304奥氏体不锈钢低气压离子渗氮组织与性能研究

在400℃、低气压下对304奥氏体不锈钢进行低温低压离子渗氮处理。采用扫描电镜、显微硬度计及万能摩擦试验机对表面改性后的304奥氏体不锈钢渗层组织、硬度及耐磨性进行了测试和分析。结果表明:304奥氏体不锈钢低温低气压渗氮形成了明显的白亮层;低气压对304奥氏体不锈钢离子渗氮具有良好的催渗效果,即渗层厚度随气压的减小而增加,在100 Pa条件下,渗层厚度达到最大值51.7μm;渗氮后试样表面硬度达到最大值1100 HV0.01;低温低气压离子渗氮能够提高304奥氏体不锈钢耐磨性,80 Pa和100 Pa是提高304奥氏体不锈钢耐磨性的最佳气压。     

气压对304奥氏体不锈钢低温离子渗氮组织与性能影响

在400℃、8 h、不同气压(80~400 Pa)条件下对304奥氏体不锈钢进行离子渗氮处理。采用扫描电镜(SEM)、X射线衍射仪、显微硬度计及万能摩擦试验机对表面改性后的304奥氏体不锈钢渗层组织、相结构、渗层硬度以及耐磨性进行了测试和分析。结果表明,400℃离子渗氮处理后304奥氏体不锈钢形成了明显的白亮层,即单相S相层;低压对304奥氏体不锈钢离子氮化具有良好的催渗效果,即渗层厚度随气压的减小而增加,在100 Pa条件下,渗层厚度达到最大值51.7μm;渗氮后试样表面硬度达到最大值1100 HV0.01;低温低压离子渗氮能够提高304奥氏体不锈钢耐磨性,80 Pa和100 Pa是提高304奥氏体不锈钢耐磨性的最佳气压。     

离子氮铝共渗方法及对42CrMo钢组织性能的影响

目的 研发离子氮铝共渗试验方法,达到不影响42CrMo钢基体组织性能前提下,显著提高试样表面硬度和耐磨性效果。方法 采用电解法在42CrMo钢表面沉积氢氧化铝膜,再在520 ℃/4 h工艺下进行离子氮铝共渗处理,并在相同工艺参数条件与传统离子渗氮进行对比。用光学显微镜、维氏显微硬度计、摩擦磨损测试机、X射线衍射仪及SEM对截面显微组织、截面硬度、耐磨性及物相等进行了测试和分析。结果 获得了离子氮铝共渗试验方法,在520 ℃/4 h相同工艺参数下,离子氮铝共渗形成的化合物层和有效硬化层厚度比常规离子渗氮显著增加,其中,化合物层厚度由17.24 μm增加到52.13 μm,有效扩散层从175 μm增加到1 050 μm,相当于等离子处理效率提升6倍;同时,渗层形成了AlN及FexAl强化相,大幅度提高了渗层的硬度及耐磨性能。表面硬度由750HV0.025提高到1 250HV0.025,摩擦因数由常规离子渗氮0.52下降到0.29,磨损率由常规离子渗氮3.22×10^?5 g/(m.N)下降到1.21×10^?5 g/(m.N),磨痕明显减轻。结论 采用电解硝酸铝生成氢氧化铝沉淀附着在工件表面作为预处理,获得了离子氮铝共渗试验方法,与常规离子渗氮相比,离子氮铝共渗形成了多层次渗层结构,大幅度提高常规离子处理效率、表面硬度及耐磨性。     

渗氮温度对奥氏体不锈钢性能的影响

利用自行研制的直流脉冲离子渗氮设备对奥氏体不锈钢进行离子渗氮,采用显微硬度计、倒置金相显微镜等手段研究了渗氮温度对奥氏体不锈钢显微硬度、金相组织、耐磨性能和耐腐蚀性能的影响.结果表明,通过离子渗氮处理得到的渗层表面硬度均在1150 HV0.05以上,耐磨性能提高4～5倍,低温离子渗氮在提高耐磨性能的同时保持其耐腐蚀件能基本不变.     

