据TaikabutsuOverseas报道，含氧化铝水泥浇注料正广泛应用于钢铁等高温工业，但其在烘干过程中由于水蒸气的快速蒸发会引起爆裂．造成耐火材料的损毁。研究选用了10种不同类型的水泥（A－J），其A12O3含量为50％～81％，主要的矿物相为CA、CAZ、LI。A，、a－Al。O。等，有效比表面积为0．7～4．7m‘·g－‘。利用不同配料组成的低水泥浇注料和铝尖晶石浇注料，制成十55mm。50mm的试样测试抗爆裂性，制成4Omm。40mm；＜160mm的试样测试养护后和烘干后的强度，并改变养护时间和养护温度。试验结果表明：对于低水泥浇注料，加入氧化铝…     

养护时间对不同结合体系的刚玉基浇注料性能的影响

为了研究养护时间对不同结合体系的刚玉基浇注料性能的影响,以致密电熔刚玉颗粒(粒度有5~3、3~1、≤1 mm)、致密电熔刚玉细粉(粒度≤0.044 mm)、α-Al2O3微粉、硅灰、电熔镁砂细粉(粒度≤0.088 mm)、纯铝酸钙水泥以及工业纯高效分散剂三聚磷酸钠等为主要原料,设计了4种不同结合体系(分别为无水泥、超低水泥、低水泥和水泥结合)的刚玉基浇注料,主要研究了养护时间对浇注料脱模、烘干及分别在1 300和1 600℃煅烧3 h后的常温耐压强度和烧后线变化率的影响。结果表明:无水泥浇注料须养护1 d以上,超低水泥和低水泥浇注料需养护3 d以上才可获得较好的物理性能,水泥浇注料的最佳养护时间为3 d。     

模内养护时间对低水泥刚玉质浇注料性能的影响

研究了模内养护时间对低水泥刚玉质浇注料强度及其他性能的影响,探讨了施工过程中缩短浇注料模内养护时间的可行性。结果表明,当模内养护时间在１２－２４ ｈ之间变化时,模内养护时间对浇注料的干燥及煅烧后的体积密度、显气孔率、耐压强度、抗折强度和永久线变化率均无明显影响,模内养护时间的延长对提高浇注料的抗爆裂性能有一定的促进作用。     

有机纤维汤加剂和养护温度对自流浇注料抗剥落性的影响

研究了聚丙烯纤维添加剂对Al2O390％低水泥自流浇注料在不同养护温度下的抗剥落性的影响；增加纤维量和提高养护温度，提高了显气孔率和平均气孔直径。对试样进行抗剥落性试验，表明常温耐压强度和弹性模量地了变化。发现增加聚丙烯纤维添加量和提高养护温度提高了抗剥落性。     

协同处置城市生活垃圾对水泥窑用耐火材料的侵蚀

为了合理选配水泥窑协同处置垃圾生产线用耐火材料,采用静态坩埚法并借助SEM研究了焚烧城市生活垃圾对水泥窑用耐碱砖、抗剥落高铝砖的侵蚀。结果表明:焚烧城市生活垃圾对水泥窑用耐火材料的侵蚀机制主要为渣渗透和渣侵蚀,焚烧垃圾时产生的含碱、硫、氯等的高温气体和耐火材料发生发应,生成了低熔点的硫酸盐、氯盐以及复合盐,使耐火材料产生反应变质,而反应变质层结构疏松,在热应力的作用下易造成剥落。因此,协同处置垃圾的水泥窑用耐火材料的选配应考虑到材料的抗侵蚀性和抗剥落性等因素,建议分解炉选用抗剥落高铝砖和抗结皮Si C浇注料,而预热器选用高强耐碱砖和高强耐碱浇注料。     

低水泥浇注料的凝固性能与结合剂系统内部相互之间的关系

设计了一个实验过程以便寻找出结合剂内部之间的相互作用对低水泥浇注料的凝固性能（流动减弱和强度）所产生的影响。混合后，被研究的结合剂的特点在于两个放热反应，其动力学与相应的低水泥浇注料的性能有关。短期的反应伴随着浇注料的流动减弱，而长期反应则伴随着水化作用产生的大量沉淀和强度的改善。填充物和外加剂的特性对这些反应的动力学也有所影响。     

有机纤维添加剂和养护温度对自流浇注料抗剥落性的影响

研究了聚丙烯纤维添加剂对Al2O390%低水泥自流浇注料在不同养护温度下的抗剥落性的影响。增加纤维量和提高养护温度,提高了显气孔率和平均气孔直径。对试样进行抗剥落性试验,表明常温耐压强度和弹性模量发生了变化。发现增加聚丙烯纤维添加量和提高养护温度提高了抗剥落性。     

