Ni-P电铸工艺参数及Cl-含量对电铸层内应力的影响

目前,对电铸层内应力的影响因素研究多集中在热处理和电铸添加剂方面,有关电铸工艺参数及Cl-的影响缺乏深入探讨.以黄铜为基体,在全硫酸盐体系中电铸Ni-P层;采用薄片阴极弯曲法研究了各工艺参数及Cl-含量对电铸Ni-P层内应力的影响.结果表明:随电流密度和pH值的增加,Ni-P电铸层的内应力由压应力转变为拉应力,且均呈增加趋势;温度升高,Ni-P电铸层的内应力显著降低;溶液中Cl-的存在会显著增加电铸层的内应力,当电铸液中的Cl-含量为25 g/L时,内应力增加到535 MPa.     

喷射电铸工艺参数对铜铸层形貌的影响

介绍了喷射电铸的相关原理,运用扫描电镜分析了相关工艺参数(电流密度、电解液喷射速度、扫描速度、扫描层数)对铜沉积层微观结构的影响,采用工艺参数:电流密度300A/dm2,电解液喷射速度4m/s,喷嘴扫描速度10mm/s制备了纳米铜块体。结果表明喷射电铸可大大提高电铸的电流密度,远高于传统电铸电流密度;电流密度、喷射速度、扫描速度以及扫描层数都对沉积层的表面生长形态有较大的影响,使用低电流密度、高喷射速度和快的扫描速度和少的扫描层数有利于获得平整、致密的沉积层。     

工艺参数对熔盐法制备钛酸铋粉体影响的研究

研究了工艺参数对熔盐法制备钛酸铋粉体晶粒形貌和尺寸的影响.发现温度、盐的种类和盐的用量能够较显著地影响晶粒的形貌和尺寸.在氯盐中,晶粒尺寸随着温度的升高而逐渐增大,晶粒最终发育为较规则的圆片状,晶粒生长按照Ostwald液相生长机理来进行.在硫酸盐中,晶粒尺寸明显大于相同条件下在氯盐中的尺寸,且晶粒形貌呈不规则片状.当原料与盐的比例<1时,随着盐用量的增加,晶粒尺寸减小,形貌更加不规则.通过调整工艺参数能够控制颗粒的尺寸和形貌,制备具有各向异性生长的钛酸铋片状粉体.     

化学镀锡工艺参数对沉积速率、镀层厚度及表面形貌的影响

目前,铜基或铁基上化学镀锡存在连续性差、沉积速率慢等问题,为实现连续化学镀锡,提高沉积速率,设计了一种新的化学镀锡工艺,考察了化学镀锡主要工艺参数(镀液主成分、pH值、温度、施镀时间)对镀层表面形貌及厚度的影响.结果表明,最佳工艺参数为:20.0～25.0 g/L氯化亚锡,70.0～75.0 g/L次亚磷酸钠,70.0～75.0 g/L硫脲,75.0～80.0 g/L硫酸,5.0～8.0 g/L甲基磺酸,50.0～8.0 g/L EDTA,2.0～4.0 g/L对苯二酚,10.0～15.0 g/L乙二醇,0.5～1.0 g/L磷酸,0.5～1.0 g/L甲醛,0.5～1.0 g/L OP-10,温度80～85℃,pH值0.6～0.8.该工艺可实现连续化学镀锡,施镀3h厚度可达32.72μm.     

磁场对铜板冷表面抑霜的可视化研究

为了研究弱磁对凝结液滴冻结和结霜过程的影响。通过在冷表面两侧施加永磁铁的方式,探究磁场(0—70 mT)和液滴冻结时间、大小、霜厚及结霜质量的关系。实验结果表明:在相同的工况下,随着磁场强度的增加,冷表面上发生液滴冻结的时间逐渐延长,但随湿度增加到一定程度时,液滴冻结的时间与磁场强度的关系并不是呈线性关系;另外,在不同磁场强度下,冻结液滴的尺寸不同;在结霜过程中,霜层生长的速度随着磁场强度的增加而变缓,结霜质量随之减少。以上的结果表明,一定的磁场强度对冷表面上液滴的冻结和霜层的生长均能起到一定的抑制作用,但随着冷表面温度的降低和环境湿度的增加,磁场对液滴冻结和结霜过程的抑制作用会减弱。     

