Performance and characterization of Ru/Al2O3 and Ru/SiO2 catalysts modified with Mn for Fischer–Tropsch synthesis

Mn effect and characterization on γ-Al₂O₃-, -Al₂O₃- and SiO₂-supported Ru catalysts were investigated for Fischer–Tropsch synthesis under pressurized conditions. In the slurry phase Fischer–Tropsch reaction, γ-Al₂O₃ catalysts showed higher performance on CO conversion and C₅⁺ selectivity than -Al₂O₃ and SiO₂ catalysts. Moreover, Ru/Mn/γ-Al₂O₃ exhibited high resistance to catalyst deactivation and other catalysts were deactivated during the reaction. From characterization results on XRD, TPR, TEM, XPS and pore distribution, Ru particles were clearly observed over the catalysts, and γ-Al₂O₃ catalysts showed a moderate pore and particle size such as 8 nm, where -Al₂O₃ and SiO₂ showed highly dispersed ruthenium particles. The addition of Mn to γ-Al₂O₃ enhanced the removal of chloride from RuCl₃, which can lead to the formation of metallic Ru with moderate particle size, which would be an active site for Fischer–Tropsch reaction. Concomitantly, manganese chloride is formed. These schemes can be assigned to the stable nature of Ru/Mn/γ-Al₂O₃ catalyst.     

η-Al2O3与γ-Al2O3在CS2催化水解反应中的性能比较

通过制备高纯度的前驱体湃铝石获得了η-Al₂O₃材料,采用XRD验证了η-Al₂O₃与γ-Al₂O₃在晶相结构上的差异,比较了两者的表面形貌、织构及酸碱性能,结果显示,η-Al₂O₃与γ-Al₂O₃的比表面积相当,但η-Al₂O₃具有更弱的弱碱位和较少的强碱位,并拥有丰富的中等强度酸性位。将η-Al₂O₃与γ-Al₂O₃作为催化剂应用于CS₂水解反应,结果表明,在(200~450) ℃测试温度范围内,η-Al₂O₃催化剂对CS₂的水解活性始终优于γ-Al₂O₃,两种催化剂上CS₂反应的浓度效应也明显不同,推测与它们的酸碱性质影响了对CS₂的吸附能力有关,导致两者催化CS₂水解反应遵循了不同的机制。     

Effect of La on the thermal stability of Pd/γ-Al2O3 catalytic membranes

Lanthanum-doped Pd/γ-Al₂O₃ and Pd/γ-Al₂O₃ membranes were prepared by sol-gel methods. The thermal stability of the unsupported Pd/γ-Al₂O₃ and La/Pd/γ-Al₂O₃ membranes was investigated with BET (including average pore size, pore volume and BET surface area), XRD, and DTA techniques. The average pore size of the Pd/γ-Al₂O₃ membranes increased sharply after sintering at temperatures higher than 1000°C. Addition of 3 mol% lanthanum can raise the temperature of the γ-Al₂O₃ to-Al₂O₃ phase transformation significantly. This improves the thermal stability of the Pd/γ-Al₂O₃ catalytic membranes.     

Effect of phosphorus addition on the hydrotreating activity of NiMo/Al2O3 carbide catalyst

A series of phosphorus promoted γ-Al₂O₃ supported NiMo carbide catalysts with 0–4.5 wt.% P, 13 wt.% Mo and 2.5 wt.% Ni were synthesized and characterized by elemental analysis, pulsed CO chemisorption, BET surface area measurement, X-ray diffraction, near-edge X-ray absorption fine structure, DRIFT spectroscopy of CO adsorption and H₂ temperature programmed reduction. X-ray diffraction patterns and CO uptake showed the P addition to NiMo/γ-Al₂O₃ carbide, increased the dispersion of β-Mo₂C particles. DRIFT spectra of adsorbed CO revealed that P addition to NiMo/γ-Al₂O₃ carbide catalyst not only increases the dispersion of Ni-Mo carbide phase, but also changes the nature of surface active sites. The hydrodenitrogenation (HDN) and hydrodesulfurization (HDS) activities of these P promoted NiMo/γ-Al₂O₃ carbide catalysts were performed in trickle bed reactor using light gas oil (LGO) derived from Athabasca bitumen and model feed containing quinoline and dibenzothiophene at industrial conditions. The P added NiMo/γ-Al₂O₃ carbide catalysts showed enhanced HDN activity compared to the NiMo/γ-Al₂O₃ catalysts with both the feed stocks. The P had almost no influence on the HDS activity of NiMo/γ-Al₂O₃ carbide with LGO and dibenzothiophene. P addition to NiMo/γ-Al₂O₃ carbide accelerated CN bond breaking and thus increased the HDN activity.     

