Simple and fast synthesis of LiFePO4-C composite for lithium rechargeable batteries by ball-milling and microwave heating

A very simple and rapid method for synthesizing LiFePO₄-C composite has been developed by vibrant type ball-milling for 30 min and microwave heating for 2–4 min. X-ray diffraction and Mössbauer spectroscopy verify that well-crystallized LiFePO₄ without Fe³⁺ impurities is obtained. From laser particle size analysis and transmission electron microscopy, it is confirmed that a LiFePO₄-C composite with fine and uniform particle size (mean particle size ≤0.640 μm, D75 in volume distribution ≤0.592 μm) and with extremely uniform carbon distribution is prepared by vibrant type ball-milling and microwave heating. The LiFePO₄-C delivers a high initial discharge capacity of 161 mAh g⁻¹ at C/10 and shows very stable cycling behaviour.     

Surfactant based sol–gel approach to nanostructured LiFePO4 for high rate Li-ion batteries

Porous nanostructured LiFePO₄ powder with a narrow particle size distribution (100–300 nm) for high rate lithium-ion battery cathode application was obtained using an ethanol based sol–gel route employing lauric acid as a surfactant. The synthesized LiFePO₄ powders comprised of agglomerates of crystallites <65 nm in diameter exhibiting a specific surface area ranging from 8 m² g⁻¹ to 36 m² g⁻¹ depending on the absence or presence of the surfactant. The LiFePO₄ obtained using lauric acid resulted in a specific capacity of 123 mAh g⁻¹ and 157 mAh g⁻¹ at discharge rates of 10C and 1C with less than 0.08% fade per cycle, respectively. Structural and microstructural characterization were performed using X-ray diffraction (XRD), scanning electron microscopy (SEM) and high-resolution transmission electron microscopy (HRTEM) with energy dispersive X-ray (EDX) analysis while electronic conductivity and specific surface area were determined using four-point probe and N₂ adsorption techniques.     

Effect of synthesis temperature on the properties of LiFePO4/C composites prepared by carbothermal reduction

LiFePO₄/C composite cathode materials were synthesized by carbothermal reduction method using inexpensive FePO₄ as raw materials and glucose as conductive additive and reducing agent. The precursor of LiFePO₄/C was characterized by differential thermal analysis and thermogravimetry. The microstructure and morphology of the samples were characterized by X-ray diffraction (XRD), scanning electron microscopy (SEM), transmission electron microscope (TEM) and particle size analysis. Cyclic voltammetry (CV) and charge/discharge cycling performance were used to characterize their electrochemical properties. The results showed that the LiFePO₄/C composite synthesized at 650 °C for 9 h exhibited the most homogeneous particle size distribution. Residual carbon during processing was coated on LiFePO₄, resulting in the enhancement of the material's electronic properties. Electrochemical measurements showed that the discharge capacity first increased and then decreased with the increase of synthesis temperature. The optimal sample synthesized at 650 °C for 9 h exhibited a highest initial discharge capacity of 151.2 mA h g⁻¹ at 0.2 C rate and 144.1 mA h g⁻¹ at 1 C rate with satisfactory capacity retention rate.     

Effects of carbon coating and iron phosphides on the electrochemical properties of LiFePO4/C

Carbon coated LiFePO₄ (LiFePO₄/C) with different contents of high electron conductive iron phosphide phase was synthesized by an aqueous sol–gel method in a reductive sintering atmosphere. Different synthesis parameters were used for adjusting the microstructure and phase compositions of the products. The effects of the carbon coating and iron phosphides on the electrochemical properties of the LiFePO₄/C electrodes were studied by means of testing the discharge capacities at rates of 0.1–5C (1C = 170 mAh g⁻¹) and analyzing the CV curves. The results show that carbon coating in a content of 1.5 wt.% derived from the carbon source of ethylene glycol greatly decreases the particle size of LiFePO₄ in one order in the specific surface area, and significantly improves the rate capability of LiFePO₄. The effect of the content of FeP on the capacity of the carbon coated LiFePO₄ was different at different discharge rates. Increasing the content of FeP from 1.2 to 3.7 wt.% slightly decreases the capacity of LiFePO₄/C at low discharge rate (0.1C and 1C), but obviously increases the capacity of LiFePO₄/C when the discharge rate is increased to 5C. For the carbon free sample, even it also has 1.8 wt.% FeP, it still possesses poor capacity due to the large particle size of LiFePO₄ and the lack of conductivity. And too much iron phosphides lowers the discharge capacity of the electrode since they are inert for the deinsertion/insertion of lithium ion.     

