国产TP310HCbN钢在高温应力下的组织结构

为探讨TP310HCbN的强化机理和失效原因,借助透射电镜和扫描电镜对国产TP310HCbN钢在高温应力作用下的组织结构进行研究。结果表明：经高温应力作用,晶内析出面心立方结构的M₂₃C₆碳化物和简单四方结构的NbCrN,晶界也析出M₂₃C₆碳化物,长时间试验条件下M₂₃C₆上析出σ相;高温应力下析出的M₂₃C₆和NbCrN提高了TP310HCbN钢持久断裂试样的硬度;晶内和晶界析出的M₂₃C₆碳化物的晶格常数均为基体的3倍,并与基体保持完全共格关系;随着试验时间延长,M₂₃C₆碳化物数量增多。对于国产TP310HCbN钢,在运行环境下需关注σ相和碳化物的分布、尺寸及其数量。     

超超临界锅炉用TP310HCbN奥氏体耐热钢管化学成分优化探讨

对国外提供的TP310HCbN奥氏体耐热钢管技术交流资料、ASMESA-213标准、Code case 2115和2115—1以及国外研发时实际成分范围、国外实物管的成分检测结果、质量证明书成分进行了对比,分析了TP310HCbN化学成分特点,并提出了此钢管的成分控制范围及目标值。     

宝钢07Cr25Ni21NbN钢管通过技术评审

<正>2011年1月11日在上海,全国锅炉压力容器标准化技术委员会组织专家对宝钢超(超)临界锅炉用07Cr25Ni21NbN(TP310HCbN/S31042)钢管进行了技术评审。宝山钢铁股份有限公司采用EAF电炉冶炼+AOD脱碳+LF钢包精炼进行炼钢,并通过"热挤压十冷轧/冷拔"工艺生产的锅炉用07Cr25Ni21NbN奥氏体耐热钢无缝钢管,经上海锅炉厂有限公司试验和上海发电设备成     

07Cr25Ni21NbN奥氏体耐热无缝钢管的研制

为满足超超临界电站锅炉过热器、再热器的制造要求,宝山钢铁股份有限公司开展了07Cr25Ni21NbN(TP310HCbN/S31042)奥氏体耐热无缝钢管的研制。论述了该钢种的成分优化设计、生产工艺过程及性能评定,数据表明,所生产的产品技术指标和性能均符合GB 5310—2008及ASME SA-213标准要求。     

铬钼钒螺栓钢高温持久强韧性的研究

本文叙述了Cr-Mo-V螺栓钢的蠕变脆性和蠕变断裂韧性概念。蠕变断裂切性可用来度量Cr-Mo-V钢的蠕变脆性。试验结果表明,蠕变裂纹扩展速度随钢的蠕变断裂韧性增高而降低。文中还建立了蠕变断裂韧性与蠕变断裂缺口敏感性的关系。由此表明,当蠕变断裂韧性值大于0.175mm时,就消除了蠕变断裂缺口敏感性。文中还研究了可消除Cr-Mo-V螺栓钢蠕变脆性的一种热处理新工艺。     

取消10CrMo910钢厚壁管接头焊后热处理的研究

用深缺口插销法评定１０ＣｒＭｏ９１０钢的冷裂纹和再热裂纹的敏感性，对未经焊后热处理与经过焊后热处理的１０ＣｒＭｏ９１０钢厚壁管接头的性能进行了高温模拟对比试验。试验结果表明：３５ｍｍ厚的１０ＣｒＭｏ９１０钢接头焊前预热１８０￣２００℃可防止冷裂纹；１０ＣｒＭｏ９１０钢只有轻微的再热裂纹敏感性，取消焊后热处理的１０ＣｒＭｏ９１０钢接头在高温运行过程中不会产生再热裂纹；未经焊后热处理的１０ＣｒＭｏ９１     

ЭП182钢螺栓的金属技术监督

一、前言自70年代以来,我国火电厂安装苏制670-140型锅炉和K200-130-3型汽轮机所用的合金钢紧固件,皆为20X_1M_1Φ_1TP(182)钢所制。这种钢具有组织稳定、持久强度高、抗松驰性能好、脆性转变温度低、室温缺口敏感性小等一系列适于做高温紧固件的优点,因而被认为是制作电厂高温紧固件的理想钢种。但是,无论从国外报道或国内在运行期间的观察试验结果看,随着运行时间的增长,此种钢     

T92钢高温时效硬度变化试验及蠕变性能研究

为了研究T92铁素体钢在高温时效后的硬度变化,对其在温度700℃、725℃和750℃下进行了时效试验,结果表明,随温度的提高和时间的延长,T92钢的硬度会逐渐下降,时效温度是硬度变化的主要影响因素;硬度的降低会加剧材料蠕变寿命的损耗.结合试验数据拟合出时效硬度与Larson-Miller参数之间的关系,按照Larson-Mmer参数整理得到T92钢的硬度下降规律与试验值基本一致.     

