Synthesis and characterization of LiNi0.6Mn0.4−xCoxO2 as cathode materials for Li-ion batteries

LiNi_0.6Co_xMn_0.4−xO₂ (x = 0.05, 0.10, 0.15, 0.2) cathode materials are prepared, and their structural and electrochemical properties are investigated using X-ray diffraction (XRD), scanning electron microscope (SEM), X-ray photoelectron spectroscopy (XPS), differential scanning calorimetric (DSC) and charge–discharge test. The results show that well-ordering layered LiNi_0.6Co_xMn_0.4−xO₂ (x = 0.05, 0.10, 0.15, 0.2) cathode materials are successfully prepared in air at 850 °C. The increase of the Co content in LiNi_0.6Mn_0.4−xCo_xO₂ leads to the acceleration of the grain growth, the increase of the initial discharge capacity and the deterioration of the cycling performance of LiNi_0.6Mn_0.4−xCo_xO₂. It also leads to the enhancement of the ratio Ni³⁺/Ni²⁺ in LiNi_0.6Co_xMn_0.4−xO₂, which is approved by the XPS analysis, resulting in the increase of the phase transition during cycling. This is speculated to be main reason for the deteriotion of the cycling performance. All synthesized LiNi_0.6Co_xMn_0.4−xO₂ samples charged at 4.3 V show exothermic peaks with an onset temperature of larger than 255 °C, and give out less than 400 J g⁻¹ of total heat flow associated with the peaks in DSC analysis profile, exhibiting better thermal stability. LiNi_0.6Co_0.05Mn_0.35O₂ with low Co content and good thermal stability presents a capacity of 156.6 mAh g⁻¹ and 98.5% of initial capacity retention after 50 cycles, showing to be a promising cathode materials for Li-ion batteries.     

Effect of Bi oxide surface treatment on 5 V spinel LiNi0.5Mn1.5−xTixO4

The effect of Bi surface treatment on LiNi_0.5Mn_1.5−xTi_xO₄ was examined. As a result, Bi surface film around 20 nm thick was confirmed to be fabricated on the surface of 5 V spinel LiNi_0.5Mn_1.5−xTi_xO₄ by transmission electron microscopy (TEM) and energy dispersion X-ray spectrometer (EDX) analysis. The Bi compound was confirmed to be Bi₂O₃ by X-ray diffraction analysis. Cycle behavior was also found to be improved by Bi treatment. A retention capacity of up to around 85% was achieved after 500 cycles at 20 °C, while a retention capacity as high as 70% was obtained after 500 cycles, even at 45 °C. Storage performance was also improved with Bi treatment. Recovery capacity of more than 90% was obtained with Bi treatment after storage for 1 week at 60 °C. The increased resistance in storage was also suppressed with Bi treatment, which would be due to the suppression of electrolyte decomposition by the Bi coating film. It was found that Bi treatment had the effect of decreasing the dissolution of Mn, Ni and Ti of the elements of the cathode active material, due to inductively coupled plasma (ICP) analysis. Based on these results, the Bi surface coating was found to have a remarkable effect on the improvement of the cells with 5 V spinel.     

Structural and transport properties of LixNi1−y−zCoyMnzO2 cathode materials

In this work structural and transport properties of layered LiNi_1−y−zCo_yMn_zO₂ (y = 0.25, 0.35, 0.5 and z = 0.1) cathode materials are presented. In the considered group of oxides, LiNi_1−y−zCo_yMn_zO₂, there is no clear correlation between electrical conductivity and the a parameter (M-M distance in the octahedra layers). A non-monotonic modification of electrical properties of Li_xNi_0.65Co_0.25Mn_0.1O₂ cathode materials is observed upon lithium deintercalation.     

