Synthesis, characterization and evaluation of NiMo/SiO2–Al2O3 catalysts prepared by the pH-swing method

NiMo/(X)SiO₂–Al₂O₃ catalysts were synthesized with various SiO₂ contents (X = 0, 10, 25 and 50 wt%) using the pH-swing method. In order to find the optimum SiO₂ content, the catalysts were evaluated in the hydrodesulfurization of 4,6-DMDBT, hydrogenation of naphthalene and hydrodenitrogenation of carbazole. Kinetic parameters of Langmuir–Hinshelwood type equations for all the reaction systems were estimated. FTIR analysis of CO adsorption for the sulfided catalysts shows that the amount of coordinatively unsaturated Mo sites promoted by nickel (CUS-NiMoS) follows the order NiMo/10ASA > NiMo/25ASA > NiMo/0ASA. This tendency agrees with the results obtained in catalytic activity.     

乙二胺四乙酸对NiMo/Al_2O_3催化剂加氢脱氮性能的影响

以氧化铝为载体,Ni和Mo为金属活性组分,添加不同含量乙二胺四乙酸,采用等体积浸渍法制备系列Ni Mo(x)/Al_2O_3(x为乙二胺四乙酸与Ni物质的量比)重质油加氢处理催化剂,考察乙二胺四乙酸加入量对催化剂加氢脱氮性能的影响,并采用N_2物理吸附-脱附、XRD和HRTEM等对催化剂进行表征。结果表明,乙二胺四乙酸的加入增强了金属组分与氧化铝载体间的相互作用,降低了MoS_2活性相的堆垛层数和片层长度,促进了活性相的分散。乙二胺四乙酸与Ni物质的量比为0.5时,MoS_2活性相堆垛层数和片层长度达到良好的结合,对应的催化剂Ni Mo(0.5)/Al_2O_3具有最优的加氢脱氮性能。     

Maya crude hydrodemetallization and hydrodesulfurization catalysts: An effect of TiO2 incorporation in Al2O3

Hydrotreating of Maya heavy crude oil over high specific surface area CoMo/TiO₂–Al₂O₃ oxide supported catalysts was studied in an integral reactor close to industrial practice. Activity studies were carried out with Maya crude hydrodesulfurization (HDS), hydrodemetallization (HDM), hydrodenitrogenation (HDN), and hydrodeasphaltenization (HDAs) reactions. The effect of support composition, the method of TiO₂ incorporation, and the catalyst deactivation are examined. Supported catalysts are characterized by BET specific surface area (SSA), pore volume (PV), pore size distribution (PSD), and atomic absorption. It has been found that sulfided catalysts showed a wide range of activity variation with TiO₂ incorporation into the alumina, which confirmed that molybdenum sulfided active phases strongly depend on the nature of support. The pore diameter and nature of the active site for HDS, HDM, HDN, and HDAs account for the influence of the large reactant molecules restricted diffusion into the pore, and/or the decrease in the number of active sites due to the MoS₂ phases buried with time-on-stream. The textural properties and hysteresis loop area of supported and spent catalysts indicated that catalysts were deactivated at the pore mouth due to the metal and carbon depositions. The atomic absorption results agreed well regarding the textural properties of spent catalysts. Thus, incorporation of TiO₂ with γ-Al₂O₃ alters the nature of active metal interaction with support, which may facilitate the dispersion of active phases on the support surface. Therefore, the TiO₂ counterpart plays a promoting role to HDS activity due to the favorable morphology of MoS₂ phases and metal support interaction.     

Hydrogenation of naphthalene on NiMo- Ni- and Ru/Al2O3 catalysts: Langmuir–Hinshelwood kinetic modelling

