生坯密度对烧结 Nd-Fe-B 磁体结构与性能的影响

结合国内烧结Nd-Fe-B磁体工业生产过程，研究了压制成型时生坯密度变化对烧结Nd—Fe—B磁体致密化程度、显微组织、取向度与磁性能的影响。试验结果表明，生坯密度的提高可促进烧结致密化过程，抑制烧结过程晶粒的不均匀长大，提高取向度，改善磁性能。     

无重稀土烧结Nd-Fe-B磁体的显微结构和磁性能研究

对Ga、Al、Cu和Zr共同掺杂的烧结Nd-Fe-B磁体磁性能和显微结构进行研究,并通过回火工艺对磁体的矫顽力进行调控。结果表明：当一级回火为900℃×150 min,且二级回火为500℃×180 min时,磁体矫顽力H_cj从烧结态的14.33 kOe大幅提高到二级回火态的19.86 kOe,提高了38.6%;方形度H_k/H_cj由0.86增加到0.97;剩磁B_r仅从烧结态13.51 kGs略微下降到二级回火态的13.46 kGs;富稀土相分布更加连续和明显。研究分析表明,矫顽力大幅增加主要是由于含有少量的富Nd相和贫B相的烧结Nd-Fe-B磁体中Ga的掺杂改变了晶界相湿润性,降低了富稀土相中Fe元素的含量。本研究为无重稀土高矫顽力和高剩磁烧结Nd-Fe-B磁体步入产业化夯实了理论基础。     

高性能烧结Nd-Fe-B磁体关键制造技术的开发与应用

烧结Nd-Fe-B永磁材料由于具有低成本、高磁性能而广受人们关注。近20年来，为了提高磁体的磁性能、温度稳定性能和抗腐蚀性能，国内外开展了大量的研究工作。据此，简要综述了近年来高性能烧结Nd-Fe-B磁体关键制造技术的开发与应用状况。     

烧结Nd-Fe-B磁体的温度稳定性缺陷分析

采用SEM、EDAX及粒度分析手段,研究了烧结Nd-Fe-B磁体开路磁通不可逆损失(hirr)异常偏高的原因。结果表明,磁体显微组织中晶粒尺寸分布不均匀及存在少量粗大晶粒,是导致其温度稳定性缺陷的主要因素,表现为少数产品hirr异常偏高。在磁体工业生产过程中,改进原料的铸锭和制粉技术,避免出现粗大粉末颗粒,减少极细粉末颗粒的数量,保证磁体显微组织精细均匀,是制备温度稳定性高的烧结Nd-Fe-B磁体的基本措施。     

烧结钕铁硼磁体的开发与应用

本文介绍了烧结钕铁硼 ( Nd- Fe- B)磁体的开发现状 ,并概述了国内外生产与市场应用。     

添加Gd或Ho对烧结Nd-Fe-B磁体结构与性能的影响

添加不同数量的Gd或Ho,制备了(33-x)(Pr-Nd)-xGd-0.2Cu-0.75Al-1.10B -64.95Fe和(33-x)(Pr-Nd)-xHo-0.2Cu-0.75Al-1.10B-64.95Fe(x是质量分数,x=0,1,3,5)烧结磁体,分析了添加Gd或Ho对材料磁性能、温度稳定性及显微组织的影响....     

高居里温度Nd-Fe-B磁体的制备及温度稳定性研究

本文通过研究磁体(PrNd)27.8CoxDy3FebalB0.97(x=20,25)在不同热处理工艺下的磁性能、密度及晶粒大小,以探寻其最佳热处理工艺,并对磁体的温度稳定性进行了研究.结果表明:较高的Co含量使磁体的居里温度Tc大幅提高,但会导致内禀矫顽力Hcj下降;磁体的温度稳定性(温度系数与不可逆磁通损失hirr...     

Recycle for Sludge Scrap of Nd-Fe-B Sintered Magnet as Isotropic Bonded Magnet

The reduction diffusion method was performed for the sludge scrap of Nd-Fe-B sintered magnets with adding Ca metal to recover the oxidized Nd-Fe-B phase. After washing the resultant powders to remove Ca metal component, the powders obtained were recycled as an isotropic magnetic powder by the melt spinning method. The magnetic properties of powders as recycled were inferior, especially for the coercivity value, due to the deletion of rare earth metals during the washing process. The adjustment of metal composition, i.e., the addition of Nd metal, at the melt spinning process improved the magnetic properties to be Br=～0.75 T, Hcj=～0.93 mA·m-1, and(BH)max=～91 kJ·m-3. The magnetic properties of the bonded magnets prepared from the composition-adjusted powders were Br=～0.66 T, Hcj=～0.92 mA·m-1, and(BH)max=～70 kJ·m-3, which are approximately comparable to the commercially available MQPB boned one(Br=～0.73 T, Hcj=～0.79 mA·m-1, and(BH)max=～86 kJ·m-3).     

NdFeB磁体的烧结过程研究

研究了在真空和氩气中烧结对NdFeB磁体磁性能和微观组织的影响.结果发现:经真空烧结的磁体磁性能有较大的个体差异,而在氩气中烧结的磁体磁性能则基本均匀一致,与前者相比,其剩磁平均值高0.05～0.09 T,内禀矫顽力要高1.6 MA/m左右,磁能积约高40 kJ/m3.SEM照片显示,在氩气气氛中烧结的磁体的微观组织更加均匀,而经真空烧结的磁体则有较多的缺陷.     

