抑制剂对WC-15wt%Co硬质合金性能的影响

研究了抑制剂的不同种类和添加量对WC-15wt%Co硬质合金性能的影响。添加抑制剂可以抑制烧结过程中的晶粒长大及非均匀长大,提高合金的各项性能。在原始WC粉末粒度较粗的合金中添加一定量的VC/Cr3C2,也可以制取WC晶粒度达到亚微米级的合金。     

氧化铬对超细WC-10%Co硬质合金组织和性能的影响

研究了氧化铬添加对超细WC-10%Co硬质合金组织和性能的影响,重点是添加量和高能球磨时间对WC晶粒度、合金组织和合金性能的影响,并分析了氧化铬抑制晶粒长大的机理。研究结果表明:球磨细化了WC晶粒,提升了合金性能,但过分球磨则会导致合金中缺陷增加和WC晶粒的异常长大;抑制剂Cr2O3有效地抑制了晶粒长大,合金中的WC晶粒度随抑制剂加入量的增加而细化,但过多的抑制剂会导致缺碳相和孔隙度的增加,降低了合金的强度。因此适当的球磨和合适的Cr2O3加入量将会在生产低孔隙度、高硬度、高抗弯强度的超细硬质合金中发挥作用。     

WC-Ni和WC-Fe硬质合金中WC晶粒的长大及长大抑制

研究了WC-10wt%Ni硬质合金中WC晶粒长大行为,以及加入(0~2)wt%的碳化物抑制剂(VC,Cr3C2,TaC,TiC和ZrC)对晶粒长大的抑制作用。合金总碳含量是Ni粘结剂合金中WC晶粒长大的一个关键因素,即使添加大量抑制剂也是如此。与低碳合金比较,高碳合金中WC晶粒粗化更明显,从而使得硬度大大降低。VC是WC-Ni硬质合金最有效的晶粒长大抑制剂,随后依次是TaC,Cr3C2,TiC和ZrC。硬度随抑制剂的含量增加而升高,但是有一个最大值,一旦超过此最大值,抑制剂增加,硬度却大约相同。WC-Fe-VC硬质合金实验结果表明,在WC-Fe硬质合金中,即使未加抑制剂,…     

VC/Cr_3C_2及配碳量对WC-0.5Co超细硬质合金组织与性能的影响

以超细WC粉末和超细WC-6Co复合粉末为原料,添加VC/Cr3C2作为晶粒长大抑制剂,同时进行配碳,采用高能球磨和气压强化烧结制备晶粒度小于0.5μm的WC-0.5Co超细硬质合金,研究了不同VC/Cr3C2添加量及配碳量对其组织与性能的影响。结果表明:VC/Cr3C2有效抑制了烧结过程中WC晶粒的长大,显著提高了WC-0.5Co超细硬质合金的硬度。当VC/Cr3C2添加量为0.73%(质量分数,下同)时,合金的硬度(HV0.05)最高,达到32 658 MPa;同时一定的配碳量有利于控制合金中的脱碳,提高合金性能,当配碳量为0.2%时,WC-0.5Co-0.73VC/Cr3C2合金的综合力学性能最好,断裂韧性为6.935 MPa·m1/2,维氏硬度(HV0.05)为32 216 MPa。     

以镍和铁为粘结相的硬质合金中WC晶粒长大及其抑制

研究了在WC—10wt％Ni合金中添加(0～2)wt％的作抑制剂的碳化物(VC．Cr3C2，TaC，TiC和ZrC)，FSSS粒度为0．6μm的WC粉末(SEM平均粒度为0．351xm)的WC晶粒长大及抑制其长大的情况：在Ni粘结相硬质合金中，即使在抑制剂的添加量加大的情况下，合金的总碳对于WC晶粒长大仍是一个极其重要的因素：与低碳牌号相比，高碳合金的晶粒长大是非常显著的，这导致了硬度明显地降低：迄今为止VC被证明是WC—Ni硬质合金中最有效的晶粒长大抑制荆，紧接其后是TaC，Cr3C2，TiC和ZrC。硬度随添加量的增加而增加，但是达到最大值后硬度保持不变：在WC-Fe-(VC)合金上的试验表明在以Fe作粘结相的合金中，即使不添加抑制剂，WC的晶粒长大也会受到极其明显的限制：粘结相的化学性质极大地影响了WC晶粒的连续和不连续长大：其化学性质是由粘结相基体(Fe，C0，Ni)的性质、合金的总碳(这一点决定了粘结相基体的成分)以及抑制剂的添加量所决定的．     

超细晶硬质合金中VC／Cr3C2对晶粒长大的抑制作用及机理研究

研究了超细晶硬质合金VC／Cr3C2抑制剂作用及抑制机理。研究发现复合添加VC／Cr3C2可以有效抑制WC—10Co合金烧结过程中晶粒的连续长大，合金平均晶粒尺寸为0．5μm，具有较高TRS（横向断裂强度TransverseRuptureStrength）和硬度。TEM和EDS分析发现抑制剂元素的主要存在方式是溶解在粘结相中且分布均匀，未发现抑制剂元素偏聚和第二相析出，说明抑制机理在于抑制剂元素溶入粘结相Co后，显著降低W，C在Co中的溶解度，使液相烧结阶段WC晶粒的溶解一析出过程受到阻碍，从而抑制液相烧结阶段的晶粒连续长大。     

