Dispersive SnO2 nanosheets: Hydrothermal synthesis and gas-sensing properties

SnO₂ nanosheets with the thickness of 10 nm were successfully synthesized by a simple hydrothermal process at 180 °C for 12 h. The samples were characterized by X-ray power diffraction, scanning electron microscopy, transmission electron microscopy, and high-resolution transmission electron microscopy. The sensor performance of the as-prepared SnO₂ nanosheets for ethanol and carbon monoxide was measured. The results indicate that the sensor exhibited high response, quick response-recovery kinetics, and good repeatability.     

Synthesis of novel SnO2/ZnSnO3 core-shell microspheres and their gas sensing properities

Large-scale novel core-shell structural SnO₂/ZnSnO₃ microspheres were successfully synthesized by a simple hydrothermal method with the help of the surfactant poly(vinyl pyrrolidone) PVP. The as-synthesized samples were characterized using X-ray powder diffraction (XRD), scanning electron microscopy (SEM), transmission electron microscopy (TEM), and high-resolution transmission electron microscopy (HRTEM). The results indicate that the shell was formed by single crystalline ZnSnO₃ nanorods and the core was formed by aggregated SnO₂ nanoparticles. The effects of PVP and hydrothermal time on the morphology of SnO₂/ZnSnO₃ were investigated. A possible formation mechanism of these hierarchical structures was discussed. Moreover, the sensor performance of the prepared core-shell SnO₂/ZnSnO₃ nanostructures to ethanol was studied. The results indicate that the as-synthesized samples exhibited high response and quick response-recovery to ethanol.     

Hydrothermal synthesis of hollow ZnSnO3 microspheres and sensing properties toward butane

Hollow ZnSnO₃ microspheres were successfully prepared by hydrothermal method at 160 °C for 12 h. The prepared material was characterized by field emission scanning electron microscope (FESEM), transmission electron microscope (TEM) and X-ray diffraction measurements (XRD). The average diameter of the hollow ZnSnO₃ microspheres was in the range of 400-600 nm. Compared with solid ZnSnO₃ microspheres structure, the hollow ZnSnO₃ microspheres showed better response (S) to butane. To 500 ppm butane, the sensor response (S) of the hollow ZnSnO₃ microspheres was 5.79 at the optimum operating temperature of 380 °C, and the response and recovery time were 0.3 s and 0.65 s, respectively. The sensitivities of sensors based on this material were linear with the concentration of butane in the range of 100-1000 ppm.     

Enhancing performance of FSP SnO2-based gas sensors through Sb-doping and Pd-functionalization

Via flame spray pyrolysis (FSP), SnO₂ gas sensing layers have been doped with 0.01-4 wt% Sb as well as 0.01 wt% Pd in combination with 1 wt% Sb. Characterization of these materials through X-ray diffraction (XRD), Brunauer-Emmett-Teller (BET) surface analysis, and transmission electron microscopy (TEM) revealed particle grain sizes and crystallinity unchanged by the presence of Sb and/or Pd. The addition of Sb to SnO₂ resulted in the significant decrease in baseline resistance; up to two orders of magnitude in dry air at 300 °C and three orders of magnitude in humid air at 300 °C, which is significant for FSP-prepared gas sensors with high porosity and low particle coordination number since they typically suffer from high baseline resistance. While the baseline resistance was improved with Sb-doping, the sensor signal (R₀/R_gas) remained constant over all concentrations explored. Moreover, regarding the surface functionalization of SnO₂ with Pd in combination with Sb-doping, the reduction of baseline resistance was preserved without influencing sensor signal.     

The influence of catalytic activity on the response of Pt/SnO2 gas sensors to carbon monoxide and hydrogen

The article presents the results of research studies on ceramics SnO₂ sensors with Pt catalysts. The role of catalysis in gas sensing mechanisms was investigated. In order to obtain samples with different catalytic activity but with identical Pt loading, the Pt/SnO₂ catalysts were calcined at different temperatures (400-800 °C). Structural analysis of these samples was performed. Among the sensors manufactured with Pt/SnO₂, the highest sensitivity was shown for the sensor obtained with Pt/SnO₂ sample sintered at 800 °C. The correlation between catalytic activity and sensor sensitivity is given.     

