油气田集输管道压接工艺技术研究

针对油气田集输管道中特别是内涂层管道的连接补口问题,成功开发了D159mm×8mm内涂层无缝钢管压接技术,既保证接头与钢管等强,又保证了内涂层的连续性,管道连接后不需要内补口和无损探伤,可满足油气田集输管道工作要求。文章介绍了D159mm×8mm内涂层无缝钢管压接接头型式、压接接头性能试验及分析。     

小口径钢管道内涂层挤涂工艺技术及设备

在高含水油田，用于油气集输及污水回注的钢质管道受到日益严重的内腐蚀，胜利油田油建一公司研究开发的D48～180mm钢管道内涂层挤涂工艺技术及设备，满足钢管道内壁除锈及内防腐涂层的质量要求，较好地解决了内涂层上薄下厚和弯头、不易挤涂的难题。本文介绍挤涂工艺流程、挤涂器、设备技术参数、特点及应用效果。     

油气集输管道内涂层金属腐蚀失效机理研究

为防止集输管道内壁腐蚀并提高输送效率,常常使用内涂层。但由于涂层缺陷的存在,在腐蚀介质的作用下管道内涂层会逐渐失效剥落,使金属大面积腐蚀。为此,对内涂层的失效机理和涂层下金属的反应过程进行了探讨,并找出两者之间的内在联系。     

内防腐涂层管道接头的连接与防护

有机涂层、无机涂层和聚合物内衬等在石油管道内防腐方面得到广泛应用,但由于现场施焊时的高温作用,会使焊缝两侧附近的防护涂层烧焦或脱落,从而失去对管道的保护作用。针对这一情况,综述了国内外对内防腐涂层管道的主要连接方式和管口连接处的保护措施,如:自动补口机法、机械连接法、内衬保护套(管)焊接法、记忆合金套法、不锈钢接头法、无内补口技术等,并简要介绍了各种方法的优缺点。     

内防腐管道的外套式机械压接组对及补口

输油管道在敷设施工中多采用焊接方法组对联头，针对因焊接烧损防腐内涂层造成的管道补口难题，提出采用外套式机械压接法代替传统的焊接方法，并介绍外套式机械压接接头型式，分析接头的应力状态及整体抗力。应变测试结果与现场埋地应用试验均表明，该联头方式具有施工速度快、机械化程度高、不损坏防腐内涂层、不需进行管道补口、适用范围宽等优点，且成本略低于焊接的方法。     

镍-磷合金镀管道采用不锈钢接头技术

聚合物溶液与铁离子接触会发生化学降解，导致粘度损失，影响驱油效果。采用镍一磷合金镀管道可避免聚合物母液输送时的化学降解。介绍了采用不锈钢接头技术替代内补口的试验研究结果，并通过强度、硬度试验和金相组织分析等科学地确定了不锈钢接头的经济长度。     

内涂层管子的经济效果

输气技术发展方向之一是提高输气效率，改善输气经济效益。由于内涂层管子具有很多优点，50多年来它在天然气输送管道中得到了广泛应用。文章论述了输气管道采用内涂层管子的经济效益。     

国外天然气管道内涂层评价技术研究进展

对新建、已建管道的内涂层材料,服役运行后的内涂层的完整性、安全性、可靠性进行评估具有重要意义。文章总结了国外近年来开展的天然气管道增输联合工业项目JIP(Joint Industry Project)研究的最新部分成果,包括JIP目标、流体与涂层材料的交互作用、流量提高、直径355.6 mm管道内涂层表面结构调整等,并提出了相应的建议。     

埋地钢质管道煤焦油瓷漆外覆盖层涂装工艺

本文介绍了煤焦油瓷漆的性能及管道外防腐作业线的工艺流程，包括上管、传动、抛丸除锈、涂底漆、瓷漆加热、瓷漆浇涂、水冷定型等工艺。经89km新疆轮库复线工程D508mm钢管煤焦油瓷漆防腐涂装实际应用证明，该作业线运转正常，操作简便，各项指标均达到了设计要求。     

Influence of ilmenite ore particles as pigment on the anticorrosion and mechanical performance properties of polyamine cured epoxy for internal coating of gas transmission pipelines