Effect of Cr doping on the structural,electrochemical properties of Li[Li0.2Ni0.2−x/2Mn0.6−x/2Crx]O2 (x = 0, 0.02, 0.04, 0.06, 0.08) as cathode materials for lithium secondary batteries

Prospective positive-electrode (cathode) materials for a lithium secondary battery, viz., Li[Li_0.2Ni_0.2−x/2Mn_0.6−x/2Cr_x]O₂ (x = 0, 0.02, 0.04, 0.06, 0.08), were synthesized using a solid-state pyrolysis method. The structural and electrochemical properties were examined by means of X-ray diffraction, cyclic voltammetry, SEM and charge–discharge tests. The results demonstrated that the powders maintain the α-NaFeO₂-type layered structure regardless of the chromium content in the range x ≤ 0.08. The Cr doping of x = 0.04 showed improved capacity and rate capability comparing to undoped Li[Li_0.2Ni_0.2Mn_0.6]O₂. ac impedance measurement showed that Cr-doped electrode has the lower impedance value during cycling. It is considered that the higher capacity and superior rate capability of Cr-doping samples would be ascribed to the reduced resistance of the electrode during cycling.     

Pillared layered Li1−2xCaxCoO2 cathode materials obtained by cationic exchange under hydrothermal conditions

A simple method has been employed to prepare pillared layered Li_1−2xCa_xCoO₂ cathode materials by cationic exchange under hydrothermal conditions. The synthesized materials were characterized by means of X-ray diffraction (XRD), inductively coupled plasma-atomic emission spectroscopy (ICP-AES), field emission scanning electron microscope (FE-SEM) and galvanostatic charge–discharge cycling. The XRD data of the products show that they are single phases and retain the layered α-NaFeO₂ type structure. The FE-SEM images of the materials prepared by hydrothermal method show uniform small particles, and the particle size of the materials is about 200 nm. The initial discharge specific capacities of layered LiCoO₂ and pillared layered Li_0.946Ca_0.027CoO₂ cathode materials calcined at 800 °C for 5 h within the potential range of 3.0–4.3 V (vs. Li⁺/Li) are 144.6 and 142.3 mAh g⁻¹, respectively, and both materials retain good charge–discharge cycling performance. However, with increasing upper cutoff voltage, the pillar effect of Ca²⁺ in Li_1−2xCa_xCoO₂ becomes more significant. The pillared layered Li_0.946Ca_0.027CoO₂ has a higher capacity with an initial discharge specific capacity of 177.9 and 215.8 mAh g⁻¹ within the potential range of 3.0–4.5 and 4.7 V (vs. Li⁺/Li), respectively, and retains good charge–discharge cycling performance.     

Performance of LiNi0.5Mn1.5O4 prepared by solid-state reaction

LiNi_0.5Mn_1.5O₄ was prepared through a solid-state reaction using various Ni precursors. The effect of precursors on the electrochemical performance of LiNi_0.5Mn_1.5O₄ was investigated. LiNi_0.5Mn_1.5O₄ made from Ni(NO₃)₂·6H₂O shows the best charge–discharge performance. The reversible capacity of LiNi_0.5Mn_1.5O₄ is about 145 mAh g⁻¹ and remained 143 mAh g⁻¹ after 10 cycles at 3.0–5.0 V. The XRD results showed that the precursors and the dispersion methods had significant effect on their phase purity. Pure spinel phase can be obtained with high energy ball-milling method and Ni(NO₃)₂·6H₂O as precursor. Trace amount of NiO and Li₂MnO₃ phase were detected in LiNi_0.5Mn_1.5O₄ with manual-mixture method and using Ni(CH₃COO)₂·6H₂O, NiO and Ni₂O₃ as precursors.     

Effect of CO2 on layered Li1+zNi1−x−yCoxMyO2 (M = Al,Mn) cathode materials for lithium ion batteries

We investigated the effect of CO₂ on layered Li_1+zNi_1−x−yCo_xM_yO₂ (M = Al, Mn) cathode materials for lithium ion batteries which were prepared by solid-state reactions. Li_1+zNi_(1−x)/2Co_xMn_(1−x)/2O₂ (Ni/Mn mole ratio = 1) singularly exhibited high storage stability. On the other hand, Li_1+zNi_0.80Co_0.15Al_0.05O₂ samples were very unstable due to CO₂ absorption. XPS and XRD measurements showed the reduction of Ni³⁺ to Ni²⁺ and the formation of Li₂CO₃ for Li_1+zNi_0.80Co_0.15Al_0.05O₂ samples after CO₂ exposure. SEM images also indicated that the surfaces of CO₂-treated samples were covered with passivation films, which may contain Li₂CO₃. The relationship between CO₂-exposure time and CO₃²⁻ content suggests that there are two steps in the carbonation reactions; the first step occurs with the excess Li components, Li₂O for example, and the second with LiNi_0.80Co_0.15Al_0.05O₂ itself. It is well consistent with the fact that the discharge capacity was not decreased and the capacity retention was improved until the excess lithium is consumed and then fast deterioration occurred.     