Pt/Pt-Ce/γ-Al2O3催化氧化甲苯研究

通过等体积浸渍法制备单贵金属Pt/γ-Al₂O₃和双金属Pt-Ce/γ-Al₂O₃催化剂,考察Ce对催化剂活性的影响,确定催化剂最优配比。结果表明,当Pt的负载量为质量分数0.5%时,Pt/γ-Al₂O₃催化活性最高;当Pt的负载量为质量分数0.2%,Ce的负载量为质量分数1.0%时,Pt-Ce/γ-Al₂O₃催化剂的催化活性最高。Pt-Ce/γ-Al₂O₃催化剂的甲苯转化率高于Pt/γ-Al₂O₃催化剂。随着Pt负载量增大,催化剂孔容、孔径减小。粉体式催化剂性能优于整体式催化剂,但差别不大;Ce的添加有助于催化剂活性的提升。     

Surface properties and reactivity of Cu/γ-Al2O3 catalysts for NO reduction by C3H6: Influences of calcination temperatures and additives

The influences of calcination temperatures and additives for 10 wt.% Cu/γ-Al₂O₃ catalysts on the surface properties and reactivity for NO reduction by C₃H₆ in the presence of excess oxygen were investigated. The results of XRD and XPS show that the 10 wt.% Cu/γ-Al₂O₃ catalysts calcined below 973 K possess highly dispersed surface and bulk CuO phases. The 10 wt.% Cu/γ-Al₂O₃ and 10 wt.% Mn–10 wt.% Cu/γ-Al₂O₃ catalysts calcined at 1073 K possess a CuAl₂O₄ phase with a spinel-type structure. In addition, the 10 wt.% La–10 wt.% Cu/γ-Al₂O₃ catalyst calcined at 1073 K possesses a bulk CuO phase. The result of NO reduction by C₃H₆ shows that the CuAl₂O₄ is a more active phase than the highly dispersed and bulk CuO phase. However, the 10 wt.% Mn–10 wt.% Cu/γ-Al₂O₃ catalyst calcined at 1073 K possesses significantly lower reactivity for NO reduction than the 10 wt.% Cu/γ-Al₂O₃ catalyst calcined at 1073 K, although these catalysts possess the same CuAl₂O₄ phase. The low reactivity for NO reduction for 10 wt.% Mn–10 wt.% Cu/γ-Al₂O₃ catalyst calcined at 1073 K is attributed to the formation of less active CuAl₂O₄ phase with high aggregation and preferential promotion of C₃H₆ combustion to CO_x by MnO₂. The engine dynamometer test for NO reduction shows that the C₃H₆ is a more effective reducing agent for NO reduction than the C₂H₅OH. The maximum reactivity for NO reduction by C₃H₆ is reached when the NO/C₃H₆ ratio is one.     

Deactivation studies over NiO/γ-Al2O3 catalysts for partial oxidation of methane to syngas

Two types of NiO/γ-Al₂O₃ catalysts prepared by the impregnation and the sol–gel method were used for the partial oxidation of methane to syngas at 850°C (GHSV1.8×10⁵ lkg⁻¹ h⁻¹). The effects of the carbon deposition, the loss and sintering of nickel and the phase transformation of γ-Al₂O₃ support on the catalytic performance during 80 h POM reaction were investigated with a series of characterization such as XRD, BET, AAS, TG, and XPS. The results indicated that the carbon deposition and the loss and sintering of nickel could not cause the serious decrease of catalytic performance over NiO/γ-Al₂O₃ catalyst during the short-time reaction. However, the slow process of the support γ-Al₂O₃ phase transforming into -Al₂O₃ could slowly decrease the performance of NiO/γ-Al₂O₃ catalysts. Aimed at the reasons of the deactivation, an improved catalyst was obtained by the complexing agent-assisted sol–gel method.     