SnO2 thin film sensor with enhanced response for NO2 gas at lower temperatures

Semiconducting SnO₂ thin films having higher value of electrical conductivity have been deposited using RF sputtering technique in the reactive gas environment (30% O₂ + 70% Ar) using a metallic tin (Sn) target for detection of oxidizing NO₂ gas. The effect of growth pressure (12-18 mTorr) on the surface morphology and structural property of SnO₂ film was studied using Atomic force microscopy (AFM), Scanning electron microscopy (SEM) and X-ray Diffraction (XRD) respectively. Film deposited at 16 mTorr sputtering pressure was porous with rough microstructure and exhibits high sensor response (∼2.9 × 10⁴) towards 50 ppm NO₂ gas at a comparatively low operating temperature (∼100 °C). The sensor response was found to increase linearly from 1.31 × 10² to 2.9 × 10⁴ while the response time decrease from 12.4 to 1.6 min with increase in the concentration of NO₂ gas from 1 to 50 ppm. The reaction kinetics of target NO₂ gas on the surface of SnO₂ thin film at the Sn sites play important role in enhancing the response characteristics at lower operating temperature (∼100 °C). The results obtained in the present study are encouraging for realization of SnO₂ thin film based sensor for efficient detection of NO₂ gas with low power consumption.     

Fabrication of N-type Fe2O3 and P-type LaFeO3 nanobelts by electrospinning and determination of gas-sensing properties

N-type Fe₂O₃ nanobelts and P-type LaFeO₃ nanobelts were prepared by electrospinning. The structure and micro-morphology of the materials were characterized by X-ray diffraction (XRD) and scanning of electron microscopy (SEM). The gas sensing properties of the materials were investigated. The results show that the optimum operating temperature of the gas sensors fabricated from Fe₂O₃ nanobelts is 285 °C, whereas that from LaFeO₃ nanobelts is 170 °C. Under optimum operating temperatures at 500 ppm ethanol, the response of the gas sensors based on these two materials is 4.9 and 8.9, respectively. The response of LaFeO₃-based gas sensors behaves linearly with the ethanol concentration at 10-200 ppm. Sensitivities to different gases were examined, and the results show that LaFeO₃ nanobelts exhibit good selectivity to ethanol, making them promising candidates as practical detectors of ethanol.     

Enhanced H2S sensing characteristics of Pt doped SnO2 nanofibers sensors with micro heater

Gas sensors were designed and fabricated using oxide nanofibers as the sensing materials on micro platforms using micromachining technology. Pure and Pt doped SnO₂ nanofibers were prepared by electrospinning and their H₂S gas sensing characteristics were subsequently investigated. The sensing temperatures of 300 and 500 °C could be attained at the heater powers of 36 and 94 mW, respectively, and the sensors showed high and fast responses to H₂S. The responses of 0.08 wt% Pt doped SnO₂ nanofibers to 4-20 ppm H₂S, were 25.9-40.6 times higher than those of pure SnO₂ nanofibers. The gas sensing characteristics were discussed in relation to the catalytic promotion effect of Pt, nano-scale morphology of electrospun nanofibers, and sensor platform using micro heater.     

Synthesis and gas sensing properties of bundle-like α-Fe2O3 nanorods

Bundle-like α-Fe₂O₃ nanostructures were successfully synthesized by a simple calcination of β-FeOOH precursor derived from a hydrothermal method in the presence of poly(vinyl pyrrolidone). The as-prepared products were characterized by X-ray power diffraction, field emission scanning electron microscopy, and transmission electron microscopy. The results indicated that bundle-like nanostructures were composed of well-aligned single crystalline nanorods with the diameters of 20-30 nm and the lengths of 200-300 nm. The gas sensing properties of as-prepared products were investigated. It was found that the sensor based on α-Fe₂O₃ nanostructure exhibited high response, quick response-recovery, and good repeatability to acetone at 250 °C.     

