反应条件对双醛山药淀粉醛基含量的影响

以山药淀粉为原料,高碘酸盐为氧化剂制备双醛山药淀粉,考察了反应温度、反应时间、pH值、淀粉浆液质量分数,高碘酸钠与淀粉葡萄糖单元的摩尔比对醛基含量的影响。实验结果表明,制备醛基含量大于90%的双醛淀粉的适宜工艺条件为:反应温度40℃,反应时间4 h,pH值为4.0,淀粉浆液质量分数为20%,高碘酸钠与淀粉葡萄糖单元摩尔比为1.1:1,在此条件下醛基含量高达97.5%。     

双醛淀粉制备工艺的优化研究

采用高碘酸盐氧化玉米淀粉的方法制备双醛淀粉,探讨了pH值、高碘酸钠与淀粉摩尔比、高碘酸钠浓度、反应温度、反应时间及投料方式对双醛淀粉中醛基含量的影响,得出双醛淀粉制备工艺的优化条件。结果显示,在pH值为1.2～1.5、高碘酸钠与淀粉的摩尔比为1.1∶1、高碘酸钠浓度为0.5mol/L、反应温度在33～40℃之间、反应时间3h条件下,并采用将淀粉加入到高碘酸钠溶液中的投料方式,可得到高醛基含量的双醛淀粉。     

高碘酸钠氧化木薯淀粉制备双醛淀粉工艺研究

以NaIO_4作氧化剂,氧化木薯淀粉制备双醛淀粉的适宜工艺条件为:淀粉乳含量10%,高碘酸钠与淀粉物质的量之比1.1:1,反应溶液pH值3,反应温度40℃,搅拌反应3h。在选定的试验条件下,制备的双醛淀粉产品中双醛含量93.5%,产率96.7%。制得的双醛淀粉经红外光谱表征,波长1 750cm~(-1)处出现明显吸收峰,波长2 750cm~(-1)处出现弱吸收峰,说明产物中醛基的存在。     

木薯双醛淀粉的理化性质

使用高碘酸钠氧化木薯淀粉制备了醛基含量5%～85%的双醛淀粉(DAS-5～DAS-85),利用FT-IR、凝胶渗透色谱(GPC)、X射线衍射(XRD)、偏光显微镜、扫描电镜(SEM)研究了双醛淀粉的结构和性质,结果显示:木薯淀粉分子量高于1 000万,醛基含量为5%时淀粉重均分子量降为9300。氧化反应首先发生在淀粉非晶区,而后破坏结晶区,醛基含量高于39%时淀粉变为无定型结构。随醛基含量增加,双醛淀粉糊化温度升高,糊化焓减小,颗粒表面变粗糙,结构塌陷。在25℃下,质量分数为10%的DAS-85溶液放置6 h出现透明沉淀, DAS-53溶液放置12 h出现透明沉淀, DAS-39溶液48 h后仍澄清。     

大米双醛淀粉制备工艺的研究

双醛淀粉应用领域广泛,本文以大米淀粉为原料,用高碘酸钠作为氧化剂来制备大米双醛淀粉,从单因素实验到正交实验探索到大米淀粉双醛化的优化工艺条件:反应温度35℃、反应时间4h、反应pH=3.5、NaIO4水溶液浓度为0.3mol/L、高碘酸钠和原大米淀粉的摩尔比为1.1∶1;此条件下可以制备得到双醛化程度接近100%的大米淀粉。     

光促催化拟均相低温氧化法制备双醛淀粉

以马铃薯淀粉为原料,NaIO_4为氧化剂,用紫外光照催化拟均相制备双醛淀粉。通过单因素和正交试验优化得到最佳氧化条件为:反应温度为40℃,pH为3,反应时间为2.5 h,高碘酸钠浓度为0.5 mol/L。此时产品的醛基质量分数可达97.68%、产率为85.65%;经红外光谱、紫外可见光谱、偏光显微、色度和理化等的测定,结果表明所制备产物为双醛淀粉,且品质质量与市售品或文献值相符。用紫外光照射对拟均相低温氧化法制备DAS有明显促进作用,且波长短、功率高和效果好。在活化阶段对淀粉的活化有提高作用,且有紫外光活化使DAS产率从无光照的71.82%增加至82.01%,醛基质量分数从80.78%提高到92.87%,且光照活化效果顺序是254 nm365nm无光照;在氧化反应阶段紫外光照对NaIO_4氧化淀粉成DAS有促催化作用,紫外光照产率提高了5.66%~8.85%,醛基含量提高了2.53%~8.68%,而光照催化氧化效果顺序是254 nm/25 W254 nm/15 W365 nm/25 W365nm/15 W无光照。     

淀粉载体固定化脲酶的研究

脲酶是一种来源广泛的植物蛋白酶,能高效、专一的催化尿素分解.本文利用双醛淀粉(DAS)作为酶固定化载体对脲酶进行固定化.同时研究反应温度,反应时间,pH,载体的醛基含量,载体与酶的配比对固定化酶活性的影响.经实验确定,最佳工艺条件为:双醛淀粉载体醛基含量80%,反应pH值6.0,反应温度25℃,反应时间25h,酶与载体的配比为1:1(mL/g)     

