铸态及快淬态La2Mg（Ni0.85Co0.15）9Crx（x=0～0.2）电极合金的微观结构及电化学性能

为了提高La-Mg-Ni系（PuNi3）型贮氢合金的电化学循环稳定性,在La2Mg（Ni0.85Co0.15）9合金中加入微量Cr,用铸造及快淬工艺制备了La2Mg（Ni0.85Co0.15）9Crx（x=0,0.1,0.2）贮氢合金.分析测试了铸态及快淬态合金的电化学性能及微观结构,研究了Cr对铸态及快淬态合金微观结构及电化学性能的影响.结果表明,铸态及快淬态合金具有多相结构,包括（La,Mg）Ni3相（PuNi3结构））,LaNi5相和一定量的LaNi2相.快淬对合金的相组成没有影响,但使合金的相丰度产生变化.Cr的加入提高了铸态及快淬态合金的循环稳定性,但使合金的容量下降.合金的循环寿命随淬速的增加而增加,铸态及快淬态合金均有优良的活化性能.     

快淬La—Mg—Ni系贮氢合金的电化学性能及微观结构

采用铸造及快淬工艺制备了La—Mg-Ni系（PuNi3型）贮氢合金La0.7Mg0.3Ni2.55-Co0.45Cux（x=0～0．4），分析测试了铸态及快淬态合金的电化学性能与微观结构，研究了Cu替代Ni及快淬工艺对合金微观结构及电化学性能的影响。结果表明：铸态及快淬态合金具有多相结构，包括（La，Mg）Ni3相和LaNi5相和一定量的LaNi2相。快淬处理对合金的相组成没有影响，但使合会的衍射峰趋于均匀一致。Cu替代Ni使合金的电化学容量下降，但使合金的循环稳定性及放电电压特性得到改善。快淬可提高合金的循环稳定性，但使合金的容量下降。     

La0.7Mg0.3Ni2.55-xCo0.45Alx(x=0～0.4)贮氢合金的循环稳定性

为了提高La-Mg-Ni系贮氢合金的循环稳定性,以Al部分替代Ni,采铸造及快淬工艺制备了La0.7Mg0.3Ni2.55-xCo0.45Alx(x=0,0.1,0.2,0.3,0.4)电极合金,研究了Al替代量及快淬工艺对合金微观结构及电化学循环稳定性的影响。X射线衍射分析结果表明:铸态及快淬态合金具有多相结构,包括(La,Mg)Ni3相、LaNi5相和一定量的LaNi2相;Al替代使铸态合金中LaNi2相的量显著增加,但对快淬态合金中LaNi2相的相丰度影响不显著。电化学测试结果表明:随Al替代量的增加,合金的循环寿命大幅度提高;快淬处理可以提高合金的循环寿命,但随Al替代量的增加,淬速对循环寿命的影响减小。     

Improved Cycle Stability of La0.75-xPrxMg0.25Ni3.2Co0.2Al0.1 (x=0-0.4) Electrode Alloys by Melt Spinning

为了改善 La-Mg-Ni 系 A2B7型电极合金的电化学循环稳定性,用 Pr 部分替代合金中的 La,并用熔体快淬工艺制备了La0.75-xPrxMg0.25Ni3.2Co0.2Al0.1(x = 0, 0.1, 0.2, 0.3, 0.4)电极合金。用 XRD、SEM、TEM 分析了铸态及快淬态合金的微观结构。结果表明,铸态及快淬态合金均具有多相结构,包括 2 个主相(La,Mg)Ni3及 LaNi5和 1 个残余相 LaNi2。熔体快淬导致 LaNi5相增加而(La,Mg)Ni3相减少。电化学测试结果表明,熔体快淬显著地提高合金的电化学循环稳定性。当淬速从 0 m/s (铸态被定义为淬速 0 m/s)增加到 20 m/s 时,x=0 合金 100 次充放循环后的容量保持率从 65.32%增加到 73.97%,x=0.4 合金的容量保持率从 79.36%增加到 93.08%。     

