The Effect of SiO_2 Additive on Super-hydrophilic Property of TiO_2-SiO_2 Thin Film by Sol-gel Method

TiO2-SiO2 thin films have been prepared on slide glass substrates by sol-gel method, and the effect of SiO2 additive on photo-generated hydrophilicity of TiO2 thin film was investigated by measuring the contact angle of water, the microstructure, the transmittance, the photocatalytic activity and the specific surface area . The results showed that 10mol% of SiO2 additive was the most effective for decreasing contact angle of water. The SiO2 additive of less than 30mol% has a suppressive effect on the crystal growth of anatase in calcinations, resulting in a large surface area. Consequently, the super-hydrophilicity was improved.     

TiO_2薄膜的亲水性及光催化自清洁效果

以溶胶-凝胶法为基础,在普通玻璃表面制备了具有纳米尺寸气孔、纳米及微米尺寸复合气孔结构的TiO2薄膜或TiO2/SiO2复合薄膜,并考察了它们的亲水性能及表面经空气中灰尘污染后,其超亲水性能在紫外光照射下的恢复能力。所有纯TiO2薄膜于制备后测试的表面水接触角均达到0°。SiO2的掺杂量较小（10%）时,SiO2的掺入增大了薄膜的水接触角,但随着SiO2掺杂量的增大,接触角减小,可达到超亲水效果。表面污染的薄膜经紫外光照射后,其超亲水性的光致恢复能力基本不受前驱体溶胶的陈化时间、SiO2掺杂浓度、表面形态的影响,但与薄膜的光催化活性有关。4层以上的薄膜或带有SiO2中间隔离层的薄膜由于可以抑制玻璃基底中Na＋扩散至薄膜表面,光催化降解灰尘污染物的能力较高,紫外光照射后均能恢复其超亲水性能。     

纳米TiO2-SiO2自清洁复合薄膜制备及其光催化机理

采用溶胶-凝胶法在普通载玻片上制备TiO2-SiO2复合薄膜,研究SiO2添加量对光催化活性的影响,探讨TiO2光催化的机理．结果表明：光催化性随SiO2含量的增加而增加。但SiO2添加量过大,煅烧过程中对TiO2锐钛矿相晶粒生长有抑制作用,而且光催化活性有所下降．当SiO2添加量为30％时,在紫外光照1h时TiO2-SiO2薄膜的光催化活性最佳．     

在线常压化学气相沉积方法制备TiO_2自洁薄膜玻璃(英文)

利用常压化学气相沉积技术,在浮法玻璃线上制备了TiO2自洁薄膜玻璃。研究了水和氧气对薄膜沉积速率的影响,结果表明水和氧气的加入增加了薄膜的沉积速率。分别用原子力显微镜和X-射线衍射分析仪研究了薄膜的表面形貌和晶型结构,薄膜表面的平均粗糙度为84 nm,其晶型由锐钛矿和金红石组成。同时还研究了自洁玻璃的光催化活性和亲水性,随着紫外光照时间的增加,薄膜的光催化活性增加且对水的接触角由光照前的54°降到光照后的6°。     

TiO2／SiO2核壳结构微粒的合成及超疏水防紫外线功能织物的制备

以正硅酸乙酯为前驱体,采用溶胶-凝胶法在纳米TiO2表面包覆SiO2壳层,制备TiO2／SiO2核壳结构复合微粒,并将其负载在涤纶织物上,然后对织物进行疏水化处理,得到具有超疏水和防紫外线双重功能的织物．采用透射电子显微镜对复合微粒进行了表征;采用扫描电子显微镜对涤纶及处理后的涤纶织物的表面形貌进行了观察;采用视频光学接触角测量仪对涤纶织物表面的润湿性能进行测试;对织物超疏水性能的稳定性以及织物的紫外线防护性能进行了研究．结果表明：TiO2／SiO2复合微粒在纤维表面的负载不仅极大地提高了纤维表面的粗糙性,有利于超疏水表面的形成,并且由于TiO2的引入使织物获得了良好的紫外线防护性能;SiO2壳层对TiO2的包覆降低了TiO2的光催化作用,从而有效地提高了超疏水表面的紫外光照射稳定性．     

