Ir Diffusion Barriers in Ni/Au Ohmic Contacts to <Emphasis Type="Italic">p</Emphasis>-Type CuCrO<Subscript>2</Subscript>

The use of Ir diffusion barriers in Ni/Au-based Ohmic contacts to p-type CuCrO₂ layers was investigated. A specific contact resistance of ~5 × 10⁻⁴ Ω cm² was achieved after annealing at 500°C for the Ir-containing contacts, and the contacts were rectifying for lower anneal temperatures. In this case, the contact resistance was basically independent of the measurement temperature, indicating that tunneling is the dominant transport mechanism in the contacts. The morphology for the Ir-containing contacts was still smooth at 500°C although Auger electron spectroscopy depth profiling showed that some of the nickel had diffused to the surface and had oxidized. Contacts annealed at 800°C showed that some copper and most of the nickel had diffused to the surface and oxidized. The presence of the Ir diffusion barrier does increase the thermal stability of the contacts by ∼200°C compared to conventional Ni/Au contacts. By contrast, the use of other materials such as TaN, ZrN, and W₂B₅ as the diffusion barrier led to poorer thermal stability, with the contact resistance increasing sharply above 400°C.     

Effect of Cryogenic Temperature Deposition of Various Metal Contacts on Bulk Single-Crystal <Emphasis Type="Italic">n</Emphasis>-Type ZnO

The effect of cryogenic temperatures during metal deposition on the contact properties of Pd, Pt, Ti, and Ni on bulk single-crystal n-type ZnO has been investigated. Deposition at both room and low temperature produced contacts with Ohmic characteristics for Ti and Ni metallizations. By sharp contrast, both Pd and Pt contacts showed rectifying characteristics after deposition with barrier heights between 0.37 eV and 0.69 eV. Changes in contact behavior were measured on Pd to anneal temperatures of ∼300 °C, showing an increase in barrier height along with a decrease in ideality factor with increasing annealing temperature. This difference with annealing temperature is in sharp contrast to previous results for Au contacts to ZnO. There were no differences in near-surface stoichiometry for the different deposition temperatures; however, low temperature contacts demonstrated some peeling/cracking for Pt and Pd.     

Ohmic contacts to n-type GaN using Pd/Al metallization

Ohmic contacts to n-type GaN grown by metalorganic chemical vapor deposition were formed using a Pd/Al-based metallization. Ohmic contact resistances and specific contact resistances were investigated as a function of rapid thermal annealing temperature, Pd interlayer thickness, and annealing time. As-deposited Pd/AI was found to produce rectifying contacts while the metallization exhibited ohmic characteristics after annealing at temperatures as low as 400°C. A minimum contact resistance of 0.9 ohm-mm (specific contact resistance = 1.2 × 10⁻⁵ ohm-cm²) was obtained upon annealing at 650°C for 30 s. For comparison, Al and Ti/Al contacts were also investigated. Auger electron spectroscopy, secondary ion mass spectrometry, and x-ray diffraction were used to investigate metallurgical reactions.     

Low resistance bilayer Nd/Al ohmic contacts on n-type GaN

A bilayer Nd/Al metallization structure has been deposited onto low pressure organometallic vapor phase epitaxy grown n-type GaN ( 1 × 10¹⁸ cm⁻³) by electron-beam evaporation. Ohmic metal contacts were patterned photolithographically for standard transmission line measurement, and then thermally annealed at temperatures ranging from 200 to 350°C and from 500 to 650°C using conventional thermal annealing (CTA) and rapid thermal annealing (RTA), respectively. The lowest values for the specify contact resistivity of 9.8 × 10⁻⁶ Ω−cm² and 8 × 10⁻⁶ Ω−cm² were obtained using Nd/Al metallization with CTA of 250°C for 5 min and RTA of 600°C for 30 s. Examination of the surface morphology using atomic force microscopy as a function of annealing temperature revealed that the surface roughness was strongly influenced by conventional thermal annealing, it was smooth in the temperature range from 550 to 650°C for rapid thermal annealing. Auger electron spectroscopy depth profiling was employed to investigate the metallurgy and interdiffusion of contact formation.     

Interdiffusion of the p-InP with Au−Zn,Ti/Au,Pd/Au,Ti/Pd/Au at interface and their electrical properties

 In this report,the interdiffusion between the p-InP with Au-Zn,Ti/Au,Pd/Au and Ti/Pd/Au at interface have been investigated by Auger electron spectroscopy and electron spectroscopy for chemical analysis.The surface morphology for the heat treatment are observed with scanning electron microscopy. It is found that the indiffusion of Au is easier than that of Pd and Ti and the outdiffusion of In is easier than that of P.The combination state of In and Au is formed during the heat treatment of p-InP/Au-Zn. The effects of the alloying temperature and time on the specific contacts resistance of p-InP/Au-Zn system are studided.The low specific contact resistance,p_c=2.4-2.7×10~(-4)Ω-cm~2,is obtained when alloying at 450℃ for 2 min or at 350℃ for 30 min. These results indicate that the specific contact resistance strongly depend on the“interdiffusion degree”.The Zn in Au-Zn ahoy distributes onto the most surface layer of p-InP/Au-Zn system during evaporation process and heat treatment.It may be one of the reasons for the higher specific contacts resistance.     