Examination of Au/SnO2 core-shell architecture nanoparticle for low temperature gas sensing applications

Au/SnO₂ core-shell structure nanoparticles (NPs) were synthesized using two methods, microwave and conventional precipitation. In both cases, the size of the Au core was 12-18 nm and the thickness of the SnO₂ shell was 8-12 nm. The particle size of SnO₂ synthesized using the microwave and precipitation method was 3-5 nm and 1-2 nm, respectively. Upon heating to 400-600 °C, both particles maintained their core-shell morphology but the smaller SnO₂ particles prepared using the precipitation method were more sintered. The resistance changes in films of these particles were measured as a function of CO concentration. The Au/SnO₂ particles prepared using the microwave method showed higher sensor response than those prepared using the precipitation method, even providing a significant signal at testing temperatures approaching ambient conditions, thereby affording a new class of material for gas sensing. Both sets of core-shell particles showed higher sensor response than the SnO₂ nanoparticles. The role of the Au core as a catalyst in improving the adsorption and oxidation of CO gas is important for improving the low temperature response. In addition, the maintenance of the size of SnO₂ in the microwave method during sintering contributed to the higher response towards CO sensing.     

Selectivity of flame-spray-made Nb/ZnO thick films towards NO2 gas

Unloaded ZnO and Nb/ZnO nanoparticles containing 0.25, 0.5 and 1 mol.% Nb were produced in a single step by flame-spray pyrolysis (FSP) technique. The nanoparticles were characterized by X-ray diffraction (XRD), scanning electron microscopy (SEM) and transmission electron microscopy (TEM). The BET surface area (SSA_BET) of the nanoparticles was measured by nitrogen adsorption. FSP yielded small Nb particles attached to the surface of the supporting ZnO nanoparticles, indicating a high SSA_BET. The morphology and accurate size of the primary particles were further investigated by TEM. Nb/ZnO nanoparticles paste composed of ethyl cellulose and terpineol as binder and solvent respectively was coated on Al₂O₃ substrate interdigitated with gold electrodes to form thick films by spin coating technique. After the sensing tests, the morphology and the cross-section of sensing film were analyzed by SEM and EDS analyses. The influence on a low dynamic range of Nb concentration on NO₂ response (0.1-4 ppm) of thick film sensor elements was studied at the operating temperatures ranging from 250 to 350 °C in the presence of dry air. The optimum Nb concentration was found be 0.5 mol.% and 0.5 mol.% Nb exhibited an optimum NO₂ response of ∼1640 and a short response time (27 s) for NO₂ concentration of 4 ppm at 300 °C.     

Ag nanoparticles modified TiO2 spherical heterostructures with enhanced gas-sensing performance

Monodispersed TiO₂ spherical colloids with diameters of about 250 nm were prepared by a sol-gel method. Heterostructural Ag-TiO₂ spheres were manipulated by surface engineering, in which the Ag nanoparticles with an average size of 10 nm were uniformly distributed on the surface of the TiO₂ nanospheres by in situ reduction and growth. The gas-sensing properties of the TiO₂ nanospheres and heterostructural Ag-TiO₂ nanospheres to ethanol and acetone were measured at 350 °C. The results indicated that Ag nanoparticles greatly enhanced the response, stability and response characteristic of TiO₂ nanospheres to the tested gases. Response times of Ag-TiO₂ sensor to 30 ppm acetone and 50 ppm ethanol were <5 s.     

The low temperature polysilicon (LTPS) thin film MOS Schottky diode on glass substrate for low cost and high performance CO sensing applications

The Au/SnO₂/n-LTPS MOS Schottky diode prepared on a glass substrate for carbon monoxide (CO) sensing applications is studied. The n-LTPS (n-type low temperature polysilicon) is prepared by excimer laser annealing and PH₃ plasma treatment of an amorphous Si thin film on glass substrate. The developed Schottky diode exhibits a high relative response ratio of ∼546% to 100 ppm CO ambient under condition of 200 °C and −3 V bias. The response ratio is better than the reported SnO₂ based resistive type CO sensors of 100% and 37%, respectively on poly-alumina and glass substrates or comparable to 390% of Pt-AlGaN/GaN Schottky diode CO sensor. Thus, the Au/SnO₂/n-LTPS Schottky diode has the potential to develop a low cost high performance CO sensor.     