Interactions NO—CO and O2—NO—CO on CuCo2O4/γ-Al2O3 and on γ-Al2O3- and CuCo2O4/γ-Al2O3-supported Pt, Rh and Pt—Rh catalysts, a transient response study

The interactions NO—CO and O₂—NO—CO have been studied onCuCo₂O₄γ-Al₂O₃ and on γ-Al₂O₃- and CuCo₂O₄γ-Al₂O₃-supported Pt, Rh and Pt—Rh catalysts. The deposition of noble metals (Pt, Rh and Pt—Rh) on CuCo₂O₄γ-Al₂O₃ instead of γ-Al₂O₃ is beneficial in: lowering the temperature at which maximum N₂O is formed and decreasing the maximum N₂O concentration attained; lowering the onset temperature of NO to N₂ reduction, and increasing the N₂ selectivity; preserving the activity towards NO to N₂ reduction on a higher level following the concentration step NO + COO₂+ NO + CO and changing the conditions from stoichiometric to oxidizing (50% excess of oxidants). The reason for this behaviour of the CuCo₂O₄γ-Al₂O₃-based noble metal catalysts is the formation (reversible) of a reduced surface layer on the CuCo₂O₄ supported spinel under the conditions of a stoichiometric NO + CO mixture.     

NO reduction by CH4 in the presence of O2 over La2O3 supported on Al2O3

Dispersing La₂O₃ on δ- or γ-Al₂O₃ significantly enhances the rate of NO reduction by CH₄ in 1% O₂, compared to unsupported La₂O₃. Typically, no bend-over in activity occurs between 500° and 700°C, and the rate at 700°C is 60% higher than that with a Co/ZSM-5 catalyst. The final activity was dependent upon the La₂O₃ precursor used, the pretreatment, and the La₂O₃ loading. The most active family of catalysts consisted of La₂O₃ on γ-Al₂O₃ prepared with lanthanum acetate and calcined at 750°C for 10 h. A maximum in rate (mol/s/g) and specific activity (mol/s/m²) occurred between the addition of one and two theoretical monolayers of La₂O₃ on the γ-Al₂O₃ surface. The best catalyst, 40% La₂O₃/γ-Al₂O₃, had a turnover frequency at 700°C of 0.05 s⁻¹, based on NO chemisorption at 25°C, which was 15 times higher than that for Co/ZSM-5. These La₂O₃/Al₂O₃ catalysts exhibited stable activity under high conversion conditions as well as high CH₄ selectivity (CH₄ + NO vs. CH₄ + O₂). The addition of Sr to a 20% La₂O₃/γ-Al₂O₃ sample increased activity, and a maximum rate enhancement of 45% was obtained at a SrO loading of 5%. In contrast, addition of SO⁼₄ to the latter Sr-promoted La₂O₃/Al₂O₃ catalyst decreased activity although sulfate increased the activity of Sr-promoted La₂O₃. Dispersing La₂O₃ on SiO₂ produced catalysts with extremely low specific activities, and rates were even lower than with pure La₂O₃. This is presumably due to water sensitivity and silicate formation. The La₂O₃/Al₂O₃ catalysts are anticipated to show sufficient hydrothermal stability to allow their use in certain high-temperature applications.     

低成本大比表面积γ-Al2O3的制备

以廉价无机铝盐硫酸铝为原料,氨水为沉淀剂,十二烷基硫酸钠为添加剂,采用简单沉淀法制备得到较大比表面积γ-Al₂O₃。通过N₂低温物理吸附-脱附、X射线衍射、红外光谱、热重、元素分析、扫描及透射电镜等,研究制备过程中沉淀温度、溶液pH值和添加剂用量对产物γ-Al₂O₃及其前驱体的晶相结构、形貌织构等性质的影响。结果表明,在沉淀温度75 ℃、硫酸铝浓度0.25 mol·L^-1、溶液pH=9.0、老化时间12 h和n(十二烷基硫酸钠)∶n[Al₂(SO₄)₃]=0.375∶1条件下,所得前驱体(拟薄水铝石)经600 ℃焙烧后,可获得大比表面积(416.65 m²·g^-1)γ-Al₂O₃,并且样品中因十二烷基硫酸钠添加,引入的S及Na等杂质含量极少。     