Low resistance, thermally stable Au/Pt/Ti/WSiN ohmic contacts on n+-InGaAs/n-GaAs layer systems

The electrical properties of the ohmic contact systems Au/Pt/Ti/WSiN and Au/Pt/Ti to n⁺-InGaAs/GaAs layers grown by metalorganic vapor phase epitaxy were investigated and compared to each other. The thermal stability properties of these contact systems were characterized by accelerated stress tests at elevated temperatures and by complementary thin film x-ray diffraction analysis to evaluate the microstructural properties of degraded and nondegraded structures. The goal of these efforts was to develop stable, homogeneous emitter contacts for power heterojunction bipolar transistors. It was found that for both contact systems the best (specific) contact resistance R_c (ρ _c) is about 0.05 Ωmm (2 × 10⁻⁷ Ωcm²) in the as-deposited state. Au/Pt/Ti/WSiN contacts show no degradation after aging at 400°C for more than 20 h. This is in contrast to standard Au/Pt/Ti contacts which significantly degrade even after short time annealing at 400°C. The good long-time stability of the Au/Pt/Ti/WSiN system is related to the advantageous properties of the reactively sputtered WSiN barrier layer.     

Ohmic contact formation in palladium-based metallizations to n-Type InP

Two Pd-based metallizations have been systematically studied, i.e., Au/Ge/Pd and Pd/Ge contacts to n-type InP, in an attempt to better understand the role of the metallization constituents in forming ohmic contacts. Ohmic contacts were obtained with minimum specific resistances of 2.5 × 10⁻⁶ Ω-cm² and 4.2 × 10⁻⁶ Ω-cm² for the Au/Ge/Pd and the Pd/Ge contacts, respectively. The annealing regime for ohmic contact formation is 300-375°C for the Au/Ge/Pd/InP system and 350-450°C for the Pd/GelnP system. Palladium, in both cases, reacts with InP to form an amorphous layer and then an epitaxial layer at low temperatures, providing good metallization adhesion to InP substrates and improved contact morphology. Ohmic contact formation in both contacts is attributed to Ge doping, based on the solid state reaction-driven decomposition of an epitaxial layer at the metallization/InP interface, producing a very thin, heavily doped InP layer. Gold appears to be responsible for the difference in contact resistance in the two systems. It is postulated that Au reacts strongly with In to form Au-In compounds, creating additional In site vacancies in the InP surface region (relative to the Au-free metallization), thereby enhancing Ge doping of the InP surface and lowering the contact resistance. Both contacts degrade and ultimately become Schottky barriers again if over annealed, due to consumption of additional InP, which destroys the heavily doped InP layer.     

Very low resistance ohmic contacts to n-GaN

Ohmic contacts with low resistance are fabricated on n-GaN films using Al/Ti bilayer metallization. GaN films used are 0.3 μm thick layers with carrier concentrations of 1 × 10¹⁹ cm⁻³ grown on the c-plane sapphire by ion-removed electron cyclotron resonance molecular beam epitaxy. The lowest value for the specific contact resistivity (ρ_c) of 1.2×10⁻⁸ Ω·cm² was obtained with furnace annealing at 500°C for 60 min. This result shows the effectiveness of high carrier concentration GaN layers and the low temperature annealing for the realization of low resistance ohmic contacts. Sputtering Auger electron spectroscopy analysis reveals that Al diffuses into Ti layer and comes into contact with the GaN surface.     

Vanadium-based ohmic contacts to n-type Al<Subscript>0.6</Subscript>Ga<Subscript>0.4</Subscript>N

Four vanadium-based contacts to n-type Al_0.6Ga_0.4N were compared in this work. Both V/Al/Pd/Au and V/Al/V/Au contacts with optimized layer thicknesses provided lower specific-contact resistances than did the previously reported V/Al/Pt/Au ohmic contact. Specific contact resistances of the V/Al/Pd/Au (15 nm/85 nm/20 nm/95 nm) and V/Al/V/Au (15 nm/85 nm/20 nm/95 nm) contacts were 3×10⁻⁶ Ω·cm² and 4×10⁻⁶ Ω·cm², respectively. On the other hand, an analogous V/Al/Mo/Au contact never became ohmic, even after it was annealed at 900°C for 30 sec. Compared to the V/Al/Pd/Au contact, the V/Al/V/Au contact required a less severe annealing condition (30 sec at 700°C instead of 850°C). The V/Al/V/Au contact also provided a smoother surface, with a root-mean-square (RMS) roughness of 39 nm.     

