回火热处理对轧制钛/钢复合板界面组织与性能的影响

研究了500~670 ℃回火热处理对轧制钛/钢复合板界面组织与性能的影响,以期为复合板热加工的工艺参数制定提供指导。对轧态和回火态的钛/钢复合板进行了拉伸、冲击和剪切试验测试,并利用光学显微镜、扫描电镜、X射线衍射等研究手段表征了复合板的界面组织、剪切断口形貌及断口反应相。结果表明,回火热处理后,钛/钢复合板的剪切性能降低,随着回火温度的升高,剪切强度呈现下降趋势。轧态和回火态复合板界面反应相均为β Ti和TiC,其中TiC反应相的厚度随着回火温度的升高呈现增厚趋势。TiC脆性相厚度的增加导致了复合板剪切强度的下降,且使得剪切断口呈现脆性断裂倾向增大,撕裂特征减弱,呈现出明显的平滑断裂特征。     

非对称热轧单面不锈钢-碳钢复合板生产工艺研究

釆用“电子束真空焊接制坯+热轧”的工艺在钢厂热连轧生产线上进行了“316L不锈钢+Q345C碳 钢”的单面不锈钢复合板热轧生产。采用非对称制坯及异步轧制的手段生产出了高品质单面不锈钢复合板,所生 产的不锈钢复合板界面剪切强度大于320 MPa、屈服强度大于370 MPa、抗拉强度大于520 MPa、断后伸长率大于 30%,各项指标均达到GB/T8165-2008的要求。不锈钢层和碳钢层结合度良好,复合界面平直,无明显缺陷,不锈 钢与碳钢之间实现了良好的冶金结合,结合率达100% 。     

热轧不锈钢复合板界面剪切强度测定

 为了相对精确测定复合板结合界面的剪切强度,对热轧不锈钢复合板进行了系列剪切试验。利用扫描电镜和EDS能谱仪对热轧不锈钢复合板剪切后的界面微观特征进行了研究,发现剪切断裂一般发生在界面区域中强度较低的部位,温轧及冷轧复合板的经验公式并不适合预测热轧不锈钢复合板的剪切强度。根据台阶根部加工在不同位置的系列剪切试验可相对准确确定热轧不锈钢复合板的剪切强度。     

轧制温度对TA1/Q345复合板性能的影响

相对于爆炸复合法和爆炸轧制复合法而言,采用真空-轧制生产钛钢复合板的方法更加适应大规模生产需要.本实验将TA1钛材置于两块Q345钢材中间组成组合坯,组合坯经抽真空至0.1 Pa后密封,在840~930℃下进行加热轧制,对轧制复合样进行力学性能检测,并利用扫描电镜、X射线衍射分析及显微硬度仪对组织与界面结合度进行分析.在该实验条件下,钛钢复合板剪切强度在159 MPa以上,达到了1类复合板标准要求,870℃轧制复合板性能较优.900和930℃轧制时,钛发生相变,同时在界面处生成了较多的金属问化合物,钛和钢的变形抗力相差过大和变形不协调导致界面附近的内应力变大,这些因素都降低了界面的剪切强度.840℃轧制后剪切强度低的原因是由于温度过低影响了界面附近元素的扩散.     

CrNiMo-CrNi3Mo-CrNiMo三层复合超高强度钢板开发

为了开发同时具有超高强度和良好韧性的低合金超高强度钢板,采用30MnCrNiMo连铸坯和33MnCrNi3Mo钢锭,经过真空复合焊接,高温轧制,淬火+低温回火热处理工艺研制出15 mm CrNiMo-CrNi3MoCrNiMo三层复合超高强度钢板;利用探伤、拉伸、冷弯、冲击、硬度等试验检验其结合度和力学性能;利用光学显微镜、扫描电镜等分析三层复合超高强度钢的组织和冲击断口形貌。结果表明,采用该工艺生产的三层复合超高强度钢板结合性良好,能够满足GB/T 7734-2015Ⅰ级探伤要求;复合钢板的综合力学性能良好,结合面处硬度值存在明显的过渡区域;结合面组织和基体组织均为回火马氏体组织。     

