304不锈钢激光搭接焊接头的组织及力学性能

采用脉冲激光焊技术焊接304不锈钢薄板。利用光学显微镜、扫描电镜、万能试验机等分析检测手段,研究304不锈钢焊接接头的微观组织特点及激光功率对接头组织及力学性能的影响规律。结果表明,焊缝中心为细小的等轴晶,焊缝边缘为柱状晶组织,热影响区不明显。随着激光功率的增加,焊缝抗拉强度增大。激光功率为2.6 kW时,焊缝抗拉强度达到最大值491.7 MPa。继续增加激光功率,焊缝组织粗化,焊接接头抗拉强度降低。拉伸试样均在焊缝处发生断裂,焊缝中心是焊接接头最薄弱的部位。     

304不锈钢薄板激光焊搭接接头组织及性能

研究0.8 mm厚度304不锈钢薄板的搭接连续激光焊工艺,分析接头的显微组织和部分力学性能。与电阻缝焊接头进行比较,结果表明:激光焊成形良好,在适当的工艺规范下,激光焊和电阻缝焊的水压试验都可以达到8.0 MPa;激光焊的热影响区更窄并且焊缝中组织为奥氏体;较电阻缝焊焊缝呈更均匀、细小的柱状晶;两种焊接方法的拉伸剪切试验的断裂位置均位于母材。     

TiNi形状记忆合金与不锈钢激光钎焊接头界面组织特征

通过扫描电子显微镜、能谱仪及X射线衍射技术分析TiNi形状记忆合金与1Cr18Ni9Ti不锈钢激光钎焊接头界面反应层的组织结构特征。结果表明：TiNi形状记忆合金与不锈钢激光钎焊接头钎缝主要由α-Ag固溶体、α′-Cu固溶体和Ag-Cu共晶相组成;不锈钢/银基钎料界面反应区由3层连续的反应层构成,分别为：奥氏体（A）,马氏体（M）/A和M/α-Ag＋α′-Cu＋M;TiNi形状记忆合金/银基钎料界面反应层主要由Ti（Ni,Cu）＋（Ni,Cu）Ti2化合物组成。     

Cf/SiC复合材料与304不锈钢钎焊接头组织与性能

采用Ti-Zr-Be活性钎料作为连接层,在一定工艺参数下真空钎焊C_f/SiC复合材料和304不锈钢.利用SEM,EDS,XRD和俄歇谱仪分析接头微观组织结构,利用剪切试验检测接头力学性能,分析了工艺参数对接头抗剪强度的影响.结果表明,在复合材料附近形成ZrC+TiC+Be₂C/Ti-Si反应层,连接层中主要包含FeZr₂,锆基固溶体,BeTi,Ti-Zr固溶体等反应产物,304不锈钢附近形成FeTi/αFe反应层.在连接温度为950℃,连接时间为60min时,接头室温抗剪强度最高为109.3 MPa,断裂位置为C_f/SiC复合材料与中间层连接界面靠近复合材料端.     

Ni含量对304/Sn-8Sb-4Cu-xNi/304钎焊接头组织与剪切性能的影响

研究了Ni含量对Sn-8Sb-4Cu-xNi(x=0, 0.5, 1和2,质量分数)钎料熔点和微观组织的影响,用Sn-8Sb-4CuxNi钎料对304不锈钢进行钎焊连接,分析了接头的界面组织与剪切性能.结果表明,添加不同含量的Ni后,Sn-8Sb-4Cu-xNi均为近共晶钎料,其熔点约为245℃;Sn-8Sb-4Cu钎料组织由α相基体、Sb₂Sn₃+Cu₆Sn₅+Sn复合相和Cu₆(Sn,Sb)₅相组成.添加Ni元素后,钎料中块状Cu₆(Sn,Sb)₅转变为细小、均匀分布的(Cu,Ni)₆(Sn,Sb)₅.当Ni含量小于1%时,随Ni含量的增加,钎料中的复合相和(Cu,Ni)₆(Sn,Sb)₅相均增加;当Ni含量为2%时,钎料中的复合相和(Cu,Ni)₆(Sn,Sb)₅相均减少,但(...     