Influence of Excessive SiO2 or TiO2 on the Electric Properties of

The dependence of electrical properties of Ba0.92Ca0.08TiO3 PTCceramics on the SiO2 or TiO2 content was studied. The dependence of room temperature resistivity on the SiO2 content was determined by the variation of the microstructure of Ba0.92Ca0.08TiO3 PTC ceramics. It was shown that a small amount of excessive TiO2 (2mol%) added could increase the dielectric constant of materials, and it results in a reducing of the potential height (e*φ) of grain boundary. Thus, samples with particularly low room temperature resistivity were obtained. The relationship of PTC effect with the TiO2 content was also discussed by using the chemistry defect theory. The inferior PTC effect caused by excessive TiO2 may be concerned with the behavior of oxygen vacancies in the grains of ceramics.     

PVC建筑膜材的表面处理及其亲水性能研究

为制备具有亲水和防污自清洁性能的PVC建筑薄膜,在经低温等离子体改性的PVC薄膜表面涂覆SiO2作为隔离层,然后采用旋涂法将TiO2涂覆于薄膜表面,制备得到PVC/SiO2/TiO2复合膜。利用XRD、FTIR、SEM、EDS等测试手段对复合膜的形貌和结构进行表征,并用接触角测试仪测定了其亲水性能,经紫外光照后,复合膜的接触角由42.2°降为10.9°,结果表明TiO2层的涂覆大大地提高了PVC薄膜的亲水性能。     

TiO2/SiO2复合气凝胶的制备与传热特性

针对SiO2气凝胶红外遮光性能差的问题,以纳米二氧化钛作为掺杂剂,以正硅酸乙酯(TEOS)为原料,采用溶胶-凝胶工艺和非超临界干燥方法制备了不同TiO2掺杂量的纳米孔改性SiO2气凝胶复合材料,研究了pH值和乙醇含量对凝胶时间的影响,并采用SEM、TEM和BET方法分别对凝胶的表面形貌和孔结构进行了分析表征.结果表明,当pH为6时,乙醇/TEOS为8∶1(摩尔比)时,可得到掺杂均匀、完整的TiO2/SiO2凝胶;热处理后的复合气凝胶具有网状纳米孔结构;当掺杂量小于5％时,干凝胶平均孔径为20～50 nm,比表面积均大于1 000 m2/g.通过红外透过率及消光性能比较,TiO2掺杂SiO2干凝胶复合材料的红外光屏蔽功能较纯SiO2气凝胶提高了50％.     

Preparation and photocatalytic activity of Cu^2＋-doped TiO2/SiO2

Cu2+-doped nanostructured TiO2-coated SiO2. (TiO2./SiO2) particles were prepared by the layer-by-layer assembly technique and their photocatalytic property was studied. TiO2 colloids were synthesized by the sol-gel method using TiOSO4 as a precursor. The experimental results showed that TiO2 nanopowders on the surface of SiO2 particles were well distributed and compact. The amount of TiO2 increased with the increase in coating layers. The shell structure appeared to be composed of anatase titania nanocrystals at 550℃. The 2-layer coated TiO2 particles on the surface showed a higher degradation rate compared with all the dif-ferent-layer samples. The photocatalytic activity of Cu2+-doped TiO2/SiO2 was higher than that of undoped TiO2/SiO2. The optimum dopant content was about 0.10wt%.     

