Colorless polyimides from 2,3,3′,4′-biphenyltetracarboxylic dianhydride (α-BPDA) and various aromatic bis(ether amine)s bearing pendent trifluoromethyl groups

A series of organosoluble and light-colored polyimides (III) was prepared from 2,3,3′,4′-biphenyltetracarboxylic dianhydride (α-BPDA) with various fluorinated aromatic bis(ether amine)s via two-step method with thermal or chemical imidization of poly(amic acid)s yielded polyimides. The III series had inherent viscosity of 0.74-1.01 dl/g and showed excellent solubility in a variety of organic solvents. They were soluble in the amide polar solvent, ether-type solvent, and chlorinated solvent. These polyimide films also showed a high optical transparency and less color intensity, with an ultraviolet-visible absorption edge of 369-382 nm and low b^* values (a yellowness index) of 5.0-11.7. Glass-transition temperature of the III series was recorded at 244-319 °C and higher than the isomeric polyimides V series. Compared with the nonfluorinated polyimides IV, the III series showed lighter-colored and lower dielectric constants and moisture absorptions. The good tensile properties and excellent thermal properties of the III series were also observed.     

Synthesis and properties of organosoluble polyimides based on 1,1-bis[4-(4-amino-2-trifluoromethylphenoxy)phenyl]cyclohexane

New aromatic diamine with cyclohexane cardo group substituted with trifluoromethyl group in the side chain, 1,1-bis[4-(4-amino-2-trifluoromethylphenoxy)phenyl]cyclohexane (II), was prepared through the nucleophilic substitution reaction of 1,1-bis(4-hydroxyphenyl)cyclohexane and 2-chloro-5-nitrobenzotrifluoride in the presence of potassium carbonate, to yield the intermediate dinitro compound I, followed by catalytic reduction with hydrazine and Pd/C to afford the diamine II. Fluorinated polyimides (IVa-g) were prepared from the II with various aromatic dianhydrides via thermal or chemical imidization of poly(amic acid). These polyimides had inherent viscosity ranging from 0.72 to 1.16 dl/g and showed excellent solubility in a variety of organic solvents. They were soluble in a concentration of 10% in the amide polar solvent, and 1-5% in the other testing solvents. IV films showed good mechanical properties, excellent thermal stability. The 10% weight loss temperature was above 476 °C in nitrogen or air, and the glass transition temperature was recorded at 214-278 °C. In comparison of the IV series with the analogous nonfluorinated polyimides (V series) based on 1,1-bis[4-(4-aminophenoxy)phenyl]cyclohexane (II′), IV series revealed better solubility, lighter-colored and lower dielectric constants and moisture absorptions. Their films had cut-off wavelengths in the range of 364-414 nm, b^* value (a yellowness index) ranging from 3.3 to 66.3, dielectric constants of 3.02-3.55 (1 MHz), with moisture absorption of 0.16-0.36 wt%.     

Synthesis and properties of novel organosoluble polyimides derived from 1,4-bis[4-(3,4-dicarboxylphenoxy)]triptycene dianhydride and various aromatic diamines

A novel triptycene-based dianhydride, 1,4-bis[4-(3,4-dicarboxylphenoxy)]triptycene dianhydride, was prepared from 4-nitro-N-methylphthalimide and potassium phenolate of 1,4-dihydroxytriptycene (1). The aromatic nucleophilic substitution reaction between 4-nitro-N-methylphthalimide and 1 afforded triptycene-based bis(N-methylphthalimide) (2), which hydrolyzed and subsequently dehydrated to give the corresponding dianhydride (3). A series of new polyimides containing triptycene moieties were prepared from the dianhydride monomer (3) and various diamines in m-cresol via conventional one-step polycondensation method. Most of the resulting polyimides were soluble in common organic solvents, such as chloroform, THF, DMAc and DMSO. The polyimides exhibited excellent thermal and thermo-oxidative stabilities with the onset decomposition temperature and 10% weight loss temperature ranging from 448 to 486 °C and 526 to 565 °C in nitrogen atmosphere, respectively. The glass transition temperatures of the polyimides were in the range of 221-296 °C. The polyimide films were found to be transparent, flexible, and tough. The films had tensile strengths, elongations at break, and tensile moduli in the ranges 95-118 MPa, 5.3-16.2%, and 1.03-1.38 GPa, respectively. Wide-angle X-ray diffraction measurements revealed that these polyimides were amorphous.     