Potentiostatically deposited nanostructured CoxNi1−x layered double hydroxides as electrode materials for redox-supercapacitors

Cobalt–nickel layered double hydroxides (Co_xNi_1−x LDHs) were deposited onto stainless steel electrodes by the potentiostatic deposition method at −1.0 V vs. Ag/AgCl using various molar ratios of Co(NO₃)₂ and Ni(NO₃)₂ in distilled water. Their structure and surface morphology were studied by using X-ray diffraction analysis, energy dispersive X-ray spectroscopy and scanning electron microscopy. A network of Co_xNi_1−x LDH nanosheets was obtained. The nature of the cyclic voltammetry and charge–discharge curves suggested that the Co_xNi_1−x LDHs exist in the form of solid solutions. The capacitive characteristics of the Co_xNi_1−x LDHs in 1 M KOH electrolyte showed that Co_0.72Ni_0.28 LDHs had the highest specific capacitance value, 2104 F g⁻¹, which is also the highest yet reported value for oxide materials in general.     

Structural and transport properties of layered Li1+x(Mn1/3Co1/3Ni1/3)1−xO2 oxides prepared by a soft chemistry method

In this work structural and transport properties of layered Li_1+x(Mn_1/3Co_1/3Ni_1/3)_1−xO₂ oxides (x = 0; 0.03; 0.06) prepared by a “soft chemistry” method are presented. The excessive lithium was found to significantly improve transport properties of the materials, a corresponding linear decrease of the unit cell parameters was observed. The electrical conductivity of Li_1.03(Mn_1/3Co_1/3Ni_1/3)_0.97O₂ composition was high enough to use this material in a form of a pellet, without any additives, in lithium batteries and characterize structural and transport properties of deintercalated Li_1.03−y(Mn_1/3Co_1/3Ni_1/3)_0.97O₂ compounds. For deintercalated samples a linear increase of the lattice parameter c together with a linear decrease of the parameter a with the increasing deintercalation degree occurred, but only up to 0.4-0.5 mol of extracted lithium. Further deintercalation showed a reversal of the trend. Electrical conductivity measurements performed of Li_1.03−y(Mn_1/3Co_1/3Ni_1/3)_0.97O₂ samples (y = 0.1; 0.3; 0.5; 0.6) showed an ongoing improvement, almost two orders of magnitude, in relation to the starting composition. Additionally, OCV measurements, discharge characteristics and lithium diffusion coefficient measurements were performed for Li/Li⁺/Li_1.03−y(Mn_1/3Co_1/3Ni_1/3)_0.97O₂ cells.     

La1−xSrxCoO3 (x = 0.1-0.5) as the cathode catalyst for a direct borohydride fuel cell

Direct borohydride fuel cells (DBFCs), with a series of perovskite-type oxides La_1−xSr_xCoO₃ (x = 0.1-0.5) as the cathode catalysts and a hydrogen storage alloy as the anode catalyst, are studied in this paper. The structures of the perovskite-type catalysts are mainly La_1−xSr_xCoO₃ (_x = 0.1-0.5) oxides phases. However, with the increase of strontium content, the intensities of the X-ray diffraction peaks of the impure phases La₂Sr₂O₅ and SrLaCoO₄ are gradually enhanced. Without using any precious metals or expensive ion exchange membranes, a maximum current density of 275 mA cm⁻² and a power density of 109 mW cm⁻² are obtained with the Sr content of x = 0.2 at 60 °C for this novel type of fuel cell.     

