Synthesis of pH‐ and temperature‐responsive chitosan‐graft‐poly[2‐(N,N‐dimethylamino) ethyl methacrylate] copolymer and gold nanoparticle stabilization by its micelles

Novel pH‐ and temperature‐responsive chitosan‐graft‐poly[2‐(N,N‐dimethylamino)ethyl methacrylate] (chitosan‐g‐PDMAEMA) copolymers were successfully synthesized by homogeneous atom transfer radical polymerization (ATRP) under mild conditions. Chitosan macroinitiator was prepared by phthaloylation of amino groups of chitosan and subsequent acylation of hydroxyl groups of chitosan with 2‐bromoisobutyryl bromide. The copolymers were obtained by ATRP of 2‐(N,N‐dimethylamino)ethyl methacrylate and they can self‐assemble into stable micelles in water. Hybrid micelles with a PDMAEMA corona incorporating gold nanoparticles (Au NPs) were prepared in situ via the reduction of HAuCl₄ with NaBH₄. The pH and temperature responses of the copolymer micelles and hybrid micelles were characterized using UV‐visible spectroscopy and dynamic laser light scattering. The morphology of the micelles was observed using transmission electron microscopy and atomic force microscopy. The PDMAEMA corona of the micelles acts as the ‘nanoreactor’ and the ‘anchor’ for the in situ formation and stabilization of Au NPs. Therefore, the spatial distribution of Au NPs within the micelles can be tuned by varying the temperature and pH value. Copyright © 2010 Society of Chemical Industry     

Reactivity ratios and copolymer properties of 2‐(diisopropylamino)ethyl methacrylate with methyl methacrylate and styrene

Free radical copolymerization kinetics of 2‐(diisopropylamino)ethyl methacrylate (DPA) with styrene (ST) or methyl methacrylate (MMA) was investigated and the corresponding copolymers obtained were characterized. Polymerization was performed using tert‐butylperoxy‐2‐ethylhexanoate (0.01 mol dm^?3) as initiator, isothermally (70 °C) to low conversions (<10 wt%) in a wide range of copolymer compositions (10 mol% steps). The reactivity ratios of the monomers were calculated using linear Kelen–Tüd?s (KT) and nonlinear Tidwell–Mortimer (TM) methods. The reactivity ratios for MMA/DPA were found to be r₁ = 0.99 and r₂ = 1.00 (KT), r₁ = 0.99 and r₂ = 1.03 (TM); for the ST/DPA system r₁ = 2.74, r₂ = 0.54 (KT) and r₁ = 2.48, r₂ = 0.49 (TM). It can be concluded that copolymerization of MMA with DPA is ideal while copolymerization of ST with DPA has a small but noticeable tendency for block copolymer building. The probabilities for formations of dyad and triad monomer sequences dependent on monomer compositions were calculated from the obtained reactivity ratios. The molar mass distribution, thermal stability and glass transition temperatures of synthesized copolymers were determined. Hydrophobicity of copolymers depending on the composition was determined using contact angle measurements, decreasing from hydrophobic polystyrene and poly(methyl methacrylate) to hydrophilic DPA. Copolymerization reactivity ratios are crucial for the control of copolymer structural properties and conversion heterogeneity that greatly influence the applications of copolymers as rheology modifiers of lubricating oils or in drug delivery systems. © 2015 Society of Chemical Industry     

Novel poly(methyl methacrylate)‐block‐polyurethane‐block‐poly(methyl methacrylate) tri‐block copolymers through atom transfer radical polymerization

Poly(methyl methacrylate)‐block‐polyurethane‐block‐poly(methyl methacrylate) tri‐block copolymers have been synthesized successfully through atom transfer radical polymerization of methyl methacrylate using telechelic bromo‐terminated polyurethane/CuBr/N,N,N,N″,N″‐pentamethyldiethylenetriamine initiating system. As the time increases, the number‐average molecular weight increases linearly from 6400 to 37,000. This shows that the poly methyl methacrylate blocks were attached to polyurethane block. As the polymerization time increases, both conversion and molecular weight increased and the molecular weight increases linearly with increasing conversion. These results indicate that the formation of the tri‐block copolymers was through atom transfer radical polymerization mechanism. Proton nuclear magnetic resonance spectral results of the triblock copolymers show that the molar ratio between polyurethane and poly (methyl methacrylate) blocks is in the range of 1 : 16.3 to 1 : 449.4. Differential scanning calorimetry results show T_g of the soft segment at ?35°C and T_g of the hard segment at 75°C. © 2008 Wiley Periodicals, Inc. J Appl Polym Sci, 2008     

