冷轧成形钛/钢层状复合板界面结合强度的影响因素EI北大核心CSCD

采用冷轧复合法制备钛/钢层状复合板,研究轧制压下率、轧制道次、表面粗糙度、原材料状态和轧制速率对钛/钢层状复合板界面结合强度的影响。结果表明:界面作用力和轧制力对界面的作用时间是影响钛/钢层状复合板界面结合强度的主要因素。轧制压下率、表面粗糙度和原材料状态通过影响界面作用力来影响钛/钢层状复合板的界面结合强度;轧制速率通过影响轧制力对界面的作用时间来影响钛/钢层状复合板的界面结合强度;钛/钢层状复合板的冷轧复合效果与轧制道次无关,只有单道次轧制压下率超过临界轧制压下率时,才能实现冷轧复合。     

冷轧成形钛/钢层状复合板界面结合强度的影响因素

采用冷轧复合法制备钛/钢层状复合板,研究轧制压下率、轧制道次、表面粗糙度、原材料状态和轧制速率对钛/钢层状复合板界面结合强度的影响。结果表明:界面作用力和轧制力对界面的作用时间是影响钛/钢层状复合板界面结合强度的主要因素。轧制压下率、表面粗糙度和原材料状态通过影响界面作用力来影响钛/钢层状复合板的界面结合强度;轧制速率通过影响轧制力对界面的作用时间来影响钛/钢层状复合板的界面结合强度;钛/钢层状复合板的冷轧复合效果与轧制道次无关,只有单道次轧制压下率超过临界轧制压下率时,才能实现冷轧复合。     

轧制制备铝/镁复合板数值模拟和翘曲变形控制

目的 选用5052铝合金与AZ31B镁合金作为复合材料进行热轧复合,研究铝/镁复合板轧制过程的数值模拟和翘曲变形控制.方法 对铝/镁复合板在不同轧制温度、轧制压下率和轧辊预加热轧制工艺下的热轧过程进行模拟.对轧制变形区铝/镁复合板的应力分布进行分析,讨论其对铝/镁复合板变形协调性的影响.最后在不同轧制工艺下进行单道次热轧实验,制备铝/镁(5052/AZ31B)复合板并与模拟结果进行对比.结果 有限元模拟和热轧实验结果表明,随着轧制压下率的增大和轧制温度的升高,铝/镁复合板的翘曲增大;将靠近铝基体侧轧辊预加热后,可以有效改善铝/镁复合板的翘曲问题.以轧制温度450℃为例,轧制压下率逐渐增大时,复合板的延伸性逐渐增大,复合板的翘曲也逐渐增大.将下轧辊预加热到50℃,其余轧制参数不变,轧制后复合板整体较为平直,翘曲明显比轧辊未预加热时小.结论 通过轧辊预加热轧制工艺可以有效控制铝/镁复合过程中的翘曲变形问题.     

电子封装用Cu/Mo/Cu复合材料的工艺研究

研究了浸涂助复剂(铝基合金)和室温轧制工艺对Cu/Mo/Cu复合界面结合强度的影响,简述了Cu/Mo/Cu复合板室温轧制成形工艺过程,详细分析了表面和界面清理、初道次轧制临界变形率及热处理工艺等因素对复合板结合强度的影响.实验结果得出,钼板浸涂Al-Mn-Zn-Sn合金助复剂后的热处理温度为800～850℃;初道次轧制变形率为45%最佳;复合轧制后合适的退火工艺为450℃,保温60 min.     

轧制复合法制备硅浓度梯度高硅钢薄带的织构演变

采用"热轧复合+冷轧减薄+退火"方法成功制备了0.20mm厚的硅浓度梯度高硅钢薄带,并采用SEM和X射线衍射技术对制备过程中组织和织构演变进行了研究。热轧复合板微观组织呈明显层状分布,复合界面为紧密冶金结合且经过83%的大冷轧变形未开裂。热轧和冷轧复合板带中均形成强α和γ织构,再结晶退火后形成强γ织构。冷轧和退火织构沿板厚呈显著的梯度分布特征,其主要来自于复合界面两侧硅浓度和初始热轧织构的差异性以及冷变形的不均匀性。     

钛网添加对镁/铝复合板微观组织和力学性能影响研究

目的 有效抑制镁/铝复合板界面处金属间化合物的形成。以钛网为中间金属夹层,研究它对镁/铝复合板微观组织和力学性能的影响。方法 利用复合轧制技术制备以钛网为中间金属夹层的镁/铝-钛复合板,采用扫描电子显微镜(SEM)、电子背散射衍射仪(EBSD)、万能试验机等对复合板退火前后的微观组织和力学性能进行表征和分析,系统研究中间层钛网对轧制态和退火态复合板微观组织、织构、拉伸性能、界面结合强度的影响规律。结果 中间层钛网均匀分布在镁/铝-钛复合板界面处,钛网的添加能有效抑制复合板退火过程中镁-铝金属间化合物的连续生长,减少金属间化合物的数量。与镁/铝复合板相比,钛网的添加对轧制态和退火态复合板中镁层和铝层的平均晶粒尺寸和织构类型的影响较小。与镁/铝复合板相比,钛网的添加降低了轧制态复合板的界面剪切强度和延伸率,但极大提升了退火态复合板的界面剪切强度、拉伸强度和延伸率。结论 中间层钛网的添加可有效减少复合板界面处金属间化合物的数量,提升退火态复合板的综合力学性能。     

