比和粉煤灰掺量。经实践,可有效控制加气混凝土砌块墙体和抹灰墙体的裂缝。     

加气混凝土专用抗裂抹面砂浆的研制

通过加入甲基纤维素醚、可再分散乳胶粉、聚丙烯纤维等聚合物,粉煤灰掺合料对砂浆进行改性,研制的加气混凝土专用抗裂抹面砂浆。本课题通过分析几种聚合物掺量对砂浆性能影响因素的大小,得出最佳掺量,找出砂浆最佳配比。经测试,研制的加气混凝土专用抗裂抹面砂浆可操作性好,便于施工,与加气混凝土粘结强度高,抗裂性能好。     

加气混凝土用新型抹灰砂浆的研制

针对加气混凝土传统抹灰砂浆存在的保水性差、粘结强度低、易开裂空鼓等缺陷,研制了一种主要性能指标大大优于《蒸压加气混凝土用砌筑砂浆与抹面砂浆》（JC890-2001）标准的加气混凝土用新型抹灰砂浆,研究了保水剂、胶粉、膨胀剂等外加剂对砂浆性能的影响,并对各种外加剂对砂浆的改性机理进行了讨论。     

外加剂对大掺量非等级粉煤灰、煤矸石干混砂浆性能的影响

针对利用非等级粉煤灰配制干混砂浆,用于加气混凝土砌筑与抹灰时存在和易性差、粘结强度低、泌水大的缺陷。研究了胶粉、保水剂和木纤维等几种外加剂对大掺量粉煤灰煤矸石干混砂浆性能的影响,分析各组分不同掺量对干混砂浆性能的影响规律。最后确定出各种外加剂组分较适宜的掺量范围:胶粉掺量1%左右;保水剂掺量0.1%左右;木纤维掺量0.2%左右。试验结果表明:通过添加外加剂,大掺量非等级粉煤灰和煅烧煤矸石作胶凝材料的干混砂浆综合性能得到了大幅提升,具有很好的利用价值。     

巴基斯坦粉细砂在抗裂抹灰砂浆中的应用研究

通过试验探究粉细砂作为集料制备抗裂抹灰砂浆的可行性,研究胶砂比、纤维素醚、可再分散乳胶粉、聚丙烯纤维及其掺量对抗裂抹灰砂浆力学性能、保水性、抗裂性、粘结性以及干缩性能的影响。结果表明：直接利用该粉细砂制备的普通抹灰砂浆,收缩大、韧性低、易开裂。掺入纤维素醚、可再分散性乳胶粉、聚丙烯纤维可以大幅度提高抗裂抹灰砂浆的保水性、粘结性、柔韧性和抗裂性,并且能降低其干燥收缩。当胶砂比为0.5,纤维素醚的掺量为0.15%,可再分散性乳胶粉的掺量为0.8%,聚丙烯纤维掺量为0.9 kg/m3时,制备出的抹灰砂浆具有较高的抗裂性能。     

加气混凝土砌块墙体配套砂浆研究

加气混凝土砌块强度高、保温隔热性好、质量轻、可加工性强、生产能耗低,能同时满足墙材革新和节能要求。但由于加气混凝土的多孔特性使得传统砂浆用于砌筑和抹灰时容易产生开裂、空鼓甚至脱落等问题,这严重阻碍了加气混凝土的广泛应用。针对这些问题,在对复合外加剂的各个组分(塑化剂、可再分散乳胶粉、纤维素醚、聚丙烯纤维等)对砂浆主要力学性能和工作性能(强度、保水性、收缩性等)的影响实验对比后,确定了加气混凝土配套砌筑砂浆、界面砂浆和抹灰砂浆的配比,并与普通砂浆进行了性能对比,效果显著。     

有机物改性的加气混凝土抹面砂浆

通过试验测试橡胶粉及可再分散乳胶粉掺量对加气混凝土抹面砂浆性能的影响。结果表明：橡胶粉的掺入,可降低抹面砂浆的压折强度及粘结强度,提高抹面砂浆的柔韧性及抗冲击性。可再分散乳胶粉可改善橡胶粉与水泥砂浆的结合力．随着掺量增加．抹面砂浆粘结强度明显提高。     

聚丙烯纤维、801胶、海菜粉、粉煤灰对加气混凝土墙体抹面砂浆性能的影响

在确定抹面砂浆胶砂比情况下,通过正交试验和工程验证试验,研究聚丙烯纤维、801胶、海菜粉、粉煤灰对砂浆保水性、密度、抗折强度、抗压强度、粘结强度和收缩率的影响,并给出加气混凝土墙体抹面砂浆配合比设计建议。     

