Effect of Y on microstructure evolution and mechanical properties of Mg−4Li−3Al alloys

To obtain magnesium alloys with a low density and improved mechanical properties, Y element was added into Mg−4Li−3Al (wt.%) alloys, and the effect of Y content on microstructure evolution and mechanical properties was investigated by using optical microscopy, scanning electron microscopy and tensile tests. The results show that mechanical properties of as-cast Mg−4Li−3Al alloys with Y addition are significantly improved as a result of hot extrusion. The best comprehensive mechanical properties are obtained in hot-extruded Mg−4Li−3Al−1.5Y alloy, which possesses high ultimate tensile strength (UTS=248 MPa) and elongation (δ=27%). The improvement of mechanical properties of hot-extruded Mg−4Li−3Al−1.5Y alloy was mainly attributed to combined effects of grain refinement, solid solution strengthening and precipitation strengthening.     

Effects of Mg content on microstructure and mechanical properties of low Zn-containing Al−xMg−3Zn−1Cu cast alloys

Effects of Mg content on the microstructure and mechanical properties of low Zn-containing Al?xMg? 3Zn?1Cu cast alloys (x=3?5, wt.%) were investigated. As Mg content increased in the as-cast alloys, the grains were refined due to enhanced growth restriction, and the formation of η-Mg(AlZnCu)₂ and S-Al₂CuMg phases was inhibited while the formation of T-Mg₃₂(AlZnCu)₄₉ phase was promoted when Mg content exceeded 4 wt.%. The increase of Mg content encumbered the solution kinetics by increasing the size of eutectic phase but accelerated and enhanced the age-hardening through expediting precipitation kinetics and elevating the number density of the precipitates. As Mg content increased, the yield strength and tensile strength of the as-cast, solution-treated and peak-aged alloys were severally improved, while the elongation of the alloys decreased. The tensile strength and elongation of the peak-aged Al?5Mg?3Zn?1Cu alloy exceed 500 MPa and 5%, respectively. Precipitation strengthening implemented by T′ precipitates is the predominant strengthening mechanism in the peak-aged alloys and is enhanced by increasing Mg content.     

Effect of Al addition on microstructure and mechanical properties of Mg−Gd−Zn alloys

The microstructure evolution and mechanical properties of Mg?15.3Gd?1Zn alloys with different Al contents (0, 0.4, 0.7 and 1.0 wt.%) were investigated. Microstructural analysis indicates that the addition of 0.4 wt.% Al facilitates the formation of 18R-LPSO phase (Mg₁₂Gd(Al, Zn)) in the Mg?Gd?Zn alloy. The contents of Al₁₁Gd₃ and Al₂Gd increase with the increase of Al content, while the content of (Mg, Zn)₃Gd decreases. After homogenization treatment, (Mg, Zn)₃Gd, 18R-LPSO and some Al₁₁Gd₃ phases are transformed into the high-temperature stable 14H-LPSO phases. The particulate Al?Gd phases can stimulate the nucleation of dynamic recrystallization by the particle simulated nucleation (PSN) mechanism. The tensile strength of the as-rolled alloys is improved remarkably due to the grain refinement and the fiber-like reinforcement of LPSO phase. The precipitation of the β′ phase in the peak-aged alloys can significantly improve the strength. The peak-aged alloy containing 0.4 wt.% Al achieves excellent mechanical properties and the UTS, YS and elongation are 458 MPa, 375 MPa and 6.2%, respectively.     

