Quantified NOx adsorption on Pt/K/gamma-Al2O3 and the effects of CO2 and H2O

A multi-component NO_x-trap catalyst consisting of Pt and K supported on γ-Al₂O₃ was studied at 250 °C to determine the roles of the individual catalyst components, to identify the adsorbing species during the lean capture cycle, and to assess the effects of H₂O and CO₂ on NO_x storage. The Al₂O₃ support was shown to have NO_x trapping capability with and without Pt present (at 250 °C Pt/Al₂O₃ adsorbs 2.3 μmols NO_x/m²). NO_x is primarily trapped on Al₂O₃ in the form of nitrates with monodentate, chelating and bridged forms apparent in Diffuse Reflectance mid-Infrared Fourier Transform Spectroscopy (DRIFTS) analysis. The addition of K to the catalyst increases the adsorption capacity to 6.2 μmols NO_x/m², and the primary storage form on K is a free nitrate ion. Quantitative DRIFTS analysis shows that 12% of the nitrates on a Pt/K/Al₂O₃ catalyst are coordinated on the Al₂O₃ support at saturation.

When 5% CO₂ was included in a feed stream with 300 ppm NO and 12% O₂, the amount of K-based nitrate storage decreased by 45% after 1 h on stream due to the competition of adsorbed free nitrates with carboxylates for adsorption sites. When 5% H₂O was included in a feed stream with 300 ppm NO and 12% O₂, the amount of K-based nitrate storage decreased by only 16% after 1 h, but the Al₂O₃-based nitrates decreased by 92%. Interestingly, with both 5% CO₂ and 5% H₂O in the feed, the total storage only decreased by 11%, as the hydroxyl groups generated on Al₂O₃ destabilized the K–CO₂ bond; specifically, H₂O mitigates the NO_x storage capacity losses associated with carboxylate competition.     

Mean field modelling of NOx storage on Pt/BaO/Al2O3

A mean field model, for storage and desorption of NO_x in a Pt/BaO/Al₂O₃ catalyst is developed using data from flow reactor experiments. This relatively complex system is divided into five smaller sub-systems and the model is divided into the following steps: (i) NO oxidation on Pt/Al₂O₃; (ii) NO oxidation on Pt/BaO/Al₂O₃; (iii) NO_x storage on BaO/Al₂O₃; (iv) NO_x storage on Pt/BaO/Al₂O₃ with thermal regeneration and (v) NO_x storage on Pt/BaO/Al₂O₃ with regeneration using C₃H₆. In this paper, we focus on the last sub-system. The kinetic model for NO_x storage on Pt/BaO/Al₂O₃ was constructed with kinetic parameters obtained from the NO oxidation model together with a NO_x storage model on BaO/Al₂O₃. This model was not sufficient to describe the NO_x storage experiments for the Pt/BaO/Al₂O₃, because the NO_x desorption in TPD experiments was larger for Pt/BaO/Al₂O₃, compared to BaO/Al₂O₃. The model was therefore modified by adding a reversible spill-over step. Further, the model was validated with additional experiments, which showed that NO significantly promoted desorption of NO_x from Pt/BaO/Al₂O₃. To this NO_x storage model, additional steps were added to describe the reduction by hydrocarbon in experiments with NO₂ and C₃H₆. The main reactions for continuous reduction of NO_x occurs on Pt by reactions between hydrocarbon species and NO in the model. The model is also able to describe the reduction phase, the storage and NO breakthrough peaks, observed in experiments.     

Influence of CO2 and H2O on NOx storage and reduction on a Pt–Ba/γ-Al2O3 catalyst