Synthesis,characterization, and thermal behavior study of methyl methacrylate polymers containing 4‐carbazole substitutes

A new polymerizable monomer, [4‐(9‐ethyl)carbazolyl]methyl methacrylate ( 2 ), was synthesized by reacting of methacrylic acid and 4‐hydroxymethyl‐9‐ethyl carbazole ( 1 ) by esterification procedure in the presence of N,N′‐dicyclohexylcarbodiimide. The resulting monomer was then polymerized free‐radically to form the poly(methyl methacrylate) containing 4‐(9‐ethyl)carbazolyl pend ent groups. Also, copolymerization of monomer 2 with various acrylic monomers such as methyl methacrylate, ethyl methacrylate, methyl acrylate, ethyl acrylate, and n‐butyl acrylate by azobisisobutyronitrile as a free radical polymerization initiator gave the related copolymers in high yields. The structure of all the resulted compounds was characterized and confirmed by FTIR and ¹H NMR spectroscopic techniques. The average molecular weight of the obtained polymers was determined by gel permeation chromatography using tetrahydrofurane as the solvent. The thermal gravimetric analysis and differential scanning calorimeter instruments were used for studying of thermal properties of polymers. It was found that, with the incorporation of bulky 4‐(9‐ethyl)carbazolyl substitutes in side chains of methyl methacrylate polymers, thermal stability and glass transition temperature of polymers are increased. © 2006 Wiley Periodicals, Inc. J Appl Polym Sci 102: 4989–4995, 2006     

Synthesis of Y‐shaped poly(N,N‐dimethylamino‐2‐ethyl methacrylate) and poly(trimethylene carbonate) from a new heterofunctional initiator

A new amphiphilic Y‐shaped copolymer, comprised of hydrophobic Poly(trimethylene carbonate) (PTMC) and hydrophilic Poly(N,N‐dimethylamino‐2‐ethyl methacrylate) (PDMAEMA), was designed and synthesized by a combination of atom transfer radical polymerization (ATRP) and ring‐opening polymerization (ROP) using a new heterofunctional initiator, Br‐Init‐(OH)₂, bearing one initiation site for ATRP and two for ROP. At first, a new trifunctional core molecule bearing hydroxyl group and bromine moieties, Br‐Init‐(OH)₂, was synthesized via protection followed by esterification reaction of 5‐ethyl‐5‐hydroxymethyl‐2,2‐dimethyl‐1,3‐dioxane with 2‐bromoisobutyryl bromide and deprotection. In the presence of trifunctional core molecule, Br‐Init‐(OH)₂, target Y‐shaped miktoarm star copolymers, (PTMC)₂‐ b‐PDMAEMA, were successfully synthesized by sequence conducting the ROP of TMC and ATRP of DMAEMA. The Y‐shaped copolymers were characterized by ¹H NMR and GPC measurements. Subsequently, the self‐assembly behavior of these copolymers was investigated by dynamic light scattering method and transmission electron microscopy, which indicated that these amphiphilic Y‐shaped copolymers can self‐assemble into micelles and possess distinct pH‐dependent size in aqueous milieu. The results indicate that the amphiphilic Y‐shaped copolymers had the pH‐responsive properties similar to the expected PDMAEMA. POLYM. ENG. SCI., 2011. © 2011 Society of Plastics Engineers     

Vesicular and micellar self‐assembly of stimuli‐responsive poly(N‐isopropyl acrylamide‐b‐9‐anthracene methyl methacrylate) amphiphilic diblock copolymers