Effects of minor Sc and Zr additions on mechanical properties and microstructure evolution of Al−Zn−Mg−Cu alloys

The effects of minor Sc and Zr additions on the mechanical properties and microstructure evolution of Al−Zn−Mg−Cu alloys were studied using tensile tests, scanning electron microscopy (SEM) and transmission electron microscopy (TEM). The ultimate tensile strength of the peak-aged Al−Zn−Mg−Cu alloy is improved by about 105 MPa with the addition of 0.10% Zr. An increase of about 133 MPa is observed with the joint addition of 0.07% Sc and 0.07% Zr. For the alloys modified with the minor addition of Sc and Zr (0.14%), the main strengthening mechanisms of minor addition of Sc and Zr are fine-grain strengthening, sub-structure strengthening and the Orowan strengthening mechanism produced by the Al₃(Sc,Zr) and Al₃Zr dispersoids. The volume of Al₃Zr particles is less than that of Al₃(Sc,Zr) particles, but the distribution of Al₃(Sc,Zr) particles is more dispersed throughout the matrix leading to pinning the dislocations motion and restraining the recrystallization more effectively.     

Effect of Sn content on microstructure and tensile properties of as-cast and as-extruded Mg−8Li−3Al−(1,2,3)Sn alloys

The effects of Sn content on microstructure and tensile properties of as-cast and as-extruded Mg−8Li−3Al− (1,2,3)Sn (wt.%) alloys were investigated by X-ray diffractometry (XRD), optical microscopy (OM), scanning electron microscopy (SEM) and tensile test. It is found that, as-cast Mg−8Li−3Al−(1,2,3)Sn alloys consist of α-Mg+β-Li duplex matrix, MgLiAl₂ and Li₂MgSn phases. Increasing Sn content leads to grain refinement of α-Mg dendrites and increase in content of Li₂MgSn phase. During hot extrusion, complete dynamic recrystallization (DRX) takes place in β-Li phase while incomplete DRX takes place in α-Mg phase. As Sn content is increased, the volume fraction of DRXed α-Mg grains is increased and the average grain size of DRXed α-Mg grains is decreased. Increasing Sn content is beneficial to strength but harmful to ductility for as-cast Mg−8Li−3Al−(1,2,3)Sn alloys. Tensile properties of Mg−8Li−3Al− (1,2,3)Sn alloys are improved significantly via hot extrusion and Mg−8Li−3Al−2Sn alloy exhibits the best tensile properties.     

Effect of Gd content on microstructure and dynamic mechanical properties of solution-treated Mg−xGd−3Y−0.5Zr alloy

The effect of Gd content ranging from 6.5 wt.% to 8.5 wt.% on microstructure evolution and dynamic mechanical behavior of Mg?xGd?3Y?0.5Zr alloys was investigated by optical microscopy, X-ray diffraction, scanning electron microscopy and split Hopkinson pressure bar. The microstructure of as-cast Mg?xGd?3Y?0.5Zr alloys indicates that the addition of Gd can promote grain refinement in the casting. Due to the rapid cooling rate during solidification, a large amount of non-equilibrium eutectic phase Mg₂₄(Gd,Y)₅ appears at the grain boundary of as-cast Mg?xGd?3Y?0.5Zr alloys. After solution treatment at 520 °C for 6 h, the Mg₂₄(Gd,Y)₅ phase dissolves into the matrix, and the rare earth hydrides (REH) phase appears. The stress?strain curves validate that the solution-treated Mg?xGd?3Y?0.5Zr alloys with optimal Gd contents maintain excellent dynamic properties at different strain rates. It was concluded that the variation of Gd content and the agglomeration of residual REH particles and dynamically precipitated fine particles are key factors affecting dynamic mechanical properties of Mg?xGd?3Y?0.5Zr alloys.     

Effects of Sn on microstructure of as-cast and as-extruded Mg–9Li alloys

The effects of Sn addition on the microstructure of as-cast and as-extruded Mg–9Li alloys were investigated. The results show that α-Mg, β-Li, Li₂MgSn, and Mg₂Sn are primary phases in the microstructures of the as-cast and as-extruded Mg–9Li–xSn (x=0, 5; in mass fraction, %) alloys. Li₂MgSn phase evolves from continuously net-like structure in the as-cast state to fine granular in the as-extruded state. After the extrusion, Mg–9Li–5Sn alloy has finer microstructures. Li₂MgSn or Mg₂Sn compound can act as the heterogeneous nucleation sites for dynamic recrystallization during the extrusion due to the crystallography matching relationship. Extrusion deformation leads to dynamic recrystallization, which results in the grain refinement and uniform distribution. The as-extruded Mg–9Li–5Sn alloy possesses the lowest grain size of 45.9 μm.     

