Oil-Lubricated Fretting Behaviors of 304 Stainless Steels under Different Fretting Strokes and Normal Loads

The influence of oil lubrication on the fretting wear behaviors of 304 stainless steel flat specimens under different fretting strokes and normal loads has been investigated. The results proved that fretting regimes and fretting wear behaviors of 304 stainless steels were closely related to the fretting conditions. In general, the increase in normal load could increase wear damage during sliding wear. However, according to the results, a significant reduction in wear volume and increase in friction coefficient was observed when the normal load was increased to critical values of 40 and 50 N at a fretting stroke of 50 μm due to the transformation of the fretting regime from a gross slip regime to partial slip regime. Only when the fretting stroke further increased to a higher value of 70 μm at 50 N, fretting could enter the gross slip regime. There was low wear volume and a high friction coefficient when fretting was in the partial slip regime, because oil penetration was poor. The wear mechanisms were fatigue damage and plastic deformation. There was high wear volume and low friction coefficient when fretting was in the gross slip regime, because the oil could penetrate into the contact surfaces. Unlike the wear mechanisms in the partial slip regime, fretting damage of 304 stainless steels was mainly caused by abrasive wear in the gross slip regime.     

Effect of contact load on fretting fatigue behaviour of steel wires

Abstract

The tension–tension fretting fatigue tests of steel wires were performed on a self-made fretting fatigue test equipment under contact loads ranging from 40 to 70 N and a strain ratio of 0·8. The results showed that when the contact load increased, the fretting regime of steel wires transformed from gross slip regime to mixed fretting regime. The fretting fatigue life in the mixed fretting regime was significantly lower than that in the gross slip regime. The main fretting wear mechanisms in the gross slip regime, where there were serious fretting damage and a lot of wear debris, were abrasive wear and fatigue wear. Microcracks were observed in the fretting scar of the mixed fretting regime, and the main fretting wear mechanisms were adhesive and fatigue wears. The fretting wear scar was the fatigue source region, and the fatigue fracture surface could be divided into three regions.     

Investigation into effects and interaction of various fretting fatigue variables under slip-controlled mode

Fretting fatigue behavior of unpeened and shot-peened Ti–6Al–4 V was investigated using a dual-actuator test setup which was capable of applying an independent pad displacement while maintaining a constant cyclic load on the specimen. The fretting regime was identified based on the shape of the hysteresis loop of tangential force versus relative slip range and the evolution of normalized tangential force. The fretting regime changed from stick to partial slip and then to gross slip with increasing relative slip range, and the transition from partial to gross slip occurred at a relative slip range of 50–60 μm regardless of the applied cyclic load, surface treatment, contact load and contact geometry. The fretting fatigue life initially decreased as the relative slip range increased and reached a minimum value, and then increased with increase of the relative slip range due to the transition in fretting regime from partial slip to gross slip. Shot-peened specimens had longer fatigue life than unpeened specimens at a given relative slip range, but the minimum fatigue life was found to be at the same value of relative slip range for both shot-peened and unpeened specimens. Tangential force was directly related to relative slip and this relationship was independent of other fretting variables.     

Analysis of the Fretting Conditions in a Contact Between an Epoxy Thermoset and a Glass Counterface

The fretting conditions in a contact between an epoxy thermoset and a glass counterface have been investigated using a specific device which allows in situ observation of the contact area. The critical displacement for transition from partial slip to gross slip conditions was investigated by the in situ detection of the micro-displacements and by the analysis of the fretting loops. Experimental results were in good relation with the theoretical predictions derived from Mindlin's approach of incipient sliding. Depending on the loading conditions, a progressive change from gross slip to partial slip conditions was found to occur during the early stages of the fretting loading, i.e., before the appearance of any macroscopic damage such as cracking or particle detachment. These fretting conditions were synthesized in a fretting map giving the boundary between various fretting regimes as a function of the normal load, the imposed displacement and the number of cycles.     