激光熔覆工艺参数对熔覆层质量的影响

为了在工件表面获得最佳的熔覆层,以40CrNi2MoA钢为基材、Ni35和Ni25为粉末,采用不同工艺参数进行了激光熔覆,检测了熔覆层的组织结构,分析了其随熔覆工艺参数变化的规律,确定了最佳工艺条件。结果表明:采用最佳熔覆工艺修复工件可得到组织致密、无裂纹、无气孔的熔覆层;熔覆层与基体呈优良的冶金结合。     

工艺参数对液相还原法制备超细银粉形貌特征的影响

研究硝酸银浓度、抗坏血酸浓度、反应体系温度及pH值、添加剂种类及用量对液相还原法制备超细银粉形貌特征的影响,借助SEM、粒度仪、比表面仪和颗粒图像分析仪对银粉进行表征和分析。结果表明,pH值是同时影响银粉形状、粒度和分散性的显著因素,添加剂用量和抗坏血酸浓度分别是影响银粉形状及分散性的显著因素;随着pH值由2逐渐增大至10,银粉呈现由无规则多面体至棒状、类球形的形状变化,平均粒径逐渐减小;随着添加剂用量增加,银粉呈现由异形至球形、刺球型的形状变化,其用量质量分数为2.5%时颗粒球形度值最大;随着抗坏血酸浓度增加,银粉的分散性逐渐变差,其浓度为0.5 mol/L时分散性最好。     

低变形镍模具微电铸加工的工艺优化(英文)

微电铸工艺提供了一种有效的技术手段来制造金属模具,这种金属模具可被用于微图形的复制.模具的微电铸加工存在一个瓶颈问题:模具表面的不平整.金属模具的弯曲是造成模具表面不平整的主要原因之一.金属模具的弯曲变形会对微结构的复制精度产生影响.为了获得低变形镍模具,对微电铸工艺参数进行了优化.优化后的微电铸液中含有的镍离子质量浓度为80～90 g/L,硼酸的质量浓度为40～45 g/L,并且加入了0.3%L-1的润湿剂,其pH值控制在3.7～4.2之间.微电铸液的温度保持在50～55℃.在微电铸过程中,采用了电流密度为2～3A/dm2的脉冲电流,占空比为0.2.结果表明:采用优化后的工艺参数,可以获得低变形的镍模具,其变形量下降了19%.利用优化后的微电铸工艺,加工了一种可以用于热压工艺的镍模具,模具上的图形线宽为5μm,深度为5μm.     

激光多层熔覆纳米陶瓷层工艺参数优化

为了深入了解激光多层熔覆工艺与涂层性能之间的关系,采用压片预置式激光多层熔覆工艺制备了纳米Al2O3-13%TiO2(质量分数)陶瓷层;通过3因素3水平正交试验分析了激光熔覆熔池闭环控制温度、超声振动频率及保温箱预热温度对涂层结合强度的影响,并对激光熔覆工艺参数进行了优化;通过扫描电镜(SEM)和结合强度测试研究了最优工艺下所得涂层的形貌和性能。结果表明:影响涂层结合强度的因素主次顺序依次为熔池闭环控制温度、保温箱预热温度、超声振动频率;激光多层熔覆纳米Al2O3-13%TiO2涂层最佳工艺参数为熔池闭环控制温度2 500℃,超声振动频率50 kHz,保温箱预热温度400℃;优化工艺熔覆的涂层各层之间无明显界面,涂层内部致密、连续,基本无孔隙及贯穿性大裂纹,涂层结合强度明显提高,达66.3 MPa。     

加热工艺对微合金钢Ti、Nb固溶及奥氏体晶粒长大的影响

研究含Ti、Nb微合金钢HJ58轧制前不同加热温度和保温时间对Ti、Nb固溶量及奥氏体晶粒尺寸的影响规律,讨论微合金元素Ti、Nb的存在状态及作用机理,提出了合理的加热工艺以指导生产.     

弱交流磁场下裸铜表面结晶特性研究

本文研究了环境温度恒定为25℃、相对湿度为49%、体积为0. 01 m L的液滴在-20℃裸铜底板的冻结实验,发现在附加交流磁场强度分别为2. 0×10^-3、2. 5×10^-3、3. 0×10^-3、3. 5×10^-3、4. 0×10^-3、4. 5×10^-3、5. 0×10^-3、5. 5×10^-3、6. 0×10^-3T的作用下,液滴结晶过冷度增大,最大过冷度提高了2. 08℃;但附加磁场会减小成核驱动力;相比无磁场情况下,液滴冷凝时间减少,凝结粒径相比无磁场下较小。通过对在相同温湿度下自然对流条件的冷铜底板结霜可视化研究发现,由于附加磁场使极性水分子有序的在底板排列,较无磁场下液滴结晶过程熵增更小,在宏观上呈现液滴有序排列。此外,实验发现在0～6×10^-3T的磁场强度范围,随着磁场强度的增大,平板单位面积结霜量减小,单位面积结霜量与交流磁场强度有较高的相关性,得到了拟合关...     

