氢化丁腈橡胶耐热配方的优选研究

研究了硫化剂DCP用量、助硫化剂TAIC用量和耐热助剂种类及用量对氢化丁腈橡胶耐热空气老化性能的影响.结果表明,当硫化剂DCP用量为4.5份、助硫化剂TAIC用量为3份并加入15份甲基丙烯酸镁时,氢化丁腈橡胶耐热空气老化性能最佳;175℃×96 h热空气老化后,氢化丁腈橡胶拉伸强度变化率仅为-2.0％,拉断伸长率变化率...     

正交设计法优化三元乙丙橡胶/丙烯酸酯橡胶并用胶的硫化体系

采用正交设计法研究硫化剂DCP/TCY并用硫化体系中硫化剂和促进剂用量对三元乙丙橡胶(EPDM)/丙烯酸酯橡胶(ACM)并用胶物理性能的影响。结果表明:硫黄和氧化锌用量对EPDM/ACM并用胶拉伸强度有显著影响,硫化剂DCP用量对拉伸强度有一定影响;硫化剂DCP、TCY和硫黄用量均对撕裂强度有显著影响,氧化锌用量对撕裂强度有一定影响;硫化剂DCP、促进剂DM和氧化锌用量对并用胶的耐热老化性能有影响;在正交设计试验范围内,并用胶综合性能较好的优化配方为:硫化剂DCP 3,硫化剂TCY 2,硫黄0.3,促进剂DM 0.25,氧化锌5。     

硫化体系对氢化丁腈橡胶/氯丁橡胶并用胶性能的影响

研究硫化体系对氢化丁腈橡胶(HNBR)/氯丁橡胶(CR)(并用比70/30)并用胶硫化特性、物理性能和耐热老化性能的影响。结果表明:采用硫化剂DCP/助硫化剂TAIC硫化体系时,HNBR/CR并用胶的焦烧时间较长,拉断伸长率较大,拉断永久变形较小,耐热老化性能较好;当硫化剂DCP用量为5份、助硫化剂TAIC用量为3份时,并用胶的硫化速率较大,加工安全性、耐油性能、综合物理性能和耐热老化性能较好。     

茂金属聚烯烃弹性体/聚丙烯热塑性硫化胶的制备与性能研究

采用双螺杆挤出机制备茂金属聚烯烃弹性体(POE)/聚丙烯(PP)热塑性硫化胶(TPV),考察硫化剂双25用量、助硫化剂TAIC用量和POE/PP共混比对TPV微观结构、动态力学性能、物理性能和耐热空气老化性能的影响。结果表明,硫化剂双25用量为2份、助硫化剂TAIC用量为5份、POE/PP共混比为60/40~70/30时,在保证POE/PP TPV顺利挤出的前提下,POE/PP TPV的综合性能较优。     

过氧化物对246型氟橡胶压缩永久变形的影响

研究过氧化物品种、硫化剂DCP和助交联剂TAIC用量以及硫化剂种类对氟橡胶性能的影响.结果表明:在过氧化物BIPB,DBPMH,DCP,DCBP和BPO中,DCP硫化的氟橡胶综合物理性能较好,压缩永久变形较小;随着硫化剂DCP用量的增大,氟橡胶的压缩永久变形呈减小趋势,硫化剂DCP用量为3份时,氟橡胶的物理性能较好,压缩永久变形较小;随着助交联剂TAIC用量的增大,氟橡胶的压缩永久变形呈减小趋势,助交联剂TAIC用量为5份时,氟橡胶的压缩永久变形较小;硫化剂DCP硫化的氟橡胶耐压缩永久变形性能优于3#硫化剂,但不如双酚AF/BPP.     

硫化剂BIPB硫化氢化丁腈橡胶性能的研究

研究硫化剂BIPB(1,4-双叔丁基过氧化二异丙基苯)用量对氢化丁腈橡胶性能的影响。结果表明:随着硫化剂BIPB用量的增大,混炼胶的焦烧时间和正硫化时间均缩短,交联效率提高;硫化胶的拉伸强度、耐热性能、耐油性能和压缩永久变形性能均提高。硫化剂BIPB用量为4份时,硫化胶的综合物理性能达到最优。     