The deposition of γ-Al2O3 layers on ceramic and metallic supports for the preparation of structured catalysts

Deposition of γ-Al₂O₃ washcoats onto Aluminium and FeCrAlloy^® supports in the form of slabs and onto -Al₂O₃ tubes was performed according to a two-step procedure involving: (a) deposition of a bohemite primer, (b) deposition of the γ-Al₂O₃ layer, both by dip coating into powder dispersions in HNO₃ aqueous solutions. We present herein data concerning the effects of the major preparation variables (HNO₃ and H₂O concentrations in the dispersion, withdrawal velocity, drying temperature, number of dipping cycles, calcination temperature) on the deposited coating load and on the adherence of the washcoat. Based on a rheological characterisation of the γ-Al₂O₃ dispersions, we propose also a correlation between their apparent viscosity and the washcoat load. Finally, we briefly illustrate the activity in catalytic combustion reactions of structured Pd-based catalysts prepared according to the investigated washcoating methods.     

K2CO3/γ-A12O3催化剂在棉籽油制备生物柴油中的应用

利用等体积浸渍法制备K₂CO₃/γ-A1₂O₃负载型固体碱催化剂,应用于棉籽油和甲醇酯交换反应制备生物柴油。对催化剂使用前的保存条件、水分、重复使用性能、游离脂肪酸影响以及失活和再生进行了分析。结果表明,固体催化剂K₂CO₃/γ-Al₂O₃具有较好的抗水性,酸度对催化剂影响明显,重复使用4次未经活化的催化剂,催化活性明显降低,催化剂应密封保存。K₂CO₃/γ-A1₂O₃负载型固体碱催化剂经济实惠且催化效果良好。     

CO气相偶联合成草酸二甲酯Pd/α-Al2O3催化剂失活与再利用

作为合成气制乙二醇关键步骤之一,CO与亚硝酸甲酯合成草酸二甲酯备受关注。综述了近年来CO气相偶联合成草酸二甲酯Pd/α-Al₂O₃催化剂失活与再利用研究进展,探讨催化剂再利用工艺存在的问题,指出应根据在工业应用中出现的问题对Pd/α-Al₂O₃催化剂进行失活研究,在此基础上开发针对性的再生工艺;钯催化剂回收方面萃取法和吸附法逐渐成为研究重点,高效、低耗、短流程绿色工艺的开发是失活钯催化剂再利用的发展方向。     

Carbon formation and its influence on ethanol steam reforming over Ni/Al2O3 catalysts

Ethanol steam reforming was studied over Ni/Al₂O₃ catalysts. The effect of support (- and γ-Al₂O₃), metal loading and a comparison between conventional H₂ reduction with an activation method employing a CH₄/O₂ mixture was investigated. The properties of catalysts were studied by N₂ physisorption, X-ray diffraction (XRD) and temperature programmed reduction (TPR). After activity tests, the catalysts were analyzed by scanning electron microscopy (SEM) and thermogravimetric analysis (TG/DTA). Ni supported on γ-Al₂O₃ was more active for H₂ production than the catalyst supported on -Al₂O₃. Metal loading did not affect the catalytic performance. The alternative activation method with CH₄/O₂ mixture affected differently the activity and stability of the Ni/γ-Al₂O₃ and the Ni/-Al₂O₃ catalyst. This activation method increased significantly the stability of Ni/-Al₂O₃ compared to H₂ reduction. SEM and TG/DTA analysis indicate the formation of filamentous carbon during the CH₄/O₂ activation step, which is associated with the increasing catalyst activity and stability. The effect of temperature on the type of carbon formed was investigated; indicating that filamentous coke increased activity while encapsulating coke promoted deactivation. A discussion about carbon formation and the influence on the activity is presented.     