高Dy含量烧结Nd-Fe-B的晶界扩散处理研究

研究了晶界扩散处理对高Dy含量烧结Nd-Fe-B磁体性能和结构的影响。经蒸镀渗Dy晶界扩散处理,高Dy含量Nd-Fe-B磁体的矫顽力从1 713 kA/m提高至2 161 kA/m,而剩磁和最大磁能积基本没有下降,处理后磁体内Dy平均质量分数仅增加0.30%。不同深度片层分析表明,虽然磁体近表面片层比中心片层的Dy含量高,但是片层间矫顽力相差较少,而且所有片层的矫顽力均远高于未处理磁体片层的矫顽力。电子探针Dy元素面分布结果显示,在未处理高Dy含量磁体的晶界与主相中均存在Dy元素富集区且富集浓度较低,而经扩散处理后,晶界富Nd相中的Dy富集区浓度及所占比例明显提高;包括磁体芯部在内,磁体内大部分角隅处富Nd相内Dy含量明显增加,进一步提高了高Dy含量磁体内部各处的矫顽力。     

Grain Growth Behavior in Sintered Nd-Fe-B Magnets

The Nd2Fe14B grain growth behavior in sintered Nd-Fe-B magnets was quantitatively described.The effects of sintering temperature and time,and alloy powder size and its distribution on grain growth process were analyzed.Hence,possible grain growth mechanisms in these magnets were qualitatively discussed.The Nd2Fe14B grain growth proceeded at quite a high rate in the initial 0~1 h of sintering and from then onwards the grain growth rate decreased.A large average particle size or a wide particle size distribution of initial alloy powders was found to remarkably accelerate the grain growth process and even result in the occurrence of abnormal grain growth.On the basis of experimental results,two grain growth mechanisms were considered to operate during sintering of Nd-Fe-B magnets,that is,dissolution and re-precipitation of Nd2Fe14B particles,and Nd2Fe14B particle growth by coalescence.It was believed that Nd2Fe14B particle growth by coalescence not only produced a large average grain size and a wide grain size distribution,but also was the fundamental reason for the formation of abnormally large grains in the microstructure of sintered Nd-Fe-B magnets.     

Application of Rare Earth Magnet Nd-Fe-B in Solid-Liquid Separation

Application of Rare Earth Magnet Nd-Fe-B in Solid-Liquid Separation     

Effect of LiF on Densification and Mechanical Properties of Dy-α-Sialon Ceramics

The effect of LiF on the densification and mechanical properties of hot-pressed Dy-α-sialon ceramics was studied. Comparatively, without LiF as sintering additive, the pure Dy-α-sialon ceramic should be sintered at 1750 ℃. When LiF is used, the sintering temperature of the Dy-α-sialon is greatly lowered to 1500～1650 ℃. Obviously, the addition of LiF has a strong effect on the improvement in densification. Meanwhile, the resultant Dy-α-sialon has no significant changes in the mechanical properties.     

钕铁硼永磁体电镀Ni-P非晶态合金镀层

研究了钕铁硼永磁体电镀Ni-P非晶态合金镀液组成、工艺参数和工艺流程,分析了影响镀层性能的影响因素,包括电流密度、温度、镀液的pH值及亚磷酸的含量等。测定了镀层与基体的结合强度;用中性盐雾试验评定了镀层的耐蚀性。结果表明,Ni-P非晶态合金化学稳定性好,耐蚀性优异,是钕铁硼永磁体的一种理想保护镀层。     

还原—扩散法制取Nd-Fe-B系磁体

为了降低具有卓越永磁性的Nd-Fe-B磁体的制造成本,使之更快得到推广使用,本文研究了采用还原—扩散工艺路线,直接用Nd₂O₃作为原材料制取Nd-Fe-B磁体的方法、研究了基本组元Nd和添加元素CO、Al的含量对永磁性能的影响,成功地制造出Nd-Fe-B系永磁体。其中最佳性能为Br＝1.30 T,_MH_C＝0.46 MA/m,(BH)_max＝286.5 KJ/m³。实验结果还表明,氧在合金中起着有害作用,为了获得优异的磁性能,含氧量必须被控制在0.8%以下。     

Nd-Fe-B磁体热等静压烧结的实验研究

研究了热等静压烧结对Nd-Fe-B磁体的致密度、显微组织及磁性能的影响.结果表明:与常压烧结磁体相比,热等静压烧结磁体的内部存在较多的孔洞,致密度、晶粒取向度及磁性都有所降低.用加热Ar气热膨胀而产生热等静压进行烧结的办法不适于制造高性能的烧结磁体.     

Investigation of Abnormal Grain Growth in Sintered Nd-Fe-B Permanent Magnet

The abnormal growth of grains of sintering Nd13.6 Dy0.4 Fe79.5 B6.5 magnets were investigated in low oxygen manufacturing process.The abnormal growth of grains occurs easily when the sintering temperature is higher than 1080℃ during the manufacture process.In the magnets, the oxygen content is less than 700 × 10-6 and the average particle size of powder is smaller than 4 μm.The squareness of demagnetization curve of magnet is deteriorated.For high performance magnets, the abnormal growth grain should be avoided by selecting a suitable sintering temperature.     

Recycling of waste Nd-Fe-B sintered magnets by doping with dysprosium hydride nanoparticles

Recycling of waste sintered Nd-Fe-B permanent magnets by doping DyH3 nanoparticles was investigated. The effect of the DyH3 nanoparticles on the microstructure and magnetic properties of the recycled m...     

Nd-Fe-B永磁材料的粉末注射成形技术

介绍了目前采用的几种粉末注射成形用Nd-Fe-B磁粉的制备方法及特点;讨论了粘结剂、改性剂及磁场取向对注射成形Nd-Fe-B粘结剂磁体和烧结磁体最终磁性能的影响;指出了注射成形Nd-Fe-B磁体的现在以及潜在的应用市场。在此基础上,指出了今后开展研究工作的方向。