Effects of Zn content on as-cast microstructure and mechanical properties of Mg-xZn-4A 1 alloys containing TiC and rare earth elements

The effects of Zn content on the as-cast microstructure and mechanical properties of Mg-xZn-4Al alloys containing TiC and rare earth elements were investigated by optical microscopy（OM）, scanning electron microscopy（SEM） analysis, X-ray diffraction （XRD） analysis and tensile test. The results show that Zn content which increased from 8% to 12% does not obviously influence on the alloy phase type of the Mg-xZn-4Al experimental alloys containing 0.25%RE and 1%TiC, but with Zn content increasing from 8% to 12%, the amount of Mg32（Al,Zn）49 phase in the as-cast microstructure of the experimental alloys increases and its distribution becomes more continuous. In addition, the Mg-10Zn-4Al alloy containing 0.25%RE and 1TiC has the highest ultimate tensile strength at room temperature and 150 ℃ and highest yield strength and elongation at 150 ℃ Furthermore, with Zn content increasing from 8% to 12%, the yield strength and elongation of Mg-xZn-4Al experimental alloys containing 0.25%RE and 1%TiC increase and decrease at room temperature, respectively.     

Simulation on microstructure evolution and mechanical properties of Mg−Y alloys: Effect of trace Y

The influence of trace Y on the microstructure evolution and mechanical properties of Mg_100?xY_x (x=0.25, 0.75, 1.5, 3, 4, 5, at.%) alloys during solidification process was investigated via molecular dynamics (MD) simulations. The results show that the Mg_100?xY_x alloys are mainly characterized by a face-centered cubic (FCC) crystal structure; this is different from pure metal Mg, which exhibits a hexagonal close packed (HCP) structure at room temperature. Among these alloys, Mg_99.25Y_0.75 has a larger proportion of FCC cluster structures, with the highest fraction reaching 56.65%. As the content of the Y increases up to 5 at.% (Mg₉₅Y₅ alloy), the amount of amorphous structures increases. The mechanical properties of the Mg_100?xY_x alloys are closely related to their microstructures. The Mg_99.25Y_0.75 and Mg₉₇Y₃ alloys exhibit the highest yield strengths of 1.86 and 1.90 GPa, respectively. The deformation mechanism of the Mg?Y alloys is described at the atomic level, and it is found that a difference in the FCC proportion caused by different Y contents leads to distinct deformation mechanisms.     

Effect of Al addition on microstructure and mechanical properties of Mg−Zn−Sn−Mn alloy

The microstructure and properties of the as-cast, as-homogenized and as-extruded Mg−6Zn−4Sn−1Mn (ZTM641) alloy with various Al contents (0, 0.5, 1, 2, 3 and 4 wt.%) were investigated by OM, XRD, DSC, SEM, TEM and uniaxial tensile tests. The results show that when the Al content is not higher than 0.5%, the alloys are mainly composed of α-Mg, Mg₂Sn, Al₈Mn₅ and Mg₇Zn₃ phases_. When the Al content is higher than 0.5%, the alloys mainly consist of α-Mg, Mg₂Sn, MgZn, Mg₃₂(Al,Zn)₄₉, Al₂Mg₅Zn₂, Al₁₁Mn₄ and Al₈Mn₅ phases. A small amount of Al (≤1%) can increase the proportion of fine dynamic recrystallized (DRXed) grains during hot-extrusion process. The room- temperature tensile test results show that the ZTM641−1Al alloy has the best comprehensive mechanical properties, in which the ultimate tensile strength is 332 MPa, yield strength is 221 MPa and the elongation is 15%. Elevated- temperature tensile test results at 150 and 200 °C show that ZTM641−2Al alloy has the best comprehensive mechanical properties.     