真空轧制钛/钢复合板的组织与性能

钛/钢复合板兼具钢的良好力学性能及钛的优异耐腐蚀性,广泛应用于石油、化工、电力及海洋工程等领域。南钢采用真空轧制复合法制备的钛/钢复合板,不添加过渡层,其拉伸性能、弯曲性能及剪切强度等均满足标准要求,而且剪切强度平均在209 MPa左右,超过标准要求的140 MPa。钛/钢复合板的各项性能达到GB/T8547-2006标准R1类复合板的要求。     

轧制复合厚钢板的界面组织及力学性能

摘要：以Q345钢为原料，采用组坯抽真空热轧复合的方法制备了55mm的厚板，利用OM和SEM观察界面微观组织，结果表明，基体和复合界面组织均为珠光体+铁素体，再结晶细化晶粒效果显著。随累计压下率的增加，界面缺陷减少，界面结合强度提高，当累计压下率达到66.0%时，界面剪切强度达到321MPa，Z向抗拉强度达到520MPa，断后伸长率最高达到39.5%，满足GB/T 1591—2008《低合金高强度钢》的要求。但复合界面经强酸深度腐蚀后，即使经多道次轧制变形，其仍然存在被强酸腐蚀的痕迹；同时，冲击试验结果表明，复合界面的冲击功低于母材的冲击功。     

真空热轧法制备不锈钢复合板组织和力学性能

 为了研究轧制温度对复合板界面结合强度的影响,采用真空热轧法制备了不锈钢复合板,利用OM、EPMA观察分析了不锈钢复合板界面组织和合金元素扩散。结果表明,碳钢中碳、铁元素向不锈钢扩散,不锈钢中铬、镍等元素向碳钢扩散,界面处出现Si-Mn-O三元化合物,合金元素扩散随轧制温度的升高而趋于严重。远离界面碳钢的组织为铁素体和珠光体组织,靠近界面碳钢的组织为铁素体组织。碳钢至界面处硬度先减小后升高,界面至不锈钢内部硬度先升高后下降,距界面约40 μm碳钢侧的维氏硬度值最低约为121.8HV,距界面约20 μm不锈钢侧的维氏硬度值最高约为245.5HV。从1 100到1 300 ℃,剪切强度随轧制温度的升高而升高,1 300 ℃轧制获得的界面剪切强度为463 MPa,远远超过基体的剪切强度。     

真空制坯热轧钛/钢复合板工艺及性能

钛/钢复合板的需求量日益增多，真空制坯热轧复合法（VRC）是制备高性能钛/钢复合板的有效工艺。介绍了钛/钢复合板制备工艺的国内外现状和工艺特点。依托863重点项目“钛/钢复合板研究与生产技术开发”和十三五重大课题“容器板轧制复合原理与关键技术”，利用真空制坯热轧复合法（VRC）在实验室和钢厂进行了一系列钛/钢复合板的轧制试验，对复合板的界面组织与力学性能进行了分析。实验室制备的钛/钢复合板，界面生成了明显的TiC层，未发现氧化物等杂质，断口有大量韧窝生成，复合界面平均拉剪强度达到了230MPa。钢厂试生产的钛/钢复合板，宽幅达到3500mm，界面生成连续的β- Ti层，拉剪断口未检测到氧化物，拉伸、冲击、弯曲等力学性能均满足国家标准，剪切强度均在196MPa以上，已达国内领先水平。     

纯铁中间层对热轧不锈钢复合板性能的影响

 为了减少不锈钢和碳钢热轧复合时结合界面形成脆性化合物,提高复合板的力学性能,在轧制温度为1 000、1 100及1 200 ℃,压下量约为70%的条件下,进行了添加不同厚度纯铁中间层的真空热轧复合试验。通过光学显微镜、SEM观察以及拉伸试验等,研究了纯铁中间层对复合板界面微观组织和拉伸性能的影响。结果表明,当加入不同厚度纯铁中间层时,同温度下不锈钢/碳钢复合板拉伸性能都有不同程度的提高。并且在小于70%压下量下,2 mm厚度的纯铁中间层可以完全阻止碳钢中的碳元素向不锈钢侧扩散,避免了碳铬化合物的形成,使结合界面的组织得到改善,力学性能得到提高。     