Mixed cement containing fly ash for masonry and plastering work

A class-F fly ash was used in making masonry mortars suitable for brick joints and for plastering. The mortars were made of a locally produced mixed cement and fly ash at 20% and 40% cement replacement with and without the addition of an air entraining agent/plasticiser. The testing programme includes the determination of water demand, relations between water-to-binder ratio and flow, setting time, air content, water retention, compressive strength and flexural strength.The obtained results suggest that fairly coarse grade class-F fly ash can be incorporated into mortars as replacement of the mixed cement for joint and plastering. The main concern is the low water retention which would be minimized by using a better grade/finer fly ash or by incorporation of plasticiser. Mixed cement containing 20–40% fly ash can be used to make Type N or Type S mortars. Furthermore, relations between flow values and water to binder ratio (W/B) of the mixed cement containing fly ash are developed as a practical aid for selection and formulation of mortar for brick construction and rendering/plastering.     

用于加气混凝土轻质砌筑砂浆的影响因素

针对用于加气混凝土的普通砂浆存在容重大,粘结差,易造成砌块建筑产生冷桥的问题,通过正交试验研究了膨胀珍珠岩占砂浆集料的体积比率和三种外加剂(保水剂、胶粉、木纤维)因素对大掺量非等级粉煤灰和煤矸石干混砂浆整体性能的影响,并确定出用于加气混凝土的轻质砌筑砂浆各影响因素的最优化配比掺量。     

加气混凝土砌块砂浆配合比的研究

加气混凝土砌块是一种替代粘土砖的良好墙体材料,但采用传统施工方法施工的墙体极易产生裂缝。本文利用本地区常用的材料,选取了粉煤灰与胶凝材料用量比,水胶比、平均浆体厚度这三个因素,通过正交试验来摸清它们对砂浆的工作性能和力学性能的影响。在初步配合比试验的基础上选取三组工作性能和力学性能良好的配合比,掺入由聚丙烯纤维和海菜粉等组成的添加剂,优化后的专用砂浆的保水性、粘结强度、折压比和粘压比有较大的提高。     

粉煤灰对砂浆性能影响的研究

在砂浆中加入粉煤灰,不但能降低砂浆的成本,而且还能够改善砂浆的施工性能、提高砂浆保温性能。在满足加气混凝土(泡沫混凝土)抹面砂浆粘结强度高、收缩率低的前提下,粉煤灰掺量30%时,所配制的砂浆导热系数为0.1953W/m.K,与加气混凝土(泡沫混凝土)砌块导热系数接近,具有良好的保温效果。     

新型抗裂抹灰砂浆的研制

为了使抹灰砂浆能够适应当前新型墙体材料的要求,针对传统抹灰砂浆施工性能差、保水性差、黏结强度低以及易开裂等缺点,通过研究保水剂、淀粉醚、憎水剂和聚丙烯纤维对抹灰砂浆性能的影响,研制了一种施工性能好、保水性好、收缩率低、黏结强度高、不易开裂的新型抹灰砂浆,并对外加剂的改善机理进行了讨论.     

矿物掺合料对机制砂浆性能影响

研究了磨细石灰石粉、粉煤灰和矿渣掺合料对机制砂砂浆物理力学性能的影响。当矿物掺量由10%向40%递增,结果表明:矿渣试件7d强度下降,28d强度高于基准试件;砂浆流动性提高但保水性降低。粉煤灰试件、石灰石粉试件的7d和28d强度低于基准试件,石灰石粉试件强度降低尤甚;粉煤灰砂浆流动性先升高而后降低,以20%或者30%为拐点,石灰石粉会显著提高砂浆的保水性,但对砂浆强度有不利影响。矿渣与石灰石粉复合制备的砂浆,其稠度、保水性和强度满足工程实际对砂浆的要求,且优于粉煤灰与石灰石粉复合制备的砂浆。     

加气混凝土砌块抹面砂浆憎水性能研究

随着加气混凝土砌块用量的增加,其配套抹面砂浆的应用已经越来越普及,为了和砌块强度相匹配,抹面砂浆抗压强度相对较低,因此容易造成其抗渗性能偏低,吸水率大,导致砌块墙体抗渗性能极低甚至没有抗渗性能,特别是外墙体和卫生间等结构部位的渗漏现象屡见不鲜。本文研究了常见的憎水剂品种和掺量对抹面砂浆抗渗性能的影响,同时分析了憎水剂对砂浆粘结强度的影响。