The Electrical Resistivity of Cement Paste Incorporated with Retarder

1　IntroductionThefunctionoftheretarderistooffsetthesettingtimeofcement basedmaterials .Thus ,itdelaysboththeinitialsettingandfinalsetting .Thecommonmethodtode terminethesettingtimesadoptsthepenetrationresis tance .Theindirectmethodistousetheelectricalresis tivity[1,2 ] tomeasurecementhydrationcurveandthentocomparewiththesettingtime .Previousresearchersusedtheelectrodestomeasuretheelectricalresistivitythatwillcausethecontactproblemsbetweenthecement basedma terialsandelectrodes .Inthispaper ,a…     

Early age compressive strength of pastes by electrical resistivity method and maturity method

The compressive strength development of Portland cement pastes was investigated by the electrical resistivity method and the maturity method. The experiments were carried out on the cement pastes with different water-cement ratios at different curing temperatures. The results show that the application of the maturity method has limitation to obtain the strength. It is found that both of the compressive strength and the electrical resistivity follow hyperbolic trend for all the mixes. The hyperbolic equation of each mix is obtained to estimate the ultimate resistivity value which can probably be reached. The relationship between electrical resistivity and compressive strength of the cement pastes is established based on the test results and interpreted by the empirical Archie equation and a strength-porosity equation. The relationship between the electrical resistivity after temperature correction and the compressive strength was linear and independent of curing temperature and water-cement ratio.     

再生砖骨料混凝土架构模型试验研究

通过试验研究水灰质量比、粒径级配、再生砖骨料和砂体积分数对混凝土抗压强度的影响以及灰砂质量比对水泥石抗压强度的影响,分析骨浆体积比、灰砂质量比、再生砖骨料和砂体积分数对混凝土架构贡献强度的影响. 结果表明,再生砖骨料混凝土的抗压强度随着水灰质量比的减小而增大,当骨料粒径为19~26.5 mm时抗压强度达到最大值;当再生砖骨料体积分数为30%~43.2%时,混凝土抗压强度和再生砖骨料构架贡献强度都随着再生砖骨料体积分数的增大而增大,且都随着砂体积分数的增大而增大;当灰砂质量比为0.33~1.33时,水泥砂浆试件的抗压强度随着灰砂质量比的增大而增大;当再生砖骨料体积分数为40%和43.2%时,灰砂质量比与再生砖骨料架构贡献强度以及骨浆体积比与再生砖骨料架构贡献强度均高度线性相关;再生砖骨料架构贡献强度高于混凝土强度,主要集中在再生砖骨料体积分数为40%~43.2%,特别是再生砖骨料体积分数为43.2%、砂体积分数为18%~26%.     

再生混凝土基本力学性能试验分析

进行了再生混凝土配合比设计,完成了再生混凝土基本力学性能相关试验,并以天然骨料混凝土作为基准进行对比,主要研究了再生混凝土的立方体抗压强度、立方体劈裂抗拉强度、抗折强度的影响因素及变化规律。通过试验数据的统计回归,建立了再生混凝土抗压强度公式,给出了再生混凝土各项强度指标之间关系式。     

自密实再生骨料混凝土不同龄期的力学性能

为了分析自密实再生骨料混凝土(RA-SCC)不同养护龄期的力学性能,并比较自密实再生骨料混凝土(RA-SCC)与天然骨料混凝土(NA-C)、自密实天然骨料混凝土(NA-SCC)的力学性能差异,开展了以养护龄期、混凝土强度、混凝土类型为参数的立方体抗压强度、劈裂抗拉强度试验研究.结果表明:RA-SCC与NA-C、NA-SCC的7 d强度发展速率基本一致,但其56和90 d的强度发展速率则显著高于NA-C,略高于NA-SCC; 28 d劈裂抗拉强度比NA-C降低了约38. 3%～56. 1%,比NA-SCC降低了约17. 5%～21. 3%; RA-SCC的脆性特征较NA-C和NA-SCC更为明显.     