Highly optically transparent/low color polyimide films prepared from hydroquinone- or resorcinol-based bis(ether anhydride) and trifluoromethyl-containing bis(ether amine)s

Two series of novel polyimides (5a-g and 6a-g) containing flexible ether linkages and pendent trifluoromethyl (CF₃) groups were synthesized from 1,4-bis(3,4-dicarboxyphenoxy)benzene dianhydride (3a) and 1,3-bis(3,4-dicarboxyphenoxy)benzene dianhydride (3b) with various CF₃-substituted aromatic bis(ether amine)s (4a-g) via ring-opening polyaddition to poly(amic acid)s, followed by thermal or chemical imidization. These polyimides were readily soluble in a variety of organic solvents and could be solution-cast into flexible and tough films. The cast films exhibited high optical transparency and almost no color, with a UV-vis absorption edge of 368-382 nm and a very low b^∗ value (a yellowness index) of 6.2-15.5. They had good thermal stability with glass-transition temperatures of 186-288 °C, and most of them did not show significant decomposition before 500 °C. Moreover, these polyimide films also possessed low dielectric constants of 2.79-3.49 (at 1 MHz) and low water uptakes (<0.65 wt%).     

Colorless and high organosoluble polyimides from 2,5-bis(3,4-dicarboxyphenoxy)-t-butylbenzene dianhydride and aromatic bis(ether amine)s bearing pendent trifluoromethyl groups

A series of polyimides III_a-h characterized by colorlessness, high transparency, high solubility, and good mechanical property, was synthesized from the aromatic dianhydride, 2,5-bis(3,4-dicarboxyphenoxy)-t-butylbenzene dianhydride (I), and various aromatic diamines (II_a-h) with pendent trifluoromethyl group via polyaddition, chemical imidization, and direct cast films. The III series showed more colorless than the polyimides (V and VI series) of 2,2-bis(3,4-dicarboxyphenyl)hexafluoropropane dianhydride (6FDA) contained, the VI series was synthesized from the II with 6FDA. These films III had cut-off wavelengths between 371 and 376 nm, as well as b* value (a yellowness index) ranging from 3.0 to 4.7. In fact, it is so far the most colorless aromatic polyimide in our systematical researches. The III series had inherent viscosity ranging from 0.72 to 1.33 dL/g and showed excellent solubility in a variety of organic solvents. They were soluble in a concentration of 5-10% in the amide polar solvent, ether solvent, and chlorinated solvent. These films showed strength tensile of 97-123 MPa, dielectric constants of 2.78-3.28 (1 MHz), and moisture absorptions of 0.11-0.36 wt%. The glass transition temperature of the III series was recorded at 214-259 °C, the 10% weight loss temperature was over 468 °C, and the residue was more than 47% at 800 °C in nitrogen.     

Effects of internal linkage groups of fluorinated diamine on the optical and dielectric properties of polyimide thin films

To investigate the difference of the trifluoromethyl (CF₃) group and ether group affecting the optical property of fluorinated polyimides (PIs), we prepared 4,4′-bis(4-amino-2-trifluoromethylphenoxy)diphenyl ether (4) with three ether groups and 2,2-bis[4-(4-amino-2-trifluoromethylphenoxy)phenyl]hexafluoropropane (5) with four CF₃ groups with 2-chloro-5-nitrobenzotrifluoride and 4,4′-dihydroxydiphenyl ether or 2,2-bis(4-hydroxyphenol)hexafluoropropane. Two series of organosoluble and light-colored PIs (4a-4c, 5a-5c) were synthesized from 4 and 5 with various aromatic dianhydrides: 3,3,4,4-benzophenonetetracarboxylic dianhydride (BTDA) (a), 4,4-oxydiphthalic anhydride (ODPA) (b), and 4,4-hexafluoroisopropylidenediphthalic anhydride (6FDA) (c), prepared through a typical two-step polymerization method. These PIs were soluble in amide polar solvents and even in less polar solvents. The glass-transition temperatures (T_g) of 4a-5c were 221-249 °C and the 10% weight-loss temperatures were above 530 °C. Their films had cutoff wavelengths between 339 and 399 nm and yellowness index ranges from 1.95 to 42.60. The dielectric constants estimated from the average refractive indices are 2.59-2.93 (1 MHz). In a comparison of the PI series based on 4, 5, and 4,4′-bis(4-amino-2-trifluoromethylphenoxy)biphenyl (6), we found that the CF₃ group and ether group on the diamine had almost same effect in lowering the color, but the ether group had better thermal stability. The color intensity of the three PI series was lowered in the following order: 6 > 4 > 5. The PI 5c, synthesized from diamine 5 and dianhydride c, had six CF₃ groups in a repeated segment and ether group at the same time, so it exhibited the lightest color among the three series.     