复合节能结构件在水泥窑上的应用

0前言水泥窑很多部位使用不定形耐火材料,特别是在结构复杂的预分解系统内。但新型干法水泥窑温较高、转速较快、结构复杂,水泥厂为了提高产量和生产效率,多采用强化煅烧工艺、提高窑体转速、加大喷煤量等措施,使窑内火焰温度升高、温度波动较大、热应力增加,加上窑载荷增大,碱、氯、硫等有害物质富集,给水泥窑用耐火材料的正常使用带来了严重的挑战。尤其是篦冷机、窑头罩、三次风管弯头、烟室等部位采用的浇注料经常受到损毁,需要停窑检修,严重影响水泥窑运行效率。开发长寿、高效、节能的耐火材料制品,解决水泥窑运行因为浇注料损毁修炉而制约运行效率,成为水泥行业迫切需要的解决的共性难题。     

矾土耐火浇注料性能研究的实验设计

使用实验规划方法研究了低水泥耐火浇注料的制备条件对其使用性能的影响结果。使用正交Blackett-Burman设计,论证了加水量、振动时间、养护条件和煅烧条件对制得的耐火浇注料使用性能(室温下的表观密度、开口气孔率、永久线变化率、杨氏模量、抗折强度和耐压强度)的影响。结果表明,在实验条件下所研究的性能之中,只有搅拌时间是一个可以忽略的因子,它对制备过程中低水泥矾土浇注料的使用性能没有重大影响。     

高性能耐火浇注料新品种

随着建材工业“由大变强、靠新出强”发展战略的实施，水泥工业中新型干法水泥回转窑得到了迅速发展，由于其具有窑温更高、窑速更快、窑系统结构更复杂、碱等挥发性组分侵蚀严重等特性，因此，对耐火材料提出了新的要求。回转窑热负荷的加大，特别是窑口与喷煤管部位，温度高、波动大，并存在物料及二次风的冲刷，原有耐火浇注料由于热震性差、高温热态强度低，使用过程中易产生开裂而剥落。使用周期短，窑口部位为４～６个月，喷煤管部位为２～３个月。新型干法水泥窑的预热器，由于水泥原料中有害杂质碱、氯、硫的循环富集作用，使得预热…     

碳化硅对低水泥结合氧化铝空心球浇注料性能的影响

以3种粒度级别的氧化铝和氧化铝微粉为原料,以铝酸钙水泥为结合剂,采用振动浇注成型的方法制备了低水泥结合氧化铝空心球浇注料。利用耐火材料检测设备和扫描电子显微镜(SEM)研究了加入碳化硅对低水泥氧化铝空心球浇注料性能及微观结构的影响。研究结果表明,适量加入碳化硅对提高该种浇注料的体积密度、常温耐压强度和热震稳定性有利。     

低水泥自流耐火浇注料

简述了加有ＳｉＯ２、Ａｌ２Ｏ３微粉的高铝质低水泥自流浇注料中所涉及的化学过程。研究了ＳｉＯ２、Ａｌ２Ｏ３微粉、高铝水泥含量、加水量对低水泥耐火浇注料物理性能的影响。讨论了分散剂、促凝剂、延迟硬化剂在低水泥自流耐火浇注料中的作用。     

水泥窑用低水泥浇注料性能的研究

以矾土为主要原料,铝酸钙水泥和硅微粉为结合系统,研究了不同热处理温度对水泥窑用低水泥浇注料性能的影响。试样自然干燥24h脱模后,再经110℃烘干24h,分别于300℃、500℃、700℃、900℃、1100℃、1300℃和1500℃热处理3h。检测各温度热处理后试样的体积密度(B.D)、线变化率(P.L.C)、常温抗折强度(M.O.R)、常温耐压强度(C.C.S)、常温耐磨性能以及试样的热膨胀系数和抗热震性能。结果表明,随着热处理温度的提高,水泥窑用低水泥浇注料的体积密度呈现先减小后不变再增大的变化规律;线变化率呈现收缩先增大后减小再增大的变化规律;常温抗折强度和常温耐压强度呈现先增大后减小再增大的变化规律。水泥窑用低水泥浇注料经过1500℃热处理后的磨损量小于经过1300℃热处理后的磨损量。水泥窑用低水泥浇注料具有相对优良的抗热震性能。     

铁水预处理用喷枪浇注料的研制与使用

介绍了宝钢三期工程铁水预处理喷枪浇注料的研制过程及使用情况。选择Al2 O3-SiO2 系材质 ,采用低水泥结合技术 ,通过各种性能的综合研究 ,使喷枪浇注料能适应苛刻的使用条件。研制的喷枪浇注料可替代进口料 ,不仅保证了生产的顺利进行 ,也为宝钢节省了大量外汇。     

