Stack system of PECVD amorphous silicon and PECVD silicon oxide for silicon solar cell rear side passivation

A stack of hydrogenated amorphous silicon (a‐Si) and PECVD‐silicon oxide (SiO_x) has been used as surface passivation layer for silicon wafer surfaces. Very good surface passivation could be reached leading to a surface recombination velocity (SRV) below 10 cm/s on 1 Ω cm p‐type Si wafers. By using the passivation layer system at a solar cell's rear side and applying the laser‐fired contacts (LFC) process, pointwise local rear contacts have been formed and an energy conversion efficiency of 21·7% has been obtained on p‐type FZ substrates (0·5 Ω cm). Simulations show that the effective rear SRV is in the range of 180 cm/s for the combination of metallised and passivated areas, 120 ± 30 cm/s were calculated for the passivated areas. Rear reflectivity is comparable to thermally grown silicon dioxide (SiO₂). a‐Si rear passivation appears more stable under different bias light intensities compared to thermally grown SiO₂. Copyright © 2008 John Wiley & Sons, Ltd.     

Light‐enhanced surface passivation of TiO2‐coated silicon

Titanium dioxide is shown to afford good passivation to non‐diffused silicon surfaces and boron‐diffused surfaces after a low‐temperature anneal. The passivation most likely owes to the significant levels of negative charge instilled in the films, and passivation is enhanced by illumination—advantageous for solar cells—indicating that a titanium dioxide photoreaction is at least partly responsible for the low surface recombination. We demonstrate a surface recombination velocity of less than 30 cm/s, on a 5‐Ω cm n‐type silicon, and an emitter saturation current density of 90 fA/cm² on a 200‐Ω/sq boron diffusion. If these titanium dioxide passivated boron‐diffused surfaces were employed in a crystalline silicon solar cell, an open‐circuit voltage as high as 685 mV could be achieved. Given that TiO₂ has a high refractive index and was deposited with atmospheric pressure chemical vapour deposition, an inexpensive technique, it has the potential as a passivating antireflection coating for industrial boron‐diffused silicon solar cells. Copyright © 2011 John Wiley & Sons, Ltd.     

Role of hydrogen in the surface passivation of crystalline silicon by sputtered aluminum oxide

Aluminum oxide films can provide excellent surface passivation on both p‐type and n‐type surfaces of silicon wafers and solar cells. Even though radio frequency magnetron sputtering is capable of depositing aluminum oxide with concentrations of negative charges comparable to some of the other deposition methods, the surface passivation has not been as good. In this paper, we compare the composition and bonding of aluminum oxide deposited by thermal atomic layer deposition and sputtering, and find that the interfacial silicon oxide layer and hydrogen concentration can explain the differences in the surface passivation. Copyright © 2010 John Wiley & Sons, Ltd.     

Front and rear silicon‐nitride‐passivated multicrystalline silicon solar cells with an efficiency of 18.1%

A solar cell process designed to utilise low‐temperature plasma‐enhanced chemical vapour deposited (PECVD) silicon nitride (SiN_x) films as front and rear surface passivation was applied to fabricate multicrystalline silicon (mc‐Si) solar cells. Despite the simple photolithography‐free processing sequence, an independently confirmed efficiency of 18.1% (cell area 2 × 2 cm²) was achieved. This excellent efficiency can be predominantly attributed to the superior quality of the rear surface passivation scheme consisting of an SiN_x film in combination with a local aluminium back‐surface field (LBSF). Thus, it is demonstrated that low‐temperature PECVD SiN_x films are well suited to achieve excellent rear surface passivation on mc‐Si. Copyright © 2002 John Wiley & Sons, Ltd.     

