铸坯及轧材中元素偏析行为分析

帘线钢由于含有较高的碳含量，极易在连铸过程中产生中心偏析和疏松、缩孔缺陷，影响成品稳定性。目前，轻压下工艺作为一种改善铸坯内部质量的有效方法之一，被广泛应用于连铸生产中。实验以LX86帘线钢为例，制定不同拉速下的轻压下实验方案，进行工业试验。使用碳硫检测仪、电子探针(EPMA)等对工业试验后铸坯及轧材元素偏析情况进行检测，试验结果表明，拉速设定为2.2 m/min时，铸坯中心碳偏析指数由1.136降低至1.062,轧材中碳、硅元素偏析指数得到改善，有效改善了铸坯内部元素均匀性，为后续成品的质量稳定性提供了支撑。     

连铸工艺参数对SWRH82B钢160 mm x 160 mm坯中心碳偏析的影响

试验研究了结晶器电磁搅拌频率、拉速、过热度及二冷强度对SWRH82B连铸小方坯中心碳偏析的影响。研究结果表明,结晶器搅拌电流为300 A时,低电磁搅拌频率下铸坯中心碳偏析情况较好;拉速为1.8 m/min时,提高二冷比水量有利于改善中心碳偏析,但二冷比水量过高会加剧偏析;拉速为1.8 m/min时,二冷比水量为0.75 L/kg较为合适,拉速为1.9 m/min时,二冷比水量为0.8 L/kg是比较合适的;当过热度在20～30℃时,过热度对铸坯中心碳偏析的影响不大。     

连铸工艺参数对SWRH82B钢160 mm×160 mm坯中心碳偏析的影响

试验研究了结晶器电磁搅拌频率、拉速、过热度及二冷强度对SWRH82B连铸小方坯中心碳偏析的影响。研究结果表明,结晶器搅拌电流为300 A时,低电磁搅拌频率下铸坯中心碳偏析情况较好;拉速为1.8 m/min时,提高二冷比水量有利于改善中心碳偏析,但二冷比水量过高会加剧偏析;拉速为1.8 m/min时,二冷比水量为0.75 L/kg较为合适,拉速为1.9 m/min时,二冷比水量为0.8 L/kg是比较合适的;当过热度在20～30℃时,过热度对铸坯中心碳偏析的影响不大。     

小方坯齿轮钢连铸过程中的宏观偏析模拟

基于国内某厂齿轮钢小方坯连铸生产过程,利用ProCAST软件建立移动切片模型,能够高效模拟连铸过程中的宏观偏析,模型分别模拟研究了不同过热度、二冷水量和拉坯速度等对宏观偏析的影响。模拟结果与碳偏析检测结果吻合良好,验证了移动切片模型模拟连铸坯宏观偏析的准确性。由于溶质浮力的影响,内弧侧的宏观偏析强于外弧侧。随着过热度的增加,铸坯中心碳偏析度从1.06增加至1.15。过热度控制在25 ℃范围内,可以保证铸坯的宏观碳偏析度控制在1.10范围内。随着连铸二冷水量的增加,铸坯中心偏析改善程度较小,铸坯中心碳偏析度从1.16降低至1.13。随着拉坯速度的增加,铸坯中心偏析呈现加重的趋势,铸坯中心碳偏析度由1.14增加至1.21,拉坯速度控制在1.4 m·min–1范围内,可保证铸坯中心碳偏析度低于1.15。      

连铸工艺对铸坯碳偏析影响的研究

钢液凝固过程中碳的不均匀分布是导致铸坯低倍碳偏析的主要原因,研究了钢水过热度、拉速、电磁搅拌强度对铸坯碳偏析指数的影响。在正常生产条件下,将中间包浇铸过热度控制在20～30℃、拉速1.8 m/min、结晶器电磁搅拌在200 A和4 Hz,对铸坯碳偏析改善有利,碳偏析指数降到了1.02。     

82B中心网状渗碳体产生原因及改善方法

研究了网状渗碳体级别与盘条及连铸坯中心碳偏析之间的定量关系,同时分析了影响铸坯中心偏析的关键连铸参数。结果表明:盘条中偏析比超过1.20就会有网状渗碳体形成;连铸坯中碳偏析指数大于1.16,盘条中就会出现超标的网状渗碳体。降低过热度,降低拉速,增大二冷水比水量,可以有效地降低铸坯中心偏析。通过工艺调整,铸坯中心平均碳偏析指数由1.13降低为1.08,网状渗碳体判次比例由2.0%降低为0.8%。     

连铸工艺参数对45#、70#钢铸坯冶金效果影响的探讨

通过对45#、70#钢铸坯低倍组织情况的分析以及连铸工艺参数的总结，探讨出钢水过热度、拉速、塞棒自动控制、二冷配水及电磁搅拌等连铸工艺参数对铸坯低倍组织的影响。通过对45#、70#钢中心碳偏析分析，表明随着钢中碳含量升高，连铸拉速、钢水过热度的增加，铸坯中心碳偏析有增大趋势。     

7#铸机大方坯断面生产重轨钢铸坯质量评价

文章通过对7#铸机设备改造后生产的大方坯断面重轨钢坯内外部质量对比,分析了结晶器电磁搅拌、动态二冷配水、动态轻压下对铸坯的中心碳偏析指数、疏松及铸坯凝固组织的影响,得出7#铸机两个大方坯断面重轨钢在合理拉速、过热度匹配下,采用结晶器电磁搅拌+轻压下工艺后,铸坯内部质量良好,不仅使铸坯等轴晶比率为52.3%~58.3%,也可使铸坯中心碳偏析指数控制在1.07以下。     