高炉出铁沟岔口用超低水泥浇注料预制件的研制

通过对耐火骨料、粉料的选择和级配、超微粉和外加剂的使用、铝酸盐水泥的使用以及水用量等问题的研究,制定了出铁沟耐火浇注料的配制方法。利用该方法配制出超低水泥浇注料,并用其制作出高炉出铁沟岔口用预制件。     

Microwave and conventional treatment of low-cement high-alumina castables with different water to cement ratios; Part I. Drying

The aim of this study was to determine the effect of the microwave and conventional drying method on the strength, porosity and composition of low-cement alumina castables with various water to cement ratios (wcr). High-alumina low-cement castable samples were prepared with different w/c ratios: 0.64, 0.75, 0.82 and 1.13. Changes in wcr were effected through volumetric replacement of cement with 0–0,045-mm tabular alumina having a comparable particle size. Water content in all the composition was constant (4,5%). After curing, the samples were dried conventionally in a laboratory electric drier or in a laboratory microwave drier. After drying open porosity and modulus of rupture were determined. The pore size distribution, pore median and tortuosity of the samples were measured by the mercury porosimetry method. Phase composition was determined using X-ray diffraction. The Rietveld method was used for quantitative analysis. It was found that at low wcr (0.62) the main hydrate formed in the castable was C₃AH₆, which caused a release of a smaller amount of water during the drying process, mainly pore water, resulting in lower open porosity and lower pore size than in the castables with a high wcr (1.13). At a low wcr, the strenght of castable was higher due to a higher amount of hydrates, low porosity and small pore size. On the other hand, at a high wcr, the strength of castable was lower owing to a higher amount of water released in the drying process, which led to loosening the structure of castable. With an increased water-to-cement ratio the degree of CA₂ hydration decreased. The temperature rise due to cement hydration probably influenced the kinetics of this process.     

耐火材料用有机-无机复合结合剂的研制

以水泥为结合剂的浇注料中含有CaO,在烧成过程中能够生成低共熔相而影响了其高温性能。为了提高浇注料的高温使用性能,需要在保证浇注料具有一定的常温强度的基础上,研制低水泥或者无水泥的新型结合剂来替代水泥结合剂。以丙烯酰胺体系为基础,探讨了丙烯酰胺系有机-无机结合剂在矾土基浇注料中的实际使用效果。结果表明,浇注料在110℃烘干后的体积密度、显气孔率、耐压和抗折强度等常温性能良好,尤其是抗折强度得到很大的提高。在不同高温烧成后,有机结合剂的浇注料性能得到提高。     

细粉总量对低水泥浇注料性能的影响

对低水泥浇注料进行了降低细粉总量的研究，结果表明：对1级矾土熟料而言，细粉总量降至21％仍能保证成型性能，其他性能也能保持较高的水平，适当地降低低水泥浇注料的细粉总量是可行的。     

低碱高硅率高铁水泥的研发与生产实践

通过优选碱含量低的原材料、采用高硅率生料配料、改进熟料煅烧工艺操作、合理控制水泥粉磨指标,研发生产了水泥碱含量小于0.40%、熟料硅率为3.5的低碱高硅率高铁水泥,满足了国家重点工程高铁建设项目需要。     

Thermodynamic evaluation and properties of refractory materials for steel ladle purging plugs in the system Al2O3-MgO-CaO

The influence of iron oxide in the phase relationships of Al₂O₃-MgO-CaO and Al₂O₃-MgO purging plug refractory material has been studied by the thermodynamic analysis tool FactSage. Results showed that the system without CaO to be advantageous on the onset temperature of liquid phase, and on the liquid content at defined chemical composition and temperature. Therefore, CaO negatively influences the iron-rich slag resistance of the purging plug material. Analysis of used purging plugs proved the thermodynamic results. They showed that spinel solid solution and calcium hexaluminate as stable phases were formed in the reaction with iron oxide slag.Corundum-spinel castables with and without calcium aluminate cement were investigated in the laboratory to compare the relevant technical properties. In the cement bonded castable, the curing and drying strength are increased by increasing the cement content. However high cement addition requires higher water demand, which results in higher open porosity and a lower hot modulus of rupture (HMoR). In the CaO-free, no-cement castable with hydratable alumina binder, the water demand is slightly higher when compared to the ultra-low cement castable. However, the curing and drying strength are still slightly higher for the no-cement castable. As there is no significant difference in HMoR with various hydratable alumina binder additions, low dosage of such binder in the range of two to four percent is normally recommended to avoid excessive water addition. Cement bonded castables (with CaO) show some advantages to the no-cement castable (non-CaO) regarding HMoR, however the no-cement castable could have advantages regarding the iron-rich slag resistance and thermal shock resistance.