温度对AISI304奥氏体不锈钢离子渗氮的影响

对AISI304奥氏体不锈钢进行脉冲电流辉光离子渗氮处理,在不同处理温度(480 ℃、520 ℃、580 ℃)下渗氮8 h后,获得了一定厚度的渗氮层.通过对渗层进行金相分析和硬度测试表明,随着渗氮温度升高,渗层厚度增大,显微硬度先增大后减小.综合温度对渗层厚度与显微硬度的影响,AISI304奥氏体不锈钢卡套辉光离子渗氮温度可采用520 ℃,渗氮后渗层厚度为90 μm,显微硬度为1317 HV0.1.     

42CrMo钢的钛催渗等离子渗氮工艺

研究了不同渗氮时间下钛元素对42CrMo钢常规离子渗氮工艺的作用效果,表征分析了不同渗氮工艺下试样表面的渗层组织及性能。结果表明,钛催渗离子渗氮试样的表面硬度和渗层深度均明显高于常规离子渗氮。在535℃×3 h的工艺条件下,钛催渗离子渗氮试样渗层的表面硬度达到887.4 HV0.2,渗氮层厚度约为400μm。钛元素的加入促进了氮元素的渗透和扩散,在试样表面生成高硬度化合物TiN。相较于相同保温时间下的常规离子渗氮,钛催渗离子渗氮试样表面硬度提高了60 HV0.2,渗层厚度增加了80μm,渗氮效率提升了约25%。与常规离子渗氮相比,钛催渗离子渗氮工艺具有显著优势,不仅有利于改善渗层组织性能,增强渗氮效果,还提高了渗氮效率,使渗氮周期明显缩短。     

微量钛对离子渗氮渗层特性及性能的影响

为调控离子渗氮渗层特性,获得少脆性化合物层、厚韧性扩散层的渗氮层,提高离子渗氮渗层抗冲击性和重载下的耐磨性,对 42CrMo 钢进行了添加微量钛的创新离子渗氮处理。 利用光学显微镜、SEM、XRD 和显微硬度计对渗层的截面显微组织、表面形貌和成分、物相和截面硬度进行了测试和分析。 结果表明:添加微量钛离子渗氮可显著改善渗层特性,获得少化合物层的高硬高韧渗氮层,同时显著提高离子渗氮效率。 在 540 ℃ ×4 h 工艺条件下,添加微量钛可使离子渗氮有效硬化层厚度显著增加,由常规离子渗氮的 225 μm 增加到 380 μm,即渗氮效率提高近 70%;有效硬化层厚度提高的情况下,化合物层厚度反而减薄,由常规离子渗氮的 19 μm 降低到 10 μm,即化合物层厚度降低了约 50%;渗层中化合物层与有效硬化层之比值由常规离子渗氮的 8. 5%降低到 2. 6%。 同时添加微量钛离子渗氮渗层中形成了高硬度强化相 TiN,使渗层表面硬度由 703 HV0. 05 提高至 895 HV0. 05 。 添加微量钛离子渗氮获得了薄化合物层、高硬高韧、厚有效硬化层的优良渗氮层特性,该渗层特性对改善离子渗氮零部件抗冲击性和重载下的耐磨性具有重要研究和应用价值。     

奥氏体不锈钢循环离子氮氧共渗工艺研究

对OCr18Ni9奥氏体不锈钢进行氮氧共渗循环离子渗氮试验,并和常规离子渗氮进行对比.利用光学显微镜、显微硬度计、XRD及磨损仪对渗氮层进行分析.结果表明,氮氧共渗循环离子渗氮比常规离子渗氮的渗氮速度快,渗层比常规离子渗氮厚;表面硬度为920 HV0.05(比常规离子渗氮高20 HV0.05),硬度梯度平缓;渗层中的ε相减少,γ'相增多;且渗层中的微量Fe3O4降低了表面摩擦系数,使工件经氮氧共渗循环离子渗氮后获得更高耐磨性.     