Synthesis and electrochemical properties of Li1−xFe0.8Ni0.2O2–LixMnO2 (Mn/(Fe + Ni + Mn) = 0.8) material

A new type of Li_1−xFe_0.8Ni_0.2O₂–Li_xMnO₂ (Mn/(Fe + Ni + Mn) = 0.8) material was synthesized at 350 °C in air atmosphere using a solid-state reaction. The material had an XRD pattern that closely resembled that of the original Li_1−xFeO₂–Li_xMnO₂ (Mn/(Fe + Mn) = 0.8) with much reduced impurity peaks. The Li/Li_1−xFe_0.8Ni_0.2O₂–Li_xMnO₂ cell showed a high initial discharge capacity above 192 mAh g⁻¹, which was higher than that of the parent Li/Li_1−xFeO₂–Li_xMnO₂ (186 mAh g⁻¹). We expected that the increase of initial discharge capacity and the change of shape of discharge curve for the Li/Li_1−xFe_0.8Ni_0.2O₂–Li_xMnO₂ cell is the result from the redox reaction from Ni²⁺ to Ni³⁺ during charge/discharge process. This cell exhibited not only a typical voltage plateau in the 2.8 V region, but also an excellent cycle retention rate (96%) up to 45 cycles.     

High power and high capacity cathode material LiNi0.5Mn0.5O2 for advanced lithium-ion batteries

Single-phase lithium nickel manganese oxide, LiNi_0.5Mn_0.5O₂, was successfully synthesized from a solid solution of Ni_1.5Mn_1.5O₄ that was prepared by means of the solid reaction between Mn(CH₃COO)₂·4H₂O and Ni(CH₃COO)₂·4H₂O. XRD pattern shows that the product is well crystallized with a high degree of Li–M (Ni, Mn) order in their respective layers, and no diffraction peak of Li₂MnO₃ can be detected. Electrochemical performance of as-prepared LiNi_0.5Mn_0.5O₂ was examined in the test battery by charge–discharge cycling with different rate, cyclic voltammetry (CV), and electrochemical impedance spectroscopy (EIS). The cycling behavior between 2.5 and 4.4 V at a current rate of 21.7 mA g⁻¹ shows a reversible capacity of about 190 mAh g⁻¹ with little capacity loss after 100 cycles. High-rate capability test shows that even at a rate of 6C, stable capacity about 120 mAh g⁻¹ is retained. Cyclic voltammetry (CV) profile shows that the cathode material has better electrochemical reversibility. EIS analysis indicates that the resistance of charge transfer (R_ct) is small in fully charged state at 4.4 V and fully discharged state at 2.5 V versus Li⁺/Li. The favorable electrochemical performance was primarily attributed to regular and stable crystal structure with little intra-layer disordering.     

Influence of S and Ni co-doping on structure, band gap and electrochemical properties of lithium manganese oxide synthesized by soft chemical method

Ni-doped lithium manganese oxysulfides with a nominal composition of LiNi_xMn_2−xO_4−δS_δ (0 ≤ x ≤ 0.5 and 0 ≤ δ ≤ 0.1) have been synthesized by an alanine-assisted, low-temperature combustion process, followed by calcination at 700 °C in air. Quantitative X-ray phase analyses show that the spinel structure of LiMn₂O₄ is retained for all compositions. However, analysis of the vibrational peaks observed in Fourier transformed infrared (FTIR) spectroscopy suggests that the Fd3m crystal symmetry is retained only up to x ≤ 0.4 and changes to P4₃32 symmetry for x = 0.5. A systematic change in microstructure is observed with increasing Ni content in presence of S. The shape of the particles changes from spherical (LiMn₂O₄) to icosahedron (LiNi_0.2Mn_1.8O_4−δS_δ) to octahedron (LiNi_0.5Mn_1.5O_4−δS_δ). UV-vis spectroscopy shows that the band structure of pristine LiMn₂O₄ is strongly influenced by hybridization among Mn 3d and O 2p orbitals near the Fermi level and the band gap (1.45 eV) gradually decreases with increasing nickel content and reaches the minimum (1.35 eV) for LiNi_0.4Mn_1.6O_4−δS_δ. Electrochemical results on 2032 coin-type cells, fabricated with the synthesized powders as the positive electrode (cathode) and Li metal as the negative electrode (anode), reveal that the substitution of S for O and Ni for Mn in LiMn₂O₄ enhances the structural integrity of the spinel host, which in turn increases the electrochemical cycleability. A high initial discharge capacity of 155 mAh g⁻¹ is obtained for a LiNi_0.4Mn_1.6O_4−δS_δ/Li cell with about 87% capacity retention (135 mAh g⁻¹) after 25 cycles at a current density of 0.2 mA cm⁻². All LiNi_xMn_2−xO_4−δS_δ/Li cells (x = 0.2-0.5) show excellent reversibility with nominal capacity fading (0.04-0.2 mAh per cycle) at a current density of 0.2 mA cm⁻².     