Structural and properties of nanocrystalline WO3/TiO2-based humidity sensors elements prepared by high energy activation

Nanocrystalline WO₃/TiO₂-based powders have been prepared by the high energy activation method with WO₃ concentration ranging from 1 to 10 mol%. The samples were thermal treated in a microwave oven at 600 °C for 20 min and their structural and micro-structural characteristics were evaluated by X-ray diffraction, Raman spectroscopy, EXAFS measurements at the Ti K-edge, and transmission electron microscopy. Nitrogen adsorption isotherms and H₂ Temperature Programmed Reduction were also carried out for physical characterization. The crystallite and particle mean sizes ranged from 30 to 40 nm and from 100 to 190 nm, respectively. Good sensor response was obtained for samples with at least 5 mol% WO₃ activated for at least 80 min. Ceramics heat-treated in microwave oven for 20 min have shown similar sensor response as those prepared in conventional oven for 120 min, which is highly cost effective. These results indicate that WO₃/TiO₂ ceramics can be used as a humidity sensor element.     

Fe2O3 modified thick films of nanostructured SnO2 powder consisting of hollow microspheres synthesized from pyrolysis of ultrasonically atomized aerosol for LPG sensing

Nanostructured hollow spheres of SnO₂ with fine nanoparticles were synthesized by ultrasonic atomization. Thick film gas sensors were fabricated by screen printing technique. Different surface modified films (Fe₂O₃ modified SnO₂) were obtained by dipping them into an aqueous solution (0.01 M) of ferric chloride for different intervals of time followed by firing at 500 °C. The structural and microstructural studies of the samples were carried out using XRD, SEM, and TEM. The sensing performance of pure and modified films was studied by exposing various gases at different operating temperatures. One of the modified sample exhibited high response (1990) to 1000 ppm of LPG at 350 °C. Optimum amount of Fe₂O₃ dispersed evenly on the surface_, adsorption and spillover of LPG on Fe₂O₃ misfits and high capacity of adsorption of oxygen on nanostructured hollow spheres may be the reasons of high response.     

Highly sensitive and selective LPG sensor based on α-Fe2O3 nanorods

The α-Fe₂O₃ nanorods were successfully synthesized without any templates by calcining the α-FeOOH precursor in air at 300 °C for 2 h and their LPG sensing characteristics were investigated. The α-FeOOH precursor was prepared through a simple and low cost wet chemical route at low temperature (40 °C) using FeSO₄·7H₂O and CH₃COONa as starting materials. The formation of α-FeOOH precursor and its topotactic transformation to α-Fe₂O₃ upon calcination was confirmed by X-ray diffraction measurement (XRD), X-ray photoelectron spectroscopy (XPS), field emission scanning electron microscopy (FESEM) and transmission electron microscopy (TEM) analysis. The α-Fe₂O₃ nanorods exhibited outstanding gas sensing characteristics such as, higher gas response (∼1746-50 ppm LPG at 300 °C), extremely rapid response (∼3-4 s), relatively slow recovery (∼8-9 min), excellent repeatability, good selectivity and lower operating temperature (∼300 °C). Furthermore, the α-Fe₂O₃ nanorods are able to detect up to 5 ppm for LPG with reasonable response (∼15) at the operating temperature of 300 °C and they can be reliably used to monitor the concentration of LPG over the range (5-60 ppm). The experimental results clearly demonstrate the potential of using the α-Fe₂O₃ nanorods as sensing material in the fabrication of LPG sensors. Plausible LP G sensing mechanism of the α-Fe₂O₃ nanorods is also discussed.     