Optimized solid-state synthesis of LiFePO4 cathode materials using ball-milling

Olivine-type LiFePO₄ cathode materials were synthesized by a solid-state reaction method and ball-milling. The ball-milling time, heating time and heating temperature are optimized. A heating temperature higher than 700 °C resulted in the appearance of impurity phase Fe₂P and growth of large particle, which was shown by high resolution X-ray diffraction and field emission scanning electron microscopy. The impurity phase Fe₂P exhibited a considerable capacity loss at the 1st cycle and a gradual increase in discharge capacity upon cycling. Moreover, it exhibited an excellent high-rate capacity of 104 mAh g⁻¹ at 3 C in spite of the large particle size. The optimum synthesis conditions for LiFePO₄ were ball-milling for 24 h and heat-treatment at 600 °C for 3 h. LiFePO₄/Li cells showed an enhanced cycling performance and a high discharge capacity of 160 mAh g⁻¹ at 0.1 C.     

Hydrothermal preparation of LiFePO4 nanocrystals mediated by organic acid

Well-crystallized LiFePO₄ nanoparticles have been directly synthesized in a short time via hydrothermal process in the presence of organic acid, e.g. citric acid or ascorbic acid. These acid-mediated LiFePO₄ products exhibit a phase-pure and nanocrystal nature with size about 50-100 nm. Two critical roles that the organic acid mediator plays in hydrothermal process are recognized and a rational mechanism is explored. After a post carbon-coating treatment at 600 °C for 1 h, these mediated LiFePO₄ materials show a high electrochemical activity in terms of reversible capacity, cycling stability and rate capability. Particularly, LiFePO₄ mediated by ascorbic acid can deliver a capacity of 162 mAh g⁻¹ at 0.1 C, 154 mAh g⁻¹ at 1 C, and 122 mAh g⁻¹ at 5 C. The crystalline structure, particle morphology, and surface microstructure were characterized by high-energy synchrotron X-ray diffraction (XRD), transmission electron microscopy (TEM) and scanning electron microscopy (SEM), and Raman spectroscopy, respectively. And the electrochemical properties were thoroughly investigated by galvanostatic test and electrochemical impedance spectroscopy (EIS).     

A simple,cheap soft synthesis routine for LiFePO4 using iron(III) raw material

An order olivine structure LiFePO₄ was synthesized with a simple rheological phase reaction (RPR) of LiOH·H₂O and FePO₄·4H₂O in the presence of PEG as a reductive agent and carbon source. A required amount of water was added to the starting materials to form the rheological precursor and decomposed at 700 °C to form the crystalline phase LiFePO₄ directly, without ball-milling, preparation of intermediates, pre-sintering and post-deposition treatment. Fine particles with an average particle size about 216 nm are examined by scanning electron microscopy (SEM) and optical particle size analyzer. An initial discharge capacity of 157 mAh g⁻¹ was achieved for the as-prepared LiFePO₄ material with a rate of 0.1C (17 mA g⁻¹), what's more, this material shows excellent specific capacity, charge–discharge efficiency and cycle efficiency at high current rates, almost no capacity loss can be observed up to 40 cycles with the rate of 1, 2 and 3C at room temperature. The simple, cheap process as well as the excellent high-rate performance makes this RPR method feasible commercially.     

Synthesis of carbon-coated LiFePO4 nanoparticles with high rate performance in lithium secondary batteries

A novel preparation technique was developed for synthesizing carbon-coated LiFePO₄ nanoparticles through a combination of spray pyrolysis (SP) with wet ball milling (WBM) followed by heat treatment. Using this technique, the preparation of carbon-coated LiFePO₄ nanoparticles was investigated for a wide range of process parameters such as ball-milling time and ball-to-powder ratio. The effect of process parameters on the physical and electrochemical properties of the LiFePO₄/C composite was then discussed through the results of X-ray diffraction (XRD) analysis, field-emission scanning electron microscopy (FE-SEM), transmission electron microscopy (TEM), the Brunauer-Emmet-Teller (BET) method and the use of an electrochemical cell of Li|1 M LiClO₄ in EC:DEC = 1:1|LiFePO₄. The carbon-coated LiFePO₄ nanoparticles were prepared at 500 °C by SP and then milled at a rotating speed of 800 rpm, a ball-to-powder ratio of 40/0.5 and a ball-milling time of 3 h in an Ar atmosphere followed by heat treatment at 600 °C for 4 h in a N₂ + 3% H₂ atmosphere. SEM observation revealed that the particle size of LiFePO₄ was significantly affected by the process parameters. Furthermore, TEM observation revealed that the LiFePO₄ nanoparticles with a geometric mean diameter of 146 nm were coated with a thin carbon layer of several nanometers by the present method. Electrochemical measurement demonstrated that cells containing carbon-coated LiFePO₄ nanoparticles could deliver markedly improved battery performance in terms of discharge capacity, cycling stability and rate capability. The cells exhibited first discharge capacities of 165 mAh g⁻¹ at 0.1 C, 130 mAh g⁻¹ at 5 C, 105 mAh g⁻¹ at 20 C and 75 mAh g⁻¹ at 60 C with no capacity fading after 100 cycles.     