跨结晶器电磁搅拌器对重轨钢大方坯中心偏析的改善

以 2 8 0 mm× 32 5 mm重轨钢大方坯的试验数据为依据 ,分析了跨结晶器电磁搅拌形式下电磁搅拌参数 (电流和搅拌频率 )和连铸工艺参数 (拉速和过热度 )对铸坯中心碳偏析的影响 ,并对改善中心偏析的作用机理进行了探讨。为了更合理地分析中心偏析 ,还对不同直径的取样钻头造成同一铸坯中心偏析的分析偏差进行了必要的研究。     

连铸工艺参数对高碳连铸坯成分偏析的影响

高碳钢连铸坯的质量受拉速、二冷比水量、钢水过热度的影响较大。本文以SWRH382B预应力钢铸坯为研究对象,研究了拉速、二冷比水量、钢水过热度三个连铸参数对铸坯中心碳偏析的影响,从而得出了最佳的连铸工艺。     

Heat Transfer and Central Segregation of Continuously Cast High Carbon Steel Billet

A numerical model of heat transfer was developed to investigate the heat transfer of continuously cast billet with the aid of surface temperature tests by ThermaCAMTM researcher and nail shooting experiments. The effects of secondary cooling practice and casting speed on the solidification process and central segregation of carbon were investigated as well with the actual central segregation tests. The results show that the surface center and billet center temperatures exhibit a different pattern during solidification, and the solidified shell thickness is presented as an ＂S＂ type. With the increase of secondary cooling intensity and the decrease of casting speed, the end points of the solidus line and the liquidus line move forward, and the central segregation level of carbon decreases. The optimal casting condition is suggested for continuously cast high carbon billet with F-EMS （final electromagnetic stirring）.     

控制高碳钢中心碳偏析的工艺实践

针对方坯连铸过程中产生的连铸坯中心偏析问题,日钢第一炼钢厂采取了一系列控制措施,如减少钢液成分波动、降低中间包内钢液过热度、制定合适的拉速和温度匹配制度并保持恒拉速、优化结晶器电磁搅拌参数、控制合适的二冷强度、使用凝固末端电磁搅拌等,使高碳钢铸坯中心偏析明显改善,w[C]≥0.60%的高碳钢中心碳偏析(≤1.5级)合格率100%。     

降低SWRH82B铸坯中心偏析的探索与实践

通过大量的现场取样,结合实验室研究手段,系统的研究钢水过热度、拉速、二次冷却强度等工艺参数对高碳连铸坯中心偏析的影响,从而得出最佳的生产参数控制范围,改善swRH82B高碳钢连铸坯的中心偏析,提高铸坯质量和加工性能。     

70钢小方坯芯部质量优化

建立小方坯连铸凝固传热模型,通过测温和射钉试验校核模型,模型计算结果与测温和射钉试验结果间的相对误差分别为0.1％和0.64％,说明模型能够有效反映小方坯连铸的凝固传热情况.提高拉速后,铸坯的中心偏析和疏松加重.为优化高拉速下连铸坯的中心质量,依据模型计算结果及前人安装经验,将末端电磁搅拌安装装置由原来距离结晶器弯月面...     

采用220mm^2连铸机生产高碳铬轴承钢的连铸工艺研究

在用220mm^2的连铸机连铸GCr15轴承钢方坯的基础工艺上,通过调整连铸时钢水过热度、拉速、二冷配水、电磁搅拌的参数来减少连铸轴承钢大方坯的中心碳偏析及中心疏松等低倍组织缺陷,从而提高GCr15轴承钢方坯的质量。     

高碳钢铸坯缺陷机理探讨

通过对高碳钢铸坯的中心偏析、内部夹杂、表面裂纹的形成机理、影响因素、控制措施的分析,弄清了高碳钢铸坯缺陷的成因,为炼钢厂高碳钢的冶炼和连铸工艺的制定奠定了基础,还提出了铸坯中心缺陷最小化设计原则。     

工艺参数对高碳钢小方坯中心缺陷的影响

系统地研究了首钢三炼钢4号铸机拉速和比水量对优质高碳钢小方坯中心缺陷的影响。首先在典型工况下分别调整了拉速和比水量,将拉速2．6m／min降低到了2．0m／min,铸坯的中心偏析、疏松得到了改善,同时中心缩孔在一定程度上有所恶化,因此将拉速优化为2．2m／min。随着比水量的降低(1．0～0．7)L／kg,中心偏析先恶化,然后改善,中心疏松和中心缩孔均得到了改善,因此将比水量控制在0．7L／kg。最后将拉速和比水量进行了优化匹配。结果表明对于首钢三炼钢4号铸机将拉速控制在2．2m／min、冷却强度控制在0．8L／kg有益于优质高碳钢小方坯中心缺陷的改善。     

SWRH82B钢的生产工艺改进

连铸坯的中心碳偏析是SWRH82B在拉拔过程中出现笔尖状断裂的最主要原因,通过在连铸过程中调整水量分配和优化结晶器电磁搅拌参数,可以减轻铸坯碳偏析程度,线材获得良好的拉拔性能。