Synthesis and electrochromic properties of aromatic polyimides bearing pendent triphenylamine units

A series of aromatic polyimides with pendent triphenylamine group were synthesized from equimolar mixtures of 4,4′-oxydianiline (ODA) and 4-(3,5-diaminobenzamido)triphenylamine (4), 4-(3,5-diaminobenzamido)-4′,4″-di-tert-butyltriphenylamine (t-Bu-4) or 4-(3,5-diaminobenzamido)-4′,4″-dimethoxytriphenylamine (MeO-4) with two aromatic tetracarboxylic dianhydrides (DSDA or 6FDA) via a conventional two-step procedure that included a ring-opening polyaddition to give poly(amic acid)s, followed by chemical imidization. These polyimides exhibited good solubility in polar organic solvents and could be solution-cast into flexible and strong films. They showed excellent thermal stability, with T_g values in the range of 284–309 °C. The polyimides derived from diamines t-Bu-4 and MeO-4 exhibited reversible electrochemical oxidation, accompanied by strong color changes with high contrast ratio and electrochromic stability. For the polyimides derived from diamine 4, the coupling reaction between the triphenylamine radical cations occurred during the oxidative process forming a tetraphenylbenzidine structure, which resulted in an additional oxidation state and color change together with enhanced near-IR absorption at fully oxidized state.     

Synthesis and nonlinear optical properties of soluble fluorinated polyimides containing hetarylazo chromophores with large hyperpolarizability

The novel fluorinated polyimides with side-chain nonlinear optical (NLO) chromophores were synthesized from hydroxyl polyimides, followed by the Mitsunobu reaction with NLO chromophores. Molecular structural characterization for the resulting polymers was achieved by ¹H NMR, FT-IR, UV-Vis spectra, elemental analysis and gel permeation chromatography (GPC). The polymers exhibit excellent solubility in common organic solvents, good film-forming properties, high glass transition temperature (T_g) in the range from 193 to 200 °C and thermal stability up to 290 °C. The polyimides P1 and P2 containing hetarylazo chromophores with large hyperpolarizability possess a high electro-optic (EO) coefficient (r₃₃), which is larger than that of the polyimide P3 attached DR1. Excellent temporal stability and low optical losses in the range of 1.9-2.1 dB/cm at 1.55 μm were observed for these polymers. Such new NLO fluorinated polyimides are distinguished by an excellent combination of NLO activity, temporal stability, and optical loss.     

Properties of organosoluble aromatic polyimides from 3′-trifluoromethyl-3,4′-oxydianiline

A colorless fluorinated diamine, 3′-trifluoromethyl-3,4′-oxydianiline (3′-CF₃-3,4′-ODA) (II) was prepared through the nucleophilic substitution reaction of 3-nitrophenol and 2-chloro-5-nitrobenzotrifluoride by catalytic reduction with hydrazine and Pd/C. A series of Polyimides V were synthesized from the diamine II with various aromatic dianhydrides III_a-f via thermal and chemical imidization. These polyimides had inherent viscosities ranging from 0.88 to 1.12 dl/g. A comparison of V, VI to analogous polyimides VII, VIII. VI, VII and VIII was based on 3′4-ODA, 3-CF₃-4,4′-ODA, 4,4′-ODA, respectively. In terms of the color of PI revealed that the color intensity of phenoxy-containing amine of the meta-structure and the para-structure with the CF₃ group would fell off color intensity. The color intensity of the four polyimide series was lessened in the following order: V>VII>VI>VIII. The solubility of V is better than VI, VII and VII. The polyimide V films had a tensile strength ranging from 124 to 147 MPa, elongation at break from 9 to 65%, and initial modulus from 2.3 to 2.8 GPa. The glass transition temperature of polymers was recorded at 234-313 °C. They had 10% weight loss at a temperature above 515 °C and left more than 50% residue even at 800 °C in nitrogen. Compared with polyimides VI, V showed the lower dielectric constants of 2.80-3.50 (40 MHz), and moisture absorptions in the range of 0.44-1.02 wt%.     