Dually responsive amphiphilic diblock copolymers consisting of hydrophilic poly(N‐isopropyl acrylamide) [poly(NIPAAm)] and hydrophobic poly(9‐anthracene methyl methacrylate) were synthesized by reversible addition fragmentation chain‐transfer (RAFT) polymerization with 3‐(benzyl sulfanyl thiocarbonyl sulfanyl) propionic acid as a chain‐transfer agent. In the first step, the poly(NIPAAm) chain was grown to make a macro‐RAFT agent, and in the second step, the chain was extended by hydrophobic 9‐anthryl methyl methacrylate to yield amphiphilic poly(N‐isopropyl acrylamide‐b‐9‐anthracene methyl methacrylate) block copolymers. The formation of copolymers with three different hydrophobic block lengths and a fixed hydrophilic block was confirmed from their molecular weights. The self‐assembly of these copolymers was studied through the determination of the lower critical solution temperature and critical micelle concentration of the copolymers in aqueous solution. The self‐assembled block copolymers displayed vesicular morphology in the case of the small hydrophobic chain, but the morphology gradually turned into a micellar type when the hydrophobic chain length was increased. The variations in the length and chemical composition of the blocks allowed the tuning of the block copolymer responsiveness toward both the pH and temperature. The resulting self‐assembled structures underwent thermally induced and pH‐induced morphological transitions from vesicles to micelles and vice versa in aqueous solution. These dually responsive amphiphilic diblock copolymers have potential applications in the encapsulation of both hydrophobic and hydrophilic drug molecules, as evidenced from the dye encapsulation studies. © 2018 Wiley Periodicals, Inc. J. Appl. Polym. Sci. 2018 , 135, 46474.     

Copolymerization of N‐(4‐carboxyphenyl) itaconimide or N‐(4‐carboxyphenyl) itaconamic acid with methyl methacrylate

This paper describes the synthesis and characterization of N‐(4‐carboxyphenyl) itaconamic acid (CPA) and N‐(4‐carboxyphenyl) itaconimide (CPI) obtained by reacting itaconic anhydride with p‐aminobenzoic acid. Structural and thermal characterization of CPA and CPI was done using ¹H‐NMR, FTIR, and differential scanning calorimetry (DSC). Copolymerization of CPA or CPI with methyl methacrylate (MMA) in solution was carried out at 60 °C using azobisisobutyronitrile as an initiator and dimethyl acetamide or THF as solvent. Feed compositions having varying mole fractions of CPA or CPI ranging from 0.05–0.20 or 0.1–0.5 were taken to prepare copolymers. Copolymerizations were terminated at low percentage conversion. Structural characterization of copolymers was done by ¹H‐NMR and elemental analysis. Copolymer composition was determined using percentage nitrogen content. The reactivity ratios were r₁ (MMA) = 0.68 ± 0.06 and r₂ (CPI) = 0.46 ± 0.06. The intrinsic viscosity [η] was determined using an Ubbelohde suspension level viscometer. [η] decreased with increasing mole fraction of N‐(p‐carboxyphenyl) itaconimide or N‐(p‐carboxyphenyl) itaconamic acid in copolymers. Glass transition temperature and thermal stability of the copolymers were determined using DSC and thermogravimetric analysis, respectively. The glass transition temperature (T_g) as determined from DSC scans increased with increasing amounts of CPA or CPI in copolymers. A significant improvement in the char yield was observed upon copolymerization. © 2005 Wiley Periodicals, Inc. J Appl Polym Sci 98: 1909–1915, 2005     

Copolymerization and thermal behavior of methyl methacrylate with N‐(phenyl/p‐tolyl) itaconimides

