Sliding wear characteristics of plasma-sprayed Al2O3 and Cr2O3 coatings against copper alloy under severe conditions

Al₂O₃ and Cr₂O₃ coatings were deposited by atmospheric plasma spraying and their tribological properties dry sliding against copper alloy were evaluated using a block-on-ring configuration at room temperature. It was found that the wear resistance of Al₂O₃ coating was superior to that of the Cr₂O₃ coating under the conditions used in the present study. This mainly attributed to its better thermal conductivity of Al₂O₃ coating, which was considered to effectively facilitate the dissipation of tribological heat and alleviate the reduction of hardness due to the accumulated tribological heat. As for the Al₂O₃ coating, the wear mechanism was plastic deformation along with some micro-abrasion and fatigue-induced brittle fracture, while the failure of Cr₂O₃ coating was predominantly the crack propagation-induced detachment of transferred films and splats spallation.     

Influence of Al2O3 reinforcement on the abrasive wear characteristic of Al2O3/PA1010 composite coatings

In the present study, the abrasive wear characteristics of Al₂O₃/PA1010 composite coatings were tested on the turnplate abrasive wear testing machine. Steel 45 (quenched and low-temperature tempered) was used as a reference material. The experimental results showed that when the Al₂O₃ particles have been treated with a silane coupling agent (γ-aminopropyl-triethoxysilane), the abrasive wear resistance of Al₂O₃/PA1010 composite coatings has a good linear relationship with the volume fraction of Al₂O₃ particles in Al₂O₃/PA1010 composite coatings and the linear correlation coefficient is 0.979. Under the experimental conditions, the size of Al₂O₃ particles (40.5-161.0 μm) has little influence on the abrasive wear resistance of Al₂O₃/PA1010 composite coatings. By treating the surface of Al₂O₃ particles with the silane coupling agent, the distribution of Al₂O₃ particles in PA1010 matrix is more homogeneous and the bonding state between Al₂O₃ particles and PA1010 matrix is better. Therefore, the Al₂O₃ particles make the Al₂O₃/PA1010 composite coatings have better abrasive wear resistance than PA1010 coating. The wear resistance of Al₂O₃/PA1010 composite coatings is about 45% compared with that of steel 45.     

Comparison of wear behaviour of plasma-sprayed Al2O3 coatings with and without laser treatment

This paper studies experimentally the effects of CO₂ laser-treatment on the wear behaviour of plasma-sprayed Al₂O₃ coatings, in linear contact sliding (dry, abrasive and lubricated) against SAE 4620 steel. Tests were carried out using a block-on-ring friction and wear tester, under different loads at different speeds. The wear mechanism and the changes in adherence, porosity and microstructure by laser treatment were also investigated. Results show a better wear behaviour for both laser-treated ceramic coating and its paired steel under dry and abrasive conditions, compared with the case without laser treatment. The lubricated wear behaviour of the laser-treated ceramic coating, however, is not improved. The changes in microhardness, porosity and adherence caused by the laser treatment are responsible for the change in wear behaviour of the ceramic coating.     

Effect of lubricants on the friction and wear of Al2O3 against gray cast iron

The tribological behavior of ceramic Al₂O₃ coupled with gray cast iron (PHT) with different lubricants was investigated using a ring-on-block wear tester. In the wear test, air, distilled water, emulsion and oil were used as lubricants respectively in order to check the lubricating effectiveness of lubricants and the friction mechanism of solid graphite in the cast iron. Wear testing of 0.8% C steel (T8) sliding with Al₂O₃ was also carried out to compare with the test using gray cast iron. From these data the tribological behavior of graphite in the iron can be evaluated. The results show that the friction and wear of tested couples are decreased using different lubricants in the following order: air, distilled water, emulsion and oil. When lubricating with air and water, graphite in the iron as solid lubricant can decrease the friction and wear of the couples. However, when lubricating with emulsion and oil, graphite does not show the advantage of decreasing friction and wear.     