The importance of the hydrodearomatisation (HDA) is increasing together with tightening legislation of fuel quality and exhaust emissions. The present study focuses on hydrogenation (HYD) kinetics of the model aromatic compound naphthalene, found in typical diesel fraction, in n-hexadecane over a NiMo (nickel molybdenum), Ni (nickel) and Ru (ruthenium) supported on trilobe alumina (Al₂O₃) catalysts. Kinetic reaction expressions based on the mechanistic Langmuir–Hinshelwood (L–H) model were derived and tested by regressing the experimental data that translated the effect of both naphthalene and hydrogen concentration at a constant temperature (523.15 and 573.15 K over the NiMo catalyst and at 373.15 K over the Ni and Ru/Al₂O₃ catalysts) on the initial reaction rate. The L–H equation, giving an adequate fit to the experimental data with physically meaningful parameters, suggested a competitive adsorption between hydrogen and naphthalene over the presulphided NiMo catalyst and a non-competitive adsorption between these two reactants over the prereduced Ni and Ru/Al₂O₃ catalysts. In addition, the adsorption constant values indicated that the prereduced Ru catalyst was a much more active catalyst towards naphthalene HYD than the prereduced Ni/Al₂O₃ or the presulphided NiMo/Al₂O₃ catalyst.     

ZrO2/SiO2- and La2O3/Al2O3-supported platinum catalysts for CH4/CO2 reforming

Surface-phase ZrO₂ on SiO₂ (SZrOs) and surface-phase La₂O₃ on Al₂O₃ (SLaOs) were prepared with various loadings of ZrO₂ and La₂O₃, characterized and used as supports for preparing Pt/SZrOs and Pt/SLaOs catalysts. CH₄/CO₂ reforming over the Pt/SZrOs and Pt/SLaOs catalysts was examined and compared with Pt/Al₂O₃ and Pt/SiO₂ catalysts. CO₂ or CH₄ pulse reaction/adsorption analysis was employed to elucidate the effects of these surface-phase oxides.

The zirconia can be homogeneously dispersed on SiO₂ to form a stable surface-phase oxide. The lanthana cannot be spread well on Al₂O₃, but it forms a stable amorphous oxide with Al₂O₃. The Pt/SZrOs and Pt/SLaOs catalysts showed higher steady activity than did Pt/SiO₂ and Pt/Al₂O₃ by a factor of three to four. The Pt/SZrOs and Pt/SLaOs catalysts were also much more stable than the Pt/SiO₂ and Pt/Al₂O₃ catalysts for long stream time and for reforming temperatures above 700 °C. These findings were attributed to the activation of CO₂ adsorbed on the basic sites of SZrOs and SLaOs.     

Ni/Al_2O_3催化剂的CO_2-TPD表征

Ni/Al_2O_3催化剂是甲烷二氧化碳重整反应制取合成气研究最多、最具应用潜力的一种催化剂。通过对催化剂进行CO_2-TPD研究,考察还原态Ni/Al_2O_3催化剂的CO_2脱附特性。结果表明,浸渍法制备的Ni/Al_2O_3催化剂CO_2脱附曲线呈现双峰,分别在(60~65)℃和(350~380)℃出现高低温两个活性位;高温CO_2吸附量为3.0 cm~3·g~(-1),低温CO_2吸附量为24.0 cm~3·g~(-1)。催化剂的CO_2吸附量与其Ni含量无关。考察选用不同载体的CO_2脱附行为,发现以Al_2O_3为载体的催化剂CO_2吸附量是MgO和SiO_2为载体催化剂的2~4倍,以TiO_2为载体的催化剂几乎不吸附CO_2。     

Characterization of Ni---W/A12O3-SiO2 aromatics saturation catalysts used in a one-year commercial HDS run

A series of Ni---W/A1₂O₃-SiO₂ catalysts with different A1₂O₃/SiO₂ ratios were prepared and loaded in a commercial HDS unit for a year. The catalytic properties of the freshly sulfided and spent catalysts were investigated by performing structural analyses and model test reactions. The aggregation of the WS₂ slabs in the lateral direction, which was observed by EXAFS and TEM, was a major cause of the catalyst deactivation. The addition of SiO₂ into the catalyst support was found to suppress the structural changes of the catalyst.     

Investigation of CoNiMo/Al2O3 catalysts: Relationship between H2S adsorption and HDS activity

Sulfidation of trimetallic CoNiMo/Al₂O₃ catalysts was studied by thermogravimetry at 400 °C under flow and pressure conditions. Results were compared with those obtained on prepared and industrial CoMo/Al₂O₃ and NiMo/Al₂O₃ catalysts. The amount of sorbed H₂S on the sulfided solids was measured at 300 °C in the H₂S pressure range 0–3.5 MPa at constant H₂ pressure (3.8 MPa). The adsorption isotherms were simulated using a model featuring dissociated adsorption of H₂S on supported metal sulfides and bare alumina. The amount of sulfur-vacancy sites could thus be determined under conditions close to industrial practice. A relationship with activity results for thiophene HDS and benzene hydrogenation was sought for.     