In this paper, the effect of CO₂ and H₂O on NO_x storage and reduction over a Pt–Ba/γ-Al₂O₃ (1 wt.% Pt and 30 wt.% Ba) catalyst is shown. The experimental results reveal that in the presence of CO₂ and H₂O, NO_x is stored on BaCO₃ sites only. Moreover, H₂O inhibits the NO oxidation capability of the catalyst and no NO₂ formation is observed. Only 16% of the total barium is utilized in NO storage. The rich phase shows 95% selectivity towards N₂ as well as complete regeneration of stored NO. In the presence of CO₂, NO is oxidized into NO₂ and more NO_x is stored as in the presence of H₂O, resulting in 30% barium utilization. Bulk barium sites are inactive in NO_x trapping in the presence of CO₂·NH₃ formation is seen in the rich phase and the selectivity towards N₂ is 83%. Ba(NO₃)₂ is always completely regenerated during the subsequent rich phase. In the absence of CO₂ and H₂O, both surface and bulk barium sites are active in NO_x storage. As lean/rich cycling proceeds, the selectivity towards N₂ in the rich phase decreases from 82% to 47% and the N balance for successive lean/rich cycles shows incomplete regeneration of the catalyst. This incomplete regeneration along with a 40% decrease in the Pt dispersion and BET surface area, explains the observed decrease in NO_x storage.     

Effect of hydrogen on reaction intermediates in the selective catalytic reduction of NOx by C3H6

Selective catalytic reduction of NO_x by C₃H₆ in the presence of H₂ over Ag/Al₂O₃ was investigated using in situ DRIFTS and GC–MS measurements. The addition of H₂ promoted the partial oxidation of C₃H₆ to enolic species, the formation of –NCO and the reactions of enolic species and –NCO with NO_x on Ag/Al₂O₃ surface at low temperatures. Based on the results, we proposed reaction mechanism to explain the promotional effect of H₂ on the SCR of NO_x by C₃H₆ over Ag/Al₂O₃ catalyst.     

Kinetic modelling of sulfur deactivation of Pt/BaO/Al2O3 and BaO/Al2O3 NOx storage catalysts

In this work, a kinetic model is constructed to simulate sulfur deactivation of the NO_x storage performance of BaO/Al₂O₃ and Pt/BaO/Al₂O₃ catalysts. The model is based on a previous model for NO_x storage under sulfur-free conditions. In the present model the storage of NO_x is allowed on two storage sites, one for complete NO_x uptake and one for a slower NO_x sorption. The adsorption of SO_x is allowed on both of these NO_x storage sites and on one additional site which represent bulk storage. The present model is built-up of six sub-models: (i) NO_x storage under sulfur-free conditions; (ii) SO₂ storage on NO_x storage sites; (iii) SO₂ oxidation; (iv) SO₃ storage on bulk sites; (v) SO₂ interaction with platinum in the presence of H₂; (vi) oxidation of accumulated sulfur compounds on platinum by NO₂. Data from flow reactor experiments are used in the implementation of the model. The model is tested for simulation of experiments for NO_x storage before exposure to sulfur and after pre-treatments either with SO₂ + O₂ or SO₂ + H₂. The simulations show that the model is able to describe the main features observed experimentally.     

Impact of support oxide and Ba loading on the NOx storage properties of Pt/Ba/support catalysts: CO2 and H2O effects

A series of 1 wt.%Pt/_xBa/Support (Support = Al₂O₃, SiO₂, Al₂O₃-5.5 wt.%SiO₂ and Ce_0.7Zr_0.3O₂, x = 5–30 wt.% BaO) catalysts was investigated regarding the influence of the support oxide on Ba properties for the rapid NO_x trapping (100 s). Catalysts were treated at 700 °C under wet oxidizing atmosphere. The nature of the support oxide and the Ba loading influenced the Pt–Ba proximity, the Ba dispersion and then the surface basicity of the catalysts estimated by CO₂-TPD. At high temperature (400 °C) in the absence of CO₂ and H₂O, the NO_x storage capacity increased with the catalyst basicity: Pt/20Ba/Si < Pt/20Ba/Al5.5Si < Pt/10Ba/Al < Pt/5Ba/CeZr < Pt/30Ba/Al5.5Si < Pt/20Ba/Al < Pt/10BaCeZr. Addition of CO₂ decreased catalyst performances. The inhibiting effect of CO₂ on the NO_x uptake increased generally with both the catalyst basicity and the storage temperature. Water negatively affected the NO_x storage capacity, this effect being higher on alumina containing catalysts than on ceria–zirconia samples. When both CO₂ and H₂O were present in the inlet gas, a cumulative effect was observed at low temperatures (200 °C and 300 °C) whereas mainly CO₂ was responsible for the loss of NO_x storage capacity at 400 °C. Finally, under realistic conditions (H₂O and CO₂) the Pt/20Ba/Al5.5Si catalyst showed the best performances for the rapid NO_x uptake in the 200–400 °C temperature range. It resulted mainly from: (i) enhanced dispersions of platinum and barium on the alumina–silica support, (ii) a high Pt–Ba proximity and (iii) a low basicity of the catalyst which limits the CO₂ competition for the storage sites.     