基于双重扩展自适应卡尔曼滤波的汽车状态和参数估计

准确实时地获取行驶过程中的状态信息是汽车动态控制系统研究的关键,为此提出了一种新的汽车状态估计器。建立了包含不准确模型参数和未知时变统计特性噪声的非线性汽车动力学模型,针对该非线性系统提出一种双重扩展自适应卡尔曼滤波算法（DEAKF）。该算法采用两个卡尔曼滤波器并行运算,状态估计和参数估计互相更新,同时将带遗忘因子的噪声统计估值器嵌入到状态校正过程和参数校正过程之间,以解决系统的噪声时变问题。基于ADAMS的虚拟试验和实车试验结果表明,该算法的状态估计精度高于EKF方法和DEKF方法的状态估计精度,同时具有良好的模型参数校正能力,对汽车动态控制系统中估计器的设计具有理论指导意义。
     

Study on rotational fretting wear of 7075 aluminum alloy

Rotational fretting wear tests in a ball-on-flat configuration have been successfully realized on a special rotational fretting rig developed from an ultra-low-speed reciprocating rotational driver. The rotational fretting behavior of 7075 aluminum alloy against 52 100 steel was studied under different angular displacement amplitudes and normal loads. The results showed that both F_t?θ and F_t/F_n curves can be used to characterize the rotational fretting running behavior, which exhibited different curve shapes and variation trends in different fretting running regimes. The rotational fretting behavior of 7075 aluminum alloy was strongly dependent on the angular displacement amplitude, normal load and number of cycles. The wear of 7075 aluminum alloy was characterized by slight attrition in the partial slip regime, while a combination of delamination, abrasive and oxidative wear was found in the slip and mixed fretting regimes. The formation of a central bulge probably due to plastic flow was observed under gross slip condition of the rotational fretting mode.     

人股骨皮质骨轴面微动摩擦磨损特性研究

采用高精密微动试验台外加体液恒温循环装置,在一定法向载荷和不同位移幅值条件下,研究了天然活性人股骨皮质骨对纯钛的微动摩擦磨损行为。试验结果显示：随位移幅值的增加,股骨皮质骨的微动运行状态从部分滑移向完全滑移状态转变,详细讨论了不同位移幅值下摩擦因数随循环次数的演变规律。微观观察表明：接触表面处于部分滑移状态时损伤轻微,而在完全滑移状态下磨损较严重。人股骨皮质骨的磨损机理主要表现为磨粒磨损和微骨折导致的剥层剥落。微动磨痕的深度随位移幅值的增加而增加,而且磨痕深度与摩擦因数有很好的对应关系。研究认为控制植入体/骨界面的微动幅度有利于提高皮质骨抗微动损伤的能力。     

Fretting behavior of shot peened Ti-6Al-4V under slip controlled mode

Fretting tests of shot peened Ti-6Al-4V were conducted under slip controlled mode using a dual actuator test setup which could apply an independent pad displacement at a given applied bulk stress. Fretting regime was identified based on the hysteresis loop of tangential force versus relative slip range and the evolution of tangential force. Fretting regime changed from partial slip to mixed slip and then to gross slip with increasing relative slip range, and the transition from mixed to gross slip occurred at a relative slip range of ∼50 μm regardless of the applied bulk stress magnitude for both shot peened and unpeened specimens. Fretting fatigue life initially decreased as the relative slip range increased and reached to a minimum value, and then increased with an increase of the relative slip range due to the transition in fretting regime from mixed slip to gross slip. Shot peened specimens had longer fatigue life than unpeened specimens at a given relative slip range, but the minimum fatigue life was at the same value of the relative slip range for both shot peened and unpeened specimens. The relationship between relative slip and fatigue life was also found to be independent of the applied bulk stress level. Further, tangential force was directly related to relative slip and this relationship was independent of other fretting variables.     

Effect of Cold Rolling on the Fretting Wear Behavior and Mechanism in Inconel 690 Alloy

The influence of cold rolling on the fretting wear behavior and mechanism of Inconel 690 alloy at 320?°C in air was studied. The wear volume and worn surface were obtained and analyzed using laser scanning confocal microscopy, electron back-scattering diffraction, scanning electron microscopy, and energy-dispersive X-ray spectroscopy. The grinding surface and strain distribution were also studied by electron back-scattering diffraction to analyze the mechanism of fretting damage. The results indicated that with an increase in cold rolling reduction, the microhardness was increased. However, the friction coefficient and wear volume first increased and then decreased. The characteristics of fretting areas changed from a gross slip regime to a partial slip regime. Accordingly, the damage mechanism in the gross slip regime was a combination of oxidative wear, abrasive wear, and delamination, whereas the damage mechanism in the partial slip regime was mainly adhesive wear.     