Effects of a second phase on the tribological properties of Al2O3 and ZrO2 ceramics

The tribological properties of four different materials are investigated, tetragonal zirconia (Y-ZTP), Al₂O₃ dispersed in Y-TZP (ADZ), ZrO₂ dispersed in Al₂O₃ (ZTA) and Al₂O₃ (with 300 ppm MgO). These materials are used as a cylinder sliding against a plate of Y-TZP (TZ-3Y)). Compared to Y-TZP, the wear resistance of ADZ composites is increased by a factor of 4–10. At a contact pressure of 230 MPa, a wear transition for Y-TZP is observed from plastic deformation to microchipping and microfracture due to the high interfacial temperature (450°C–550°C) generated by frictional heating. Because of the higher elastic modulus, hardness and fracture toughness at high temperature, ADZ composites show better wear resistance and a higher transition contact pressure (over 400 MPa) under the present conditions. For Al₂O₃, the transition from mild to severe wear occurs when the contact pressure is changed from 250 to 400 MPa. For ZTA ceramics, the wear behaviour does not change because of the presence of a compressive layer due to the zirconia phase transformation during sliding.

In water the wear resistance for ADZ and ZY5 is almost two orders of magnitude higher than the results under dry conditions. Reduction of the interfacial temperature by using water and the formation of a hydroxide layer at the contact surface by the tribochemical reaction of water with the ceramic, as observed by XPS, gives a positive effect on wear resistance.     

High-temperature tribological properties of spark-plasma-sintered Al2O3 composites containing barite-type structure sulfates

Al₂O₃–50BaSO₄–20Ag, Al₂O₃–50BaSO₄–10SiO₂, Al₂O₃–50(mass%)SrSO₄, Al₂O₃–50PbSO₄–5SiO₂, Al₂O₃–50BaSO₄ and Al₂O₃–50BaCrO₄ composites (mass%) were prepared by spark plasma sintering and their microstructure and high-temperature tribological properties were evaluated. Al₂O₃–50BaSO₄–20Ag composites (mass%) showed the lowest friction coefficients at the temperature ranging from 473 to 1073 K. Thin Ag film was observed on the wear tracks of the composites above 473 K. In addition, the friction coefficients of Al₂O₃ composites containing SrSO₄ and PbSO₄ were as low as those of Al₂O₃–BaSO₄ and Al₂O₃–BaCrO₄ composites at the temperatures up to 1073 K. The thin films formed on the wear tracks of the Al₂O₃–SrSO₄ composites were composed of Al₂O₃ and SrSO₄ phases, while the films formed on the wear tracks of the Al₂O₃–PbSO₄–SiO₂ composites consisted of Al₂O₃, PbSO₄ and SiO₂ phases.     

Tribological behavior of select MAX phases against Al2O3 at elevated temperatures

The layered M_n+1AC_n ternary carbides – MAX phases – Ta₂AlC, Ti₂AlC, Cr₂AlC and Ti₃SiC₂ were tested under dry sliding conditions against alumina at 550 °C and 3 N load (for a stress of ≈0.08 MPa) using a pin-on-disk tribometer. Ta₂AlC and Ti₂AlC exhibited low specific wear rates, SWRs, (≤1 × 10⁻⁶ mm³/N m), while the coefficients of friction, μ, were 0.9 and 0.6, respectively. At 0.4, μ of Ti₃SiC₂ was the lowest measured, but the SWR, at ≈2 × 10⁻⁴ mm³/N m, was high. With a μ of 0.44 and a SWR of 6 × 10⁻⁵ mm³/N m the Cr₂AlC sample was in between. No visible wear of Al₂O₃ counterparts was observed in all the tribocouples. Tribofilms, which were mainly comprised of X-ray amorphous oxides of the M and A elements and, in some cases, unoxidized grains of the corresponding MAX phases, were formed on the contact surfaces. The correlations between observed tribological properties and tribofilm characteristics are discussed.     

Effects of anti-wear additives on friction and wear properties of Cr2O3 coating

The effects of some anti-wear additives on the friction and wear behaviour of plasma-sprayed Cr₂O₃ coating were investigated using a block-on-ring tester at ambient conditions. The results show that zinc dialkyldithiophosphate (ZDDP), tricesyl phosphate (TCP) and tributyl phosphate (TBP) significantly reduce the wear of Cr₂O₃ coating lubricated by paraffin oil. Additive concentrations as well as sliding time have great influence on the wear. The friction coefficient varies slightly with test conditions. The analysis by XPS of worn surfaces indicates that the wear resistance of these additives is due to the formation of tribochemical reaction films by reacting with Cr₂O₃ coatings.     