Study of contact resistivity, mechanical integrity, and thermal stability of Ti/Al and Ta/Al ohmic contacts to n-type GaN

The annealing conditions and contact resistivities of Ta/Al ohmic contacts to n-type GaN are reported for the first time. The high temperature stability and mechanical integrity of Ti/Al and Ta/Al contacts have been investigated. Ta/Al (35 nm/115 nm) contacts to n-type GaN became ohmic after annealing for 3 min at 500°C or for 15 s at 600°C. A minimum contact resistivity of 5×10⁻⁶Ω cm² was measured after contacts were repatterned with an Al layer to reduce the effect of a high metal sheet resistance. Ti/Al and Ta/Al contacts encapsulated under vacuum in quartz tubes showed a significant increase in contact resistivity after aging for five days at 600°C. Cross section transmission electron microscopy micrographs and electrical measurements of aged samples indicate that the increased contact resistivity is primarily the result of degradation of the metal layers. Minimal reactions at the metal/GaN interface of aged samples were observed.     

Electrical characteristics of thermally stable Ru and Ru/Au ohmic contacts to surface-treated p-type GaN

The electrical and thermal properties of Ru and Ru/Au ohmic contacts on two-step-surface-treated p-GaN have been investigated using current-voltage (I–V) measurements and Auger electron spectroscopy. It is shown that annealing at 700°C for 2 min in a flowing N₂ atmosphere improves the I–V characteristics of the contacts. For example, the annealed Ru and Ru/Au schemes produce a specific contact resistance of 3.4 (±0.9)×10⁻³ and 1.2 (±1.1)×10⁻³ Ωcm², respectively. It is also shown that annealing results in a large reduction (by ∼100 meV) in the Schottky barrier heights of the Ru and Ru/Au contacts, compared to the as-deposited ones. The electrical properties of the two-step-surface-treated Ru/Au contacts are compared with those of the conventionally treated contacts.     

Ohmic contacts to n-type GaN

Ohmic contacts to n-GaN using Ag, Au, TiN, Au/Ti, Au/Mo/Ti, and Au/Si/Ti have been studied. The Fermi level of GaN appears to be unpinned, and metals and compounds with work functions less than the electron affinity resulted in ohmic contacts. Reactively sputter deposited TiN was ohmic as deposited. However, Au/Ti, Au/Mo/Ti, and Au/Si/Ti required heat treatments to form ohmic contacts, with the best being an RTA at 900°C. Ag and Au were shown to diffuse across the GaN surface at T>500°C; therefore, they are unstable, poor ohmic contact metallizations as single metals. The other contact schemes were thermally stable up to 500°C for times of 30 min.     

Ta/Au ohmic contacts to n-type ZnO

Ta/Au ohmic contacts are fabricated on n-type ZnO (∼1 × 10¹⁷ cm⁻³) epilayers, which were grown on R-plane sapphire substrates by metal organic chemical vapor deposition (MOCVD). After growth and metallization, the samples are annealed at 300°C and 500°C for 30 sec in nitrogen ambient. The specific contact resistance is measured to be 3.2×10⁻⁴ Ωcm² for the as-deposited samples. It reduces to 5.4×10⁻⁶ Ωcm² after annealing at 300°C for 30 sec without significant surface morphology degradation. When the sample is annealed at 500°C for 30 sec, the specific contact resistance increases to 3.3 × 10⁻⁵ Ωcm². The layer structures no longer exist due to strong Au and Ta in-diffusion and O out-diffusion. The contact surface becomes rough and textured.     

Microstructural and electrical investigation of Ni/Au ohmic contact on p-type GaN

Electrical properties of Ni/Au ohmic contacts on p-type GaN were interpreted with the change of microstructure observed under transmission electron microscopy. The contact resistivity was decreased from 1.3×10⁻² to 6.1×10⁻⁴ Ωcm² after annealing at 600°C. The reduction is due to the dissolution of Ga atoms into Au−Ni solid solution formed during annealing, via the generation of Ga vacancies. Thus, net concentration of holes increased below the contact, resulting in the reduction of contact resistivity. At 800°C, N atoms decomposed; reacted with Ni, and forming cubic Ni₄N. Consequently, N vacancies, acting as donors in GaN, were generated below the contact, leading to the increase of contact resistivity to 3.8×10⁻² Ωcm².     

