焊前热处理对Ti-22Al-25Nb/TC11异种合金焊接接头组织与性能的影响

采用不同初始组织的Ti-22Al-25Nb合金与TC11合金进行焊接,然后再用同样规范对焊件进行近等温锻造和热处理。利用OM对焊件接头的显微组织进行了观察,并拉伸测试了Ti-22Al-25Nb/TC11异种合金接头的强度。结果表明:焊前经固溶处理过的Ti-22Al-25Nb合金B2晶粗大,焊后经等温锻造和热处理之后析出的O相较多,使得焊接接头强度和塑性均有降低;Ti-22Al-25Nb/TC11异种合金接头的显微组织内含有O相、α相、β相及少量α2相。     

热处理对Ti-22Al-25Nb/TC11双合金焊接接头组织与性能的影响

对经近等温锻造后的Ti-22Al-25Nb/TC11双合金电子束焊接接头进行了梯度热处理与双重热处理,采用OM、TEM观察了Ti-22Al-25Nb/TC11双合金接头界面组织,并对其室温性能进行了对比分析。结果表明,梯度热处理后双合金接头Ti-22Al-25Nb基体析出相以细小颗粒状α2相为主,TC11基体出现网状组织;双重热处理后Ti-22Al-25Nb基体以短棒状的O相为主,TC11基体以魏氏组织为主;双重热处理后Ti-22Al-25Nb/TC11双合金接头的室温力学性能均低于梯度热处理后的双合金接头,这与其焊缝区析出的α相增加有关。因此,梯度热处理优异于双重热处理。     

热处理对Ti-22Al-25Nb/TC11双合金接头组织与性能的影响

对经近等温锻造后的Ti-22Al-25Nb/TC11双合金电子束焊接头进行了梯度热处理与双重热处理,采用OM、TEM观察了Ti-22Al-25Nb/TC11双合金接头界面组织,并对其室温性能进行了对比分析。结果表明,梯度热处理后双合金接头Ti-22Al-25Nb基体析出相以细小颗粒状α₂相为主,TC11基体出现网状组织;双重热处理后Ti-22Al-25Nb基体以短棒状的O相为主, TC11基体以魏氏组织为主;双重热处理后Ti-22Al-25Nb/TC11双合金接头的室温力学性能均低于梯度热处理后的双合金接头,这与其焊缝区析出的α相增加有关。因此,梯度热处理优异于双重热处理。     

热处理制度对Ti-22Al-25Nb/Ti60双合金焊接接头组织与性能的影响

研究了锻后不同热处理制度对Ti-22Al-25Nb/Ti60双合金焊接接头显微组织和力学性能的影响。结果表明：Ti-22Al-25Nb/Ti60双合金试样经不同工艺热处理后焊缝组织得到不同程度的细化,强度和塑性均得到提高。热处理制度为990 ℃×1 h, AC+750 ℃4 h, AC时,Ti60合金热影响区组织主要由大量细小的等轴α相、少量的片状α相及β转变组织组成,其强度与塑性最佳,且有较好的匹配。     

Ti-22Al-27Nb合金线性摩擦焊接头组织与显微硬度分析

对Ti-22Al-27Nb合金进行了线性摩擦焊及热处理试验,并对热处理前后焊接接头的微观组织和显微硬度进行测量分析. 结果表明,利用线性摩擦焊方法焊接Ti-22Al-27Nb合金得到的接头无焊接缺陷. 焊态下,焊缝区形成了B2单相区组织. 热力影响区为B2 + O + α₂相三相区,出现等轴α₂相,针状O相几乎消失. 热处理后在焊缝区析出板条状O相和针状O相,热力影响区为O相均匀分布的两相区. 母材处的显微硬度值最低约为300 HV,随着向焊缝靠近,显微硬度值逐渐增加,焊缝中心达到最大值354 HV. 热处理后,由于板条O相和针状O相的沉淀析出,使焊缝中心显微硬度急剧增加.     

