影响NBR/PVC共混硫化胶性能因素的研究

系统研究了影响丁腈橡胶/聚氯乙烯(NBR/PVC)共混胶性能的主要因素,包括PVC塑化温度、增塑剂用量、橡塑比、PVC的聚合度、NBR的丙烯腈质量分数。研究结果表明,塑化温度在160℃、增塑剂用量为20份、橡塑比为60/40~70/30时,NBR/PVC共混硫化胶综合性能较好。随着PVC聚合度的提高,NBR/PVC共混硫化胶力学性能得到提高;NBR中丙烯腈含量的增大有利于NBR/PVC共混硫化胶性能的提高。     

NBR／PVC共混发泡配方设计及制品性能

研究了ＮＢＲ／ＰＶＣ共混发泡的配方组成,确定了橡塑比,硫化体系,发泡剂,填料,增塑剂的最佳用量,分析了各配方组分对模压发泡制品性能的影响,并初步探讨了模压发泡制品的动态力学性能。     

NBR改性PVC性能的研究

主要研究了丁腈橡胶改性软质聚氯乙烯的性能,探讨了不同含量的ＮＢＲ和交联剂对共混物的力学性能,弹性性能,流动性能的影响,制得了既具有高弹性,又具有好的流动性的热塑性橡胶。     

NBR/PVC的浅色共混胶性能研究

在NBR/PVC为基体的浅色共混胶材料中加入白炭黑,探究改变作为补强剂的白炭黑用量对NBR/PVC浅色共混橡塑材料的硫化特性、力学性能和耐老化等性能的影响.结果表明:当白炭黑用量达到50 phr时,断裂伸长率为386％,硬度为70度,拉伸强度为13.3 MPa,耐寒性能良好,脆性温度为-48℃,耐油性符合GB/T 16...     

新型改性丁腈橡胶对PVC糊树脂力学性能的影响

通过试验配方设计、样条制备及性能检测,讨论了不同含量的改性粉末丁腈橡胶对PVC糊树脂力学性能的影响.结果表明,随着弹性体用量的增大,软质PVC材料的拉伸强度下降,断裂伸长率得到明显改善.新型改性粉末丁腈橡胶能够改善PVC糊树脂的性能.     

PVC糊料成型靴外底配方的改进

在ＰＶＣ糊状树脂中，添加１０～５０２份丙烯酸树脂，４～４５份粘度为１５～３０Ｐａ．ｓ的液状腈橡胶为主成分，使ＰＶＣ糊料成型靴外底的耐寒性显著提高，防滑优异，即使在－２０℃的低温下也可保持适宜的柔软性。     

PVC糊树脂对旋转模塑用PVC增塑糊性能的影响

通过ＰＶＣ糊树脂种类对旋转模塑用ＰＶＣ增塑类性能的影响进行较为深入的研究,从而为旋转模塑用ＰＶＣ增塑糊中糊树脂种类的确定提供了有益的参考。     

PVC/NBR热塑性弹性体加工流变性能研究

采用反应挤出动态硫化法制备了聚氯乙烯／丁腈橡胶(PVC／NBR)热塑性弹性体，用锥板流变仪、毛细管流变仪和转矩流变仪研究了动态硫化的PVC／NBR热塑性弹性体的流交性能和塑化性能。实验结果表明，动态硫化的PVC／NBR热塑性弹性体的熔体属于剪切稀化的假塑性流体，具有良好的返炼性能，综合性能超过国外同类产品。     

聚氯乙烯糊状树脂市场分析

介绍了聚氯乙烯糊树脂的发展及应用,以及聚氯糊状树脂的供求关系和主要市场分析。     

液体丁腈橡胶改性聚氯乙烯泡沫塑料的研制

研究采用液体丁腈橡胶（ＬＮＢＲ）改性聚氯乙烯制造ＰＶＣ泡沫塑料的过程,并考察了ＬＮＢＲ、增塑剂、填料、发泡剂用量和发泡时间等因素对ＰＶＣ泡沫性能的影响。     

纳米CaCO_3改性PVC糊及其软制品力学性能研究

研究了活性纳米碳酸钙(CaCO3)用量对PVC糊树脂的粘度及其软制品拉伸强度、伸长率等力学性能的影响。结果表明,随CaCO3加入量(0～30份)的增加,PVC糊树脂粘度明显提高;纳米碳酸钙加入量为15份时,PVC软制品的拉伸强度达到最高值;纳米碳酸钙加入量越大,伸长率越低,其中加入量为5～15份时,伸长率下降幅度较小,加入量大于15份时,伸长率大幅度降低。     