On the activation of Pt/Al2O3 catalysts in HC-SCR by sintering: determination of redox-active sites using Multitrack

A highly dispersed Pt/Al₂O₃ catalyst was used for the selective catalytic reduction of NO_x using propene (HC-SCR). Contact with the reaction gas mixture led to a significant activation of the catalyst at temperatures above 523 K. According to CO chemisorption data and HRTEM analysis, Pt particles on the activated catalyst had sintered. The redox behavior of the fresh and sintered catalysts was investigated using Multitrack, a TAP-like pulse reactor. If Pt particles on the catalyst are highly dispersed (average size below 2 nm), only a small part (10%) of the total number of Pt surface sites as determined by CO chemisorption (Pt_surf) participates in H₂/O₂ redox cycles (Pt_surf,redox) in Multitrack conditions. For a sintered catalyst, with an average particle size of 2.7 nm, the number of Pt_surf and Pt_surf,redox sites are in good agreement. Similar results were obtained for both catalysts using NO as the oxidant. The low number of Pt_surf,redox sites on highly dispersed Pt/Al₂O₃ is explained by the presence of a kinetically more stable—probably ionic—form of Pt---O bonds on all surface sites of the smaller Pt particles, including corner, edge and terrace sites. When the average particle size shifts to 2.7 nm, the kinetic stability of all Pt---O bonds is collectively decreased, enabling the participation of all Pt surface sites in the redox cycles.

A linear correlation between the NO_x conversion in HC-SCR, and the amount of Pt_surf,redox was found. This suggests that redox-active Pt sites are necessary for catalytic activity. In addition, the correlation could be significantly improved by assuming that Pt_surf,terrace sites of the particles larger than 2.7 nm are mainly responsible for HC-SCR activity in steady state conditions. Implications of these results for the pathway of HC-SCR over Pt catalysts are discussed.     

Reactor and in situ FTIR studies of Pt/BaO/Al2O3 and Pd/BaO/Al2O3 NOx storage and reduction (NSR) catalysts

The reduction of NO under cyclic “lean”/“rich” conditions was examined over two model 1 wt.% Pt/20 wt.% BaO/Al₂O₃ and 1 wt.% Pd/20 wt.% BaO/Al₂O₃ NO_x storage reduction (NSR) catalysts. At temperatures between 250 and 350 °C, the Pd/BaO/Al₂O₃ catalyst exhibits higher overall NO_x reduction activity. Limited amounts of N₂O were formed over both catalysts. Identical cyclic studies conducted with non-BaO-containing 1 wt.% Pt/Al₂O₃ and Pd/Al₂O₃ catalysts demonstrate that under these conditions Pd exhibits a higher activity for the oxidation of both propylene and NO. Furthermore, in situ FTIR studies conducted under identical conditions suggest the formation of higher amounts of surface nitrite species on Pd/BaO/Al₂O₃. The IR results indicate that this species is substantially more active towards reaction with propylene. Moreover, its formation and reduction appear to represent the main pathway for the storage and reduction of NO under the conditions examined. Consequently, the higher activity of Pd can be attributed to its higher oxidation activity, leading both to a higher storage capacity (i.e., higher concentration of surface nitrites under “lean” conditions) and a higher reduction activity (i.e., higher concentration of partially oxidized active propylene species under “rich” conditions). The performance of Pt and Pd is nearly identical at temperatures above 375 °C.     