Preparation and Properties of Ag-TiO_2 Thin Films on Glass Substrates

1　ＩｎｔｒｏｄｕｃｔｉｏｎＩｎ 1970ｓ ,ｔｈｅｐｈｏｔｏｃａｔａｌｙｔｉｃｐｒｏｐｅｒｔｙｏｆｔｉｔａｎｉｕｍｄｉｏｘｉｄｅ (ＴｉＯ2 )ｗａｓｆｏｕｎｄｂｙＦｕｊｉｓｈｉｍａｅｔａｌ[1] .ＴｉＯ2 ｉｓｗｈｉｔｅｉｎｃｏｌｏｒ,ｉｎｅｘｐｅｎｓｉｖｅ ,ａｎｄｎｏｎｔｏｘｉｃ .Ｂｅｃａｕｓｅｏｆｉｔｓｓｔｒｏｎｇｐｈｏｔｏｃａｔａｌｙｔｉｃｅｆｆｅｃｔ ,ＴｉＯ2 ｉｓｕｓｅｄｉｎｔｈｅｔｒｅａｔｍｅｎｔｏｆｗａｓｔｅｗａｔｅｒａｎｄｔｈｅｐｕｒｉｆｉｃａｔｉｏｎｏｆａｉｒａｓａｎａｎｔｉｂａｃｔｅｒｉａ…     

等离子体处理Tencel织物的TiO_2/SiO_2溶胶自清洁整理

利用等离子体对Tencel织物进行预处理,然后使用TiO_2/SiO_2凝胶对织物进行自清洁整理,以提高Tencel织物的自清洁性能。采用扫描电子显微镜(SEM)、视频光学接触角测量仪、电脑测色配色仪和紫外可见近红外分光光度仪对织物的表面形态、亲水性、自清洁性和防紫外性进行了表征。K/S值的下降表明等离子体处理能够降低污渍在织物表面的上染,ΔE值的显著提高显示不仅经过等离子体预处理的织物自清洁性能得到显著提高,UPF值的增加表明等离子体预处理织物的紫外性能得到提高。     

Ti O2／Si O2复合光催化剂制备工艺参数优化及其表征

先以无机钛盐、硅酸盐为原料制取聚合硅酸硫酸钛,再通过液相水解法制得TiO2/SiO2复合光催化剂,并用SE M、X R D、BE T和甲基橙脱色率对复合光催化剂进行表征. 结果表明,TiO2/SiO2复合光催化剂制备优化工艺参数为：Ti（S O4）2作钛源、Ti/Si摩尔比为12 ： 1、水解反应p H值为6、煅烧温度为650oС,以此条件制备的复合光催化剂对甲基橙脱色率可达98 .6 %以上;TiO2/SiO2复合光催化剂为一种分散均匀的纳米级球形颗粒,其成分为以锐钛矿为主的TiO2,SiO2的复合有效抑制了TiO2晶粒的生长,同时提高了TiO2的热稳定性.     

Preparation of TiO_2 Thin Film and Its Antibacterial Activity

1　IntroductionInrecentyears ,theuseofinorganicantimicrobialagentshasattractedinterestforthecontrolofmicrobes[1-3 ] .Thekeyadvantagesofinorganicantimicro bialagentsareimprovedsafetyandstability ,ascomparedwithorganicantimicrobialagents .Atpresent,mostanti…     

液位沉降法制备 Ti O2薄膜及其性能研究

以钛酸丁酯为前驱液,无水乙醇为溶剂,乙酰丙酮为稳定剂,制备了 TiO2溶胶,采用液位沉降法在清洁的玻璃衬底上镀制TiO2薄膜。研究了添加剂聚乙二醇（1000）、p H、衬底温度对 TiO2溶胶在玻璃基板上附着性的影响;研究了液位沉降速度、容器倾角以及溶胶附着性对TiO2薄膜厚度的影响。考察了TiO2薄膜的表面形貌、晶相、光催化性能。结果表明,采用PEG与 Ti4＋的质量比为1,不调节pH的TiO2溶胶,在沉降速度为7 cm/min ,容器倾角为30°所制得的TiO2薄膜的光催化性能最好,光照3 h时其光催化降解率高达52.1％。     

纳米无机添加剂对聚偏氟乙烯膜的疏水性影响

使用非溶剂致相分离法制备聚偏氟乙烯(PVDF)膜,考察了不同铸膜液浓度下PVDF膜的疏水性,研究添加疏水性纳米粒子对PVDF膜疏水性的影响.结果表明:PVDF膜的疏水性随着铸膜液中PVDF含量的升高而降低,疏水性随着纳米颗粒添加量的增大而升高;当铸膜液中PVDF质量分数为10%,纳米SiO2质量分数为2.5%时,PVDF膜的接触角可达136°;当铸膜液中PVDF质量分数为10%,纳米TiO2质量分数为15%时,PVDF膜的接触角可达141°.     

