Immiscibility Area in the System TiO2–ZrO2–SiO2

A furnace for use in conjunction with the X-ray spectrometer was developed which was capable of heating small powdered specimens in air to temperatures as high as 1850°C. This furnace was also used for the heating and quenching of specimens in air from temperatures as high as 1850°C. An area of two liquids coexisting between 20 and 93 weight % TiO₂ above 1765°± 10°C. was found to exist in the system TiO₂–SiO₂, which is in substantial agreement with the previous work of other investigators. The area of immiscibility in the system TiO₂–SiO₂ was found to extend well into the system TiO₂–ZrO₂–SiO₂. The two liquids were found to coexist over a major portion of the TiO₂ (rutile) primary-phase area with TiO₂ (rutile) being the primary crystal beneath both liquids. The temperature of two-liquid formation in the ternary was found to fall about 80°C. with the first additions of ZrO₂ up to 3%. With larger amounts of ZrO₂ the change in the temperature of the boundary of the two-liquid area was so slight as to be within the limits of error of the temperature measurement. Primary-phase fields for TiO₂ (rutile), tetragonal ZrO₂, and ZrTiO₄ were found to exist in the system TiO₂–ZrO₂–SiO₂. SiO₂ as high cristobalite is known to exist in the system TiO₂–ZrO₂–SiO₂.     

Zirconium Aluminum Carbides: New Precursors for Synthesizing ZrO2–Al2O3 Composites

ZrO₂–Al₂O₃ nanocrystalline powders have been synthesized by oxidizing ternary Zr₂Al₃C₄ powders. The simultaneous oxidation of Al and Zr in Zr₂Al₃C₄ results in homogeneous mixture of ZrO₂ and Al₂O₃ at nanoscale. Bulk nano- and submicro-composites were prepared by hot-pressing as-oxidized powders at 1100°–1500°C. The composition and microstructure evolution during sintering was investigated by XRD, Raman spectroscopy, SEM, and TEM. The crystallite size of ZrO₂ in the composites increased from 7.5 nm for as-oxidized powders to about 0.5 μm at 1500°C, while the tetragonal polymorph gradually converted to monolithic one with increasing crystallite size. The Al₂O₃ in the composites transformed from an amorphous phase in as oxidized powders to θ phase at 1100°C and α phase at higher temperatures. The hardness of the composite increased from 2.0 GPa at 1100°C to 13.5 GPa at 1400°C due to the increase of density.     

Sintering and Crystallization of CaO–Al2O3–ZrO2–SiO2 Glasses Containing Different Amount of Al2O3

In this work several complementary techniques have been employed to carefully characterize the sintering and crystallization behavior of CaO–Al₂O₃–ZrO₂–SiO₂ glass powder compacts after different heat treatments. The research started from a new base glass 33.69 CaO–1.00 Al₂O₃–7.68 ZrO₂–55.43SiO₂ (mol%) to which 5 and 10 mol% Al₂O₃ were added. The glasses with higher amounts of alumina sintered at higher temperatures (953°C [lower amount] vs. 987°C [higher amount]). A combination of the linear shrinkage and viscosity data allowed to easily find the viscosity values corresponding to the beginning and the end of the sintering process. Anorthite and wollastonite crystals formed in the sintered samples, especially at lower temperatures. At higher temperatures, a new crystalline phase containing ZrO₂ (2CaO·4SiO₂·ZrO₂) appeared in all studied specimens.     

A Study of the Phase Relations of ZrO2–TiO2 and ZrO2–TiO2–SiO2

The phase relations of the systems ZrO₂–TiO₂ and ZrO₂–TiO₂–SiO₂ were investigated. X-ray diffraction techniques served as the principal means of analysis. The binary system ZrO₂–TiO₂ was found to be one of partial solid solutions with no intermediate compounds. A eutectic point was found to exist at 50 to 55 weight % ZrO₂ and 1600°C. A preliminary investigation of the ternary system ZrO₂–TiO₂–SiO₂, although not extensive, resulted in a better understanding of this system, with a fairly accurate location of some of its boundary lines. A eutectic point was located at 2% ZrO₂, 10% TiO₂, and 88% SiO₂ at approximately 1500°C.     