Experimental and simulated analysis of front versus all‐back‐contact silicon heterojunction solar cells: effect of interface and doped a‐Si:H layer defects

Front silicon heterojunction and interdigitated all‐back‐contact silicon heterojunction (IBC‐SHJ) solar cells have the potential for high efficiency and low cost because of their good surface passivation, heterojunction contacts, and low temperature fabrication processes. The performance of both heterojunction device structures depends on the interface between the crystalline silicon (c‐Si) and intrinsic amorphous silicon [(i)a‐Si:H] layer, and the defects in doped a‐Si:H emitter or base contact layers. In this paper, effective minority carrier lifetimes of c‐Si using symmetric passivation structures were measured and analyzed using an extended Shockley–Read–Hall formalism to determine the input interface parameters needed for a successful 2D simulation of fabricated baseline solar cells. Subsequently, the performance of front silicon heterojunction and IBC‐SHJ devices was simulated to determine the influence of defects at the (i)a‐Si:H/c‐Si interface and in the doped a‐Si:H layers. For the baseline device parameters, the difference between the two device configurations is caused by the emitter/base contact gap recombination and the back surface geometry of IBC‐SHJ solar cell. This work provides a guide to the optimization of both types of SHJ device performance, predicting an IBC‐SHJ solar cell efficiency of 25% for realistic material parameters. Copyright © 2013 John Wiley & Sons, Ltd.     

20.1%‐efficient crystalline silicon solar cell with amorphous silicon rear‐surface passivation

We have developed a crystalline silicon solar cell with amorphous silicon (a‐Si:H) rear‐surface passivation based on a simple process. The a‐Si:H layer is deposited at 225°C by plasma‐enhanced chemical vapor deposition. An aluminum grid is evaporated onto the a‐Si:H‐passivated rear. The base contacts are formed by COSIMA (contact formation to a‐Si:H passivated wafers by means of annealing) when subsequently depositing the front silicon nitride layer at 325°C. The a‐Si:H underneath the aluminum fingers dissolves completely within the aluminum and an ohmic contact to the base is formed. This contacting scheme results in a very low contact resistance of 3.5 ±0.2 mΩ cm² on low‐resistivity (0.5 Ω cm) p‐type silicon, which is below that obtained for conventional Al/Si contacts. We achieve an independently confirmed energy conversion efficiency of 20.1% under one‐sun standard testing conditions for a 4 cm² large cell. Measurements of the internal quantum efficiency show an improved rear surface passivation compared with reference cells with a silicon nitride rear passivation. Copyright © 2005 John Wiley & Sons, Ltd.     

Bulk and surface passivation of silicon solar cells accomplished by silicon nitride deposited on industrial scale by microwave PECVD

Bulk and surface passivation by silicon nitride has become an indispensable element in industrial production of multicrystalline silicon (mc‐Si) solar cells. Microwave PECVD is a very effective method for high‐throughput deposition of silicon nitride layers with the required properties for bulk and surface passivation. In this paper an analysis is presented of the relation between deposition parameters of microwave PECVD and material properties of silicon nitride. By tuning the process conditions (substrate temperature, gas flows, working pressure) we have been able to fabricate silicon nitride layers which fulfill almost ideally the four major requirements for mc‐Si solar cells: (1) good anti‐reflection coating (refractive index tunable between 2·0 and 2·3); (2) good surface passivation on p‐type FZ wafers (S_eff<30 cm/s); (3) good bulk passivation (improvement of IQE at 1000 nm by 30% after short thermal anneal); (4) long‐term stability (no observable degradation after several years of exposure to sunlight). By implementing this silicon nitride deposition in an inline production process of mc‐Si solar cells we have been able to produce cells with an efficiency of 16·5%. Finally, we established that the continuous deposition process could be maintained for at least 20 h without interruption for maintenance. On this timescale we did not observe any significant changes in layer properties or cell properties. This shows the robustness of microwave PECVD for industrial production. Copyright © 2005 John Wiley & Sons, Ltd.     

