ABS/NBR TPV的压缩Mullins效应及其可逆回复研究

采用动态硫化法制备了丙烯腈-丁二烯-苯乙烯三元共聚物(ABS)/丁腈橡胶(NBR)热塑性硫化胶(TPV),研究了其压缩Mullins效应及其可逆回复,对其微观结构进行表征,并探讨了压缩Mullins效应的产生及可逆回复机制。结果表明：在TPV的单轴循环压缩过程中存在明显的Mullins效应,且同一压缩应变下,最大压缩应力、内耗和tanδ均在第一次加载-卸载循环中达到最大值,在第二次循环压缩时发生显著下降,但此后趋于缓慢下降;提高压缩后样品的热处理温度,二次循环压缩时的最大压缩应力的回复程度增大,且110 ₀C热处理时压缩Mullins效应的回复最佳;FE-SEM研究表明,尺寸为10~15 μm的NBR硫化胶粒子均匀地分散在刻蚀样品表面。     

EAA/NBR TPV压缩应力松弛可逆回复机制及模型构建

采用动态硫化法制备了乙烯-丙烯酸共聚物/丁腈橡胶热塑性硫化胶(EAA/NBR TPV),系统研究了其力学性能、微观结构、压缩应力松弛及可逆回复行为,探讨了可逆回复机制并构建了数学模型,还研究了橡塑比对可逆回复不同阶段应力松弛时间的影响。结果表明,当EAA/NBR质量比为40/60时,TPV综合性能最佳且应力松弛行为主要由EAA连续相提供,此时NBR分散相对应力松弛行为的影响较小;升高热处理温度或延长热处理时间均可显著加快TPV压缩应力松弛可逆回复程度;当热处理温度接近EAA树脂相熔点时,TPV可逆回复程度接近100%。     

ABS/NBR热塑性硫化胶压缩Mullins效应及其可逆恢复的研究

研究丙烯腈-丁二烯-苯乙烯三元共聚物(ABS)/丁腈橡胶(NBR)热塑性硫化胶(TPV)的压缩Mullins效应及其可逆恢复。结果表明:NBR粒子均匀分散在TPV表面,其粒径为10~15μm;在循环单轴压缩过程中TPV出现明显Mullins效应,且同一压缩应变下,TPV的最大压缩应力、内耗和损耗因子(tanδ)均在第1次加载-卸载循环时达到最大,在第2次加载-卸载循环时显著下降,此后呈缓慢下降趋势;随着压缩次数增加,TPV的瞬时残余形变和应力软化因子(Ds)增大;随着压缩应变增大,TPV的最大压缩应力、瞬时残余形变、内耗和tanδ均显著增大,Ds减小;随着热处理温度升高,TPV在第2次循环压缩时最大压缩应力的恢复程度增大,热处理温度为110℃时,TPV压缩Mullins效应的恢复效果最佳。     

HIPS/HVPBR热塑性硫化胶压缩永久变形可逆回复的模型及机制

采用动态硫化法制备了高抗冲聚苯乙烯(HIPS)/高乙烯基聚丁二烯(HVPBR)热塑性硫化胶(TPV),研究了橡塑比和热处理温度对压缩永久变形可逆回复的影响,探讨了可逆回复机制并构建了数学模型。结果表明,提高橡塑比和热处理温度,压缩永久变形的可逆回复程度和回复速度明显提高;热处理温度接近基体Tg时,体系的压缩永久变形几乎完全可逆;基于可逆回复过程,探讨压缩永久变形的可逆回复机制,并构建了其数学模型,进而探讨了橡塑比和热处理温度对可逆回复各阶段松弛时间的影响。     

丁腈橡胶/乙烯-乙酸乙烯共聚物热塑性硫化胶的Mullins效应形成机制及可逆回复

采用动态硫化法制备了丁腈橡胶(NBR)/乙烯-乙酸乙烯共聚物(EVA)热塑性硫化胶(TPV),考察了其压缩Mullins效应及其在不同温度下的可逆回复行为,并与EVA及NBR静态硫化胶进行了对比。结果表明,在单轴循环压缩过程中NBR/EVA TPV及EVA均存在明显的Mullins效应,在一定压缩应变下,第1次加载-卸载的最大压缩应力和内耗出现最大值,第2次循环压缩时则显著降低,之后下降趋势减缓。升高热处理温度,第2次单轴循环压缩时压缩Mullins效应的回复程度增大。在NBR静态硫化胶的单轴循环压缩过程中未观察到明显的Mullins效应。     

EVA/NBR TPV压缩Mullins效应的研究

采用动态硫化法制备了乙烯-醋酸乙烯共聚物(EVA)/丁腈橡胶(NBR)热塑性硫化胶(TPV),系统研究了EVA/NBR TPV压缩Mullins效应。结果表明,随着EVA/NBR共混比及压缩应变的增大,TPV压缩Mullins行为趋于显著;当压缩应变一定时,首次循环加载-卸载过程中最大压缩应力、内耗和tanδ均达到最大值,而第2次加载-卸载过程中均发生大幅下降,之后下降趋势逐渐减弱。在相同应变下,EVA/NBR共混比60/40的TPV最大压缩应力、残余变形、内耗、应力软化因子和tanδ均大于共混比40/60的TPV,变化幅度较为明显。     