Catalytic removal of perchloroethylene (PCE) over supported chromium oxide catalysts

The oxidation of perchloroethylene (PCE) was investigated over chromium oxide catalysts supported on SiO₂, SiO₂–Al₂O₃, activated carbon, mordenite type zeolites, MgO, TiO₂ and Al₂O₃. Supported chromium oxide catalysts were more active than any other metal oxide catalysts including noble metal examined in the present study. PCE removal activity of chromium oxide catalysts mainly depended on the type of supports and the content of metal loaded on the catalyst surface. TiO₂ and Al₂O₃ containing high surface areas were effective for the high performance of PCE removal, since the formation of well dispersed Cr(VI) active reaction sites for the present reaction system, was enhanced even for the high Cr loading on the catalyst surface. CrO_x catalysts supported on TiO₂ and Al₂O₃ also exhibited stable PCE removal activity at a low feed concentration of PCE of 30 ppm up to 100 h at 350°C. However, significant catalyst deactivation was observed at high PCE concentration of 10 000 ppm. CrO_x/TiO₂ revealed stronger water tolerance than CrO_x/Al₂O₃ due to the surface hydrophobicity.     

Catalytic activities of Co(Ni)Mo/TiO2–Al2O3 catalysts in gasoil and thiophene HDS and pyridine HDN: effect of the TiO2–Al2O3 composition

The effect of the TiO₂–Al₂O₃ mixed oxide support composition on the hydrodesulfurization (HDS) of gasoil and the simultaneous HDS and hydrodenitrogenation (HDN) of gasoil+pyridine was studied over two series of CoMo and NiMo catalysts. The intrinsic activities for gasoil HDS and pyridine HDN were significantly increased by increasing the amount of TiO₂ into the support, and particularly over rich- and pure-TiO₂-based catalysts. It is suggested that the increase in activity be due to an improvement in reducing and sulfiding of molybdena over TiO₂. The inhibiting effect of pyridine on gasoil HDS was found to be similar for all the catalysts, i.e., was independent of the support composition. The ranking of the catalysts for the gasoil HDS test differed from that obtained for the thiophene test at different hydrogen pressures. In the case of gasoil HDS, the activity increases with TiO₂ content and large differences are observed between the catalysts supported on pure Al₂O₃ and pure TiO₂. In contrast, in the case of the thiophene test, the pure Al₂O₃-based catalyst appeared relatively more active than the catalysts supported on mixed oxides. Also, in the thiophene test the difference in intrinsic activity between the pure Al₂O₃-based catalyst appeared relatively more active than the catalysts supported on mixed oxides. Also in the thiophene test, the difference in intrinsic activity between the pure Al₂O₃- and pure TiO₂-based catalysts is relatively small and dependent on the H₂ pressure used. Such differences in activity trend among the gasoil and the thiophene tests are due to a different sensitivity of the catalysts (by different support or promoter) to the experimental conditions used. The results of the effect of the H₂ partial pressure on the thiophene HDS, and on the effect of H₂S concentration on gasoil HDS demonstrate the importance of these parameters, in addition to the nature of the reactant, to perform an adequate catalyst ranking.     

A study on the preparation of supported metal oxide catalysts using JRC-reference catalysts. I. Preparation of a molybdena–alumina catalyst. Part 1. Surface area of alumina

This is the first report of a group study on the preparation of a MoO₃/Al₂O₃ catalyst to find predominant preparation parameters for better and reproducible catalyst preparations. Variously prepared MoO₃/Al₂O₃ catalysts possessing 13 wt% MoO₃ were subjected to multiprong characterizations and catalytic tests. It was found that the surface area of the support was the most predominant preparation parameter for the dispersion of Mo oxide species; the dispersion increased as the surface area of the support increased. The formation of crystalline MoO₃ was observed at a surface Mo concentration higher than 3.2 Mo nm⁻². With sulfided MoO₃/Al₂O₃, it was established that the dispersion of Mo sulfide species increased with increasing surface area of the support and was in proportion to that of Mo oxide precursor species. The hydrodesulfurization activity of sulfided MoO₃/Al₂O₃ was proportional to the NO adsorption capacity. It is suggested that a homogeneous distribution of Mo oxide species is attained by an equilibrium adsorption technique. However, it was revealed that the surface area of the catalyst and Mo distribution were considerably modified by preparation parameters, such as drying processes, other than the surface area.     

