涂层开裂对几种热喷涂涂层抗蚀效果的影响

研究了涂层开裂对高速火焰喷涂Ni-Cr/Cr3C2、高速火焰喷涂Ni60B/WC、高速电弧喷涂Fe-Al/Cr3C2、高速电弧喷涂FeCrAl四种涂层抗蚀效果的影响.研究结果表明,涂层开裂导致不同涂层的抗蚀效果有不同程度的下降;基体暴露在外进而被腐蚀是抗蚀效果下降的主要原因;基体被暴露的面积不同是抗蚀效果下降程度不同的直接原因.和涂层开裂和涂层抗蚀效果的影响的研究有待于进一步深入.     

高速火焰喷涂Fe-Al/Cr3C2复合涂层抗高温腐蚀性能研究

利用高速火焰喷涂方法,选用自主研发的Fe-Al/Cr3C2喷涂粉材,在20钢基体上制备Fe-Al/Cr3C2复合涂层。研究了复合涂层在650℃的抗高温腐蚀性能。采用SEM,XRD,EDS等先进测试手段分析了复合涂层的抗高温腐蚀机理。结果表明：Fe-Al/Cr3C2复合涂层在650℃的抗高温腐蚀性能明显优于基体20钢,并且优于Fe-Al涂层,其腐蚀动力学曲线呈抛物线变化;复合涂层经腐蚀后,内层生成的致密Al2O3及Cr2O3阻止了高温腐蚀的进一步深入。现场应用表明,Fe-Al/Cr3C2复合涂层具有广泛的应用前景。     

高速电弧喷涂Fe-Al/Cr3C2复合涂层的组织与性能

采用Fe-Al/Cr3C2粉芯丝材和高速电弧喷涂技术(HVAS)原位合成了铁铝金属间化合物涂层,并研究了涂层的显微组织与性能.结果表明,高速电弧喷涂Fe-Al/Cr3C2涂层中生成了多种物相,主要是Fe3Al和FeAl相,同时还包括Fe3C硬质点相及FeO*Al2O3和Cr2O3氧化物相等.涂层具有很高的热震结合强度及相对基体较高的显微硬度,密度和孔隙率较低.     

纳米TiC对高速电弧喷涂FeNiTi/Cr3C2涂层组织与性能的影响

研制适用于火电厂超临界锅炉管道抗高温冲蚀的FeNiTi/Cr3C2高速电弧喷涂材料,研究了纳米TiC对于高速电弧喷涂层组织与性能的影响。结果表明:FeNiTi/Cr3C2涂层基体相结构为含Cr、Ti元素的Fe-Ni基固溶体;添加纳米TiC可以明显提高涂层的硬度、内聚强度和结合强度;涂层表现出了良好的抗热腐蚀性能,腐蚀时间超过50h,达到20钢的15倍;添加纳米TiC的FeNiTi/Cr3C2涂层具有优良的抗高温冲蚀性能。     

低碳钢表面电弧喷涂层FeNiCr/Cr_3C_2与NiCrTi的热腐蚀性能

采用高速电弧喷涂工艺在低碳钢基体表面制备了FeNiCr/Cr3C2和NiCrTi两种电弧喷涂涂层。通过光学显微镜对涂层的显微组织进行了观察研究。试验选用摩尔比为7：3的Na2SO4＋K2SO4饱和水溶液涂刷在涂层表面,在700℃的条件下进行了156 h的热腐蚀试验。通过腐蚀动力学测试对电弧喷涂涂层的抗热腐蚀性能进行了评估。采用了X射线衍射,扫描电镜和能谱分析技术对热腐蚀机理进行了探讨。结果表明,两种电弧喷涂涂层具有致密的层状结构,涂层中含有少量空隙。在涂层表面生成的连续致密的氧化膜使得NiCrTi涂层具有良好的抗热腐蚀性能。FeNiCr/Cr3C2涂层则遭受了较严重的氧化腐蚀和硫化腐蚀,并且有内硫化物析出,抗热腐蚀性能较差。     

高速电弧喷涂涂层的结合强度与结合方式研究

通过高速电弧喷涂Fe-Al／Cr3C2涂层及其他三种涂层的抗拉和抗热震性能的研究，揭示该涂层的结合机理及提高涂层结合强度的途径。研究发现，添加Cr元素可明显提高涂层的结合强度；涂层的结合方式主要为机械和物理结合；通过提高喷涂温度和速度等可以提高涂层的结合强度。     

电站锅炉防护用Fe-Al/Cr3C2涂层性能研究及应用

使用高速电弧喷涂技术结合Fe-Al/Cr3C2粉芯丝材制备了铁铝金属间化合物涂层,对涂层的常温与高温性能进行了研究,并进行了应用的探索.结果表明,Fe-Al/Cr3C2复合涂层具有典型的层状结构、较高的结合强度和硬度;涂层的耐高温冲蚀性能良好,温度升高、角度增大,冲蚀性能提高;由于Cr2O3的存在以及涂层结合能的提高,Fe-Al/Cr3C2涂层的高温抗腐蚀性能较高;其常温和高温耐磨损性能也较高;应用研究表明,该涂层适合用于电站锅炉＂四管＂的防护.     