Role of CeO2 in Ni/CeO2–Al2O3 catalysts for carbon dioxide reforming of methane

Ni catalysts supported on γ-Al₂O₃, CeO₂ and CeO₂–Al₂O₃ systems were tested for catalytic CO₂ reforming of methane into synthesis gas. Ni/CeO₂–Al₂O₃ catalysts showed much better catalytic performance than either CeO₂- or γ-Al₂O₃-supported Ni catalysts. CeO₂ as a support for Ni catalysts produced a strong metal–support interaction (SMSI), which reduced the catalytic activity and carbon deposition. However, CeO₂ had positive effect on catalytic activity, stability, and carbon suppression when used as a promoter in Ni/γ-Al₂O₃ catalysts for this reaction. A weight loading of 1–5 wt% CeO₂ was found to be the optimum. Ni catalysts with CeO₂ promoters reduced the chemical interaction between nickel and support, resulting in an increase in reducibility and stronger dispersion of nickel. The stability and less coking on CeO₂-promoted catalysts are attributed to the oxidative properties of CeO₂.     

Highly dispersed NiW/γ-Al2O3 catalyst prepared by hydrothermal deposition method

This article describes a novel hydrothermal deposition method for preparing highly dispersed NiW/γ-Al₂O₃ catalysts and demonstrates its advantages over the conventional impregnation method. Via the hydrothermal precipitation reactions between sodium tungstate and hydrochloric acid and between nickel nitrate and urea, respectively, the active species W and Ni were deposited on γ-Al₂O₃. In the hydrothermal deposition of WO₃, a surfactant hexadecyltrimethyl ammonium bromide (CTAB) was used to prevent the aggregation of WO₃. The characterization results obtained by means of X-ray photoelectron spectroscopy (XPS), N₂ adsorption and high-resolution transmission electron microscopy (HRTEM) measurements showed that compared with the catalyst prepared by the conventional impregnation method, the catalyst with the same metal contents prepared by the hydrothermal deposition had much higher W and Ni dispersion, higher specific surface area, larger pore volume, the significantly decreased slab length and slightly increased stacking degree of sulfided W species, leading to the significantly enhanced dibenzothiophene (DBT) hydrodesulfurization (HDS) activity. The DBT HDS assessment results also revealed that the catalyst containing 17.7 wt% WO₃ and 2.4 wt% NiO prepared by the hydrothermal deposition method had the similar DBT HDS activity as a commercial NiW/γ-Al₂O₃ catalyst containing 23 wt% WO₃ and 2.6 wt% NiO, resulting in the greatly decreased amount of active metals for achieving the same HDS activity.     

Study of Ag/La0.6Sr0.4MnO3 catalysts for complete oxidation of methanol and ethanol at low concentrations