This study describes the synthesis, characterization, and thermal behavior of copolymers of methyl methacrylate (MMA) and N‐p‐tolyl itaconimide (PTI)/N‐phenyl itaconimide (I). Homopolymerization and copolymerization of N‐(phenyl/p‐tolyl) itaconimide with MMA was carried out by use of various mole fractions of N‐aryl itaconimide in the initial feed from 0.1 to 0.5, using azobisisobutyronitrile as an initiator and tetrahydrofuran as the solvent. The copolymer composition was determined by ¹H‐NMR spectroscopy using the proton resonance signals attributed to –OCH₃ of MMA (δ = 3.5–3.8 ppm) and the aromatic protons (δ = 7.0–7.5 ppm) of N‐aryl itaconimide. The reactivity ratios of the monomers were found to be r₁ (PTI) = 1.33 ± 0.05/r₂ (MMA) = 0.24 ± 0.03 and r₁ (I) = 1.465 ± 0.035/r₂ (MMA) = 0.385 ± 0.005. The molecular weight of the copolymers decreased with increasing mole fraction of N‐aryl itaconimide in the copolymers. Glass‐transition temperature (T_g) and thermal stability of PMMA increased with increasing amounts of itaconimides in the polymer backbone. A significant increase in the percentage char yield at 700°C was observed on incorporation of a low mole fraction of N‐aryl itaconimides. © 2003 Wiley Periodicals, Inc. J Appl Polym Sci 89: 1195–1202, 2003     

Atom transfer radical copolymerization of glycidyl methacrylate and methyl methacrylate

Glycidyl methacrylate (GMA) and methyl methacrylate (MMA) copolymers were synthesized by atom transfer radical polymerization (ATRP). The effect of different molar fractions of GMA, ranging from 0.28 to 1.0, on the polymer polydispersity index (weight‐average molecular weight/number‐average molecular weight) as the indicator of a controlled process was investigated at 70°C, with ethyl 2‐bromoisobutyrate as an initiator and 4,4′‐dinonyl‐2,2′‐bipyridyne (dNbpy)/CuBr as a catalyst system in anisole. The monomer reactivity ratios (r values) were obtained by the application of the conventional linearization Fineman–Ross method (r_GMA = 1.24 ± 0.02 and r_MMA = 0.85 ± 0.03) and by the Mayo–Lewis method (r_GMA = 1.19 ± 0.04 and r_MMA = 0.86 ± 0.03). The molecular weights and polydispersities of the copolymers exhibited a linear increase with GMA content. The copolymer compositions were determined by ¹H‐NMR and showed a domination of syndiotactic structures. The glass‐transition temperatures (T_g) of the copolymers analyzed by differential scanning calorimetry (DSC) decreased in the range 105–65°C with increasing GMA units. © 2011 Wiley Periodicals, Inc. J Appl Polym Sci, 2012     

Free radical copolymerization of N,N‐dimethylaminoethyl methacrylate with styrene and methyl methacrylate: monomer reactivity ratios and glass transition temperatures

BACKGROUND: The properties of copolymers depend strongly on their composition; therefore in order to tailor some for specific applications, it is necessary to control their synthesis, and, in particular, to know the reactivity ratios of their constituent monomers. Free radical copolymerizations of N,N‐dimethylaminoethyl methacrylate (DMAEM) with styrene (ST) and methyl methacrylate (MMA) in toluene solution using 1‐di(tert‐butylperoxy)‐3,3,5‐trimethylcyclohexane as initiator at 70 °C were investigated. Monomer reactivity ratios were determined for low conversions using both linear and nonlinear methods. RESULTS: For the DMAEM/ST system the average values are r₁ = 0.43 and r₂ = 1.74; for the DMAEM/MMA system the average values are r₁ = 0.85 and r₂ = 0.86. The initial copolymerization rate, R_p, for DMAEM/ST sharply decreases as the content of ST in the monomer mixture increases up to 30 mol% and then attains a steady value. For the DMAEM/MMA copolymerization system the composition of the feed does not have a significant influence on R_p. The glass transition temperatures (T_g) of the copolymers were determined calorimetrically and calculated using Johnston's sequence length method. A linear dependence of T_g on copolymer composition for both systems is observed: T_g increases with increasing ST or MMA content. CONCLUSION: Copolymerization reactivity ratios enable the design of high‐conversion processes for the production of copolymers of well‐defined properties for particular applications, such as the improvement of rheological properties of lubricating mineral oils. Copyright © 2009 Society of Chemical Industry     

Copolymerization of N‐aryl substituted itaconimide with methyl methacrylate: Effect of substituents on monomer reactivity ratio and thermal behavior