690合金材料的微动磨损特性研究

利用微动磨损试验机,在载荷50N以及位移幅值为60μm、100μm、150μm的工况下,研究了690合金材料在常温下的微动磨损行为及其动力学特性,采用激光共焦扫描显微镜(LCSM)和扫描电子显微镜(SEM)观察磨痕微观形貌。结果表明,载荷和位移幅值对微动特征有很大的影响,微动运行完全处于滑移状态。在滑移区,滑移磨损严重、磨痕面积大。690合金材料的磨损机制主要表现为磨粒磨损与剥层的共同作用。     

聚四氟乙烯基粘结固体润滑涂层微动磨损性能研究

在不同位移幅值与载荷条件下研究了酚醛环氧粘结聚四氟乙烯(PTFE)基固体润滑涂层的微动磨损特性，并利用扫描电子显微镜、表面轮廓仪和傅里叶表面红外仪等对涂层磨斑进行分析。结果表明，粘结PTFE基涂层具有良好的抗微动损伤性能，随循环次数的变化只存在部分滑移区和滑移区，部分滑移区的损伤轻微，滑移区的损伤强烈依赖于栽荷，其损伤与PTFE分子链在往复交变载荷作用下的疲劳断裂相关。     

粘结石墨固体润滑涂层微动磨损性能研究

在不同位移幅值与载荷下研究了粘结石墨固体润滑涂层的微动磨损特性，并利用扫描电镜和X射线衍射仪分析了涂层微动磨斑。结果表明：粘结石墨涂层具有良好的抗微动损伤性能，随循环次数的变化只存在部分滑移区和滑移区，部分滑移区涂层损伤轻微；滑移区损伤严重，主要表现为裂纹萌生和扩展，最终按剥层机制呈层状剥落。     

Development of a test device for the evaluation of fretting in point contact

Fretting wear and fatigue may occur between any two contacting surfaces, wherever short‐amplitude reciprocating sliding is present for a large number of cycles. A test device has been developed for the evaluation of fretting fatigue and wear in partial and gross slip conditions. Three similar sphere‐on‐plane contacts run at the same time. Normal force, tangential force or displacement amplitude and constant bulk stress can be controlled and measured separately. Reciprocating tangential displacement is produced with rotational motion, the amplitude and frequency of which can be adjusted and controlled accurately by an electric shaker. The number of load cycles for crack initiation and growth is determined with strain‐gauge measurements near the fretting point of contact. The contact surfaces are measured with 3D optical profilometer before fretting measurements to determine actual contact geometry. The measurements were done with quenched and tempered steel. The initial results indicate that cracks are mostly formed in partial slip conditions, whereas fretting wear is more heavily involved in gross slip conditions. The initiation of a crack occurs near the edge of the contact in the slip direction, where the calculated cracking risk has its maximum value in partial slip conditions. The number of cracks increases as the displacement amplitude, i.e. friction force, increases in partial slip conditions. Copyright © 2008 John Wiley & Sons, Ltd.     

Fretting wear mechanisms of Zircaloy-4 and Inconel 600 contact in air

The fretting wear behavior of the contact between Zircaloy-4 tube and Inconel 600, which are used as the fuel rod cladding and grid, respectively, in PWR nuclear power plants was investigated in air. In this study, number of cycles, slip amplitude and normal load were selected as the main factors of fretting wear. The results indicated that wear increased with load, slip amplitude and number of cycles but was affected mainly by the slip amplitude. SEM micrographs revealed the characteristics of fretting wear features on the surface of the specimens such as stick, partial slip and gross slip which depended on the slip amplitude. It was found that fretting wear was caused by the crack generation along the stick-slip boundaries due to the accumulation of plastic flow at small slip amplitudes and by abrasive wear in the entire contact area at high slip amplitudes.     

Nanofretting Behavior of Monocrystalline Silicon (100) Against SiO2 Microsphere in Vacuum

With an atomic force microscopy, the tangential nanofretting between spherical SiO₂ tips and monocrystalline Si(100) surface was carried out at various displacement amplitudes (0.5–250 nm) under vacuum condition. Similar to fretting, the nanofretting of Si(100)/SiO₂ pair could also be divided into stick regime and slip regime upon the transition criterion. However, it was found that the energy ratio corresponding to the transition between two nanofretting regimes varied between 0.32 and 0.64, which was higher than the normal value of 0.2 for the transition criterion to determine the partial slip and gross slip regimes in fretting. One of the reasons may be attributed to the effect of adhesion force, since whose magnitude is at the same scale to the value of the applied normal load in nanofretting. During the nanofretting process of Si(100)/SiO₂ pair, the adhesion force may induce the increase in the maximum static friction force and prevent the contact pair from slipping. The higher the applied load, or the higher the adhesion force, the larger will be the transition displacement amplitude between two regimes in nanofretting. Different from fretting wear, the generation of hillocks was observed on Si(100) surface under the given conditions in nanofretting process. With the increase in the displacement amplitude in slip regime of nanofretting, the height of hillocks first increased and then attained a constant value. Compared to chemical reaction, the mechanical interaction may be the main reason responsible for the formation of silicon hillocks during the nanofretting in vacuum. The results in the research may be helpful to understand the nanofretting failures of components in MEMS/NEMS.     