不同润滑条件下氧化铝陶瓷衬板的磨损机制

在干摩擦、水润滑、油润滑3种不同润滑条件下对氧化铝陶瓷进行摩擦磨损试验。利用SEM对磨损后的磨痕进行观察并进行显微组织结构分析,探讨不同介质下氧化铝陶瓷的磨损机制。结果表明:氧化铝陶瓷材料干摩擦条件下的磨损机制为大量的脆性剥落和大量的磨粒磨损,在水润滑条件下为较少的脆性剥落和轻微的磨粒磨损,在油润滑条件下为很少的脆性剥落和极微的磨粒磨损;液体润滑剂可使氧化铝陶瓷材料的磨损量大幅度降低,其中油润滑条件的减磨效果最为突出。     

Friction and wear properties of UHMWPE/Al2O3 ceramic under different lubricating conditions

Friction and wear behavior of ultra-high molecular weight polyethylene (UHMWPE) sliding against Al₂O₃ ceramic under dry sliding, and lubrication of fresh plasma, distilled water and physiological saline were investigated with a self-made pin-on-disk apparatus at 37±1°C. The worn surfaces were examined with a scanning electron microscope (SEM). The results show that the friction behavior of UHMWPE is very sensitive to its water absorption state. The wear rate of UHMWPE under dry sliding is the highest and under plasma lubrication is the lowest. The wear mechanisms are different under dry friction and various lubricating conditions.     

The effect of Al2O3 on the friction performance of automotive brake friction materials

This study consists of two stages. In the first stage, bronze-based break linings were produced and friction-wear properties of them were investigated. In the second stage, 0.5%, 1%, 2% and 4% alumina (Al₂O₃) powders were added to the bronze-based powders and Al₂O₃ reinforced bronze-based break linings were produced. Friction–wear properties of the Al₂O₃ reinforced samples were aslo investigated and compared to those of plain bronze-based ones. For this purpose, friction coefficient and wear behaviour of the samples were tested on the grey cast iron disc. The hardness and density of the samples were also determined. Microstructures of the samples before and after the sintering and the worn surfaces of the wear specimens were examined using a scanning electron microscope (SEM). The sample compacted at 350 MPa and sintered at 820 °C exhibited the optimum friction–wear behaviour. With increase in friction surface temperature, a reduction in the friction coefficient of the samples was observed. The lowest reduction in the friction coefficient with increasing temperature was for the 2% and 4% Al₂O₃ reinforced samples. The SEM images of the sample indicated that increase in Al₂O₃ content resulted in adhesive wear. With increase in Al₂O₃ content, a reduction in mass loss of the samples was also observed. Overall, the samples reinforced with 2% and 4% Al₂O₃ exhibited the best results.     

Friction and wear behaviour of Thordon XL and LgSn80 in sliding against plasma-sprayed Cr2O3 coatings

This paper studies the friction and wear behaviour of two important bearing materials, Thordon XL and LgSn80, in dry and lubricated sliding vs. plasma-sprayed Cr₂O₃ coatings. As a reference, AISI 1043 steel is also studied under the same conditions. SEM, EDS and surface topography were employed to study the wear mechanisms. The results indicate that the Thordon XL/Cr₂O₃ coating pair gives the lowest dry friction coefficient (0.16) under a normal load of 45.3 N (pressure 0.453 MPa) at a velocity of 1 m/s. The dry friction coefficient of Thordon XL/Cr₂O₃ coating increases to 0.38 under a normal load of 88.5 N (pressure 0.885 MPa). The dry friction coefficients of the LgSn80/Cr₂O₃ coating are in the range of 0.31–0.46. Secondly, both dry wear rate under low normal load (45.3 N) and lubricated wear rate under a load of 680 N for Thordon XL are lower than those of LgSn80 in sliding against plasma-sprayed Cr₂O₃ coatings at a speed of 1 m/s. However, under a normal load of 88.5 N the dry wear rate of Thordon XL is much higher than that of LgSn80. Thirdly, a high viscosity lubricant (SAE 140) leads to lower wear for Thordon XL and LgSn80 than a low viscosity lubricant (SAE 30). Finally, the dominating wear mechanism for Thordon XL is shear fracture when against the plasma-sprayed Cr₂O₃ ceramic coating. For LgSn80 against plasma-sprayed Cr₂O₃ ceramic coating, abrasive wear is the governing failure mechanism.     