骨料含量对混凝土拉伸徐变等性能影响的试验研究

通过试验研究骨料含量对混凝土抗压强度、劈裂抗拉强度和自收缩的影响,结果表明:混凝土的抗压强度和劈裂抗拉强度在1d龄期时,受骨料含量的影响较小;骨料含量在55%~70%的范围内,混凝土3,7,14,28d龄期时的抗压强度和劈裂抗拉在随着骨料含量的增加而逐渐增加,骨料含量在70%增加到75%时,混凝土的抗压强度和劈裂抗拉强度随着骨料含量的增加而逐渐减小;混凝土的拉伸徐变的变形随骨料含量的增加而增大;混凝土的自收缩随着骨料含量的增加而逐渐减小。     

C30再生粗骨料混凝土和易性和抗压强度研究

以砖混结构建筑拆卸下来的混凝土块为原材料制备C30再生粗骨料混凝土,利用正交设计方法,研究了再生粗骨料取代率、水灰比、砂率对再生混凝土28d抗压强度及和易性的影响。结果表明再生粗骨料取代率是影响混凝土28d抗压强度及和易性的最主要因素;随着再生粗骨料取代率的增加,强度与和易性均下降;使再生粗骨料取代率为60％,水灰比为0．5,砂率为36％,通过合理的配合比可以配制出28d强度达到46．3MPa的混凝土。     

自密实再生骨料混凝土的基本力学性能

为了揭示以100%再生骨料作为粗骨料的自密实再生骨料混凝土(RA-SCC)的基本力学性能,以及比较其与天然骨料混凝土(NA-C)、天然骨料自密实混凝土(NA-SCC)之间的力学性能差异,进行了混凝土抗压强度等级为C30～C50的力学试验研究.结果表明:与NA-C和NA-SCC相比,RA-SCC的拉压比更小、脆性更大,而棱柱体强度与抗压强度的比值略有提高; RA-SCC的抗折强度与抗压强度的比值与NA-SCC基本相同,但显著低于NA-C; RA-SCC的弹性模量小于NA-C和NA-SCC.     

废砖骨料对再生混凝土抗压与收缩性能的影响

以废砖粗骨料的等体积取代率为变化因素,在分析预吸水处理与裹浆处理条件下,废砖粗骨料等体积取代废弃混凝土粗骨料对再生混凝土抗压强度影响的基础上,着重探讨了废砖粗骨料体积取代率对再生混凝土收缩变形性能的影响。研究结果表明,等体积取代率为25%时,预吸水处理与裹浆处理均可最有效地降低再生混凝土的收缩变形,而对再生混凝土抗压强度却没有明显的降低作用。等体积取代率为25%时,预吸水处理下再生混凝土的抗收缩变形性能优于裹浆处理,而裹浆处理下再生混凝土抗压强度高于预吸水处理。     

废旧塑料改性砂浆力学性能研究

用片状和圆柱状塑料骨料等取代砂浆中的砂子,研究塑料骨料取代量、形状对水泥砂浆流动度、抗弯强度、抗压强度、抗弯挠度和断裂韧性的影响.结果表明,随片状塑料骨料掺量增加,砂浆流动度、抗压强度、抗弯强度、断裂韧性都快速下降,抗弯挠度增加;随圆柱状塑料骨料掺量增加,砂浆流动度增加,抗压强度下降,抗弯强度在低掺量时变化不明显,断裂韧性先增加后下降,抗弯挠度逐渐增加.     

Autogenous Shrinkage of High Strength Lightweight Aggregate Concrete

The characteristic of autogenous shrinkage（AS） and its effect on high strength lightweight aggregate concrete（HSLAC） were studied.The experimental results show that the main shrinkage of high strength concrete is AS and the amount of cement can affect the AS of HSLAC remarkably,At the early stage the AS of HSLAC is lower than that of high strength normal concrete,but it has a large growth at the later stage.The AS of high strength normal concrete becomes stable at 90d age,but HSLAC still has a high AS growth .It is found that adjusting the volume rate of lightweight aggregate,mixing with a proper dosage of fly ash and raising the water saturation degree of lightweight aggregate can markedly reduce the AS rate of HSLAC.     

水泥稳定再生混凝土骨料基层的性能研究

通过对水泥稳定再生混凝土骨料基层的试验研究,考察了水泥稳定再生混凝土骨料基层的力学性能和收缩性能,结果表明:水泥稳定再生混凝土骨料基层切实可行,具有良好经济效应,更重要的是具有广阔的应用效果,其中抗压强度、抗拉强度、弹性模量略低于同剂量的水稳碎石,收缩性能略大于同剂量的水稳碎石,完全满足基层的要求.     