ABS/PLA合金的制备及力学性能研究

研究了丙烯腈-丁二烯-苯乙烯共聚物/聚乳酸(ABS/PLA)合金的不同配比对其性能的影响,并从其中找出最优配比,然后再对最优配比的合金材料进行性能优化,从而提高其力学性能,达到在既保持生物、环保、低碳的同时,还能减少原有性能损失甚至提高原有性能的目的。研究结果表明:当ABS/PLA为9:1时,合金的综合性能最佳;加入复合增韧剂后,合金材料的力学性能明显提高,其缺口冲击强度从5 k J/m2提高到16 k J/m2。     

ABS/SBR共混体系的动态硫化技术及工艺研究

研究了动态硫化技术对丙烯腈-丁二烯-苯乙烯共聚物/丁苯橡胶(ABS/SBR)共混物性能的影响,讨论了硫化工艺条件及不同硫化剂用量对ABS/SBR共混体系的力学性能、耐热性及加工流动性的影响.结果表明,当硫化温度为180℃,螺杆转速为120 r/min时,体系混炼效果最好;在一定范围内,随着硫化剂用量的增加,体系的力学性能逐渐增强,当硫磺用量为0.6 phr时,体系的综合性能最佳.     

ABS/PS共混改性研究

采用在材料熔融挤出共混过程中提高双螺杆挤出机螺杆转速的方法,研究了较高螺杆转速条件下双螺杆挤出机的机械剪切应力和弹性体的种类、用量等因素对丙烯腈-丁二烯-苯乙烯共聚物(ABS)/聚苯乙烯(PS)共混材料力学性能和加工流动性能的影响。结果表明,双螺杆挤出机的高剪切应力可促进分散相颗粒的分散和界面结合力的增强,引起共混材料力学性能和熔体流动速率的改善。丁腈橡胶(NBR)粉末对ABS/PS共混材料具有增容增韧作用,挤出共混温度为220℃,螺杆转速在720 r/min,NBR粉末质量分数为10%时,ABS/PS共混材料的缺口冲击强度为16.4 kJ/m2,比改性前约提高1.6倍,达到ABS树脂冲击韧性的指标,并保持了良好的加工流动性。     

基于ABS/废旧NBR胶粉热塑性弹性体的制备及性能

采用熔融共混法制备了丙烯腈-丁二烯-苯乙烯三元共聚物(ABS)/废旧NBR胶粉(WNBRP)复合体系,以氯化聚乙烯(CPE)为增容剂改善其界面相容性,研究了CPE用量对其力学性能和微观结构的影响。结果表明,CPE可显著改善ABS/WNBRP复合体系的综合性能,且CPE含量为18份时,综合力学性能最佳;基体中CPE的存在,一方面可以增强ABS与WNBRP的界面相容性,另一方面可以提高基体ABS的塑性变形能力;FE-SEM研究表明,与ABS/WNBRP复合体系相比,增容TPE的断面形貌较为平整,界面结合较好,力学性能提升显著。     

ABS/NBR热塑性弹性体的制备

采用动态硫化法制备了丙烯腈-T二-苯乙烯3元共聚物／丁腈橡胶（ABS／NBR）热塑性弹性体（TPV），研究了硫化剂种类及用量、NBR中丙烯腈含量、橡塑比、增塑剂等对TPV力学性能的影响。结果表明采用丙烯腈较高的NBR制备的TPV综合性能优良，在试验范围内硫黄用量1．5份为宜。适量的增塑剂可以降低TPV硬度，但会导致拉伸性能下降。实验表明，TPV重复加工性能较好。     

Effect of dynamic vulcanization on properties and morphology of nylon/SAN/NBR blends: A new compatibilization method of nylon/ABS blends

Dynamically vulcanized blends of nylon, styrene–acrylonitrile copolymer (SAN), and nitrile–butadiene rubber (NBR) were examined for mechanical properties, Shore D hardness, Vicat softening temperature, impact process, and phase morphology. The effect of a curing system such as phenolic formaldehyde resins (PF), dicumylperoxide (DCP), and a sulfur system on the mechanical properties of the nylon/SAN/NBR blends was studied, and dynamic vulcanization with a PF system was found to lead to outstanding toughness of the blends. The effect of PF content on the mechanical properties, Shore D hardness, and heat resistance of the nylon/SAN/NBR blends was also investigated. With increasing PF content the notched‐impact strength and Vicat softening temperature (VST) of the nylon/SAN/NBR (50/25/25) blends evidently improved, but tensile strength and Shore D hardness of the blends changed slightly. It can be concluded that the nylon/SAN/NBR (50/25/25) blends dynamically vulcanized by high‐content PF can attain excellent comprehensive mechanical properties, especially supertoughness, at room temperature. SEM was used to investigate the effect of dynamic vulcanization on disperse‐phase particle size, particle size distribution, and phase morphology. It was obvious that disperse‐phase particle size decreased with an increasing PF content. Thermal behavior and miscibility of dynamically vulcanized nylon/SAN/NBR with PF were investigated by DMTA. © 2003 Wiley Periodicals, Inc. J Appl Polym Sci 87: 2057–2062, 2003     

