1.
粉煤灰负载TiO2光催化剂及其光催化活性的研究 总被引:7,自引:0,他引:7
以粉煤灰分子筛为载体 ,采用溶胶凝胶法制备TiO2 负载膜光催化剂 ,通过XRD、SEM、BET比表面积等技术 ,对粉煤灰分子筛负载TiO2 光催化剂的形貌和晶型结构进行了表征 ,考察了制备条件和二氧化钛负载量对TiO2 光催化活性的影响。 相似文献
2.
3.
用溶胶-凝胶法制得的纳米Fe3+/TiO2分别以玻璃和琼脂糖为负载体,采用浸渍-提拉法制备Fe3+/TiO2玻璃负载膜,水热合成法制得Fe3+/TiO2琼脂糖凝胶负载膜,通过降解某制药厂的制药废水,探讨两种负载膜对纳米Fe3+/TiO2光催化活性的影响及用琼脂糖为载体的可行性。结果表明,两种负载膜中纳米Fe3+/TiO2的晶相不变,但琼脂糖凝胶负载膜中纳米Fe3+/TiO2粒子的团聚较少,且不易脱落,重复使用性能高,光催化活性明显较Fe3+/TiO2玻璃负载膜强,从而显示了琼脂糖为载体的可行性、优越性和实用性。 相似文献
4.
用溶胶-凝胶法制得的纳米Fe3+/TiO2分别以玻璃和琼脂糖为负载体,采用浸渍-提拉法制备Fe3+/TiO2玻璃负载膜,水热合成法制得Fe3+/TiO2琼脂糖凝胶负载膜,通过降解某制药厂的制药废水,探讨两种负载膜对纳米Fe3+/TiO2光催化活性的影响及用琼脂糖为载体的可行性。结果表明,两种负载膜中纳米Fe3+/TiO2的晶相不变,但琼脂糖凝胶负载膜中纳米Fe3+/TiO2粒子的团聚较少,且不易脱落,重复使用性能高,光催化活性明显较Fe3+/TiO2玻璃负载膜强,从而显示了琼脂糖为载体的可行性、优越性和实用性。 相似文献
5.
6.
7.
8.
9.
10.
以蜂窝陶瓷为载体,采用溶胶-凝胶法在蜂窝陶瓷结构表面负载了多层TiO2光催化剂,并对其进行了显微结构分析和XRD物相分析,考察了蜂窝陶瓷镀膜前后吸附性能。结果表明:负载的TiO2光催化剂主要以锐钛矿形式存在,同时伴有少量金红石形态;蜂窝陶瓷负载TiO2光催化剂后其微孔结构及吸附性能没有明显变化,蜂窝陶瓷负载TiO2后对甲基橙的降解率在初始阶段不及TiO2粉体高,但是随着反应时间的延长,TiO2粉体将发生沉降团聚而活性降低,负载在蜂窝陶瓷上的TiO2对甲基橙的降解率高于粉体。 相似文献
11.
制备条件对新颖负载型TiO_2光催化剂活性的影响 总被引:8,自引:0,他引:8
开发新颖玻璃弹簧填料型载体 ,采用浸渍 -烧结法制备纳米 Ti O2 负载型光催化剂 ,研究不同制备条件对其催化活性的影响。结果表明 ,该负载型催化剂较佳制备条件为 :P2 5 Ti O2 浸渍浆料浓度为 0 .5 % ,浸渍次数为 5次 ,焙烧温度为 40 0°C、时间为 3 h。该负载型光催化剂具有高的光照射表面积 /体积比、空隙率很大、床层压降低 ,以及在催化剂填充空间光辐射分布较均匀 ,导致有效的光催化反应体积成倍增加的优点。 相似文献
12.
13.
14.
N/TiO2光催化剂的制备及掺杂过程分析 总被引:1,自引:0,他引:1
以饱和尿素溶液水解沉淀钛酸四丁酯制备水合TiO2,再于400~700℃的空气气氛下煅烧2 h,制得淡黄色的N/TiO2光催化剂. 对N/TiO2光催化剂的物相、粒径、比表面积及光吸收性能进行了测试和表征,结果表明,样品的粒径为10~30 nm,比表面积为30~70 m2/g,能吸收400 nm以上的可见光;N/TiO2光催化剂在波长420 nm的荧光灯激发下,经180 min对2,4-二氯苯酚的光催化降解率超过40%. 通过TG-DTA, FT-IR及XPS等测试,分析了N/TiO2光催化剂的氮掺杂过程,表明掺杂氮源均匀存在于水合TiO2中,并在TiO2从无定型转为锐钛矿型的过程中以T?-N化学键的形式进入了TiO2的晶格. 相似文献
15.