19%‐efficient and 43 µm‐thick crystalline Si solar cell from layer transfer using porous silicon

We present a both‐sides‐contacted thin‐film crystalline silicon (c‐Si) solar cell with a confirmed AM1.5 efficiency of 19.1% using the porous silicon layer transfer process. The aperture area of the cell is 3.98 cm². This is the highest efficiency ever reported for transferred Si cells. The efficiency improvement over the prior state of the art (16.9%) is achieved by implementing recent developments for Si wafer cells such as surface passivation with aluminum oxide and laser ablation for contacting. The cell has a short‐circuit current density of 37.8 mA cm⁻², an open‐circuit voltage of 650 mV, and a fill factor of 77.6%. Copyright © 2011 John Wiley & Sons, Ltd.     

Rapid thermal processing of next generation silicon solar cells

Rapid and potentially low‐cost process techniques are analyzed and successfully applied towards the fabrication of high‐efficiency mono‐ and multicrystalline Si solar cells. First, a novel dielectric passivation scheme (formed by stacking a plasma silicon nitride film on top of a rapid thermal oxide layer) is developed that serves as antireflection coating and reduces the surface recombination velocity (S_eff) of the 1˙3 Ω‐cm p‐Si surface to approximately 10 cm/s. The essential feature of the stack passivation scheme is its ability to withstand short 700 – 850°C anneal treatments used to fire screen printed (SP) contacts, without degradation in S_oeff. The stack also lowers the emitter saturation current density (J_oe) of 40 and 90 Ω/□ emitters by a factor of three and 10, respectively, compared to no passivation. Next, rapid emitter formation is accomplished by diffusion under tungsten halogen lamps in both belt line and rapid thermal processing (RTP) systems (instead of in a conventional infrared furnace) . Third, a combination of SP aluminium and RTP is used to form an excellent back surface field (BSF) in 2 min to achieve an effective back surface recombination velocity (S_eff) of 200 cm/s on 2˙3 Ω‐cm Si. Finally, the above individual processes are integrated to achieve: (1) >19% efficient solar cells with emitter and Al‐BSF formed by RTP and contacts formed by vacuum evaporation and photolithography, (2) 17% efficient manufacturable cells with emitter and Al‐BSF formed in a belt line furnace and contacts formed by SP. Copyright © 2000 John Wiley & Sons, Ltd.     

High‐rate deposition of a‐Si:H thin layers for high‐performance silicon heterojunction solar cells

In this paper, we describe a technique for high‐quality interface passivation of n‐type crystalline silicon wafers through the growth of hydrogenated amorphous Si (a‐Si:H) thin layers using conventional plasma‐enhanced chemical vapor deposition. We investigated the onset of crystallization of the a‐Si:H layers at various deposition rates and its effect on the surface passivation properties. Epitaxial growth occurred, even at a low substrate temperature of 90 °C, when the deposition rate was as low as 0·5 Å/s; amorphous growth occurred at temperatures up to 150 °C at a higher deposition rate of 4·2 Å/s. After optimizing the intrinsic a‐Si:H layer deposition conditions and then subjecting the sample to post‐annealing treatment, we achieved a very low surface recombination velocity (7·6 cm/s) for a double‐sided intrinsic a‐Si:H coating on an n‐type crystalline silicon wafer. Under the optimized conditions, we achieved an untextured heterojunction cell efficiency of 16·7%, with a high open‐circuit voltage (694 mV) on an n‐type float‐zone Si substrate. On a textured wafer, the cell efficiency was further enhanced to 19·6%. Copyright © 2011 John Wiley & Sons, Ltd.     