ZrO2/SiO2- and La2O3/Al2O3-supported platinum catalysts for CH4/CO2 reforming

Surface-phase ZrO₂ on SiO₂ (SZrOs) and surface-phase La₂O₃ on Al₂O₃ (SLaOs) were prepared with various loadings of ZrO₂ and La₂O₃, characterized and used as supports for preparing Pt/SZrOs and Pt/SLaOs catalysts. CH₄/CO₂ reforming over the Pt/SZrOs and Pt/SLaOs catalysts was examined and compared with Pt/Al₂O₃ and Pt/SiO₂ catalysts. CO₂ or CH₄ pulse reaction/adsorption analysis was employed to elucidate the effects of these surface-phase oxides.

The zirconia can be homogeneously dispersed on SiO₂ to form a stable surface-phase oxide. The lanthana cannot be spread well on Al₂O₃, but it forms a stable amorphous oxide with Al₂O₃. The Pt/SZrOs and Pt/SLaOs catalysts showed higher steady activity than did Pt/SiO₂ and Pt/Al₂O₃ by a factor of three to four. The Pt/SZrOs and Pt/SLaOs catalysts were also much more stable than the Pt/SiO₂ and Pt/Al₂O₃ catalysts for long stream time and for reforming temperatures above 700 °C. These findings were attributed to the activation of CO₂ adsorbed on the basic sites of SZrOs and SLaOs.     

The activity and characterization of sol–gel Sn/Al2O3 catalyst for selective catalytic reduction of NOx in the presence of oxygen

Catalytic performance of Sn/Al₂O₃ catalysts prepared by impregnation (IM) and sol–gel (SG) method for selective catalytic reduction of NO_x by propene under lean burn condition were investigated. The physical properties of catalyst were characterized by BET, XRD, XPS and TPD. The results showed that NO₂ had higher reactivity than NO to nitrogen, the maximum NO conversion was 82% on the 5% Sn/Al₂O₃ (SG) catalyst, and the maximum NO₂ conversion reached nearly 100% around 425 °C. Such a temperature of maximum NO conversion was in accordance with those of NO_x desorption accompanied with O₂ around 450 °C. The activity of NO reduction was enhanced remarkably by the presence of H₂O and SO₂ at low temperature, and the temperature window was also broadened in the presence of H₂O and SO₂, however the NO_x desorption and NO conversion decreased sharply on the 300 ppm SO₂ treated catalyst, the catalytic activity was inhibited by the presence of SO₂ due to formation of sulfate species (SO₄²⁻) on the catalysts. The presence of oxygen played an essential role in NO reduction, and the activity of the 5% Sn/Al₂O₃ (SG) was not decreased in the presence of large oxygen.     

A study of the behaviour of Pt supported on CeO2–ZrO2/Al2O3–BaO as NOx storage–reduction catalyst for the treatment of lean burn engine emissions

The behaviour of a Pt(1 wt.%) supported on CeO₂–ZrO₂(20 wt.%)/Al₂O₃(64 wt.%)–BaO(16 wt.%) as a novel NO_x storage–reduction catalyst is studied by reactivity tests and DRIFT experiments and compared with that of Pt(1%)–BaO(15 wt.%) on alumina. The former catalyst, designed as a hydrothermally stable sample, is composed of an alumina modified with Ba ions and an overlayer of ceria-zirconia. The results pointed out that during the calcination barium ions migrates over the surface of the catalyst which thus show a good NO_x storage–reduction behaviour comparable with that of Pt–BaO on alumina, although Ba ions result much better dispersed.     