Synthesis of 0.4Pb(Mg1/3Nb2/3)O3–0.3Pb(Mg1/2W1/2)O3–0.3PbTiO3 Ceramics by Metal Alkoxide Method, and Its Dielectric Properties

0.4Pb(Mg_1/3Nb_2/3)O₃–0.3Pb(Mg_1/2W_1/2)O₃–0.3PbTiO₃+ x MgO ( x = 0 to 0.04) were prepared by a metal alkoxide method. The percent of perovskite phase of the calcined powders increased with increased calcination temperatures. About 89% of perovskite phase was obtained at 1050°C. The dielectric constant of the pellets fired at 1100°C was increased by the addition of 10 wt% excess Mg(OC₂H₅)₂ and had a maximum value of 7532 at 1 kHz.     

Phase Transformation and Densification Behavior of Microwave-Sintered Si3N4–Y2O3–MgO–ZrO2 System

A 2.45 GHz microwave-sintered Si₃N₄–Y₂O₃–MgO system containing various amounts of ZrO₂ secondary additives have been studied with respect to phase transformation and densification behavior. The temperature dependent dielectric properties were measured from 25°C to 1400°C using a conventional cavity perturbation technique. Phase transformation behavior was studied using X-ray diffractometry. Microwave sintered results were compared with those of conventional sintered results. It has been found that α to β phase transformation was completed at a lower temperature in microwave-sintered samples than those of the conventionally sintered samples. Density of the microwave-sintered samples increased up to 2.5 wt% of ZrO₂ addition and thereafter it showed a tendency to decrease or remain constant. The decrease in density is attributed to the pore generation caused by decomposition due to the localized over heating.     

Al2O3–ZrO2–SiO2 Ternary Glasses for Molybdenum Oxidation Barriers

The wettability of binary and ternary glasses belonging to SiO₂–Al₂O₃–ZrO₂ diagram has been studied using the sessile drop technique at 1750° and 1800°C. The ternary SiO₂–Al₂O₃–ZrO₂ (90–5–5 wt%) glass has proved to be well appropriated as a molybdenum oxidation barrier coating. The addition of 5 wt% of MoO₂ slightly improves its wettablity at higher temperatures without affecting its oxidation barrier properties. The Mo comes into the glass network as a mixture of Mo⁵⁺, Mo⁴⁺, and Mo⁶⁺. After oxidation at 1000°C in oxygen atmosphere, the molybdenum remains in the glass network as Mo⁶⁺.     

Oxidation of ZrB2–SiC: Influence of SiC Content on Solid and Liquid Oxide Phase Formation

The effect of SiC concentration on the liquid and solid oxide phases formed during oxidation of ZrB₂–SiC composites is investigated. Oxide-scale features called convection cells are formed from liquid and solid oxide reaction products upon oxidation of the ZrB₂–SiC composites. These convection cells form in the outermost borosilicate oxide film of the oxide scale formed on the ZrB₂–SiC during oxidation at high temperatures (≥1500°C). In this study, three ZrB₂–SiC composites with different amounts of SiC were tested at 1550°C for various durations of time to study the effect of the SiC concentration particularly on the formation of the convection cell features. A calculated ternary phase diagram of a ZrO₂–SiO₂–B₂O₃ (BSZ) system was used for interpretation of the results. The convection cells formed during oxidation were fewer and less uniformly distributed for composites with a higher SiC concentration. This is because the convection cells are formed from ZrO₂ precipitates from a BSZ oxide liquid that forms upon oxidation of the composite at 1550°C. Higher SiC-containing composites will have less dissolved ZrO₂ because they have less B₂O₃, which results in a smaller amount of precipitated ZrO₂ and consequently fewer convection cells.     