The article describes the synthesis and characterization of N‐(4‐methoxy‐3‐chlorophenyl) itaconimide (MCPI) and N‐(2‐methoxy‐5‐chlorophenyl) itaconimide (OMCPI) obtained by reacting itaconic anhydride with 4‐methoxy‐3‐chloroanisidine and 2‐methoxy‐5‐chloroanisidine, respectively. Structural and thermal characterization of MCPI and OMCPI monomers was done by using ¹H NMR, FTIR, and differential scanning calorimetry (DSC). Copolymerization of MCPI or OMCPI with methyl methacrylate (MMA) in solution was carried out at 60°C using AIBN as an initiator and THF as solvent. Feed compositions having varying mole fractions of MCPI and OMCPI ranging from 0.1 to 0.5 were taken to prepare copolymers. Copolymerizations were terminated at low percentage conversion. Structural characterization of copolymers was done by FTIR, ¹H NMR, and elemental analysis and percent nitrogen content was used to calculate the copolymer composition. The monomer reactivity ratios for MMA–MCPI copolymers were found to be r₁ (MMA) = 0.32 ± 0.03 and r₂ (MCPI) = 1.54 ± 0.05 and that for MMA–OMCPI copolymers were r₁ (MMA) = 0.15 ± 0.02 and r₂ (OMCPI) = 1.23 ± 0.18. The intrinsic viscosity [η] of the copolymers decreased with increasing mole fraction of MCPI/or OMCPI. The glass transition temperature as determined from DSC scans was found to increase with increasing amounts of OMPCI in copolymers. A significant improvement in the char yield as determined by thermogravimetry was observed upon copolymerization. © 2006 Wiley Periodicals, Inc. J Appl Polym Sci 101: 2391–2398, 2006     

Structural estimation of particle arrays at air–water interface based on silica particles with well‐defined and highly grafted poly(methyl methacrylate)

Silica nanoparticles with well‐defined, highly grafted dense poly(methyl methacrylate) (MMA) were prepared by surface‐initiated activators regenerated by electron transfer for atom transfer radical polymerization (ARGET ATRP) of methyl methacrylate with an initiator‐fixed silica particle in the presence of air. Two different polymerizations of MMA were carried out under the same conditions using tris[2‐(dimethylamino)ethyl]amine (Me₆TREN) and N,N,N′,N′,N″‐pentamethyldiethylene‐triamine (PMDETA) as the ligand, respectively. In the CuCl₂/PMDETA system, polymerization appeared to be more controlled with a lower polydisperisty compared with the CuCl₂/Me₆TREN system. The monolayer of these particles was formed at the air–water interface using Langmuir‐Blodgett (LB) technique. Multilayers of the particles were fabricated by repetition of LB depositing. A surface pressure–area (π–A) measurement and SEM observation were used to characterize the particle arrays. POLYM. ENG. SCI., 2010. © 2009 Society of Plastics Engineers     

Synthesis and characterization of poly(dimethylamino ethyl methacrylate)–poly(ethylene oxide)–poly(dimethylamino ethyl methacrylate) triblock copolymers

Novel, monodispersed, and well‐defined ABA triblock copolymers [poly(dimethylamino ethyl methacrylate)–poly(ethylene oxide)–poly(dimethylamino ethyl methacrylate)] were synthesized by oxyanionic polymerization with potassium tert‐butanoxide as the initiator. Gel permeation chromatography and ¹H‐NMR analysis showed that the obtained products were the desired copolymers with molecular weights close to calculated values. Because the poly(dimethylamino ethyl methacrylate) block was pH‐ and temperature‐sensitive, the aqueous solution behavior of the polymers was investigated with ¹H‐NMR and dynamic light scattering techniques at different pH values and at different temperatures. The micelle morphology was determined with transmission electron microscopy. © 2009 Wiley Periodicals, Inc. J Appl Polym Sci, 2009     

Free‐radical copolymerization and kinetic treatment of methyl methacrylate with N‐P‐tolylmaleimide