β相区凝固的铸造γ-TiAl基合金的微观组织(英文)

采用光学显微镜(OM)、扫描电镜(SEM)、透射电镜(TEM)及差示扫描量热仪(DSC)研究Ti-43Al-4Nb铸态合金及其热处理态合金的显微组织以及相转变行为。结果表明:通过从β相区凝固的方法可以获得组织细小的铸态Ti-43Al-4Nb合金;凝固过程中γ晶能够直接从β相中形核,β相与γ相沿初始α晶界共存,有效地抑制了铸态Ti-43Al-4Nb合金晶粒的长大;Ti-43Al-4Nb合金在凝固过程中的相转变顺序为L→L+β→β→α+β→α+βr→α+γ+βr→(α2+γ)片层+γ+βr;经1250℃、16h热处理后,Ti-43Al-4Nb合金的显微组织与铸态组织相比有一定程度的粗化;由于Nb元素的充分扩散以及β相的非平衡状态,经过上述热处理过程后残余β相能够被完全消除。     

改造Ti-24Al-15Nb-1.5Mo/TC11双合金焊缝组织与增强连接界面性能的工艺

研究近等温锻造+梯度热处理工艺对Ti-24Al-15Nb-1.5Mo/TC11双合金焊接接头的显微硬度变化、合金元素扩散趋势、显微组织特征和拉伸性能的影响.结果表明:近等温锻造+梯度热处理能使焊接接头得到强化.经近等温锻造和梯度热处理后焊缝熔合区形成的马氏体α'和α"相分解为α(α2)+β的平衡组织;TC11合金热影响区的魏氏组织转变为网篮组织;试样具有良好的500℃高温综合性能(σb:840 MPa,δ:18.5%,ψ:65%).     

0.2%氢对Ti-22Al-25Nb合金O相转变和B2相再结晶的影响

通过对Ti-22Al-25Nb合金置氢,研究氢对Ti-22Al-25Nb合金O转变及B2再结晶过程的影响。结果表明,在添加质量分数0.2%的氢后Ti-22Al-25Nb合金的热处理过程中,相变过程加快,相变点降低。并且氢促进B2相再结晶过程,960℃时的晶粒尺寸从135μm细化到60μm。在升温过程中氢促进强化相O相分解为B2相,并促进α2相从颗粒状转变为条状。在750℃保温时氢促进O相在晶界处优先析出并迅速长大,氢加快了B2→O相的转变过程。     

固溶处理对Ti-14Al-10Nb合金组织及摩擦磨损性能的影响

研究了固溶处理对Ti-14Al-10Nb合金显微组织和摩擦磨损性能的影响规律。结果表明,锻态Ti-14Al-10Nb合金的显微组织由α₂相和β相组成,其中α₂相呈细小、弯曲的棒状形态。固溶温度的升高促进了显微组织中α₂相向β相的转变,导致α₂相的含量减少,同时棒状α₂相的形态逐渐粗化。锻态Ti-14Al-10Nb合金的摩擦因数及磨损量均小于经固溶处理后试样,表明锻态时合金的耐磨性较好;而且随着固溶温度的升高,α₂相溶解程度增加,合金耐磨性随之下降。Ti-14Al-10Nb合金主要磨损形式为磨粒磨损和氧化磨损。     

高Nb-TiAl合金激光焊接头组织与力学性能研究

采用金相显微镜、扫描电镜、电子探针、 X射线衍射等方法研究了Ti-45Al-8.5Nb合金激光焊接头组织、化学成分和组成相的演变规律,并利用显微硬度仪对焊接接头区的显微硬度分布进行了测试。结果表明,焊接接头与基体组成相相同,均为α2,γ和B2相;焊缝中心区组织为二次熔融的枝晶组织,α2相含量高于基体的,显微硬度高于热影响区和基体的。     

热加工历史对Ti-24A1-15Nb-1.5Mo/TC11双合金盘焊接界面组织与性能的作用

采用电子束焊连接,随后近等温锻造+梯度热处理的工艺加工Ti-24Al-15Nb-1.5Mo/TC11双合金盘,通过OM、SEM、TEM、XRD等研究双合金盘的焊接界面状况.结果表明,经此工艺加工的Ti-24A1-15Nb-1.5Mo/TC11双合金盘的高温拉伸性能较优,焊缝的高温强度大于TC11钛合金,但室温拉伸性能分散度较大.采用梯度热处理不能消除经50%变形的双合金盘的焊缝到TC11侧热影响区的晶界α相.焊缝区簇状α_2相的形成与在近等温锻造、梯度热处理加热保温过程中Al、Nb元素从α_2相中分离出来有关.     