Synthesis, electroluminescence, and photovoltaic properties of dendronized poly(p-phenylene vinylene) derivatives

Two dendronized poly(p-phenylene vinylene) (PPV) derivatives, ED-PPV and BB-PPV, have been successfully synthesized according to the Gilch route. The obtained polymers possess excellent solubility in common solvents, good thermal stability with 5% weight loss temperature of more than 340 °C. The weight-average molecular weight (M_w) and polydispersity index (PDI) of ED-PPV and BB-PPV are in the range of (1.26-2.34)×10⁵ and 1.37-1.45, respectively. Polymer light-emitting diodes (PLEDs) with the configuration of ITO/PEDOT:PSS/polymer/Ca/Al devices were fabricated, and the PLEDs emitted green-yellow light. The turn-on voltages of the PLEDs based on ED-PPV and BB-PPV were approximately 4.3, and 4.5 V, respectively. The PLED devices of ED-PPV exhibited the maximum luminance of about 157 cd/m² at 10.5 V. Photovoltaic cells with the configuration of ITO/PEDOT:PSS/polymer:C₆₀ (1:1)/Al were also fabricated, and the energy conversion efficiency of the devices based on ED-PPV and BB-PPV was measured to be 0.58, and 0.014%, respectively, under the white light at 75 mW/cm².     

Organic-inorganic hybrid materials from a new octa(2,3-epoxypropyl)silsesquioxane with diamines

Hybrid materials based on a new polyhedral oligomeric silsesquioxane, octa(2,3-epoxypropyl)silsesquioxane (OE) with diamines of 4,4′-methylenedianiline (DDM) and 5-trifluoromethyl-1,3-phenylenediamine (FPA) were prepared and characterized. OE was synthesized from cage-structured octaallylsilsesquioxane (OA) with m-chloroperbenzoicacid. The FTIR studies suggested that the N-H bond in diamines was not completely reacted with epoxy group due to steric hindrance and also extensive hydrogen bonding existed in the hybrid materials. The retention of the cage structure in the prepared hybrid materials was suggested by the FTIR and ²⁹Si NMR studies. The OE/FPA hybrid materials had superior thermal/mechanical characteristics than the OE/DDM due to the higher rigidity of the FPA than that of DDM or the silicon-fluorine interaction enhancing crosslinking reaction or hydrogen bonding. The prepared OE/FPA had a T_g of 170 °C, which was higher than diglycidyl ether of bisphenyl A (DGEBA)/DDM at the same stoichiometric ratio. It also had excellent thermal, mechanical, and dielectric characteristics with high storage modulus of 1.8 GPa (30 °C) and 0.3 GPa (250 °C), low coefficient of thermal expansion of 86 μm/m °C, and dielectric constant of 2.19. Thus, it can be high performance materials with potential applications for electronic packaging.     