The free‐radical copolymerization of methyl methacrylate (MMA) with N‐P‐tolylmalemide (NPTMI) at 77°C in cyclohexanone solution initiated by AIBN was studied. The copolymer composition was calculated from the nitrogen content estimated by the Mico–Kijedldahl's method and by elemental analysis. The reactivity ratios have been calculated by Fineman and Ross method. The monomer reactivity ratios were r_NPTMI = 1.24, r_MMA = 2.1. The glass transition temperature (T_g) of the copolymers were determined by torsion braid analysis (TBA). The thermal stability was determined by thermogravimetric analysis (TGA). T₅₀, temperature at which the weight loss reaches 50%, was abstained. The results showed that the M _n and M _w increased, whereas the NPTMI feed content increased. The T_g and T₅₀ increased dramatically. © 2003 Wiley Periodicals, Inc. J Appl Polym Sci 91: 867–870, 2004     

Synthesis of methyl methacrylate and N‐aryl itaconimide block copolymers via atom‐transfer radical polymerization

The paper describes the synthesis of block copolymers of methyl methacrylate (MMA) and N‐aryl itaconimides using atom‐transfer radical polymerization (ATRP) via a poly(methyl methacrylate)–Cl/CuBr/bipyridine initiating system or a reverse ATRP AIBN/FeCl₃·6H₂O/PPh₃ initiating system. Poly(methyl methacrylate) (PMMA) macroinitiator, ie with a chlorine chain‐end (PMMA‐Cl), having a predetermined molecular weight (M_n = 1.27 × 10⁴ g mol^?1) and narrow polydispersity index (PDI = 1.29) was prepared using AIBN/FeCl₃·6H₂O/PPh₃, which was then used to polymerize N‐aryl itaconimides. Increase in molecular weight with little effect on polydispersity was observed on polymerization of N‐aryl itaconimides using the PMMA‐Cl/CuBr/Bpy initiating system. Only oligomeric blocks of N‐aryl itaconimides could be incorporated in the PMMA backbone. High molecular weight copolymer with a narrow PDI (1.43) could be prepared using tosyl chloride (TsCl) as an initiator and CuBr/bipyridine as catalyst when a mixture of MMA and N‐(p‐chlorophenyl) itaconimide in the molar ratio of 0.83:0.17 was used. Thermal characterization was performed using differential scanning calorimetry (DSC) and dynamic thermogravimetry. DSC traces of the block copolymers showed two shifts in base‐line in some of the block copolymers; the first transition corresponds to the glass transition temperature of PMMA and second transition corresponds to the glass transition temperature of poly(N‐aryl itaconimides). A copolymer obtained by taking a mixture of monomers ie MMA:N‐(p‐chlorophenyl) itaconimide in the molar ratio of 0.83:0.17 showed a single glass transition temperature. Copyright © 2005 Society of Chemical Industry     

Rapid removal of Cr(VI) ions from aqueous solutions by the macroporous poly(N,N′‐dimethylamino ethyl methacrylate) hydrogels

To improve the adsorption ability of hexavalent chromium [Cr(VI)], the macroporous poly(N, N′‐dimethylamino ethyl methacrylate) [poly(DMAEMA)] hydrogels were successfully fabricated by free‐radical copolymerization in ethanol/water mixture using N, N′‐dimethylamino ethyl methacrylate (DMAEMA) as the monomer, N, N′‐methylenebisacrylamide (MBAA) as the cross‐linker, and Na₂SO₄ solution as the porogen. The effects of various parameters, such as the concentration of Na₂SO₄ solutions, the dosage of MBAA, pH values, adsorption kinetic, and isotherm curves, were all investigated through systematic experiments. Scanning electron microscope (SEM) was employed to characterize the various pore structures. The experimental results showed that the influence of Na₂SO₄ solution to the pore morphology in the matrix was significant. The poly(DMAEMA) hydrogels can effectively adsorb Cr(VI) ions in aqueous media, and the macroporous structures could obvious improve the response rate and adsorption capacity. These results prove that the macroporous poly(DMAEMA) gels can be treated as a potential material for environmental pollution control. © 2012 Wiley Periodicals, Inc. J. Appl. Polym. Sci., 2013     

Synthesis and characterization of N‐acryloylcarbazole/methyl methacrylate copolymers