NO reduction by CH4 in the presence of O2 over La2O3 supported on Al2O3

Dispersing La₂O₃ on δ- or γ-Al₂O₃ significantly enhances the rate of NO reduction by CH₄ in 1% O₂, compared to unsupported La₂O₃. Typically, no bend-over in activity occurs between 500° and 700°C, and the rate at 700°C is 60% higher than that with a Co/ZSM-5 catalyst. The final activity was dependent upon the La₂O₃ precursor used, the pretreatment, and the La₂O₃ loading. The most active family of catalysts consisted of La₂O₃ on γ-Al₂O₃ prepared with lanthanum acetate and calcined at 750°C for 10 h. A maximum in rate (mol/s/g) and specific activity (mol/s/m²) occurred between the addition of one and two theoretical monolayers of La₂O₃ on the γ-Al₂O₃ surface. The best catalyst, 40% La₂O₃/γ-Al₂O₃, had a turnover frequency at 700°C of 0.05 s⁻¹, based on NO chemisorption at 25°C, which was 15 times higher than that for Co/ZSM-5. These La₂O₃/Al₂O₃ catalysts exhibited stable activity under high conversion conditions as well as high CH₄ selectivity (CH₄ + NO vs. CH₄ + O₂). The addition of Sr to a 20% La₂O₃/γ-Al₂O₃ sample increased activity, and a maximum rate enhancement of 45% was obtained at a SrO loading of 5%. In contrast, addition of SO⁼₄ to the latter Sr-promoted La₂O₃/Al₂O₃ catalyst decreased activity although sulfate increased the activity of Sr-promoted La₂O₃. Dispersing La₂O₃ on SiO₂ produced catalysts with extremely low specific activities, and rates were even lower than with pure La₂O₃. This is presumably due to water sensitivity and silicate formation. The La₂O₃/Al₂O₃ catalysts are anticipated to show sufficient hydrothermal stability to allow their use in certain high-temperature applications.     

On the dynamic behavior of “NOx-storage/reduction” Pt–Ba/Al2O3 catalyst

The NO_x storage and reduction functions of a Pt–Ba/Al₂O₃ “NO_x storage–reduction” catalyst has been investigated in the present work by applying the transient response and the temperature programmed reaction methods, by using propylene as the reducing agent. It is found that: (i) the storage of NO_x occurs first at BaO and then at BaCO₃, which are the most abundant sites following regeneration of catalyst with propylene; (ii) the overall storage process at BaCO₃ is slower than at BaO; (iii) CO₂ inhibits the NO_x storage at low temperatures; (iv) the amount of NO_x stored up to catalyst saturation at 350 °C corresponds to 17.6% of Ba; (v) the reduction of stored NO_x groups is fast and is limited by the concentration of propylene in the investigated T range (250–400 °C); (vi) selectivity to N₂ is almost complete at 400 °C but is significantly lower at 300 °C due to the formation of NO which can be tentatively ascribed to the presence of unselective Pt–O species.     

A comparison study on non-thermal plasma-assisted catalytic reduction of NO by C3H6 at low temperatures between Ag/USY and Ag/Al2O3 catalysts

A comparison study was carried out on non-thermal plasma (NTP)-assisted selective catalytic reduction (SCR) of NO_x by propene over Ag/USY and Ag/Al₂O₃ catalysts. Ag/USY was almost inactive in thermal SCR while it showed obvious activities in NTP-assisted SCR at 100 °C–200 °C. Although the NO_x conversion over Ag/Al₂O₃ was also enhanced at 300 °C–400 °C by the assistance of NTP, it was ineffective below 250 °C. The intermediates over Ag/USY and Ag/Al₂O₃ were investigated using in situ DRIFTS method. It was found that key intermediates in HC-SCR, such as NCO, CN, oxygenates and some N-containing organic species were enriched after the assistance of NTP. The differences in the behaviors of above intermediates were not found between these two kinds of catalysts. However, some evidences suggested that different properties of the absorbed NO_x species resulted in the distinction of SCR reactions over Ag/USY and Ag/Al₂O₃. TPD profiles of Ag/Al₂O₃ showed that nitrates formed over the catalyst were quite stable at low temperatures, which might occupy the active sites and were unfavorable to SCR reactions. The nitrates over Ag/USY were unstable, among which the unidentate nitrate species is probably contributed to the SCR reactions at low temperatures.     