Effect of the External Magnetic Field on the Resonance Scattering in Cuprate Superconductors

Within the kinetic energy driven superconducting mechanism, the effect of a uniform external magnetic field on the resonance scattering in cuprate superconductors in the superconducting state is studied. It is shown that the commensurate resonance scattering at zero external magnetic field is induced into the incommensurate resonance scattering by applying a large enough external magnetic field. The part of the spin excitation dispersion seems to be an hourglass-like dispersion, which breaks down at the heavily low energy regime.     

The Effect of External Magnetic Field on a Vacuum Arc

The effect of an external longitudinal magnetic field on the time required for anode spot formation in a high-current (5 to 12 kA) vacuum arc is experimentally studied, and the minimal value of a magnetic field inhibiting the anode spot formation is determined. The experimental results are compared with theory. The phenomenon of break of current in a low-current (100 to 300 A) vacuum discharge upon superposition of a magnetic field with transverse component on the discharge is investigated. The probability of break of current increases with the magnetic field. The possible mechanism of break of current is discussed.     

Effect of External Nonuniform Magnetic Field on Flux Creep Process in Superconductor

The effect of an external nonuniform magnetic field on the flux creep rate in a high-temperature superconductor with trapped magnetic flux was studied. The magnetic relaxation was suppressed when the superconductor was put into a field of permanent magnets or when it approached a ferromagnet. The effect arises when the field sources (being magnetized, the ferromagnet produces its own field) are placed near the superconductor surface, where the flux line ends are located. For these cases, we carried out the calculations of vortex and current density distributions, which demonstrate that reverse currents flow in the near-surface regions of the sample. This verifies the hypothesis suggested earlier about the influence of counter Lorentz forces retarding the creep of the vortices. In the interpretation of the results, we also take into consideration the magnetic force acting on the vortex ends in the external nonuniform magnetic field that allows us to explain the experimental results, in which the current structure in the sample is unipolar.     

电化学刻蚀参数对高阻厚壁宏孔硅阵列表面形貌的影响

采用光电化学刻蚀方法,在电阻率为4～5 kΩ·cm的n-型[100]单晶硅片上制备了厚壁有序宏孔硅阵列。通过对比有限元法模拟诱导坑周围的电场分布,研究了刻蚀参数(电解液、光照、电压)对阵列表面形貌的影响。在刻蚀成孔的过程中,诱导坑对孔的限制受电场分布和实验条件的共同影响,出现刻蚀偏离的现象。模拟结果显示,诱导坑上的电场强度沿着单晶硅的[100]和[110]晶向的分布。这种分布的结果是,随着光照强度的提高和刻蚀溶液表面自由能的降低刻蚀由原光刻图形的(110)面向(100)面偏离。提高刻蚀电压可抑制刻蚀偏离,有利于诱导坑快速刻蚀成孔,从而形成规整的厚壁宏孔硅阵列。     

Quantitative Prediction of Surface Hardness in 12CrMoV Steel Plate Based on Magnetic Barkhausen Noise and Tangential Magnetic Field Measurements

Both magnetic Barkhausen noise (MBN) and tangential magnetic field (TMF) strength can be applied in the quantitative prediction of surface hardness of ferromagnetic specimens. The prediction accuracy depends on the selected model and the input parameters of the model. In this study, the relationship between the surface hardness of 12CrMoV steel plate and the measured MBN and TMF signals is investigated with multivariable linear regression (MLR) model and BP neural network technique. A comparative study between the MLR and BP model is conducted. The external validation results show that the BP model utilizing four MBN features as the input nodes has a smaller average prediction error (3.7%) than that of the MLR model (13.2%). Features extracted from the MBN and TMF signals are combined together as the input parameters of the BP model in order to achieve high accuracy. After adding two more TMF features into the input nodes of the BP network, the external validation results suggest that the average prediction error is decreased from 3.7 to 3.5%.     

磁场干摩擦学的研究进展

简要介绍了目前国内外关于磁场条件下金属材料干摩擦学的研究现状,评述了磁场参数对金属材料摩擦学性能的影响机制.指出今后在考虑气氛环境等多种因素的综合作用下,应建立标准化试验方法及理论模型,并着重从材料微观层面对磨损机理进行了探讨.