奥氏体不锈钢稀土催渗离子渗氮工艺研究

对304、316L奥氏体不锈钢采用不同氮一氢比的气氛,在不同温度和不同保温时间进行了离子渗氮和稀土催渗离子渗氮。结果表明,经580℃在氮一氢比为1：3的气氛中稀土催渗离子渗氮9h,304和316L钢的渗层深度分别为0．12mm和0．112mm,表面硬度达1000HV0．1左右,与常规离子渗氮工艺相比,渗氮时间缩短了1h。     

离子渗氮和固溶复合处理制备深层含氮奥氏体不锈钢

目的 通过离子渗氮和固溶复合处理制备深层含氮奥氏体不锈钢,获得硬度、耐蚀性和耐磨性等综合性能优良的奥氏体不锈钢。方法 将304奥氏体不锈钢试样放在LD-8CL型直流等离子体渗氮炉内,在400 Pa下进行560 ℃、4 h的离子渗氮处理,渗氮后进行1050 ℃、8 h的固溶处理。使用HXD-1000TMC型显微硬度计、DMI-3000M型金相显微镜、D/max-2500型X射线衍射仪（XRD）、Thermo250XI型X射线光电子能谱仪（XPS）、CS 350电化学测量系统和万能摩擦磨损试验机,对经过复合处理的304不锈钢的截面硬化梯度、截面组织、物相、表面成分、耐蚀性和耐磨性进行研究分析,验证此复合处理对获得硬度高、耐蚀性和耐磨性好等综合性能优良的奥氏体不锈钢的适用性。结果 经过复合处理,不锈钢表面的氮原子数分数为1.56 %,且为单一奥氏体相?N。?N所对应的衍射峰相对于不锈钢基体向左偏移,有效硬化层深达1.0 mm,不锈钢的表面硬度从基体的210HV0.025提高到308HV0.025。不但提高了深层含氮奥氏体不锈钢的耐磨性,而且提高了不锈钢的耐蚀性,腐蚀电位从基体的-0.534 V提高到-0.422 V,摩擦系数由基体的0.8降到0.7。结论 离子渗氮和固溶复合处理适用于制备综合性能优良的深层含氮奥氏体不锈钢。工艺设计时,可以根据材料服役要求,选择合适的固溶工艺,从而获得满足不同综合性能要求的含氮不锈钢。     

Effects of electrode contact condition on electrical dynamic resistance during resistance spot welding

This study systematically investigates the effects of electrical resistance at the workpiece/electrode interface or electrode face on temperature dependent dynamic resistance during resistance spot welding (RSW). To evaluate temperature transport equations of mass, momentum, energy, species and magnetic field intensity in workpieces, the energy and magnetic equations in the electrode are solved. Contact resistances composed of constriction and film resistances are functions of hardness, temperature, electrode force and surface conditions. The results show that dynamic resistance is complicated due to different variations of film and constriction resistances with temperature at not only the faying surface but also the electrode face in the early stage, i.e. shorter than around 3 cycles. Dynamic resistance in this stage is fortunately insignificant to transport processes. When the power is off, dynamic resistance depends on competition between decreased bulk resistance and increased constriction resistance at the electrode face. Decreased constriction resistance at the electrode face reduces dynamic resistance and temperature.     

Measurement of dynamic resistance in resistance spot welding

The conventional methods of determining the dynamic resistance were mostly done by measuring the voltage and current at secondary side of transformer in resistance welding machines, in which the measuring set-up normally interferes with the movement of electrode, and the measuring precision is influenced by inductive noise caused by the high welding current. In this study, the dynamic resistance is determined by measuring the voltage at primary side and current at secondary side. This increases the accuracy of measurement because of higher signal-noise ratio, and allows to apply to in-process system without any wires connected to electrodes.     

碳含量对Al0.5Co0.5NiCrFe高熵合金涂层组织与性能的影响

使用氩弧熔覆制备不同碳含量Al_0.5Co_0.5NiCrFe高熵合金涂层,研究碳含量对Al_0.5Co_0.5NiCrFe高熵合金涂层组织与性能的影响。结果表明:碳加入后,高熵合金均由单一的FCC结构组成,并没有表征出其他物质,但根据高熵合金显微组织与能谱分析可以发现,高熵合金的枝晶间有碳铬化合物生成。高熵合金涂层的组织为典型的树枝晶结构,随着碳含量的增加,组织不断细化。随碳含量的增加,高熵合金涂层的硬度不断升高,当碳含量为4%时,硬度(383.2 HV0.5)和耐磨性均为最佳。随碳含量的不断增加,高熵合金的耐腐蚀性先增强后减弱,碳含量为2%时耐腐蚀性最佳。根据单位面积氧化增量,高熵合金的抗氧化性先增大后减小,当碳含量为2%时,抗氧化性最佳。     