Impact of redox conditions on thermal deactivation of NOx traps for diesel

Performance of NO_x traps after high-temperature treatments in different redox environments was studied. Two types of treatments were considered: aging and pretreatment. Lean and rich agings were examined for a model NO_x trap, Pt–Ba/Al₂O₃. These were done at 950 °C for 3 h, in air and in 1% H₂/N₂, respectively. Lean aging had a severe impact on NO_x trap performance, including HC and CO oxidation, and NH₃ and N₂O formation. Rich aging had minimal impact on performance, compared to fresh/degreened performance. Deactivation from lean aging was essentially irreversible due to Pt sintering, but Pt remained dispersed with the rich aging. Pretreatments were examined for a commercially feasible fully formulated NO_x trap and two model NO_x traps, Pt–Ba/Al₂O₃ and Pt–Ba–Ce/Al₂O₃. Pretreatments were done at 600 °C for 10 min, and used feed gas that simulated diesel exhaust under several conditions. Lean pretreatment severely suppressed NO_x, HC, CO, NH₃ and N₂O activities for the ceria-containing NO_x traps, but had no impact on Pt–Ba/Al₂O₃. Subsequently, a relatively mild rich pretreatment reversed this deactivation, which appears to be due to a form of Pt–ceria interaction, an effect that is well known from early work on three-way catalysts. Practical applications of results of this work are discussed with respect to NO_x traps for light-duty diesel vehicles.     

Catalytic oxidation of HCN over a 0.5% Pt/Al2O3 catalyst

The adsorption of HCN on, its catalytic oxidation with 6% O₂ over 0.5% Pt/Al₂O₃, and the subsequent oxidation of strongly bound chemisorbed species upon heating were investigated. The observed N-containing products were N₂O, NO and NO₂, and some residual adsorbed N-containing species were oxidized to NO and NO₂ during subsequent temperature programmed oxidation. Because N-atom balance could not be obtained after accounting for the quantities of each of these product species, we propose that N₂ and was formed. Both the HCN conversion and the selectivity towards different N-containing products depend strongly on the reaction temperature and the composition of the reactant gas mixture. In particular, total HCN conversion reaches 95% above 250 °C. Furthermore, the temperature of maximum HCN conversion to N₂O is located between 200 and 250 °C, while raising the reaction temperature increases the proportion of NO_x in the products. The co-feeding of H₂O and C₃H₆ had little, if any effect on the total HCN conversion, but C₃H₆ addition did increase the conversion to NO and decrease the conversion to NO₂, perhaps due to the competing presence of adsorbed fragments of reductive C₃H₆. Evidence is also presented that introduction of NO and NO₂ into the reactant gas mixture resulted in additional reaction pathways between these NO_x species and HCN that provide for lean-NO_x reduction coincident with HCN oxidation.     

Lean NOx reduction with CO + H2 mixtures over Pt/Al2O3 and Pd/Al2O3 catalysts

The reduction of NO_x by hydrogen under lean burn conditions over Pt/Al₂O₃ is strongly poisoned by carbon monoxide. This is due to the strong adsorption and subsequent high coverage of CO, which significantly increases the temperature required to initiate the reaction. Even relatively small concentrations of CO dramatically reduce the maximum NO_x conversions achievable. In contrast, the presence of CO has a pronounced promoting influence in the case of Pd/Al₂O₃. In this case, although pure H₂ and pure CO are ineffective for NO_x reduction under lean burn conditions, H₂/CO mixtures are very effective. With a realistic (1:3) H₂:CO ratio, typical of actual exhaust gas, Pd/Al₂O₃ is significantly more active than Pt/Al₂O₃, delivering 45% NO_x conversion at 160 °C, compared to >15% for Pt/Al₂O₃ under identical conditions. The nature of the support is also critically important, with Pd/Al₂O₃ being much more active than Pd/SiO₂. Possible mechanisms for the improved performance of Pd/Al₂O₃ in the presence of H₂+CO are discussed.     

The reduction phase in NOx storage catalysis: Effect of type of precious metal and reducing agent

The effect of different reducing agents (H₂, CO, C₃H₆ and C₃H₈) on the reduction of stored NO_x over PM/BaO/Al₂O₃ catalysts (PM = Pt, Pd or Rh) at 350, 250 and 150 °C was studied by the use of both NO₂-TPD and transient reactor experiments. With the aim of comparing the different reducing agents and precious metals, constant molar reduction capacity was used during the reduction period for samples with the same molar amount of precious metal. The results reveal that H₂ and CO have a relatively high NO_x reduction efficiency compared to C₃H₆ and especially C₃H₈ that does not show any NO_x reduction ability except at 350 °C over Pd/BaO/Al₂O₃. The type of precious metals affects the NO_x storage-reduction properties, where the Pd/BaO/Al₂O₃ catalyst shows both a high storage and a high reduction ability. The Rh/BaO/Al₂O₃ catalyst shows a high reduction ability but a relatively low NO_x storage capacity.     