填充剂、热稳定剂及碳黑对PVC糊性能影响

考察了填充剂、热稳定剂及碳黑对PVC糊流变性能、存放性能及其力学性能的影响。结果表明,加入纳米TiO_2,PVC糊的粘度在剪切速率变化时,粘度变化很大,存放10d后粘度下降很少,仅下降0．3 Pa·s。玻璃微珠和滑石粉对PVC糊的硬度影响较为明显；添加硬脂酸钡,PVC糊存放10d后粘度仅下降0．4 Pa·s,存放性能较好；碳黑用量为0．5g时,PVC糊流动性能基本不变。     

聚氯乙烯糊树脂装置的国产化改造

介绍了对进口的聚氯乙烯糊树脂生产装置的国产化改造技术。通过采用半管换热技术、三层式喷嘴、可拆卸式轴封和中段平衡管改进了聚合釜,并对控制系统、干燥系统、研磨系统以及助剂进行改进。改造后的装置更有利于生产工艺的控制和设备的长期稳定运转。     

Blends of PVC and epoxidized liquid natural rubber: Studies on impact modification

Liquid natural rubber of different molecular masses L‐LNR, and H‐LNR were subjected to varying degree of epoxidation (L‐ELNR‐10, L‐ELNR‐20, L‐ELNR‐30, L‐ELNR‐40, L‐ELNR‐50, H‐LNR‐20, and H‐LNR‐50) and the products were incorporated into PVC at various compositions by the solution blending method. These blend systems were subjected to tensile testing, tensile impact measurements, and SEM studies. It was observed that blends with L‐ELNR‐20 showed highest impact strength modification, followed by L‐ELNR‐10 and L‐ELNR‐30. High impact properties showed by these blends are attributed to the optimum level of compatibility existing between the blend components. Tensile impact fracture studies revealed that the failure pattern for this blend system is intermediate between the brittle fracture of rigid PVC and ductile fracture of PVC/L‐ELNR‐50 samples. Blends up to 30 mol % of epoxidation showed partially compatible heterogeneous nature exhibiting domain morphology. Blends of liquid rubber with higher degree of epoxidation showed deterioration in tensile strength, modulus, yield strength, and tensile impact strength due to plasticization of PVC caused by the higher polar interaction between PVC chains and the oxirane rings. Effect of ELNR molecular weight was studied and it is found that the impact modification is higher for the L‐ELNR blends compared to the H‐ELNR blends. © 2008 Wiley Periodicals, Inc. J Appl Polym Sci, 2009     

石墨烯/二氧化钛对PVC薄膜性能影响

以石墨粉和三氯化钛为原料,通过Hummers和水解法制备得石墨烯/二氧化钛(G/TiO2),将G/TiO2作为填料添加到聚氯乙烯(PVC)中,探究其对PVC薄膜性能的影响.结果表明,添加G/TiO2提高了PVC薄膜的力学性能、抗静电性能和耐紫外老化性能.添加G/TiO2的PVC薄膜的拉伸强度由纯PVC薄膜的12.79 ...     

PVC糊树脂颗粒形态研究

用扫描电镜结合粒度分析方法,研究了微悬浮法和种子乳液法PVC糊树脂颗粒形态特征,并探讨了颗粒形态与增塑糊黏度之间的关系。     

竹粉/PVC发泡复合材料的制备与性能研究

采用模压法制备了竹粉/聚氯乙烯(PVC)发泡复合材料,研究了邻苯二甲酸二辛酯(DOP)、发泡剂偶氮二甲酰胺(AC)、竹粉、成核剂及成型压力对复合材料密度和力学性能的影响。结果表明:添加DOP使复合材料密度和拉伸强度下降,断裂伸长率快速增大;AC发泡剂用量增加,复合材料密度减小;竹粉用量增加,复合材料密度增加,力学性能变差;纳米二氧化钛和轻质碳酸钙的添加能有效改善复合材料的性能,其最佳用量为2份;复合材料最佳成型压力为6 MPa。