Electrochemical properties of LiFePO4 prepared via hydrothermal route

LiFePO₄ as a cathode material for rechargeable lithium batteries was prepared by hydrothermal process at 170 °C under inert atmosphere. The starting materials were LiOH, FeSO₄, and (NH₄)₂HPO₄. The particle size of the obtained LiFePO₄ was 0.5 μm. The electrochemical properties of LiFePO₄ were characterized in a mixed solvent of ethylene carbonate and diethyl carbonate (1:1 in volume) containing 1.0 mol dm⁻³ LiClO₄. The hydrothermally synthesized LiFePO₄ exhibited a discharge capacity of 130 mA h g⁻¹, which was smaller than theoretical capacity (170 mA h g⁻¹). The annealing of LiFePO₄ at 400 °C in argon atmosphere was effective in increasing the discharge capacity. The discharge capacity of the annealed LiFePO₄ was 150 mA h g⁻¹.     

Effect of mechanical activation process parameters on the properties of LiFePO4 cathode material

Pure, nano-sized LiFePO₄ and carbon-coated LiFePO₄ (LiFePO₄/C) positive electrode (cathode) materials are synthesized by a mechanical activation process that consists of high-energy ball milling and firing steps. The influence of the processing parameters such as firing temperature, firing time and ball-milling time on the structure, particle size, morphology and electrochemical performance of the active material is investigated. An increase in firing temperature causes a pronounced growth in particle size, especially above 600 °C. A firing time longer than 10 h at 600 °C results in particle agglomeration; whereas, a ball milling time longer than 15 h does not further reduce the particle size. The electrochemical properties also vary considerably depending on these parameters and the highest initial discharge capacity is obtained with a LiFePO₄/C sample prepared by ball milling for 15 h and firing for 10 h at 600 °C. Comparison of the cyclic voltammograms of LiFePO₄ and LiFePO₄/C shows enhanced reaction kinetics and reversibility for the carbon-coated sample. Good cycle performance is exhibited by LiFePO₄/C in lithium batteries cycled at room temperature. At the high current density of 2C, an initial discharge capacity of 125 mAh g⁻¹ (73.5% of theoretical capacity) is obtained with a low capacity fading of 0.18% per cycle over 55 cycles.     

Synthesis and electrochemical properties of olivine LiFePO4 prepared by a carbothermal reduction method

LiFePO₄/C composite cathode material was prepared by carbothermal reduction method, which uses NH₄H₂PO₄, Li₂CO₃ and cheap Fe₂O₃ as starting materials, acetylene black and glucose as carbon sources. The precursor of LiFePO₄/C was characterized by differential thermal analysis and thermogravimetry. X-ray diffraction (XRD), scanning electron microscopy (SEM) micrographs showed that the LiFePO₄/C is olivine-type phase, and the addition of the carbon reduced the LiFePO₄ grain size. The carbon is dispersed between the grains, ensuring a good electronic contact. The products sintered at 700 °C for 8 h with glucose as carbon source possessed excellent electrochemical performance. The synthesized LiFePO₄ composites showed a high electrochemical capacity of 159.3 mAh g⁻¹ at 0.1 C rate, and the capacity fading is only 2.2% after 30 cycles.     

Synthesis and characterization of Carbon Nano Fiber/LiFePO4 composites for Li-ion batteries

Carbon Nano Fibers (CNFs) coated with LiFePO₄ particles have been prepared by a non-aqueous sol–gel technique. The functionalization of the CNFs by HNO₃ acid treatment has been confirmed by Raman and XPS analyses. The samples pure LiFePO₄ and LiFePO₄–CNF have been characterized by XRD, SEM, RAMAN, XPS and electrochemical analysis. The LiFePO₄–CNF sample shows better electrochemical performance compared to as-prepared LiFePO₄. LiFePO₄–CNF (10 wt.%) delivers a higher specific capacity (∼140 mAh g⁻¹) than LiFePO₄ with carbon black (25 wt.%) added after synthesis (∼120 mAh g⁻¹) at 0.1C.     