送丝速度对Ti-3Al-6Mo-2Fe-2Zr钛合金激光填丝焊接头组织与性能的影响

采用Ti-6Al-4V(TC4)焊丝对2 mm厚的Ti-3Al-6Mo-2Fe-2Zr钛合金进行激光填丝焊接,利用光学显微镜、扫描电子显微镜、X射线能谱仪等分析测试方法研究了送丝速度对接头显微组织和力学性能的影响. 结果表明,由于从熔合线至母材受到焊接热作用逐渐递减,热影响区组织依次为单一β相、基体β相 + 初生α_p相、基体β相 + 初生α_p相 + 少量次生α_s相. 焊缝中有针状α'相生成,且分布不均匀. 随着送丝速度的增加,针状α'相的数量增加,尺寸增大. 激光填丝焊接头的抗拉强度及断后伸长率均低于母材,随送丝速度的增加,接头抗拉强度上升,断后伸长率下降.其原因在于TC4焊丝的加入,促使针状α'相在焊缝中析出,送丝速度加快,造成焊缝中钼当量[Mo]_eq降低,析出的针状α'相数量进一步增多,尺寸增大. 针状α'相的析出提高了焊缝强度,当送丝速度大于1.0 m/min时,接头的断裂位置为热影响区.     

电子束焊接热输入对Ti-24Al-15Nb-1.5Mo/TC11双合金焊接接头组织和显微硬度的影响

利用OM,SEM,能谱分析和显微硬度等测试方法对Ti-24Al-15Nb-1.5Mo/TC11双合金焊接接头的显微组织特征及硬度进行了分析.结果表明,焊接热输人为135 kJ/m时,焊缝熔合区柱状晶由均匀密集的α'相针状马氏体和少量α相组成,显微硬度平均值为447 HV.焊接热输入增大到150 kJ/m时,熔合区α'相明显减少,焊缝TC11合金侧热影响区的短针状α+β组织变为粗大的长针状组织,Ti-24Al-15Nb-1.5Mo热影响区的β晶粒变得更粗,显微硬度平均值降为402 Hv.这主要是因为增大热输入使焊缝合金元素含量的比例发生变化,并且冷却速度下降使焊缝组织形态和分布改变,最终导致显微硬度降低.合金元素Ti,Al,Nb的含量在焊缝边界发生突变,但在焊缝熔合区达到一个新的平衡.

Abstract：

Microstructure evolution characterization of the Ti-24Al-15Nb-1.5Mo/TC11 dual alloys welded joints obtained on the condition of different electron beam heat input was studied by optical microscope, scanning electron microscope, energy spectrum and micro-hardness analysis. The results show that the energy input have an important effect on the microstructure, grain size, micro-hardness and alloy elements content of welded joints. The microstructure is made up of homogeneous acicular martensite α' phase in fusion zone (FZ) and the average micro-hardness value is 447HV when heat input E = 135 kJ/m is utilized. With heat input increasing to 150 kJ/ m, the number of α'phase decreases in FZ, short acicular α + β phase become coarser in heat-affected zone(HAZ) of TC11, coarse β grains become larger in HAZ of Ti-24Al-15Nb-1.5Mo and the average micro-hardness value drops to 402HV. The result is attributed to the changed content of alloy elements and lower cooling velocity caused by increasing heat input. The content of element Ti, Al and Nb is changed abruptly in the boundary of the joint, but these elements evenly distribute in each zone and hardly diffuse.     

High-Temperature Oxidation Behavior of Ti-22Al-27(Nb, Zr) Alloys

研究了Ti2Al Nb基合金Ti-22Al-(27-x)Nb-x Zr(x=0,1,6,at%)在650~800℃的氧化行为。采用XRD和SEM等测试技术对此温度区间形成的氧化层特征进行了分析。结果表明,相比Ti-22Al-27Nb,含锆合金具有较好的抗氧化性能。Ti-22Al-(27-x)Nb-x Zr合金在650℃氧化100 h,主要氧化产物为Ti O2,而在800℃氧化100 h,Ti O2,Al2O3和Al Nb O4为主要产物,但是在Ti-22Al-21Nb-6Zr合金中还有Zr O2生成。Ti-22Al-26Nb-1Zr合金具有优异抗氧化性能,归因于氧化产物细化形成了致密的氧化层,而Ti-22Al-21Nb-6Zr合金,虽然在800℃也形成了较多Al2O3,但是氧化层中的Zr O2为氧的快速扩散提供通道,进而导致该合金氧化增重明显。     

TC4合金TIG焊接头组织转变与力学性能分析

针对TC4合金TIG焊接头微观组织特征以及焊接过程中的组织转变规律进行了研究,并对接头力学性能进行了分析.经历TIG焊接热循环之后,焊缝及热影响区粗晶区晶粒严重粗化,热影响区晶粒尺寸具有突变特征,过渡区组织呈带状分布,不存在明显的细晶区.升温过程中(α+β)→β转变过程包括两个阶段:原始β→高温β转变和原始α→高温β转变,而且在原始α→高温β转变开始之前,原始β→高温β转变已经完成.冷却过程中在β→α'转变区间冷速较慢时,α'相首先在高温β晶界上形核,并向晶内生长,生成针状α';在快速冷却时,α'相在晶内大量形核,形成"筐篮"组织.硬度测量结果表明,粗晶区部位存在一个软化区;接头抗拉强度与母材接近,接头性能优异.