Minimization of the cation mixing in Li1+x(NMC)1−xO2 as cathode material

Li_1+x(Ni_1/3Mn_1/3Co_1/3)_1−xO₂ layered materials were synthesized by the co-precipitation method with different Li/M molar ratios (M = Ni + Mn + Co). Elemental titration evaluated by inductively coupled plasma spectrometry (ICP), structural properties studied by X-ray diffraction (XRD), Rietveld analysis of XRD data, scanning electron microscopy (SEM) and magnetic measurements carried out by superconducting quantum interference devices (SQUID) showed the well-defined α-NaFeO₂ structure with cationic distribution close to the nominal formula. The Li/Ni cation mixing on the 3b Wyckoff site of the interlayer space was consistent with the structural model [Li_1−yNi_y]_3b[Li_x+yNi_{(1−x)/3−y}Mn_(1−x)/3Co_(1−x)/3]_3aO₂ (x = 0.02, 0.04) and was very small. Both Rietveld refinements and magnetic measurements revealed a concentration of Ni²⁺-3b ions lower than 2%; moreover, for the optimized sample synthesized at Li/M = 1.10, only 1.43% of nickel ions were located into the Li sublattice. Electrochemical properties were investigated by galvanostatic charge-discharge cycling. Data obtained with Li_1+x(Ni_1/3Mn_1/3Co_1/3)_1−xO₂ reflected the high degree of sample optimization. An initial discharge capacity of 150 mAh g⁻¹ was delivered at 1 C-rate in the cut-off voltage of 3.0-4.3 V. More than 95% of its initial capacity was retained after 30 cycles at 1 C-rate. Finally, it is demonstrated that a cation mixing below 2% is considered as the threshold for which the electrochemical performance does not change for Li_1+x(Ni_1/3Mn_1/3Co_1/3)_1−xO₂.     

Nonflammable electrolyte for 3-V lithium-ion battery with spinel materials LiNi0.5Mn1.5O4 and Li4Ti5O12

The compatibility between dimethyl methylphosphonate (DMMP)-based electrolyte of 1 M LiPF₆/EC + DMC + DMMP (1:1:2 wt.) and spinel materials Li₄Ti₅O₁₂ and LiNi_0.5Mn_1.5O₄ was reviewed, respectively. The cell performance and impedance of 3-V LiNi_0.5Mn_1.5O₄/Li₄Ti₅O₁₂ lithium-ion cell with the DMMP-based nonflammable electrolyte was compared with the baseline electrolyte of 1 M LiPF₆/EC + DMC (1:1 wt.). The nonflammable DMMP-based electrolyte exhibited good compatibility with spinel Li₄Ti₅O₁₂ anode and high-voltage LiNi_0.5Mn_1.5O₄ cathode, and acceptable cycling performance in the LiNi_0.5Mn_1.5O₄/Li₄Ti₅O₁₂ full-cell, except for the higher impedance than that in the baseline electrolyte. All of the results disclosed that the 3 V LiNi_0.5Mn_1.5O₄/Li₄Ti₅O₁₂ lithium-ion battery was a promising choice for the nonflammable DMMP-based electrolyte.     

Physical and electrochemical properties of spherical Li1+x(Ni1/3Co1/3Mn1/3)1−xO2 cathode materials

A (Ni_1/3Co_1/3Mn_1/3)CO₃ precursor with an uniform, spherical morphology was prepared by coprecipitation using a continuously stirred tank reactor method. The as-prepared spherical (Ni_1/3Co_1/3Mn_1/3)CO₃ precursor served to produce dense, spherical Li_1+x(Ni_1/3Co_1/3Mn_1/3)_1−xO₂ (0 ≤ x ≤ 0.15) cathode materials. These Li-rich cathodes were also prepared by a second synthesis route that involved the use of an M₃O₄ (M = Ni_1/3Co_1/3Mn_1/3) spinel compound, itself obtained from the carbonate (Ni_1/3Co_1/3Mn_1/3)CO₃ precursor. In both cases, the final Li_1+x(Ni_1/3Co_1/3Mn_1/3)_1−xO₂ products were highly uniform, having a narrow particle size distribution (10-μm average particle size) as a result of the homogeneity and spherical morphology of the starting mixed-metal carbonate precursor. The rate capability of the Li_1+x(Ni_1/3Co_1/3Mn_1/3)_1−xO₂ electrode materials, which was significantly improved with increased lithium content, was found to be better in the case of the denser materials made from the spinel precursor compound. This result suggests that spherical morphology, high density, and increased lithium content were key factors in enabling the high rate capabilities, and hence the power performances, of the Li-rich Li_1+x(Ni_1/3Co_1/3Mn_1/3)_1−xO₂ cathodes.     

