SBS／MMA／BA／MAA四元接枝共聚及其产物粘接性能

研究了SBS与甲基丙烯酸（MAA）和甲基丙烯酸甲酯（MMA）,丙烯酸丁酯（BA）的四元接枝共聚,探讨了MMA／BA质量比,MMA与BPO用量,反应时间,反应温度及固化时间对粘接性能的影响,并将该四元接枝胶的性能与三元胶和SBS／MMA／BA／AA四元胶进行了比较,结果发现：该四元胶对聚烯烃的粘接强度及室温固化性能优于SBS／MMA／BA三元胶,尤其与异氰酸酯配合使用时,其效果更佳,而且该四元胶的粘接强度,耐水及耐热性能均优于SBS／MMA／BA／AA四元胶。     

BA／VAc／AN／AA共聚乳液胶粘剂的研制

介绍了一种丙烯酸丁酯／醋酸乙烯酯／丙烯腈／丙烯酸四元共聚乳液胶粘剂的制备方法,该胶具有良好的耐黄变性,可替代天然橡胶胶乳应用于EVA低发泡体与腈纶绒面布的复合。     

VAC／BA／MMA三元共聚物的合成及其防水性能

本文介绍VAC、BA与MMA共聚合提高聚合物防水性的规律。共聚物用作胶粘剂,固化后70℃水煮30h不开胶。—30℃冷冻30天胶的性能不变。粘接PVC装饰膜其性能符合HG4—1197—79部颁标准。共聚物对于木材、玻璃、陶瓷、瓷砖、混凝土墙面、壁纸、薄铁、包装纸箱密封条、均有良好的粘接性。     

CR/MMA/SBS三元接枝胶粘剂

本文采用甲基丙烯酸甲酯(MMA)与氯丁橡胶(CR)和苯乙烯-丁二烯-苯乙烯嵌段共聚物(SBS)进行溶液接技聚合制成具有良好性能的CR/MMA/SBS三元接枝胶粘利。从而解决了一些制鞋材枓的难粘问题。     

VAc/BA/AA共聚乳液胶粘剂的制备与性能研究

以醋酸乙烯酯(VAc)为原料、丙烯酸(AA)和丙烯酸丁酯(BA)为改性单体、过硫酸铵(APS)为引发剂、辛基酚聚氧乙烯醚(OP-10)和烷基酚聚氧乙烯醚琥珀酸酯磺酸钠(MS-1)为新型乳化剂体系,采用半连续种子乳液聚合法制备了VAc/BA/AA共聚乳液胶粘剂。研究了引发剂用量、乳化剂配比及用量、单体及种子单体用量对乳液性能的影响,并采用FT-IR对其结构进行表征。研究结果表明,当m(VAc)∶m(BA)∶m(AA)∶m(APS)∶m(OP-10)∶m(MS-1)=83∶14∶3∶0.4∶1.25∶0.25、w(种子单体)=17%(相对于总单体而言)时,乳液的综合性能最佳。     

聚烯烃塑料用胶粘剂SBS／MMA／BA／MAA的合成与性能研究

以甲基丙烯酸（MAA）为功能单体,与SBS和甲基丙烯酸甲酯（MMA）、丙烯酸丁酯（BA）进行四元接枝共聚,合成了聚烯烃塑料用胶粘剂,探讨了不同溶剂、MMA／BA配比、MAA和BPO用量以及固化时间对粘接性能的影响,并对该四元接枝胶的性能与三元胶和SBS／MMA／BA／AA四元接枝胶进行了比较。结果发现：四元接枝胶性能优于三元胶,特别是与异氰酸酯配合时,剪切强度、固化速度明显提高,四元胶的优化配方是120＃汽油：甲苯：乙酸乙酯为8：1：1,MMA：BA配比3：1,MAA加入量7份,BPO用量1．5－2份（以100份SBS计）。     

St/MMA/(mono-BM)三元无皂乳液共聚动力学

在PVA助溶稳定剂的作用下,通过间歇法无皂种子乳液聚合制备了St/MMA/(mono-BM)三元共聚物。研究了单体总浓度[M],引发剂浓度[I],PVA浓度[P],聚合温度对St/MAA/(mono-BM)无皂种子乳液聚合动力学的影响。实验表明:Rp∝[M]2.38,-M w∝[M]0.62;Rp∝[I]0.883,-M w∝[I]-0.71。采用粒度测定仪,凝胶色谱和示差扫描量热法表征了共聚物乳液。粒度分析显示乳液总平均粒径为55 nm;DSC谱图显示三元共聚物只有单个Tg,聚合体系不存在微相分离区;GPC谱表明共聚物分子质量分布仅为1.28,接近单分散体系。     

SBS／MMA—BA接技贴塑胶的研究

本文选用ＭＭＡ和ＢＡ为接枝单体，对ＳＢＳ进行溶液接枝共聚改性，并配合增粘树脂制备了贴塑胶。探讨了单体用量、引发剂用量和反庆温度对接枝共聚反应的影响。并用红外光谱验证了接枝共聚物的存在，阐述了溶剂和增粘树脂的选用原则。试验结果表明，该胶对纸／ＢＯＰＰ的复合具有良好的粘接强度。     