New amphiphilic fluorescent CBABC-type pentablock copolymers containing pyrene group by two-step atom transfer radical polymerization (ATRP) and its self-assembled aggregation

A series of novel amphiphilic fluorescent CBABC-type pentablock copolymers (Py-PMMA-PEG4600-PMMA-Py) were prepared from BAB-type amphiphilic triblock copolymer (PMMA-PEG4600-PMMA) as macroinitiator with various contents of 1-(methacryloyloxyethylamino-carboxylmethyl) pyrene (PyMOI) by atom transfer radical polymerization (ATRP) in toluene using CuBr/2,2-bipyridine as catalyst system. Triblock copolymer (PMMA-PEG4600-PMMA) was prepared by ATRP and obtained from Br-PEG4600-Br as macroinitiator with methyl methacrylate in tetrahydrofuran using the same catalyst. The molecular weights of pentablock copolymers which were reinitiated by PMMA-PEG4600-PMMA macroinitiator were calculated from ¹H NMR spectra up to 42,400 gmol⁻¹. The polydispersity of pentablock copolymers obtained from GPC analysis was narrow between 1.10 and 1.38. The crystallinity of triblock copolymer (PMMA-PEG4600-PMMA) was decreased slightly with incorporating PMMA segment. Introducing the bulky pyrene substituent into pentablock copolymer, the melting temperature was not observed and all pentablock copolymers showed amorphous patterns in wide-angle X-ray scattering (WAXS) due to decrease in the degree of crystallinity of polymer chain because of disturbing regular packing. The temperatures at 10% weight loss (Td₁₀), examined by TG analysis, showed values ranging from 265 to 323 °C in nitrogen and 264 to 313 °C in air. Fluorescence spectra of Py-PMMA-PEG4600-PMMA-Py exhibited stronger excimer emission at ca. 480 nm due to the aggregations of pyrene group formed via interaction of the hydrophobic chains. The more content of PyMOI segment in pentablock copolymers can obtain the higher emission intensity ca. 480 nm. When there were higher PyMOI contents (84.9 wt% PyMOI) in pentablock copolymers, they formed larger aggregates (210 nm) in SEM micrographs. On the other hand, while increasing the concentration of the polymer solution in THF, the morphology was changed from spherical (0.1 mg/mL) to chainlike (1.0 mg/mL) aggregates.     

Structure-property relationships for a series of polyimide copolymers with sulfonated pendant groups

A series of high molecular weight, sulfonated polyimide copolymers (8a-f) with controlled acid contents have been obtained using 2,2′-bis(4-sulfobenzyloxy)benzidine (14) prepared via a flexible synthetic route. This series of novel sulfonated polyimide membranes were found to possess higher hydrolytic stability than polyimides in which the sulfonic acid groups are bound directly to the polymer main chain. An in-depth analysis of conductivity data was also performed for 8 and compared to the results for Nafion^® (1), sulfonated poly(ether ether ketone) (2) and a main-chain sulfonated polyimide (3). In order to remove the influence of acid strength, the proton mobility value for 8 at infinite dilution was calculated and found to be 1.2(±0.6) × 10⁻³ cm² s⁻¹ V⁻¹. A catalyst-coated membrane (CCM)-MEA based on a polyimide incorporating 60% sulfonated monomer (8d) was found to exhibit comparable beginning-of-life fuel cell performance as a Nafion^®-based CCM MEA at 50 °C.     

Synthesis and properties of novel soluble polyimides having a spirobisindane-linked dianhydride unit

A new synthetic procedure was elaborated allowing the preparation of semiaromatic dianhydride. N-Methyl protected 4-chlorophthalic anhydride was nitrated with HNO₃ to produce N-methyl-4-chloro-5-nitrophthalimide (1). The aromatic nucleophilic substitution reaction between 5,5′,6,6′-tetrahydroxy-3,3,3′,3′-tetramethyl-1,1-spirobisindane and 1 afforded spirobisindane-linked bis(N-methylphthalimide) (2), which was hydrolyzed and subsequently dehydrated to give the corresponding dianhydride (3). The latter was polymerized with five different aromatic diamines to afford a series of aromatic polyimides. The properties of polyimides such as inherent viscosity, solubility, UV transparency and thermal stability were investigated to illustrate the contribution of the introduction of spirobisindane groups into the polyimide backbone. The resulting polyimides were readily soluble in polar solvents such as chloroform, THF and N-methyl-2-pyrrolidone. The glass-transition temperatures of these polyimides were in the range of 254-292 °C. The tensile strength, elongation at break, and Young's modulus of the polyimide film were 68.8-106.6 MPa, 5.9-9.8%, 1.7-2.0 GPa, respectively. The polymer films were colorless and transparent with the absorption cutoff wavelength at 286-308 nm.     