Multi‐crystalline Si solar cells with very fast deposited (180 nm/min) passivating hot‐wire CVD silicon nitride as antireflection coating

Hot‐wire chemical vapor deposition (HWCVD) is a promising technique for very fast deposition of high quality thin films. We developed processing conditions for device‐ quality silicon nitride (a‐SiN_x:H) anti‐reflection coating (ARC) at high deposition rates of 3 nm/s. The HWCVD SiN_x layers were deposited on multicrystalline silicon (mc‐Si) solar cells provided by IMEC and ECN Solar Energy. Reference cells were provided with optimized parallel plate PECVD SiN_x and microwave PECVD SiN_x respectively. The application of HWCVD SiN_x on IMEC mc‐Si solar cells led to effective passivation, evidenced by a V_oc of 606 mV and consistent IQE curves. For further optimization, series were made with HW SiN_x (with different x) on mc‐Si solar cells from ECN Solar Energy. The best cell efficiencies were obtained for samples with a N/Si ratio of 1·2 and a high mass density of >2·9 g/cm³. The best solar cells reached an efficiency of 15·7%, which is similar to the best reference cell, made from neighboring wafers, with microwave PECVD SiN_x. The IQE measurements and high V_oc values for these cells with HW SiN_x demonstrate good bulk passivation. PC1D simulations confirm the excellent bulk‐ and surface‐passivation for HW SiN_x coatings. Interesting is the significantly higher blue response for the cells with HWCVD SiN_x when compared to the PECVD SiN_x reference cells. This difference in blue response is caused by lower light absorption of the HWCVD layers (compared to microwave CVD; ECN) and better surface passivation (compared to parallel plate PECVD; IMEC). The application of HW SiN_x as a passivating antireflection layer on mc‐Si solar cells leads to efficiencies comparable to those with optimized PECVD SiN_x coatings, although HWCVD is performed at a much higher deposition rate. Copyright © 2007 John Wiley & Sons, Ltd.     

硅系太阳电池表面钝化技术比较

通过对硅片的少数载流子有效寿命、硅太阳电池的反射损失和光谱响应这三个方面的研究,比较了目前主要的硅太阳电池表面钝化技术,对这些钝化技术的优缺点进行了分析和评价.从上述三个方面的比较可以看出,RTO/SiNx堆叠钝化技术在提高硅太阳电池性能上是最优的,具有良好的应用前景.     

An effective way to simultaneous realization of excellent optical and electrical performance in large‐scale Si nano/microstructures

Despite the optical advantage of near‐zero reflection, the silicon nanowire arrays (SiNWs)‐based solar cells cannot yet achieve satisfactory high efficiency because of the serious surface recombination arising from the greatly enlarged surface area. The trade‐off between reflection and recombination fundamentally prevents the conventional SiNWs structure from having both minimal optical and electrical losses. Here, we report the simultaneous realization of the best optical anti‐reflection (the solar averaged reflectance of 1.38%) and electrical passivation (the surface recombination velocity of 44.72 cm/s) by effectively combining the Si nano/microstructures (N/M‐Strus) with atomic‐layer‐deposition (ALD)‐Al₂O₃ passivation. The composite structures are prepared on the pyramid‐textured Si wafers with large‐scale 125 × 125 mm² by the two‐step metal‐assisted chemical etching method and the thermal ALD‐Al₂O₃ treatment. Although the excellent optical anti‐reflection is observed because of the complementary contribution of Si N/M‐Strus at short wavelength and ALD‐Al₂O₃ at long wavelength, the low recombination has also been realized because the field effect passivation is enhanced for the longer and thinner SiNWs through the more effective suppression of the minority carrier movement and the reduction of the pure‐pyramid‐textured surface recombination. We have further numerically modeled the Al₂O₃‐passivated Si N/M‐Strus‐based solar cell and obtain the high conversion efficiency of 21.04%. The present work opens a new way to realize high‐efficiency SiNWs‐based solar cells. Copyright © 2014 John Wiley & Sons, Ltd.     