ABS/石墨/NBR导热复合材料性能的研究

采用熔融共混法制备丙烯腈-丁二烯-苯乙烯共聚物(ABS)/石墨/丁腈橡胶(NBR)导热复合材料,通过热常数分析仪、同步热分析仪、扫描电子显微镜、力学性能测试等手段研究了NBR、ABS高胶粉及石墨(G)的添加量对ABS复合材料导热性能及力学性能的影响。结果表明,ABS高胶粉和NBR均能明显提高ABS的热导率和缺口冲击强度,但是丁腈胶粉的改性效果优于高胶粉。以NBR作为ABS复合材料的增韧剂,随着石墨含量的增大,增韧效果下降,ABS复合材料的热导率提高到纯ABS的5倍,热分解温度提高40℃左右,热膨胀系数下降。当ABS/G/NBR复合材料的质量比为60/15/25时,其热导率为纯ABS的2倍,缺口冲击强度达21.8 kJ/m2,明显高于纯ABS(2.6kJ/m2)。     

丁腈橡胶/聚甲醛共混物动态硫化的研究

采用２４０２树脂硫化体系以动态硫化方法制备了了腈橡胶（ＮＢＲ）／聚甲醛（ＰＯＭ）热塑性弹性体。研究了丙烯睛含量、硫化体系、橡塑比等对共混物性能的影响。实验结果表明：ＮＢＲ中丙烯睛含量增加，共混物的拉伸强度显著提高；随着ＰＯＭ用量增加，共混物的强度略有提高，表观粘度降低，加工性能改善，电性能、老化性能和耐油性能均得到明显提高。ＤＳＣ分析表明，共混物中ＰＯＭ的结晶度明显比纯ＰＯＭ低，熔点也有所下降。     

NBR／HDPE热塑弹性体的形态与性能

用动态硫化方法制备也ＮＢＲ／ＨＤＰＥ共混型热塑弹性体,电子显微镜研究其形态表明,尽管ＮＢＲ的用量超过了ＨＤＰＥ,但ＮＢＲ仍为分散相,ＨＤＰＥ为连续相,使该材料表现出热塑性。应力－应变性能和动态力学研究表明,该产品在室浊下表现出良好的弹性行为,且力学性能较好,但永久变形较大。     

NBR/聚丙烯酸酯橡胶共混物动态硫化的研究

ＮＢＲ的溴化酚醛树脂硫化体系和聚丙烯酸酯橡胶（ＡＣＭ）的硫化剂ＡＢＳ会相互干扰，产生硫化不相容性，导致ＮＢＲ，ＡＣＭ和ＮＢＲ／ＡＣＭ共混物性能下降。通过在ＮＢＲ／ＡＣＭ共混物中加入溴化酚醛树脂对ＮＢＲ进行动态硫化，然后加入ＡＢＳ对ＡＣＭ进行静态硫化的方法，能够较好地解决这两种不相容硫化体系的相容性问题，所得到的共混物表现出良好的物理性能，且优于相应的静态硫化共混物。同时考察了ＮＢＲ／ＡＣＭ的共混比对共混物性能的影响。     

EVM/NBR动态硫化共混物性能的研究

研究了橡胶型乙烯醋酸乙烯酯共聚物（ＥＶＭ）／ＮＢＲ共混比、硫黄和叔丁基酚醛树脂（２４０２树脂）硫化体系对共混物性能的影响，并对比了动态硫化和静态硫化共混物在性能上的差异。试验结果表明，ＥＶＭ／ＮＢＲ共混比显著影响共混物的力学性能，而采用ＮＢＲ预先动态硫化的方法后，共混物胶料的挤出口型膨胀率明显减小，老化性能得到改善，同时减弱了硫黄和２４０２树脂等硫化体系对ＥＶＭ硫化的影响，使多种硫化体系可以共存于共混物中。ＤＳＣ分析表明ＥＶＭ／ＮＢＲ动态硫化共混物只有一个玻璃化温度，且介于ＥＶＭ和ＮＢＲ之间，说明ＥＶＭ和ＮＢＲ具有良好的相容性。     

动态硫化制备PA/SAN/NBR合金冲击性能的研究

采用酚醛树脂（PF）、DCP和硫磺等硫化体系对PA／SAN／NBR共混体系进行动态硫化,研究了该共混体系的缺口冲击强度、冲击行为和分散相形态。结果发现,PF比其它硫化体系更有效,可制得超韧的PA／SAN／NBR（50／25／25）合金;SEM照片表明,随着PF用量增加,共混体系中分散相粒子变小,形态变规则,动态硫化体系的相容性变好。