Synthesis and characterization of alternating fluorene-based copolymers containing diaryl- and non-substituted bithiophene units

A series of soluble alternating fluorene-based copolymers containing diaryl- and non-substituted bithiophene units are synthesized by palladium-catalyzed Suzuki coupling reaction. All polymers demonstrate green colors of photoluminescence (PL) in chloroform, good thermal stability (with decomposition temperatures above 436 °C), and high glass transition temperatures (in the range of 120-144 °C). Owing to the large steric hindrance of diaryl substituents on bithiophenes in the polymers (P2-P4), the aggregation of solids is reduced as well as the solubility is improved, so the performance of their PLED devices are superior to that of the non-substituted polymer (P1). Compared with P1, the introduction of substitutents at 3,3′-position of bithiophene in P2-P4 has significant effects on the photophysical properties of resulting polymers in solution and solid states. Though the PL quantum yield of P1 is much higher than those of diaryl-substituted polymers (P2-P4), the PLED device of P1 has the worst electroluminescence (EL) properties due to the poor solubility of P1. Consequently, among these polymers, the device made of P3 as an emitter has the highest luminance of 2590 cd/m² at 9.5 V. For optimum device performance, a device of P3 blended with PVK can be further enhanced to a brighter luminance of 4284 cd/m² at 18 V.     

Synthesis, characterization, and high gas permeability of poly(diarylacetylene)s having fluorenyl groups

Diarylacetylenes having fluorenyl groups and other substituents (trimethylsilyl, t-butyl, bromine, fluorine) (1a-1) were polymerized with TaCl₅-n-Bu₄Sn. Monomers 1a-l produced high molecular weight polymers 2a-l (M_w 5.1 × 10⁵-1.3 × 10⁶) in 12-59% yields. All of the polymers were soluble in common organic solvents, and gave tough free-standing membranes by the solution casting method. The onset temperatures of weight loss of polymers 2a-l in air were over 400 °C, indicating considerably high thermal stability. All the polymer membranes showed high gas permeability; e.g., the oxygen permeability coefficient (PO₂) of 2a was as large as 4800 barrers. Membrane 2d possessing two fluorine atoms at meta and para positions of the phenyl ring showed the highest oxygen permeability (PO₂ = 6600 barrers) among the present polymers.     

New host copolymers containing pendant triphenylamine and carbazole for efficient green phosphorescent OLEDs

A series of vinyl copolymers (P1-P6) containing pendant hole-transporting triphenylamine (11-88 mol%) and carbazole chromophores were synthesized by radical copolymerization to investigate the influence of triphenylamine groups upon optoelectronic properties. The copolymers were readily soluble in common organic solvents and their weight-average molecular weights (M_ws) were between 1.41 × 10⁴ and 2.24 × 10⁴. They exhibited moderate thermal stability with T_d = 402-432 °C at 5% weight loss. The emission spectra (both PL and EL) of the blends [P1-P6 with 4 wt% Ir(ppy)₃] showed dominant green emission (517 nm) attributed to Ir(ppy)₃ due to efficient energy transfer from P1-P6 to Ir(ppy)₃. The HOMO levels of P1-P6, estimated from onset oxidation potentials in cyclic voltammeter, were −5.42 to −5.18 eV, which are much higher than −5.8 eV of conventional poly(9-vinylcarbazole) (PVK) host owing to high hole-affinity of the triphenylamine groups. The optoelectronic performances of phosphorescent EL devices, using P1-P6 as hosts and Ir(ppy)₃ as dopant (ITO/PEDOT:PSS/P1-P6:Ir(ppy)₃ (4 wt%):PBD (40 wt%)/BCP/Ca/Al), were greatly improved relative to that of PVK. The best performance was obtained with P4 device, in which the maximum luminance and luminance efficiency were 11?501 cd/m² and 10.6 cd/A, respectively.     