Zr替代La对快淬态A2B7型电极合金结构及电化学性能的影响

用铸造及快淬工艺制备了A2B7型电极合金,合金的名义成分为La0.75-xZrxMg0.25Ni3.2Co0.2Al0.1 (x = 0, 0.05, 0.1, 0.15, 0.2)。深入研究了Zr替代La对合金微观结构及电化学性能的影响。用XRD、SEM、TEM分析了合金的结构。结果表明,铸态及快淬态合金均具有多相结构,含有两个主相(La,Mg)Ni3和LaNi5以及一个残余相LaNi2。Zr替代La使合金中LaNi5相明显增加,并促进快淬态合金中形成非晶相。电化学测试的结果表明,Zr替代La明显降低合金的放电容量,但显著改善合金的电化学循环稳定性。当Zr含量小于0.1时,合金的放电容量随淬速的增加而先增加后减小,合金的循环稳定性随淬速的增加而单调增加。     

铸态及快淬态La-Mg-Ni系(PuNi3型)贮氢合金的循环稳定性

用铸造及快淬工艺制备了La-Mg-Ni系(PuNi3型)La2Mg(Ni0.85Co0.15)9Bx(x=0～0.2)贮氢合金,分析测试了铸态及快淬态合金的微观结构与循环稳定性,研究了硼及快淬工艺对合金微观结构及电化学循环稳定性的影响.结果表明,铸态合金具有多相结构,包括(La,Mg)Ni3相和LaNi5相,一定量的LaNi2相及微量的Ni2B相,经大于15 m/s淬速快淬处理后Ni2B相消失,并且其它相的相对量随淬速的变化而变化.硼的加入提高了铸态及快淬态合金的循环稳定性,但其作用机理完全不同.合金的循环寿命随淬速的增加而增加,但快淬工艺对La-Mg-Ni系贮氢合金循环寿命的改善非常有限.     

快淬工艺对La0．7Mg0．3Ni2．55-xCo0．45Alx（x=0～0．4）电极合金微观结构及电化学性能的影响

用铸造及快淬工艺制备了La-Mg-Ni系（PuNi3型）电极合金La0．7Mg0．3Ni2．55-xCo0．45Alx（x=0，0．1，0．2，0．3，0．4），研究了快淬工艺对合金微观结构及电化学性能的影响。XRD分析结果表明，铸态及快淬态合金具有多相结构，包括（La，Mg）Ni3相和LaNi5相和一定量的LaNi2相，快淬处理对合金的相组成没有影响，但使相的相对含量产生变化。TEM及SEM分析结果表明，快淬处理显著改善合金的成分均匀性，使晶粒细化。Al替代Ni不利于非晶相的形成，但使快淬态合金的晶粒显著细化。电化学测试结果表明，快淬处理显著提高合金的循环稳定性，但不同程度地降低合金的放电容量和活化性能，快淬对放电电压特性的影响是复杂的。     

铸态及快淬态La0. 55 M0. 2 Mg0. 25 Ni3.2C00.2 Al0.1（M=Zr，Pr）合金的电化学贮氢动力学

为了改善La-Mg-Ni系A2B7型电极合金的动力学性能,用M（M=Zr,Pr）部分替代合金中的A侧元素La。用真空快淬技术制备了La0. 55 M0. 2 Mg0. 25 Ni3.2C00.2 Al0.1（M=Zr,Pr）电极合金,探索了快淬工艺参数对合金电化学贮氢动力学性能的影响。用XRD、SEM及TEM表征了铸态及快淬态合金的结构,结果发现,铸态及快淬态合金均由多相组成,包括两个主相（La,Mg）2Ni7和LaNi5以及残余相LaNi2。快淬Pr替代合金具有微晶、纳米晶结构,而在快淬Zr替代合金中发现明显的非晶相。电化学测试结果表明,合金的高倍率放电能力随淬速的增加先增加后减小。电化学交流阻抗（EIS）、Tafd极化曲线及电位阶跃测试的结果都表明,合金的电化学贮氢动力学性能随淬速的增加先上升后下降。     