热轧7075/AZ31B复合板的显微组织及结合性能

为了研究热轧铝/镁复合板结合强度的变化规律,本文综合考虑压下率、轧制温度和轧制速度等多种轧制参数,单道次热轧制备了7075 Al/AZ31B Mg复合板。结果表明:在复合板轧制过程中由于热和强变形作用组织发生了动态再结晶,且增大轧制速度有助于镁基体产生完全动态再结晶。在相同轧制温度下,铝镁复合板结合强度均随压下率增加先升高后降低;强度升高是由于界面元素扩散宽度的增大和镁合金近界面晶粒组织的细化所致,强度降低是由于大变形导致镁基体近界面处产生裂缝,以及塑性功产生热量过多使得镁基体温度升高导致的镁侧晶粒长大所致。对复合板进行拉剪实验,铝镁结合界面剪切强度较低时,断裂发生在复合界面处且成脆性断裂特征,强度较高时断口形貌呈韧性断裂特征,断裂发生在镁基体侧。      

热处理对316L/Q235复合板组织与力学性能的影响

 对热轧不锈钢复合板热处理前后状态进行了对比研究,利用扫描电镜对显微组织进行了观察和成分分析,利用维氏硬度计测量了试样硬度,通过剪切、拉伸试验对试样的力学性能进行了研究。结果表明,真空热轧复合板能实现良好复合,碳钢侧为铁素体和珠光体组织;不锈钢侧为奥氏体组织。热处理后试样界面结合性能提高,试样剪切强度、屈服强度和抗拉强度都相应提高。高温阶段快速冷却＋低温阶段缓慢冷却的热处理制度适用于316L/Q235不锈钢复合板热处理。     

Dissimilar Friction Stir Welding of Carbon Steel and Stainless Steel: Some Observation on Microstructural Evolution and Stress Corrosion Cracking Performance

Specimens of carbon steel (CS) and stainless steel (SS) 316 was joined together by double sided butt joint Friction Stir Welding method. Effect of the tool rotational speed and specimen preheat temperature on resultant microstructure and mechanical behavior was studied. Constant traveling speed of 100 mm/min, tool rotational speed of 500 and 1000 rpm in combination with preheat temperature of 50 and 100 °C was employed for this study. No sign of root crack was observed in all specimens. Optical microscopy identified four distinct zones characterized as the stir zone, thermal mechanically affected zone (TMAZ) in both SS and CS specimen, and heat affected zone (HAZ) in CS specimen. No HAZ in SS was observed. Scanning electron microscopy revealed formation of a thin void layer on several locations at the boundary between the TMAZ and the re-oriented region of SS side, while on the CS side no voids were identified. The grain size on the TMAZ of CS was observed to be smaller compared to the HAZ region. No sign of root crack was observed in all specimens. The specimens were subjected to U bend. Specimens joined with 1000 rpm rotational speed developed a brittle behavior and failed in U bend test. The extent of the crack and brittleness was proportional to the applied preheat. U bent specimens from 500 rpm rotation demonstrated a good stress corrosion cracking behavior in 30,000 ppm solution of sodium chloride (NaCl).     

轧制复合生产特厚板工艺

采用Q345连铸坯料,经过表面清理、焊接组坯和抽真空至1×10^-3 Pa后密封,分别采用两阶段控轧和再结晶型控轧两种轧制工艺进行轧制.用剪切、拉伸和冷弯试验检验复合板的力学性能,利用扫描电镜观察分析复合板的组织与结合面.结果表明:两种轧制工艺生产出的钢板各项力学性都能达标;再结晶控轧工艺比两阶段控轧工艺复合效果更好,并生产出的钢板厚向性能更加均匀.试验条件下的轧制复合包含机械啮合与再结晶两种机制.     