Influence of Calcium Sulfate State and Fineness of Cement on Hydration of Portland Cements Using Electrical Measurement

1 IntroductionThe calcium sulfate state includes gypsum, hemi-hydrate and anhydrite .Inthe modern Portland cement in-dustry,the gypsumis used as a setting retarder for reac-tion with C3A[1]. With the presence of gypsumin theformof CaSO4·2H2O,the gypsum dissolves and reactsprimarily with C3A and C4AF to form ettringite . Thisettringite isinitiallyformed with a veryfine-needle crystalstructure ,whichforms a diffusion barrier onthe surface ofthe cement . This coating avoids the unwanted fl…     

铝酸钙水泥对氧化镁系包埋料性能的影响

以铝酸钙水泥作为结合剂、电熔氧化镁和电熔白刚玉作为原料以及刚玉球作为混磨介质,在聚氨酯滚筒中混磨2h后制得氧化镁系包埋料,研究结合剂铝酸钙水泥含量对氧化镁系包埋料性能的影响。结果表明,随着铝酸钙水泥含量的增加,氧化镁系包埋料的初凝时间缩短,流动性变差;对比110℃热处理试样,经900℃热处理试样显气孔率上升,体积密度下降。当铝酸钙水泥含量大于20％时,铝酸钙水泥的加入可明显地提高氧化镁系包埋料的耐压强度。     

轻骨料混凝土的强度影响因素分析

由于轻骨料混凝土的强度影响因素较多,在实际工程中往往对配合比的控制比较困难,为了便于控制实际工程的各种参数,对不同水胶比、筒压强度、不同粒径范围的粗骨料以及不同减水率的减水剂进行了大量的试验。结果表明,上述四种参数对轻骨料混凝土的强度具有很大的影响。轻骨料混凝土与普通混凝土相似,强度随着水胶比的增加而降低;当混凝土7 d的抗压强度达到28 d强度的70%左右时,试块的抗压强度并不与粒径范围成正比;陶粒的筒压强度对试块的强度具有较大的影响,在进行工程应用时,应严格控制粗骨料的质量;在相同的水泥用量的条件下,减水剂的减水率对于试块的抗压强度有很大的影响。     

再生砼抗压强度的试验研究

研究不同再生粗骨料取代率混凝土棱柱体轴心抗压强度和立方体抗压强度的关系,在掺入减水剂与不掺减水剂两种配合比下再生粗骨料的取代率分别为0、30%、50%和100%。试验结果表明,再生混凝土轴心抗压强度比相同条件下的普通混凝土轴心抗压强度偏小,且随着再生粗骨料取代率的增加而减小。     

鲍罗米公式在预测轻骨料混凝土28d强度方面的应用

研究结果表明,用鲍罗米公式推测轻骨料混凝土28 d抗压强度的误差较大.实测出不同配合比的轻骨料混凝土28 d抗压强度和相应的28 d胶砂试块抗压强度,运用多元线性回归分析的方法完善了鲍罗米公式,所得公式能较准确地预测轻骨料混凝土28 d抗压强度,具有现实指导意义.     

An Improvement in Electrical Properties of Asphalt Concerete

1　ＩｎｔｒｏｄｕｃｔｉｏｎＥｌｅｃｔｒｉｃａｌｌｙｃｏｎｄｕｃｔｉｖｅｃｅｍｅｎｔｃｏｎｃｒｅｔｅｉｓｒｅｓｅａｒｃｈｅｄｉｎｔｈｅｗｏｒｌｄｆｏｒａｂｏｕｔｔｅｎｙｅａｒｓ .Ｓｏｍｅｒｅｍａｒｋａｂｌｅａｃｈｉｅｖｅ ｍｅｎｔｓｈａｖｅｂｅｅｎｍａｄｅｉｎｔｈｉｓｆｉｅｌｄ[1- 6] .Ｉｔｈａｓｂｅｅｎｐｒｏｖｅｄｔｈａｔｃｏｎｄｕｃｔｉｖｅｃｅｍｅｎｔｃｏｎｃｒｅｔｅｉｓａｍｕｌｔｉｆｕｎｃｔｉｏｎ ａｌａｎｄｓｍａｒｔｍａｔｅｒｉａｌ,ｗｈｉｃｈｈａｓａｎｅｘｔｅｎｓｉｖｅａｐｐｌｉｃａｔｉｏｎ…     

粗集料嵌锁型高性能混凝土的研究

采用砂浆包覆粗集料的工艺制备出了一种粗集料能够充分接触并有效嵌锁的高性能混凝土,并与普通C60高性能混凝土作对比研究了其性能。研究表明:在此方法制备的混凝土中,粗集料的体积分数达到了59%以上,粗集料在混凝土中可充分发挥强度骨架作用,混凝土28d抗压强度达到了70～90MPa。另外,以此种方法制备的混凝土具有较高的弹性模量、较好的体积稳定性和抗氯离子渗透性能。