VAC-BA-MAA三元乳液共聚制人造花底胶

本文论述了VAC－BA－MAA为混合单体三元共聚制取乳液，乳液加增稠剂配制成胶，该胶手感柔软，光泽度高，可作人造花底胶使用。     

丙烯酸酯—醋酸乙烯共聚乳液胶粘剂的研究

介绍了丙烯酸酯－醋酸乙烯共聚乳液胶粘剂的合成工艺,主要影响因素和其性能特点。     

VAC/BA/AN/AA四元共聚乳液研制

研制VAC／BA／AN／AA四元共聚乳液，讨论乳液的稳定性、耐水性、耐寒性、粘接强度和抗蠕变性。     

水乳型非织造布用粘合剂的研制

研究常用水乳型非织造布用粘合剂的主单体、交联单体、乳化剂、引发剂选择与用量以及聚合生产工艺对产品性能的影响。     

Preparation of high solids stable translucent nanolatexes of MMA/BA copolymers and MMA/BA/Veova-10 terpolymers with low MFFT using green industrial surfactants

In this study, high solids (∼40 wt%) stable translucent nanolatexes of MMA/BA copolymers and MMA/BA/Veova-10 terpolymers with MFFT ≤ 0 °C were synthesized by a modified semi-continuous microemulsion copolymerization. Ammonium persulfate was used as initiator and a redox system for post-polymerization to reduce the free monomers and achieve over 99.9% conversion. Methacrylic acid or acrylic acid at 1 wt% (calculated on monomers) and a combination of various “green” industrial anionic and non-ionic surfactants free of alkylphenol ethoxylates (APEO-free) at low concentrations (up to 10 wt% on monomers) were used. The resulting latexes were composed of polymer nanoparticles with average diameter size 50–80 nm and low polydispersity index. These friendly to the environment latexes can be potentially used as impregnation primer instead of classic solvent acrylic primers in architectural coatings.     

三单体接枝共聚物对PP/云母填充体系性能的影响

将固相法接枝合成的聚丙烯与甲基丙烯酸甲酯／马来酸酐／丙烯酸丁酯的接枝共聚物PP-g-MMA/MAH/BA应用于PP／云母填充体系。研究接枝物对体系的力学性能、微观形态、热性能、加工性能及表面性能等的影响。结果表明，在PP／云母填充体系中加入适当的三单体接枝共聚物，可提高体系的拉伸强度、弯曲强度、维卡软化点及表面极性，并降低制品的成型收缩率；同时，体系的加工性能也得到改善。     

反应性乳化剂对MMA/BA乳液聚合的影响

将不同性质的反应性乳化剂应用于MMA／BA乳液聚合，对聚合过程的特性、乳胶粒子的大小和形态及乳液的性能进行了研究，发现不同性质的反应性乳化剂对无皂乳液聚合有不同的影响。     

有机硅改性VAc/BA/AA共聚乳液胶粘剂的研究

介绍了有机硅改性 VAc/BA/AA共聚乳液胶粘剂的合成工艺 ,讨论了预乳化工艺、乳化剂体系、PVC及改性共聚单体对粘接强度、耐水性等乳液性能的影响 ;结果表明 ,通过采用预乳化工艺、适宜的乳化剂体系和 PVA,引入有机硅、BA、AA等单体对 PVAc乳液进行共聚改性 ,可以合成综合性能优异的乳液胶粘剂     

SBS/MMA-BA接枝贴塑胶的研究

本文选用MMA和BA为接技单体，对SBS进行溶液接枝共聚改性，并配合增粘树脂制备了贴塑胶。探讨了单体用量、引发剂用量和反应温度对接枝共聚反应的影响，并用红外光谱验证了接枝共聚物的存在，阐述了溶剂和增粘树脂的选用原则。试验结果表明．该胶对纸／BOPP的复合具有良好的粘接强度。     

聚乙烯醇在二元和三元共聚乳液中的作用

本文通过实验讨论了ＰＶＡ对ＶＡＣ／ＭＭＡ二元共聚乳液性能的影响及对ＶＡＣ／ＢＡ／ＭＭＡ三元共聚乳的作用。     

无三苯CR/SBS/MMA/BA自交联鞋用胶粘剂的研制

采用复合引发剂 ,以N 羟甲基丙烯酰胺 (NAM )及丙烯酸 (AA)为功能单体 ,与CR、苯乙烯 丁二烯嵌段共聚物 (SBS)、甲基丙烯酸甲酯 (MMA)和丙烯酸丁酯 (BA)进行多元共混接枝共聚 ,再配以混合型增粘树脂 ,研制出不含苯、甲苯和二甲苯 (简称三苯 )自交联环保型鞋用胶粘剂。探讨了SBS用量、MMA/BA配比、功能单体NAM及AA用量对胶粘剂粘合性能的影响。结果表明 ,CR/SBS/MMA/BA/AA/NAM自交联型接枝胶粘剂对非极性鞋材的粘合性能明显优于CR/MMA/BA三元接枝胶和CR/SBS/MMA/BA四元接枝胶。