Improved high-rate charge/discharge performances of LiFePO4/C via V-doping

V-doped LiFePO₄/C cathode materials were prepared through a carbothermal reduction route. The microstructure was characterized by X-ray diffraction, X-ray photoelectron spectroscopy and scanning electron microscopy. The electrochemical Li⁺ intercalation performances of V-doped LiFePO₄/C were compared with those of undoped one through galvanostatic intermittent titration technique, cyclic voltamperometry, and electrochemical impedance spectrum. V-doped LiFePO₄/C showed a high discharge capacity of ∼70 mAh g⁻¹ at the rate of 20 C (3400 mA g⁻¹) at room temperature. The significantly improved high-rate charge/discharge capacity is attributed to the increase of Li⁺ ion “effective” diffusion capability.     

A study on the electrochemical characteristics of LiFePO4 cathode for lithium polymer batteries by hydrothermal method

Phospho-olivine LiFePO₄ cathode materials were prepared by hydrothermal reaction at 150 °C. Carbon black was added to enhance the electrical conductivity of LiFePO₄. LiFePO₄-C powders (0, 3, 5 and 10 wt.%) were characterized by X-ray diffraction (XRD) and transmission electron microscope (TEM). LiFePO₄-C/solid polymer electrolyte (SPE)/Li cells were characterized electrochemically by charge/discharge experiments at a constant current density of 0.1 mA cm⁻² in a range between 2.5 and 4.3 V vs. Li/Li⁺, cyclic voltammetry (CV) and ac impedance spectroscopy. The results showed that initial discharge capacity of LiFePO₄ was 104 mAh g⁻¹. The discharge capacity of LiFePO₄-C/SPE/Li cell with 5 wt.% carbon black was 128 mAh g⁻¹ at the first cycle and 127 mAh g⁻¹ after 30 cycles, respectively. It was demonstrated that cycling performance of LiFePO₄-C/SPE/Li cells was better than that of LiFePO₄/SPE/Li cells.     

Study of LiFePO4 cathode materials coated with high surface area carbon

LiFePO₄ is a potential cathode material for 4 V lithium-ion batteries. Carbon-coated lithium iron phosphates were prepared using a high surface area carbon to react precursors through a solid-state process, during which LiFePO₄ particles were embedded in amorphous carbon. The carbonaceous materials were synthesized by the pyrolysis of peanut shells under argon, where they were carbonized in a two-step process that occurred between 573 and 873 K. The shells were also treated with a proprietary porogenic agent with the goal of altering the pore structure and surface area of the pyrolysis products. The electrochemical properties of the as-prepared LiFePO₄/C composite cathode materials were systematically characterized by X-ray diffraction, scanning electron microscope, element mapping, energy dispersive spectroscopy, Raman spectroscopy, and total organic carbon (TOC) analysis. In LiFePO₄/C composites, the carbon not only increases rate capability, but also stabilizes capacity. In fact, the capacity of the composites increased with the specific surface area of carbon. The best result was observed with a composite made of 8.0 wt.% with a specific surface area of 2099 m² g⁻¹. When high surface area carbon was used as a carbon source to produce LiFePO₄, overall conductivity increased from 10⁻⁸ to 10⁻⁴ S cm⁻¹, because the inhibition of particle growth during the final sintering process led to greater specific capacity, improved cycling properties and better rate capability compared to a pure olivine LiFePO₄ material.     

LiFePO4 with enhanced performance synthesized by a novel synthetic route

Pure LiFePO₄ was synthesized by heating an amorphous LiFePO₄. The amorphous LiFePO₄ obtained through lithiation of FePO₄·xH₂O by using oxalic acid as a novel reducing agent at room temperature. FePO₄·xH₂O was prepared through co-precipitation by employing FeSO₄·7H₂O and H₃PO₄ as raw materials. X-ray diffraction (XRD), scanning electron microscopy (SEM) observations showed that LiFePO₄ composites with fine particle sizes between 100 nm and 200 nm, and with homogenous sizes distribution. The electrochemical performance of LiFePO₄ powder synthesized at 500 °C were evaluated using coin cells by galvanostatic charge/discharge. The synthesized LiFePO₄ composites showed a high electrochemical capacity of 166 mAh g⁻¹ at the 0.1C rate, and possessed a favorable capacity cycling maintenance at the 0.1C, 0.2C, 0.5C and 1C rate.     