铝/钛/铝三层复合板热轧工艺及微观组织研究

钛/铝层状复合材料具有两种材料优异的特性,能够满足一些特殊工程需要。开发了热轧复合技术,成功制备了铝(1100)/钛(TA2)/铝(1100)三层复合板。研究了复合板轧制过程中的关键轧制技术参数(临界压下率和轧制复合工艺条件)。利用光学显微镜和SEM观察了钛/铝复合板及结合界面形貌,分析了不同退火温度对复合板力学性能的影响。基于实验结果,描述了影响复合板质量和有助于提高复合板结合强度的关键工艺过程。     

铜／铝冷轧复合板剥离性能及界面摩擦分析

采用同步轧制方法制备铜／铝复合板,研究了轧制变形量对于铜／铝复合板结合强度和剥离表面形貌的影响,分析了轧制复合界面摩擦机理。研究结果表明,复合板结合强度、剥离表面粘铝、铜基体表面裂纹数都随着轧制变形量的增大而增大。变形量为50％时,结合强度为2N／mm,变形量为60％时,结合强度为7N／mm,变形量为70％时,结合强度为14N／mm。轧制过程中,新鲜金属从结合面裂纹中挤压出来,受界面摩擦力剪切作用,两新鲜金属搓合在一起形成良好结合。     

铜钢复合板弯片成形数值模拟与成形试验

铜钢复合钢板HALF弯片弯曲半径小,冲压成形变形量大,易出现复合界面开裂、脱层问题.采用ABAQUS三维有限元软件对HALF弯片热成形过程进行数值模拟,分析了600℃、700℃、800℃、900℃成形温度下弯片应力、弯片厚度及复合界面选定点应力,并进行了铜钢复合板HALF弯片热成形试验,测定复合界面结合率与剪切强度.结...     

微张力对不锈钢/碳钢界面复合质量及原子扩散的影响

随着绿色可持续化工业进程的推进和人类资源开发向海洋的转移,耐腐蚀钢筋市场需求量逐渐提高。本工作采用有限元仿真技术建立不锈钢/碳钢复合钢筋四道次连续轧制模型,深入研究不同轧制工况对复合钢筋覆层壁厚均匀度以及界面“空洞”缺陷的影响;通过加载拉应力工况建立COMPASS力场下的界面模型,探究复合钢筋界面原子扩散行为。宏/微观模拟研究表明：微张力轧制会促使双金属界面形成“空洞”,但能显著抑制轧制过程中“耳子”缺陷的产生;拉应力(微张力)升高有效促进了界面沿(111)晶面滑移,并产生了有序度高且一致的界面结构。复合界面微观组织试验同样表明,在高温高压微张力作用下,界面元素过渡平缓,金属碎粒与孔洞消失;近界面区域主要为铁素体晶粒,且越靠近界面珠光体含量越少,渗碳作用越明显。本研究有助于揭示不锈钢/碳钢高压微张力复合过程中金属流动规律及界面原子迁移机制,为优化复合工艺奠定理论基础。     

Insertion of triangulated surfaces into a meccano tetrahedral discretization by means of mesh refinement and optimization procedures

In this paper, we present a new method for inserting several triangulated surfaces into an existing tetrahedral mesh generated by the meccano method. The result is a conformal mesh where each inserted surface is approximated by a set of faces of the final tetrahedral mesh. First, the tetrahedral mesh is refined around the inserted surfaces to capture their geometric features. Second, each immersed surface is approximated by a set of faces from the tetrahedral mesh. Third, following a novel approach, the nodes of the approximated surfaces are mapped to the corresponding immersed surface. Fourth, we untangle and smooth the mesh by optimizing a regularized shape distortion measure for tetrahedral elements in which we move all the nodes of the mesh, restricting the movement of the edge and surface nodes along the corresponding entity they belong to. The refining process allows approximating the immersed surface for any initial meccano tetrahedral mesh. Moreover, the proposed projection method avoids computational expensive geometric projections. Finally, the applied simultaneous untangling and smoothing process delivers a high‐quality mesh and ensures that the immersed surfaces are interpolated. Several examples are presented to assess the properties of the proposed method.     