长期运行后异种钢焊接接头组织性能研究

对长期运行后的TP347H与钢102异种钢焊接接头进行了组织与性能试验研究,对其组织老化与性能变化进行了分析。结果表明,长期运行后钢102金相组织达到4级球化,TP347H钢有沿晶碳化物析出,钢102侧熔合线处存在一个过渡层,该处析出较多碳化物,硬度较高,母材中的碳向焊缝迁移。     

TP304H奥氏体耐热钢锅炉管的组织性能研究

为了研究在高温高压下长期使用及发生过热爆管的TP304H奥氏体耐热钢的组织性能,分别对某再热器TP304H锅炉管样进行了金相组织分析、电子探钟试验、扫描电镜能谱分析及常温机械性能试验等.研究表明,在高温高压下TP304H奥氏体耐热钢的组织中会析出Cr23C6,并沿晶界析出σ相,从而造成TP304H奥氏体耐热钢的冲击韧性、塑性和抗氧化性能降低,使固溶体中产生晶界贫铬,增加了晶间腐蚀敏感性.σ相析出越多,TP304H钢的强度就越低.     

异种钢焊接接头组织老化及损伤状态评估方法

简要阐述了以TP304H、TP347H为代表的奥氏体不锈钢与以T91、T22为代表的马氏体和珠光体型耐热钢组成的异种钢焊接接头在国内外电站的应用情况及运行过程中暴露的安全问题,如焊接接头组织老化、力学性能劣化、熔合线附近氧化缺口的生成以及管子内壁氧化层厚度增大等;并介绍了现场无损检验、割管取样实验室评估和管子内壁氧化层厚度现场测量等三种评估方法。     

The influence of short-term strength on the notch sensitivity and crack growth resistance of the metal of rotors under creep conditions

Comparative assessment of the effect the yield strength has on the characteristics of EI-415 steel under creep conditions is carried out based on the results from long-term (for more than 70000 h) tests of notched samples at an elevated temperature. The metal of three rotors (EI-415 steel) (one after it had been in operation for 137000 h and the other two in the delivery state with relatively increased and decreased levels of yield strength) was used as material under study. The notch sensitivity was evaluated from the ratio between the long-term strength of smooth samples and that of notched samples tested for long-term strength with recording the crack opening width. The resistances to crack incipience and to crack growth with a preset rate were determined from the lengths of cracks appeared at the end of two auxiliary notches of a smaller depth, and the creep fracture toughness was calculated from the break conditions. It is shown that the metal the properties of which are at the lower boundary of yield strength requirements is slightly more advantageous in the level of the above-mentioned characteristics.     

纳米粒子和钢纤维增强混凝土断裂能研究

为了研究纳米SiO2、钢纤维和预切口小梁试件相对裂缝深度对钢纤维增强纳米混凝土断裂韧性的影响,通过三点弯曲试件断裂试验,测得了试件的断裂能以及竖向荷载与裂缝嘴张开位移和裂缝尖端张开位移的关系曲线。试验结果表明：钢纤维和纳米SiO2在一定掺量范围内可使混凝土的断裂能提高;当纳米SiO2掺量小于5%时,试件断裂能随着纳米粒子掺量的增加而逐渐增大,而当纳米SiO2掺量超过5%后,试件断裂能随纳米粒子用量增大而逐渐下降;掺纳米粒子混凝土的断裂能随着钢纤维体积掺量的增加逐渐增大,当纤维体积掺量超过2%后又逐渐减小;三点弯曲断裂小梁试件相对切口深度对断裂能有较大影响,随着相对切口深度的增大,试件断裂能逐渐减小。     

不同表面处理的TP304钢在高温水蒸气中的氧化行为研究

对3种表面状态的TP304钢，即TP304钢基材，表面沉积CeO2薄膜以及表面先喷丸处理后再沉积CeO2薄膜的3种试样，在600℃进行高温水蒸气氧化行为试验研究。绘出氧化动力学曲线，并探讨氧化机理。分析了上述两种表面处理工艺对TP304钢抗高温水蒸气氧化性能的影响。     

基于全通滤波器的IIR陷波器在抑制电力线通信中的谐波干扰的研究

从滤波器的系数敏感度出发 ,提出用基于全通滤波器的IIR陷波器来抑制电力线通信信号中的谐波干扰。详细论述了这种陷波器的设计方法 ,分析了其在低频段的系数敏感度。通过实际数据验证了这种滤波器能够有效地抑制电力线通信信号中的谐波干扰 ,大大提高了信噪比。     

TP304H奥氏体不锈钢锅炉管长期高温运行后的组织变化分析和研究

对TP304H钢管在电厂长期高温运行后的组织变化和析出相进行了研究和分析,所得结果表明在长期高温、高压的运行过程中,TP304H钢管组织特征发生明显变化,析出相增加,主要是M23C6型碳化物和σ相,并随着析出物的增加,奥氏体耐热钢的机械性能下降,直至被破坏。为此,指出高温是影响析出相形成的主要因素。     

我国首台超临界机组X20CrMoV121钢受热面管状态分析

为全面了解火电厂X20CrMoV121钢受热面管长期运行后的安全状况,对某电厂X20CrMoV121钢末级过热器管及高温再热器管进行了力学性能测试、显微组织分析及高温持久强度试验。试验结果表明,运行管与原始管相比强度有所下降;沉淀相发生熟化,同时还出现了局部板条特征减弱,板条内出现亚结构,位错密度明显降低,且在亚结构内位错呈定向排列的趋势;高温持久强度仍然高于设计值。综合分析认为,经12万h运行后的X20CrMoV121钢管产生了一定程度的老化,但仍可满足设计工况下安全运行的要求。