Deep HDS over NiMo/Zr-SBA-15 catalysts with varying MoO3 loading

In the present work, with the aim of searching for new, highly effective catalysts for deep HDS, a series of NiMo catalysts with different MoO₃ loadings (6–30 wt.%) was prepared using SBA-15 material covered with ZrO₂-monolayer as a support. Prepared catalysts were characterized by N₂ physisorption, small- and wide-angle XRD, UV–vis diffuse reflectance spectroscopy, temperature-programmed reduction, SEM-EDX and HRTEM, and their catalytic activity was evaluated in the 4,6-dimethyldibenzothiophene hydrodesulfurization (HDS). It was observed that ZrO₂ incorporation on the SBA-15 surface improves the dispersion of the Ni-promoted oxidic and sulfided Mo species, which were found to be highly dispersed, up to 18 wt.% of MoO₃ loading. Further increase in metal charge resulted in the formation of MoO₃ crystalline phase and an increase in the stacking degree of the MoS₂ particles. All NiMo catalysts supported on ZrO₂-modified SBA-15 material showed high activity in HDS of 4,6-DMDBT. The best catalyst having 18 wt.% MoO₃ and 4.5 wt.% NiO was almost twice more active than the reference NiMo/γ-Al₂O₃ catalyst. High activity of NiMo/Zr-SBA-15 catalysts and its evolution with metal loading was related to the morphological characteristics of the MoS₂ active phase determined by HRTEM.     

Preferential oxidation of CO over CuO/CeO2 and Pt-Co/Al2O3 catalysts in micro-channel reactors

Micro-channel plates with dimension of 1 mm × 0.3 mm × 48 mm were prepared by chemical etching of stainless steel plates followed by wash coating of CeO₂ and Al₂O₃ on the channels. After coating the support on the plate, Pt, Co, and Cu were added to the plate by incipient wetness method. Reaction experiments of a single reactor showed that the micro-channel reactor coated with CuO/CeO₂ catalyst was highly selective for CO oxidation while the one coated with Pt-Co/Al₂O₃ catalyst was highly active for CO oxidation. The 7-layered reactors coated with two different catalysts were prepared by laser welding and the performances of each reactor were tested in large scale of PROX conditions. The multi-layered reactor coated with Pt-Co/Al₂O₃ catalyst was highly active for PROX and the outlet concentration of CO gradually increased with the O₂/CO ratio due to the oxidation of H₂ which maintained the reactor temperature. The multi-layered reactor coated with CuO/CeO₂ showed lower catalytic activity than that coated with Pt catalyst, but its selectivity was not changed with the increase of O₂/CO ratios due to the high selectivity. In order to combine advantages (high activity and high selectivity) of the two individual catalysts (Pt-Co/Al₂O₃, CuO/CeO₂), a serial reactor was prepared by connecting the two multi-layered micro-channel reactors with different catalysts. The prepared serial reactor exhibited excellent performance for PROX.     

助剂Ba对Pd/Al_2O_3和Pt/Al_2O_3催化剂的C1-C3烷烃催化燃烧性能的影响

通过浸渍法制备了Al_2O_3负载的Pd和Pt催化剂,考察催化剂的甲烷、乙烷和丙烷催化燃烧活性,以及助剂Ba对催化性能的影响。对于Pd/Al_2O_3催化剂,加入Ba使活性物种PdO颗粒变大和还原温度升高,形成更稳定的PdO活性物种,是Pd-Ba/Al_2O_3催化剂活性提升的主要原因。对于Pt/Al_2O_3催化剂,加入Ba助剂使活性物种Pt0含量降低,PtO_x与Al_2O_3载体相互作用增强,使PtO_x物种更难被还原为Pt~0,导致Pt-Ba/Al_2O_3催化剂活性降低。Pd和Pt催化剂催化烷烃氧化反应活性规律一致:丙烷乙烷甲烷。Pd/Al_2O_3催化剂有利于C—H键活化,Pt/Al_2O_3催化剂有利于C—C键活化。Pt/Al_2O_3催化剂对C1-C3烷烃氧化活性的差别明显大于Pd/Al_2O_3催化剂。Pt/Al_2O_3催化剂对碳比例高的烷烃活性更高。     