Enhanced room temperature response of SnO2 thin film sensor loaded with Pt catalyst clusters under UV radiation for LPG

The room temperature response characteristics of SnO₂ thin film sensor loaded with platinum catalyst clusters are investigated for LPG under the exposure of ultraviolet radiation. The SnO₂-Pt cluster sensor structures have been prepared using rf sputtering. Combined effect of UV radiation exposure (λ = 365 nm) and presence of Pt catalyst clusters (10 nm thick) on SnO₂ thin film sensor surface is seen to lead to an enhanced response (4.4 × 10³) for the detection of LPG (200 ppm) at room temperature whereas in the absence of UV illumination a comparable response (∼5 × 10³) could be obtained but only at an elevated temperature of 220 °C. The present study therefore investigates the effect of UV illumination on LPG sensing characteristics of SnO₂ sensors loaded with Pt clusters of varying thickness values. Results indicate the possibility of utilizing the sensor structure with novel dispersal of Pt catalyst clusters on SnO₂ film surface for efficient detection of LPG at room temperature under the illumination of UV radiations.     

Ultrahigh ethanol response of SnO2 nanorods at low working temperature arising from La2O3 loading

The influences of La₂O₃ loading on the ethanol sensing properties of SnO₂ nanorods were investigated. An obvious enhancement of response was obtained. The response of 5 wt% La₂O₃ loaded SnO₂ nanorods was up to 213 for 100 ppm ethanol at low working temperature of 200 °C, while that of pure SnO₂ nanorods is 45.1. The improvement in response might be attributed to the presence of basic sites, which facilitated the dehydrogenation process. While the working temperature was increased to 300 °C, the sensor response decreased to 16 for 100 ppm ethanol. Additionally, the La₂O₃ loaded SnO₂ nanorods sensors showed good selectivity to ethanol over methane and hydrogen. Our results demonstrated that the La₂O₃ loaded SnO₂ nanorods were promising in fabricating high performance ethanol sensors which could work at low temperature.     

Electrical response of Sm2O3-doped SnO2 to C2H2 and effect of humidity interference

Pure and Sm₂O₃-doped SnO₂ are prepared through a sol–gel method and characterized by X-ray diffraction (XRD) and transmission electron microscopy (TEM). The sensor based on 6 wt% Sm₂O₃-doped SnO₂ displays superior response at an operating temperature of 180 °C, and the response magnitude to 1000 ppm C₂H₂ can reach 63.8, which is 16.8 times larger than that of pure SnO₂. This sensor also shows high sensitivity under various humidity conditions. These results make our product be a good candidate in fabricating C₂H₂ sensors.     

Nano particulate SnO2 based resistive films as a hydrogen and acetone vapour sensor

SnCl₂ (solution) was spin coated on soda lime glass and Al₂O₃ substrate to obtain nano-particulate tin oxide film, directly by sintering at 550 °C for 40 minutes (min). The surface morphology and crystal structure of the tin oxide films were analyzed using atomic force microscopy (AFM) and X-ray diffraction (XRD). The size of SnO₂ nanostructure was determined from UV-vis and found to be ?3 nm. These films were tested for sensing H₂ concentration of 0.1-1000 ppm at optimized operating temperature of 265 °C. The results showed that sensitivity (R_air/R_gas per ppm) goes on increasing with decreasing concentration of test gas, giving concentration dependent changes. Special studies carried out at low concentration levels (0.1-1 and 1-10 ppm) of H₂, give high sensitivity (200 × 10⁻³/ppm) for lowest concentration (0.1-1 ppm) of H₂. The selectivity for H₂ against relative humidity (RH), CO₂, CO and LPG gases is also good. The sensor, at operating temperature of 200 °C, is showing nearly zero response to 300 ppm of H₂, and offering response to acetone vapour of 11 ppm. Selectivity for acetone against RH% and CO₂ was also studied. These sensors can be used as H₂ sensor at an operating temperature of 265 °C, and as an acetone sensor at the operating temperature of 200 °C.