快淬工艺对La-Mg-Ni系贮氢合金微观结构及电化学性能的影响

用铸造及快淬工艺制备了La-Mg-Ni系（PuNi3型）贮氢合金La2Mg（Ni0．85Co0.15）9Bx（x=0，0．1，0．2），分析测试了铸态及快淬态合金的微观结构与电化学性能，研究了硼及快淬工艺对合金微观结构及电化学性能的影响。结果表明，铸态合金具有多相结构，主相包括（La，Mg）Ni3相（PuNi3型）和LaNi5相，残余相为一定量的LaNi2相和微量的Ni2B相，经快淬处理后Ni2B相消失，并且其它相的相对量随淬速的变化而变化。不含硼合金的容量随淬速的增加而单调减小，含硼合金的容量随淬速变化有一个极大值。合金的循环寿命随淬速的增加而增加，铸态及快淬态合金均有优良的活化性能。     

铸态及快淬态La_(0.55)M_(0.2)Mg_(0.25)Ni_(3.2)Co_(0.2)Al_(0.1)(M=Zr,Pr)合金的电化学贮氢动力学

为了改善La-Mg-Ni系A2B7型电极合金的动力学性能,用M(M=Zr,Pr)部分替代合金中的A侧元素La。用真空快淬技术制备了La0.5 5M0.2Mg0.25Ni3.2Co0.2Al0.1(M=Zr,Pr)电极合金,探索了快淬工艺参数对合金电化学贮氢动力学性能的影响。用XRD、SEM及TEM表征了铸态及快淬态合金的结构,结果发现,铸态及快淬态合金均由多相组成,包括两个主相(La,Mg)2Ni7和LaNi5以及残余相LaNi2。快淬Pr替代合金具有微晶、纳米晶结构,而在快淬Zr替代合金中发现明显的非晶相。电化学测试结果表明,合金的高倍率放电能力随淬速的增加先增加后减小。电化学交流阻抗(EIS)、Tafel极化曲线及电位阶跃测试的结果都表明,合金的电化学贮氢动力学性能随淬速的增加先上升后下降。     

Structures and electrochemical performances of La_(0.75-x)Zr_xMg_(0.25)Ni_(3.2)Co_(0.2)Al_(0.1) (x=0-0.2) electrode alloys prepared by melt spinning

The La-Mg-Ni system A2B7-type electrode alloys with nominal composition La0.75-xZrxMg0.25Ni3.2Co0.2Al0.1(x=0,0.05, 0.1,0.15,0.2)were prepared by casting and melt-spinning.The influences of melt spinning on the electrochemical performances as well as the structures of the alloys were investigated.The results obtained by XRD,SEM and TEM show that the as-cast and spun alloys have a multiphase structure,consisting of two main phases(La,Mg)Ni3 and LaNi5 as well as a residual phase LaNi2.The melt spinning leads to an obvious increase of the LaNi5 phase and a decrease of the(La,Mg)Ni3 phase in the alloys.The results of the electrochemical measurement indicate that the discharge capacity of the alloys(x≤0.1)first increases and then decreases with the increase of spinning rate,whereas for x0.1,the discharge capacity of the alloys monotonously falls.The melt spinning slightly impairs the activation capability of the alloys,but it significantly enhances the cycle stability of the alloys.     

快淬对RE-Mg-Ni系A_2B_7型贮氢合金动力学性能的影响(英文)EI北大核心CSCD

合金的电化学贮氢动力学性能是其应用于动力电池的重要因素。为了提高RE-Mg-Ni系A2B7型贮氢合金的动力学性能,用M(M=Pr,Zr)部分替代La,并采用快淬处理制备了La0.65M0.1Mg0.25Ni3.2Co0.2Al0.1(M=Pr,Zr)电极合金。研究了元素替代和快淬处理对合金结构及电化学贮氢动力学性能的影响。XRD及TEM结果显示,铸态及快淬态合金均为多相结构,包含(La,Mg)2Ni7和LaNi5主相以及少量的残余相LaNi2。Pr替代快淬态合金为纳米晶结构,而Zr替代快淬态合金为类非晶结构,说明Zr部分替代La促进了非晶的形成。电化学测试表明合金的高倍率放电性能(HRD)随着快淬速度的增加先增大后减小。此外,电化学阻抗谱(EIS),塔菲尔极化曲线以及电势阶跃测试均表明合金的电化学动力学性能随着快淬速度的增加先增大后减小。     