Electrochemical properties of LiFePO4 prepared via ball-milling

LiFePO₄ cathode materials with distinct particle sizes were prepared by a planetary ball-milling method. The effects of particle size on the morphology, thermal stability and electrochemical performance of LiFePO₄ cathode materials were investigated. The ball-milling method decreased particle size, thereby reducing the length of diffusion and improving the reversibility of the lithium ion intercalation/deintercalation. It is worth noting that the small particle sample prepared using malonic acid as a carbon source achieved a high capacity of 161 mAh g⁻¹ at a 0.1 C rate and had a very flat capacity curve during the early 50 cycles. However, the big particle samples (∼400 nm) decayed more dramatically in capacity than the small particle size samples (∼200 nm) at high current densities. The improvement in electrode performance was mainly due to the fine particles, the small size distribution, and the increase in electronic conductivity as a result of carbon coating. The structure and morphology of the ground LiFePO₄ samples were characterized with XRD, FE-SEM, TEM, EDS, and DSC techniques.     

One-dimensional nanostructures as electrode materials for lithium-ion batteries with improved electrochemical performance

One-dimensional (1D) nanosize electrode materials of lithium iron phosphate (LiFePO₄) nanowires and Co₃O₄–carbon nanotube composites were synthesized by the hydrothermal method. The as-prepared 1D nanostructures were structurally characterized by X-ray diffraction, scanning electron microscopy, and transmission electron microscopy. We tested the electrochemical properties of LiFePO₄ nanowires as cathode and Co₃O₄–carbon nanotubes as anode in lithium-ion cells, via cyclic voltammetry and galvanostatic charge/discharge cycling. LiFePO₄ nanorod cathode demonstrated a stable performance over 70 cycles, with a remained specific capacity of 140 mAh g⁻¹. Nanocrystalline Co₃O₄–carbon nanotube composite anode exhibited a reversible lithium storage capacity of 510 mAh g⁻¹ over 50 cycles. 1D nanostructured electrode materials showed strong potential for lithium-ion batteries due to their good electrochemical performance.     

Physical and electrochemical properties of LiFePO4/C composite cathode prepared from various polymer-containing precursors

The goal of this research was to study the effect of various polymer-containing precursors on the performance of LiFePO₄/C composite. A coprecipitation method was applied to prepare a series of LiFePO₄/C materials by calcinating amorphous LiFePO₄ with various polymer compounds at 600 °C. The materials were characterized by X-ray diffraction, scanning electron microscopy, transmission electron microscopy, particle size analysis, thermal analysis, BET specific surface area, Raman spectral analysis and electrochemical methods. The results showed that the structure of polymer precursors played an important role in improving the performance of LiFePO₄/C composites. The residual carbon produced by the pyrolysis of polymers with functionalized aromatic groups exhibited a better capacity in the LiFePO₄/C composites. A polyaromatic compound, e.g. polystyrene, with more functionalized aromatic groups displayed improved performance because its decomposition temperature was close to the temperature of the LiFePO₄ phase transformation, which resulted in fine particle size and uniform carbon distribution on the composite surface. According to Raman spectral analysis, polystyrene with more aromatic groups has a lower I_D/I_G and sp³/sp² peak ratio indicating more highly graphite-like carbon formation during polymer pyrolysis and exhibited a better capacity.     

Cathode performance of olivine-type LiFePO4 synthesized by chemical lithiation

Chemical lithiation with LiI in acetonitrile was performed for amorphous FePO₄ synthesized from an equimolar aqueous suspension of iron powder and an aqueous solution of P₂O₅. An orthorhombic LiFePO₄ olivine structure was obtained by annealing a chemically lithiated sample at 550 °C for 5 h in Ar atmosphere. The average particle size remained at approximately 250 nm even after annealing. The lithium content in the sample was quantitatively confirmed by Li atomic absorption analysis and ⁵⁷Fe Mössbauer spectroscopy. While an amorphous FePO₄/carbon composite cathode has a monotonously decreasing charge–discharge profile with a reversible capacity of more than 140 mAh g⁻¹, the crystallized LiFePO₄/carbon composite shows a 3.4 V plateau corresponding to a two-phase reaction. This means that the lithium in the chemically lithiated sample is electrochemically active. Both amorphous FePO₄ and the chemically lithiated and annealed crystalline LiFePO₄ cathode materials showed good cyclability (more than 140 mAh g⁻¹ at the 40th cycle) and good discharge rate capability (more than 100 mAh g⁻¹ at 5.0 mA cm⁻²). In addition, the fast-charge performance was found to be comparable to that with LiCoO₂.