Thermally stable Nb and Nb/Au ohmic contacts to p-GaN

We have investigated Nb single and Nb/Au metallization schemes for the formation of thermally stable ohmic contacts to p-GaN. It is shown that the asdeposited Nb and Nb/Au contacts exhibit rectifying behavior. However, both the contacts produce ohmic characteristics when annealed at 850°C. Measurements show that the 850°C Nb/Au and Nb contacts yield a specific contact resistance of 1.9×10⁻⁸ and 2×10⁻² ωcm², respectively. Schottky barrier heights are found to decrease with increasing annealing temperature. A comparison of the XRD and electrical results shows that the formation of gallide phases such as Ga-Nb and Ga-Au compounds, play a role in forming ohmic contacts. Atomic force microscopy results show that the surface morphology of the Nb contacts is fairly stable up to 850°C, while the Nb/Au contacts are slightly degraded upon annealing at 850°C.     

Study of the Formation Mechanism of Cu/Ge/Pd Ohmic Contact to <Emphasis Type="Italic">n</Emphasis>-Type InGaAs

This study investigates electrical characteristics and the formation mechanism of the Cu/Ge/Pd Ohmic contact to n-type InGaAs. After annealing the contact at 250°C for 20 min, Cu₃Ge and Pd₁₂Ga₅As₂ compounds formed and Ge diffused into the InGaAs layer, achieving a heavily doped InGaAs layer with a low contact resistivity of 1 × 10⁻⁶ Ω cm². Thermal stability tests were performed on the Cu/Ge/Pd Ohmic contact to InGaAs after Ohmic contact formation, showing no obvious degradation after a 72 h reliability test at 250°C. The results indicate excellent electrical characteristics and thermal stability using Cu/Ge/Pd as an Ohmic contact metal to an n-InGaAs layer.     

Thermally stable Ge/Cu/Ti ohmic contacts to n-type GaN

The performance of a novel Ge/Cu/Ti metallization scheme on n-type GaN has been investigated for obtaining thermally and electrically stable low-resistance ohmic contacts. Isochronal (2 min.) anneals in the 600–740°C temperature range and isothermal (690°C) anneals for 2–10 min. duration were performed in inert atmosphere. For the 690°C isothermal schedule, ohmic behavior was observed after annealing for 3 min. or longer with a lowest contact resistivity of 9.1 × 10⁻⁵ Ωcm² after the 10 min. anneal for a net donor doping concentration of 9.2 × 10¹⁷ cm^−Ω3. Mean roughness (R_a) for anneals at 690°C was almost constant at around 5 nm, up to an annealing duration of 10 min., which indicates a good thermal stability of the contact scheme.     

Improved Long-Term Thermal Stability At 350°C Of TiB2–Based Ohmic Contacts On AlGaN/GaN High Electron Mobility Transistors

AlGaN/GaN High Electron Mobility Transistors (HEMTs) were fabricated with Ti/Al/TiB₂/Ti/Au source/drain Ohmic contacts and a variety of gate metal schemes (Pt/Au, Ni/Au, Pt/TiB₂/Au or Ni/TiB₂/Au) and subjected to long-term annealing at 350°C. By comparison with companion devices with conventional Ti/Al/Pt/Au Ohmic contacts and Pt/Au gate contacts, the HEMTs with boride-based Ohmic metal and either Pt/Au, Ni/Au or Ni/TiB₂/Au gate metal showed superior stability of both source-drain current and transconductance after 25 days aging at 350°C.     

Electrical characteristics and structural properties of ohmic contacts to p-type 4H-SiC epitaxial layers

Epitaxial films grown by low-temperature liquid phase epitaxy on p-type 4H-SiC were used as strongly doped subcontact layers for making low-resistance contacts to the p-type material. The layers had a bulk resistivity of ∼0.02 Ω · cm and an aluminum atom concentration of ∼1.5×10²⁰ cm⁻³. The absence of polytype inclusions and the distinct crystalline quality of the strongly doped subcontact layers was confirmed by x-ray diffraction methods. Ohmic contacts with resistivities less than 10⁻⁴ Ω · cm² were prepared by depositing and then annealing multilayer metal mixtures containing Al and Ti. The structural properties and energy characteristics of the resulting ohmic contacts are discussed. Fiz. Tekh. Poluprovodn. 33, 1334–1339 (November 1999)     

A transmission electron microscopy study of microstructure evolution with increasing anneal temperature in Ti/Al ohmic contacts to n-GaN

Al(200 nm)/Ti(20 nm)/n-GaN contacts have been studied using transmission electron microscopy (TEM) and the resulting microstructures correlated with the observed variation in specific contact resistance (ρ_c). A minimum ρ_c value of 7×10⁻⁷ Ωcm² was obtained after annealing at 550°C for 1 min in argon. Bulk metal and interfacial phases have been characterized, and explanations for the observed electrical behavior are proposed. A transition from TiN to AlN at the interface occurs between 650°C and 700°C.