高速火焰喷涂Fe-Al/Cr3C2复合涂层的组织与性能

用高速火焰喷涂法在20钢上制备Fe-Al／Cr3C2复合涂层。利用配有能谱仪的扫描电镜分析涂层表面形貌和所含元素,利用X射线衍射仪分析涂层的相组成,并测试了涂层的结合强度、显微硬度、孔隙率等性能。结果表明,高速火焰喷涂Fe-Al／Cr3C2复合涂层中主要包括Fe、Al以及FeAl、Fe3Al、Cr3C2相,Cr3C2增强相呈点状均匀分布涂层中;涂层具有较高的结合强度、硬度和较低的孔隙率。     

高速电弧喷涂FeMnCrAl/Cr3C2涂层的组织及抗高温氧化性能

使用高速电弧喷涂技术在20钢样品表面制备了FeMnCrAl/Cr3C2涂层,采用光学显微镜、场发射扫描电镜、能谱分析和X射线衍射等方法,对FeMnCrAl/Cr3C2涂层的显微组织和抗高温氧化性能进行了研究,并与电弧喷涂FeMnCr/Cr3C2涂层、316L不锈钢涂层和20 钢做了对比试验.研究结果表明:三种涂层增重均明显低于20 钢;FeMnCrAl/Cr3C2涂层氧化增重约为FeMnCr/Cr3C2涂层的1/3,略高于316L不锈钢涂层,FeMnCrAl/Cr3C2涂层氧化后表面生成具有保护性的、致密的含Al氧化膜和Cr与Fe的复合氧化物,阻碍了涂层进一步氧化,但存在不均匀性,原因是电弧喷涂层成分的微观不均匀性和涂层中存在孔隙.     

高速火焰喷涂Fe-Al/Cr3C2复合涂层的冲蚀性能研究

用高速火焰喷涂方法,在20钢基体上喷涂制备Fe-Al/Cr3C2复合涂层,对涂层的抗650℃冲蚀特性进行研究,利用扫描电镜分析冲蚀后涂层表面形貌.结果表明,高速火焰喷涂Fe-Al/Cr3C2复合涂层的冲蚀特性在300℃、450℃、650℃时分别主要为脆性冲蚀、塑性冲蚀和脆性冲蚀、塑性冲蚀;冲蚀角度对涂层的耐冲蚀性能有较大影响,30°时涂层的抗冲蚀能力优于90°时;温度升高,涂层的抗冲蚀性能提高.     

Tribological properties of high velocity arc sprayed Fe-Al based composite coatings at elevated temperature

Fe-Al based intermetallic composite coatings were in-situ synthesized using Fe-Al/Cr3C2 or Fe-Al/WC cored wires and high velocity are spraying (HVAS) technology. The tribological properties of the Fe-Al based intermetallic composite coatings were investigated using a ball-on-disc tribotester from room temperature to 650 ℃. The results show that the coatings have relatively high bond strength and micro-hardness. The tribological properties of Fe-Al/Cr3C2 and Fe-Al/WC composite coatings were further analyzed and compared. Low and stable wear rates of the Fe-Al based intermetallic composite coatings were indicated from room temperature to 650 ℃. The excellent wear resistance of the composite coatings in high temperature was discussed.     

Corrosion Behavior of Fe–Al Coatings Fabricated by Pack Aluminizing Method

In this study,the two kinds of Fe–Al coatings were fabricated by pack aluminizing on low-carbon steel at different temperatures.The corrosion behavior of the Fe–Al coatings in artificial seawater was investigated by the electrochemical and weight loss techniques.Results show that the thickness of coating layer increases with increasing aluminizing temperature.The coatings exhibit high micro-hardness and good metallurgical bonding with the substrate.In comparison with the steel substrate,the corrosion current density Icorrof the Fe–Al coatings is always lower than that of substrate,about 1/38 or 1/33 after 2 h immersion,and 1/3 or 1/6 for 720 h immersion.As can be seen from the weight loss curve,the Fe–Al coatings show less loss than that of the substrate within 30-day immersion.The corrosion products formed on the surface of the coatings include oxides of Al,Mg,Fe and Ca,and pitting defect has also been found.The Fe–Al coating with higher content of Fe_2Al_5 has better corrosion resistance.     