Comparison of catalytic activity and selectivity of Pd/(OSC + Al2O3) and (Pd + OSC)/Al2O3 catalysts

The effect of the Pd addition method into the fresh Pd/(OSC + Al₂O₃) and (Pd + OSC)/Al₂O₃ catalysts (OSC material = Ce_xZr_1−xO₂ mixed oxides) was investigated in this study. The CO + NO and CO + NO + O₂ model reactions were studied over fresh and aged catalysts. The differences in the fresh catalysts were insignificant compared to the aged catalysts. During the CO + NO reaction, only small differences were observed in the behaviour of the fresh catalysts. The light-off temperature of CO was about 20 °C lower for the fresh Pd/(OSC + Al₂O₃) catalyst than for the fresh (Pd + OSC)/Al₂O₃ catalyst during the CO + NO + O₂ reaction. For the aged catalysts lower NO reduction and CO oxidation activities were observed, as expected. Pd on OSC-containing alumina was more active than Pd on OSC material after the agings. The activity decline is due to a decrease in the number of active sites on the surface, which was observed as a larger Pd particle size for aged catalysts than for fresh catalysts. In addition, the oxygen storage capacity of the aged Pd/(OSC + Al₂O₃) catalyst was higher than that of the (Pd + OSC)/Al₂O₃ catalyst.     

Performance of spent sulfide catalysts in hydrodesulfurization of straight run and nitrogen-removed gas oils

After the test run of several months two kinds of commercial catalysts (NiMo/Al₂O₃ and CoMo/Al₂O₃) were examined in hydrodesulfurization (HDS) of straight run (SRGO) and nitrogen-removed gas oils, at 340 °C under 50 kg/cm² H₂. Hydrogen renewal between stages was attempted to show additional inhibition effects of the by-products such as H₂S and NH₃. Spent NiMo/Al₂O₃ and CoMo/Al₂O₃ catalysts showed contrasting activities in HDS and susceptibility to nitrogen species, according to their catalytic natures, compared to those of their virgin ones. HDS over spent NiMo/Al₂O₃ was significantly improved by removal of nitrogen species, while that over spent CoMo/Al₂O₃ was much improved by H₂ refreshment. The activity for refractory sulfur species such as 4,6-dimethyldibenzothiophene was reduced more severely than that for the reactive sulfur species such as benzothiophenes over spent catalysts. The effects of both two-stage hydrodesulfurization and nitrogen-removal were markedly reduced over the spent NiMo when compared with those over virgin NiMo one. The acidity of the catalysts was correlated with the inhibition susceptibility by nitrogen species as well as H₂S and NH₃. Spent catalysts apparently lost their activity due to the carbon deposition, which covered the active sites more preferentially. The spent NiMo catalyst carried more deposited carbon with larger C/H ratio and nitrogen content. Higher acidity was found to be present on the NiMo catalyst, but this was greatly decreased by the carbon deposition. Additionally, the reactivity of nitrogen species in HDS was briefly discussed in relation to the acidity of the catalyst and its deactivation by carbon deposition.     

HDS and HDN activity of molybdenum and nickel–molybdenum catalysts supported on alumina–titania carriers

Alumina–titania supports containing 5–50 wt.% of TiO₂ were prepared by coprecipitation method using inorganic precursors (sodium aluminate and titanium chloride). DTA-TGA, XRD, SEM, TPD_NH3, and IR spectroscopy were used to characterise these materials. The study shows that the promoting effect of nickel on the HDS activity of molybdenum catalysts supported on Al₂O₃TiO₂ is significantly lower than that for molybdenum catalyst supported on Al₂O₃, and depends on the TiO₂ content. The SEM results show that in the case of rich Al support (20 wt.% of TiO₂) molybdenum was aggregated on the external surface of the catalyst, whereas it was uniformly dispersed on the external surface of alumina. Results also show that molybdenum is preferably supported on aluminum oxide. Application of Al₂O₃TiO₂ oxides enhances the HDN activity of nickel–molybdenum catalysts. The highest HDN efficiency was obtained for the NiMo/Al₂O₃TiO₂ catalyst containing 50 wt.% of TiO₂. HDN activity was found to depend on protonic acidity and anatase content.     