Copolymers containing pendant styryltriphenylamine and carbazole groups: Synthesis, optical, electrochemical properties and its blend with Ir(ppy)3

A series of vinyl copolymers (PVKST12-PVKST91) and homoploymer PVST containing pendant hole-transporting 4-(4-oxystyryl)triphenylamine (12-100 mol%) and carbazole chromophores were synthesized by radical copolymerization and employed as host for Ir(ppy)₃ phosphor to tune emission color. They were characterized using the ¹H NMR, FT-IR, absorption and photoluminescence spectra, elemental analysis, GPC, cyclic voltammetric and thermal analysis (DSC, TGA). Their weight-average molecular weights (M_w) and decomposition temperatures (T_d) were 1.46-5.68 × 10⁴ and 356-399 °C, respectively. The HOMO levels of PVKST12-PVKST91 and PVST, estimated from the onset oxidation potentials in cyclic voltammograms, were −5.40 to −5.14 eV, which are much higher than −5.8 eV of the conventional host poly(9-vinylcarbazole) (PVK) owing to high hole-affinity of the 4-(4-oxystyryl)triphenylamine groups. Therefore, copolymers PVKST are effective in reducing hole-injection barrier between the PEDOT:PSS and emitting layer. Electroluminescent devices [ITO/PEDOT:PSS/PVKST:Ir(ppy)₃:PBD/BCP/Ca/Al] using the hole-transporting PVKST as host were fabricated to tune the emission color. Their EL spectra showed a major emission at 515 nm and a minor peak at 435 nm attributed to Ir(ppy)₃ and 4-(4-oxystyryl)triphenylamine, respectively. The C.I.E. 1931 coordinates shift from (0.29, 0.61) for PVK to (0.33, 0.42) for PVST with an increase in 4-(4-oxystyryl)triphenylamine content.     

Syndiotactically enriched 1,2-selective polymerization of 1,3-butadiene initiated by iron catalysts based on a new class of donors

A series of phosphoryl (PO) contained compounds: triethylphosphate (a), diethylphenylphosphate (b), ethyldiphenylphosphate (c) triarylphosphates (d and h-m), triphenylphosphine oxide (e), phenyl diphenylphosphinate (f) and diphenyl phenylphosphonate (g) have been prepared. Iron catalysts, which are generated in situ by mixing the compounds with Fe(2-EHA)₃ and AlⁱBu₃ in hexane, are tested for butadiene polymerization at 50 °C. Phosphates donated catalysts have been, unprecedently, found to conduct extremely high syndiotactically (pentad, rrrr = 46.1-94.5%) enriched 1,2-selective (1,2-structure content = 56.2-94.3%) polymerization of butadiene. Introduction of electron withdrawing substituents on phenyl rings oftriphenylphosphate (k-m) remarkably promotes catalytic activity, while bulky substituent isopropyl at 2-position (h) has beneficial influence on regioselectivity. Employment of e, f or g as donor, results in a suppressed monomer conversion, accompanied by deteriorated 1,2-regioselectivity. The effects of polymerization conditions such as reaction temperature, types of cocatalysts and polymerization medium are also investigated by using catalyst system with tri(2,4-difluorophenyl)phosphate (m) as donor. Highly tolerance to polymerization temperature up to 80 °C is observed for the first time in the iron-based catalyst.     

Poly(7-oxanorbornenes) carrying 2,2,6,6-tetramethylpiperidine-1-oxy (TEMPO) radicals: Synthesis and charge/discharge properties

TEMPO-containing 7-oxanorbornene monomers 1-4 (TEMPO = 2,2,6,6-tetramethylpiperidine-1-oxy) were synthesized and polymerized via ring-opening metathesis using a ruthenium carbene catalyst. Monomers 1 and 3 gave polymers with number-average weights of 80?100 and 112?200 in 85 and 96% yields, respectively, whereas monomers 2 and 4 did not provide high molecular weight polymers. Poly(1) and poly(3) were soluble in common solvents including CHCl₃, CH₂Cl₂ and THF, while insoluble in hexane, diethyl ether and MeOH. They were thermally stable up to ca. 240 °C according to the TGA measurements in air. The secondary batteries utilizing the present polymers as cathode-active material demonstrated reversible charge/discharge processes, whose discharge capacities were 107 and 92.8 A h/kg, and displayed excellent high-rate charge and discharge properties. These cells demonstrated excellent cycle life, e.g., the discharge capacities of poly(1) and poly(3) showed less than 10% decrements even after 100 cycles.