耐火材料与洁净钢的关系

从化学热力学分析讨论了耐火氧化物及复合氧化物与钢液中平衡氧含量的关系 ,钢液中氧含量与氧势的关系 ,耐火氧化物与钢中硫含量 ,耐火氧化物及结合剂与钢中磷含量 ,耐火材料中残余水分及有机结合剂与钢中氢含量的关系 ,以及炼超低碳钢时的碳污染等问题。     

Reaction between zinc oxide and chamotte refractories

Conclusions As a result of chemical reaction between chamotte and zinc oxide, zinc aluminate ZnAl₂O₄ and zinc silicate Zn₂SiO₄ are formed.The mullite is not chemically resistant under the action of zinc oxide. Even at 900°C mullite reacts with zinc oxide, forming ZnAl₂O₄ and SiO₂.In accordance with the quantity of melt formed in the refractory under the action of zinc oxide, high-alumina products should be more resistant to the action of vapors and oxides of zinc at elevated temperatures than chamotte and semiacid refractories.Translated from Ogneupory, No. 7, pp. 36–39, July, 1971.     

含钒渣对铝碳材料的侵蚀

为了探讨含矾渣对铝碳材料的侵蚀机制,用动态感应抗渣法研究了w(V2O5)=10%、碱度2.8,w(V2O5)=6%、碱度2.8,w(V2O5)=6%、碱度1.44的3种含钒渣对铝碳材料的侵蚀。结果表明:随着V2O5含量(w)由6%增加到10%,铝碳材料的熔损指数增加;随着碱度的增加,铝碳材料的熔损指数也增加;添加电熔镁砂有助于提高铝碳材料的抗侵蚀性能。显微分析表明:V、Ti元素渗透能力强,渗透深,而尖晶石可固溶少量V2O5、MnO及FeO。     

洁净钢生产技术的发展与耐火材料的相互关系

概述了洁净钢生产技术的发展概况,以及基础耐火材料和功能耐火材料在炉外精炼、中间包冶金和结晶器冶金中的应用和作用;着重评述可为洁净钢生产创造清洁环境和减少污染,有利于提高钢的纯净度和生产效率的耐火材料;指出洁净钢作为钢铁工业的一个战略发展目标,必将给耐火材料带来无限的机遇和光明的前景。     

Hot slag resistance of refractories

Conclusions It is proposed to test refractories for hot-slag resistance by which is meant the complex property typifying the wear resistance of refractories with the single-sided action of high temperature and slags and subsequent sharp cooling.A laboratory gas-oxygen furnace design was developed for testing the slag resistance with one-sided heating with the aim of forming zones in the specimens.The spalling resistance of zonal magnesite-chromite and periclase-spinel goods was determined.According to the slag resistance and operating spalling resistance the periclase-spinel refractories are better than the spalling-resistant magnesite-chromite.     

钢渣陶粒与钢渣的除磷性能对比

以钢渣为主要原料,添加少量黏土和造孔剂制备陶粒,对钢渣陶粒和钢渣的理化性能、除磷效果、等温吸附特征做了对比。结果发现,钢渣陶粒具有质轻、多孔等特征,除磷效果明显优于钢渣。在20 ℃条件下,两种材料对磷的等温吸附均符合Langmuir模型,钢渣陶粒的理论最大吸附量是钢渣的3.3倍。对除磷失效的钢渣陶粒和钢渣进行XRF检测和化学分析,结果表明,两种材料对磷的去除都以生成磷酸钙沉淀为主,前者所含的磷酸二钙型产物比例较高。     

钢包粘渣与包衬耐火材料

阐明了钢包粘渣与包衬耐火材料存在一定的关系 ,抗渣渗透性差、容易出现开裂的包衬耐火材料容易粘渣。为防止钢包粘渣 ,适于采用抗侵蚀性和抗渣渗透性优良的尖晶石砖、铝尖晶石 (或铝镁 )浇注料、低密度浇注料以及抗剥落性好的刚玉 -锆英石浇注料作包衬耐火材料     

酸性铬铁渣对耐火材料侵蚀的试验研究

为了研究冶炼铬铁的竖炉炉缸用耐火材料受酸性渣侵蚀情况,利用化学试剂CaO、MgO、SiO2、Al2O3和铬铁矿配制了不同碱度(分别为0.31、0.45和0.55)的酸性铬铁渣,采用静态坩埚法,分别在1500℃、1550℃、1580℃保温3h条件下,对高铝质、莫来石质、铝碳质、铝碳化硅质、刚玉-莫来石质、刚玉质和棕刚玉-碳化硅质等耐火材料进行侵蚀试验,比较了不同耐火材料被侵蚀和渗透的程度。试验结果表明:随着铬铁渣碱度和温度的增加,耐火材料的侵蚀量都有所增加;铬铁渣对铝碳砖的侵蚀和渗透程度均很轻,对莫来石砖和棕刚玉-碳化硅砖的较轻;而对刚玉、刚玉-莫来石砖渗透程度很严重,但侵蚀很轻;对高铝砖和铝-碳化硅砖侵蚀程度严重。