Structure, morphology, and cathode performance of Li1−x[Ni0.5Mn1.5]O4 prepared by coprecipitation with oxalic acid

The cathode materials Li_1−x[Ni_0.5Mn_1.5]O₄ prepared by coprecipitation from acetate solution by oxalic acid and annealing at 900 °C in air had the preferred disordered Ni and Mn on the 16d octahedral sites of a spinel structure. The coprecipitation method provides better crystallinity than the phase previously obtained by quenching from the melt. Polycrystalline octahedral-shaped particles with smooth surfaces contained trace amounts of a Li_yNi_1−yO impurity that introduced some Mn(III) into the spinel phase. Half-cells cycled at 0.2 C rate between 3.5 and 4.8 V versus Li exhibited a flat voltage V ≈ 4.7 V with a small step at x ≈ 0.5 and a capacity at room temperature of 130 mAh g⁻¹ that showed no fade after 50 cycles. A small capacity fade was initiated with a cut-off voltage ≥4.9 V; a significant capacity loss between 2 and 5 C cycling rates was reversible to 134 mAh g⁻¹ on returning to 0.1 C after 50 cycles at 10 C between 3.5 and 5.0 V.     

Photocatalytic hydrogen production over CuGa2−xFexO4 spinel

Recovery of hydrogen from industrial H₂S waste using spinel photocatalyst was studied. Spinel metal oxide photocatalysts (CuGa_2−xFe_xO₄ for x = 0.8, 0.6 and 0.4) were synthesized by ceramic route. They were loaded with 0.5 and 1 wt% noble metal oxide, RuO_2. Their XRD pattern revealed a single phase cubic spinel crystalline structure for all the catalysts. SEM displayed small size cubic particles with the particle size decreasing with the decrease in iron content. 1 wt% RuO₂ loaded CuGa_1.6Fe_0.4O₄ decomposed H₂S in aqueous 0.5 M KOH solution under visible light (λ ≥ 420 nm) irradiation and generated H₂ to the tune of 10,045 μmol/h, giving rise to a high quantum efficiency of 21% at 510 nm.     

Synthesis and photoelectrochemical study of BiWxV1−xO4+x/2 films by a polymer-assisted method

A series of BiW_xV_1−xO_4+x/2 films were coated on fluorine-doped tin oxide (FTO) glass by a polymer-assisted method and examined as photoelectrodes for photoelectrochemical measurements under Xe lamp light irradiation in a 0.5 M Na₂SO₄ solution. The compositions, structural, optical and morphologic properties of the films were characterized by XPS, XRD, UV–vis and SEM. The results showed the successfully synthesized films and their photoelectrochemical activities, revealing that the amount of tungsten had an important effect on the photoelectrochemical activities of BiW_xV_1−xO_4+x/2 films and the highest incident photon to current conversion efficiency (IPCE) was obtained when x equaled 0.1.     

The influence of compositional change of 0.3Li2MnO3·0.7LiMn1−xNiyCo0.1O2 (0.2 ≤ x ≤ 0.5, y = x − 0.1) cathode materials prepared by co-precipitation

Cathode materials prepared by a co-precipitation are 0.3Li₂MnO₃·0.7LiMn_1−xNi_yCo_0.1O₂ (0.2 ≤ x ≤ 0.4) cathode materials with a layered-spinel structure. In the voltage range of 2.0-4.6 V, the cathodes show more than one redox reaction peak during its cyclic voltammogram. The Li/0.3Li₂MnO₃·0.7LiMn_1−xNi_yCo_0.1O₂ (x = 0.3, y = 0.2) cell shows the initial discharge capacity of about 200 mAh g⁻¹. However, when x = 0.2 and y = 0.1, the cell exhibits a rapid decrease in discharge capacity and poor cycle life.