Effect of MgO Addition on the Microstructure Development of 3 mol% Y2O3—ZrO2

MgO addition to 3 mol% Y₂O₃–ZrO₂ resulted in enhanced densification at 1350°C by a liquid-phase sintering mechanism. This liquid phase resulted from reaction of MgO with trace impurities of CaO and SiO₂ in the starting powder. The bimodal grain structure thus obtained was characterized by large cubic ZrO₂ grains with tetragonal ZrO₂ precipitates, which were surrounded by either small tetragonal grains or monoclinic grains, depending on the heat-treatment schedule.     

Phase Equilibrium in the System PbO-TiO2–ZrO2

Phase equilibrium relations in the system PbO–TiO₂–ZrO₂ were studied by quenching in the range where the PbO content is 50 mole % and more. Isotherms were examined at 1100°, 1200°, and 1300°C and tie lines were determined between the liquid and solid solution in equilibrium. The incongruent melting point of PbZrO₃ was 1570°C and the equilibrium between liquid, PbO-type solid, and PbZrO₃ is peritectic. Pb(Zr,Ti)O₃ solid solutions containing more than 14 mole % PbZrO₃ decomposed to liquid, ZrO₂, and Pb(Zr,Ti)O₃ and the decomposition temperature rises from 1340° to 1570°C with increasing PbZrO₃ content. The system PbTiO₃–PbZrO₃ should not be treated as a binary, but as a section of the ternary system.     

SiO2–PbO–CaO–ZrO2–TiO2–(B2O3–K2O), A New Zirconolite Glass–Ceramic System: Crystallization Behavior and Microstructure Evaluation

Zirconolite (CaZrTi₂O₇) is a mineral that has a high containment capacity for actinides and lanthanides and is considered to be a good candidate for the immobilization of radioactive wastes. The glass–ceramic technique seems to be a very suitable and convenient method to produce zirconolite crystals by precipitating them in a specific glass matrix. In this study, development of a new zirconolite-based glass–ceramic belonging to SiO₂–PbO–CaO–ZrO₂–TiO₂–(B₂O₃–K₂O) system was investigated. The presence of PbO, together with B₂O₃ and K₂O, allowed the preparation of a X-ray diffraction (XRD) amorphous glass with a relatively high concentration of ZrO₂ and TiO₂, which was successfully converted to a glass–ceramic containing 34 wt% of zirconolite after heating at 770°C for 4 h. Differential thermal analysis, XRD, scanning electron microscope, and energy dispersive X-ray spectroscopy were used to determine the crystallization conditions, identify the crystallized phases, determine their compositions and quantities and observe and analyze the microstructures. The zirconolite crystals showed a platelet morphology with a monoclinic structure characterized by a =1.246 nm, b =0.7193 nm, c =1.128 nm, and β=100.508°.     

Novel Mg2Zr5O12/Mg2Zr5O12–ZrO2–MgF2 Gradient Layer Coating on Magnesium Formed by Microarc Oxidation

A novel Mg₂Zr₅O₁₂-based coating on magnesium was formed by microarc oxidation (MAO) in a K₂ZrF₆-containing electrolyte. The structure of the coating was examined by X-ray diffraction using the grazing angle method, scanning electron microscopy, and transmission electron microscopy. The friction and wear properties of the MAO-coated and -uncoated Mg samples were evaluated in a ball-on-disk testing system. The corrosion resistance of the coating in a 3.5% NaCl solution was investigated by the potentiodynamic polarization test. The coating is relatively dense and composed of a Mg₂Zr₅O₁₂–ZrO₂–MgF₂ inner layer and a nanocrystalline Mg₂Zr₅O₁₂ outer layer with a maximum hardness of 1240 Hv. The friction coefficient of the coating against Si₃N₄ is 0.35 under a dry-sliding condition. The corrosion resistance of the magnesium substrate is improved considerably by MAO treatment. The corrosion potential of the Mg₂Zr₅O₁₂-coated sample is −1.43 V with a current density as low as 7.06 × 10⁻⁸ A/cm². It is expected that the coating can considerably protect magnesium from wear and corrosion.     