正交优化制备双醛淀粉研究

双醛淀粉毒性低,化学活性高,广泛用于各种工业,是一种很重要化工原料,但我国对双醛淀粉开发和生产还处于起步阶段。该研究以玉米淀粉为原料,高碘酸钠为氧化剂,采用正交优化法对制备双醛淀粉工艺条件进行研究;最佳工艺条件为:反应温度为35℃,反应时间为3.5小时,高碘酸钠浓度为0.5 mol／L,pH值为4.0,高碘酸钠与淀粉摩尔比为1.1:1。     

超声波辅助法制备双醛淀粉复合膜及其性能研究

以马铃薯淀粉为原料,高碘酸钾为氧化剂制备双醛淀粉,然后添加一定的添加剂,采用流延法制备双醛淀粉复合膜。结果表明:超声处理能提高双醛淀粉醛基含量,当马铃薯淀粉质量分数为5%、高碘酸钾/淀粉质量比为1.4∶1时,醛基含量为62.39%;添加明胶的双醛淀粉复合膜表面光滑平整,力学性能高,综合性能好。     

双醛淀粉上浆剂的制备研究

利用高碘酸钠氧化可溶性淀粉制得双醛淀粉(DAS)，用碱滴定法，测其氧化度(醛基含量)．并研究不同反应时间、初始pH值、温度对产物氧化度的影响，确定最佳反应条件，分别是反应时间1.2h，初始pH值1．4．     

Modified Corn Starches with Improved Comprehensive Properties for Preparing Thermoplastics

A novel method of starch modification was developed to obtain thermoplastic starch plastics with improved comprehensive properties. Corn starch was oxidized under mild conditions using sodium periodate to prepare dialdehyde starch, which had an acceptable average molecular weight. The dialdehyde starch with 35.2% carbonyl content was reacted with different alcohols (methanol, ethanol, and glycol) to prepare a series of novel starch derivatives, whose structures were characterized by ¹H‐NMR and FT‐IR. The thermogravimetric analysis showed that these starch derivatives had an improved thermal stability compared with dialdehyde starch. Thermoplastic starch and its derivatives were prepared when water and glycerol were added as plasticizers. The modified thermoplastic starch and its derivatives had better mechanical properties than other modified starches, and lower humidity absorption than conventional thermoplastic starches. The highest tensile strength and elongation at break reached 17.5 MPa and 149%, respectively, and the highest humidity absorption was about 37%.     

Effect of acetylation on the properties of corn starch

Acetylated corn starches with different degrees of substitution (DS 0.85, DS 1.78, DS 2.89) were synthesized by the reaction of corn starch with acetic anhydride in the presence of acetic acid under varying reaction temperatures. The product was characterized by FTIR spectroscopy, ¹H NMR, X-ray diffraction and contact angle measurement. Acid-base titration and ¹H NMR methods were employed to determine the degree of substitution of product. FTIR spectroscopic analysis showed that the characteristic absorption intensities of esterified starch increased with increase in the degree of substitution, and the characterized peak of hydroxyl group almost disappeared in the spectrum of DS 2.89 acetylated starch. The detailed chemical microstructure of native starch and acetylated starch was confirmed by ¹H NMR, ¹³C NMR and ¹³C–¹H COSY spectra. Analysis of ¹H NMR spectra of acetylated starches was assigned accurately. Strong peaks in X-ray diffraction of acetylated starch revealed that new crystalline regions were formed. Compared with native starch, the hydrophobic performance of acetylated starch esters was increased. The contact angle of acetylated starch with DS 2.89 was 68.2°.     

双醛淀粉湿强剂的合成

研究了以木薯淀粉为原料、以高碘酸钠为氧化剂合成双醛淀粉的工艺条件，通过对不同氧化度双醛淀粉的红外光谱和结晶研究，对制备DAS的反应进程进行了探讨，结果表明，根据需要可制得不同氧化程度的双醛淀粉，与原淀粉相比其物理和化学性质都发生了很大的变化。     

甘薯交联淀粉的制备与结构表征

以三偏磷酸钠为交联剂,水分散法制备了甘薯交联淀粉,应用红外光谱、X射线衍射、扫描电镜和偏光显微镜等分析测试方法,观察和研究了不同取代度甘薯交联淀粉的颗粒形貌及其结晶结构。结果表明,产物取代度随交联反应时间的延长而增大;交联反应主要发生在淀粉分子的无定形区,在结晶区也有一定程度的反应;随着取代度的增大,淀粉颗粒表面发生了明显变化,同时出现了大小球体相分离的现象,说明了交联反应主要发生在甘薯淀粉颗粒的表面和大小球体间的联接处;交联淀粉的偏光十字清晰易见;1016.28cm-1的吸收峰强度加强,证实在淀粉中引入了磷酸根基团。     