Electrochemical hydrogen storage characteristics of La0.75-xMxMg0.25Ni3.2Co0.2Al0.1 (M =Zr, Pr; x =0, 0.1) alloys prepared by melt spinning

In order to ameliorate the electrochemical hydrogen storage performances of La-Mg Ni system A2B7-type electrode alloys,the partial substitution ofM (M =Zr,Pr) for La was performed.The melt spinning technology was used to fabricate the La0.75-xMxMg0.25Ni3.2Co0.2Al0.1 (M =Zr,Pr; x =0,0.1) electrode alloys.The influences of the melt spinning and substituting La with M (M =Zr,Pr) on the structures and the electrochemical hydrogen storage characteristics of the alloys were investigated.The analysis of XRD,SEM,and TEM reveals that the as-cast and spun alloys have a multiphase structure composed of two main phases (La,Mg)2Ni7 and LaNi5 as well as a residual phase LaNi2.The as-spun (M =Pr) alloy displays an entire nanocrystalline structure,while an amorphous-like structure is detected in the as-spun (M =Zr) alloy,implying that the substitution of Zr for La facilitates the amorphous formation.The electrochemical measurements exhibit that the substitution of Pr for La clearly increases the discharge capacity of the alloys; however,the Zr substitution brings on an adverse impact.Meanwhile,the M (M =Zr,Pr) substitution significantly enhances its cycle stability.The melt spinning exerts an evident effect on the electrochemical performances of the alloys,whose discharge capacity and high rate discharge ability (HRD) first mount up and then fall with the growing spinning rate,whereas their cycle stabilities monotonously augment as the spinning rate increases.     

铸态和退火态A2B7型La—Mg—Ni系合金的电化学研究

为了改善铸态La3MgNi14合金的电化学性能,在0．3MPa氩气气氛下对La3MgNi14合金进行了10h退火处理,退火温度分别为1123,1223和1323K。采用x射线衍射（XRD）、扫描电镜（SEM）和电化学实验研究了合金的微观结构和电化学性能。结果表明,铸态及1123K温度退火后的合金由LaNi5相、（La,Mg）2Ni7相以及少量的LaNi2相组成。1223K温度退火后合金含有LaNis,（La,Mg）2Ni7和（La。Mg）Ni3相。1323K温度退火后合金的主相为LaNi5和（La,Mg）Ni3相。与铸态合金相比,退火后合金组织更加均匀,晶粒长大。随着退火温度的增加,合金的一些电化学性能（如最大放电容量、放电效率、循环稳定性）以及动力学参数（如高倍率放电性能）增强,而电位差和电荷迁移电阻降低。在本研究范围内,为了放电容量和循环稳定性之问的平衡,铸态La3MgNi14合金的适宜退火温度为1323K。     

纳米晶和非晶Mg20-xLaxNi10(x=0-6)贮氢合金的贮氢行为

用快淬技术制备了Mg2Ni型贮氢合金,合金的名义成分为Mg20-xLaxNi10 (x = 0, 2, 4, 6)。用XRD、SEM、HRTEM分析了合金的微观结构。发现不含La的快淬合金中没有非晶相,但含La快淬合金中显示以非晶相为主。当La含量x≤2时,铸态合金的主相为Mg2Ni相,但随着La含量的进一步增加,铸态合金的主相改变为(La,Mg)Ni3+LaMg3相。应用Sieverts设备研究了铸态及快淬态合金的吸放氢量及动力学,结果表明,x=2的合金吸放氢量及动力学随淬速的增加而增加,但对于x=6的合金,结果是相反的。电化学测试结果表明,x=2合金的放电容量随淬速的增加而增加,而对于x=6合金,结果也是相反的。快淬显著地提高了x=2, 6合金的循环稳定性