Rapid Rate Sintering of Nanocrystalline ZrO2−3 mol% Y2O3

Conventional ramp-and-hold sintering with a wide range of heating rates was conducted on submicrometer and nanocrystalline ZrO₂–3 mol% Y₂O₃ powder compacts. Although rapid heating rates have been reported to produce high density/fine grain size products for many submicrometer and smaller starting powders, the application of this technique to ZrO₂–3 mol% Y₂O₃ produced mixed results. In the case of submicrometer ZrO₂–3 mol% Y₂O₃, neither densification nor grain growth was affected by the heating rate used. In the case of nanocrystalline ZrO₂–3 mol% Y₂O₃, fast heating rates severely retarded densiflcation and had a minimal effect on grain growth. The large adverse effect of fast heating rates on the densification of the nanocrystalline powder was traced to a thermal gradient/differential densification effect. Microstructural evidence suggests that the rate of densification greatly exceeded the rate of heat transfer in this material; consequently, the sample interior was not able to densify before being geometrically constrained by a fully dense shell which formed at the sample exterior. This finding implies that rapid rate sintering will meet severe practical constraints in the manufacture of bulk nanocrystalline ZrO₂–3 mol% Y₂O₃ specimens.     

Densification and Phase Transformation During Pressureless Sintering of Nanocrystalline ZrO2–Y2O3–CuO Ternary System

ZrO₂–Y₂O₃–CuO nanocrystalline powders have been synthesized using a chemical coprecipitation method. Nano-powders were compacted uniaxially and densified in a muffle furnace. Densification studies show that the presence of CuO accelerates the densification process of ZrO₂(3Y). A fully dense (>96%) pellet of ZrO₂(3Y)/5 mol% CuO was obtained after sintering at 900°C, with a very small grain size of 44 nm calculated by X-ray line broadening.     

Influence of the Y2O3 Content and Temperature on the Mechanical Properties of Melt-Grown Al2O3–ZrO2 Eutectics

The effect of Y₂O₃ content on the flexure strength of melt-grown Al₂O₃–ZrO₂ eutectics was studied in a temperature range of 25°–1427°C. The processing conditions were carefully controlled to obtain a constant microstructure independent of Y₂O₃ content. The rod microstructure was made up of alternating bands of fine and coarse dispersions of irregular ZrO₂ platelets oriented along the growth axis and embedded in the continuous Al₂O₃ matrix. The highest flexure strength at ambient temperature was found in the material with 3 mol% Y₂O₃ in relation to ZrO₂(Y₂O₃). Higher Y₂O₃ content did not substantially modify the mechanical response; however, materials with 0.5 mol% presented a significant degradation in the flexure strength because of the presence of large defects. They were nucleated at the Al₂O₃–ZrO₂ interface during the martensitic transformation of ZrO₂ on cooling and propagated into the Al₂O₃ matrix driven by the tensile residual stresses generated by the transformation. The material with 3 mol% Y₂O₃ retained 80% of the flexure strength at 1427°C, whereas the mechanical properties of the eutectic with 0.5 mol% Y₂O₃ dropped rapidly with temperature as a result of extensive microcracking.     

Microstructural Characterization of ZrO2 Particles Prepared by Reaction of Gaseous ZrCl4 with Fe2O3

The microstructure of ZrO₂ fine particles produced by a novel synthesis method at 450° and 950°C has been studied. The fundamentals of the synthesis method, which involves both chemical and diffusion phenomena, are presented. The method is based on mass transport through the gaseous phase between metallic zirconium and Fe₂O₃ powder. The mass-transporting chemical species are zirconium and iron chlorides. This article focuses on the microstructure and structure of ZrO₂ particles formed by the reaction between gaseous ZrCl₄ and solid Fe₂O₃, which is a relevant reaction step that occurs during the synthesis process. The resulting ZrO₂ crystals grown on Fe₂O₃ particles have been analyzed using transmission electron microscopy. Microstructural characterization has been complemented by X-ray diffractometry analysis. Tetragonal-ZrO₂ is produced at 450°C and monoclinic-ZrO₂ single crystals are produced at 950°C.     

