Li2O对连铸保护渣熔化性能的影响

实验研究了Li2O对连铸保护渣熔化性能的影响规律,测定了实验渣系的熔化温度、熔化速度和结晶温度.结果表明,在实验渣基本成分条件下,Li2O的质量分数为3%时,实验保护渣具有较好的熔化性能.     

中薄板坯连铸保护渣研究

系统地研究了中薄板坯连铸保护渣的化学成分与理化性能，熔化温度、熔化速度和粘度的关系，探讨了保护渣中的Al2O3、F^-、碳质量分数及碱度的大小对保护渣理化性能的影响，得到了优化的保护渣成分，为开发满足现场工艺要求的中薄板坯连铸保护渣提供理论依据和指导。     

BN对超低碳钢连铸保护渣性能的影响

采用C BN作为骨架粒子,研究开发了一种新型的超低碳钢保护渣.其性能可以满足超低碳钢连铸的需要.C BN作为骨架粒子可以使保护渣的粘度减小、熔化温度降低、熔化速度降低、结晶温度降低.     

碱度和Al2O3对中碳钢宽厚板连铸结晶器保护渣粘度和熔化温度的影响

分别研究了碱度为0.92,1.0,1.14,碱度为1.0时Al2O3的质量分数为4.3％,5.0％,6.1％时中碳钢宽厚板连铸结晶器保护渣粘度和熔化温度的变化.试验结果表明,随着保护渣的碱度由0.92升高到1.14,保护渣的粘度逐渐降低.碱度的不断增加保护渣的半球点温度迅速上升.本渣系中随着Al2O3的质量分数由4.3％增加到6.1％,保护渣粘度逐渐降低,保护渣粘度的降低保证了保护渣的润滑特性.Al2O3质量分数的增加对保护渣半球点温度的影响不是很剧烈,对保护渣的熔化温度起到降低的作用.     

CaO-BaO-Al2O3-SiO2-MgO-CaF2精炼渣系熔化温度研究

利用正交试验的方法进行CaO-BaO-Al2O3-SiO2-MgO-CaF2精炼渣系熔化温度的研究,结果表明,BaO的质量分数在0～15％范围内精炼渣系的熔化温度随BaO含量升高而降低;CaO/Al2O3含量比值由1增加到2,精炼渣系熔化温度逐渐升高,而CaO/Al2O3含量比值由2增加到4,精炼渣系熔化温度又开始下降;SiO2的质量分数由8％～20％,精炼渣系熔化温度随SiO2含量升高而升高.     

不同熔化条件对Na2O·4TeO2玻璃性能的影响

探索了不同熔化条件对 Na2 O· 4Te O2 玻璃性能的影响 ,确定了 Na2 O- Te O2 系统玻璃的合理的熔化条件。通过热分析和红外分析等手段 ,对由不同原料在不同熔化条件下所得到的玻璃进行了分析 ,发现熔化条件不同时 ,由不同原料所得玻璃的性能也有很大差别。当熔化温度较低、熔化时间较短时 ,玻璃中存在未分解完全的来自原料的原子基团。由不同原料所得的玻璃的 DSC曲线和抗析晶能力差别很大。随着熔化温度的升高和熔化时间的延长 ,由不同原料熔化所得玻璃的性能趋于一致。在 80 0℃下熔化 1 h是亚碲酸钠玻璃较合适的熔化条件     

保护渣成分对结晶矿相的影响

熔融保护渣在MoSi2高温电阻炉内以2℃／min降温速率冷却至室温，制成薄片，采用岩相显微镜分析保护渣的结晶矿相．结果表明：在本实验条件下，结晶矿相主要有枪晶石，硅灰石，黄长石，个别渣样有霞石，萤石，橄榄石；增大保护渣碱度，能促进保护渣结晶；随着渣中CaF2，Na2O，K2O和Li2O质量分数的增大，保护渣结晶化率增大；随着渣中Al2O3，MgO，BaO和MnO质量分数的增大，保护渣结晶化率减小．     