Effect of Gd on microstructure,mechanical properties,and corrosion behavior of as-homogenized Mg−8Li−3Al−2Zn−0.2Zr alloy

The microstructure observation, tensile test, electrochemical measurement, and corrosion morphology characterization were conducted to study the effect of Gd on the microstructure, mechanical properties, and corrosion behavior of as-homogenized Mg?8Li?3Al?2Zn?0.2Zr (LAZ832?0.2Zr) alloy. The addition of trace Gd can improve the mechanical properties of as-homogenized LAZ832?0.2Zr alloy by refining the microstructure, reducing the content of AlLi softening phase, and forming Al₂Gd strengthening phase. Meanwhile, the addition of trace Gd can weaken the microgalvanic corrosion between matrix phase and AlLi phase, inhibit the galvanic corrosion between α-Mg phase and β-Li phase, and result in the formation of dense oxide film containing Gd₂O₃, thereby improving the corrosion resistance of the alloy. When the Gd content is 1.0 wt.%, the alloy shows the best comprehensive properties with the ultimate tensile strength of 189.8 MPa, elongation of 42.3%, and corrosion rate (determined by hydrogen evolution) of 0.86 mm·a^?1.     

Effects of trace Ag on precipitation behavior and mechanical properties of extruded Mg−Gd−Y−Zr alloys

The effects of trace Ag element on the precipitation behaviors and mechanical properties of the Mg−7.5Gd− 1.5Y−0.4Zr (wt.%) alloy by means of tensile test, X-ray diffractometry, scanning electron microscopy, electron backscattered diffractometry, and scanning transmission electron microscopy. There is an unusual texture (〈0001〉//extrusion direction) in the extruded Mg−Gd−Y−Zr alloys containing 0.5 wt.% Ag. During the aging periods at 225 °C, the addition of the trace Ag does not form new precipitates, just accelerates aging kinetics, and refines β′ precipitates, thereby increasing the number density of the β′ precipitates by Ag-clusters. Moreover, the Mg−Gd−Y−Zr alloy containing 0.5 wt.% Ag shows the most excellent synergy of strength and plasticity (408 MPa of ultimate tensile strength, 265 MPa of yield strength, and 12.9% of elongation to failure) after peak-aging.     

Effects of Al content on the corrosion properties of Mg–4Y–xAl alloys

The corrosion performances of Mg–4Y–xAl (x = 1, 2, 3, and 4 wt%) alloys in the 3.5% NaCl electrolyte solution are investigated by electrochemical tests, weight loss measurement and corrosion morphology observation. The results indicate that corrosion modes for the alloys are localized corrosion and the filiform type of attack. With Al concentration increasing from 1 to 4 wt%, the corrosion rate of Mg–4Y–xAl alloys decreases firstly and then increases, and WA42 alloy shows the best corrosion resistance. The addition of Al element to Mg–4Y alloys leads to the formation of Al₂Y and Al₁₁Y₃ intermetallic compounds and reduces the proportion of Mg₂₄Y₅ phase. Corrosion resistance of the Mg–4Y–xAl alloys mainly depends on the size and distribution of the second phases. Besides, the addition of excessive Al can greatly consumes the Y element in the matrix, thus leading to a less protective film on the alloys. The effect of the relative Volta potential changes between the second phases and α-Mg on corrosion resistance of Mg–4Y–xAl alloys is insignificant. The main corrosion products of the Mg–4Y–xAl alloys are Mg(OH)₂, Mg₃(OH)₅Cl·4H₂O, Mg_0.72Al_0.28(CO₃)_0.15(OH)_1.98(H₂O)_0.48, and Mg₄Al₂(OH)₁₂CO₃·3H₂O.     