SUS304不锈钢MAG焊接头组织与性能

通过金相观察、力学性能和耐晶间腐蚀性能试验,研究了SUS304不锈钢MAG焊接头组织与性能。结果表明,接头的抗拉强度不低于母材,而且塑性良好。焊缝为奥氏体组织,呈较为粗大的柱状晶形态,且与母材熔合良好;过热区的晶粒长大不严重。焊态时,焊接接头的腐蚀速率与母材相当,经敏化处理,接头的腐蚀速率大大增加。     

SUS304不锈钢MAG焊接头组织与性能

通过金相观察、力学性能和耐晶间腐蚀性能试验，研究了SUS304不锈钢MAG焊接头组织与性能。结果表明，接头的抗拉强度不低于母材，而且塑性良好。焊缝为奥氏体组织，呈较为粗大的柱状晶形态，且与母材熔合良好；过热区的晶粒长大不严重。焊态时，焊接接头的腐蚀速率与母材相当，经敏化处理，接头的腐蚀速率大大增加。     

T2紫铜/304不锈钢激光钎焊接头组织及性能

采用铜锰镍钎料,使用激光焊机对T2紫铜和304不锈钢进行了激光钎焊。通过扫描电子显微镜、拉伸试验机测试分析了搭接形式下的钎缝宏观形貌、焊接接头力学性能及钎料元素的扩散情况。结果表明,在紫铜/不锈钢的激光钎焊时,焊接电流对钎缝成形的影响最大、脉冲频率次之、脉冲宽度的影响最小,对应的正交试验极差分别为17.35,15.66,7.91;钎料与母材发生良好的扩散并形成固溶体;钎缝中Fe,Cr元素扩散明显并存在条块状铜基固溶体,在最优的焊接工艺参数下,钎焊接头的抗剪强度达到35.75 MPa。     

UNS S32750超级双相不锈钢激光焊接头微观组织与耐蚀性能

以UNS S32750超级双相不锈钢为研究对象,采用光学显微镜、扫描电子显微镜、透射电子显微镜、电子探针显微分析仪对激光焊接头微观组织和元素分布进行表征,采用临界点蚀温度测试方法研究激光功率对激光焊接头点蚀行为的影响规律.结果表明,提高激光功率可显著增加焊缝中奥氏体含量,并且在一定程度上抑制Cr₂N析出.此外,激光焊焊缝具有比母材更低的耐点蚀性能.但随着激光功率的增加,焊缝中耐蚀的奥氏体含量增加,同时降低了Cr₂N析出倾向,因此其耐点蚀性能也逐渐增强.与双相钢母材相比,激光焊焊缝中Cr,Ni,Mo等合金元素在铁素体与奥氏体中的分配差异性显著减小,而N原子的分配差异性增加,因此焊缝中铁素体具有比奥氏体更低的耐点蚀指数,进而优先被选择性腐蚀.对于双相钢母材,点蚀主要发生在δ/γ相界和夹杂处,而激光焊焊缝的点蚀主要以铁素体内大量析出的Cr₂N作为点蚀萌生位置,并向弱相铁素体内快速发展.     

新型不锈钢热交换器真空钎焊接头的组织分析

采用扫描电镜（SEM）、显微硬度计、金相微镜等方法对新型不锈钢热交换器真空钎焊的接头组织性能进行了分析。试验结果表明，在1118－1130℃钎焊0Cr17Ni12Mo2不锈钢，保温10－20min，在钎缝中形成的柱状晶使接头处有良好的结合状态。钎焊接头由靠近钎缝的奥氏体(γ－Fe)、Cu向γ－Fe中扩散形成的固溶体以及Cu-Ag共晶组织组成。共晶组织中先结晶的α固溶体比后结晶的β固溶体的显微硬度明显高一些。     

不锈钢板激光焊接接头组织与性能

时不锈钢板进行激光焊与氩弧焊时比试验。结果表明：激光焊焊缝中晶粒尺寸小于氩弧焊焊缝的晶粒尺寸。而激光焊接接头的显微硬度高于氩弧焊的，激光焊件断口边缘有解理面存在，焊缝中心呈韧窝状。对于薄板件焊接，激光焊接质量较好。     

Microstructure and mechanical properties of a laser welded low carbon–stainless steel joint

This article reports on an experimental investigation to understand and subsequently control the alloying composition in laser welding of austenitic stainless steel and low carbon steel. An energy dispersive spectrometer was used to analyse the alloying composition, while microscopy and tensile tests were used to study the microstructure, and mechanical performance of the welded joint respectively. The investigation revealed that above a certain specific point energy the material within the melt pool is well mixed and the laser beam position can be used to control the mechanical properties of the joint. This finding was confirmed using a numerical model based on computational fluid dynamics (CFD) of melt pool dynamics. Strategies to control the composition leading to dramatic changes in hardness, microstructure and mechanical properties of the dissimilar laser welded joint are discussed.     