苯加氢预反应器催化剂用硫化剂的选择

通过对几种钻钼催化剂用硫化剂性能的对比，为苯加氢预反应器催化剂选定二甲基二硫（DMDS）为硫化剂。     

硫化体系对SBR/NR并用胶性能的影响

研究硫化体系对丁苯橡胶(SBR)/天然橡胶(NR)并用胶性能的影响。结果表明:当硫化体系的总有效硫质量份为0.86时,在硫化剂S-80用量为0.8份、促进剂TMTD用量为0.4份、硫化剂DTDM-80用量为1.5份时,并用胶的综合性能最佳,适用于大多数橡胶制品的生产;在促进剂TMTD的用量为0.4份时,硫化剂S-80和DTDM-80的配比对并用胶的物理性能和耐热老化性能均有很大影响,通过调整硫化剂S-80和DTDM-80的用量,可以得到适用于不同场合的、综合性能优异的SBR/NR并用胶。     

氢化丁腈橡胶过氧化物硫化体系的研究

研究硫化剂DCP和助交联剂TAC用量对氢化丁腈橡胶（HNBR）胶料性能的影响。结果表明：当助交联剂TAC用量为3份时,随着硫化剂DCP用量的增大,HNBR胶料的焦烧时间和正硫化时间缩短,硫化胶的物理性能提高,压缩永久变形明显减小,耐热氧老化性能有所改善;当硫化剂DCP用量为4份时,随着助交联剂TAC用量的增大,HNBR胶料的门尼粘度降低,硫化胶的定伸应力增大,压缩永久变形减小,耐热氧老化性能变化不大;硫化剂DCP和助交联剂TAC用量对HNBR硫化胶浸油后的物理性能有一定影响,但对体积膨胀率影响不大。     

助交联剂PDM和硫黄用量对CM/EPDM并用胶性能的影响

试验研究在过氧化物硫化体系下助交联剂N,N'-间亚苯基双马来酰亚胺(PDM)和硫黄用量对氯化聚乙烯橡胶(CM)/EPDM并用胶性能的影响.结果表明:在硫化剂DCP/助交联剂PDM硫化体系下,当硫化剂DCP用量为3份、助交联剂PDM用量为1.5～2份时,CM/EPDM并用胶的综合性能较好;在硫化剂DCP/硫黄硫化体系下,...     

ACM/FKM并用胶耐热性和耐油性研究

笔者是以ACM和FKM为主要原料研究耐热性和耐油性的材料，对其合成所采用的配合剂（如填充剂、加工助剂、加工助剂、防老剂、吸酸剂和硫化促进剂）、二段硫化条件及硫化条件对样品的性能（如耐热性、耐油性和压缩永久变形）进行了探讨，实验结果显示：ACM/FKM合金其耐热性接近氟橡胶，而耐油性接近ACM。     

New type of phenolic resin: Curing reaction of phenol‐novolac based benzoxazine with bisoxazoline or epoxy resin using latent curing agent and the properties of the cured resin

In this study, we aimed to reduce the cure time, and to lower the cure temperature of the benzoxazine compound. Therefore, curing reaction of benzoxazine with bisoxazoline or epoxy resin using the latent curing agent and the properties of the cured resins were investigated. The cure behavior of benzoxazine with bisoxazoline or epoxy resin using the latent curing agent was monitored by differential scanning calorimetry and measurements for storage modulus (G′). The properties of the cured resin were estimated by mechanical properties, electrical insulation, water resistance, heat resistance, and flame resistance. As a result, it was confirmed that by using the latent curing agent, cure time of benzoxazine and bisoxazoline or epoxy resin was reduced, and cure temperature was lowered. And it was found that the curing reaction using phenol‐novolac based benzoxazine (Na) as the benzoxazine compound could proceed more rapidly than that using bisphenol‐A based benzoxazine (Ba) as the benzoxazine compound. However, the cured resins from Ba and bisoxazoline or epoxy resin using the latent curing agent showed good heat resistance, flame resistance, and mechanical properties compared with those from Na and bisoxazoline or epoxy resin using the latent curing agent. © 2009 Wiley Periodicals, Inc. J Appl Polym Sci, 2009     

Glass fiber‐reinforced composite based on benzoxazine resin

In this study, we aimed to prepare and characterize glass fiber‐reinforced composites (GFRP) based on benzoxazine resins. Therefore, the molten resin from benzoxazine and bisoxazoline with the latent curing agent was used as the matrix resin, and the properties of GFRP based on the molten resins were investigated. The properties of GFRP were estimated by mechanical properties, heat resistance, and flame resistance. As a result, it was found that GFRP based on the molten resins from benzoxazine and bisoxazoline with the latent curing agent showed good heat resistance, flame resistance, and mechanical properties compared with those of the conventional GFRP. © 2009 Wiley Periodicals, Inc. J Appl Polym Sci, 2009     