马铃薯交联淀粉的制备与结构表征

以三偏磷酸钠为交联剂,水分散法制备了马铃薯交联淀粉,应用红外光谱、X射线衍射、扫描电镜和偏光显微镜等分析测试方法,观察和研究了不同取代度马铃薯交联淀粉的颗粒形貌及其结晶结构。结果表明,产物取代度随交联反应时间的延长而增大;交联反应主要发生在淀粉分子的无定形区,在结晶区也有一定程度的反应;随着取代度的增大,淀粉中受侵蚀的颗粒增多,颗粒表面的小凹痕数量明显增加,部分颗粒表面变粗糙,颗粒内部出现凹陷甚至爆裂;交联淀粉的偏光十字清晰易见;1 017.08cm-1的吸收峰强度加强,证实在淀粉中引入了磷酸根基团。     

乌冬面专用变性淀粉及其结构表征

采用交联―酯化―预糊化复合变性制备乌冬面专用改性淀粉,并与木薯原淀粉、交联淀粉及交联―酯化淀粉进行比较。结果表明,交联淀粉偏光显微及颗粒形貌没发生明显变化,交联变性并未破坏淀粉结晶结构;交联―酯化淀粉颗粒出现粘连和聚集现象,部分颗粒表面出现凹陷和裂纹现象;红外光谱表明,交联―酯化―预糊化复合变性淀粉在1 728 cm–1、1 247 cm–1附近出现新的吸收峰,分子内引入乙酰基团,X–射线衍射光谱显示,交联―酯化―预糊化复合变性淀粉在5.6°和22°处衍射峰强度减弱,A型特征峰加强,结晶类型由"C"型向"A"型转变;交联―酯化淀粉经预糊化处理后,淀粉颗粒膨胀破裂,结晶结构受到彻底破坏,淀粉偏光十字消失,但预糊化处理未破坏淀粉分子化学键。     

响应面试验优化交联马铃薯淀粉制备工艺及体外消化性质研究

以马铃薯淀粉为原料,三偏磷酸钠(STMP)和三聚磷酸钠(STPP)以质量比99:1的比例混合作为交联剂,制备交联马铃薯淀粉。以结合磷含量为指标,交联剂用量、反应pH值、反应温度和反应时间为因素,运用响应面法进行优化,确定最优工艺条件为交联剂用量为淀粉干质量的16%、反应时间4.5h、反应pH11.5、反应温度55℃;在最优工艺条件的基础上,通过改变交联剂用量制备一系列不同结合磷含量的交联淀粉并研究它们的体外消化性质。结果表明,随着交联马铃薯淀粉结合磷含量的增加,其所含的抗性淀粉也随之增加。     

交联氧化乙酰化蜡质玉米淀粉性质的研究

以蜡质玉米淀粉为原料、三偏磷酸钠为交联剂、次氯酸钠为氧化剂、醋酸酐为乙酰化试剂,采用湿法工艺制备交联氧化乙酰化复合变性淀粉,并利用扫描电镜(SEM)及红外光谱仪(FT-IR)分析其淀粉颗粒的形貌及结构。结果显示:复合变性处理后的淀粉白度升高至97.2,糊透光率升高至71.0%,耐酸及抗剪切性能也有所改善。扫描电镜图表现了淀粉颗粒形貌的变化,红外光谱图中展现的各基团的特征吸收峰表明其分子结构发生了改变。蜡质玉米淀粉采用复合变性的处理手段,有益于增强其在食品加工领域的应用价值。     

酸法制备多孔淀粉及其特性研究

以玉米淀粉为原料,分别用不同浓度的盐酸溶液和复合酶在一定条件下制备多孔淀粉。对制得的多孔淀粉进行形态结构和部分性质的测定,并对两种方式处理所得产品的吸水性和吸油性进行对比。结果显示,料液比1∶4、8%浓度的盐酸溶液、45℃下水浴反应20h制备的多孔淀粉在吸水和吸油性能上与酶法制备的多孔淀粉较为相似,同时相对于原淀粉性能有很大的提高。扫描电子显微镜(SEM)显示,酶法制备的多孔淀粉表面布有类似蜂窝状的孔洞或凹坑,而酸法制得的多孔淀粉颗粒具有随机性,效果不如酶法处理。与原淀粉相比,酸法制备的多孔淀粉糊化开始温度略微升高,而峰值黏度有很大降低。酸法制备多孔淀粉的方法简单廉价,相对酶法具有工业生产价值及较高的价格优势。     

制备羧甲基淀粉的研究

羧甲基淀粉是重要的变性淀粉之一，用途广泛。本研究用乙醇溶剂法制备羧甲基淀粉。结果表明，增加一氯醋酸用量，降低淀粉乳浓度，能提高醚化取代度；氢氧化钠用量和水份含量对反应影响显著，选用适当的量能有效地促进醚化反应；在一定范围内，随着反应温度升高，反应时间延长，取代度随之增高。乙醇溶剂法能有效地抑制淀粉在反应过程中糊化，反应进行均匀，并且具有反应时间短、操作简单，易于控制，能制得高取代度、高质量产品等优点。