纳米Fe-Al/Cr_3C_2复合涂层的制备及性能研究

目的制备纳米Fe-Al/Cr_3C_2复合涂层并对比分析结合强度、显微硬度、孔隙率,为利用热喷涂技术治理易损部件提供有效手段。方法运用自主研发的造粒系统,成功对高活性的纳米Fe-Al/Cr_3C_2复合喷涂粉体实施团聚造粒。使用高速火焰喷涂方法,在结构材料表面制备出了纳米Fe-Al/Cr_3C_2复合涂层。测试了纳米Fe-Al/Cr_3C_2复合涂层的基本性能,包括结合强度、显微硬度、孔隙率。结果纳米Fe-Al/Cr_3C_2复合喷涂材料的粒径由原始的50 nm团聚到最终的114~178μm,团聚后的纳米颗粒呈圆形或椭圆形,各成分比例保持原始比例,团聚颗粒内部仍然保持纳米粉体状态。纳米Fe-Al/Cr_3C_2表面及截面元素分布均匀、致密,纳米涂层的孔隙率、硬度和结合强度分别是微米涂层的0.25倍、1.39倍和2.43倍。结论团聚后的纳米Fe-Al/Cr_3C_2颗粒满足热喷涂材料的相关要求,纳米Fe-Al/Cr_3C_2比微米涂层具有更精细的涂层结构和更优异的基本性能。     

粘结底层材料的耐锌蚀性能研究

用等离子喷涂技术制备了用作粘结底层的Al/Ni、Fe-Al涂层,研究对比了这两种涂层在锌液中的耐腐蚀性能。结果表明,Fe-Al比Al/Ni有更好的耐锌蚀性。     

Fe-Al金属间化合物研究概况与发展方向

本文系统阐述了Fe-Al金属间化合物的室温脆性本质和用热加工处理、合金化等传统工艺提高其室温塑性的研究成果,以及Fe-Al金属间化合物纳米化增塑的最新研究进展,并详细介绍了Fe-Al金属间化合物作为高温耐磨耐蚀涂层和高温气体净化多孔材料的研究新动向。     

高速电弧喷涂Fe-Al涂层在800℃下的氧化性能

采用高速电弧喷涂技术(HVAS)在20G钢基体上制备了Fe-Al金属间化合物涂层，测试了涂层在800℃下的氧化性能．结果表明，Fe-Al涂层的氧化动力学曲线近似呈现对数规律，其在5h后的氧化增重低于20G钢；涂层的氧化物为Al2O3、Fe2O3、Fe3O4和FeO等，且其分布不均匀；涂层表面优先形成具有保护性的Al2O3膜，阻止了涂层的进一步氧化。     

温度对高速电弧喷涂Fe-Al/Cr3C2涂层的影响

采用Fe—Al／Cr3C2粉芯丝材和高速电弧喷涂技术(HVAS)原位合成了复合涂层，对不同温度下涂层的组织和性能进行了研究。结果表明，随着温度的升高，涂层的耐冲蚀性能提高，涂层的耐蚀性能变化不大，涂层的结合强度提高，并且涂层表面氧化物膜增多，涂层组织颗粒变小，涂层结合处出现冶金结合。     

Fe/Cr涂层抗热腐蚀性能研究

设计制造出Fe/Cr粉芯丝材,利用电弧喷涂技术制备出耐高温腐蚀的工作涂层。运用光学显微镜、扫描电子显微镜(SEM)、X射线衍射仪(XRD)等研究了电弧喷涂Fe/Cr合金涂层的微观结构、腐蚀动力学和高温下的腐蚀性能。结果表明,该涂层组织致密,涂层中形成Cr2O3或尖晶石型氧化物是其具有优异的抗高温腐蚀性能的主要原因,涂层抗高温腐蚀性能较好。     

耐熔锌腐蚀涂层在热镀锌设备中的应用

综述了表面涂层技术在热镀锌内加热金属保护套管中的应用现状，分析了目前国内外常用的耐锌蚀涂层材料及其耐锌蚀机理，同时指出Fe-Al、Mo-W、Fe-B3个系列的合金涂层材料具有广阔的应用前景.