Low-Temperature Phase Equilibria by the Flux Method and the Metastable–Stable Phase Diagram in the ZrO2–CeO2 System

Low-temperature phase equilibria ranging from 1000° to 1200°C in the ZrO₂–CeO₂ system were investigated by annealing compositionally homogeneous ZrO₂–CeO₂ solid solutions in a Na₂B₂O₇.1 NaF flux. The 5 mol% CeO₂ samples decomposed into monoclinic ( m ) and tetragonal ( t ) phases during annealing at 1100°2 and 1120°C, and the t -phase transformed diffusionlessly into monoclinic ( m ') symmetry during quenching. A eutectoid reaction, t → ( m + c ), was confirmed to occur at 1055°± 10°C, where the equilibrium compositions of the t -, m -, and c -phases were 11.2 ± 2.8, 0.9 ± 0.9, and 84 ± 1 mol% CeO₂, respectively. The equilibrium phase boundaries were almost independent of the annealing time and/or the flux:sample ratio, which indicates that the flux accelerates the reaction rate withouts affecting the equilibration. The previous data are discussed using metastable–stable phase diagrams. The discrepancies of the low-temperature phase diagram in the literature are attributable to either regarding the metastable phase boundaries as stable ones or ignoring the sluggish kinetics.     

Synthesis of the Orthorhombic Phase of 2Y˙ZrO2

A mixture of tetragonal and monoclinic 2Y˙ZrO₂ (2 mol% Y₂O₃–ZrO₂) powder was treated from 400° to 800°C and from 4 to 7 GPa for 30 min. The products were identified by powder XRD, Raman spectroscopy, and TEM. Results indicated that an orthorhombic phase was synthesized at T=400° to 600°C and P>4 GPa. The lattice parameters were obtained as a=0.505, b=0.525, and c=0.509 nm; the density was 6.17 Mg/m³. The orthorhombic phase always coexisted with the tetragonal phase in the products. The amounts of the tetragonal phase before and after treatment remained largely unchanged, whereas the amount of new orthorhombic phase was nearly the same as the decreased amount of the monoclinic phase. It was assumed, therefore, that only the monoclinic phase transformed into the orthorhombic phase.     

Phase Relations and Ordering in the Systems MgO-Y2O3-ZrO2 and CaO-MgO-ZrO2

The phase relations in the systems MgO-Y₂O₃-ZrO₂ and CaO-MgO-ZrO₂ were established at 1220° and 1420°C. The system MgO-Y₂O₃-ZrO₂ possesses a much-larger cubic ZrO₂ solid solution phase field than the system CaO-MgO-ZrO₂ at both temperatures. The ordered δ phase (Zr₃Y₄O₁₂) was found to be stable in the system ZrO₂-Y₂O₃ at 1220°C. Two ordered phases φ₁ (CaZr₄O₉) and φ₂ (Ca₆Zr₁₉O₄₄) were stable at 1220°C in the system ZrO₂-CaO. At 1420°C no ordered phase appears in either system, in agreement with the previously determined temperature limits of the stability for the δ, φ₁, and φ₂ phases. The existence of the compound Mg₃Y_zO₆ could not be confirmed.     

In-Plane Polarized 0.7Pb(Mg1/3Nb2/3)O3–0.3PbTiO3 Thin Films

Ferroelectric 0.7Pb(Mg_1/3Nb_2/3)O₃–0.3PbTiO₃ (PMN-PT) thin films were deposited on ZrO₂/SiO₂/silicon substrates using a chemical-solution-deposition method. Using a thin PZT film as a seed layer for the PMN-PT films, phase-pure perovskite PMN-PT could be obtained via rapid thermal annealing at 750°C for 60 s. The electrical properties of in-plane polarized thin films were characterized using interdigitated electrode arrays on the film surface. Ferroelectric hysteresis loops are observed with much larger remanent polarizations (∼24 μC/cm²) than for through-the-thickness polarized PMN-PT thin films (10–12 μC/cm²) deposited on Pt/Ti/Si substrates. For a finger spacing of 20 μm, the piezoelectric voltage sensitivity of in–plane polarized PMN-PT thin films was ∼20 times higher than that of through-the-thickness polarized PMN-PT thin films.