水性环氧树脂固化剂的制备及其与乳液相容性的研究

以液态环氧树脂E-51和乙二胺为原料,成功制得一种水性环氧固化剂,并用冰醋酸中和成盐。通过控制冰醋酸的加量,调节产物的亲水亲油值,使其能与自制的水性环氧树脂乳液复配制备环氧树脂涂料;并研究了固化剂与乳液的相容性。采用FT-IR、 ¹H-NMR、环氧值表征固化剂结构。测试了涂膜的动态力学性能、热力学性能、平衡吸水率、耐酸碱性、铅笔硬度等。结果表明:当中和度为50%时,涂膜的力学性能、耐水性、耐酸碱性、硬度均较好。     

共混比对ACM／FKM共混胶性能的影响

采用硫化剂TCY为共硫化剂,研究了共混比对丙烯酸酯橡胶／氟橡胶共混胶的硫化特性、力学性能、耐热老化性能和耐油性能的影响。结果表明：TCY可以同时硫化两种橡胶;ACM／FKM共混比为20／80时．硫化胶具有较好综合力学性能和耐热老化性能;随着ACM用量的增加,硫化胶耐油性能逐渐下降。     

常温固化氟碳涂料的研究

以三氟氯乙烯-乙烯基化合物共聚物（亦称FEVE树脂）为基料,异氰酸酯HDI三聚体为固化剂制成常温固化型双组分氟碳涂料。该涂料具有一般氟树脂涂料的超长耐候性和耐温性、优良的耐化学介质腐蚀性、卓越的防污染、良好的机械性能以及品位典雅的装饰性能,同时具有一般涂料的溶解性、可常温固化性等。分析讨论了树脂的氟含量、主要助剂、固化剂、溶剂的选用对涂料主要性能的影响。     

多功能交联剂WY9188、HV-268、WK901对TBR胎面胶性能的影响

本文主要研究了多功能交联剂WY9188、HV-268、WK901对TBR胎面胶性能的影响。结果表明,多功能交联剂的加入一定程度上可改善胶料的抗硫化返原性能、物理机械性能、滚动阻力以及磨耗性能,其中,WY9188作为一种新型的多功能交联剂具有较为突出的综合优势,在填加量为0.5phr时胶料具有较好的力学性能并且能很好地平衡轮胎抗湿滑性、滚动阻力和磨耗特性。     

氟橡胶/氯醚橡胶并用胶的加工性能与硫化性能

氟橡胶(FKM)具有耐高温、耐油及耐多种化学药品侵蚀的特点,但加工性能不好,本文通过氟橡胶与氯醚橡胶(CO)并用改性,结果表明,CO的加入改善了FKM的加工性能,当CO并用份数少于40份时,FKM为连续相,CO超过40份时,CO转变为连续相。FKM/CO并用胶需用双硫化体系硫化,当FKM采用AF/BPP硫化时,CO采用NA-22/MgO或TCY/MgO/CaCO3硫化体系,并用胶有较好的硫化效果。     

SW861抗皱整理剂的研制和应用

论述了ＳＷ８６１抗皱整理剂的合成、性能和使用条件．该整理剂系以新型的高分子脲醛、聚丙烯酸酯、有机硅酮体为主体的多功能抗皱整理剂，特别是真丝织物经ＳＷ８６１抗皱整理剂整理后，有在不影响其强力伸长的条件下，提高织物的抗皱弹性和耐磨性．     

具有早期耐水汽性水性木器涂料的研制

开发了一种早期耐水汽性良好的单组分水性木器涂料,讨论了乳液的选择、成膜助剂的复配以及消光剂、手感助剂的选择搭配对涂料性能的影响。实验发现:以丙烯酸乳液、亲水型和憎水型搭配的成膜助剂组合、微粉化有机改性聚合物消光剂与有机硅类型的手感助剂制备的水性木器涂料涂膜具有较好的早期耐水汽性。该涂料产品适用于家庭涂装市场中消费者对浴室门等一些特殊部位的涂装应用场合,并已取得良好效果。