A study on friction and wear characteristics of nanometer Al2O3 /PEEK composites under the dry sliding condition

The friction and wear properties of the polyetheretherketone (PEEK) based composites filled with 5 mass% nanometer or micron Al₂O₃ with or without 10 mass% polytetrafluroethylene (PTFE) against the medium carbon steel (AISI 1045 steel) ring under the dry sliding condition at Amsler wear tester were examined. A constant sliding velocity of 0.42 m s⁻¹ and a load of 196 N were used in all experiments. The average diameter 250 μm PEEK powders, the 15 or 90 nm Al₂O₃ nano-particles or 500 nm Al₂O₃ particles and/or the PTFE fine powders of diameter 50 μm were mechanically mixed in alcohol, and then the block composite specimens were prepared by the heat compression moulding. The homogeneously dispersion of the Al₂O₃ nano-particles in PEEK matrix of the prepared composites was analyzed by the atomic force microscopy (AFM). The wear testing results showed that nanometer and micron Al₂O₃ reduced the wear coefficient of PEEK composites without PTFE effectively, but not reduced the friction coefficient. The filling of 10 mass% PTFE into pure PEEK resulted in a decrease of the friction coefficient and the wear coefficient of the filled composite simultaneously. However, when 10 mass% PTFE was filled into Al₂O₃/ PEEK composites, the friction coefficient was decreased and the wear coefficient increased. The worn scars on the tested composite specimen surfaces and steel ring surfaces were observed by scanning electron microscopy (SEM). A thin, uniform, and tenacious transferred film on the surface of the steel rings against the PEEK composites filled with 5 mass% 15 nm Al₂O₃ particles but without PTFE was formed. The components of the transferred films were detected by energy dispersive spectrometry (EDS). The results indicated that the nanometer Al₂O₃ as the filler, together with PEEK matrix, transferred to the counterpart ring surface during the sliding friction and wear. Therefore, the ability of Al₂O₃ to improve the wear resistant behaviors is closely related to the ability to improve the characteristics of the transfer film.     

Friction and wear behaviour of plasma-sprayed Cr2O3 coatings against steel in a wide range of sliding velocities and normal loads

This study investigates the influence of sliding speed and normal load on the friction and wear of plasma-sprayed Cr₂O₃ coatings, in dry and lubricated sliding against AISI D2 steel. Friction and wear tests were performed in a wide speed range of 0.125–8 m/s under different normal loads using a block-on-ring tribometer. SEM, EDS and XPS were employed to identify the mechanical and chemical changes on the worn surfaces. A tangential impact wear model was proposed to explain the steep rising of wear from the minimum wear to the maximum wear. The results show that the wear of Cr₂O₃ coatings increases with increasing load. Secondly, there exist a minimum-wear sliding speed (0.5 m/s) and a maximum-wear sliding speed (3 m/s) for a Cr₂O₃ coating in dry sliding. With the increase of speed, the wear of a Cr₂O₃ coating decreases in the range 0.125–0.5 m/s, then rises steeply from 0.5 m/s to 3 m/s, followed by a decrease thereafter. The large variation of wear with respect to speed can be explained by stick-slip at low speeds, the tangential impact effect at median speeds and the softening effect of flash temperature at high speeds. Thirdly, the chemical compositions of the transfer film are a-Fe₂O₃ in the speed range 0.25–2 m/s, and FeO at 7 m/s. In addition, the wear mechanisms of a Cr₂O₃ coating in dry sliding versus AISI D2 steel are adhesion at low speeds, brittle fracture at median speeds and a mixture of abrasion and brittle fracture at high speeds. Finally the lubricated wear of Cr₂O₃ coating increases sharply from 1 to 2.8 m/s.     

Friction and wear of MgO single crystals on sintered Al2O3 in vacuum

Experiments were carried out on the wear of MgO single crystals on sintered Al₂O₃ using a pin-on-disk type machine in a vacuum chamber. Minimum values of friction and wear with a smooth wear surface were found in the range 10^?2–10⁰ Torr; these were shifted to higher values and/or to poor vacuum with increasing sliding velocities. High wear rates in a high vacuum were due to repeated micro brittle fractures because of adhering wear fragments. Low wear rates in a poorer vacuum were caused by the tearing off of the laminated surface film by plastic flow.     