Copolymers of N‐acryloylcarbazole (A) and methyl methacrylate (M) were synthesized in different in‐feed ratios. The composition of the copolymer was determined by the help of ¹H NMR spectrum. The comonomer reactivity ratios determined by Kelen‐Tudos (KT) and nonlinear error‐in‐variables methods were r_A = 1.12 ± 0.16, r_M = 0.94 ± 0.14, and r_A = 1.05, r_M = 0.90, respectively. Complete spectral assignments of the ¹H and ¹³C ¹H NMR spectra of the copolymers were done by the help of distortionless enhancement by polarization transfer (DEPT) and two‐dimensional NMR techniques, such as heteronuclear single quantum coherence (HSQC), total correlation spectroscopy (TOCSY), and heteronuclear multiple bond correlation (HMBC). The methine, α‐methyl, and carbonyl carbon resonances were found to be sequence sensitive. The signals obtained were broad because of the restricted rotation of bulky carbazole group and the quadrupolar effect of nitrogen present in carbazole moiety. Glass transition temperatures (T_g) were determined by differential scanning calorimetry and were found to be characteristic of copolymer composition. As the N‐acryloylcarbazole content increases, the T_g increases from 378.3 K for poly(methyl methacrylate) to 430.4 K for poly(N‐acryloylcarbazole). Variation in T_g with the copolymer composition were found to be in good agreement with theoretical values obtained from Johnston and Barton equations. © 2006 Wiley Periodicals, Inc. J Appl Polym Sci 100: 2667–2676, 2006     

Synthesis of poly(epichlorohydrin‐g‐methyl methacrylate) and poly(epichlorohydrin‐g‐styrene) graft copolymers by a combination of cationic and photopolymerization methods

Poly(epichlorohydrin‐g‐styrene) and poly (epichlorohydrin‐g‐methyl methacrylate) graft copolymers were synthesized by a combination of cationic and photoinitiated free‐radical polymerization. For this purpose, first, epichlorohydrin was polymerized with tetrafluoroboric acid (HBF₄) via a cationic ring‐opening mechanism, and, then, polyepichlorohydrin (PECH) was reacted ethyl‐hydroxymethyl dithio sodium carbamate to obtain a macrophotoinitiator. PECH, possessing photolabile thiuram disulfide groups, was used in the photoinduced polymerization of styrene or methyl methacrylate to yield the graft copolymers. The graft copolymers were characterized by ¹H‐NMR spectroscopy, differential scanning calorimetry, and gel permeation chromatography. © 2007 Wiley Periodicals, Inc. J Appl Polym Sci, 2008     

Synthesis of well‐defined comb‐like amphiphilic copolymers with protonizable units in the pendent chains: 2. Poly(2‐(dimethylamino)ethyl methacrylate) grafted poly(methyl methacrylate‐co‐2‐hydroxyethyl methacrylate) copolymers and their association behavior in aqueous solution

Narrow‐distribution, well‐defined comb‐like amphiphilic copolymers are reported in this work. The copolymers are composed of poly(methyl methacrylate‐co‐2‐hydroxyethyl methacrylate) (P(MMA‐co‐HEMA)) as the backbones and poly(2‐(dimethylamino)ethyl methacrylate) (PDMAEMA) as the grafted chains, with the copolymer backbones being synthesized via atom‐transfer radical polymerization (ATRP) and the grafted chains by oxyanionic polymerization. The copolymers were characterized by gel permeation chromatography (GPC), Fourier‐transform infrared (FT‐IR) spectroscopy and ¹H NMR spectroscopy. The aggregation behavior in aqueous solutions of the comb‐like amphiphilic copolymers was also investigated. ¹H NMR spectroscopic and surface tension measurements all indicated that the copolymers could form micelles in aqueous solutions and they possessed high surface activity. The results of dynamic light scattering (DLS) and scanning electron microscopy (SEM) investigations showed that the hydrodynamic diameters of the comb‐like amphiphilic copolymer aggregates increased with dilution. Because of the protonizable properties of the graft chains, the surface activity properties and micellar state can be easily modulated by variations in pH. Copyright © 2004 Society of Chemical Industry