Effect of Pt on the water resistance of Co-zeolites upon the SCR of NOx with CH4

The objective of this work was to study the promotional effect of Pt on Co-zeolite (viz. mordenite, ferrierite, ZSM-5 and Y-zeolite) and Co/Al₂O₃ on the selective catalytic reduction (SCR) of NO_x with CH₄ under dry and wet reaction stream. After being reduced in H₂ at 350°C, the PtCo bimetallic zeolites showed higher NO to N₂ conversion and selectivity than the monometallic samples, as well as a combination of the latter samples such as mechanical mixtures or two-stage catalysts. After the same pretreatment, under wet reaction stream, the bimetallic samples were also more active. Among the other catalysts studied with 5% of water in the feed, (NO = CH₄ = 1000 ppm, O₂ = 2%), the NO conversion dropped to zero over Co_2.0Mor at 500°C and GHSV = 30,000 h⁻¹, whereas it is 20% in Pt_0.5Co_2.0Mor. In Pt/Co/Al₂O₃ the NO_x conversion dropped below 5% with only 2% of water under the same reaction conditions. The specific activity given as molecules of NO converted per total metal atom per second were 16.5 × 10⁻⁴ s⁻¹ for Pt_0.5Co_2.0Fer, 13 × 10⁻⁴ s⁻¹ for Pt_0.5Co_2.0Mor, 4.33 × 10⁻⁴ s⁻¹ for Pt_0.5Co_2.0ZSM-5 and 0.5 × 10⁻⁴ s⁻¹ for Pt/Co/Al₂O₃. The Y-zeolite-based samples were inactive in both mono and bimetallic samples. The species initially present in the solid were Pt° and Co°, together with Co²⁺ and Pt²⁺ at exchange positions. Co° seems not to participate as an active site in the SCR of NO_x. Those species remained after the reaction but some reorganization occurred. A synergetic effect among the different species that enhances both the NO to NO₂ reaction, the activation of CH₄ and also the ability of the catalyst to adsorb NO, could be responsible for the high activity and selectivity of the bimetallic zeolites.     

Water-induced bulk Ba(NO3)2 formation from NO2 exposed thermally aged BaO/Al2O3

Phase changes in high temperature treated (>900 °C) 8 or 20 wt% BaO supported on γ-Al₂O₃ model lean NO_x trap (LNT) catalysts, induced by NO₂ and/or H₂O adsorption, were investigated with powder X-ray diffraction (XRD), solid state ²⁷Al magic angle spinning nuclear magnetic resonance (MAS NMR) spectroscopy, and NO₂ temperature programmed desorption (TPD) experiments. After calcination in dry air at 1000 °C, the XRD and solid state ²⁷Al MAS NMR results confirm that stable surface BaO and bulk BaAl₂O₄ phases are formed for 8 and 20 wt% BaO/Al₂O₃, respectively. Following NO₂ adsorption over these thermally treated samples, some evidence for nanosized Ba(NO₃)₂ particles are observed in the XRD results, although this may represent a minority phase. However, when water was added to the thermally aged samples after NO₂ exposure, the formation of bulk crystalline Ba(NO₃)₂ particles was observed in both samples. Solid state ²⁷Al MAS NMR is shown to be a good technique for identifying the various Al species present in the materials during the processes studied here. NO₂ TPD results demonstrate a significant loss of uptake for the 20 wt% model catalysts upon thermal treatment. However, the described phase transformations upon subsequent water treatment gave rise to the partial recovery of NO_x uptake, demonstrating that such a water treatment of thermally aged catalysts can provide a potential method to regenerate LNT materials.