Fischer–Tropsch synthesis over Re-promoted Co supported on Al2O3, SiO2 and TiO2: Effect of water

The activity and selectivity of rhenium promoted cobalt Fischer–Tropsch catalysts supported on Al₂O₃, TiO₂ and SiO₂ have been studied in a fixed-bed reactor at 483 K and 20 bar. Exposure of the catalysts to water added to the feed deactivates the Al₂O₃ supported catalyst, while the activity of the TiO₂ and SiO₂ supported catalysts increased. However, at high concentrations of water both the SiO₂ and TiO₂ supported catalyst deactivated. Common for all catalysts was an increase in C₅₊ selectivity and a decrease in the CH₄ selectivity by increasing the water partial pressure. The catalysts have been characterized by scanning transmission electron microscope (STEM), BET, H₂ chemisorption and X-ray diffraction (XRD).     

Coke study on MgO-promoted Ni/Al2O3 catalyst in combined H2O and CO2 reforming of methane for gas to liquid (GTL) process

MgO-promoted Ni/Al₂O₃ catalysts have been investigated with respect to catalytic activity and coke formation in combined steam and carbon dioxide reforming of methane (CSCRM) to develop a highly active and stable catalyst for gas to liquid (GTL) processes. Ni/Al₂O₃ catalysts were promoted through varying the MgO content by the incipient wetness method. X-ray diffraction (XRD), BET surface area, H₂-temperature programmed reduction (TPR), H₂-chemisorption and CO₂-temperature programmed desorption (TPD) were used to observe the characteristics of the prepared catalysts. The coke formation and amount in used catalysts were examined by SEM and TGA, respectively. H₂/CO ratio of 2 was achieved in CSCRM by controlling the feed H₂O/CO₂ ratio. The catalysts prepared with 20 wt.% MgO exhibit the highest catalytic performance and have high coke resistance in CSCRM. MgO promotion forms MgAl₂O₄ spinel phase, which is stable at high temperatures and effectively prevents coke formation by increasing the CO₂ adsorption due to the increase in base strength on the surface of catalyst.     

Simultaneous HDS and HDN over supported PtSn catalysts in comparison to commercial NiMo/Al2O3

The performance of platinum-tin catalysts, supported on Al₂O₃ and SiO₂ and subjected to reduction prior to use, has been studied. The catalysts were characterized in reduced forms by X-ray diffraction (XRD) and XPS. The surface properties were determined by N₂ BET specific surface area and CO chemisorption. The model compounds were 4,6-dimethyldibenzothiophene (4,6DMDBT) and carbazole. The PtSn catalysts supported on either Al₂O₃ or SiO₂ were characterised by high activity, but the catalyst PtSn/SiO₂ was found the most effective, even more effective than the commercial KF848 catalyst. Both PtSn catalysts studied were more effective in the reaction of 4,6DMDBT hydrogenation, the dominant product obtained with the use of PtSn/Al₂O₃ was methyl-cyclohexyltoluene (MCHT) and with PtSn/SiO₂ the dominant product was dimethylbicyclohexyl (DMBCH). The amount of dimethylbiphenyl (DMBPh) obtained was small and practically independent of the contact time. In the HDN reaction of carbazole the most active was PtSn/SiO₂. It was also more active in the consecutive reaction of isomerisation of the main product of the HDN reaction, bicyclohexyl (BCH) to methylcyclopentylcyclohexane (MCPCH). The large differences shown in the hydrotreating activity specially in the HDN reaction between PtSn catalysts supported on Al₂O₃ and SiO₂ result from the physicochemical properties of both samples. The significantly higher CO chemisorption for PtSn/SiO₂ indicates the presence of larger amount of metallic species and better hydrogenation properties so important for deep hydrotreating process.