Abstract：

The microstructure and phase transformation of TC4 alloy weld joints during TIG welding were investigated. The mechanical properties of the welded joints were also tested. When the TC4 alloy was heated by TIG arc, grains in the weld bead and heat affected zone (HAZ) were badly coarsening. The grain size in HAZ has mutant character. The microstructure in the transition region presented zonal distribution. There was no obvious fine grained region. In temperature-rise period, the transformation of (α + β)→β was divided into two processes which included the original β→ high-temperature β and the original α→ high-temperature β. And the previous phase transformation was finished before the next starting. In the cooling process, slowly cooling rate introduced α' phases nucleating at the high-temperature β grain boundary in the β→α transform temperature range. The α' martensite grew up into the center of the β grains and generated acicular martensite. With quicker cooling rate, large numbers of α' phase nucleated in the high-temperature β grains and generated orthogonally oriented martensites. Hardness measurements show there is a softened zone in HAZ. Tensile strength of welded joint was approximate with the base metal. And the properties of the welded joints were good.     

Ti-23Al-17Nb激光焊接接头的组织性能研究

通过室温和高温拉伸性能测试研究焊后热处理和同步预热对Ti-23Al-17Nb(原子分数,下同)合金CO_2激光焊接接头性能的影响.结果表明,接头室温和高温拉伸性能低,焊后真空热处理提高接头室温和高温拉伸性能,仍低于母材;同步预热接头室温强度和塑性与母材相当,高温强度与焊后热处理效果相当.组织分析显示,焊缝存在两个腐蚀衬度区,组织为B2相,热影响区晶粒由熔合线到母材逐渐细化,焊后热处理和同步预热改变β相基体上α2相的析出.     

Ti-6Al-4V钛合金搅拌摩擦焊缝的织构(英文)

采用W-Re合金搅拌头对α+β双相Ti-6Al-4V钛合金进行搅拌摩擦焊并在合适的工艺参数下获得无缺陷焊缝,利用取向成像显微镜对Ti-6Al-4V钛合金搅拌摩擦焊缝的织构进行研究。Ti-6Al-4V钛合金母材为轧制退火态,组织由变形的初生α相和转变β组织构成,具有典型的轧制织构。焊核区组织与母材明显不同,由大量的等轴动态再结晶晶粒组成,并在搅拌摩擦焊过程中形成{φ1=30°,φ=62°,φ2=30°}取向的织构。     

梯度热处理对Ti3Al/TC11双合金焊接界面组织和显微硬度的影响

研究经近等温变形的Ti3Al/TC11双合金在梯度热处理前后,焊接界面显微组织和显微硬度的变化。结果表明,Ti3Al侧热影响区的显微组织在梯度热处理前后变化较小是因为晶界α2相较稳定;焊缝区显微组织变化较大,究其原因是近等温变形造成的晶粒破碎和Ti、Al、Nb等原子的扩散,造成α、α2相互制衡,致使不能形成连续晶界α2或晶界α;TC11合金基体经过梯度热处理后从网篮组织转变成等轴组织;显微硬度的提高是因为Ti、Al、Nb扩散,造成α、α2尺寸小、弥散分布所致。     

DEFORMATION-INDUCED α2→γ TRANSFORMATION IN A HOT DEFORMED Ti-45A1-10Nb ALLOY

1.IntroductionTwo-phase(a2 7)TiAl-basedall0ysarecurrentlyunderextensiveinvestigationbe-causetheirmechanicalpr0pertiesaresuperi0rtoeitherthesinglephasecr20rtheryall0ysl1].Themicrostructureofthetwo-phasealloyswasf0undtohaveastronginfluence0ntheme-chanicalpr0pertiesI2].Themainmicrostructuralcharacteristics0ftheall0yswithlamellarstructurewhichconsistsofalternatinglayers0f0rdered7anda2lamellaewiththecri-entationrelati0nship{lll}./(OOO1)..3<11O>./<1120>.,)havebeenstudiedindetailbymanyinvestigat0r…