VC/Cr_3C_2添加剂对超细硬质合金组织及性能的影响(英文)

研究了VC/Cr3C2添加剂对WC-12Co超细硬质合金的显微组织、硬度和抗弯强度(TRS)的影响.结果表明,舍一定比例VC/Cr3C2添加剂的合金具有更均匀的微观组织和优异的力学性能.当添加剂含量(质量分数)为0.5%VC/0.2%Cr3C2时,1430℃烧结制备的WC-12Co超细硬质合金的抗弯强度达3786 MPa,硬度达91.7 HRA.VC添加剂对WC晶粒的连续长大和非连续长大的抑制作用比Cr3C2添加剂更有效.此外,当烧结温度较高时,VC/Cr3C2添加剂对WC晶粒长大的抑制效果更显著.VC和Cr3C2添加剂抑制WC晶粒长大的作用机理为:VC和Cr3C2添加剂降低了WC相在粘结相中的过饱和度,从而降低烧结温度下粘结相中WC相溶解-析出过程的驱动力,起到阻碍WC晶粒长大的作用.     

添加VC与Cr_3C_2对超细晶硬质合金烧结过程的影响

系统研究晶粒长大抑制剂VC和Cr3C2对WC-8%Co超细晶硬质合金烧结过程中收缩率、相变温度和晶粒长大的影响。研究表明,WC-8%Co超细晶硬质合金的烧结收缩和致密化过程主要发生在固相烧结阶段,在液相出现前,合金的致密化程度已达到95%。晶粒长大抑制剂VC和Cr3C2的加入,显著降低了超细晶硬质合金烧结过程中液相出现的温度,且不同程度地阻碍了WC-8%Co超细晶硬质合金烧结过程中致密化的进程和速度。与未加入晶粒长大抑制剂的合金相比,其致密化的进程大约延迟80℃。     

超细硬质合金晶粒生长抑制剂VC、Cr_3C_2作用机理的研究

本文以液相复合-连续还原碳化方法制备的掺杂有VC和Cr3C2抑制剂的纳米复合WC-10Co粉末为原料,采用真空烧结+低压处理的工艺制备超细WC-10Co硬质合金,运用原子力显微镜(AFM)和场发射扫描电镜(FESEM)确定VC和Cr3C2抑制剂在硬质合金中的分布,讨论其抑制晶粒生长的机理。一部分VC、Cr3C2抑制剂吸附在WC晶粒表面形成30nm～50nm的沉淀物,降低WC晶粒的表面能;一部分VC、Cr3C2溶解在Co相中,降低WC在液相中的溶解度;其余VC、Cr3C2沉积在WC晶界,从而有效地抑制WC晶粒的长大。     

VC和Cr_3C_2抑制剂的应用和图解优化设计

本文主要介绍了VC和Cr3C2的添加量对超细硬质合金的晶粒长大抑制效果,绘制出了VC和Cr3C2的含量与合金的硬度和横向断裂强度之间的三维关系图,从此三维图中可以直观、方便地找到获得硬质合金优良性能的抑制剂优化成分范围。     

微量钴对无金属粘结相WC硬质合金烧结致密化与WC晶粒生长行为的影响

采用Cr3C2、VC掺杂超细WC为原料和无压真空烧结工艺,通过合金微观组织结构的观察与分析,研究了添加质量分数为0.3%的Co对无金属粘结相WC硬质合金烧结致密化与WC晶粒生长行为的影响。结果表明,微量Co的存在加速了WC的烧结致密化过程,与此同时也导致了WC晶粒明显的各向异性非连续晶粒长大。在上述研究基础上,提出了一种无金属粘结相WC硬质合金的低成本制备工艺,探讨了超细硬质合金中WC晶粒生长机制,提出了超细硬质合金的质量改进建议。     

Synthesis of Cr-doped APT in the evaporation and crystallization process and its effect on properties of WC-Co cemented carbide alloy

WC grain size has significant effect on WC-Co cemented carbide alloy properties. In order to inhibit WC grain growth during sintering process, grain growth-inhibitor Cr₃C₂ is usually added to tungsten carbide powder in advance through mechanical milling. While, homogeneous distribution of Cr₃C₂ in the tungsten carbide powder is difficult to achieve and result in abnormal growth of WC grains. For this purpose of growth-inhibitor uniform distribution, (CH₃COO)₃Cr is added into ammonium tungstate solution during evaporation and crystallization process to prepare Cr-doped APT powder, which can be used as precursor for ultrafine-grained WC-Co cemented carbide alloy preparation. Compared with conventional APT powder, the Cr-doped APT has smaller particle size and bulk density, moreover, chromium is evenly distributed within it. The Cr-doped APT is then used to produce Cr-doped tungsten powder, which also has smaller particle size than that of conventional tungsten powder. Cr-doped tungsten powder is subsequently prepared into tungsten carbide powder and WC-Co cemented carbide alloy through carbonization and sintering process, respectively. Compared with conventional WC-Co cemented carbide alloy, the obtained WC-Co cemented carbide alloy has smaller mean WC grain size (0.36 μm), and more uniform microstructure. Furthermore, the phenomenon of WC grain abnormal growth during sintering process is not observed, because the grain growth-inhibitor Cr₃C₂ is well dispersed in tungsten carbide and cobalt composite powder. Results show that the obtained WC-Co cemented carbide alloy presents better mechanical properties (HRA, bending strength, coercive force) than those of conventional WC-Co cemented carbide alloy. Accordingly, the novel addition of (CH₃COO)₃Cr during the evaporation and crystallization process is the key factor of ultrafine-grained WC-Co cemented carbide alloy production.     