紫铜感应钎焊接头组织及性能

以紫铜板材为对象,利用Sn-58Bi和Sn-0.7Cu钎料对紫铜进行感应钎焊实验,保温不同的时间,采用光学显微镜、显微硬度计、接合强度测试仪等方法对钎焊接头进行组织分析和性能测试。结果表明,利用Sn-58Bi和Sn-0.7Cu钎料和感应钎焊技术可以实现紫铜的连接。Sn-58Bi感应钎焊接头界面处均形成了一层薄而连续的金属间化合物Cu6Sn5。随着保温时间的增加,焊缝中富Bi相逐渐减少。Sn-0.7Cu钎料接头的显微硬度在保温时间为10 s时最大。随着保温时间的增加,金属间化合物层厚度逐渐增加,接头强度随之降低。     

27SiMn钢表面激光熔覆304不锈钢的组织和性能

利用激光熔覆技术在液压支架立柱母材27SiMn钢表面进行了不同激光功率的单道激光熔覆304不锈钢试验,选择出熔覆层质量最佳时的激光功率,并在该功率下进行多层累加激光熔覆304不锈钢试验。分析了熔覆层材料的显微组织,对比分析了27SiMn钢基体和304不锈钢熔覆层的拉伸性能和断口形貌。结果表明,熔覆层和基体之间实现了良好的冶金结合,熔覆层材料中呈现出了具有典型定向凝固特征的柱状晶;熔覆层材料的抗拉强度与基体相当,伸长率明显高于基体;熔覆层和基体材料的拉伸断口处均出现了具有典型塑性断裂特征的韧窝,且熔覆层材料的韧窝尺寸及深度明显大于基体材料。     

高强不锈钢激光熔覆层的组织与性能

针对核装备零部件维修再制造的需要,采用激光熔覆技术制备高强韧马氏体不锈钢熔覆层,以改善核装备零部件的表面性能,随后对熔覆层试样分别进行300 ℃和500 ℃保温2 h的回火处理。采用OM、SEM、显微硬度计、万能拉伸试验机等设备测试了试样的组织和性能。结果表明,原始试样的抗拉强度为1719 MPa,断后伸长率在15%左右,硬度为550 HV0.2,耐磨性较差;当回火温度为300 ℃时,出现逆转变奥氏体,硬度降至500 HV0.2,抗拉强度降为1662 MPa,断后伸长率超过15%,耐磨性提高;当回火温度上升到500 ℃时,逆转变奥氏体减少,碳化物逐渐析出,出现二次硬化,硬度又上升至530 HV0.2,抗拉强度降至1582 MPa,断后伸长率降至14%左右,耐磨性与原始试样相当。该高强马氏体不锈钢熔覆层整体耐腐蚀性均优于1Cr13钢,具有良好的耐腐蚀能力。     

2205双相不锈钢搅拌摩擦焊接头组织和性能

采用不同搅拌头转速,研究了搅拌头转速对4 mm厚2205双相不锈钢板材搅拌摩擦焊接头组织及性能的影响. 结果表明,当焊接速度为50 mm/min时,搅拌头转速在600 ~ 800 r/min的范围内,均可获得表面成形良好且内部无缺陷的接头.接头搅拌区在动态再结晶的作用下组织得到细化,硬度值较高,热影响区在焊接热作用下组织粗化,硬度值较低.整个接头的铁素体含量在50% ~ 60%范围内,且随着转速的升高搅拌区的铁素体含量有所增加. 当转速为600 r/min时,接头的抗拉强度达到最大824 MPa,为母材的97.3%,断裂位置为接头的热影响区.     

高氮奥氏体不锈钢仰焊焊接接头组织与性能研究

通过金相观察、力学性能和耐蚀性能试验,采用00Cr20Ni15Mo2N钢研究了高氮奥氏体不锈钢焊条电弧仰焊焊接接头的组织与性能,并对其焊接工艺进行了适当的实践与探讨。结果表明,接头的抗拉强度不低于母材,而且塑性良好。焊缝为100%奥氏体组织,呈较为粗大的柱状晶形态,且与母材熔合良好;过热区的晶粒长大不严重。焊态时,焊接接头的腐蚀速率与母材相当,经敏化处理的晶间腐蚀试样,弯曲90°后未发现因晶间腐蚀而产生的裂纹。均匀腐蚀全浸试验的年均腐蚀速度为1.32×10~(-3)mm/年,具有良好的耐腐蚀性能。     

低碳钢表面激光熔覆不锈钢的组织和性能

采用JHM-1GY-400型脉冲Nb∶YAG固体激光器和316L不锈钢粉末在20低碳钢表面制备了激光熔覆层。利用OM、XRD、SEM等表征方法分析了不锈钢熔覆层的物相组成和显微组织,并分别利用旋转摩擦试验机和电化学工作站对熔覆层和基材的耐磨损和耐腐蚀性进行了研究。试验结果表明,不锈钢熔覆层厚度约为50 μm,由γ相(奥氏体)和α相(铁素体)组成,其显微组织主要包括细小的树枝晶、粗大的胞状晶以及平面晶;不锈钢熔覆层表面硬度约为基材的2倍,摩擦因数比基材低0.0418,磨损量更低,不锈钢熔覆层比基材具有更高的耐磨性。与基材相比,不锈钢熔覆层具有更低的自腐蚀电流和更高的自腐蚀电位,其耐腐蚀性能更优异。