超低碳钢连铸保护渣的特点

为了使保护渣良好地完成5个方面的作用，最重要的就是使控制结晶器保护渣粉形成“三层结构”．为此，在渣粉中配加适当碳粉以控制熔化速度．如果渣子熔化速度控制得合适，在结晶器液面上会形成“液渣-烧结-粉渣”的合理结构，再加上钢液面波动小，钢渣界面波动较小，渣中的碳消耗殆尽，不会造成铸坯增碳．     

F,MgO对包钢高炉渣性能影响的实验研究

根据目前包钢高炉渣的成分采用二次回归方法配制合成渣,通过对合成渣的粘度、熔化性温度及熔化区间的测定,研究F和MgO对包钢高炉渣性能的影响程度,寻求适宜的高炉渣成分.实验结果表明,当炉渣中w(F)≤1%时,CaF2具有降低炉渣开始熔化温度,增加炉渣熔化区间,降低炉渣热焓,降低炉渣粘度和炉渣熔化性温度的作用.随着炉渣中MgO的质量分数的增加,炉渣的热稳定性提高,炉渣粘度降低,当w(MgO)=11.652%时,熔化性温度达到最高值.     

小直径金属线材单晶化技术原理及工艺

在系统研究单晶连铸的基础上，提出小直径线材单晶化技术，该技术结合区域熔化技术和连续铸造技术，实现了“三个连续”，即送料连续、加热熔化连续、引锭连续．他能克服单晶连铸对所制备的单晶线材长度和直径的限制．理论和工艺实验结果表明，小直径线材单晶化技术满足制备单晶线材对固液界面的要求，可将直径较粗的多晶金属线材直接拉制成长度不受限制、直径较细的单晶金属线材，功率和连铸速度适当配合时，可在较大范围内获得表面光滑的单晶铜线材。     

B_2O_3、Al_2O_3和R_2O对CaO—SiO_2—P_2O_5生物微晶玻璃熔融特性的影响及相变研究

本文采用高温粘度计、高温显微镜和扫描电镜研究了B_2O_3、A1_2O_3和R_2O组分对CaO-SiO_2-P_2O_5系统生物微晶玻璃的熔制过程、熔融特性、相变和显微结构的影响。结果发现:该系统玻璃在高温范围有相变(分相或析晶)发生,玻璃熔体有特殊的粘度温度曲线,适当添加某些组分,可以改善熔制特性、控制相交范围和微观结构。     

Research on mold flux for hypo-peritectic steel at high casting speed

Mold fluxes having adaptable properties were developed in the laboratory to solve quality defects, such as depressions and longitudinal cracks when casting hypo-peritectic steel at high casting speed. Firstly, the effect of components on the high basicity mold flux properties was first studied using the orthogonal method. In the scope of the studied content, Li2O has the largest effect on the melting temperature, and the least effect on the viscosity; CaF2 has the largest effect on the viscosity, and the least effect on the melting temperature; Na2O and CaO/SiO2 have no obvious influence on the melting temperature and viscosity. Secondly, two powders (Z1 and Z6) have reasonable viscosity-temperature curves, higher solidification temperatures, and porous structure after solidification, but the crystal property of Z6 is worse than that of Z1, and thus Z1 is more suitable for continuous casting hypo-peritectic steel at high casting speed. Thirdly, a higher basicity of powder, a less free enthalpy of crystal compound, and a lower baffle energy are good for a higher tendentiousness of crystal.     

Acting mechanism of F, K, and Na in the solid phase sintering reaction of the Baiyunebo iron ore

The effect of F,K,and Na on the solid phase reaction of the Baiyunebo iron ore was investigated by differential thermal analysis (DTA) and X-ray diffraction(XRD).It has been identified that alkaline elements K and Na in the Baiyunebo ore instigate the formation of low melting point compounds Na_2SiO_3 and Na_2O·Fe_2O_3 and the generation of molten state in the solid phase sintering.Element F in the Baiyunebo ore facilitates the formation of cuspidine compound 3CaO·2SiO_2·CaF_2 in the solid phase reaction...     