Laser processing of Al2O3/a‐SiCx:H stacks: a feasible solution for the rear surface of high‐efficiency p‐type c‐Si solar cells

We explore the potential of laser processing aluminium oxide (Al₂O₃)/amorphous silicon carbide (a‐SiC_x:H) stacks to be used at the rear surface of p‐type crystalline silicon (c‐Si) solar cells. For this stack, excellent quality surface passivation is measured with effective surface recombination velocities as low as 2 cm/s. By means of an infrared laser, the dielectric film is locally opened. Simultaneously, part of the aluminium in the Al₂O₃ film is introduced into the c‐Si, creating p+ regions that allow ohmic contacts with low‐surface recombination velocities. At optimum pitch, high‐efficiency solar cells are achievable for substrates of 0.5–2.5 Ω cm. Copyright © 2012 John Wiley & Sons, Ltd.     

Highest efficiency rapid thermal processed multicrystalline silicon solar cells

The formation of pn junctions and surface passivation by rapid thermal processing is being proved as a new and competitive method for silicon solar cell production. As the main process mechanisms are enhanced, the total process time at high temperature can be kept in the minute range, for the realization of emitter, back surface field (BSF) and surface passivation. In this work, we demonstrate for the first time that this knowledge, avoiding any in‐situ annealing step acquired on the sc‐Si, can also be applied on industrial mc‐Si (Polix_©) without bulk degradation, leading to a record conversion efficiency of 16·7%. Copyright © 2001 John Wiley & Sons, Ltd.     

Bulk resistivity optimization for low‐bulk‐lifetime silicon solar cells

Guidelines are presented which are designed to achieve planar solar cell efficiencies as high as 17.5% using existing fabrication technologies and silicon substrates with lifetimes as low as 20 μs. Device simulations are performed to elucidate the need and impact of base doping optimization for different back‐surface passivation schemes, cell thicknesses, emitter profiles, and degrees of dopant–defect interaction. Results indicate that optimal resistivity is a function of back‐surface passivation, with the aluminum back‐surface field (BSF) requiring the highest resistivity, the oxide/nitride stack passivation excelling at an intermediate resistivity, and the ohmic contact needing the lowest resistivity. A comparison of simulated 300 and 100 μm cells shows that thinner cells magnify the differences in optimal resistivity for the three back‐surface passivation schemes. A lifetime model is used to account for dopant–defect interaction that can lower bulk lifetime at higher doping levels. It is demonstrated that cell efficiency decreases and optimal resistivity increases at higher levels of dopant–defect interaction. Simulated devices with an optimized base doping showed an efficiency improvement of as much as 2% (absolute) compared with identical devices with a typical base doping level (1.6 or 1.8 Ω cm) and bulk lifetime of 20 μs. Copyright © 2001 John Wiley & Sons, Ltd.     

Optimization of interdigitated back contact silicon heterojunction solar cells: tailoring hetero‐interface band structures while maintaining surface passivation

Interdigitated back contact silicon heterojunction (IBC‐SHJ) solar cells have the potential for high open circuit voltage (V_OC) due to the surface passivation and heterojunction contacts, and high short circuit current density (J_SC) due to all back contact design. Intrinsic amorphous silicon (a‐Si:H) buffer layer at the rear surface improve the surface passivation hence V_OC and J_SC, but degrade fill factor (FF) from an “S” shape J–V curve. Two‐dimensional (2D) simulation using “Sentaurus device” demonstrates that the low FF is related to the valence band offset (energy barrier) at the hetero‐interface. Three approaches to the buffer layer are suggested to improve the FF: (1) reduced thickness, (2) increased conductivity, and/or (3) reduced band gap. Experimental IBC‐SHJ solar cells with reduced buffer thickness (<5 nm) and increased conductivity with low boron doping significantly improves FF, consistent with simulation. However, this has only marginal effect on efficiency since J_SC and V_OC also decrease due to poor surface passivation. A narrow band gap a‐Si:H buffer layer improves cell efficiency to 13.5% with unoptimized passivation quality. These results demonstrate that tailoring the hetero‐interface band structure is critical for achieving high FF. Simulations predicts that efficiences >23% are possible on planar devices with optimized pitch dimensions and achievable surface passivation, and 26% with light trapping. This work provides criterion to design IBC‐SHJ solar cell structures and optimize cell performance. Copyright © 2010 John Wiley & Sons, Ltd.     