Certification Institutions Expected to Update and Transfer Information on Present Standards

Standards are the basis for production enterprises to organize production, ex-factory inspection, trade (delivery) and technical exchanges, product certification, quality arbitration and supervision.……     

Flow calorimeter for enthalpy increment measurements on condensed gases

A flow calorimeter for enthalpy increment measurements on condensed gases is presented. A better knowledge of the properties of the liquefied natural gas is needed, and therefore a liquid loop has been designed for our flow calorimeter. The fluid loop in the calorimeter is designed in order to avoid the two-phase region, since two phases would give compositional disturbances in the measurements. The avoidance of the two-phase region is made possible by increasing the pressure of the test fluid after the measurement section, then heating the fluid at super-critical pressure past the critical point. Finally, the fluid is throttled to the low-pressure gas state at the inlet condition of the compressor that circulates the fluid. To perform the pressure increase, a new cryogenic pump has been designed. To evaluate the new equipment, measurements were taken on liquid ethane over the temperature range 146–256 K at pressure between 0.9 and 5.1 MPa.     

Refrigerators Enter a New Era of Health Preservation Frestech initiates the establishment of China's first standard for household sterilization refrigerators

On November 30, 2007, the China Association for Standardization (CAS) held a press conference at Beijing Diaoyutai State Guest House. Leaders from the China Household Electric Appliance Research Institute, the China Household Electric Appliance Association, and the China Consumers' Association attended and made speeches.……     

Optimum-Simulation von Ernteprozessen

Zusammenfassung Bei der Gestaltung von Ernteprozessen — beispielsweise des Prozesses Mähdrusch, Körnertransport und -abnahme — als transportverbundene Fließarbeitsverfahren mit mindestens zwei verschiedenen Arbeitsmitteln gibt es einen großen Optimierungsspielraum. Solche Prozesse sind mehrstufige Bedienungsprozesse mit gemischter Anordnung der Bedienungseinrichtungen. Außerdem besitzen sie stark ausgeprägte räumliche Aspekte. Es wird vor allem gezeigt, welche Merkmale solcher Prozesse in Simulationsmodellen abgebildet sein müssen, welche Zielgrößen in Abhängigkeit von welchen Einflußgrößen unter Berücksichtigung welcher Prozeßbedingungen ermittelt werden sollten und wie der Bewertungsprozeß zur Ermittlung der gewünschten Informationen gestaltet werden muß.     

A study of centrifugal cast high boron high speed steel

In the present study a high‐boron high speed steel (HSS) roll material was designed. Many expensive alloy elements have been substituted by cheap boron alloy, and high‐boron high speed steel roll has been manufactured by centrifugal casting method. The microstructures, mechanical properties and wear resistance of centrifugal casting high‐boron high speed steel roll have been investigated by optical microscopy (OM), scanning electron microscopy (SEM), and X‐ray diffraction (XRD) analysis, hardness test, impact test and wear test. The results indicated that the solidification microstructures of high‐boron high speed steel roll consisted of M₂(B,C), (W,Mo)₂(B,C), M₃(B,C), M₂₃(B,C)₆ type borocarbides and martensite, a small amount of retained austenite. Borocarbides were continuously distributed over the grain boundary. After quenching from 1050 °C, local broken network appeared in partial borocarbides, and fine secondary borocarbide precipitated from the matrix. After tempering from 525 °C, the amount of precipitated borocarbide increased significantly. After heat treatment, the hardness of high‐boron high speed steel roll excelled 60 HRC, and its impact toughness excelled 8.0 J/cm². The single groove steel rolling amount of high‐boron high speed steel rolls increases by 500% than that of bainite cast iron roll, when the rolls are used in K₁ mill housing of bar mill.     

Thixotropy of Systems with Shear Thinning and Plastic Flow Behavior

The definition of the thixotropy is a decrease in viscosity with time in shear and a subsequent recovery of viscosity after the shear deformation is removed.We ...     

Brainstorming for ISO Strategy 2016-2020

正Responding to ISO’s appeal for survey for the to-be-developed ISO Strategy Plan for 2016-2020,SAC hosted a special workshop over the needs and comments of various fi elds on June 8 in Beijing.The workshop was attended by ISO President-elect and Ansteel General Manager Zhang Xiaogang,SAC Vice-Administrator Yu Xinli,and 30 experts from     

CNAS Passes APLAC's PTP Review

正The review group of Asia Pacific Laboratory Accreditation Cooperation(APLAC)carried out a 4-day peer review of the proficiency testing provider(PTP)for China National Accreditation Service for Conformity Assessment(CNAS)from July 28 to 31,2014.CNAS passed the PTP review with excellent performance.Two senior peer reviewers of APLAC made a comprehensive,rigorous and detailed review of CNAS’s PTP accreditation activities,and made the on-spot inspection of the review groups in Shanghai and Shenzhen respectively.