Al2O3对中钛高炉渣冶金性能影响的实验研究

为实现高铝矿与钒钛磁铁矿的合理搭配,研究了含铝中钛高炉渣中Al2O3含量变化对炉渣黏度及熔化性温度的影响．研究结果表明,在炉渣二元碱度1.15,W（TiO2）=12％,W（MgO）=9％的条件下,实验炉渣在W（Al2O3）=14％时具有良好的流动性和最低的熔化性温度（1348℃）．为高炉实际生产提供一定的理论依据．     

稀土Eu对发光玻璃白光发射的调控

用高温熔融法制备了Eu2O3单掺和Ce/Tb/Eu三元共掺杂的CaO-B2O3-SiO2(CBS)发光玻璃材料,并使用荧光分光光度计和CIE色度坐标对其结构以及发光特性进行了研究.光谱分析结果表明:在394nm激发下,Eu2O3单掺杂的CBS发光玻璃的发射光谱中出现了Eu3+的特征发射峰.这些发射峰主要起源于Eu3+中的4f电子的f-f跃迁;在374nm激发下,三元共掺杂发光玻璃的发射光谱中同时观测到了起源于Ce3+、Tb3+和Eu3+的蓝色、绿色和红色的三基色发射,这些发射可进一步混合成为白光发射.此外,Ce/Tb/Eu三元共掺杂发光玻璃的发光颜色,随着Eu2O3含量的增加从蓝光逐渐过渡到白光,这显示出了发光颜色的可调节性,极大地扩展了其在白光发光领域中的应用.     

稀土掺杂发光玻璃的全色显示及白光发射

用高温熔融法制备了稀土Ce、Tb和Sm单掺杂和三元共掺杂的CaO-B2O3-SiO2（CBS）发光玻璃材料,并使用荧光分光光度计和CIE色度坐标对其光谱学和发光特性进行了研究.光致发光图谱表明,单掺杂Ce、Tb和Sm的发光玻璃在光激发下分别出现了稀土离子Ce3＋、Tb3＋和Sm3＋的特征发射峰;同时,在374nm激发下,Ce/Tb/Sm三元共掺杂CBS发光玻璃的发射光谱中同时观测到了蓝光、绿光和红橙光的发射带,这些发射带的混合实现了白光的全色发射显示.此外,三元共掺杂发光玻璃显示出了发光颜色随稀土元素共掺杂比的可调节性,极大地扩展了其在白光发光二极管中的应用.     

熔融法制备纳米SiO_2颗粒

介绍了以Na2O-B2O3-SiO2玻璃为原料,采用熔融法制备钠硼硅玻璃,并通过对钠硼硅玻璃的组分,熔制温度的讨论,以及对热处理,酸浸析等后处理过程工艺参数进行调节,得到制得纳米SiO2颗粒的最优化条件。采用差示扫描量热法对热处理前的钠硼硅玻璃进行测试,用X射线衍射分析对不同温度热处理的钠硼硅进行测试,用场发射扫描电子显微镜对酸浸析后二氧化硅颗粒形貌进行表征,并对最佳的工艺条件进行了讨论。制得的SiO2颗粒粒径范围为60～100 nm,并具有比表面积大、分散性好、成本低等优点。     

各种添加剂对低温陶瓷结合剂性能的影响

实验主要研究6种添加剂对陶瓷结合剂性能影响。实验证明，随着α—Al2O3加入量的增多，结合剂的熔点逐渐升高，在加入量为15％时流动度最好；CuO、Cr2O3和Zn对结合剂熔点有明显的提高作用；Sn和Cu可以降低结合剂的熔点；加入8％Cr2O3或加入6％Sn时其流动度值最佳。