High‐efficiency black silicon interdigitated back contacted solar cells on p‐type and n‐type c‐Si substrates

This work demonstrates the high potential of Al₂O₃ passivated black silicon in high‐efficiency interdigitated back contacted (IBC) solar cells by reducing surface reflectance without jeopardizing surface passivation. Very low reflectance values, below 0.7% in the 300–1000 nm wavelength range, together with striking surface recombination velocities values of 17 and 5 cm/s on p‐type and n‐type crystalline silicon substrates, respectively, are reached. The simultaneous fulfillment of requirements, low reflectance and low surface recombination, paves the way for the fabrication of high‐efficiency IBC Si solar cells using black silicon at their front surface. Outstanding photovoltaic efficiencies over 22% have been achieved both in p‐type and n‐type 9‐cm² cells. 3D simulations suggest that efficiencies of up to 24% can be obtained in the future with minor modifications in the baseline fabrication process. Copyright © 2015 John Wiley & Sons, Ltd.     

SiOyNx/SiNx stack: a promising surface passivation layer for high‐efficiency and potential‐induced degradation resistant mc‐silicon solar cells

A thin SiO_yN_x film was inserted below a conventional SiN_x antireflection coating used in c‐Si solar cells in order to improve the surface passivation and the solar cell's resistance to potential‐induced degradation (PID). The effect of varying the flow ratio of the N₂O and SiH₄ precursors and the deposition temperature for the SiO_yN_x thin film upon material properties were systematically investigated. An excellent surface passivation was obtained on FZ p‐type polished silicon wafers, with the best results obtained with a SiO_yN_x film deposited at a very low temperature of 130 °C and with an optical refractive index of 1.8. In the SiO_yN_x/SiN_x stack structure, a SiO_yN_x film with ~6 nm thickness is sufficient to provide excellent surface passivation with an effective surface recombination velocity S_eff < 2 cm/s. Furthermore, we applied the optimized SiO_yN_x/SiN_x stack on multicrystalline Si solar cells as a surface passivation and antireflection coating, resulting in a 0.5% absolute average conversion efficiency gain compared with that of reference cells with conventional SiN_x coating. Moreover, the cells with the SiO_yN_x/SiN_x stack layers show a significant increase in their resistance to PID. Nearly zero degradation in shunt resistance was obtained after 24 h in a PID test, while a single SiN_x‐coated silicon solar cell showed almost 50% degradation after 24 h. Copyright © 2016 John Wiley & Sons, Ltd.     

18.45%‐Efficient Multi‐Crystalline Silicon Solar Cells with Novel Nanoscale Pseudo‐Pyramid Texture

Silicon‐based cells could convert more solar energy to electrical energy if the cells could absorb more light. However, the nanostructured cells have demonstrated relatively low power conversion efficiency even when its reflection is very low; thus, they are still far from becoming real products of the photovoltaic industry. Here, nanoscale pseudo‐pyramid textured multi‐crystalline silicon (Pmc‐Si) solar cells, with the best efficiency of ≈18.45%, are fabricated by using a metal‐catalyzed chemical etching plus a post alkaline etching on an industrial production line. Such Pmc‐Si solar cells have showed similar light trapping ability as single crystalline silicon solar cells of micrometer pyramid texture, and the improved efficiency is mainly ascribed to its enhanced light absorption while the nanostructured surface still keeps acceptable passivation quality, that is, the short‐circuit current density has an increase of ≈300 mA cell^–1, while the open‐circuit voltage has only a slight decrease of ≈1 mV. Further elevations of the efficiency are expected by optimizing both micrometer‐ and nanotextures, and exploring more effective passivation technique. More excitingly, the technique presented here has been verified in the production line for several batches as a real technique of low cost and high efficiency.