Effects of titanium addition on structural,mechanical, tribological,and corrosion properties of Al−25Zn−3Cu and Al−25Zn−3Cu−3Si alloys

To investigate the effect of grain refinement on the material properties of recently developed Al−25Zn−3Cu based alloys, Al−25Zn−3Cu, Al−25Zn−3Cu−0.01Ti, Al−25Zn−3Cu−3Si and Al−25Zn−3Cu−3Si−0.01Ti alloys were produced by permanent mold casting method. Microstructures of the alloys were examined by SEM. Hardness and mechanical properties of the alloys were determined by Brinell method and tensile tests, respectively. Tribological characteristics of the alloys were investigated by a ball-on-disc type test machine. Corrosion properties of the alloys were examined by an electrochemical corrosion experimental setup. It was observed that microstructure of the ternary A1−25Zn−3Cu alloy consisted of α, α+η and θ (Al₂Cu) phases. It was also observed that the addition of 3 wt.% Si to A1−25Zn−3Cu alloy resulted in the formation of silicon particles in its microstructure. The addition of 0.01 wt.% Ti to the Al−25Zn−3Cu and Al−25Zn−3Cu−3Si alloys caused a decrement in grain size by approximately 20% and 39% and an increment in hardness from HRB 130 to 137 and from HRB 141 to 156, respectively. Yield strengths of these alloys increased from 278 to 297 MPa and from 320 to 336 MPa while their tensile strengths increased from 317 to 340 MPa and from 334 to 352 MPa. Wear resistance of the alloys increased, but corrosion resistance decreased with titanium addition.     

Effects of extrusion and heat treatments on microstructure and mechanical properties of Mg–8Zn–1Al–0.5Cu–0.5Mn alloy

The effects of extrusion and heat treatments on the microstructure and mechanical properties of Mg–8Zn–1Al–0.5Cu– 0.5Mn magnesium alloy were investigated. Bimodal microstructure is formed in this alloy when it is extruded at 230 and 260 °C, and complete DRX occurs at the extruding temperature of 290 °C. The basal texture of as-extruded alloys is reduced gradually with increasing extrusion temperature due to the larger volume fraction of recrystallized structure at higher temperatures. For the alloy extruded at 290 °C, four different heat treatments routes were investigated. After solution + aging treatments, the grains sizes become larger. Finer and far more densely dispersed precipitates are found in the alloy with solution + double-aging treatments compared with alloy with solution + single-aging treatment. Tensile properties are enhanced remarkably by solution + double-aging treatment with the yield strength, tensile strength and elongation being 298 MPa, 348 MPa and 18%, respectively. This is attributed to the combined effects of fine dynamically recrystallized grains and the uniformly distributed finer precipitates.     

The effects of Sc on the microstructure and mechanical properties of hypo-eutectic Al−Si alloys

The eutectic Si microstructure in Al-8.5wt.%Si alloy was changed from large flakes to fine lamellar when the Sc amount in the alloy reached 0.2 wt.%. 0.8wt.%Sc was optimal in terms of attaining the best modification effect. Study on the distribution of the modifiers and measurement of the surface tension of Al-8.5wt.%Si alloy melt with added Sr, Na, and Sc modifiers, respectively, reveals that Sc modifies eutectic Si by a decrease of surface tension, while Sr and Na modify eutectic Si mainly by an impurity-induced twinning mechanism. Al-8.5wt.%Si-0.4wt.%Sc alloy displayed approximately 50 and 70% increases in tensile strength and elongation, respectively, over Al-8.5wt.%Si alloy in the cast state. It also presented approximately 65 and 70% increases in tensile strength and elongation, respectively, over Al-8.5wt.%Si alloy at a ppt heat-treated state at 200°C for 3 h.     