In the present work, Different high build epoxy coating formulations cured by polyamine hardener were modified by incorporation various concentrations (50, 75 and 100%) of processed micro-sized ilmenite ore (FeTiO₃) as pigment to replace all inorganic solids content to form a highly cross linked ilmenite epoxy adduct in three dimensional network. X-ray diffraction (XRD) analysis was implemented to assure the phase identification of the crystalline ilmenite particles. Dielectric light scattering measurements were accomplished to measure the particle size distribution of micro-sized ilmenite particles. The lamellar shape of the prepared ilmenite pigment particles (FeTiO₃) was illustrated by transmission electron microscopy (TEM) investigation. Flaky-like nature and the arrangement in overlapping plates of ilmenite particles were confirmed by scanning electron microscopy (SEM) technique. The anticorrosion behavior of the considered ilmenite epoxy coating formulations against unmodified blank coating were studied by accelerated corrosion experiment (salt spray chamber) after 500 h exposure in 5% NaCl solution. To confirm the previous concept, the electrochemical behavior of cured ilmenite epoxy coated steel films against unmodified epoxy in oil-wells formation water has been studied by electrochemical impedance spectroscopy (EIS) investigation. The mechanical performance properties for these films were investigated via adhesion pull-off, bend and impact coating tests to confirm their application efficiency. From the recorded results it was found that, the inhibition effect of various coating formulations was attributed to the flaky-like character of dispersed ilmenite particles which aligned parallel to the steel surface through the epoxy base matrix producing a shield of overlapping plates. This alignment enhanced protection by providing a protective barrier, increasing the film reinforcement and enhancing the inter-coat adhesion.     

JP-66型小直径射流泵特性试验研究

JP－66型小直径径射流泵体最大外径仅为φ66mm，为检验其工作性能而进行了室内试验。依据试验结果分析了该型流泵的特性，适用范围，存在的主要问题及改进方向，并定性指出JP－66型小直径径射流泵最佳喷嘴－喉管距L约等于喉管直径D。     

管道外防腐层补口技术国家标准与国际标准对比分析

从管道补口防腐层的分类、补口材料、补口防腐层的施工以及补口防腐层的性能指标,对比分析了GB/T 51241-2017和ISO 21809-3:2016关于管道外防腐层补口技术的规定。相比GB/T 51241-2017,ISO 21809-3:2016针对补口类型分类更详细;对于热收缩材料补口防腐层,ISO 21809-3:2016中设计温度规定更细致,GB/T 51241-2017对热收缩材料厚度的规定更为具体,并且还规定了原材料的性能要求;两个标准对热收缩材料补口防腐层的表面预处理要求以及施工工艺规程基本相同;在施工环境和热缩材料在管体防腐层的搭接量的规定上,GB/T 51241-2017更为严格。对于热收缩材料补口防腐层的性能指标方面,ISO 21809-3:2016增加了压痕抗力、搭接剪切强度等性能指标,两个标准对热收缩材料补口防腐层耐阴极剥离性能要求基本一致。     

聚四氟乙烯膨胀节内压爆破试验研究

推导了聚四氟乙烯波纹管和不锈钢加强圈的爆破应力与爆破压力算式,经算式计算和试件试验都表明,聚四氟乙烯波纹管的爆破系经向薄膜应力所致。阐述了爆破压力影响因素与提高爆破压力的方法     

小通径环形封井器的研制与应用

针对现有抽油杆防喷器不能满足油井带压作业的问题,研制了一种安全性和可靠性较高的小通径环形封井器。该封井器主要由壳体、球形胶心、活塞、活塞压盖和上压盖等组成,它结构简单,更换胶心方便,液压控制,操作简单便捷;胶心外表为球面,受力均匀,动静密封压力高,可密封不同直径的抽油杆杆柱。试验及应用表明,该封井器能满足现场带压起下抽油杆的要求,性能可靠,可操作性强,性能指标达到了设计要求。     

煤焦油瓷漆防腐层的施工及设备

煤焦油瓷漆具有优良的物理化学性能和稳定的防腐性能，而且原料来源广，价格低廉，近生来又开始在我国管道防腐中应用。中油管道二公司研制成功长输管道煤焦油瓷漆防腐作业线。本文介绍了煤焦油瓷漆防腐层的技术指标、施工工艺及作业线主要装置的结构特点。     

非坍塌型小通径套损井段整形扩径技术

通径ф90mm以下的套损井段的整形、扩径，一直是油田套损井大修工作中的难题。针对杏北油田套损日益严重的局面，设计了5种组合钻具，应用该项技术对11口小通径套损进行整形扩径，成功9口井，成功率达81.8%，在小通径套损井段的整形扩径中取得了良好效果，为套损井的修复提供了有效手段。     

烷基苯磺酸钠储罐内防腐蚀涂层失效原因分析

针对大庆油田工程有限公司三元配注站烷基苯磺酸钠储罐内防腐蚀涂层脱落的问题,开展了现场调查、测试与室内分析试验.现场调查发现,储罐中下部和搅拌器叶轮相对位置的内防腐蚀涂层大面积连续脱落,并有明显的分界线,说明涂层脱落与搅拌时产生的剪切力有关;涂层失效部位附着力较低,说明涂层附着力受到介质的破坏作用;室内试验分析发现,失效涂层多有微孔、微裂纹等缺陷,同时,烷基苯磺酸钠溶液表面能较低,说明烷基苯磺酸钠溶液容易渗入涂层,并造成涂层和金属基体之间附着力降低.经综合分析后认为,烷基苯磺酸钠对涂层有较强的浸润作用,可渗入到涂层与金属基体之间后,降低它们之间的附着力,受到搅拌器产生的剪切力作用后造成涂层脱落.