大电阻介质下的铝合金电阻点焊

在介绍大电阻介质材料的制备及其在铝合金点焊中的应用方法的基础上,以LF21防锈铝合金点焊为例,经金相试样分析及扫描电镜分析,对比研究了在不同的焊接电流下,应用介质材料与未应用介质材料时的熔核形貌、缺陷及组织.结果表明,未加入大电阻介质的点焊熔核均出现气孔和未熔合缺陷;而加入大电阻介质,形核效果良好,有个别小气孔但未出现影响焊点力学性能的未熔合缺陷.此外,加入大电阻介质降低了对焊件表面质量的要求,从而提高了铝合金点焊质量的稳定性;可降低焊接电流,导致较低的电极温度从而提高了电极寿命.     

合金元素对奥氏体球铁高温性能的影响

研究了合金元素对奥氏体球铁高温机械性能、抗氧化性和抗热冲击性能的影响，提出了合金元素的最佳含量。用该奥氏体耐热球铁替代原用耐热钢作渗碳、淬火炉用构件，使用寿命提高1.2～1．6倍，成本降低20％。     

硼对堆焊合金组织与性能的影响

研究了不同含硼量时堆焊合金的组织与性能。结果表明，随着含硼量的增加，堆焊层的硬度与耐磨性不断提高，堆焊层的组织状态也发生转化，逐渐由亚共析态转变为过共析态、共晶态乃至过共晶态，其中共晶组织或接近共晶态的组织抗冲击性能最好．而接近共晶成分的过共晶组织硬度与耐磨性最高。     

硼砂浴内金属材料耐蚀性及抗氧化性的研究

通过对多种耐热不锈钢进行硼砂浴腐蚀及抗氧化试验,研究了各种耐热不锈钢在硼砂浴中的耐腐蚀性及高温抗氧化性。研究结果表明,材料中元素的种类及含量对硼砂浴炉用金属材料的使用寿命有较大影响,其中Ni、Cr元素对材料的耐蚀性及抗氧化性起着决定性作用。材料中Cr含量在20%左右及Ni含量在35%左右时得到最佳的耐蚀性。Cr含量与Ni含量之和不小于45%的材料的高温抗氧化性符合硼砂浴的使用要求。耐热不锈钢的腐蚀主要集中在硼砂浴与空气的交界面处,其他位置腐蚀较弱。硼砂浴中Na2O和B2O3的存在加速了耐热不锈钢的腐蚀。这些研究结果为硼砂浴用坩埚及工夹具的选材提供了依据。     

钢铁渗铝及渗铝钢的性能

铝原子向钢中的渗透,完全遵守Ｆｉｃｋ扩散定律;同时探讨了渗铝层耐氧化、耐腐蚀、耐磨损的机理。     

Fabrication of the Coatings for the High-temperature Oxidation Resistance on Hydrogen Resistance Steel

Alumina coating is used to improve the performance of high-temperature oxidation resistance,which can be fabricated on the surface of hydrogen resistance steel by two methods,thermal oxidation of arc ion plated Al coating and reactive magnetron sputtering.Elemental composition,structures and surface morphologies of the coating were analyzed and compared in this paper.The surface of the coatings,which was made by the first method,was composed of α-Al2O3 phase and internal was Fe-Al alloy phase.The Alumina coatings made by the second method were amorphous.In addition,appearances of Alumina coatings fabricated by these two methods were quit different,which were grey and transparent respectively.Both of the two kinds of coatings meet to the needs of high-temperature oxidation resistance.     

轧辊堆焊金属的耐热疲劳性能

通过设计的热疲劳试验方法,对三种自制药芯焊丝和一种国产堆焊轧辊用实心焊丝的耐热疲劳性能及其影响因素进行了深入研究,同时对堆焊金属中热疲劳裂纹形成以及扩展机理做了进一步探讨,研究表明,堆焊金属中热疲劳裂纹的形成以及扩展是循环应力和氧化气氛共同作用的结果,堆焊金属的抗氧化性越高,抗启裂能力越强,在此基础上,得出了热疲劳裂纹形成以及扩展的机理模型图,另外,研究结果还表明,堆焊金属的组织以及组织中存在的夹杂物对耐热疲劳性能也有很大影响,均一的组织有利于提高其耐热疲劳性能,而夹杂物则促使热疲劳裂纹形成、扩展、分叉。