Effects of nano-sized TiB2 particles and Al3Zr dispersoids on microstructure and mechanical properties of Al–Zn–Mg–Cu based materials

The effects of TiB₂ and Zr on the microstructure, aging response and mechanical properties of hot-extruded Al–Zn–Mg–Cu based materials were investigated and compared by multi-scale microstructure characterization techniques. The results showed that proper addition of TiB₂ particles could refine grain size during solidification, promote dynamic recrystallization during extrusion, and inhibit grain growth during solution treatment. Meanwhile, Zr addition had minor influence on the grain refinement during solidification, but could effectively suppress recrystallization and grain growth compared with the Zr-free alloy. Furthermore, the TiB₂ addition could simultaneously enhance the aging kinetics and peak-aged hardness of the materials. Comparatively, Zr addition could also improve the peak-aged hardness with minor effect on the aging kinetics of the materials. Finally, the quench sensitivity, elastic modulus and tensile properties of the materials were compared and studied. Specifically, the relationship between the microstructure and mechanical properties, and the strengthening mechanisms were discussed in detail.     

Effect of Y addition on microstructure and mechanical properties of Mg–Zn–Mn alloy

The effects of Y on the microstructure and mechanical properties of Mg–6Zn–1Mn alloy were investigated. The results show that the addition of Y has significant effect on the phase composition, microstructure and mechanical properties of Mg–6Zn–1Mn alloy. Varied phases compositions, including Mg₇Zn₃, I-phase (Mg₃YZn₆), W-phase (Mg₃Y₂Zn₃) and X-phase (Mg₁₂YZn), are obtained by adjusting the Zn to Y mass ratio. Mn element exists as the fine Mn particles, which are well distributed in the alloy. Thermal analysis and microstructure observation reveal that the phase stability follows the trend of X>W>I>Mg₇Zn₃. In addition, Y can improve the mechanical properties of Mg–Zn–Mn alloy significantly, and the alloy with Y content of 6.09% has the best mechanical properties. The high strength is mainly due to the strengthening by the grain size refinement, dispersion strengthening by fine Mn particles, and introduction of the Mg–Zn–Y ternary phases.     

Microstructure and mechanical properties of friction stir processed Al−Mg2Si alloys

The microstructure and mechanical properties of friction stir processed Al−Mg₂Si alloys were studied by TEM and EBSD. The results showed that an increase in the tool rotation speed (300−700 r/min) led to a decrease in the defect area (from 10.5 mm² to zero), whereas the defect area demonstrated the opposite trend (increased to 1.5 mm² from zero) upon further increasing the rotation speed (700−1200 r/min). The types of defects were transformed from tunnel defects to fusion defects as the rotational speed increased. The coarse Mg₂Si dendrites were broken and fine particles (smaller than 10 μm) formed in the weld nugget (WN). The amount of low-angle grain boundaries increased significantly from 57.7% to 83.6%, which was caused by an increase in the content of the deformed structure (from 1.7% to 13.6%). The hardness, ultimate tensile strength (UTS) and elongation were all greatly improved for the weld nugget. The hardness values of the WNs had the following order: R300<R1200<R500<R900<R700. The UTS and elongation had the following order: BM (base material)<R300<R1200<R500<R900<R700. The UTS and the elongation for the WN were increased by one and three times, respectively.     

Effect of Y content on microstructure and mechanical properties of 2519 aluminum alloy

The effects of yttrium（Y） content on precipitation hardening, elevated temperature mechanical properties and morphologies of 2519 aluminum alloy were investigated by means of microhardness test, tensile test, optical microscopy（OM）, transmission electron microscopy（TEM） and scanning electron microscopy（SEM）. The results show that the tensile strength increases from 485 MPa to 490 MPa by increasing Y content from 0 to 0.10%（mass fraction） at room temperature, and from 155 MPa to 205 MPa by increasing Y content from 0 to 0.20% at 300 ~C. The high strength of 2519 aluminum alloy is attributed to the high density of fine 0＇ precipitates and intermetallic compound AICuY with high thermal stability. Addition of Y above 0.20% in 2519 aluminum alloy may induce the decrease in the tensile strength both at room temperature （20 ℃） and 300℃.