金红石型TiO2/锐钛矿型TiO2/SiO2三元复合薄膜的合成

采用水热法,以钛酸正丁醑为初始原料,在FTO基底上沉积了金红石型TiO2纳米棒阵列,然后利用锐钛矿型TiO2纳米粒子及无定形SiO2对纳米棒进行了表面修饰,获得金红石型TiO2/锐钛矿型TiO2/SiO2三元复合薄膜.扫描电镜及X射线衍射分析结果表明,在FTO表面上沉积的TiO2为金红石型单晶纳米棒,其尺寸随反应时间的增加而增大.电化学测试结果表明,随着纳米棒尺寸的增大,相应复合薄膜的电化学反应电荷转移阻力增大.2种TiO2晶型混合引起的电子-空穴分离效应及混合的均匀程度直接影响到复合薄膜的光催化活性.水热反应7h得到的纳米棒阵列相应的复合薄膜显示了较好的电化学性能及光催化活性.     

直流反应磁控溅射氧化物光学薄膜及其性能研究

本文报道了应用直流反应磁控溅射技术淀积透明的TiO 2、Ta_2O_5、ZnO、Al_2O_3等氧化物光学薄膜。研究了这些氧化物薄膜的光学和机械等性能;讨论了反应溅射的SiO_x薄膜其光学吸收的反应动力学原因;摸索了TiO_2薄膜的性能与溅射镀膜条件的关系;研究了TiO_2薄膜的晶相结构;观察了TiO_2和ZnO薄膜的表面微观形貌。     

聚乙二醇添加量对TiO_2薄膜光催化性能的影响

采用溶胶－凝胶法,以钛酸丁酯为前驱体,以不同添加量的聚乙二醇（ＰＥＧ,分子量２０００）为添加剂． 在普通载玻片上制备结构可控的多孔ＴＩＯ２纳米薄膜。结果表明：通过调节ＰＥＧ添加量,可以有效地调控薄 膜的结构（如孔径和孔分布）,增大比表面积,进而可提高光催化活性。     

PVDF/TiO_2复合平板超滤膜的制备与性能研究

采用自制纳米TiO2溶胶、商品化纳米TiO2粒子溶胶表面涂覆PVDF膜制得PVDF/TiO2复合膜.通过纯水通量、截留率、接触角以及抗污染性能等实验,考察了不同粒径、浓度的纳米TiO2溶胶对PVDF膜性能的影响,并利用FT-IR和SEM表征了该复合膜的微观构造.结果表明:复合膜的分离性能得到提高,且自制纳米TiO2溶胶改性的PVDF膜综合性能较优异,其接触角由改性前的85.0°降至46.0°,并且去离子水清洗50min后,通量恢复率稳定在95%以上;FT-IR分析显示,复合膜表面羟基数有所增加;SEM观察表明,在PVDF膜表面镶嵌和吸附有一定量纳米TiO2粒子使复合膜呈现出良好的抗污染性能.     

316L不锈钢等离子渗钛-热氧化制备TiO2膜及性能

为了提高316L不锈钢的表面性能,以满足其在医用环境下服役的要求,利用等离子表面合金化和真空热氧化复合处理技术,在316L不锈钢表面制备TiO₂薄膜。借助金相显微、辉光放电发射谱（GDOED）、x-射线光电子谱（XPS）和x-射线衍射（XRD）分析薄膜的组织结构,以蒸馏水为对象进行光诱导超亲水性试验,用球-盘磨损试验对比测试薄膜与基体的摩擦学性能。结果表明：薄膜均匀致密,Ti、O元素沿层深呈梯度分布,具有锐钛矿型TiO₂结构; 薄膜具有较高的亲水性,可见光照射下,30 min内接触角降为8.5°; 在7.6 N负荷下,薄膜与Al₂O₃陶瓷球对磨时的摩擦系数为0.30~0.40,磨损率仅为1.14×10^-4 mm³·N^-1·m^-1,复合处理后薄膜耐磨减摩性能指标明显优于不锈钢基材.