工艺条件对WC-12%Co超细硬质合金性能的影响

采用不同粒度的WC粉,加入VC、Cr3C2做抑制剂,制备WC-12%Co超细硬质合金。采用D60-25型钴磁仪测量合金磁饱和,利用排水法测定合金密度,采用三点弯曲法在CMT4504拉伸机上检测合金的抗弯强度,试样抛光后在JEOL-6701F扫描电镜下观察合金的显微组织。研究了不同的WC粉末粒度、球磨时间、烧结工艺对WC-12%Co的超细硬质合金性能的影响。结果表明:过压烧结可明显提高合金抗弯强度、硬度和密度;随着球磨时间的增加,合金硬度不断上升,抗弯强度先增后减;采用0.55μm粒度WC粉制备的合金的硬度明显高于0.70μm粒度WC粉制备的合金。在本次实验中,选用0.55μm的WC粉末原料,混合料球磨85 h,通过过压烧结,可制备出性能优良的WC-12%Co超细硬质合金,硬度HV≥1 800,抗弯强度≥3 400 N/mm2。     

放电等离子烧结纳米硬质合金的研究

采用放电等离子烧结 (SPS)和普通真空烧结两种烧结工艺烧结 92WC - 8Co纳米硬质合金。放电等离子烧结 ,在 115 0℃的烧结温度、4.5kN压力下保温 5min ,烧结体就完全致密 ,其合金中的WC晶粒度小于 2 0 0nm ,硬度可达到 94.2HRA。真空烧结达到完全致密 ,烧结温度需 140 0℃ ,保温时间 30min ,WC晶粒度为 (30 0 40 0 )nm ,硬度最高为 93HRA。结果表明 :放电等离子烧结硬质合金的温度显著降低 ,烧结时间大大缩短 ,有效地抑制了WC晶粒的长大。SPS还显著降低微孔等缺陷 ,制品性能也大大提高。     

超细硬质合金WC-10Co-0.8(VC/Cr_3C_2)的烧结特征

超细硬质合金粉末粒度细小,具有高的比表面积和缺陷密度,因而具有较高的烧结活性,呈现出与普通硬质合金不同的烧结特征。因此,针对超细硬质合金特点制定合适的烧结工艺在生产超细硬质合金中是至关重要的。真空烧结超细硬质合金WC-10Co-0.8(VC/Cr3C2)的结果表明:1320℃烧结温度下的超细硬质合金,较1350℃和1380℃的密度和硬度低,WC晶粒细而孔隙度高。1350℃比1380℃具有更高的横向断裂强度(TRS)。WC-10Co-0.8(VC/Cr3C2)超细硬质合金的适宜烧结温度为1350℃。差热分析(DTA)对烧结过程中的热效应分析表明:出现液相温度为950℃,1300℃结束。同时氧化杂质被还原导致质量的损失和气体的产生。晶粒长大抑制剂VC和Cr3C2的加入,提高了氧化物杂质还原温度。     

Cr_3C_2对WC-6.5％Co硬质合金组织和性能的影响

通过向WC-6.5%Co硬质合金中添加0%～2.0%的晶粒长大抑制剂Cr_3C_2,研究了其对硬质合金组织和力学性能的影响。研究结果表明,Cr_3C_2的添加细化了WC晶粒,但不能完全抑制WC晶粒的异常长大。Cr_3C_2使合金的硬度提高,但是却降低了合金的致密度和抗弯强度。Cr_3C_2添加量为0.5%时,合金的综合性能最好。     

Effect of VC and NbC additions on microstructure and properties of ultrafine WC-10Co cemented carbides

The nanocomposite WC-Co powders were prepared through planetary ball milling method. Effects of grain growth inhibitor addition and the vacuum sintering parameters on the microstructure and properties of ultrafine WC-10Co cemented carbides were investigated using X-ray diffractometer, scanning electron microscope and mechanical property tester. The results show that VC and NbC additions can refine the WC grains, decrease the volume fraction of Co₃W₃C phase in ultrafine WC-10Co cemented carbides, and increase the hardness and fracture toughness of the base alloys. After sintering for 60 min at 1400 °C, the average grain size and hardness of ultrafine-grained WC-10Co-1VC cemented carbide are 470 nm and HRA 91.5, respectively. The fracture toughness of cemented carbide WC-10Co-1NbC alloy is over 7 MN·m^?3/2.