轧制法生产不锈钢复合板工艺研究及应用

介绍了轧制法生产不锈钢复合板的技术,并以304不锈钢和Q345R两者复合轧制为例,分析了采用该方法生产复合钢板的力学性能及复合界面组织形貌结构特征。结果表明,采用轧制法生产不锈钢复合钢板结合面无锯齿形,基层、复层组织均良好,板材拉伸断口无分层及白斑,力学性能完全满足不锈钢复合板的要求。     

非对称不锈钢热轧复合板材的纵向弯曲

在Ｎｉ－Ｃｒ不锈钢同压力容器钢复合轧制过程中，由于作为覆板的不锈钢和作为基板的压力容器钢的变形抗力不同，在常规的对称型轧机上热轧非对称型复合叠板时，将发生向变形抗力较大一侧的纵向弯曲。在随后的冷却过程中，因覆板与基板的热膨胀系数不同，上述弯曲有进一步加剧的倾向。本文对非对称型不锈钢热轧合板材的变形行为进行了分析，并提出了纵向弯曲模型，以寻求获得平直的复合板材的最佳生产工艺。     

钛/铝复合板爆炸焊接技术研究进展

通过爆炸焊接技术制备的钛/铝复合板可兼具钛合金耐腐蚀性和铝合金低成本的优点。对钛/铝复合板爆炸焊接技术的研究进展进行介绍,论述了炸药种类、质量比R、基覆板间距及爆炸焊接窗口等主要工艺参数对钛/铝复合板组织和性能的影响;分析了影响钛/铝复合板结合界面的主要因素——金属间化合物种类、扩散层和界面波形;对钛/铝复合板硬度、抗剪切强度、抗拉强度及拉伸断口的研究进行了汇总分析。最后,指出了钛/铝复合板爆炸焊接工艺研究的重点发展方向。     

Fe-20Mn-0.6C TWIP钢力学性能和微观组织的演变

 研究一种Fe-Mn-C系新型TWIP钢的力学性能和微观变形机制。采用静态拉伸方法测试Fe-20Mn-0.6C钢在热轧和冷轧及热处理后的力学性能,通过金相、X-射线衍射、透射电镜观察等方法研究该钢的微观组织演变。结果表明：试验钢经过热轧后,表现出优异的综合力学性能,伸长率高达100%,抗拉强度达到924MPa。将热轧钢板经过适量冷轧后其抗拉强度提高到1210MPa。 热轧态组织为等轴的奥氏体基体及退火孪晶,拉伸变形后其微观组织中孪晶密度显著增加,晶粒内由一套孪晶系逐渐演化为两套孪晶系,而且因变形诱导马氏体相变产生大量马氏体组织。     

Structure and Properties of Explosive Clad HSLA Steel with Titanium

The present work pertains to the study of microstructure and mechanical properties of explosively clad high strength low alloy steel with commercially pure titanium. The clad interface was characterized by metallography, hardness, shear bond strength and bend tests. The present study revealed that the clad interface was wavy in nature. Shear bond strength of clad interface was in between substrate and clad material. The three point bend tests were conducted on clad joint in such a way that cladding layer was subjected to tension and compression which have not shown any cracks at the interface. The mechanism and reasons for the observed behaviour have been discussed correlating microstructure, mechanical properties, fracture features and diffusion across the interface.     

感应加热温度对冷?热轧制成形钛/钢复合板界面的影响

对钛/钢组坯进行冷轧预复合成形,将钛/钢预复合板感应加热至热轧温度后单道次热轧成形制备了钛/钢复合板,研究了感应加热温度对钛/钢复合板的界面组织和界面结合性能的影响。结果表明,冷?热轧制复合法制备的钛/钢复合板的界面结合紧密,没有孔洞和间隙。钛/钢复合板由于感应加热和热轧的时间较短（<5 s）,钛/钢界面仅有少量硬化层碎块,没有金属间化合物析出。钛/钢复合板的界面Ti和Fe元素扩散层宽度随感应加热温度增大而增大,950 ℃时界面扩散层宽度达到8 μm。在感应加热温度为750 ~ 950 ℃的条件下,钛/钢复合板的界面结合良好。