Ag-modified La_0.6Sr_0.4MnO₃-based catalysts with the perovskite-type structure were prepared by using a citric acid sol–gel method, and their catalytic performance for complete oxidation of methanol and ethanol was evaluated and compared with that of the γ-Al₂O₃-supported catalysts, Ag/γ-Al₂O₃, Pt/γ-Al₂O₃, and Pd/γ-Al₂O₃. The results showed that the Ag-modified La_0.6Sr_0.4MnO₃-based catalysts with the perovskite-type structure displayed the activity significantly higher than that of the supported precious metal catalysts, 0.1%Pd/γ-Al₂O₃ and 0.1%Pt/γ-Al₂O₃ in the temperature range of 370–573 K. Over a 6%Ag/20%La_0.6Sr_0.4MnO₃/γ-Al₂O₃ catalyst, the T₉₅ temperature for methanol oxidation can be as low as 413 K. Even at such low reaction temperature, there were little HCHO and CO detected in the reaction exit-gas. However, for the 0.1%Pd/γ-Al₂O₃ and 0.1%Pt/γ-Al₂O₃ catalysts, the HCHO content in the reaction exit-gas reached 200 and 630 ppm at their T₉₅ temperatures. Over a 6%Ag/La_0.6Sr_0.4MnO₃ catalyst, the T₉₅ temperature for ethanol oxidation can be as low as 453 K, with a corresponding content of CH₃CHO in the exit-gas at 782 ppm; when ethanol oxidation is performed at 493 K, the content of acetaldehyde in the exit-gas can be below 1 ppm. Characterization of the catalysts by X-ray diffraction (XRD), TEM, XPS, laser Raman spectra (LRS), hydrogen temperature-programmed reduction (H₂-TPR) and oxygen temperature-programmed desorption (O₂-TPD) methods revealed that both the surface and the bulk phase of the perovskite La_0.6Sr_0.4MnO₃ played important roles in the catalytic oxidation of the alcohols, and that γ-Al₂O₃ as the bottom carrier could be beneficial in creating a large surface area of catalyst. Moreover, a small amount of Ag⁺ doped onto the surface of La_0.6Sr_0.4MnO₃ was able to partially occupy the positions of La³⁺ and Sr²⁺ due to their similar ionic radii, and thus, became stabilized by the perovskite lattice, which would be in favor of preventing the aggregation of the Ag species on the surface and enhancing the stability of the catalyst. On the other hand, modification of the Ag⁺ to the surface of La_0.6Sr_0.4MnO₃ resulted in an increase in relative content of the surface O₂²⁻/O⁻ species highly reactive toward the alcohols and aldehydes as well as CO. Besides, solution of low-valence metal oxides SrO and Ag₂O with proper amounts in the lattice of the trivalent metal perovskite-type oxide LaMnO₃ would also lead to an increase in the content of the reducible Mnⁿ⁺ and the formation of anionic vacancies, which would be favorable for the adsorption-activation of oxygen on the functioning catalyst and the transport of the lattice and surface oxygen species. All these factors would contribute to the pronounced improvement of the catalyst performance.     

The simultaneous activation of methane and carbon dioxide to C2 hydrocarbons under pulse corona plasma over La2O3/γ-Al2O3 catalyst

The pulse corona plasma has been used as an activation method for reaction of methane and carbon dioxide, the product was C₂ hydrocarbons and by-products were CO and H₂. Methane conversion and the yield of C₂ hydrocarbons were affected by the carbon dioxide concentration in the feed. The conversion of methane increased with increasing carbon dioxide concentration in the feed whereas the yield of C₂ hydrocarbons decreased. The synergism of La₂O₃/γ-Al₂O₃ and plasma gave methane conversion of 24.9% and C₂ hydrocarbons yield of 18.1% were obtained at the power input of plasma was 30 W. The distribution of C₂ hydrocarbons changed by using Pd-La₂O₃/γ-Al₂O₃ catalyst, the major C₂ product was ethylene.     

制备条件对NiMo/γ-Al2O3催化剂上萘加氢生成四氢萘的影响

采用等体积浸渍法制备加氢催化剂NiMo/γ-Al₂O₃,在悬浮床上考察不同的制备条件下NiMo/γ-Al₂O₃对萘加氢生成四氢萘的影响。结果表明,催化剂的制备条件对加氢活性有显著的影响,NiMo/γ-Al₂O₃催化剂的最佳制备条件为共浸渍法负载金属组分Ni和Mo,在500 ℃的温度下焙烧4 h。此条件下制备的催化剂上四氢萘的选择性高达95.2%。     

A comparison of sodium-modified Rh/γ-Al2O3 and Pd/γ-Al2O3 catalysts operated under simulated TWC conditions

Addition of Na to Rh/γ-Al₂O₃ and Pd/γ-Al₂O₃ catalysts operated under identical simulated TWC conditions has dramatically different effects in the two cases (although the two metals respond similarly to Na promotion of NO_x reduction in the absence of gaseous oxygen). Na addition to rhodium has a detrimental effect as manifested by severe poisoning and decreased nitrogen selectivity over the greater part of the temperature range studied. In contrast, Na promotion significantly improves the overall performance of Pd/γ-Al₂O₃ catalysts under simulated TWC conditions. This is manifested by a considerable widening of the gas composition window over which palladium delivers high NO_x conversion, whilst at the same time exhibiting markedly improved selectivity towards N₂ formation. The very different behaviour of the two metals may be understood in terms of a single underlying effect, namely, the electronic influence of sodium ions on the adsorption strength (and hence relative coverages) of the various reactants on the metal surface.