Photodegradation of Methylene Blue in a Batch Fixed Bed Photoreactor Using Activated Carbon Fibers Supported TiO2 Photocatalyst 总被引:1,自引:0,他引:1
A batch fixed bed photoreactor, using felt-form activated carbon fibers (ACF) supported TiO2 photocatalyst (TiO2/ACF), was developed to carry out photocatalytic degradation of methylene blue (MB) solution. The effects of TiO2 particle size, loaded TiO2 amount, initial MB concentration, airflow rate and successive run on the decomposition rate were investigated. The results showed that photodegradation process followed a pseudo-first-order reaction kinetic law. The apparent first-order reaction constant kapp was larger than 0.047 min-1 with half reaction time t1/2 shorter than 15 min, which was comparable to reported data using suspended Degussa P-25 TiO2 particles. The high degradation rate was mainly attributed to adsorption of MB molecules onto the surface of TiO2/ACF. The photocatalytic efficiency still remained nearly 90% after 12 successive runs, showing that successive usage of the designed photoreactor was possible. The synergic enhancement effect in combination of adsorption with ACF and photodegradation with TiO2 was proved by comparing MB removal rates in the successive degradation and adsorption runs, respectively. 相似文献
16.
负载TiO2城市污泥改性物光催化剂的制备 总被引:1,自引:0,他引:1
用城市污水处理厂的剩余污泥作原料,炭化制备活性炭吸附剂。以钛酸丁酯和无水乙醇为原料,乙酸为水解抑制剂,采用溶胶-凝胶法制备纳米TiO2粉体,利用浸渍-烧结法将其负载于制备的污泥活性炭上,获得TiO2/AC光催化剂。以重金属离子Hg2+为目标污染物进行光催化去除实验,考察了抑制剂用量、TiO2的负载量、煅烧温度等对TiO2/AC催化性能的影响。结果表明,当CH3COOH∶Ti(OBu)4=0.8~1.0时,对Hg2+的催化去除效果较好;TiO2负载量为33.3%时,TiO2/AC光催化剂具有良好的吸附性能和更高的催化活性;煅烧温度直接影响晶体的结构,550℃煅烧时生成的混合晶体具有较高的催化性能。在最佳条件下制备的TiO2/AC光催化剂对水溶液中20 mg/L的Hg2+的光催化去除率可达到88.5%。 相似文献
17.
18.
光催化降解有机磷农药的研究-玻璃弹簧负载TiO2与悬浮体系TiO2的比较 总被引:5,自引:2,他引:3
研究了利用玻璃弹簧填料为载体,采用浸涂烧结法制备负载型纳米TiO_2的过程、及其对有机磷农药敌百虫和乐果的光催化降解效果,并与单TiO_2粉末做了简单对比。结果表明:低浓度的两种有机磷农药,8W紫外灯照射2h时,无负载TiO_2对敌百虫和乐果的降解率分别为56.7%和68.6%;而玻璃弹簧负载TiO_2对二者的降解率分别为76.6%和88.7%;并且玻璃弹簧上负载的TiO_2光催化活性没有减弱,可以连续使用。同时还研究了改良型P25(P25/20)悬浮体系中的光催化降解效果,并展望了其在军事防化洗消领域中的应用前景。 相似文献
19.
20.
以磷钼酸铵为敏化剂,采用固相研磨法合成了磷钼酸铵敏化光催化剂TiO_2-PMoN。通过X射线衍射、红外吸收和紫外-可见吸收光谱法对样品进行表征,以罗丹明B为模拟污染物,评价其光催化活性。结果表明,所得TiO_2-PMoN催化剂为锐钛矿型和金红石型的混合类型,与纯磷钼酸铵相比,TiO_2-PMONH_4光催化剂在(360~850)cm~(-1)的吸收出现了宽化现象,磷钼酸铵敏化使TiO_2在可见光区的吸收增强,吸收边红移,太阳光照射40min,TiO_2-PMoN光催化降解罗丹明B的脱色率为95%。 相似文献