The friction and wear properties of nanometre SiO2 filled polyetheretherketone

Nanometre SiO₂ filled-polyetheretherketone (PEEK) composite blocks with different filler proportions were prepared by compression moulding. Their friction and wear properties were investigated on a block-on-ring machine by running a plain carbon steel (AISI 1045 steel) ring against the composite block. The morphologies of the wear traces and the transfer film were observed by scanning electron microscopy (SEM). It was found that nanometre SiO₂ filled-PEEK exhibited considerably lower friction coefficient and wear rate in comparison with pure PEEK. The lowest wear rate was obtained with the composite containing 7.5 wt.% SiO₂. The SEM pictures of the wear traces indicated that with the frictional couple of carbon steel ring/composite block (fillec with 7.5 wt.% filler), a thin, uniform, and tenacious transfer film was formed on the ring surface. It was inferred that the transfer film contributed largely to the decreased friction coefficient and wear rate of the filled PEEK composites.     

Dry sliding wear mechanism for P/M austenitic stainless steels and their composites containing Al2O3 and Y2O3 particles

Austenitic stainless steels are used in applications demanding general corrosion resistance at room or moderate operating temperatures. However, their use is often limited by the relative softness of these materials and their suceptibility to wear and galling. The present investigation deals with the dry sliding wear behaviour of two P/M austenitic stainless steels (AISI 304L and 316L) and their composites containing two different ceramic particles (Al₂O₃ and Y₂O₃) and two different sintering activators (BN and B₂Cr). Unlubricated pin-on-disc wear tests were carried out. Wear mechanisms were analysed by means of scanning electron microscopy and X-ray diffraction. A plastic deformation and particle detachment wear mechanism was revealed. Plasticity during sliding induced an austenite to martensite transformation. The presence of ceramic particles (Al₂O₃ and Y₂O₃) and sintering activators (B₂Cr, BN) improved significantly the wear resistance (especially the combination Al₂O₃ and B₂Cr). Ceramic particles limited plastic deformation while sintering activators decreased final porosity.     

Tribological performance of MoS2---B2O3 compacts

A recent investigation suggests that selected oxides perform well as additives in molybdenum disulphide (MoS₂) because of their ability to soften at asperity contacts with the result that the solid lubricant can attain and retain a preferred tribological orientation.This research determined the effectiveness of boric oxide (B₂O₃), when used as an additive in MoS₂, for substrate temperatures ranging from 21°C to 316°C. This range was used to allow the asperity contact temperature to vary below and above the softening point of B₂O₃. It was found that a moderate friction coefficient and high wear, which is attributed to the additive acting abrasively, occurred when the asperity contact temperature was well below the softening point of the oxide. When the asperity contact temperature neared the softening point of the oxide, the friction coefficient increased dramatically and wear volume was reduced. It is postulated that B₂O₃ acted adhesively at the interface resulting in a higher coefficient of friction, and wear decreased due to an attainment of a preferred orientation by the MoS₂. For asperity contact temperatures significantly above the softening point of B₂O₃, the friction coefficient returned to about the same value as for temperatures below the softening point. It is speculated that wear continued to increase moderately because of localized melting of the B₂O₃, permitting the MoS₂ to be removed from the interface. These observations support a hypothesis that an additive, such as boric oxide, can soften as the asperity contact temperature approaches the softening point temperature of the additive so that the overall tribological conditions may be improved resulting in reduced interfacial wear. Significant changes in temperature, load or sliding velocity would, of course, dramatically alter the wear characteristics observed at the interface.     

Improved wear resistance of Si3N4 tool inserts by addition of Al2O3 platelets

In the present work, Si₃N₄ matrix composites reinforced with different amounts of Al₂O₃ platelets (0, 30 and 50vol%) were produced with the aim of increasing the tribochemical resistance in the machining of steels. Tool wear was related to the linear increase of the main cutting force (F_c) with time (dF_c/dt); a real-time parameter that can be used to assess the cutting edge damage and to stop machining before the tool fails. For all machined steels, tool wear resistance increased with increasing Al₂O₃ platelet content.     

Comparison on abrasive wear of SiCrFe, CrFeC and Al2O3 reinforced Al2024 MMCs

The effects of volume fraction and size of SiCrFe, CrFeC, and Al₂O₃ particulates on the abrasive wear rate of compo-casted Al2024 metal matrix composites (MMCs) were studied. The process variables like the stirring speed, position and the diameter of the stirrer have affected the diffusion between particulates and matrix.The abrasive wear rate was decreased by the increase in particulate volume fraction of SiCrFe and CrFeC intermetallic reinforced composites over 80 grade SiC abrasive paper. The wear rates of the all composites decreased with aging treatment, and the best result was seen for the composite having a hybrite structure as SiCrFe and CrFeC particulates together. Nevertheless, the fabrication of composites containing soft particles as copper favors a reduction in the friction coefficient.