中性腐蚀环境下钢丝的微动疲劳行为

在自制的微动疲劳试验机上开展中性腐蚀环境下单根钢丝的微动疲劳实验,考察在相同接触载荷下,不同振幅对钢丝的微动疲劳行为的影响,并用扫描电子显微镜观察疲劳钢丝的磨痕和断口形貌,研究钢丝微动疲劳断裂机制.结果表明:在较大的振幅下,钢丝的微动区均处于滑移状态,而在较小振幅下,钢丝的微动区从滑移状态逐渐转变为黏着状态;磨损机制主要为磨粒磨损、疲劳磨损、腐蚀磨损和塑性变形;钢丝疲劳寿命随着微动振幅的增大而减小;钢丝的疲劳断口可分为3个区域,即疲劳源区、裂纹扩展区及瞬间断裂区.     

Wear analysis of Cu–Al coating on Ti–6Al–4V substrate under fretting condition

Fretting behavior of Cu–Al coating on Ti–6Al–4V substrate was investigated with and without fatigue load. Soft and rough Cu–Al coating resulted in abrasive wear and a large amount of debris remained at the contact surface, which caused an increase in tangential force during the fretting test under gross slip condition. Fretting in the partial slip condition also showed the wear of coating. To characterize wear, dissipated energies during fretting were calculated from fretting loops and wear volumes were obtained from worn surface profiles. Energy approach of wear analysis showed a linear relationship between wear volume and accumulated dissipated energy. This relationship was independent of fatigue loading condition and extended from partial slip to gross slip regimes. As an alternate but simple approach for wear analysis, accumulated relative displacement range was correlated with the wear volume. This also resulted in a linear relationship as in the case of accumulated dissipated energy suggesting that the accumulated relative displacement range can be used as an alternative parameter for dissipated energy to characterize the wear. When the maximum wear depth was equal to the thickness of Cu–Al coating, harder Ti–6Al–4V substrate inhibited further increase in wear depth. Only when a considerable energy was supplied through a large value of the applied displacement, wear in the substrate material could occur beyond the thickness of coating.     

An experimental study torsional fretting behaviors of LZ50 steel

Four simple fretting modes are defined according to relative motion: tangential, radial, rotational, and torsional fretting. This paper presents a new test rig that was developed from a low-speed reciprocating rotary system to show torsional fretting wear under ball-on-flat contact. Torsional fretting behavior was investigated for LZ50 steel flats against AISI52100 steel balls under various angular displacement amplitudes and normal loads. The friction torques and dissipation energy were analyzed in detail. Two types of T–θ curves in the shape of quasi-parallelograms and ellipticals were found that correspond to gross and partial slips, respectively. The experimental results showed that the dynamic behavior and damage processes depend strongly on the normal loads, angular displacement amplitudes, and cycles. In this paper, the debris and oxidation behaviors and detachment of particles in partial and gross slip regimes are also discussed. Debris and oxidation are shown to have important roles during the torsional fretting processes. The wear mechanism of torsional fretting was a combination of abrasive and oxidative wear and delamination before third-body bed formation. The mechanism was then transformed into third-body wear after a great amount of debris formed.     

桨-毂轴承材料扭动微动磨损行为研究

采用面接触扭动微动形式,以动力定位系统可调距螺旋桨桨-毂轴承摩擦副材料(CuNiAl-42CrMo4)为对象,以不同的角位移幅值模拟海水波动影响下的微动磨损行为,并结合扫描电子显微镜和超景深三维显微镜对磨痕形貌进行分析,探究桨-毂轴承摩擦副材料扭动微动磨损规律。结果表明,随着角位移幅值的增加,扭动微动依次运行于部分滑移区、混合区、滑移区,摩擦因数减小,同时磨损量增加,微动损伤中剥层机制所占的比例逐渐增加,且由于疲劳裂纹扩展的不利影响,实际运行过程中要尽量避开混合区。